By M. J. Hordon

Measurements of the 103 yield stress of ordered and disordered poly crystalline Cu ,Au were related to the ordered antiphase domain size determined by resistivity measurements. For undeformed material, a yield stress maximum wa obtained at a critical domain diameter of about 40A. Plastic deformation resulted in a marked increase in the yield stress and electrical resistivity of the ordered alloy compared to the disordered, the strain hardening rate increasing regularly with initial antiphase domain size. Order hardening was accompanied by a sharp reduction in size of the initially large domains. It has been observed that the yield stress of ordered and partially ordered Cu3Au alloy varies sensitively with antiphase domain size aid degree of order.ly2 In addition, ordering of the lattice leads to a marked increase in the strain hardening rate (order hardening) as compared to the rate for the disordered alloy. In the present investigation, changes in the electrical resistivity and yield stress of ordered polycrystalline Cudu with varying initial domain diameters were measured after tensile plastic deformation in order to examine the effect of cold work on the antiphase domain size. EXPERIMENTAL PROCEDURE Au-Cu alloy of 99.99 pct purity analyzing 50.85 wt pct Au-balance copper was obtained from the Handy-Harmon Co., N. Y., in the form of 0.061 in. diam drawn wire. Wire specimens 3 in. in length were given the following annealing treatment in nitrogen: 500" for 72 hr, 820" for 15 hr, and 450" for 5 hr, followed by a water quench. The annealing sequence resulted in a completely disordered structure with a grain size of about 0.2 mm. The disordered specimens were then reannealed at 360' in nitrogen for periods varying from 10 min to 150 hr followed by quenching to produce ordered structures with varying domain sizes. The degree of ordering and variation of domain size was followed by electrical resistivity measurements made at room temperature using a low resistance precision Kelvin double bridge apparatus. The specimen resistance was determined over a length of 4.0 cm between two brass knife-edge contacts while the specimen was immersed in an oil bath to minimize temperature variations. In addition, the current flow in the circuit was minimized by a current pulse technique in balancing the bridge in order to avoid heating the specimen. Using a sensitive galvanometer to detect the bridge null, the accuracy of the resistance measurement Wire specimens were plastically strained in tension with an Instron tensile unit at strain rates in the range 5 x 10"5 sec-' to 2 x 10"4 sec-'. Stress and extension data were fed into the Instron chart drive amplifier to obtain the actual stress-elongation curve from which the yield stress at 10"3 strain was determined. The maximum resolution of the apparatus was approximately 50 psi stress and 3 x 104 strain. At various plastic strain levels, deformation was interrupted and the electrical resistivity determined after removing the stress. RESULTS AND DISCUSSION 1) Yield Strength of Ordered Cudu. In order to determine the effect of the ordered antiphase domains on the initial yield stress, specimens were prepared with varying domain sizes ranging from zero for 5 completely disordered structure to about lo5A for a completely ordered structure by suitable annealing treatment. Domain sizes were estimated by comparing room temperature electrical resistivity data with the original data of Jones and sykes3 as modified by rdle.' In agreement with previous work, the resistivity varied sensitively with domain diameter and degree of order, decreasing from approximately 11.6 x l0- ohm-cm for the disordered structure to about 5.9 x l0- ohm-cm for ordered domains above 10"3 cm in diameter. Fig. 1 shows the change of the 103 yield stress with ordered domain size. It is evident that the maximum

