STRESS-induced twin boundary motion in the AuCd ß'phase (52.5 at. pct Au 47.5 at. pct Cd having an orthorhombic structure (space group D h)' was discussed for the case of transformation twins.' Mechanical twinning, i.e., introduction of new twin orientations by the applied stress was sometimes observed in the ß' phase which contained two transformation twin orientations. (See Ref. 2 for experimental details.) The transformation twins terminated at the mechanical twin boundary; the two initial orientations having been twinned to the new orientation as shown in Fig. l. In a "hard" tensile instrument, formation of each mechanical twin was accompanied by a sharp drop in load (and an audible click) resulting in a typical serrated load-extension curve. The mechanical twins increased in width and additional twins were nucleated as the load increased until the entire specimen was occupied by the mechanical twin orientation. A restoring force2 caused the mechanical twin and transformation twin boundaries to return towards their initial configuration on releasing the load. In a stabilized specimen* the total strain introduced by mechanical twinning was recovered on releasing the applied stress. Initial and final microstructures were identical. After decreasing gradually to a critical width, mechanical twins suddenly disappeared accompanied by audible clicks and sharp increases in load (measured at a constant rate of crosshead motion in a "hard" machine). Mechanical twins could be stabilized in any position by maintaining the applied load for a sufficient time, indicating a decrease in restoring force with time similar to that observed for transformation twins.' Orientation relationships for mechanical and transformation twins were determined and are shown in Fig. 2. The mechanical twin, T3, was twin related to transformation twin, T,, by reflection in (1ll), and twin related to transformation twin, T2, by reflection in (111)T, . T, was related to T, by reflection in(ll1)T1 . The "average" mechanical twin composition plane lay several degrees from (1ll), . In every specimen which mechanically twinned, orientation T3 was most highly favored by the applied stress, i.e., it was the twin orientation which provided the greatest change in length compatible with the direction of applied stress

Jan 1, 1961

IN comparing the living conditions of the worker or peasant of the past with those existing today, his-torians might point out many strange contrasts. From the Doomsday Book we learn that at the time of Wil-liam the Conqueror the 1,375,000 inhabitants of Eng-land and Wales owned less than 1000 horses and 5000 oxen. Even as recently as 1871 when England and Wales had a population of 31,845.000, the total number of horses in the country was estimated at 1,110,000. Compare the necessary drudgery of labor in those days with conditions in Canada today where a population of less than ten million people own 3,500,000 horses. Re-member that there is also a turbine installation in` this country of more than four million horse-power, besides steam boilers and locomotive and automobile engines which reduce the traction and hand labor of the farm and factory. Frequently, poetic license has glossed over the poverty and hardship of the common people in the "good old days," and the imagination has created an idyllic world, far from being justified by the condi-tions which actually prevailed. Simon Patten's de-scription of the Middle Ages as "A Thousand Years Without an Ice Box" came nearer portraying the true situation. No one is likely to forget that the discovery of America was an incident in Europe's attempt to find a short route to the Indies, but the fact is usually for-gotten that the summer diet in Europe in 1400-an ice-less age-was such that spices were more precious than gold. Though the glamor of the Indies may never sur-round the modern refrigerator, certainly the modern housewife is likely 'to feel that the applied art called "cookery? may attain to higher levels with the assist-ance-6f such an adjunct. Those who have spoken slightingly of the uniformity of the modern apartment and have eulogized some of the exceptional hand-made furniture which has been bequeathed by former generations, have failed to com-pare modern house furnishings with those in the typical peasant's hovel. Machine-made furniture, though with-out particularly good lines, contrasts quite favorably with the pile of rags in the corner, and the poorest gas or oil stove is better than an open fire on a dirt floor. The scientist's application of the theories of physics, chemistry, biology and mathematics .to practical prob-lems has brought about a series of kaleidoscopic trans-formations in agriculture, industry and commerce. Large scale production, improved means of communica-tion and the prevailing higher standard of living are terms which imply a very human meaning when in-terpreted as actual changes in individual living. Though the student and the teacher may deprecate the influence of commercialism upon science, humanity as a whole has received great benefits from the close relationship which has developed between science and industry, and industry in turn has done much for science through the building and endowment of laboratories and by supply-ing funds to maintain research workers.

