ARTICLE I Name and Object Sec. 1. This Division shall be known as the Institute of Metals Division of the American Institute of Mining and Metallurgical Engineers. Sec. 2. The object of the Division shall be to furnish a medium of cooperation between those interested in the field of physical metallurgy; that is, the nature, structure, alloying, fabrication, heat treatment, properties and uses of metals; to represent the AIME insofar as physical metallurgy is concerned, within the rights given in AIME Bylaw, Article XI, Sec. 2, and not inconsistent with the Constitution and Bylaws of the AIME; to hold meetings for the discussion of physical metallurgy; to stimulate the writing, publication, presentation and discussion of papers of high quality on physical metallurgy; to accept or reject papers for presentation before meetings of the Division. ARTICLE II Members Sec. 1. Any member of the AIME of any class and in good standing may become a member of this Division upon registering in writing a desire to do so, but without additional dues. Sec. 2. Any member not in good standing in the AIME shall forfeit his privileges in the Division. ARTICLE III Funds Sec. 1. The expenditure of the funds received by the Division shall be authorized by the Executive Committee of the Division. ARTICLE IV Meetings Sec. 1. The Division shall meet at the same time and place as the annual meeting of the AIME, and at such other times and places as may be determined by the Executive Committee subject to the approval of the Board of Directors of the AIME. Sec. 2. The annual business meeting shall be held within a few days before or after the annual business meeting of the AIME. Sec. 3. At a meeting of the Division, for which notice has been sent to the members of the Division through the regular mail or by publication in the Journal of Metals at least one month in advance, a business meeting may be convened by order of the Executive Committee and any routine business transacted not inconsistent with these Bylaws or with the Constitution or Bylaws of the AIME. Sec. 4. For the transaction of business, the presence of a quorum of not less than 25 members of the Division shall be necessary. ARTICLE V Officers and Government Sec. 1. The officers of the Division shall consist of a Chairman, a Senior Vice-Chairman, a Vice-Chair -man, a Secretary and a Treasurer. The office of Secretary and Treasurer may be combined in one person, if desired by the Executive Committee. Sec. 2. The government of the affairs of the Division shall rest in an Executive Committee, insofar as is consistent with the Bylaws of the Division and the Constitution and Bylaws of the AIME. Sec. 3. The Executive Committee shall consist of the Chairman, Senior Vice-Chairman, Vice-Chairman, past Chairman, Secretary, and nine members, all of whom shall be nominated and elected as provided hereafter in Article VII. Sec. 4. The Chairman, Senior Vice-Chairman and Vice-Chairman shall serve for one year each, or until their successors are elected. Each member of the Executive Committee shall serve three years. The Chairman shall remain a voting member of the Executive Committee for one year after his term as Chairman. Sec. 5. The Treasurer of the Division shall be invited to meet with the Executive Committee, but without ex-officio right to vote. He shall be appointed annually by the Executive Committee, from the membership of the Executive Committee or otherwise. Sec. 6. The annual term of office for officers of the Division shall start at the close of the Annual Meeting of the Institute and shall terminate at the close of the next Annual Meeting. ARTICLE VI Committees Sec. 1. There shall be standing committees as follows: Programs Committee. Finance Committee, Membership Committee, Annual Lecture Committee, Technical Publications Committee, Mathewson Gold Medal Committee, Nominating Committee, Education Committee and such other Committees as the Executive Committee may authorize. Sec. 2. It shall be the duty of the Programs Committee to secure the presentation of papers of appropriate character at meetings of the Division. Sec. 3. It shall be the duty of the Finance Committee to inquire into and examine the financial condition of the Division and to consider proper means of increasing its revenue and limiting its expenses. The Finance Committee shall audit the accounts of the Division and report to the Executive Committee prior to the Annual Meeting of the Division. It shall render a budget to the Executive Committee estimating receipts and expenses for the ensuing year so that action can be taken on same at the first meeting following the Annual Meeting.

Jan 1, 1953

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.' Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800' to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By A. M. Johnson, M. M. Singh

The mechanism of failure under a drill bit is still improperly understood in spite of several investigations of the subject. Generally, the cratering process under static loading conditions is considered to be similar to that achieved dynamically by impact. This paper attempts to indicate that, although the sequence of fracturing in the two cases appear to be identical, at least some dissimilarities exist. For example, the width-to-depth ratios of the craters vary to some extent, and the amount of energy consumed per unit of volume of craters is unequal for the two different loading conditions. Prevalent rock penetration processes are dominated by methods utilizing mechanical attack on rock. It is, therefore, generally accepted that a better comprehension of the mechanism of rock failure under a wedge would prove beneficial towards improving present drilling techniques. Several attempts have been made in recent years to explain how craters are formed under a drill bit, but the mechanism of failure beneath a bit is still improperly understood. 1-11 Most investigators, to date, have inferred the sequence of events occurring during crater formation from analyses of force-time diagrams,1"6 from theoretical considerations,7 or from a study of the configurations of final craters.8-l0 These analyses have led to the presentation of widely divergent models for rock failure beneath a drill bit, ranging from brittle to viscoelastic. The cratering process under dynamic loading commonly is regarded as being similar to that obtained under gradually applied, or 'static', loads. But the effect of rate of loading on the action of a bit is still disputed. Some investigators11-12 maintain that there should be no such effects, whereas others have demonstrated experimentally that these exist.13-17' The purpose of the investigation reported in this paper was to examine petrographically the damage done to rock under the action of a chisel-shaped wedge, both with 'static' and dynamic loading, and to determine if rate-of-loading effects could be detected. Significant quantitative differences in crater volumes and depths were found to exist for a given consumption of energy. On the basis of this data, an attempt was made to indicate some of the rheological properties that a proposed model should possess. All the work reported herein was conducted at atmospheric pressures. EXPERIMENTAL APPARATUS AND PROCEDURE Two types of rocks were employed for most of the experiments reported in this paper, viz. Bedford (Indiana) limestone and Vermont marble. The mechanical properties of these rocks are given in Appendix A. Actually two types of Vermont marble were used, but since no marked difference could be discerned between the two varieties (as seen in Fig. 10) the data was used collectively for the analysis. Stronger rocks were not employed owing to difficulty in generation of observable craters without damage to the equipment. Six-in. diam cores were drilled from the rock samples and embedded in 8-in, diam steel pipe with 3/8-in. wall thickness, using hydrostone to fill the annulus between the core and the pipe. This procedure was adopted to confine the rock specimen so that fractures would not propagate to the edges of the cores. This goal was achieved satisfactorily for these tests because no cracks were observed to extend into the medium surrounding the rock, even when craters were formed only 1 in. from the rock core periphery. Three to four craters were formed on a core face, because the rock damage from any one crater generally did not appear to extend into the others. Whenever, interference between damaged areas around adjacent craters was suspected, the data was rejected for purposes of the analysis. The limestone and marble samples were tested with a 60-degree, wedge-shaped bit, 1 5/8-in. in length, made of tool steel. The bit shank had two SR-4 type electrical resistance strain gages, mounted axially, to record the force-time history during the loading operation. The static indentation tests were conducted using a 50-ton capacity press fitted with an adapter for drill bit attachment. See Fig. 1. The force exerted by the bit at any instant was measured with strain gages affixed to the bit shank. An aluminum cantilever, with two SR-4 strain gages mounted near its clamped end, was employed to measure bit displacement. Both sets of gages were included in Wheatstone bridge circuits,

