By G. R. Gohn, S. M. Arnold

The results of stress-corrosion tests upon several non-ferrous sheet metals are presented in this paper. The metals include tough pitch copper, five binary brasses, two leaded brasses, one copper-silicon alloy, two tin bronzes, and two nickel-silver alloys. The tests indicate that for most of these sheet metals, externally applied bending stresses below the yield point (0.01 per cent offset) do not result in stress-corrosion cracking as determined by the A.S.T.M. Tentative Method of Mercurous Nitrate Test for Copper and Copper Alloys (B 154-41T).~ Only in the cases of low brass, high brass and medium leaded brass, all cold-worked 4 B & S numbers hard, was any corrosion cracking observed below the yield strength, and in all cases such failures occurred at stresses above the proportional limit for these materials. However, when some of the same materials which showed no evidence of stress-corrosion cracking at stresses below the yield strength, are stressed beyond the yield point, stress- corrosion cracking is quite apt to occur. Since experience has shown that some of these materials, particularly the brasses, are susceptible to stress-corrosion cracking under service conditions, these tests would indicate that, besides externally applied stress and corrosion, plastic deformation in addition to that resulting from the original cold working of the material is also required to produce conditions conducive to stress- corrosion cracking.

Jan 1, 1945

By T. Gleason

Problems involved in applying wet scrubbers to gas cleaning coal dust from thermal dryers are reviewed. Careful consideration of all the elements going into a modem coal preparation plant is required in view of the increasing difficulty of applying suitable gas cleaning equipment. This problem arises not only from the presence of finer coals to be handled, but also from the pressures applied by both the general population and the plant operators to improve the standard of gas cleaning performance. The Peabody scrubber is presented by the author as a machine designed to help improve this cleaning operation. Wet scrubbing of fine coal from thermal dryers poses a number of problems in adapting the gas cleaning equipment to the fine particulate matter. Among them are: 1) Dust in gases leaving the thermal dryer cyclones is often extremely fine with high percentages of total dust loading less than 1p in size. 2) Flue gas entering the scrubber is corrosive since the coal fired in the thermal dryer furnace is in the range of 0.7% by weight sulfur or higher. Therefore, comparatively high cost stainless steel alloys or corrosion resistant linings are required for a satisfactory service life. 3) Requirements for residual coal loadings leaving the gas scrubber are continually being lowered, while modern coal preparation operation is imposing heavier burdens on the collection system through introduction into the thermal dryer system of very fine coal previously not recovered. The advent of flotation systems in increasing numbers is typical of this trend. 4) Installation of a scrubbing system on thermal dryers is made primarily to reduce air pollution and product recovery value is of little or no value. Therefore, the operating costs of gas pressure drop and water requirements must be held to a minimum. We have, then, the basic situation which calls for comparatively high cost stainless steel alloy wet scrubbers, which must be highly effective in removing coal fines particularly in the 0 to 5-p size range. Further, the standards of scrubber performance are continually being raised towards the level where gas discharged from the scrubbers must be essentially free of any coloration due to residual dust. In view of the highly refractive nature of fine coal dust, residual loadings of 0.01 grains per cu ft or less are required to provide a color free discharge gas. In the present specifications under consideration a residual coal loading of 0.05 grains per cu ft would be considered color free, since the discharge gases are saturated in the range of 150°F. The steam plume acts as a masking agent at the point of discharge, and upon dissipation of the 150° saturated vapor stream, the effluent gas stream could be essentially color free. The specification under consideration calls for residual solids loading of 0.05 or less grains per cu ft, given a coal size distribution shown in the basic data in Table I. It is noted that the dust laden coal stream has a size distribution by weight of 33% in the 2 to 5-p size range and 55% in the 0 to 2-p size range. The particle size distribution given in the specifications does not detail the percent by weight less than 1-p in size, and more important, the size distri-