Jan 11, 1927

By R. A. Oriani

The partial molal volume of hydrogen is one of the parameters that describe the elastic interaction between the solute and the stress fields about inclusions, dislocations, and cracks. As such the partial molal volume is probably of importance in the elucidation of phenomena such as hydrogen embrittlement and hydrogen yield point. A knowledge of this quantity would also be helpful in thinking about the state of dissolved hydrogen in iron. However, because of the very low lattice solubility of hydrogen in iron the usual ways of determining the lattice expansion are not practicable. It is therefore of interest to apply the thermodynamics of stressed bodies to two sets of measurements of the effect of elastic stress upon the permeability of hydrogen in order to deduce a value of the partial molal volume, VH, of hydrogen dissolved in a iron. Beck ..' and previously de Kazinczy, observed that a uniaxial tensile stress increases the permeability of hydrogen in iron and in various steels. Beck et 01. employed Armco iron and A.I.S.I. 4340 steel, whereas de Kazinczy used a steel the composition of which was 0.13 C, 0.23 Si, 0.46 Mn, 0.006 P, and 0.038 S. Upon releasing the stress the permeability increment disappeared if the stress was below the elastic limit. Both investigators employed cathodic charging to introduce the hydrogen. de Kazinczy measured the permeation through a thin-walled tube by collecting the gas, whereas Beck et al. measured the permeation through sheets of various thicknesses by a very sensitive electrochemical technique. Both investigators measured the steady-state permeation at constant rate of hydrogen ion discharge, and Beck measured in addition the hydrogen diffusivity by a time-lag technique which is independent of the boundary conditions. Beck et al. and de Kazinczy found a linear relationship between log (J,/Jo) and the stress, where Ju/Jo is the ratio of the flux of hydrogen when the metal is under uniaxial tensile stress, a, to the flux under zero stress, for the same temperature and charging current. Beck et al. found in addition that the diffusivity of hydrogen is not changed by stress. Both investigators concluded that the observed change in permeability is due to an increase in hydrogen concentration, and furthermore that the increase in concentration is due directly to the thermodynamic effect of stress upon concentration. Accepting this assessment of the situation for reasons given below, one may use the equation3j4 in order to evaluate I/H, the partial molal volume of hydrogen. This equation is valid for the domain of a/E «¦ 1 (where E is the Young's modulus) and under the assumption that hydrogen expands the lattice isotrop-ically. From the data of Beck el al, one calculates V7H - 2.0 cu cm per g-atom, and from those of de Kazinczy one obtains 1.8 cu cm per g-atom. That the increase of concentration with stress is indeed of thermodynamic origin is attested to by the facts that the experimental results conform to the thermodynamic relation, Eq. [I], and that the results are the same whether a pure iron1 or each of two different steels172 is used. Neither of these facts wou1.d necessarily be expected if the effect of stress were, rather, to increase the ratio kn/k, of the kinetic factors of the following competing reactions: H(ads) — H (dissolved) Such a change of kinetics at the surface could be an alternative explanation of the effect of stress on the permeability. Although this writer does not deem this explanation to be the correct one for the reasons given above, it must be admitted that unambiguous proof that the phenomenon has a thermodynamic origin does not yet exist. Two kinds of experiments may be suggested. One is to plate a variety of metals on the input surface of the steel and repeat the stress experiment at a variety of hydrogen charging currents. The other is to employ somewhat thicker specimens in order to be able to apply uniaxial compressive stress. Eq. [I] shows that ln(c,/c,) depends on the sign of the stress, but it is difficult to see a physical basis for which k2/kl would depend on the sign of a. The present value of V^ in a iron agrees with phragmen's5 estimate, which he based on comparisons with the lattice expansion by hydrogen of titanium, zir-

Jan 1, 1967

By AIME AIME

THE autumn is the time that nearly all the special groups within the broad field of the Institute's activitives chose for their own special meetings. The big annual meeting in New York in February has its own special advantages, but to realize them involves sacrificing others. A meeting of a smaller group with the subjects brought up for discussion much more closely limited to a single field of interest has some advantages that a big general meeting cannot possibly have. And so the custom has gradually developed of having these smaller meetings in the autumn, at con¬venient places, so the men will not have to travel too far from the job to be present. Sometimes the meetings have for their field of interest a single phase of mineral technology, and are called divisional, and at other times they cover a diversity of topics that are locally important in that geographical area, and are then called regional meetings. Of the five meetings to be held this fall, four are divisional and one regional. Two of the divisional meetings are to be held in the same place at the same time, but with programs so arranged that they do not conflict.

Jan 1, 1930

INTRODUCTION The after-tax rate of return that properly discounts future cash flows is usually referred to as the "discounted cash flow-rate of return" (DCF-ROR). The method is also referred to as the internal rate of return, true rate of return, and investor's rate of return in some literature. According to Stermole (1974, p. 188) industry polls indicate that the DCF- ROR method is the number one economic evaluation decision method used by more than 90% of the industrial companies that use for- mal economic evaluation procedures. Other economic evaluation methods that have been used in the past, such as payback period, accounting ROR, etc., have largely given way to DCF-ROR analysis because they fail to account properly for the time value of money. DCF-ROR is generally defined as that rate of return that makes the present worth of future generated cash flow over the life of the project (including after tax salvage value) equal to the present worth of all after-tax investments. The "present worthing" of future cash flow involves discounting future cash flow to a present value according to the mathematics of compound interest at some interest rate. The determination of the interest rate that equates the present worth of future after-tax earnings with the present worth of all after-tax investments necessary to create such earnings is properly called the discounted cash flow rate of return analysis. Although present worth calculations are usually used for determining the DCF-ROR, the same results can be obtained by comparing income and costs of any equivalent point in time, i.e., future worth, etc.