Jan 1, 1968

By F. R. Jones

AT Tahawus, N. Y., National Lead Co. operates the MacIntyre development. Here the world's largest titanium mine produces 5200 long tons of ore per day and pours 8000 long tons of waste rock over its dumps. Concentrated ilmenite is sent by rail to National Lead Co. pigment plants, and a second product, magnetite, is sold to steel producers in raw form or is agglomerated and shipped as sinter. Several earlier attempts had been made to produce iron from the deposits, which have been known since 1826. These attempts failed, chiefly because of titanium impurity. In 1941 the present owners reestablished the operation for production of war-scarce ilmenite, and the impurity became the main product. The Ore: The MacIntyre ore zone is about 2400 ft long and 800 ft wide in horizontal measurements. Ore outcrops were found on the northwest side of Sanford Hill, 450 ft above Sanford Lake and 2500 ft southeast. The zone dips at about 45" toward the lake and plunges to the southwest. The ore minerals, ilmenite and magnetite, are unevenly distributed in bands roughly parallel to the long axis of the ore zone and are interspersed with bands and horses of waste. Hanging wall ores are fine grained and grade from rich ore to waste rock or gabbro. Footwall ores are coarse grained and are almost entirely ilmenite and magnetite. The foot-wall waste rock, anorthosite, is the common country rock. Several faults cut the ore zone. These faults have no great displacement but do contribute to the great physical variations in ore rock and surrounding waste. The Mine: The MacIntyre mine is an open pit operation, with benches at 35-ft intervals. The lowest bench is now 54 ft below lake level. Loading equipment consists of three electric-powered shovels (a P & H model 1400 with 4-yd dipper and two Bucyrus-Erie models 85-B with 2%-yd dippers) and one diesel-powered shovel (a Northwest model 80D with 2%-yd dipper). Ore and waste are transported to a 48x60-in. jaw crusher in ten 22-ton Euclid trucks with 300-hp diesel engines. Ordinarily the two Bucyrus-Erie 2 % -yd shovels load ore into a fleet of three or four trucks. This combination works two 8-hr shifts per day, moving 5200 long tons of ore to the crusher and removing a small portion of the waste rock. The P & H model 1400 shovel, with a fleet of four trucks, loads waste on three shifts per day. The mine operates on a 5-day week, with a small maintenance crew working Saturday. Oversize rock is broken by a dropball handled by an Osgood model 825 rubber-mounted crane.' Ore and waste are broken by drilling and blasting 9-in. diam vertical holes behind the benches. Bucyrus-Erie 42-T churn drills are used to drill the holes, which are extended 4 ft below the bench level on which the broken rock will fall. Drilling and Blasting History: In its early years the mine was equipped with Bucyrus-Erie 29-T churn drills, which drilled 6-in. holes. To keep up with production requirements the hole diameter was soon increased to 9 in., and by 1950 the three 42-T drills now in use had been acquired. Early blasting experiments with different kinds and grades of explosive led to adoption of 90 pct straight gelatin dynamite as standard. It was recognized that this explosive was expensive, and from the start of operations until 1950 extensive experiments were made using blasting agents of the ammonium nitrate family. Results were recorded as uniformly poor, with great build-up of oversize rock. The expense of these experiments, and the discouraging results, caused the abandonment of any expectation of breaking MacIntyre rock with anything but 90 pct straight gelatin dynamite. Further standardization led to 9-in. well drillhole spacings set at 16 ft in ore and 18 ft in waste, exceptions being permitted only for unusual conditions. The hole burdens were theoretically about 22 ft. Due to the extreme back-slope of bench faces, caused by blasting with heavy charges of dynamite, actual burdens were commonly well over 30 ft. Lack of precise control resulted in many holes having a burden as light as 15 ft. General practice was to stem 6 or 7 ft of hole with magnetite concentrate, the amount of stemming being left to the discretion of the pit foreman. Usually all holes in a row were fired instantaneously with Primacord detonating fuse. Millisecond delays were

Jan 1, 1957

By E. W. Stewart, G. P. Conard, J. F. Libsch

The effects of several additives upon the reduction characteristics of hydrogen-reduced ferrous formate are described. The various additives inhibit sintering of the reduced iron particles by apparently different mechanisms. The magnetic properties of the low density compacts produced from the resulting ultra-fine iron powders were improved markedly. THE permanent magnetic characteristics of ultra-fine iron powder prepared by various means have been a subject of considerable interest and experimentation in the past few years. When such particles are small enough to show single domain behavior, they possess' 1—permanent saturation magnetization, and 2—high coercive force. In the absence of domain boundaries, the only magnetization changes in a particle occur through spin rotation which is opposed by relatively large anisotropy forces. With decreasing particle size, the coercive force tends to increase to a maximum and then decrease because of the instability in magnetization associated with thermal fluctuations. Kittel' has calculated the critical diameter at which a spherical particle of iron can no longer sustain domain boundaries or walls to be approximately 1.5x10-' cm. Stoner and Wohlfarthr in England and Neel4,6 in France have shown from purely theoretical calculations that the high coercive force expected from single domain particles is dependent upon crystal anisotropy, shape anisotropy, or strain anisotropy contributions. Further work by Weil, Bertaut,' and many others has contributed much to the understanding of fine particle theory. Neel and Meikeljohn" have demonstrated that a decrease in particle size below a critical value of approximately 160A leads to a quite rapid decrease in coercive force because of the prevention of stable magnetization by thermal agitation. Lih1, working with powders prepared by the reduction of formate and oxalate salts of iron, has shown the marked influence of powder purity upon magnetic properties. Maximum coercive force was obtained in powders of approximately 65 pct metallic iron content while the maximum energy product, (BxH) occurred in powders of 85 pct metallic iron content. Careful consideration of the preceding theoretical considerations and experimental results has led to the manufacture of permanent magnets from ultra-fine ferromagnetic powders by powder metallurgy techniques. Such work has been done by Dean and Davis," the Ugine Co. of France, and Kopelman." The aforementioned work of Kopelman and the Ugine Co. was concerned somewhat with the effect of various additives upon the properties of hydrogen-reduced ferrous formate. Virtually no work, however, has been published on the effects of additives on the reduction rates of metal formates, although unpublished work by Ananthanarayanan16 howed promise of improved energy product in ultra-fine iron compacts prepared by the hydrogen reduction of a coprecipitated mixture of magnesium and ferrous formate. After consideration of the preceding information, it was hoped that a better balance between the metallic iron content and particle size of the reduced iron powder could be accomplished by a prevention of the attendant sintering of the partially reduced iron powder during the reduction reaction. It appeared possible that magnesium oxide might interpose a mechanical barrier between adjacent iron particles and prevent their sintering together, while metallic cadmium and metallic tin would interpose a liquid barrier which might accomplish the same purpose. The degree to which these materials were effective in accomplishing the foregoing objective and the experimental details associated with the work are reported in the following sections of this paper. Experimental Procedure Preparation of Formate and Oxide Mixtures: To obtain ferrous formate of reproducible reduction characteristics, a slight modification' was made in the technique of Fraioli and Rhoda." A supersaturated solution of ferrous formate was mixed with an equal volume of 95 pct ethyl alcohol and the formate crystals precipitated by stirring and screened to —325 mesh. These crystals were in the shape of elongated hexagons, approximately 4x10 micron in dimension. Various preparations of such ferrous formate, designated as lot 111, were reduced for 2 hr, yielding ultra-fine iron particles of exceedingly reproducible size, metallic iron content, and magnetic properties. The magnesium and cadmium formates were prepared by the reaction of dilute formic acid with their respective carbonates, while the tin formate was prepared by the reaction of dilute formic acid with stannous hydroxide. To evaluate the effect of metallic formate additives in intimate mixture with the ferrous formate, varying amounts of magnesium, cadmium, and tin formates were coprecipitated with the latter. The designations of these materials and their chemical compositions are given in Table I. Due to the differing solubilities of the various formates in aqueous media,