Jan 1, 1963

By G. T. Smith, R. C. Moyer

Cadmium, along with other impurities such as lead, gallium, germanium and indium, is characteristically found associated with zinc ores, the average ratio of zinc to cadmium being about 200 to 1. The increasing demand for cadmium has led most zinc producers to develop a means for its recovery. The separation and recovery of this byproduct constitutes an important development in the metallurgical field. Zinc sulphide concentrates, principally from domestic sources, are processed at Donora Zinc Works and they assay approximately 60 pct zinc, 30 pct sulphur, 0.37 pct cadmium, and 0.8 pct lead. Concentrates are roasted to convert zinc sulphide to zinc oxide. Sulphur evolved as sulphur dioxide is used to manufacture 60º Baume sulphuric acid by the lead chamber process. The roasted calcine is sintered to remove the remaining sulphur and volatile impurities. Fume from the sintering machines is collected by Cottrell pre-cipitators and sent to the Cadmium Department for cadmium removal. The sintered product, a crude zinc oxide, is then mixed with coke and salt and charged into horizontal retorts for reduction to zinc metal. Furnace residues are then passed through a Waelz kiln which recovers practically all of the remaining zinc as an oxide. This oxide is collected by Cottrell precipi-tators and returned to the sintering plant for further processing. The following discussion covers operating procedure, and equipment used in the Cadmium Department for the manufacture of cadmium and its byproducts. (See attached Flow Sheet, Fig 1.) The production of cadmium may be divided into several steps, each of which will be discussed separately. These steps are as follows: 1. Raw Materials—Sinter Plant Cottrell dust, acid sludge and sulphuric acid. 2. Sulphating—Separation of lead. 3. Purification—Separation of impurities other than zinc. 4. Precipitation—Separation of cadmium from zinc. 5. Briquetting—Preparation of sponge for charging to furnace. 6. Smelting—Distillation of cadmium metal. 7. Remelting—Casting into commercial shapes. 8. Recovery of Rare Metals—Separation of germanium, gallium and indium. Raw Materials The raw material, or Sinter Plant Cottrell dust, from which the cadmium is manufactured, is recovered by Cottrell units collecting fume from two Dwight-Lloyd sintering machines. An average analysis of this dust is 36 pct zinc, 1.5 pct sulphur, 17 pct lead, and 5.5 pct cadmium, with associated elements in smaller amounts. A lesser tonnage of material removed from the sintering machine fans, and called fan cleanings, is also treated for cadmium. It is lower grade material and analyzes approximately 41 pct zinc, 1.2 pct sulphur, 14 pct lead, and 4 pct cadmium. Cottrell dust and fan cleanings are delivered to the Cadmium Department by monorail crane in bell-bottomed dump buckets. Acid sludge and 60" Bauine sulphuric acid are received from the Acid Department. The acid sludge is a mixture of lead sulphate, sulphuric acid and zinc sulphate, and is recovered mainly from the floors of the acid chambers or storage tanks. The acid sludge is delivered to the Cadmium Plant in a lead lined bucket. The 60º Baume sulphuric acid is delivered through a lead pipe to a lead lined storage tank. Sulphating Four well ventilated lead lined sulphating tanks, 8 1/2 ft in diam by 12 ft deep, are used. These are steel tanks lined with 20 lb lead on the bottom and 16 lb lead on the ides, equipped with Hastelloy side agitators. 15 hp motors drive 24 in. propellers at 450 rpm. There are water connections to stuffing boxes to keep sludge from entering the bearings. The tanks are covered with removable wooden lids and are connected to marine plywood