Jan 1, 1980

By H. E. Swanson

A description of the field apparatus has been published by D. G. Brubaker. Data from laboratory model studies of the in-line and broadside methods of operation are detailed. The conductor models include a single sheet conductor at several strike and dip angles and a schistose-type conductor. In addition, data on the effects of the strike length and of the depth of the conductor are presented for the broadside method of operation. All of the data show that the inclintion reverses direction over the top edge of dipping single sheet conductors. Differences between anomalies over conductors dipping between 90" and 30" are subtle,but flat-lying sheets can be readily distinguished from steeply dipping sheets. Schistose conductors are easily distinguished from single sheet conductors, and a procedure is given for determing the direction of schistosity. The depth of penetration under ideal conditions is 0.7 of the coil separation. In 1950, The New Jersey Zinc Co. (of Pa.) developed a lightweight apparatus for electromagnetic prospecting. A description of this apparatus has been published by D. G. Brubaker.1 It consists of a small, battery-powered vertical source coil and a direction-finding receiving coil. Source and receiver are kept a fixed distance apart and move as a unit along the survey lines. At each receiver station the inclination of the magnetic field created by the source is measured. Two methods of operation are used, in each of which measurements are taken with a constant source-to-receiver distance and with the plane of the source oriented to pass through the receiver station. In one procedure, called the in-line method, source and receiver travel in tandem along the same line. In the other procedure, called the broadside method, source and receiver move along adjacent lines, with the source-to-receiver direction oriented parallel to the assumed strike direction. The data recorded in either case are the inclinations, measured in degrees from the horizontal, of the magnetic field created by the source. These data are plotted at the receiver stations on a map. Scale-model studies of both methods of operation have been conducted in the laboratory and are reported in this paper. APPARATUS Small source and receiving coils wound with many turns of fine copper wire were used to produce and measure an alternating magnetic field in the same manner as the field apparatus. The model source coil was mounted in a vertical position and oriented so that the receiving coil was in the plane of the source. The receiving coil was mounted in a frame so it could be rotated to obtain the inclination measurements. The source coil was excited by a 100-kc signal generator. A tuned amplifier and a voltmeter were used to detect the null position of the receiving coil. The coils used in the field apparatus are usually spaced about 400 ft. The coils used in the model work were spaced from 4 in. to 4 ft apart. Thus the scale of the model work ranges between 1/1200 to 1/100 natural size. The model conductors were aluminum-coated building paper supported on wooden frames. The conductivity-thickness product was measured using a four-electrode system and was found to be about 300 ohms-'. CONDUCTIVITY CONSIDERATIONS The electromagnetic response from a thin sheet conductor is a function of the product of the conductivity of the sheet times the thickness of the sheet times the frequency of the alternating electromagnetic field times some linear dimension of the system such as the coil separation which indicates scale. The secondary electromagnetic field produced by the conductor increases in amplitude from zero at zero conductivity to a maximum value for infinite conductivity, while the phase of the secondary field with respect to the primary field shifts from 90" at zero conductivity to 0" at infinite conductivity. Several authors2-' have shown that most of both the increase in amplitude and the change in phase of the secondary field takes place over a three-decade range of the conductivity-thickness-frequency product. Only small changes in the amplitude and

Jan 1, 1961

By A. L. Bailey, B. A. Landry

All who are even generally aware of the tremendous rate of increase in coal washing operations must realize the growing importance of the float-and-sink test. I believe it is conservative to estimate that, in the past decade, the dollar volume of float-and-sink testing has increased tenfold. It is a simple matter of economy, then, to examine the factors that determine the cost of adequate float-and-sink testing. When the Coal Preparation Section of the Bureau of Mines entered upon a greatly expanded program of such work in connection with the synthetic liquid fuels investigations, it seemed advisable to examine these factors experimentally. The principal consideration that differentiates float-and-sink test sampling from general purpose sampling, is that the original particle size must be preserved. Therefore, the total cost of the test will be directly affected by any standard that might be proposed to limit sample bulk reduction at any given particle size. For this reason, the relationship of sample size to variability of results was the first factor to be studied experimentally. Of course, the matter is rendered complex by the circumstance that the float-and-sink test, not a simple analytical measurement but a process test, comprehends a number of more-or-less independent items of fundamental data; and as shown in the report, the' variability of the samples differs with respect to these different items. This condition and the wide variety of situations in which float-and-sink test data are used, in combination with other factors, to study complex process operations, indicate the difficulty of setting up fixed standards for float-and-sink sampling and testing. At this stage at least, it is the intent rather to obtain experimental data on the principal Factors involved so that the reader may arrive more intelligently at a procedure adapted to his problem. The authors of this paper have presented experimental data showing the relationship between size of sample and particle size for different variability tolerances with respect to percentage of sink. In further studies, data are being collected to appraise also the variability of the samples with respect to float-ash content and size consist. The scope of this work will be broadened to cover particle sizes up to 4 in., and a third series of tests has yielded similar data for a much cleaner type of raw coal. Thus, the further studies will make available a fairly comprehensive meas- ure of variability with respect to size consist, percentage of sink, percentage of middlings, and percentage of ash in the float, for three coals ranging from 3.87 to 17.68 pct in refuse content (heavy sink material) and from 4.18 to 17.52 pct in middlings. Introduction At present there are no published standards for float-and-sink test sampling. During the rapid expansion of float-and-sink test work, varying procedures have been based on adaptations of the ASTM standards for sampling coal for analyses. For this reason, a special study of gross sample reduction has been undertaken to determine the limits for this step in the operation where no reduction in particle size is to be made before testing. Float-and-sink tests are made whenever a thorough study of coal characteristics is desired. The tests may be made on samples from coal-cleaning units such as jigs or tables, or coal samples may be tested which are taken from a loading boom, railroad car, or the coal seam itself. The resultant gross sample may be large and pose a problem of sample reduction. The question is, then, how much can the sample be reduced and still fall within preassigned limits of accuracy of the original gross sample of coal? Coal from channel samples may be crushed to liberate impurities and then separated into various gravity fractions from which washability curves are drawn; from these curves, it is possible to determine the cleaning characteristics of the coal. However, coal samples from coal-cleaning units cannot be

Jan 1, 1950

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,' whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham's work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy' found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By Lawrence A. Soltis