Jan 1, 1956

By T. E. Watkins, M. D. Nelson

INTRODUCTION Deeper drilling for oil is becoming more and more the rule rather than the exception. With deeper drilling come additional problems, perhaps the greatest being those brought on by the higher temperatures encountered down the hole. particularly in the Gulf Coast region of Texas and Louisiana. Temperature gradients of the order of 1.8° to 2.0°F/100 ft are not unusual, and a gradient of 2.3"F.'100 ft is found in some areas of Texas. With a mean surface temperature of 74oF, the following temperatures could be expected for a geothermal gradient of 2.0°F; 100 ft: at 10,000 it. 271°F. 12,000 ft, 314°F: 14,000 ft, 354,oF; and 16.000 ft. 394°F. Severe gelation of lime-base drilling fluid in wells that have high bottom hole temperatures has become perhaps the most serious difficulty enconntered in drilling under such conditions. Lime-base drilling fluids have been very succesefully and widely used in the drilling of wells in the Gulf Coast region because of their inherent stability toward contaminants. their ability to suppress the swelling dispersion of bentonitic shales, and their ease of maintainance. The gradual recognition: during the past few years, that these muds were. in themselve. the cause of many difficulties experienced in drilling has led to wide-pread efforts by the drilling industry. to determine the reasons for the failure of these mud systems and to develop mud systems capable of performing satisfactorily under high-temperature conditios. MANIFESTATIONS OF HIGH-TEMPERATURE GELATION it is generally possible to recognize the symptons of high-temperature gelation early enough that advance predictions can be made of serious difficulties. in mud control, and the useful life of the drilling fluids can be extended by proper treatment. Following i.; a list of the manifestations of high-temperature gelation: (1) The drill string 'takes weight' while going in the hole after a trip. In early stages of high-temperature gelation it is possible to notice a slight reduction in drill string weight as the drill pipe is lowred near the bottom of the hole. (2) Excessive pump pressure is required to .tart the circulation of drilling fluid at or near the bottom of the hole when going hack to bottom after a trip. As the severity of the gelation increases it may be necessary to break circulation a number of times when going in the hole. (3) The drilling fluid from the bottom of the hole is thick and often granular or lumpy when pumped up after making a round trip. In a severely gelled drilling fluid system such a condition may be irreversible; that is, it cannot be stirred or chemically treated to produce a satisfactory drilling fluid. (4) Completion tool.. such as logging tools or perforating guns will not sink to the bottom of the hole. On some occasions completion tools will become stuck and require a fishing job to retrieve them if the wire line attached to them is broken. It is often difficult to determine whether the condition of the drilling fluid is responsible for sticking the tool or whether the wire line becomes key seated in a crooked hole and causes the allow difficulty. When there are 110 other symptoms of high-temperature gelation. then the difficulty may usually be attributed to the latter cause. (5) In extreme cases of high-temperature gelation it is necessary to "wash" and "ream" when going back to bottom after coming out of the hole. (6) In many -instance. it has been found to be extremely difficult and expensive to 1111 production packers 2nd tubing in moderately deep oil wells which had been drilled with a lime-base drilling fluid. In such instances-the original mud had apparently "set" to a consistency approaching that of a weak cement. CAUSES OF HIGH-TEMPERATURE GELATION Extensive test; have indicated that a lime-base mud does not develop a highly gelled condition at temperatures below 250°F. whereas above that temperature such condition often develops rapidly. (Fig. 1) concurrently. the following changes are evident ill the mud: (1) The alkalinity of the mud decreases to a very low value. with both caustic soda and lime being consumed. (2) The quartz content of the mud decreases sharply. (3) The bentonitic content of the mud decreases or di-appears, with concurrent decrease or loss of base exchange capacity of mud solids. (4) New compounds formed in the mud have been found to be cal-cium silicate, calcium aluminum silicate, and calcium sodium aluminum silicate. (5) The mud loses the ability to form a filter cake of low permeability. The above characteristics have been discussed, in part. by other authors

