By Leonid V. Azároff, H. N. Murty

In the course of investigating the soft X-ray absorption spectra of Ni-A1 alloys, Das and ~zfiroff' observed an anomalous brittleness in solid solutions containing 3 to 5 at. pct Al. The brittle alloys also had anomalously larger lattice constants' and the fine structure at the nickel K edge of an alloy containing 3.96 at. pct A1 unexpectedly resembled that of NiA1 more closely than that of a solid solution containing 5.51 at. pct Al. This led them to suggest the possibility that short-range ordering was produced during the homogenization anneal to which each specimen was subjected, similar to that observed in dilute solutions of vanadium and of chromium in nickel: as the principal cause of embrittlement. It was decided to repeat the above measurements on several alloys in this composition range in order to test the above hypothesis and to establish the effect of heat treatment on the alloys' properties. Three solid solutions in this range were prepared containing, respectively, 3.16, 4.00, and 4.54 at. pct Al, in addition to alloys containing 6 and 9 pct. All samples were annealed in vacuum at 1800°F for 100 hr and then furnace-cooled to room temperature, as in the original study. The lattice constants of these alloys are shown by open circles in Fig. 1 and can be seen to fit quite closely the curve established by the previously measured values, indicated by solid circles. (The experimental errors are of the order of the size of the circles, +o.oo~R.) The three alloys containing 3 to 5 at. pct A1 were found to be quite brittle, as previously reported. In order to test the possibility of ordering, these three solid solutions were again heated to 1800°F and, following a few hours at that temperature, were quenched directly to room temperature. All three alloys lost their brittleness. In order to verify the proposed ordering hypothesis, it was decided to subject each sample to several cycles of quenching and annealing (disordering and ordering). After some experimentation, it was established that reproducible results could be obtained by anneal-

Jan 1, 1968

By W. F. Chiao, R. B. Gordon

Tile sharp-yield point found in magnesium crystals in the solulion-treated and aged condition is studied by dislocation internal-friction experiments. The results show that the sharp yield is not file to the sudden release of pinned dislocations hut is movc likely due to the rapid multiplication of an initially small number of dislocations. Recovery or the dislocation internal friction after deformation is also studied. This yecovery results from the re-pinning of dislocations by a solute, presumably nitrogen, which moves with a relatively small activation energy. SHARP-yield points, when they occur, are a striking feature of the stress-strain curve generated during a tensile test. Although commonly associated with steel, sharp yielding has been found in a variety of metallic and nonmetallic crystalline materials. In particular, sharp-yield points have been found in zinc"' and cadmium3 containing nitrogen. With this background, Geiselman and Guy4 investigated the tensile properties of magnesium single crystals containing nitrogen to see if sharp yielding also occurs in this system. They found that sharp yields did indeed occur in solution-treated and aged specimens tested at elevated temperature but were not able to give conclusive proof that the sharp yield was caused by nitrogen, a yield drop being observed even in their purest crystals. Sharp-yield points have also been found in various polycrystalline magnesium alloys.7'8 In the study of the sharp-yield phenomenon it is desired to observe the behavior of dislocations in the earliest stages of the deformation process. Internal-friction experiments are useful for this purpose because dislocation damping is sensitive to the mobility of free-dislocation segments. At low strain amplitudes the damping, A, due to the the forced vibration of dislocation segments of average length L is ? =KAL4 [1] where A is the dislocation density and K, if the applied frequency is well below the resonant frequency of the dislocation segments? is a constant for the sample under observation.5 Dislocation damping, because of the fourth-power dependence on L, is particularly sensitive to the creation of free-dislocation segments during deformation. Since sharp yielding is associated with the sudden release of pinned-dislocation segments, marked changes in the dislocation damping are expected at the yield point.6 The use of the dislocation-damping observations to help elucidate the incompletely understood mechanism of yielding in magnesium is the primary objective of the experiments reported here. PROCEDURE Many investigations have shown that very marked and rapid changes occur in the dislocation damping of of a deformed material as soon as the straining is stopped.5 It was quite essential, then, for the purpose of this investigation, to make the damping measurements during the deformation of the samples. This can only be accomplished through the use of the ultrasonic-pulse method. In this method traveling sound-wave pulses are used and, in contrast to resonating-bar methods, only the sample ends are set in vibration. Thus, the sample can be gripped along its sides in the tensile-test machine without disturbing the damping measurements. In the pulse method, the decrease in the amplitude of a sound pulse is measured as it travels back and forth through the sample. If A is the amplitude after traversing a distance x and A. is the initial amplitude, A=Aoe-ax [2] and a is called the attenuation. It is commonly measured either in units of cm-I or as db per µ sec. The observed attenuation in a metal sample is due to a number of causes. These include scattering by grain boundaries and impurity particles, thermo-elastic damping, diffraction effects, stress-induced ordering of solute atoms, and dislocation damping. The total observed attenuation in a given sample usually cannot be resolved into these various components, but changes in a due solely to changes in dislocation damping can be accurately determined, provided the experiment is arranged so that all other sources of damping are held constant. It is desired to reduce the extraneous sources of attenuation to a minimum and for this reason the experiments are done on single crystals of high purity. Magnesium crystals offer the further advantage that, when properly oriented, only a single set of slip planes is active during deformation. Crystal Preparation. The method of sample preparation is similar to that of Geiselman and Guy.4 The starting material was high-purity, sublimed magnesium rod supplied by the Dow Chemical Co. Melting under Dow 310 flux was used to reduce the nitrogen content of the starting material: the fluxing was done under an argon atmosphere and the