Jan 1, 1950

By J. Chipman, J. B. Gero, T. B. Winkler

D. C. Hilty—This paper is a useful and timely addition to our store of quantitative data relating to manganese distribution between slag and metal in steel-making processes. For some time, many of us have suspected that the values of Kmn derived by Körber and Oelsen might be too low, and this paper now appears to confirm that suspicion. Application of the new constant to openhearth data should prove interesting. The manganese deoxidation curves of fig. 4 agree fairly well with direct measurements of isothermal solubilities of oxygen in liquid iron containing manganese that have recently been made at the Union Carbide and Carbon Research Labs., Inc. According to the solubility data just mentioned, however, the curves for 1550" and 1600°C lie much closer to each other than the authors have indicated. In other words, the solubility measurements suggest that the logarithm of the oxygen solubility is not a linear function of the reciprocal of the absolute temperature, as the authors have assumed for their calculations. It seems possible that this discrepancy may be due in part to the authors' use of the distribution coefficient, L,,, obtained from Taylor and Chipman's curve for the solubility of oxygen in iron as shown in fig. 2. Taylor and Chipman gave the equation of this curve as —6320 Log % 0 - ---T + 2.734 Their data, however, can be fitted equally well by a curve having the equation: 13.23 x104 1.18x10" Log % O = 36.350 -13.23x10 Moreover, this curve also fits the authors' oxygen distribution data somewhat better than does the linear curve of Taylor and Chipman. Its use in the derivation of Lo for calculation of the deoxidation curves by the authors' eq 15 causes the effect of temperature on the calculated curves of fig. 4 to agree quite well with the temperature effect that has been observed. An experimental determination of the temperature coefficient of the manganese reaction appears to be desirable. J. E. Stukel—Because the authors have done such an excellent job, my comments will be confined to additional information. Very shortly Professor T. L. Joseph and I will publish the results of a study of the reaction between molten manganese and silica. It was found that electrolytic manganese, melted in silica crucibles, reacted with the silica to form a silico-manganese alloy containing 18 pct silicon (1500°C) and a silica saturated MnO-SiO, slag. Therefore, the presence of silicon and its oxides in the Fe-Mn-0 system will affect the equilibrium. Carbon is also an important factor. The higher the carbon content of the iron the less ability manganese has to reduce silica. As a matter of interest, recently a study of the manganese equilibrium in carbon saturated iron and blast furnace slags was completed at Carnegie Institute of Technology. As a comparison to the present study, 2 to 5 hr were required to reach equilibrium and temperature was a much more important factor than slag composition in determining the (Mn)/(MnO) ratio. These results will also be published in the near future. It can be seen, therefore, that the results of this paper cannot be applied directly to openhearth studies without a degree of flexibility. J. Chipman (authors' reply)—With regard to the effect of silicon on the manganese constant, this effect is, of course, known. Much more data is needed in order to establish it accurately, and I hope we can look forward to having some accurate data on that. Mr. Hilty suggests that a three-term expression for the Taylor-Chipman solubility of oxygen in liquid iron might fit a little better than the two-term equation. I think that it would be too great a compliment to the precision of the data to employ a three-term equation, and I would still recommend the simple, two-term expression.

Jan 1, 1951

By J. P. G. Farr, R. Brownsword

THE role of solute segregation in the formation of cellular solidification substructures in tin and its dilute alloys is well-established, see, e.g., Ref. 1. Segregation has been shown to persist during cooling, enabling solidification structures to be studied from sections taken at some distance behind the interface. In the present work, a single crystal of commercial nickel, 99.965 pct, was examined in this way. The crystal was cut from the center of a rod given a single pass in an electron beam floating zone melter. Polished sections of a nickel specimen taken normal to the growth direction showed a very fine precipitate phase, the distribution of which varied over the section. The identification of the phase proved difficult because of the small amount present and the small particle size, about 1 p: but it was shown by probe microanalysis to contain only nickel and oxygen in detectable concentrations and was probably nickel oxide, NiO. Bulk analysis of the material before melting showed there to be only 3 to 4 ppm of oxygen present, thus demonstrating a very considerable segregation concentration effect. In some areas of the section the precipitate formed a discontinuous hexagonal network suggesting decoration of the cellular boundaries known to be present in the sample2 whereas in a restricted region the precipitate formed small clusters. Occasionally it could be seen that the clusters were at the intersections of an hexagonal network of cellular dimension. It was suggested3 that this was the result of enhanced segregation to the cell boundary intersections whereas general cell boundary segregation was insufficient to give a precipitate. Enhanced nodal segregation has since been demonstrated in a number of systems.1, 4-8 The development of a suitable electrolytic etching technique (perchloric acid 20 pct v/v; ethyl alcohol 70 pct; glycerol 10 pct; current below electropolishing plateau; 1 to 2 sec etching) suggested the association of the phase with regions of solute segregation (where ko < 1); in these regions anodic attack produced grooves or depressions. In a study of the variation of solidification substructures with degree of constitutional supercooling, Biloni et a1.&apos; appear to have used standard growth conditions and varied the solute concentration. They were able to produce in a series of individual tin crystals examples of substructure ranging from planar interface through various cellular structures to den- Fig. 1—Electroetched section taken normal to the rod axis; the center of the rod lies to the left and the periphery to the right of the micrograph. The variation of structure across the section is evident. Magnification 60 times. drites. It was possible in the present nickel crystal to observe a continuous range of substructures varying with degree of supercooling across a single section as shown in Fig. 1. Growth rate, 13 mm per min, and temperature gradient were essentially constant; the variation in structure is thought to be due to a radial gradient in solute concentration ahead of the solid interface. The liquid at the interface is likely to have been richer in solute toward the periphery of the zone, the result of curvature of this interface. The type of substructure was seen to vary with increasing constitutional supercooling as follows: a) region free of precipitate. top left, Fig. 1: 6) region of nodal precipitates which became arranged in hexagons on passing from the center of the rod: c) irregular hexagonal cells with incomplete boundary precipitation; d) regular hexagonal cells of decreasing size with complete boundary precipitation. Fig. 2 shows the transition from stage 6 and Fig. 3 shows the structure in stage d. Within stage 0, the range of conditions over which irregularly positioned nodes occur appears to be small and the nodes are soon recognizable as taking up positions at the intersections of an hexagonal network as the supercooling increases.