Jan 1, 1953

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970

By J. S. Billheimer, B. H. Sage, W. N. Lacey

A restricted ternary system made up of n-pentane, tetralin, and a purified bitumen was investigated at 70, 160, and 220 °F. Most of the experimental observations were at atmospheric pressure or at 200 psi." However, some experimental measurements were carried out at a pressure of approximately 8000 psi. It was found that the purified bitumen was precipitated from its solution or dispersion in tetralin by the addition of n-pentane and that the separation occurred at lower weight fractions of n-pentane at the lower temperatures. The bitumen-tetralin solutions show some colloidal characteristics at temperatures below 160 °F when near compositions at which the bitumen separates as a solid phase. At states remote from the phase boundaries and at temperatures above 160 °F these characteristics become less evident. Under these latter circumstances the mixtures tend to follow the behavior of true solutions, particularly in regard to the approach to heterogeneous equilibrium. An increase in pressure appears to increase the solubility of bitumen in tet-ralin-n-pentane solutions. This effect is more pronounced at temperatures above 160 °F than at lower temperatures. INTRODUCTION Asphaltic phases of plastic or solid nature have appeared in numerous instances during the recovery of petroleum from underground reservoirs. Such depositions occurring underground appear to have caused adverse production histories for particular wells or zones. Because of this field experience, it is desirable to understand the factors which influence the formation or separation of the asphaltic phases from petroleum. The problem is unusually complex because the number of true components involved is very large and the details of the phase behavior encountered are difficult to ascertain experimentally. The literature relating to asphalts, asphaltines, and bitumen is voluminous and widespread.&apos; Only those references which are directly pertinent to the work at hand are cited. The separation of an asphaltic phase, hereinafter called bitumen? from naturally occurring hydrocarbon mixtures has been the subject of several investigations.2&apos;3&apos;4&apos;5&apos;6 It has been found that as many as four phases4 may be produced from a crude oil by the solution of a natural gas and propane at a pressure of 1500 psi and a temperature of 70 °F. The separation of bitumen from such naturally occurring mixtures results in at least one liquid phase which is substantially free of high molecular weight components.³ The influence of the solution of lighter hydrocarbons on the separation of bitumen from a Santa Fe Springs crude oil has been investigated. The results indicate that in the case of the methane-crude oil system, the quantity of plastic or solid phase separated reaches a maximum between 0.14 and 0.19 weight fraction methane and then decreases until negligible at higher weight fractions of methane. Similiar behavior was encountered in the case of mixtures of ethane and crude oil. The decrease in the quantity of the solid phase with an increase in the weight fraction of the lighter component appears to result from the formation of an additional liquid phase6 in which the bitumen is relatively soluble. The formation of this additional phase probably occurs at a weight fraction of methane close to that at which the quantity of separated solid reaches a maximum. A comparison of the deposition of bitumen in the field with the separation of asphalts from lubrication oil has been made&apos; and apparently the phenomena are similar. The phase behavior of bitumen also appears to be comparable to that of coal tar."&apos; The chemical and physical characteristics of asphalts and bitumen have been the subject of extended investigations which have been reviewed in some detail by Katz.¹º The conclusion was reached that the dispersion of bitumen in a number of organic liquids was not entirely colloidal since it was impossible to isolate individual dispersed particles even with the electron microscope. However, the evidence appeared to indicate that at states close to phase boundaries the extent of the dispersion of the phases influenced the equilibrium to a greater extent than is encountered in many simpler systems. From earlier study of field samples it became apparent that the phase behavior of bitumen-hydrocarbon systems was unusually complex. It was difficult to characterize in detail the phase behavior involved in naturally occurring hydrocarbon systems, even after a relatively extended investigation. For this reason, the study of a somewhat simpler system which still behaved in a similar manner became desirable. Three major constituents were necessary as-follows: a bituminous solid, a liquid constituent which was a reasonably good solvent, and a constituent in which bitumen was largely insoluble. A sam-

Jan 1, 1949

By W. N. Lacey, B. H. Sage, J. S. Billheimer

A restricted ternary system made up of n-pentane, tetralin, and a purified bitumen was investigated at 70, 160, and 220 °F. Most of the experimental observations were at atmospheric pressure or at 200 psi." However, some experimental measurements were carried out at a pressure of approximately 8000 psi. It was found that the purified bitumen was precipitated from its solution or dispersion in tetralin by the addition of n-pentane and that the separation occurred at lower weight fractions of n-pentane at the lower temperatures. The bitumen-tetralin solutions show some colloidal characteristics at temperatures below 160 °F when near compositions at which the bitumen separates as a solid phase. At states remote from the phase boundaries and at temperatures above 160 °F these characteristics become less evident. Under these latter circumstances the mixtures tend to follow the behavior of true solutions, particularly in regard to the approach to heterogeneous equilibrium. An increase in pressure appears to increase the solubility of bitumen in tet-ralin-n-pentane solutions. This effect is more pronounced at temperatures above 160 °F than at lower temperatures. INTRODUCTION Asphaltic phases of plastic or solid nature have appeared in numerous instances during the recovery of petroleum from underground reservoirs. Such depositions occurring underground appear to have caused adverse production histories for particular wells or zones. Because of this field experience, it is desirable to understand the factors which influence the formation or separation of the asphaltic phases from petroleum. The problem is unusually complex because the number of true components involved is very large and the details of the phase behavior encountered are difficult to ascertain experimentally. The literature relating to asphalts, asphaltines, and bitumen is voluminous and widespread.&apos; Only those references which are directly pertinent to the work at hand are cited. The separation of an asphaltic phase, hereinafter called bitumen? from naturally occurring hydrocarbon mixtures has been the subject of several investigations.2&apos;3&apos;4&apos;5&apos;6 It has been found that as many as four phases4 may be produced from a crude oil by the solution of a natural gas and propane at a pressure of 1500 psi and a temperature of 70 °F. The separation of bitumen from such naturally occurring mixtures results in at least one liquid phase which is substantially free of high molecular weight components.³ The influence of the solution of lighter hydrocarbons on the separation of bitumen from a Santa Fe Springs crude oil has been investigated. The results indicate that in the case of the methane-crude oil system, the quantity of plastic or solid phase separated reaches a maximum between 0.14 and 0.19 weight fraction methane and then decreases until negligible at higher weight fractions of methane. Similiar behavior was encountered in the case of mixtures of ethane and crude oil. The decrease in the quantity of the solid phase with an increase in the weight fraction of the lighter component appears to result from the formation of an additional liquid phase6 in which the bitumen is relatively soluble. The formation of this additional phase probably occurs at a weight fraction of methane close to that at which the quantity of separated solid reaches a maximum. A comparison of the deposition of bitumen in the field with the separation of asphalts from lubrication oil has been made&apos; and apparently the phenomena are similar. The phase behavior of bitumen also appears to be comparable to that of coal tar."&apos; The chemical and physical characteristics of asphalts and bitumen have been the subject of extended investigations which have been reviewed in some detail by Katz.¹º The conclusion was reached that the dispersion of bitumen in a number of organic liquids was not entirely colloidal since it was impossible to isolate individual dispersed particles even with the electron microscope. However, the evidence appeared to indicate that at states close to phase boundaries the extent of the dispersion of the phases influenced the equilibrium to a greater extent than is encountered in many simpler systems. From earlier study of field samples it became apparent that the phase behavior of bitumen-hydrocarbon systems was unusually complex. It was difficult to characterize in detail the phase behavior involved in naturally occurring hydrocarbon systems, even after a relatively extended investigation. For this reason, the study of a somewhat simpler system which still behaved in a similar manner became desirable. Three major constituents were necessary as-follows: a bituminous solid, a liquid constituent which was a reasonably good solvent, and a constituent in which bitumen was largely insoluble. A sam-