Jan 1, 1965

By J. W. Snavely

WITH all the advantages of handling bulk materials by means of belt conveyor also go some problems, one of the most persistent being that of cleaning. When sticky materials are being carried; the build-up of material on the return idler rolls results in difficulty of belt training. Much attention has been given to the problem of cleaning conveyor belts, and a great variety of cleaning devices have been developed. Even the best involve troublesome maintenance, and none can completely remove the fine particles imbedded in the belt cover, which cause rapid wear of the return idler rolls, and at the same time, of the belt cover as well. One of the major rubber companies has been promoting a two-way belt system, in which the conveyor belt is given two successive 90" twists at each end to enable it to carry material in both directions simultaneously. For many years the flat belt transmission industry has installed quarter-turn and half-turn twists in countless numbers of instances. While quarter-turn and half-turn twists in transmission belts is a familiar application, the 180" twist apparently has never been previously attempted with a conveyor belt. About a year ago, two officials of the National Iron Co. of Duluth, Lester and Lewis Erickson, proposed twisting the return run of a conveyor belt on an installation that they were designing for one of the major iron ore producers. Since then the soundness of the idea has been demonstrated, both in theory and by practical test, with the result that the installation of two conveyor belts involving the twisting of the return run is now under way. These two installations are designed to have the return run of the conveyor belt twisted 180" as it leaves the snub pulley at the head drive. The clean underside of the belt is thus placed against the idlers on the return run as well as on the carrying run. Just before it enters the tail pulley, the belt will be twisted an additional 180°, restoring it to its normal position. Because this twisting of the return run of a conveyor belt is a radical departure from accepted practice, an elaborate and extensive test was conducted early in 1950 to demonstrate that this twisting of the return run could be done successfully, also to establish application data for accomplishing this twisting, and to determine if any special equipment would be required. In studying this concept of twisting the return run of a conveyor belt, a number of problems need to be solved, primarily the ones brought about by deliberately introducing an unequal distribution of stress across the conveyor belt and controlling that maldistribution of stress, while confining it to the return run portion. The tension conditions existing in the return run of a conveyor belt are clear to all designers. First, the return run carries the initial or slack side tension of the conveyor belt, the tension that must be supplied to the return run to provide proper frictional contact between the belt and the driving pulley so that the necessary power can be transmitted from the driving pulley to the belt without slippage. This slack side tension is supplied to the belt by means of takeups, either of the gravity type, which can be vertical or horizontal, or by means of the screw type. With inclined or declined belt conveyors the slope tension also must be considered, which is the tension imposed by the weight of the belt hanging from the top pulley. This slope tension frequently can furnish part or even all of the initial tension required. The maximum value of the slope tension will be at the top pulley, and it decreases in direct proportion to the length. In addition to the foregoing, it frequently is desirable to impose arbitrarily additional slack side tension to provide sufficient tension at the loading point at the tail, so that the belt will adequately support its load between the carrying idlers. Design Conditions for Twisting A number of design conditions exist, which must be satisfied successfully to accomplish the twisting of the return run without exceeding normal working limits in any portion of the conveyor belt. It is obvious that the belt edge, in its relation to the center of the belt, must stretch in making a twist, because as the twist is accomplished, the belt edge travels through a longer path than does the center of the belt. It is further obvious that if the edge of the belt is stretched, a redistribution of stress in the belt is required to allow this edge stretching. Moreover, this stress will be unequal across the width of the belt, having a maximum value at the edges, with a minimum value at the- center of the belt. With correct initial tension in the return run of a conveyor belt, the existing slack side tension will be unequally distributed when a twist is introduced. A condition then exists in which the edge stresses,