Jan 1, 1963

By W. R. Hibbard

IN ref. 1, on the basis of tension and torsion experiments with single crystals of a brass, the values given in Table I were obtained for elastic coefficients. It was pointed out by Zener that the values for the 71.2 pct Cu were not satisfactory, since they resulted in a negative value for the bulk modulus, namely —4.17X1012 sq cm per dyne. In reevaluating the data of this investigation, it was determined that the reason for this negative bulk modulus lay in the extrapolation of the reciprocal Young's modulus to the zero value of the orientation function shown in Fig. 5 of ref. 1. This extrapolation was reevaluated by the method of least squares (50 pct probability) and a new value of the coefficient S,, was determined as 18.9220.42X 10M sq cm per dyne in lieu of the value originally reported of 18.82x10 sq cm per dyne. This new value of S, leads to a new value of S, of — 9.43 X101" sq cm per dyne. The values of the other coefficients are unchanged. results. This value compares with the value of 12.3X10 sq cm per dyne reported by Schmid and Boas? The new results are summarized in Table 11. These results follow similar qualitative trends, previously published,' relative to the effect of zinc content. However, the derived values of C11, C,, C,, and K are so sensitive to the uncertainty in the first decimal place of the S, values that they are probably not useful. This uncertainty must also apply to the previous results of Masima and Sachs," who obtained S, values from a similar extrapolation drawn wholly above their data points. Acknowledgments Advice and assistance on the statistical methods were obtained from R. W. Guard. The calculations were carried out by Miss E. Saacke.

Jan 1, 1958

By W. F. Boericke

AT Kellogg, Idaho, J. Fred Johnson is driving the 5000.-ft Hooper Tunnel under contract for the Bunker Hill & Sullivan Mining Co. This was visited by a group of engineers during the recent meeting of the A. I. M. E. at Spokane, who were impressed with several features of the work. An excellent record of advance is being made by the contractor, over 47 ft. being driven in 3 days during October, and 223 ft. advanced in 29 shifts. The size of the tunnel is 8 by 9 ft. The ground is Wallace quartzite and, save for the first hundred feet, stands well and does not require timbering. The grade is held uniformly at 0.5 per cent. Two shifts are employed, with two sets of machine men to the shift. Ingersoll-Rand S-70 drills are used. each machine being set up independently in the heading; 26-30 holes are drilled to the round; using 1 1/4: in. round hollow drill steel. A 7-hole cut is required, and these holes are blasted simultaneously, using 60 per cent gelatine, 12 sticks to the hole. Instantaneous and fire delays of electric detonators are used for the complete round. A feature of the drilling is the use of long carriage drills, necessitating fewer changes of steel, and more time spent on drilling, with less time consumed taking steel back and forth from the face. Of course, this means better blacksmithing so that the drill steel shall stand up for the added footage.

Jan 1, 1930

While the production of this state has not realized the early hopes that this coal would replace eastern coal on the Pacific Coast, it has been steady though small. Nearly all of the tonnages given are from Goodyear's, The Coal Mines of the Western Coast of the U. s., a carefully com- piled and accurate account of the development of the industry along the Pacific. [ ]

Jan 1, 1942

By GEORGE L. CHRISTIAN

T HE Tonopah Extension assay office is a two- story, concrete structure on a solid foundation of andesite, situated about 100 yd. from the company's mill, so that it will not be affected by the stamps or the tube-mills; also it will not be affected by under- ground blasting. On the second floor are the mine superintendent's office and drafting and blueprint rooms. On the ground floor are the assayer's office,' mixing room, furnace room, crusher room, chemical laboratory, parting room, store room, and change and shower room for the mine superintendent, assayers, and engineers. The crusher room is outside of the main building, and has four concrete walls, thus eliminating the jar of the crusher; it is so situated that the least possible amount of dust spreads through the main building. An 8 by 10-in. jaw crusher, which crushes to ¼ in., was made by a local foundry. Attached to the top is a small galvanized-iron hopper covered with a ¼ in. screen, on to which the sample is dumped. The fines-pass through the screen into the hopper, while the oversize is dumped into the crusher. The crushed sample and fines from the screen drop down to a set .of splits suspended from an iron rod below the crusher jaws. The small sample is caught below in a small pulp pan. The rejects drop from the splits through a 2-in. pipe on to a bucket conveyor, which dumps into a galvanized-iron hopper in an upper corner of the room. The rejects drop through a 2-in. pipe to a reject bin outside the build- ing. This bin is constructed high enough for a truck to be loaded from it by means of a chute door on the side.