Jan 1, 1949

By H. C. Gatos, A. D. Kurtz

WITH the growing interest in the mechanism of self-diffusion of metals, the study of accurate and convenient methods for determining self-diffu-sion coefficients appears highly desirable. It was with this objective in mind that the present investigation was undertaken. Gatos and Azzam1 employed an autoradiographic technique for measuring self-diffusion coefficients of gold. This method involved sectioning of the specimen through the diffusion zone and recording the radioactivity directly on a photographic film. Because of the very short range of the emitted ß rays in gold, the activity recorded on the film was essentially the true surface activity. With proper choice of the sectioning angle, sufficient resolution could be obtained and the entire concentration-distance curve recorded in one measurement. For the boundary conditions of the experiment, where an infinitesimally thin layer of radioactive material diffuses in positive and negative directions into the end faces of a rod of infinite length, the solution of the diffusion equation is C/Cn = 1/v4pDt exp (-x2/4Dt) where C is the concentration of diffusing element (photographic density in this case), C,, is the constant (depending upon amount of radioactive material), x is the diffusion distance, D is the diffusion coefficient, and t is the time. Thus, by plotting the logarithm of the concentration vs the square of the diffusion distance, a straight line results and the slope contains the diffusion coefficient. In this manner, the self-diffusion coefficient of gold can be obtained as a function of temperature. In the present investigation the results reported by Gatos and Azzam1 have been verified, and the autoradiographic technique has been further developed and applied for the determination of the self-diffusion coefficient of gold at a number of temperatures. Furthermore, the energy of activation for the self-diffusion of gold has been conveniently determined. . Experimental Techniques Preparation of Specimens: The inert gold of high purity was received in the form of a rod from which cylinders were cut and machined to a diameter of 0.500 in. The specimens were annealed to a suitably large grain size and the faces were surface ground prior to the deposition of the radioactive layer. The radioactive isotope Au198 was chosen. It was produced in the Brookhaven pile by means of the reaction Au197 + n ? Au108. It decays by ß emission (0.96 mev) to Hg108 with the subsequent emission of a y ray (0.41 mev). 70Au 108 ? 80Hg 108 + -1e°. The half life of the Au108 is 2.7 days so that a strict time schedule had to be maintained in order to secure sufficient activity until the end of the experiments. For this reason, initial activities as high as 10,000 millicuries per gram were used. The gold arrived in the form of foil and was evaporated onto one face of each gold specimen cylinder to a thickness of about 100A. A sandwich-type specimen was formed by welding two such cylinders together. Evaporation of Gold: The gold was evaporated under vacuum from heated tantalum strips which were bent in such a way as to limit the solid angle through which the gold was allowed to vaporize, thus insuring a more efficient utilization of the gold. The specimens rested on flat brass rings which had an inner diameter of 0.475 in. The entire specimen-holding assembly could be manipulated from outside the vacuum system by means of a magnet which attracted a slug of soft iron attached to the assembly. By evaporating inert gold on glass slides under conditions identical to those employed for the radioactive gold, it was found that the thickness of the films was about 100A. Welding: The welding was performed by hot pressing in a stainless steel cylinder. The inside of the cylinder was threaded and fitted for two plugs. The specimens to be welded were placed in the middle of the cylinder and two pressing disks, one at each end, were inserted to avoid shearing stresses as the plugs were tightened. Mica disks were placed between the pressing disks and the specimens to prevent them from welding. The plugs were then tightened with a hand wrench and the entire unit was placed in an argon stream for about an hour to remove the oxygen. The unit was then inserted in the center of an argon atmosphere furnace maintained at about 700°C and left there for about an hour. Because of the difference in the temperature coefficient of expansion of the two metals, as the temperature rose. the pressure on the specimen-rollple increased and a weld resulted Welding was generally satisfactory under the conditions described.

Jan 1, 1955

By R. M. Waterstrat

The phases occurring in the V-Mn system were studied by means of X-yay diffraction and metallo-paphic techniques, using are-melted alloy specimens annealed in the temperature range 800° to 1150°C and quenched. The bcc solid solution extends at 1250°C all the way from vanadium to 6-manganese. Below 1050°C the a-phase is formed, and the terminal a-manganese phase is stabilized up to about 900°C by vanadium in solid solution. IN the only previous general survey of the V-Mn system Cornelius, Bungardt and Schiedtl reported the existence of three intermediate phases corresponding to the approximate compositions VMn,, VMn, and V5Mn. The phase VMn8 has recently been identified as a o phase2 but the alloy VMn was found to have a bcc structure2 corresponding apparently to the vanadium solid solution rather than to the large cubic unit cell reported by Cornelius et al. 1 Subsequent work by Rostoker and Yamamoto3 has shown that the vanadium-base bcc solid solution extends to at least 15 pct Mn at 900°C. An alloy corresponding to the composition VMn, was examined by Elliott,4 who reported that the as-cast sample as well as samples annealed at 1200o and 1300°C had bcc structures, but that annealing at 1000°, 800") and 600°C produced two phases. One of these phases was apparently the bcc solid solution and the other resembled the o phase structure. Hellawell and Hume-Rothery5 established the phase relationships in manganese-rich alloys above 1000°C, and showed that the o phase in this system is replaced by the 6 Mn (bcc) solid solution at temperatures above 1050°C. These results suggest that a continuous bcc solid solution may exist above 1050°C between vanadium and 6 Mn. The present investigation was undertaken in order to develop more complete information in regard to this system. EXPERIMENTAL METHODS The alloys used in the present work were prepared by arc-melting electrolytic manganese having a minimum purity of 99.9 pct and vanadium lumps with a purity of 99.7 pct. The major impurities present in these metals were carbon, nitrogen, and oxygen and this would account for the small percentage of nonmetallic inclusions observed metal-lographically. The arc-melting was at first performed under a helium atmosphere and it was necessary to keep the melting times as short as possible in order to minimize the loss of manganese by vaporization. It was later found that the evaporation of manganese was considerably reduced when the melting was done under argon atmosphere. The final composition of each alloy was calculated by assuming that the total weight loss during melting was due to evaporation of manganese. Compositions which were calculated in this manner agreed reasonably well with the results of chemical analysis, as shown in Table I. Spectrographic analysis revealed the presence of contamination by tungsten, but in no case was the percentage of tungsten greater then 0.4 at. pct. The specimens were in each case broken in half and the fractured section was examined visually and microscopically for evidence of inhomogeneity. Each specimen was homogenized at temperatures near l100°C, as shown in Table I. After this treatment most specimens consisted of large columnar grains of the bcc vanadium solid solution. The etchant used in most of the metallographic work consisted of 20 pct nitric acid, 20 pct hydro-flouric acid, and 60 pct glycerine. It was found that this etchant would clearly delineate the phases present in these alloys although it does not produce any striking contrast between the phases. For certain manganese-rich alloys, a 1 pct aqueous solution of nitric acid was used. This etchant gave a brown color to the a-manganese phase, whereas the o phase was virtually unattacked and appeared very light as shown in Fig. 1. The etchants used by Cornelius et a1.l were found to produce spurious effects in some of these alloys. In particular, the vanadium-rich alloys etched in hot sulfuric acid often appeared to consist of two phases when both X-ray diffraction and etching with the glycerine-acid mixture indicated the presence of single phase bcc solid solution. A few percent of what appears to be an oxide or nitride phase was found at the grain boundaries and in the interior of the grains, especially in the vanadium-rich alloys. All alloys were annealed in sealed silica tubes containing 1 atm of pure argon and these tubes were then quenched in cold water. Although some manganese loss occurred during annealing, the loss seemed to be confined to the surface of the speci-