Jan 1, 1952

By B. E. Sundquist

The various methods based on solution models for obtaining free energies of mixing from miscibility-gap data have been applied to a number of binary-alloy systems. For nine of these systems there exist experimental thermodynamic data that permit a comparison of the results to experiment. It was found that the method of van der Toorn and Tiedema almost invariably leads to results that are physically unacceptable and that vary drastically with small changes in the miscibility-gap parameters. The subregular solution model is found in all cases, except the Al-Zn, Fe-Cr, and Cu-Pb systems, to exaggerate the free energy of mixing by 30 pct or more. The model developed by Lumsden is found to give results that are often in excellent agreement with experiment and which exaggerate the free energy of mixing by no more than 30 pct. These results and others give evidence that the Lumsden treatment of the effect of unequal atomic sizes and of imperfect configurational randomness due to deviations of AB bond energies from the mean of AA and BB bond energies is adequate for most systems. ANALYTIC expressions are frequently proposed for the dependence on composition of the activities of the components of a solution. Because the development of solution theory is incomplete, these expressions contain parameters which must be determined by experiment. The measurement of activities is often difficult and consequently such measurements are less readily available than are measurements of phase equilibria which, under certain conditions, can also be used to evaluate these parameters. For example, suppose it is known that two structurally dissimilar phases, each of known composition, in an n-com-ponent system are at equilibrium at a given temperature and pressure. n equations can be set up in terms of these parameters expressing the equality of the chemical potential of each component in the two phases. In addition, one can write the Gibbs-Duhem equation for each phase that also contains these parameters. Thus, if these n + 2 equations contain n + 2 parameters, these parameters can be determined (at the temperature in question) from the phase diagram alone. If the average number of parameters in each expression for the activity of a given component in a given phase is V then there will be 2nV parameters involved. Equating 2nV to n + 2 shows that, for n + 2, V = 1. If the temperature dependence of each parameter were to be expressed in some explicit form one could use equilibrium conditions at a number of temperatures to increase V. The situation is much improved when the two phases in equilibrium are structurally similar. It can then be assumed that, stably or metastably, two phases will become one at higher temperatures. Thus the number of parameters involved becomes nV instead of 2nV. Hence, V = 2 for n = 2 using only one temperature. (It is implied here that the activity expressions used are valid over the entire composition range.) In this investigation only the equilibrium of two structurally similar, two-component phases (miscibility-gap systems) will be considered. The various proposed solution models will be applied to a number of these systems and the results compared with available experimental results. All of the analytic expressions that have been proposed for the free energy of mixing of a two-component system are of the form where ?Gmix is the free energy of mixing per mole of solution, N1 and N2 are the mole fractions of components 1 and 2, respectively, and f(Ni, T) is some function of composition and temperature. In the "ideal" solution model f = 0. In the "regular" solution model f = a constant. Since these two models permit only a symmetric equilibrium diagram they will not be considered further here. The simplest model that permits a nonsymmetric miscibility envelope is the so-called "subregular" solution model proposed by Hardy.1 This model gives where the Ci(T) are functions of temperature only. The same expression for f is obtained from the "linear a function" model proposed by Darken and Gurry2 and applied to miscibility-gap systems by Wriedt.3 This model requires that the a function defined by be a linear function of composition (yi is the activity coefficient of component i). This model is not purely hypothetical for it has been found2 to hold true for a number of systems. It is readily shown3 that the f(Nl, T) obtained from this model is of the form given in Eq. [2]. It will be noted that the subregular solution model contains only two parameters and hence both of them can be determined at any desired temperature below the critical temperature, Tc, for a miscibility-gap systems in the manner described previously. At T, the two constants can be determined by equating the second and third derivatives of ?Cmix with composition to zero. Another two-parameter model was proposed by Lumsden4 who set

Jan 1, 1967

By Roscoe C. Clark

In a previous technical note' by Walter Rose, evidence is offered in support of the contention that "the possibility of describing oil recovery features in terms of capillary pressure phenomena has not been established entirely." It is not the purpose of this note to present further discussion of this possibility but rather to point out that the argument presented there does not appear to be generally valid. In the cited note' reference is made to the experiments of Welge2 wherein it was shown that when water was displaced by oil from a core the pressure in the water phase was less than in the oil phase but that when this oil was then produced by water drive the pressure in the water phase was greater than in the oil phase. Rose has concluded from these observations that conditions of static equilibrium did not obtain since the fluid saturations were such that phase discontinuities seemed unlikely. The argument from which this conclusion was drawn is based on the contention that "the pressure is always greatest in the non-wetting phase at each static interstitial interface of contact with the wetting phase." This premise appears to have been reached from a consideration of capillary phenomena in cylindrical tubes, although it may a1so hold for other types of pore geometry, hut as will be shown below it does not hold for all pore shapes and hence is not generally applicable. Since the pore structure of porous media such as reservoir rocks i- in general so complex as to defy exact description. it is undoubtedly of great value to establish a model in terms of pore shapes of known geometry, provided of course that the limitations of the model are recognized. That the limitations of the capillary. or cylindrical, tube model have not always been fully recognized will be evident from the following discussion of a pore of different shape hut one which may a. logically he considered a.; the capillary tube. The pore space to be considered is that shown in Fig. 1, which may be thought of as the "hole in a doughnut."* Consider the interface, A-B-A', between two immiscible fluids, P, and P2, which interface meets the solid alone a line, A-C.A'-C'. The interface A-B-A' is the surface of a spherical segmen† while the line of mutual contact be-