Jan 1, 1970

By Gordon W. Hodgson, Edward Tipman

INT&apos;RODUCTION An appreciable number of the oil fields in Western Canada are accumulations of heavy black oils in more or less unconsolidated sandstones. When the crude oils are produced by conventional means, they are frequently contaminated with both sand and oilfield water. The water is usually present as emulsified water, and the sand and other solid materials are suspended in the emulsions. The presence of the solid material in the crude oils is troublesome and, in general, little is known about the behavior of suspended solid particles in emulsions. The Stokes equation describes the behavior of suspended particles in homogeneous fluids in terms of particle size, density differential, and fluid viscosity. In the case of an emulsion, particle size and density differential introduce no difficulties, but considerable doubt centers around the viscosity term. It has been reported1 that the viscosity of an emulsion is related to the viscosity of the continuous phase by an expression of the type: n = a, (1 + a C) where n is the viscosity of the emulsion, n,, is the viscosity of the continuous phase, a is a constant, C&apos; is the volume concentration of the disperse phase. The value of 17, the coefficient of the concentration term, has been determined for various systems, and has been found to vary from a value of 1 to 4.75. The value of 2.5 has been found to be applicable to a large number of systems, and this is the value that is widely used in the equation which then becomes the Einstein equation for the viscosity of emuls~ons. It is of considerable significance that neither the particle size nor the viscosity of the disperse phase enters the expression; the expression for the viscosity of the enlulsion is based solely upon the viscosity of the continuous phase and the concentration of the disperse phase. For crude oil emulsions the Simha equation and the data presented by Fukushima and lchimurai show a non-linear dependence of the viscosity ratio on the water concentration. While it is undoubtedly reasonable to use these data for predicting the viscosity of a specific emulsion, and while it is equally reasonable to expect the calculated viscosity to predict the settling rate of a solid spherical particle in the emulsion by means of Stokes equation, there seems to be no direct evidence that this calculation is indeed sound for describing the settling rates of solid particles in emulsions of water in crude oils. PROCEDURE A direct approach to the problem was thus indicated. Laboratory equipment was designed and built for the direct determination of the rate-of-fall characteristics of solid particles in emulsions of water in oil. Although the apparatus incorporated the basic design of conventional falling-ball viscometers, the study was concerned directly with the rate-of-fall characteristics of particles in emulsions, rather than with the viscosity of the emulsions as such. The crude oil used in this study was a very heavy black crude oil—the McMurray oil obtained from oil-soaked sands outcropping on the Athabasca River in northeastern Alberta. It was produced from the sands by strip mining followed by hot-water separation of the oil in the separation plant of the Alberta Government at Bitumount&apos;. The primary plant product was a wet crude oil containing about 5 per cent solids and 35 per cent water. The final plant product was only slightly different from the native oil, having lost only about 4 per cent of its bulk as light ends during dehydration distillations. In the present investigation two kerosene dilutions of the McMurray oil were used in addition to the dry plant product. The McMurray oil contained 1.92 per cent solids. Analysis of the solids by X-ray diffraction showed the presence of kaolinite, pyrite, and illite as major constituents. with lesser amounts of quartz. Particle size of the pyrite and quartz was less than 10