Jan 1, 1962

By R. F. Shurtz

R. Duval (Mining Engineer, Ancien eleve de PEcole Polytechnique, Paris, France) I do not agree with the Eq. 3, reading: m =1/100- [(0.214x30.4) + (0.7B6 x0.00)] =6.5pct CaO If 0.214 and0.786 were proportions by weight, the equation would represent the well known mixtures law of the conventional arithmetics and 6. 5 pct CaO would be the correct average content. But it is not the case as the author states: "In samples consisting of single grains of mineral, those grains must, as already mentioned, be either of dolomite or magnesite. Since 78.6 pct of the deposit consists of magnesite and 21.4 pct of dolomite (excluding for present purpose the presence of other minerals), for any single grains picked at random the probability will be 0.214 that is it dolomite and0.786 that is it magnesite. In 1000 such samples the expected numbers of dolomite and mapesite grains will be 214 and 786 respectively." 0.214 and 0.786 would be proportions by weigbt under the necessary condition that all grains of dole mite and magnesite should have an identical weight. Obviously it is not the case, as the specific gravities are not the same for mapesite and dolomite and the volumes of the grains are different. Furthermore, because of these differences the conditions for a random sampling are not fulfilled and we are not authorized to state that the probabilities are, respectively, 0.214 and 0.786. The author however makes a simple application of Eq. 1: M = 1/n— ? fi x i . n Should we deduce that this relation is wrohg? Not at all, but when applying Eq. 1 you must not overlook what it actually. means. Eq. 1 gives a definition of the arithmetic mean of a total of n observed values Xi and nothing else. But the average conteht of a deposit has not the same significance. It is the ratio between the weight of concerned mineral in the deposit and the total weight of the deposit. As from 1000 particles the 214 of dolomite and the 786 of magnesite have not the same weight, the two definitions do not concur, and when applying Eq. 1 the result is an arithmetic mean of figures which has no connection with what is named average contentof a deposit. The situation is similar to the calculation of an average velocity. If a car travels a first mile over at 30 miles per hr and a second mile over at 60 miles per hr, when applying formula 1 you find as average velocity for the 2 miles: 30+60 ------- - 45 miles per hour. Many people calculate in this way and they do not realize that a mistake is involved. In fact the definition of he average velocity for the 2 miles is the quotient of the distance of 2 miles by the time (in hours) necessary for 2 miles travel, i.e.: 2 ---------- = 40 miles per hr. 1 + 1 30 60 In other words, the average volocity wanted is not the arithmetic but the harmonic average of the two velocities. The above mentioned bias in the calculation of the average contents of deposits is frequent, even in the assessments made by experienced engineers and is independant of what is named the sampling error. In order to supress the bias and to be able to use Eq. 1, you must apply a correction. An example on the subject can be found in an article by Duval et al. in the January 1955 issue of the &apos;&apos;Annales des Mines" (French), page 19. R. F. Schurtz (Author&apos;s Reply) Mr. Duval&apos;s position is quite correct. The proportions shown for dolomite and magnesite., respectively, of 0.214 and 0.786 are, in fact, proportions by weight uncorrected for specific gravity. In our day to day operation of producing magnesite from these mines at a very substantial rate, we do not normally make corrections for the difference between the specific gravity of dolomite and that of magnesite. If these corrections are made in Eq. 3 as shown in my article, then the numbers of grains turn out to be in proportions of 0.226 dolomite and 0.774 mapesite instead of the values actually shown in the equation. For the purposes of our work, and in view of the inherently low accuracy of the data, this correction was not deemed worthwhile making.

Jan 1, 1961

By A. U. Seybolt

The solubility limit of oxygen in columbium has been determined in the range between 775&apos; and 1100°C by means of lattice parameter measurements and microscopic examination. The solubility is a function of temperature and varies, in the range given above, from 0.25 to 1.0 pct O, respectively. BECAUSE of the marked deleterious effect of oxygen upon the mechanical properties of some of the transition metals, it is desirable to know something about the solubility of oxygen in these metals. The brittleness caused by oxygen in solution is particularly marked in the case of the group VA elements, vanadium, columbium, and tantalum. The solubility of oxygen in vanadium has already been reported in an earlier paper,&apos; and Wasilewski2 has given a value (0.9 wt pct) for the solid solubility of oxygen in tantalum at 1050°C. Brauer3 in 1941 investigated the Cb-0 system up to Cb2O5, but made no real effort to investigate the extent of oxygen solubility in the metal. He made the observation, however, that this solubility must be less than 4.76 atom pct (0.86 wt pct) oxygen. This estimate was made from X-ray diffraction results on the alloys CbO, CbO, and CbO; all alloys consisted of the terminal (Cb) solid solution plus CbO, but the last alloy containing 4.76 atom pct 0 showed only three very weak CbO lines. It is surprising that Brauer, by examining only three alloys, arrived at an estimate of the solubility which agrees very well with the results to be reported herein. Experimental Procedure A columbium strip obtained from Fansteel Metallurgical Products was cut into strips, 0.020x1/2x2 in. Two holes, about 3/16 in. in diameter, were made near the ends of the strips in order to hold them against a flat steel block for mounting in a General Electric X-ray spectrometer for lattice parameter measurements. The same holes were used to hang the specimens inside a fused silica vacuum furnace tube which was part of a Sieverts&apos; gas absorption apparatus. The apparatus and method of adding oxygen gas has been previously described.1 According to the supplier, the columbium obtained had the analysis given in Table I. After degreasing the samples, approximately 0.001 in. was etched from each side of the samples in order to remove possible surface impurities from the last rolling operation. For this purpose the following cold acid pickle was found satisfactory: 8 parts HNO3, 2 parts H2O2 and 1 part HF. Various Cb-O compositions were obtained up to 0.75 wt pct O by the gas absorption and diffusion technique. After the sample had absorbed all the oxygen gas added at 1000°C, an additional 24 hr was allowed for homogenization. This treatment appeared to be adequate, as shown by the linearity of the lattice parameter-composition plot. More concentrated alloys were prepared by arc melting mixtures of Cb and Cb2O5 since it was very time-consuming to make Cb-0 alloys in the neighborhood of 1 pct O, or over, by the diffusion method. When the flat strip specimens were used, they were ready for the X-ray spectrometer after cooling from the Sieverts&apos; apparatus. The cooling rate obtained by merely allowing the hot fused silica furnace tube to radiate to the atmosphere (when the furnace was lowered) was sufficiently fast to keep the dissolved oxygen in solution. Arc-melted alloys were reduced to —200 mesh powder in a diamond mortar, wrapped in tantalum foil, sealed off in evacuated fused silica tubes, and then heat treated as indicated in Table 11. The fused silica tubes were quickly immersed in cold water without breaking the tubes after the heat treatments. The tantalum foil prevented reaction between the fused silica and the sample; there was no reaction between the powdered samples and the foil at 1000°C, but some trouble was experienced at 1100°C. At this temperature level a reaction between the sample and the foil was sometimes observed, which resulted in erroneous parameter values. Experimental Results Hardness Tests: Since most of the X-ray samples were in the form of flat strip, it was convenient to obtain Vickers hardness numbers as a function of oxygen content. Compared to the V-O case,&apos; oxygen hardens columbium much more slowly, presumably because of the larger octahedral volume in colum-bium (about 12.0 compared to 9.3Å3 in vanadium), hence, requiring less lattice strain for solution. The plot of VHN vs wt pct O is shown in Fig. 1.