Jan 1, 1950

By Carl Wagner

AT elevated temperatures. most metals react with oxygen, sulphur, or halogen rather rapidly, although a coherent layer of the reaction product is formed and separates the two reactants from each other. The reaction proceeds, since one of the reactants or both dissolve and diffuse across the reaction product. In many cases the rate is diffusion-controlled as is indicated by the validity of the parabolic rate law of Tammann' and Pilling and Bed-worth. wott and Gurney' have suggested that diffusion processes also play an important part in the case of reduction reactions. This is confirmed by observations reported below. In general, however, the rate of reduction reactions is determined not exclusively by diffusion processes. Reduction of Silver Sulphide Above 179°C silver reacts with liquid sulphur very rapidly. Since the volume of silver sulphide is much greater than that of the equivalent amount of silver, a coherent layer of silver sulphide is formed in accordance with a rule established by Pilling and Bedworth.' According to Wagner','' silver ions and electrons migrate from the Ag-Ag,S interface across the silver sulphide layer to the Ag,S-S interface where the following chemical reaction takes place: 2 Ag +2 e + S Ag,S If silver sulphide is reduced by means of hydrogen, the equivalent volume of the reaction product, silver, is less than that of the initial substance. Accordingly, no coherent layer of silver is formed. Instead, fine filaments of silver grow from the silver sulphide surface into the ambient gas. This phenomenon has been investigated by many authors, especially by Kohlschiitter," who has also reviewed previous literature. Kohlschiitter has interpreted the observed phenomena by migration of "silver" dissolved in silver sulphide. According to Wagner,' silver ions and electrons are the migrating particles. The sequence of consecutive steps involved in the reduction of silver sulphide is shown in Fig. 1. Every- where at the silver sulphide surface, hydrogen reacts with sulphur so that excess silver ions and electrons are formed, which migrate at random until they are captured by a nucleus of metallic silver. If such a nucleus lies on the surface and material is furnished only from the base, the original nucleus is pushed outward and thus a filament grows. Removal of sulphur and formation of metallic silver may also take place at different points when silver sulphide is reduced by copper. The reaction is usually formulated as: AgL,S + 2 Cu = Cu.S + 2 Ag but the actual reaction products are silver and a solid solution of the two sulphides. Primarily, excess silver and electrons dissolved in silver sulphide are formed. After a certain degree of supersaturation has been reached, nuclei of metallic silver may form. If, however, a silver foil is in contact with the silver-sulphide phase, as is shown in Fig. 2, silver ions and electrons will migrate to the Ag,S-Ag interface where they are captured. To confirm this scheme, a composite sample, with the geometry shown in Fig. 2, was made by pressing silver sulphide tablets 0.6 cm in diam and 0.4 cm high together with a copper cylinder and a silver foil in crucibles of iron, which does not react appreciably with silver sulphide at 400°C. After heating for 3 to 7 hr at 400°C. the specimens were cut normal to the phase boundaries. It was found that the thickness of the silver foil had increased from 0.01 cm as initial value to a maximum value of 0.06 cm. In the interior of the silver sulphide tablets only traces of metallic silver were observed. These observations show clearly that silver ions and electrons may migrate over distances of several millimeters before they form metallic silver. Reduction of Cuprous Sulphide by Iron The behavior of cuprous sulphide is very similar to that of silver sulphide, since the lattices of the high temperature modifications are identical, but in Cu.S there is a variable deficit rather than an excess of metal. To investigate the displacement of copper by iron, cuprous sulphide powder covered by a copper foil was pressed in iron crucibles and heated up to 800 °C for 3 to 7 hr. The thickness of the copper foil increased from an initial value of 0.005 cm to a nlaximum value of 0.029 cm. In the interior of the