Jan 1, 1957

By R. L. Segall

AN unusual thermal etch figure in copper is described and an explanation in terms of twinning is suggested. A flat polycrystalline specimen of OFHC copper cut from a rolled sheet was electro-polished in orthophosphoric acid and annealed at 950°C in a vacuum of approximately 10-3 mm Hg for 2 hr. The specimen was found to be thermally etched, the markings on the surface being consistent with the assumption that they were the traces of the (111) planes which are developed preferentially because they have the lowest free energy. However, on one grain (the grain shown in Fig. 1) the traces formed an almost regular pentagon and at first sight it seemed unlikely that they could all be (111) traces. These traces were studied further because it was thought that they might be a type of growth spiral. A fringe pattern showed that this was not so, the grain being sensibly flat and the only features having steps were the striations and the faint curved line passing out from the center of the pentagons. To obtain some additional information, the specimen was deformed in tension. The effect of the stress was first to cause the appearance of lines running from the centers to the apexes of the pentagons and then to tilt the five segments so formed. At a much greater stress, appreciable slip appeared on the grain; these effects can be seen in Fig. 2. The micrograph was taken at a fairly late stage in the deformation and the tilting is quite marked. The magnification is the same as in Fig. 1, and although some slip can be seen it could be observed better by varying the illumination and using higher magnifications. In each segment of the grain, slip (which takes place on the (111) planes) was parallel to the side of the pentagon in that segment. The marked changes in direction of slip from segment to segment seemed to be incompatible with the presence of a regular array of subgrains. These results suggest that some of the five segments were twins. If this is so, since the twinning plane in copper is the (111) plane, the radial lines must be traces of the (111) planes on the surface. From the symmetry of the striations about the radial lines, these planes must be almost perpendicular to the surface. The angle between <III>directions in face-centered-cubic copper is 70&apos;32&apos;. If, in Fig. 3, OAB (triangle 1) is taken as matrix and OA, OB are (111) planes viewed edge on, then AB is in the correct direction to be the trace of either of the other two (111) planes on the surface. If triangle 2 is the twin (about the (111) plane perpendicular to the surface and containing OB) of triangle 1, then once again it can be shown that all lines are traces of (111) planes. Similarly, triangle 3 is the twin of triangle 2, 4 of 3, and 5 of both 4 and 1. (The sequence is, of course, quite arbitrary.) However, if this were the case there would be a discrepancy of 7&apos;20&apos; to be accounted for. It is suggested that the faint curved line passing outward from the center of the pentagon represents either a low angle boundary or a sixth small twin. The slight step shown by the fringes at this line might be an indication that the former is the case. This explanation does not account for the coincidence of obtaining a grain whose surface must be so close to (110) and obtaining the curious twinning described previously; it would be of interest to find a specific mechanism for this.