Jan 1, 1955

By Luc Delaey, Horace Pops

The structure and morphology of thermoelastic and burst type martensitic phases that form upon cooling in Cu-Zn-Si p phase alloys have been studied by transmission electron microscopy. The martensitic phases are composed of a lamellar mixture of two close-packed structures with different stacking sequence, namely ABCBCACAB (orthorhombic) and ABC (fcc). Striations within thermoelastic martensite are most likely produced during interaction with impinging burst-type martensite and not as a consequence of secondary shears. In a study of the martensitic transformation in ternary Cu-Zn based 0 phase alloys1 the dependence of the martensitic transformation temperature, M,, with composition shows variations for elements within a constant valence subgroup and between different subgroups. Such variations are not reflected in a change in habit plane, which is approximately the same for each ternary alloy, namely in the vicinity of (2, 11, 12 Ip. The fact that the habit plane remained constant, despite large differences in M, temperature and electron concentration, suggested2 that the crystal structures of the martensitic phases could be nearly the same. Crystal structures of ternary Cu-Zn based martensites have been determined recently for alloys containing the three-valent elements gallium3, 4 and aluminm. The present studies have been made to examine the structures and morphology of the martensitic phase in ternary Cu-Zn based alloys containing a four-valent element, silicon. I) PROCEDURE Two alloys were prepared by melting and casting weighed quantities of the component high-purity metals in sealed quartz tubes under half an atmosphere of argon. They were subsequently remelted by levitation under a protective atmosphere of argon. After allowing for losses of zinc as determined by the difference in weight before and after casting, the compositions in atomic percent of both alloys were established to be Cu-33.5 Zn-1.8 Si and Cu-27 Zn-5.0 Si. These alloys were homogenized in the P-phase field for 2 days at 800" C. Bulk samples consisted of a martensite phase at room temperature, the M, temperature being approximately 30&apos; and 200" for the 1.8 and the 5 pct Si alloys, respectively. Thin disks were cut from the ingots using a spark machine, and they were heated for 5 min at 800&apos; and quenched into water in order to obtain martensite. These slices were thinned chemically at room temperature in a solution consisting of 40 parts HN03, 50 part H3PO4, and 10 parts HC1 and thinned further electrolytically by the Window technique, using a voltage of 15 to 25 v and a mixture of 1 part HN03 and 2 parts methanol, which was kept at a temperature near -30° c. Foils were examined by transmission electron microscopy using a Philips EM 200 electron microscope. 11) RESULTS AND DISCUSSION 1) Structure and Morphology. Fig. 1 shows the martensitic phase in the alloy containing 1.8 at. pct Si. This phase is composed of contiguous platelets, each containing striations. The direction of the striations changes at the boundary between individual platelets. These internal markings resemble the striations that are usually identified as stacking faults, as for example in Cu-A1 martensites6-a or the lamellar mixture of two close-packed phases in Cu-Zn-Ga marten-sites.3p &apos;9 lo In the present alloys, selected-area diffraction experiments have been obtained in order to determine the nature of the striations. Figs. 2(a), (61, and (c) are electron diffraction patterns of an area inside a single martensite plate. Fig. 2(a) contains diffraction spots which correspond to two close-packed structures with different stacking sequences, namely ABCBCACAB (orthorhombic) and ABC (fcc). Spots belonging only to the fcc structure are indicated by arrows. By tilting the foil either the orthorhombic structure, Fig. 2(b), or the cubic structure shown in Fig. 2(c) may be obtained. When the foil is oriented so that only the diffraction spots of the orthorhornbic structure are present, bright-field illumination shows small lamellae, as seen in Fig. 3. In this figure the lamellae that belong to the fcc structure are bright bands inside the dark extinction contours of the orthorhombic structure. The boundaries of the lamellae are parallel to the basal planes of the orthorhombic structure and to the {Ill} planes of the cubic structure, the close-packed directions of both structures being parallel. The 5 pct Si alloy shows similar features as those described for the 1.8 at. pct Si alloy.

Jan 1, 1969

By M. A. Hosmer, Job Goostray, R. F. Harringon

In this paper, as in so many discussions of an historical nature, there is little chance for original material and much has had to be rewritten from older papers, documents, accounts, reports, and the like, some of which are of doubtful authorship or contain conflicting statistics. Fully aware of these pitfalls, the authors have tried to quote the origin where possible, and also to seek further confirmation when the statement warranted it, but they cannot assume responsibility for certain facts and dates. The Encyclopedia Britannica was frequently consulted. The authors wish to acknowledge assistance from Mackintosh-Hemp-hill Co. (formerly the Fort Pitt Works) and also from officials of the Watertown Arsenal who loaned valuable books and gave much necessary information. They are particularly indebted to Colonel Dickson of that institution. The data on modern guns were furnished by Mr. F. Brauer of the Watertown Arsenal; Mr. H. S. Chaffee assisted by obtaining records and data of work carried on by the Builders&apos; Iron Foundry of Providence, R. I. Three Epochs in History of Cannon Among the great industries of New England, the manufacture of iron was the first to receive attention. Iron ore in considerable quantities was known to exist within the territory of the Massachusetts Bay Colony; and as early as 1629 some steps appear to have been taken toward the manufacture of iron by the Court of Assistants in London, under whose patronage the colony was founded. During the next ten years, deposits of bog ore were found in numerous ponds in the Plymouth Colony; and, in 1652, iron manufacture was begun at Raynham. The "Old Colony" was known as the main seat of this industry in New England, out of which grew a concern which was later to become one of the principal