Jan 1, 1921

By J. J. Thomas

THIS investigation was undertaken to determine, if possible, the relation between static and dynamic tensile tests as measured by the work required to break test specimens slowly, in a tensile testing machine, and rapidly, by means of a falling weight. It was hoped that the investigation would throw some light on the role played by ductility under different rates of application of load. FIG. 1.-STRESS-STRAIN DIAGRAM. In problems of design, it is usually assumed that the moduli of elasticity of all steels are equal; viz., about 30,000,000. The stress-strain diagram within the elastic limit is a straight line, as shown in Fig. 1, where OA is the curve of a hard steel and OB that of a soft steel. If the modulus of elasticity is constant, as assumed, the slope of the line OC

Jan 2, 1921

By A. C. JR. Boyle

I. INTRODUCTION THE geological field work of the Bully Hill district, upon which this paper is based, was begun July 1, 1908, and covered a period of three months. The time was found too short for a complete report and the district was again visited in the early part of July, 1912,. from which time detailed study of the locality continued until September of the same year. This paper is the result of observations made in the mines in the immediate vicinity of Winthrop, Shasta county, Cal., during these two periods of study. The preparation of this report has been greatly facilitated by various courtesies rendered the writer by D. M. Riordan, President of the Bully Hill Copper Mining & Smelting Co., and by John B. Keating and Herbert R. Hanley, managing officers actively in charge at the mines. The elaboration and further study of the notes and collections were carried on in the laboratories of the Departments of Geology and Mining at Columbia University, and the writer takes pleasure also at this point in expressing his acknowledgments to Profs. James F. Kemp, A. W. Grabau, Charles P. Berkey, and William Campbell, for advice and assistance. In order that one may appreciate at first reading the significance of some of the details which follow, and for the sake of clearness, a brief outline of the geological relationships is here given, together with certain conclusions which have been reached regarding the genesis. of the ores and the gypsum masses. In the Bully Hill mining district an associated series of Triassic lavas and tuffs, chiefly andesites, is preceded as well as followed by sediments. The entire system is tilted so that the original bedding planes dip in general to the southeast. The surrounding region has been greatly disturbed, and in the immediate vicinity of the mines close folding of the later sediments and extreme shearing of the igneous rocks locally is a striking feature. Into the nearly vertical shear zones have been intruded post-Triassic dikes of various rock types in the following order: alaskite-porphyry and andesite-porphyry. Outside the area under consideration diorite dikes are known, but they will not receive attention further than to note that' they, probably, represent a differentiation product of the same magma from which the other two dikes came. In this connection all the dikes have an important bearing on the origin of the ores and of the gypsum found in the mines.

Jan 1, 1914

By H. A. Schwartz, W. Kenneth Bock

IN this paper it is shown that when the tensile strength of a given steel in various states of heat-treatment is plotted against its elongation, a straight line results. The equation of this straight line can be computed with considerable accuracy from its chemical composition. The appropriate equations are given. The logarithm of the slope of the tensile-strength locus is shown to be proportional to the cumulative effect of the total alloy addition and the position of the line to be directly proportional to the cumulative effect of the alloy content. It is further pointed out that heat-treatment is more effective than composition in determining yield ratio. The latter enters mainly by its effect on hardenability, which is briefly discussed. Reduction of area and Brinell number are given some incidental attention. The data are applicable only to steels that have been normalized and/or quenched. The steels, if normalized, may or may not have been tempered. If quenched they must have been tempered at or above 400°C. (750°F.).