Senior engineering or executive management positions are filled by engineers who are evaluated on their performance, knowledge, skill, and maturity. Not only is technical expertise required but a knowledge of sales and marketing, finance, law, industrial relations, and public affairs is necessary. The University of Wisconsin-Extension offers an innovative post-baccalaureate degree program blending technical and professional subjects the Professional Development Degree in engineering (PDD)-designed to bring various opportunities for learn-

Jan 4, 1978

HENRY M. HOWE, Bedford Hills, N. T. (communication to the Secretary?).-The authors valuable results as to the effects of the air-hardening temperature on high-speed steel may be summed up thus: Influence of Rising Air-Hardening Temperature on. High-Speed Steel Air-hardening microstructure Cutting Properties temperature S Austenite Grain Free Carbide Grains Boundaries Too low Small or Narrow Maximum Too soft undeveloped Intermediate, Well-developed Intermediate Little or even Best correct none Too high Coarse hide, even with Minimum . Weak, brittle, three-rayed crumbling stars Here the suggestion is that as the air-hardening temperature rises it causes two prominent effects, one helpful and the other harmful, the increase of the former exceeding that; of the latter up to a certain point, at which the steel is most useful, and then in turn being outrun by it. The first is the progressive dissolving of the free carbide in the austenite, increasing the stability of the red-hard state. The second is the progressive coarsening of the grains, and thickening of the intergranular cement, developing at last into spandril-like three-rayed stars of the 1,288° specimen. (2,350° F.) of Plate D, thus giving clear proof of incipient fusion, that is of crossing the solidus. This causes intergranular weakness. The individual grains may have great red-hardness, but they do not cohere. They approach the condition of a bag of emery grains.

Jan 6, 1917

By Walter J. Johnson

The coals in northern Wyoming and Montana are free-burning and non-caking and range from lignite to bituminous C in rank. Strip and underground mining are employed to supply railroad, utility, industrial, and domestic fuel. The market area includes Iowa, Nebraska, Minnesota, North and South Dakotas, Wyoming, Montana, the Pacific Northwest, and western Canada. THE larger producing coal mines in northern Wyoming are located in the Powder River Basin lying between the Black Hills region of South Dakota, eastern Wyoming, and the Big Horn Mountains in north central Wyoming, see Fig. 1. The mines are located particularly in the area along the route of the Chicago, Burlington & Quincy Railroad from Gillette, Wyo., to a point approximately 15 miles northeast of Sheridan, Wyo. Fig. 2 is a graph of coal production in the state of Wyoming from 1918 to 1951. Across the Big Horn Mountains lies the Big Horn Basin, situated between the Big Horn Mountains and the Rocky Mountains proper. Mining in the Big Horn Basin is almost entirely confined to a small area known as the Gebo Field, near the town of Kirby, which is located on the Chicago, Burlington & Quincy Railroad. This paper will describe present operating areas, making only brief reference to the history of mining and marketing primarily because of the large area to be discussed. The coal beds presently mined in the Powder River Basin are all of Tertiary age and are of Fort Union and Wasatch formations of Paleocene and Eocene ages, see Fig. 3. The Fort Union formation, consisting of 2000 to 3200 ft of alternate sandstone, shale, and coal, is divided from oldest to youngest into the Tullock, Lebo Shale, and Tongue River members. Most of the mineable coal is in the Tongue River member, which is 500 to 800 ft thick. The Carney coal bed, varying from 7 to 20 ft in thickness, is considered the base of the Tongue River member. About 85 ft above the Carney is the Monarch bed, ranging from 18 to 42 ft in thickness. At approximately 210 ft above the Monarch is what is locally known in the Sheridan district as Dietz No. 3 bed, which varies from 12 to 30 ft in thickness. One hundred feet above the Dietz No. 3 is Dietz No. 2 bed, which is 7 to 12 ft thick. At about 100 ft above the Dietz No. 2 is Dietz No. 1 bed, 7 to 15 feet in thickness. Two hundred and fifteen feet above Dietz No. 1 is the Smith bed, approximately 5 ft thick. One hundred twenty-five feet above the Smith is the Roland bed, which is estimated to be approximately 13 ft thick. The Roland bed is considered the base of the Wasatch formation, which in the Powder River Basin is 1000 to 3500 ft thick and is composed largely of shale, sandstone, and coal. The foregoing measures are the only ones above the Tongue River member that have been mined in the Sheridan field. To the east of the Sheridan field, particularly in the area of Gillette, the Roland bed is considerably thicker and is considered the thickest and most extensive coal bed in Wyoming, reaching a maximum thickness of 106 ft. From 125 to 225 ft above the Roland lies the Arvada bed, average thickness 9 ft. Three hundred seventy-five to four hundred feet above the Arvada is the Felix bed, which reaches its maximum thickness of 30 ft near Echeta on the Chicago, Burlington & Quincy Railroad. East of the Powder River the bed averages more than 10 ft in thickness, but it thins in a northwesterly direction. The highest mineable coal in the Powder River field is the Healy bed, about 400 ft above the Felix bed and exposed only in the highest parts of the area where much of it has been burned along the outcrop. Where it has not been burned, the thickness at most of the outcrops is 10 to 15 ft.