Jan 1, 1925

By J. R. Stack, H. H. Alexander

Prior to 1915, numerous attempts were made to treat tin concentrates in the United States, but for various reasons they were unsuccessful. Tin ore is said to have been found in nearly every state, but none of the deposits has proved to be of commercial importance. An annual output of a few hundred tons in Alaska is the only domestic production; hence any considerable production of tin in the United States must be from foreign ores. The most promising occurrence of tin was found in the Black Hills, S. Dak.; in the early development stage, it was called the Cornwall of America. Associated with the tin is tungsten The story is told that an exceedingly fine specimen of the Black Hills ore was sent to England to encourage stock promotion; the desired effect was produced until a skeptic chipped off a small piece, which the analysis showed to be wolframite. First Attempts at Smelting One of the first promising attempts at tin smelting in the United States was made by R. T. White at Bayonne, N. J., in 1903. Mr. White, after spending some time in England studying the methods of tin smelting, organized a company called the International Tin Co., and erected a plant to treat tin concentrates from the Straits of Malacca. About the time the plant was completed, the English Government placed an export duty of 40 per cent. ad valorem on tin concentrates exported to other than British smelters, which duty made it impossible to operate this plant so the enterprise was abandoned, As this export duty is still effective, the only source of tin-ore supply for the United States is the Bolivian concentrates. Bolivian Tin Concentrates Unlike the alluvial placer deposits, nearly all Bolivian tin occurs in lode deposits and some of the highest grade ores contain only a small

Jan 1, 1924

By T. L. Joseph

LARGE deposits of manganiferous iron ores, representing several million tons of metallic manganese, occur in the United States. The Minnesota deposits of such ore-are of outstanding importance because of their size, state of development, ease of mining and proximity to the Great Lakes, which permits water transportation to steel centers. In&apos; view of the fact that our steel industry requires large quantities of manganese, for which no satisfactory substitute-has been found, and because our reserves of ferro-grade ore are comparatively small, the development of methods that will make our large deposits of manganiferous iron ores available as a source of ferromanganese is an important problem. Realizing the importance of this problem, some years ago the North Central Station of the U. S. Bureau of Mines and the Minnesota School of Mines Experiment Station undertook jointly the development of methods for recovering the manganese content of manganiferous iron ores in a: form suitable for the production of ferromanganese, the 80 per cent. alloy indispensable in producing steel. Two types of manganiferous iron ores have been described in previous reports. I The brown ores are higher in iron and lower in manganese than the black ores; the black ores are more siliceous but contain less phosphorus. The utilization of the iron content of the brown ores in the production of steel appears to furnish the best basis for their treat-ment. The method of attack has been to work out modifications in iron and steel practice so as to recover manganese in the form of slag comparable to ferro-grade ores. The greater part of the experimental work has been conducted with a 6-ton blast furnace and a Y2-ton basic open hearth. This paper is devoted mainly to open-hearth tests in which high-phosphorus spiegel

Jan 1, 1930

By H. P. Greenwald, H. C. Howarth

The rapidly increasing use in coal mines of portable auxiliary fans, which are generally &apos;blowers" employed in connection with canvas tubing, raises questions concerning the hazards of such equipment, especially where the practices are opposed to established methods of ventilating face workings. Half a dozen or more coal-mine explosions and some fires have been attributed to the use of auxiliary fans; moreover, competent mining engineers have found many dangerous installations and methods of use-for example, intermittent running of the fans in gassy mines with consequent accumulations of firedamp at the faces. These facts have led the U. S. Bureau of Mines to issue this recommendation: "In the interest of safety, the Bureau of Mines, Department of Commerce, recommends that auxiliary fans or blowers should not be used in coal mines as a substitute for methods of regular and continuous coursing of the air to every face in the mine." The comparatively recent introduction of new types of mining machines, mechanical loaders, face conveyors, and slabbing machines has encouraged the trial of new systems of face mining, all of which have for their object the rapid advance of the faces. Although the latter has certain economic advantages, in gassy mines the rate at which gas is given off is generally found to increase in proportion to the speed of advance into new territory, which in turn increases the difficulties of efficient ventilation of the face workings. Some of the systems of advance mining being tried in connection with new mechanizing methods practically compel the use of blower fans and tubing, as single narrow places arc now driven 300 ft. or more without crosscuts. In some instances a series of parallel headings are driven without crosscuts pre-

Jan 1, 1928

By G. M. Kirwan, Joseph B. Perry

MagnEsitE is found in 22 California counties, but many of the deposits are too small or too impure to be of commercial value. Several of substantial size and quality were entirely exhausted by wartime operation. At present, three properties comprise the only known workable deposits in the state. Of these, the Western mine and the Patterson mine have been known and worked for many years, and have been described in considerable detail in various publications, therefore need only brief mention here, because of their proximity to the Bald Eagle mine. The latter, recently developed, is unusual in type of ore deposit, plant design and operation, as well as products made, and very little has been written concerning it. WESTERN MINE The Western mine, 32 miles south of Livermore, Calif., was formerly operated by C. S. Maltby. It has been a consistent producer for many years.l The ore is of amorphous variety, occurring along fracture zones in serpentine. The veins vary greatly in width, the average being perhaps 8 ft., with the maximum indicated in one early stope of 40 ft.; 2 ft. is considered the minimum for economical mining. The strike of the veins is predominantly north and south, with dip to the west varying from 40" to 75". Walls are well defined and as a rule firm and easily supported. Veins range in length from a few hundred feet to 1000 or more. Their maximum vertical extent is about 350 ft., but many run less. Early mining consisted of open-cut and glory-hole work on the larger outcrops. This was followed underground by a modified shrinkage system, the waste and low-grade horses being removed by hand sorting on the tramming levels and transported to surface dumps. Filled-stope mining is used now, in order to eliminate the handling of waste, which has

Jan 1, 1942

By Joseph B. Perry, G. M. Kirwan

MagnEsitE is found in 22 California counties, but many of the deposits are too small or too impure to be of commercial value. Several of substantial size and quality were entirely exhausted by wartime operation. At present, three properties comprise the only known workable deposits in the state. Of these, the Western mine and the Patterson mine have been known and worked for many years, and have been described in considerable detail in various publications, therefore need only brief mention here, because of their proximity to the Bald Eagle mine. The latter, recently developed, is unusual in type of ore deposit, plant design and operation, as well as products made, and very little has been written concerning it. WESTERN MINE The Western mine, 32 miles south of Livermore, Calif., was formerly operated by C. S. Maltby. It has been a consistent producer for many years.l The ore is of amorphous variety, occurring along fracture zones in serpentine. The veins vary greatly in width, the average being perhaps 8 ft., with the maximum indicated in one early stope of 40 ft.; 2 ft. is considered the minimum for economical mining. The strike of the veins is predominantly north and south, with dip to the west varying from 40" to 75". Walls are well defined and as a rule firm and easily supported. Veins range in length from a few hundred feet to 1000 or more. Their maximum vertical extent is about 350 ft., but many run less. Early mining consisted of open-cut and glory-hole work on the larger outcrops. This was followed underground by a modified shrinkage system, the waste and low-grade horses being removed by hand sorting on the tramming levels and transported to surface dumps. Filled-stope mining is used now, in order to eliminate the handling of waste, which has

Jan 1, 1942