Jan 1, 1958

T.P. 1958 D. H. DAVIS.*-Mr. Carris has ably pre¬sented the problems of coal preparation, particularly those brought about as the result of increased mechanical loading. Many mines are now crushing the run-of¬-mine raw coal through 12 or 15 in. immediately after it is dumped from the mine car and before it is handled by conveyors. At certain mines the removal of large slate mechanically has been solved by the installation of scalping screens consisting of bars or rails set at spacing of 12 to 15 in. on the top deck of the main raw-coal sizing screen. At the plants where these are in use, the plus 12 or I5-in. raw material contains 60 per cent or more free rock or slate, so that it is easier to pick coal than to pick rock. After the screening at 12 or 15 in. is accomplished, the oversize material is diverted to one side of the shaker, where a picker allows the refuse to pass off the shaker into a chute and guides the coal back onto the shaker. After the large rock has been removed, it is then advisable to reduce the size of rock by crushing before putting it onto a conveyor. A great saving in picking labor has been made by the use of such scalping screens, which in addition has maintained the plant capacity when handling a dirtier feed. The great increase in percentage of coal under 1/4 or 3/8 in., coupled with a greatly increased percentage of free impurities in this size, is the most serious problem that has been brought about by mechaniced loading. Many plants that formerly prepared good quality 1/4-in. to o or 3/8-in. to 0 slack by air¬cleaning are faced with installing facilities for wet-cleaning mechanical and heat-drying and water clarification. The change to wet prepa¬ration of fines usually affects the marketing problems for many coal companies. There will also be problems involving wastage of fine solids and stream pollution. Much work will be necessary for improvements in present practice. Pneumatic and electrostatic methods for cleaning fine coal should receive consider¬able attention in an attempt to avoid wet¬cleaning of fines. The preparation supervisor and the plant personnel should not be satisfied merely to run the cleaning-plant machinery and assume that the job will be done for them. Coal is a heterogeneous substance and in many instances is constantly changing. This is more true when full-seam methods are in use. Only persons trained to observe closely and make the necessary changes in plant operation will be able to solve the many problems that will be imposed on the preparation plants. The plants will require skillful and observant operating men. With full-seam mining methods, seams of roof coal will often be mined. Under the former mining systems these strata were not mined and frequently they contain a high per¬centage of bony and banded partings. The mining of this coal will greatly alter the washability and specific gravity characteristics of the feed to the plant. Often the percentage of 1.40 to 1.60 sp. gr. increased from 3.5 to 7.5 per cent, or nearly a 1.0 per cent increase in the ash content of the 1.60 sp. gr. float coal. Thus the cleaning problem is much more difficult, and it is unlikely the same ash content of cleaned coal can be produced as before without a decrease in recovery or the produc¬tion of a "middlings" product. Mr. Carris had this in mind when he said "The quality of the

Jan 1, 1946

By W Lindlief, Cyril Stanley Smith

Several investigators, mainly concerned with the mechanical properties of the alloys, have studied the so-called aluminum bronzes after various quenching and reheating treatments. Of these works, perhaps the most complete is that of Bouldoires, who studied changes of length, electrical conductivity, thermoelectric force, hardness and micro-structure on tempering quenched alloys containing 5 to 20 per cent of aluminum, although the work of Carpenter and Edwards,² Curry13 Greenwood,4 Braesco,5 Matsuda,67 Grard8 and others has added much to our knowledge of the changes occurring during tempering. The so-called acicular ß decomposes on tempering at temperatures between 350" C. and the eutectoid, giving rise to a Widmanstätten structure of a needles in a matrix of 6 or fine a + 6, associated with an increase in hardness and almost complete loss of ductility. Matsuda studied the eutectoid transformation by means of dilatation and electrical conductivity measurements during cooling at different rates. He found that on cooling at the rate of 10" C. per minute there was a decrease in electrical resistance and in length instead of the usual increase which occurred with slow rates of cooling. On tempering the rapidly cooled samples, the increase commenced at about 400" C. and at 520" C. the resistance and length had reached the equilibrium values. These peculiarities he accounted for as being due to a transitional phase ß&apos; being formed, ß&apos; having an electrical resistance and volume less than either ß or a + 6. Obinata9 published some electrical conductivity curves for copper-aluminum alloys showing a double break at the eutectoid temperature,