Jan 1, 1944

By ALBERT F. J. BOARDEAUX

(Canal Zone Meeting, November. 191(j.) I. GENERAL INTRODUCTION. 1. Historical. ALLUVIAL gold was first discovered in Guiana in 1852, in the sands of the Arataye river; by Paulino, a Brazilian convict. During the following years, gold was found also in the rivers Orapu, Cirubé, etc. In 1873 the famous placers of the Sinnamary system were opened: Saint-Elie, Dieu-Merci, Adieu-Tat, and Couriége. This group of mines has produced nearly $10,000,000, according to official records, not including the gold that escaped the taxes. The discoverer was a mulatto named Vitalo. Except in a few rich spots, the gold was rather evenly distributed along the creeks. In one instance, gold was found in the red dirt from the slope of a hill, which, after transport to the creek, gave an amount of 150 kilograms. The placers of the Mana system, Enfin, Elysée, Pas-Trop-Tot, date from 1878, and their production has been about $5,000,000. In 1888, the Awa placers, along the boundary between the French and Dutch Guianas, on the Maroni and its tributaries, were discovered. They have yielded $12,000,000. The only industrial company,, the Dutch Guiana French Mining Co., produced in 15 years about 2,500 kg. of gold, worth $1,500,000. From 1893 dates the famous Carsewene discovery, in territory then in dispute between France and Brazil. A settlement was made recently in favor of Brazil, by arbitration of the Switzerland State Council. Carsewene is said to have pro-duced about $18,000,000 in six years (1894-1900), but not even one-fourth of the production went through French Guiana and

Nov 1, 1910

By R. W. Gurry, L. S. Darken

The solubility of cementite in austenite is computed by thermodynamic methods from the observed solubility of graphite. It is found that the solubility of cementite is greater than that of graphite in the entire austenite temperature range. Thus the prior discrepancy between this portion of the phase diagram and the observed metastability of cementite is partially resolved. FOR several years it has been apparent that a serious discrepancy exists in certain observations pertaining to the Fe-C system. Direct experimental data indicate: 1-That the curve representing the solubility of graphite in austenite'" crosses that for cementite4 at about 945°C as shown in Fig. 1. 2— That graphite and austenite saturated therewith are stable1 relative to cementite at all temperatures between the eutectoid, about 723°C, and the eutectic, about 1153°C. These observations are mutually incompatible in view of a well-known consequence of the second law of thermodynamics, namely, that the stable phase (presumably graphite at all temperatures) has a lower solubility than the metastable phase (presumably cementite). Hence either 1 or 2 above must be in error; either the measured solubility of graphite or of cementite, or the observation as to the stability of graphite, is in error. Our present purposes are: 1—To collate the available data on cementite and prepare a table of HO — HO° and of (Fa— HO°)/T. This tabular method seems the best and most convenient way to represent the heat and free energy of formation. 2—To determine whether the measured solubilities of cementite and graphite in austenite are in accord with the above table and the measured thermodynamic properties of austenite, in order to resolve, if possible, the existing paradox of these two solubilities. Enthalpy of Cementite The enthalpy of cementite at 273 °K, H279 — HOcem, was computed by integration of the low temperature heat capacity as measured by Seltz, McDonald, and Wells" 68" to 298 °K) and as given by the Debye functions recommended by them (0" to 68°K); the result is included in Table I. At higher temperature HCem — H,,"" is given by Kelley who used the data of Naeser7 (298" to 1037°K) and of Umino8,9 (273° to 1923°K). We have recalculated Hcem — H273 cem from the data of UminoO in the following way. In the equilibrated alloy at temperature the weight fraction of cementite Pct c -Pct cr is PctC -PctCr designated f(C), and the