Jan 1, 1954

By H. Foster Bain

[Secretary's NoTE.—This paper, presented in oral abstract at the San Francisco meeting, was not at first supposed by Mr. Rain to be required for publication in the Transactions; and the excursion to Japan, in which he took part, immediately after the San Francisco meeting, delayed his presentation of the manuscript. After his return to San Francisco, Mr. Bain, in view of the importance of his paper and its discussion, kindly furnished it in full. The delay in its publication (since it was received in April last) has been due, partly to the circumstance that other contributions had meanwhile acquired the " right of way," and partly to the consideration that, the situation contemplated in Mr. Bain's paper having remained practically unchanged, the paper and its discussion would not lose force or timeliness by this lapse of time.—J. S. ] No acute observer of public affairs can have failed to observe a growing disposition on the part of the public to change emphasis in government from political equality to social justice. When our own government was founded it was felt to be sufficient to secure to each individual the fullest possible freedom of opportunity, and such a scheme was excellently adapted to the rapid development of a large territory having a small population. As the number of people in a given area increases, there are more points of contact and conflict; each must move in a smaller orbit, and there must be more regula-

Jan 1, 1913

By A. G. Metcalfe

THE failure to detect any change in the thermal properties of cobalt at the Curie point would appear to indicate that the apparatus may have a limited sensitivity. The Curie temperature has been determined by direct methods to be 1121+3°CP and 1131°C.3 The specific heat has been determined many times'.' and weighted values are given in Table I. The allotropic transformations in iron and titanium, used by the authors to test the experiment method, involved a volume change of the order of 3 pct on going from the close-packed to the body-centered-cubic lattice. These energy changes are likely to be much larger than those involved in a diffusionless transformation from a hexagonal to a cubic-close-packed lattice. However, it has been pointed out that thermal observations are unreliable in the detection of phase changes when these are near a Curie point.' James 0. McCaldin and Pol Duwez (authors' reply)—The sensitivity of the present technique is limited to first-order transformations, so that gradual changes in specific heat, e.g., in the vicinity of Curie points, are not detected. Furthermore, the existence of first-order transformations with latent heats much smaller than those occurring in the known allotropic transformations of iron and titanium is, we agree, still pending.

Jan 1, 1956

By Blake M. Caldwell, Harrold D. Owen

The continued use of permanent-type, we11 completion Iras pointed LIP the need for more powerful through-tubing perforating equipment. A new expendable shaped charge perforator has been developed in which the charges are run through the tubing in a vertical position and then opened out to a horizontal position when at the desired shooting zone. The performance of this new tool is comparable to that of conventional casing type perforators. This paper describes the new tool and its applications. Performance data in targets rind under various actual well conditions are presented. INTRODUCTION The general acceptance and increasing use of pernianent-type well completion by the oil industry has indicated the need for through-tubing perforating equipment with performance comparable to that of conventional casing type perforators.'.' To achieve the performance desired, a new, expendable, shaped charge perforator has been developed with adequate power for effectively perforating both 51/2-in. and 7-in. casing below tubing. This has been accomplished without resulting severe damage to the casing and can he obtained under extremes of pressure and temperature. The design of this new tool is a radical departure from previous concepts of tubing guns since it was felt that the two major limitations imposed by previous designs severely handicapped performance. The first of these limitations was the restriction imposed upon the length of the charges by the necessary small inside diameter of the carrier. This resulted from the necessity for compromises in designing a hermetically sealed gun small enough to allow free passage through 2-in. tubing, yet with sufficient wall thickness to withstand some minimum pressure. In an effort to overcome this limitation, the charges were in some cases placed at an angle with the axis of the well with resulting loss in effective depth of penetration. The second limitation concerned the extreme distance of the charges from the casing when the gun was fired. An example of the latter situation is demonstrated by the fact that a conventional 13/4-in. tubing gun centralized in 51/2-in., 17-lb casing has a clearance of more than 1-9/16-in. on all sides. This means that a considerable portion of the force from each charge must be expended in penetrating this 1-9/16-in. of well fluid before it even reaches the casing. With the gun centered in 7-in., 23-lb casing, the amount of fluid penetration required of each jet is in excess of 21/4-in. In a situation where the 13/4-in. gun is touching one side of the 51/2-in., 17-lb casing, the jets from the charges on the opposite side have more than 3%-in. of fluid to penetrate. A similar situation in 7-in., 23-lb casing necessitates the penetration of more than 4-9/16-in. of fluid. The penetrating effect of the charges is severely impaired in passing through so much fluid. Under such conditions, there is usually insufficient force left to penetrate the casing. Previous studies have shown the decided disadvantage of having to shoot through such an excessive quantity of well fluid.'.' The problem. then, was how to position large powerful charges close to the casing prior to firing and still manage free passage through 2-in, tubing. The solution appeared to be in some method of folding sealed charge units in an open type, expendable. 13/4-in. carrier for travel through the tubing, and unfolding them upon their arrival at the shooting zone in the casing. It was desired to control the mechanism electrically from the surface through the regular shooting cable, making the release of the charges independent of the physical characteristics of the well, yet with a provision to prevent the gun from firing until the