Jan 1, 1933

By F. F. Peng, A. D. Walters, M. R. Geer, J. W. Leonard

INTRODUCTION Washability characteristics derived from float-and-sink analysis in Chapter 4 demonstrate that coal is intrinsically heterogeneous, and this heterogeneity is also evident in the proximate, ultimate, and size analyses. A range of particles from high to low specific gravity is usually seen in the run-of-mine coal. One objective of coal preparation is to recover the high quality float material (the particles of lower specific gravity) such that the recovered product meets certain quality specifications, as well as to reject or recycle low quality particles of higher specific gravity. The maximum recovery of cleaned coal at the required quality is of major concern to plant operators. However, the quantity and quality of products of coal cleaning, determined in the operation of actual commercial cleaning plants and by theoretical calculation based on run-of-mine washability studies, are known to be different with each coal. Therefore, during the last half century, coal preparation engineers have repeatedly sought methods to predict the technical and economical efficiency of separation of cleaning equipment and systems. Many formulas have been proposed by international investigators to evaluate the efficiency of various coal cleaning operations, primarily based on the yield and/or ash of the various products of coal cleaning. Performance criteria in use today are capable of defining all of the important aspects of a given concentrating operation; however each criterion has certain restrictions or limitations. It is important, therefore, to understand how such formulas can be used and the problems involved in their construction. Technical Measure of Plant Performance Conventional means for evaluating a preparation plant&apos;s performance are generally approached through the use of equipment performance mea-

Jan 1, 1979

By W. F. Holbrook, C. E. Wood, E. P. Barrett

THE high-frequency laboratory induction furnace with a rotating liquid crucible enables research workers to conduct certain investigations heretofore very difficult or impossible to realize because vessels are not obtainable that are capable of resisting the physical conditions or the chemical actions to which they are subjected. Applications for patents covering commercial uses of centrifugal liquid crucibles were filed in the United States in 1919,1 in France in 1925, in the United States and Germany in 1926,2 and in France in 1927.3 In 1928, Schuette and Maier,4 of the Bureau of Mines, reported the construction of a whirling table beneath a high-frequency induction furnace. SHAPE AND SIZE OF CENTRIFUGAL LIQUID CRUCIBLES When a vessel containing a liquid is rotated, the inner surface of the liquid takes the shape of a paraboloid under the simultaneous action of centrifugal force and gravity. The internal dimensions of the paraboloid rotating liquid crucible are governed by the diameter of the container and .its speed of rotation. Melted Wood&apos;s metal was poured into cylinders 2 1/2 in. in diameter, which were rotated at 180, 300, and 468 r.p.m. When the metal was solid, a slurry of plaster of Paris was added, and rotation continued until the plaster had set. Fig. 1, a photograph of sections of the cylinders, shows the effect of speed of rotation of the containers upon the shape of the inner surface of the rotating liquid crucibles. TYPES OF FURNACES Three types of high-frequency induction laboratory furnaces using liquid-metal crucibles were designed and constructed by the Blast

Jan 1, 1938

By W. H. Bassett, J. C. Bradley

In considering the effects of reducing gases on hot solid copper the following conclusions have been reached. (I) Depth of deoxidation of copper heated in reducing gas is grealer the smaller the amount of cuprous oxide originally present in the copper, the range studied being from 0.015 to 0.136 per cent. oxygen. It is suggested that the reason for this diflerence in depth of deoxidation is thai, when the copper is low in cuprous oxide, the reducing gas is diluted less by the gas that is formed in the reaction than when the copper is high in cuprous oxide; and the greater the concentration of the reducing gas the deeper the deoxidation. (2) The rate of deoxidation is much more rapid at the beginning of exposure than at the end, a condition especially noticeable at temperatures around 900" C.; that is, deoxidaion is retarded as the depth penetrated by the reducing gas increases. (3) Within the accuracy of the experiments arsenic in copper up to 0.5 per cent. has no tendency to increase or decrease the action of a reducing gas on the cuprous oxide presenx in the copper. In 1912 pieces of 0.365-in. hard copper rod 1/2 in. long were heated in a porcelain tube in an electric furnace, while illuminating gas was passed through. An approximate analysis of this gas is: Hydrogen 38 per cent., carbon monoxide 30 per cent., illuminants 13 per cent., methane 10 per cent., ethane 3 per cent., carbon dioxide 3 per cent., nitrogen 2 per cent., oxygen 0.4 per cent. After heating for various lengths of time at various temperatures, samples were quenched