Jan 1, 1952

Jan 1, 1914

By Strathmore R. B. Cooke, Paul B. Queneau

The kinetics of the dissolution of scheelite in basic solutions of carbonate and fluoride were investigated. Work was also done with solutions of alkali metal chloride, hydroxide, phosphate, and mixtures of phosphate and fluoride. The study was conducted at 90 psig and at temperatures ranging from 100" to 155"C, and both natural and synthetic scheelite single crystals were used. The interaction of scheelite with carbonate solutions generally followed a parabolic rate law, and resulted in the formation of calcite crystals on the attached surface. The transport of the CO3 through the calcite to the scheelite surface was probably rate -controlling between 115" and 135°C. Positive deviations from Parabolic behavior were observed at 100" and 155?C, presumably due to the calcite grain growth, and to the formation of a noncoherent calcite layer, respectively. The leaching of scheelite with alkaline fluoride solution produced a calcium fluoride reaction-product which covered the surface as a sheet-like layer. Below 110°C the dissolution rate was parabolic; at 115" and 135°C it was linear. In the linear region, the periphery of the calcium fluoride layer lifted from the sample. Only the lower layers, braced by the scheelite substratum, remained unbroken. This bound layer, approximately constant in thickness, limited the rate at which the fluoride could attack the scheelite. The phosphate and phosphate-fluoride leaches dissolved scheelite at a linear rate; solid reaction products were respectively hydroxyapatite and fluorapatite. Sodium hydroxide and chloride were not effective leachants, and did not produce observable solid reaction products. THE feasibility of pressure leaching of scheelite pulps with basic solutions containing either carbonate or fluoride ions, as indicated by the following equations, has been established by previous investigators:1-3 200°C CaWO4s + CO37q - CaCO3s+WO4aq [1] 200°C CaWO4s + 2Faq ^ CaF2s+WO4aq [2] It is to be noted that a commercial process employing reaction [I] is in use at Union Carbide's operation near Bishop, Calif. In the earlier work referred to, it was apparent that the precipitation of the solid reaction-product on the scheelite particles sharply reduced contact of the leachant with the scheelite. We have extended this work by studying the kinetics of dissolution employing single crystals of scheelite of known exposed surface area. In addition, the effectiveness of solutions of phosphate, of phosphate with fluoride, and of chloride and hydroxide as leachants for scheelite have been investigated. EXPERIMENTAL Apparatus. The low-pressure autoclave used in this wo (100 psig maximum) is essentially that of J. Halpern4 as modified by F. A. Forward.5 Constructed entirely of 316 stainless steel, its maximum capacity is 4000 ml. The temperature in the autoclave was regulated to *0.5?C by a Wheelco thermocouple controller. A 4-in. diam, three-bladed impeller, circulated solution upward against the sample, and a strobo-scope permitted holding the stirring rate to *15 rpm. A check valve and a "pop" type safety valve were installed, a sample holder was fixed to an externally adjustable rod, and a water-cooled condenser was placed in series with the sampling valve. The stainless steel sample holder, Fig. 1, held the epoxy-mounted sample (f) five mm above the impeller. Tightening the tapered sleeve (d) positioned the epoxy-resin specimen-mount by forcing it back against the spacer (c). The mount (e) was 1 in. diam. Sample Description and Preparation. Both synthetic and natural scheelite crystals were leached. The former were single crystals of 99.95 pct purity which were leached approximately perpendicular to the "c" axis; they were supplied by the Gallard-Schlesinger Chemical Manufacturing Corp. The natural crystals, supplied by Minerals Unlimited, were transparent, analyzed 99.8 pct CaWO4, and in ultraviolet illumination exhibited the characteristic blue glow of substantially molybdenum-free scheelite. To permit exposure of an essentially constant surface area of scheelite to the leachant, the samples were mounted in Scotchcast Brand Resin No. 250 (Minnesota Mining and Manufacturing Co.). The mount-

Jan 1, 1970

By Tasuku Fuwa, John Chipman

Equilibrium data on the reactions of gases with carbon and oxygen dissolved in liquid iron are reviewed and correlated. A source of error in oxygen analysis of graphitic samples is exposed. New experimental data on the oxygen content of high -carbon iron in equilibrium with carbon monoxide indicate that the activity coefficient of oxygen is decreased by additions of carbon. The carbon-oxygen product decreases slightly with increasing carbon content. In recent years a number of investigations have been reported dealing with the equilibria between carbon and oxygen in liquid iron and gases containing carbon oxides. The laboratory study of these reactions dates back to 1931 with the publication of a paper by Vacher and Hamilton' on "The Carbon-Oxygen Equilibrium in Liquid Iron". The principal object of this study was to obtain data on the reaction shown by Eq. [3] below; their data and others by vacherZ permit evaluation of the other equilibrium constants as well. Subsequent studies have been reported by Matoba, Phragmen and Kalling and by Marshall and Chipman.5 The equilibria may be expressed by the following three equations: C + CO,= 2CO;Kl = Pc° [1] 0-+CO = CO,;K2=-P co, "0.PCO c + O = CO; K3 = In the equilibrium constants, ac and a0 are taken as equal to [% C] and [% 0] respectively in the infinitely dilute solution. At finite concentrations an activity coefficient is introduced such that ac =fc [%C], and so forth. It is to be noted that these equations represent only two independent relations, the third being derivable from any two. Richardson and Dennis have determined the conditions of equilibrium in reaction [I] at temperatures of 1560" to 1760°C. Their results have been confirmed by Rist and chipman7 who have shown how the data may be extended to cover the entire range of liquid compositions at temperatures from the eutectic up to 1760°C. An approximate confirmation has been reported by Fuwa and chipman.' These investigations also established the activity coefficient of carbon which was shown to increase rather rapidly with increasing concentration. For the very dilute solutions the value of Kl is expressed in the equation: log^i = - 7280/T+ 6.65 This equation leads to a value of Kl = 430 at 1540° C in excellent agreement with the average value of Marshall and Chipman.5 It is shown as line 1 in Fig. 1 together with the experimental observations. In the case of reaction [2] the direct experimental results can be supplemented by observations on the corresponding reaction with hydrogen, namely reaction [4]:

Jan 1, 1961

[FUQUA, H. B. and Thompson, B. E.: Oil and Gas Development and Production in North Texas for 1933, 107, 320; for 1934, 114, 417 Oil and Gas Development in West Texas 114, 438 FURMAN, W. F.: Heat and Corrosion-resisting Alloys. Printed in Oil & Gas Jnl., June 13, 1935 Furnace-bottom sand, uniformity, 73, 390 Furnace control, Isley apparatus, M27, 502 Furnaces (See also Holt-Dern; Blast Furnaces; Roasters; Wirebar, etc.): annealing: electric, 89, 424 gas-fired, 89, 425 gas vs. wood for nonferrous metals, 89, 422]

Jan 1, 1936

By E. A. Anderson

THIS seems to be the year for superlatives in A.I.M.E. meetings. The programs of the various Divisions and Institute committees offered an abundance of interesting and valuable information in the form of technical papers, symposia. and lectures to large and interested audiences. The Institute of Metals Division may hold up its head with pride for its own program. With six technical sessions, three full-day symposia, and the annual I.M.D. dinner, four meeting days were not enough and many simultaneous sessions were required. The quantity and quality of the paper were equaled by the numbers and interest of those attending.

Jan 1, 1944

By Thomas T. Read

THE fact that certain types of ore-deposits have attained their present condition through the action of descending surface waters was, perhaps, first clearly pointed out by Posepny.1 The oxidizing effects of such waters were discussed by Penrose,2 and many papers dealing with this phase of the subject have subsequently appeared. That secondary enrichment of sulphide ores, however, might be produced by descending surface waters was not clearly understood until after the copper-bearing veins of the Butte district, Mont., had been carefully studied by the geologists of the U. S. Geological Survey, al¬though De Launay3 had suggested that sulphides might be transported from point to point and re-deposited in the zone above the level of ground-water. As a result of the study of the Butte district, two papers by geologists engaged in the work appeared within a short interval. The first by Weed,4 dealing with the enrichment of veins by later metallic sulphides: and the second by Ernmons,5 treating of the secondary enrichment of ore-deposits in general. In the latter paper it was pointed out that a typical vein of sulphide ores which has been subjected to the action of descending surface waters exhibits four zones,-an upper or surface zone, in which the changes have been mainly of removal, the products being typically oxides; a second zone of oxide enrichment, in which the less soluble metals brought from above have been precipitated as carbonates or oxides; a third zone of sulphide enrichment,