Jan 1, 1955

By F. G. Tahmoush, N. J. Grant, E. P. Abrahamson

The effect of grain size on the brittle -ductile transition temperature of pure iron and three dilute Fe-W alloys has been investigated by slow bend tests. The brittle-ductile transition temperature for pure iron increased with increasing grain sizes from 8000 to 500 grains per sq mm where the transition temperature then decreased with further increase in grain size. The dilute additions of tungsten lowered the transition temperature for fine grain sizes, suppressed a reversal of the curve in the coarse grained portion, and raised the transition temperature for this region. The frequency of twin occurrence increased with increasing grain size and decreasing temperature. The object of the present investigation was to re-examine the effect of grain size on the brittle -ductile transition of pure iron and several dilute Fe-W alloys. Current literature normally presents a simple relationship between grain size and the brittle-ductile transition temperature, namely, that the transition temperature increases with increasing grain size. Heslop and etch' have studied the transition temperature of mild steel by V-notch Charpy impact tests for the grain size range between 200 and 6000 grains per sq mm. The result was a linear plot of In 1-1/2 vs brittle-ductile transition temperature, where 1 is the grain diameter. Recent experiments by sipos2 revealed the possibility of a reversal in the slope of the grain size vs transition temperature plot for pure iron; however, his investigation was limited in scope, and the data obtained were insufficient to permit a definitive curve. The present investigation was undertaken in an effort to confirm or extend the grain size effect observed in iron by Sipos. PROCEDURE All alloys were vacuum induction melted, using 99.95 pct Fe containing 0.03 pct 0 and 0.004 pct C. Four ingots were made, ranging from pure iron to iron with 0.035 pct W. The chemical composition of each alloy, after processing, is given in Table I. The four alloys were prepared as 45 lb heats and cast into 4 in. diam by 16 in. molds. They were then extruded into 3/4 in. rods at 1800oF. Specimens for chemical analysis, taken from various positions along the rods, revealed no variation in tungsten content along the length. The extruded rods were reduced to 0.156 in. diam stock by a series of cold swaging operations involving intermediate vacuum annealing treatments. This procedure yielded a final cold reduction in area ranging from 10 to 90 pct. The swaged rods were chemically cleaned, cold pressed to a cross section of 0.10 by 0.18 by 1.0 in. long (2.54 by 4.73 by 25 mm). The specimens were wrapped in iron foil and vacuum sealed (10-4 mm Hg) in quartz. Various heat treatments at temperatures from 700" to 1300oC were utilized to produce grain sizes from 8000 to 1 grain per sq mm. Grain sizes were determined by measuring the average area of grains in a polished section. In specimens with grain size greater than 20 grains per sq mm, the total number of grains in the cross section was counted and then divided by the area to yield grains per sq mm. Grain size was measured both for longitudinal and transverse cross sections. The average of the two measurements was plotted vs transition temperature. An Instron Table Model testing machine was used to determine the transition temperature of specimens tested in three point horizontal bending. The specimen was supported by two 1/4 in. dowels one in. apart. Bending was accomplished with a push rod, the end of which had an 1/8 in. radius. The head speed was 50 in. per min. Temperatures were established through the use

Jan 1, 1963

By Luis Toron, Salvador Cortes-Obregon

John D. Price (Colorado Fuel and Iron Corp., Pueblo, Colo)—The paper on the coal fields of the Oaxaca district as prepared by engineers Toron and Cortes-Obregon of the staff of the Bank of Mexico bears witness to the thorough and careful way in which the men associated with this organization perform their work. There is little to be added to their paper in way of discussion other than to confirm and amplify some of their statements. Since the only extensive and well-developed field of coking coal lies in the northeastern section of the country adjacent to Sabinas in the state of Coahuila, it follows that blast furnace plants would be located in that same region. Two such plants are now operating at Monterrey and Monclova, using coke produced at the Sabinas district mines. But the nearer of these two plants is 600 miles from Mexico City and even farther from the center of population. Transportation of products from these mills to the market area is therefore expensive, both because of the distance and the difficulty of the terrain over which it must be carried. The development of an integrated steel industry closer to the center of population has therefore long been a goal toward which the Mexican technicians have been striving. While the presence of coal of some grade has been reported in many of the states, and many ideas have been advanced regarding its possible uses in iron and steel production, deposits of anthracite in Sonora and the various coals of the Oaxaca district as reported on in this paper are the only ones that have been explored in a serious manner. The coking coal from the Mix-tepec zone appears to offer promise of producing a coke which could be used in a standard blast furnace. Several problems are indicated, however: 1—The ash in the coal is high as mined, but indications are that it can be washed to an ash content of 15 pct with a recovery of 70 pct of washed coal. 2—Such washing would increase the volatile content from 17.4 pct to about 20 pct, and in a byproduct oven this should give a coke yield of close to 80 pct with an ash content of coke under 20 pct. 3—A free swelling index of 5 appears low for a good coking coal, and below that of the coals from the Sabinas district, which show between 6 and 9. But washing of the coal should result in an improvement in this regard; in the United States coals from Utah with an index even lower than 5 have made a usable coke. 4—A coal with volatile as low as 17.4 in raw coal and 20 in washed coal would come close to being classed as a low-volatile rather than medium-volatile coal, and low-volatile coals are notorious for their high expansion properties. Several plants in the United States are making coke from straight medium-volatile coal of 26 to 28 volatile content, and one at Rosita,, Mexico, from coal of 25 volatile. But no plants to my knowledge are using coal as low as 20 volatile. Since the Rosita coal appears to be a borderline coal from the angle of its expansion properties the coking of one of the straight lower volatile must be approached with caution. 5—There are few coals possessing any degree of coking properties which cannot be used in coke production by careful attention to its preparation and blending. The fact that coals of other types are available in this same region make improvement through blending very possible. 6—There are other workable methods of reducing iron ore other than the conventional coke-blast-furnace method. These will not be discussed here but it is known that their use has been considered. The technicians of not only Mexico but also of the other Latin American countries are keenly aware of their natural resources and their national needs. This paper emphasizes the fact that the Mexican technicians are working on their problem and attempting to speed the day of self-sufficiency for their country. Salvatore Cortes-Obregon (author's reply)—I wish to thank Mr. Price for his kind remarks. The Mixtepec coal as shown in Table II has 30 pct ash and a free swelling index of 5, but when the same coal is washed to 15 pct ash it has a free swelling index of 8 to 9 and the volatiles increased from 17.4 to 20.7 pct. A satisfactory coke has been produced from blends made in the Mexican laboratory using at least 40 pct of the Mixtepec coking coals with the other Oaxaca non-coking coals. Koppers in Germany report good coke obtained from the Oaxaca coal with a blend of 80 pct Mixtepec coal. Consideration is being given the possibility of using methods other than the conventional blast furnace for the reduction of iron ore near the Oaxaca area; electric furnaces appear promising. The non-coking coals could be used to produce cheap electric energy and the coking coals to make metallurgical coke.