Jan 1, 1953

By H. Foster Bain

Jan 1, 1910

By Eric Jette

THE alloys of gold and iron were investigated in 1907 by Isaac and Tammann,1 who determined the thermal diagram for the entire system by thermal analysis and microscopic examination. They also reviewed the previous literature. Since that time the present authors have been able to find only two additional references. Guertler and Schulze2 examined the electrical resistance of iron alloys containing up to 40 per cent by weight of gold between 0° and 200° C.; the alloys were in the form of wires. The main result of this work was to confirm the solid solubility limit found by Isaac and Tammann; namely, about 20 per cent Au. More recently, Shih3 has examined the magnetic properties of gold alloys containing up to 10 weight per cent iron and particularly the range below 5 per cent. The alloys in the lower range were found to be paramagnetic; the 10 per cent alloy was ferromagnetic. The present investigation was undertaken to determine the solid solubility limits at various temperatures, particularly below the a-y transformation point of iron, since these solubilities are of some impor-tance in connection with the working of the alloys in the manufacture of certain "grey" and "blue" golds.

Jan 1, 1934

By Oliver Bowles

PRICES of quartz sold in the United States in 1938 ranged from $1.15 to $36,000 a ton. This startling variation was due simply to the differences between glass sand and rock - crystal, materials that are virtually the same in composition. It illustrates the complexities in qualities, uses, and values of industrial minerals. It is generally stated that mineral deposits are exhaustible resources which can never be replaced when depleted. This statement is no longer true with respect to certain industrial minerals now recovered in increasing quantities from that most inexhaustible of all sources of supply, the ocean. Salt has long been obtained from sea water, particularly on the Pacific Coast, and reference was made a year ago to the large bromine recovery plant at Wilmington, N. C. Now the Westvaco Chlorine Products Corp. is operating a large plant at Newark, Calif., having a capacity sufficient to recover daily from the ocean raw materials that will produce 60 tons of various magnesium products. Lime is used to precipitate the magnesia from salt-water bittern. The products are chiefly magnesium carbonate for chemical uses, periclase and other refractories, and oxychloride cement for flooring.

Jan 1, 1939

By A. L. Galpin

INTRODUCTION For many tailings ponds, particularly those having substantial watershed areas, the control of pond water levels will be a major factor influencing the operation of the pond and the design and construction of the dam retaining the pond. This paper summarizes the basic factors affecting the control of water in tailings ponds, methods of water control, and methods of estimating the variables involved. The influences that pond water levels can have on the design, construction, and stability of tailings dams are explained in order to emphasize the importance of water control in the overall planning of mine tailings disposal systems. Two examples of pond water control planning conclude the paper. BASIC FACTORS The principal factors influencing the control of water in tailings ponds are illustrated on Fig. 1. Fig. 1 (a) shows the general disposition of the tailings solids and water in the pond; the solids settle from the slurry to form "slimes", deposits sloping down into the pond from the points of discharge; these slimes hold volumes of water in the voids between solid particles; water in excess of this "retained" water forms a pool of "free" water laying over the slimes deposits. In some cases, tailings solids (and water) go to the tailings dam for its construction. Fig. 1 (b) indicates those ways additional to tailings disposal in which the pond gains or loses water. These include surface and sub-surface runoff from the pond watershed, water reclaimed from the pond for ore processing, evaporation, and seepage. Seepage losses sometimes include water draining from tailings sand placed in the dam, but a portion of the total seepage flow is often collected and returned to the pond in order to avoid downstream pollution and to recover water for re-use. PRINCIPAL REQUIREMENTS In relation to the control of water in a tailings pond, the first requirement is usually to maintain a pool sufficiently large to ensure adequate clarification of the free water prior to its reclaim for use in the mill, or its discharge from the pond.