Mar 1, 1906

By R. L. Orr, O. D. Sherby, J. E. Dorn

Creep data for pure metals at temperatures above those at which rapid recovery occurs (above about 0.45 the melting temperature) are correlatable by means of the equations and These correlations were applied successfully to data for aluminum, iron, nickel, copper, zinc, platinum, gold, and lead as well as for simple alloys. For a given metal, AH is a constant about equal to the activation energy for self-diffusion. THE early recognition that creep is stimulated by thermal activation prompted numerous investigators', ' to apply the same laws that are valid for the viscous behavior of liquids to analyses of creep data. To a good first approximation these laws are summarized by the equation were i is the creep rate; T, the absolute temperature; R, the gas constant in cal per degree per mol; T, the applied stress; AH, the activation energy in cal per mol; S', a constant dependent on the entropy of activation, the frequency of activation, and the contribution of each activation to the strain; and B', a constant dependent upon the size of the flow unit that is activated. Although Eq. 1 describes the flow of viscous fluids very accurately, its application to the creep of solids has been disappointing. Two reasons for the failure of Eq. 1 for creep are now known: First, the decelerating creep rates during primary creep demand that the internal structures of the metals are changing and that these changes might be reflected by changes in one or more of the three creep parameters S', AH, and B'. Consequently when the conventional methods of evaluating these parameters are employed by comparing the secondary creep rates at a series of temperatures and at a series of stresses, the true effects of temperature and stress are masked because of simultaneous changes in one or more of the creep parameters. Second, as will be illustrated more fully later, three distinctly different types of investigations have shown that the stress term for high temperature creep enters the analysis as and not as t/T. This rather unexpected result points sharply to a significant fundamental difference between the mechanisms for the viscous behavior of fluids and the high temperature creep of metals. More recent extensive investigations",'4 on the creep of high purity aluminum and several of its dilute a solid solutions have shown that where E is the total creep strain; temperature compensated time = for a constant temperature test; t, is the initial stress in a constant load test or the constant true stress in a constant stress test;" and t is the duration of test. • Eq. 2 is valid for either constant stress or constant load tests; but the total creep curve is difierent (i.e. the function, f, is differentl for each test. The fundamental origin of the validity of Eq. 2 is thought to arise from some equivalence of substructures in constant load creep tests at equal values of 0 or E. Both X-ray and metallographic examination revealed that practically identical lattice distortions and subgrain sizes are obtained for the same creep strain under the same load over wide ranges of test temperature.' Furthermore the room temperature tensile properties following equal creep strains at different temperatures under constant loads were also identical, illustrating that identical substructures were indeed obtained.' " A second type of correlation was obtained by differentiating Eq. 2 with respect to time, giving For the secondary creep rate, denoted by i,, But Eq. 2 reveals that 0, is a function of a, alone because the secondary creep rate in a given constant load test is always reached at a fixed value E,". Therefore where is the function that was introduced a number of years ago by Zener and Hollomon." Eq. 4 is not only valid for creep but will permit correlations between constant load creep and tensile data where e, is the rate of tensile straining and (TC is the engineering ultimate tensile strength.

Jan 1, 1955

By Samuel S. Wyer

THE following abbreviations have been used in, the text: Cassier's, Cassier's Magazine. Eng. Lond., The Engineer (London). Eng. Mag., Engineering Magazine. Eng. and Min. Jour., Engineering and Mining Journal. Eng. News, Engineering News. Eng. Rec., Engineering Record. Engng., Engineering. Engr., The Engineer (Chicago). J. I. and S. I., Journal of the Iron and Steel Institute. Jour. F. I., Journal of the Franklin Institute. Jour. Assn. Eng. Soc., Journal of the Association of Engineering Societies. Mar. Eng., Marine Engineering. . Mem, Soc. Ing. Civ., France, Memoires de la Society des Ingenieurs Civils, France. Prac. Eng., Practical Engineer. Proc. Digs. Soc. of W. Pa., Proceedings of the Engineers' Society of Western Pennsylvania. Proc. I. C. E., Proceedings of the Institute of Civil Engineers. Proc. I. 1M. E., Proceedings Institution of Mechanical Engineers. Trans. A. I. M. E., Transactions of the American Institute Mining Engineers. Sci. Am., Scientific American. Sci. Am. Sup., Scientific American Supplement. Zcitschr. d. V. D. Ing., Zeitschrift des Vereines Dentscher Ingcnieure.