Jan 1, 1955

By Leo Dana

INTRODUCTION THE object of this paper is to discuss the factors and conditions that affect the observed values of the melting points of refractory materials and to describe practical methods for the determination of these points. While it appeared to be necessary to discuss some of the general properties of silicates and refractories, these subjects have been entered into only in so far as they relate to the melting point and its determination. Refractory materials such as fireclays, firebricks, and minerals generally, may be considered to be composed of compounds of metallic oxides, solid solutions of the oxides, the pure oxides, or mixtures of the three classes together with small amounts of a variety of chemical compounds. The oxides of silica and alumina occur most commonly in refractory materials; in combination with. these, oxides of the alkali earth, the alkali, the iron group, and the rare earth metals are frequently found.

Jan 9, 1919

By J. H. Swisher

The solubility of sulfur and rate of solution of sulfur in pure Lron were measured in H2S + H2 and H2S + H2 H2O gas mixtures. The solubility and diffusivity of sulfur at 1410°Care 0.13 pet S and 1.0 x 10-5 sq cm per sec, respectively. The solubility iS the same, but the rate of sulfurization is slower in the presence of H2O in the reacting gas. Under these conditions, the over-all rate is controlled jointly by a slow surface reaction and by solid-state diffusion; the mechanism for the surface reaction has not been identified. KNOWLEDGE of the behavior of sulfur in solid iron is desirable for the metallurgy of such products as free machining steel, where a high sulfur level is required, and inclusion-free high-strength steels, where the sulfur specifications are very low. The present investigation was undertaken to check previously reported values for sulfur solubility and diffusivity in 6 iron, and to study the poisoning effect of chemisorbed oxygen on sulfurization kinetics in H2-H2S-H2O gas mixtures. All of the experiments were performed at 1410°C. The thermodynamic behavior of sulfur in 6 iron was the subject of a paper by Rosenqvist and Dunicz.' The sulfur solubility at 1400" and 1500°C was determined by equilibrating pure iron specimens with H2-H2S gas mixtures. The maximum solubility of sulfur in 6 iron was alsc determined by Barloga, Bock, and parlee2 by reacting iron wires with sulfur in sealed capsules. In another investigation, the diffusion coefficient of sulfur in 6 iron at temperatures up to 1450°C was measured by Seibel.3 The method used was to measure sulfur concentration profiles in diffusion couples containing radioactive sulfur EXPERIMENTAL Apparatus. A vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction rube was used for the experiments. The hot zone in the furnace was approximately 2 in. long with a temperature variation of ±3oC. The hot zone temperature was automatically controlled to within ±2°C, and the test temperature was measured with a pt/Pt-10 pet Rh thermocouple before and after each experiment. Flow rates of the reacting gases were obtained using capillary flow meters. Materials. The source of H2S in the gas train was a premixed cylinder containing 5 pet H2S in H2. This mixture then was diluted with additional hydrogen and argon. In some experiments, water vapor was introduced by passing hydrogen and argon through a column containing 10 pet anhydrous oxalic acid and 90 pet oxalic acid dihydrate. The vapor pressure of water above this mixture is well-known.4 Argon was used as a diluent to minimize thermal segregation of H2S in the furnace5 and to reach higher H2O:H2 ratios than could be obtained in mixtures of H2 and H2S alone. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over P2O5. The specimen stock was made by melting and vacuum-carbon deoxidizing electrolytic "Plastiron" in a zirconia crucible. The principal impurities are listed in Table I. In some of the equilibrium experiments, six-pass zone-refined iron was used to minimize impurity side effects. This zone-refined iron had a total impurity level of about 25 ppm. Procedure. Specimens were annealed in hydrogen for a period of at least 2 hr at the beginning of each experiment. The specimens were held in the reacting gas for times varying between 10 min and 17 hr, and cooled to room temperature in a water-cooled stainless-steel block at the bottom of the furnace. The pH2S/pH2 ratios reported are those for gas equilibrium at 1410°C. Calculations based on available thermodynamic data8 showed that the only other gaseous8 species that formed in significant amounts in the furnace were S2 and S. Even when water vapor was introduced into the gas mixture, the concentrations of SO2, SO, and so forth, were negligible. The initial partial pressure of H2S was therefore corrected for its partial dissociation to S2 and S in determining the equi-