Jan 1, 1972

By John Griffen

This paper records over twenty years' experience with the use of the Rheolaveur system in the United States, showing its ability to meet changing conditions caused by the dirtier mine output of present-day mechanical mining methods. Data are given on size ranges handled, number and capacity of units installed, maintenance experience, and operating results on two-product and three-product separations. IT is not the purpose of this paper to discuss the principles employed in the Rheolaveur system of fine-coal cleaning as these have been fully covered in the technical literature of the Institute."2 Rather, our purpose will be to record the highlights of over 20 years' experience in the United States with Rheolaveur fine-coal launders, which will indicate their capabilities and costs of cleaning and their adaptability to meet the changing conditions caused by present-day mechanical mining methods. Rheolaveur fine-coal launders are used in the United States to treat a wide variety of size ranges of fine coal, the coarsest being 1/2 in. to 0 and the finest about 1/8 in. to 0. In Europe feeds as coarse as 5/8 in. and as small as 1/2 mm (28-mesh) to 0 are being cleaned. The size ranges usually handled in this country are 3/8 to 1/4-in. round to 0. Thirty five units with a combined hourly feed capacity of 3200 tph have been installed in the United States. Individual units are cleaning as little as 25 tph, while others are cleaning as much as 200 tph. Rheolaveur fine-coal launders offer cleaning units of high capacity and are outstanding in requiring a minimum of building space per ton of input. Experience has shown that maintenance costs are low. Several installations were made in the Pittsburgh district from 1928 to 1930, and since that time operation has been largely two shifts per day. Minor repairs to liner plates and Rheo boxes have been required during the intervening years, but no major replacement of launders was required until 1947 and 1948. At one of these plants, launders operated for 17 years before they were replaced and during that period over 26,000,000 tons of —5/16-in. coal were cleaned. The effect of the much dirtier raw coal produced by mechanical loading of the Pittsburgh seam is shown by the following tests. The data in table I summarize the performance of a Rheo fine-coal unit when cleaning hand-loaded raw coal. The —4-in. raw coal fed to the cleaning plant analyzed only 8.16 pct ash and 1.31 pct sulphur and contained 4.6 pct sink, 1.55 sp gr. Two years later, in 1945, mechanically-loaded coal from the same mine was cleaned in the same plant. The feed, —4 in., then analyzed 20.10 pct ash and 1.53 pct sulphur and contained 20.2 pct sink, 1.55 sp gr. The performance of the Rheo fine-coal unit when cleaning this coal is given in table 11. It will be noted that the +48-mesh coal is cleaned almost as thoroughly as in table I. The large amount of high-ash slimes produced from the dirtier feed are responsible for the higher ash of —--48-mesh washed coal in table 11. In this plant the Rheo fine-coal unit did not get the full load of refuse resulting from mechanical

Jan 1, 1951

By John Griffen

This paper records over twenty years' experience with the use of the Rheolaveur system in the United States, showing its ability to meet changing conditions caused by the dirtier mine output of present-day mechanical mining methods. Data are given on size ranges handled, number and capacity of units installed, maintenance experience, and operating results on two-product and three-product separations. IT is not the purpose of this paper to discuss the principles employed in the Rheolaveur system of fine-coal cleaning as these have been fully covered in the technical literature of the Institute."2 Rather, our purpose will be to record the highlights of over 20 years' experience in the United States with Rheolaveur fine-coal launders, which will indicate their capabilities and costs of cleaning and their adaptability to meet the changing conditions caused by present-day mechanical mining methods. Rheolaveur fine-coal launders are used in the United States to treat a wide variety of size ranges of fine coal, the coarsest being 1/2 in. to 0 and the finest about 1/8 in. to 0. In Europe feeds as coarse as 5/8 in. and as small as 1/2 mm (28-mesh) to 0 are being cleaned. The size ranges usually handled in this country are 3/8 to 1/4-in. round to 0. Thirty five units with a combined hourly feed capacity of 3200 tph have been installed in the United States. Individual units are cleaning as little as 25 tph, while others are cleaning as much as 200 tph. Rheolaveur fine-coal launders offer cleaning units of high capacity and are outstanding in requiring a minimum of building space per ton of input. Experience has shown that maintenance costs are low. Several installations were made in the Pittsburgh district from 1928 to 1930, and since that time operation has been largely two shifts per day. Minor repairs to liner plates and Rheo boxes have been required during the intervening years, but no major replacement of launders was required until 1947 and 1948. At one of these plants, launders operated for 17 years before they were replaced and during that period over 26,000,000 tons of —5/16-in. coal were cleaned. The effect of the much dirtier raw coal produced by mechanical loading of the Pittsburgh seam is shown by the following tests. The data in table I summarize the performance of a Rheo fine-coal unit when cleaning hand-loaded raw coal. The —4-in. raw coal fed to the cleaning plant analyzed only 8.16 pct ash and 1.31 pct sulphur and contained 4.6 pct sink, 1.55 sp gr. Two years later, in 1945, mechanically-loaded coal from the same mine was cleaned in the same plant. The feed, —4 in., then analyzed 20.10 pct ash and 1.53 pct sulphur and contained 20.2 pct sink, 1.55 sp gr. The performance of the Rheo fine-coal unit when cleaning this coal is given in table 11. It will be noted that the +48-mesh coal is cleaned almost as thoroughly as in table I. The large amount of high-ash slimes produced from the dirtier feed are responsible for the higher ash of —--48-mesh washed coal in table 11. In this plant the Rheo fine-coal unit did not get the full load of refuse resulting from mechanical