Mar 1, 1905

By C. H. P. Lupis, Henri Gaye

There are m -I conditions for the stability of a solution of m components with respect to infinitesinzal flucturations. However, in most cases, only one of these conditions has to be considered to determine the domain of instability and the existence of this more restrictive condition greatly simplifies the calculations. It may be used advantageously for the prediction of miscibility gaps and the method is illustrated in details for the case of the Ag-Pb-Zn system. THE thermodynamic conditions for the formation of a miscibility gap may be viewed as a necessary consequence of the conditions for spinodal decomposition. A previous article1 has examined in detail the form of these conditions for multicomponent systems. There is only one condition for the stability of a binary system (with respect to infinitesimal fluctuations), but there are two conditions for a ternary system, and m — 1 conditions for an m-component system. The probability of violating a stability condition, and thus forming a miscibility gap, obviously increases with the number of components, a result which is rather intuitive since the atoms of the solution have now many more ways of redistributing themselves and introducing complexities in the form of the free energy hy-persurface. It is of interest to take advantage of this possibility of precipitating new phases and to examine which stability condition is the likeliest to be violated, that is, which stability condition is thermodynamically the most restrictive. The finding of such a condition would greatly simplify the application of the stability criteria since only one condition could then be considered, instead of m - 1. In Ref. 1, coherency strain energy terms were neglected, thus restricting the applications of the treatment to solutions where they are negligible, such as liquid alloys. In the following study the same assumption will be made. To generalize the treatment to systems where the strain energy terms are sizable, the reader is referred to Cahn's classical article on spinodal decomposition.2 Let us designate by Gij the second derivative of the Gibbs free energy with respect to the number of moles ni and n j. There are several equivalent sets of m — 1 stability conditions.' The one considered here expresses that the successive diagonal determinants of order 1, 2, ... m — 1, associated with the symmetric Gij matrix (for 2 5 i, j 5 m) are positive.' For a binary solution 1-2, the condition for stability is: O(u=G22^0 [1] For a ternary system 1-2-3, the condition [I.] is re- tained (the value of G22 will differ, of course, according to the concentration of 3) and another condition is introduced: £>(21 = G22G33 - Gl3 ^ 0 [2] In a composition diagram, these two conditions define two domains of instability. Starting at a point where the solution is stable (for instance at a point where the solution is very dilute) we gradually change the composition until the condition [I] or [2] is violated. As already noted in the literature, e.g., in the work of Prigogine and Defay,3 it is the boundary of the domain (2) which is first crossed. For if we assume that the boundary of the domain (1) is reached first, at this point G22 = 0 and the second condition is necessarily violated (D(2) = -& 5 0), in contradiction with our original assumption. An exhaustive study of the ternary regular solution case may be found in the work of Meijering.4 Moreover if the boundaries of the two domains have a common point, they also have a common tangent. For if the two lines were to cross each other as is illustrated in Fig. 1(a) any point M in the line QP would be such that £> = 0 and 0"' > 0 which, as shown above, are incompatible results. Thus, the two lines must be tangent at their common point Q as illustrated in the example of Fig. l(b). The reasoning of Fig. l(a) implies that the point Q is not a "singular" point for either boundary line. This singularity may be of two types. First, the lines meet without crossing each other and without being tangent. Second, the tangent at Q for D"' or 0"' is not single-valued. Other types of singularity are unlikely because of the usual analytical forms of D"' and 0"'. The exception to the common tangent requirement due to the first type of singularity was pointed out by John Morral;5 it occurs when the common point, Q' or (3" in Fig. l(b), is located at a boundary of the composition diagram, e.g., at the line X3 = 0. It may also be noted that at the common nonsingular point Q of D(1) and D(2), Fig. 1(b), G23 is necessarily equal to zero, whereas at a point such as Q' or Q", this conclusion is no longer valid because the product G22G33 is now indefinite (of the form 0. a). The exception to the common tangent requirement due to the second type of singularity occurs when two branches of the same boundary line intersect, for example when D(1)or D(2) decomposes into a product of functions, at a point which belongs to the boundary of the other condition. It is possible to show by a simple analytical calculation that, in this case, if Q is a singular point of D(1), then it is necessarily a singular point of D(2), and that the reciprocal is true except if G33 = 0 at Q. For the present article, however, more elaboration on these singularities appears to be unwarranted. To generalize the previous results to an m -component system, we use the mathematical theorem stating that if the diagonal determinant D(r) = 0, then

Jan 1, 1970