Jan 1, 1968

By W. A. Backofen, D. Lee

Titanium of commercial purity (RC-70) and two all-a (hcp) alloys (4Al-1/4O2 and 5Al-2.5Sn) were tested in sheet form under conditions of combined-stress loading. Plane-strain compression and plane -strain tension together with uniaxial compression and tension provided information for constructing the tension-tension and compression-compression quadvants of the plane-stress yield locus. Coordinate values were obtained from yield-strength measurements; the slope at each point was based on a plastic-strain ratio. The materials represented a wide range of plastic anisotropy, which was reflected in correspondingly varied departures of the yield locus from that for iso-tropy. The tension-tension and compression-compression quadrants were not identical. If the uniaxial yield strength is insensitive to direction and the sign of the applied stress, the Mises or perhaps the Tresca criterion is adequate for predicting the onset of yielding under combined-stress loading. The prediction is not so straightforward in plastically anisotropic material. Depending upon details of texture, combined-stress yielding resistance may be substantially different from that indicated by the usual criteria.' However. a continuum theory of yielding under such conditions is available for reasonably direct application.2,3 Whether or not it can be used successfully must, of course, depend upon how closely the conditions of the theory are satisfied in the material in question. In its present form the theory contains no provision for Bauschinger-type effects, nor does it allow for the consequences that might grow out of deformation by more than one mechanism, e.g., by slip and twinning.4 With those limitations, more importance must be attached to experimental information about the yield surface for anisotropic materials. Studies of the yield surface have generally been confined to states of plane stress (tension-tension and tension-compression) established in thin-wall tubes by externally applied forces and internal pressure. That approach would be entirely suitable for anisotropic materials if they were available in tube form or in sufficient bulk to be machined into test specimens. 6-9 It would not serve for the textured and anisotropic sheets of much current engineering interest, unless sheet could be formed into high-pressure tubing without structural change. Since there would seem to be little chance of the latter, practical alternatives are needed. One such alternative is the subject of this paper. It involves the use of a few selected but relatively simple uniaxial loading tests on sheet specimens. The underlying idea is presented here with some details relating to application and a few results bearing on how well it has worked. THE BASIS OF TESTING Conventional Measurements. Yielding for a general case of anisotropy is described by the plane-stress locus in Fig. 1. Reference directions in the sheet specimen are related to the stress coordinates as shown with the insert: x is the rolling direction, y the transverse direction, and z the through-thickness direction. The four reference-direction yield strengths (t, tension; c, compression), Xt, Xc, Yt, and Yc, are all different. Nine paths that can be followed in uniaxial loading experiments are identified. Paths 1, 2, 3, and 4 represent conventional tension and compression testing to establish Xt, Yt,.Xc, and Yc. Useful information also comes from the ratio of the transverse plastic-strain components associated with yielding and flow in conventional tension or compression. A condition to be satisfied in locus construction is that the plastic-strain vector be everywhere normal to the locus.10 The projection of the vector which would

Jan 1, 1967

By M. T. Simnad, C. E. Birchenall, M. H. Davis

The transport mechanisms previously proposed in wustite and hematite have been confirmed by movement of inert markers during the growth of these phases. By similar measurements the mechanism for magnetite has been determined. The rates of growth of multilayer scales on iron, magnetite and hematite on wustite, and hematite on magnetite have been measured. All rates are found to be diffusion controlled under the conditions of the experiments. MANY studies have been made of the rate of oxidation of iron in both the low temperature, film-forming region and the high temperature scaling range. The interpretation of the results has been greatly complicated by the formation of multi-layered scales containing the various phases of iron oxides. In most cases no attempt has been made to determine the composition of the scale and its dependence on time of oxidation in a quantitative manner. However, several recent studies'" have taken this variable into account. It is generally agreed that the growth of thick scales on iron follows a parabolic rate law for the increase of total thickness. In the thin film region agreement has been claimed with parabolic equations of various forms and with logarithmic equations. The discussion here will be concerned only with the formation of scales of considerable thickness, greater than several microns, although some of the conclusions may be applicable to thin films. A brief survey will be given of the solid phases of the iron-oxygen system, the stability of wiistite in bulk and in thin films, the relative densities of iron in the metal and oxides, and the kinetics of forma- tion of oxide scales on iron. New experimental results will be introduced at several points during the discussion, and an attempt will be made to formulate a mechanistic picture consistent with these observations. The experimental techniques are described in an appendix. Iron-Oxygen System Fig. la shows the iron-oxygen phase diagram. Wüstite ("FeO"): The lowest of the oxides has a NaCl type cubic lattice formed by close-packing of the relatively large oxide ions with the smaller iron ions arranged in the interstices. The ionic radius for 0' is about 1.3 A, while Fe++ has a radius of about 0.8A and Fe"' about 0.7A. Its range of existence on the phase diagram is very wide for an ionic material of this type and does not seem to include the stoi-chiometric composition FeO. These deviations appear to be well established as vacancies on iron lattice sites by the comparison of lattice parameters and densities for a series of compositions by Jette and Foote.4 The limits of the field are disputed, but the work which seems most reliable" indicates vacancies in from 5 pct to more than 12 pct of the iron sites. In order for the crystal to be electrically neutral, there must be electron holes which correspond to the formation of trivalent iron ions equal to twice the number of vacancies. Magnetite ("Fe³O4"): Considerable disagreement also exists in the literature about the stable range of the Fe³O4 field. Some diagrams show the Fe³O4 composition to be lower in oxygen than the formula indicates, but Schenck6 gives a diagram from the

Jan 1, 1952