Jan 1, 1951

By Edward H. Robie

NEVER before have the annual company reports in the mineral industry field exhibited the typo-graphical art so abundantly as does the current crop. Time was when most company reports made a drab appearance and dry reading, mostly confined to financial data and text that gave little information to the public or technical men. Now, the dollar statistics assume less importance. Considerable information is given on what is going on at the company's plants, new equipment being installed, new methods, properties under development, ore reserves and grades, and similar information of interest to professional men working in the field. We have one suggestion for further improvement: The names of the officers and directors of the company are always given, but only a few companies give the names of the principal operating officials. We think, in the case of a mine for example, that the name of the general manager, his assistant, the mine and mill superintendents, and any other top operating officials who have been largely responsible for the success of operations, are worthy of mention. The reports are now widely read and this recognition is due them. Conspicuous among the annual reports that we happen to have seen, in point of typographical attractiveness, are that of the Texas Co., celebrating its fiftieth anniversary with a gold-plated cover and gold printing inside; and that of Noranda Mines Ltd., with a red and black cover that would attract attention anywhere. Comment on economics, taxes, and labor give an excellent picture of what our industry is facing. Consider the following, from the report of the Union Oil Co. of California:

Jan 1, 1952

DAVID THOMAS 1871 R. W. RAYMOND 1872-1874 A. L. HOLLEY 1875 ABRAM S. HEWITT 1876 T. STERRY HUNT 1877 ECKLEY B. COXE 1878-1879 WILLIAM P. SHINN 1880 WILLIAM METCALF 1881 RICHARD P. ROTHWELL 1852 ROBERT W. HUNT 1883 JAMES C. BAYLES 1884-1855 ROBERT H. RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B. POTTER 1888 RICHARD PEARCE 1889 ABRAM S. HEWITT 1890 JOHN BIRKINBINE 1891-1892 H. D4. HOWE 1893 JOHN FRITZ 1894 J. D. WEEKS 1895 E. O. SPILSBURY 1896 THOMAS M. DROWN 1897 CHARLES KIRCHHOFF 1898

Jan 1, 1941

DAVID THOMAS 1871 R. W. RAYMOND 1872-1874 A. L. HOLLEY 1875 ABRAM S. HEWITT 1876 T. STERRY HUNT 1877 ECKLEY B. COXE 1878-1879 WILLIAM P. SHINN 1880 WILLIAM METCALF 1881 RICHARD P. ROTHWELL 1852 ROBERT W. HUNT 1883 JAMES C. BAYLES 1884-1855 ROBERT H. RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B. POTTER 1888 RICHARD PEARCE 1889 ABRAM S. HEWITT 1890 JOHN BIRKINBINE 1891-1892 H. D4. HOWE 1893 JOHN FRITZ 1894 J. D. WEEKS 1895 E. O. SPILSBURY 1896 THOMAS M. DROWN 1897 CHARLES KIRCHHOFF 1898

Jan 1, 1942

DAVID THOMAS 1871 R. W. RAYMOND 1872-1874 A. L. HOLLEY 1875 ABRAM S. HEWITT 1876 T. STERRY HUNT 1877 ECKLEY B. COXE 1878-1879 WILLIAM P. SHINN 1880 WILLIAM METCALF 1881 RICHARD P. ROTHWELL 1852 ROBERT W. HUNT 1883 JAMES C. BAYLES 1884-1855 ROBERT H. RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B. POTTER 1888 RICHARD PEARCE 1889 ABRAM S. HEWITT 1890 JOHN BIRKINBINE 1891-1892 H. D4. HOWE 1893 JOHN FRITZ 1894 J. D. WEEKS 1895 E. O. SPILSBURY 1896 THOMAS M. DROWN 1897 CHARLES KIRCHHOFF 1898

Jan 1, 1943

DAVID THOMAS 1871 R. W. RAYMOND 1872-1874 A. L. HOLLEY 1875 ABRAM S. HEWITT 1876 T. STERRY HUNT 1877 ECKLEY B. COXE 1878-1879 WILLIAM P. SHINN 1880 WILLIAM METCALF 1881 RICHARD P. ROTHWELL 1852 ROBERT W. HUNT 1883 JAMES C. BAYLES 1884-1855 ROBERT H. RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B. POTTER 1888 RICHARD PEARCE 1889 ABRAM S. HEWITT 1890 JOHN BIRKINBINE 1891-1892 H. D4. HOWE 1893 JOHN FRITZ 1894 J. D. WEEKS 1895 E. O. SPILSBURY 1896 THOMAS M. DROWN 1897 CHARLES KIRCHHOFF 1898

Jan 1, 1944

Bailey, Lewis Newton, Master Engineer, Senior Grade, 4th Regiment, U. S. Engineers, Headquarters Company, died of pneumonia at Camp Merritt, N. J., on April 30, 1.918. Baird, Louis, Lieut., Royal Field Artillery, British Army, died on the battlefield in 1915. Cobeldick, William Morley, Royal Engineers, died from gas poisoning on October 7, 1915. Dougall, Ralph, killed in action Evans, Alfred Winter, Lieut.-Col., New Zealand_ Rifle Brigade, D. S. 0., D. C. M., killed in action on October 12, 1917. Hague, William, 1st Lieut., Engineer Officers' Reserve Corps, died in active service.

Jan 8, 1918

By S. A. Falconer

D. A. Dahlstrom—Mr. Falconer has done an admirable job of proving the adaptability of the cyclone to the beneficiation of a very difficult size range in the preparation of coal. The addition of the cyclone to other coarser size methods makes it economically feasible for the coal operator to rigorously control his marketed products at a high and uniform quality level down to the 48 and 100-mesh size. Furthermore, it should be pointed out that by utilizing the cyclone as a deslimer or classifier the —3 200-mesh fraction, usually containing large percentages of undesirable material, can also be quickly and cheaply removed from the clean coal. Advantages of such a step are several: (1) Reduction of ash content, especially where clays and slimes are serious. (2) lower moisture content of the final coal. (3) easier mechanical and thermal de-watering of the fine coal due to higher cake and bed permeabilities. The author has indicated that adjustable control means should be installed on the cyclone operating on a heavy-media slurry. This also holds true for the cyclone acting as classifier, deslimer or preliminary dewatering agent and is worthy of special emphasis. Such controls, while not necessarily automatic, must be simple, rapidly adjustable, and require a minimum of attention. Three methods available to the operator are (1) throttling valve on the feed line, (2) back pressure valve on the overflow, and (3) adjustable diameter underflow nozzles. The first two, while fulfilling the specifications, suffer the disadvantage of restricting capacity if severe throttling is necessary. The third method has little effect on capacity and easily maintains an underflow of correct moisture content. Several designs are possible, but two find the widest application. The first was developed by Robert Piros of The Truax-Traer Coal Co. and uses a simple casting containing two holders for underflow nozzles which can be rotated about an axis parallel to the cyclone centerline. These holders retain the underflow nozzle flush with the conical section walls. When a change in nozzle diameter is required, the new size is placed in the spare holder and rotated into place. A second design utilizes a soft rubber cylindrical tube which is compressed or released from three sides, causing the inner diameter of the tube to decrease or increase. This is achieved by using a machine-threaded,

Jan 1, 1951

By S. A. Falconer

D. A. Dahlstrom—Mr. Falconer has done an admirable job of proving the adaptability of the cyclone to the beneficiation of a very difficult size range in the preparation of coal. The addition of the cyclone to other coarser size methods makes it economically feasible for the coal operator to rigorously control his marketed products at a high and uniform quality level down to the 48 and 100-mesh size. Furthermore, it should be pointed out that by utilizing the cyclone as a deslimer or classifier the —3 200-mesh fraction, usually containing large percentages of undesirable material, can also be quickly and cheaply removed from the clean coal. Advantages of such a step are several: (1) Reduction of ash content, especially where clays and slimes are serious. (2) lower moisture content of the final coal. (3) easier mechanical and thermal de-watering of the fine coal due to higher cake and bed permeabilities. The author has indicated that adjustable control means should be installed on the cyclone operating on a heavy-media slurry. This also holds true for the cyclone acting as classifier, deslimer or preliminary dewatering agent and is worthy of special emphasis. Such controls, while not necessarily automatic, must be simple, rapidly adjustable, and require a minimum of attention. Three methods available to the operator are (1) throttling valve on the feed line, (2) back pressure valve on the overflow, and (3) adjustable diameter underflow nozzles. The first two, while fulfilling the specifications, suffer the disadvantage of restricting capacity if severe throttling is necessary. The third method has little effect on capacity and easily maintains an underflow of correct moisture content. Several designs are possible, but two find the widest application. The first was developed by Robert Piros of The Truax-Traer Coal Co. and uses a simple casting containing two holders for underflow nozzles which can be rotated about an axis parallel to the cyclone centerline. These holders retain the underflow nozzle flush with the conical section walls. When a change in nozzle diameter is required, the new size is placed in the spare holder and rotated into place. A second design utilizes a soft rubber cylindrical tube which is compressed or released from three sides, causing the inner diameter of the tube to decrease or increase. This is achieved by using a machine-threaded,

Jan 1, 1951