Jan 1, 1926

By N. P. Goss

ASTERISM appearing in X-ray Laue dia-grams is an extremely sensitive index of changes in the internal structures of indi-vidual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.1-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not con-clusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made be-tween mosaic and distorted grain struc-tures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example,7 has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-14 to 10-15 c.c., or 10-5 cm. in size.

Jan 1, 1940

By N. P. Goss

ASTERISM appearing in X-ray Laue dia-grams is an extremely sensitive index of changes in the internal structures of indi-vidual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.1-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not con-clusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made be-tween mosaic and distorted grain struc-tures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example,7 has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-14 to 10-15 c.c., or 10 5 cm. in size.

Jan 1, 1940

By Bror Nordberg

SAND and gravel are unconsolidated granular materials resulting from the natural disintegration of rocks. The two materials nearly al- ways occur together, variably proportioned in widely available de- posits. A commercial sand comprises the fine granular material, usually less than f in. in diameter (ASTM Designation C58-28), and gravel consists of the coarse, granular material larger than sand (ASTM Designation C125-46T). Gravel falls within the range of 1/4 in. and a top size usually of 3 ½ in. Chemical definition is impossible. Sand and gravel are always of secondary origin. They were formed from various massive rocks through the action of chemical and mechanical forces; then transported, abraded, washed, sorted, and classified by streams, glaciers, waves, or winds, to be redeposited in beds as they are found. Chief disintegrating forces in the reduction of rocks into granular particles were frost, rain, the dissolving action of acid and alkaline ground waters, the mechanical action of streams and waves, and the action of glaciers. Method of formation and deposition have imparted physical properties to sands and gravels that largely determine the commercial value of the materials for particular use and influence the manner of exploitation. In the early days of the commercial industry, purchasing specifications were relatively lenient but in. the past decade much more rigid quality requirements have had to be met for acceptance by all classes of purchasers. The trend to further severity in requirements is a challenge to the industry that commands full knowledge of the nature of raw materials at hand and skillful application of processing into commercial products. Mechanical strength, the ability to resist disintegration, chemica

Jan 1, 1949

By Richard F. Miller, W. E. Milligan

Work was undertaken two years ago at the Hammond Laboratory for the purpose of determining the magnitude of the elastic range in single crystals of pure metals by means of creep tests, the assumption being made that if a true elastic range exists, the elastic limit represents the maximum stress for no creep. A sensitive extensometer was constructed, and creep tests were made on zinc single crystals at a variety of loads and temperatures1. It was soon discovered that there is no measurable elastic limit in ductile zinc single crystals at, or above, room temperature. The inference that pure metallic single crystals may not possess a definite elastic range was not justified, however, since zinc had been tested in creep only above its recrystallization temperature, and several investigator2,3,4 had already shown that above the recrystallization temperature polycrystalline metals will flow under very small stresses, while below that temperature stresses of a much larger magnitude are required. For that reason, it was decided to extend the study of the elastic limit to other metals having a higher recrystallization temperature than zinc. Aluminum and silver were selected, because of the ease of obtaining pure materials and of preparing large single crystals, and because the crystallo-graphic glide system of these metals is well known. Owing to the limited time available, the elastic range was investigated by slow tensile tests rather than by creep tests. Production of Specimens A luminum Recrystallized single crystals were prepared from 99.95 per cent aluminum supplied by the Aluminum Company of America. The ingots were melted in an Acheson graphite crucible in a gas furnace, and cast

Jan 1, 1937

By C. H. Mathewson, H. M. Day

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By H. M. Day, C. H. Mathewson

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By A. F. Meston

Centrifugal force has been used for centuries for separating liquids but machines for doing this are a comparatively recent development. The use of these machines is being extended into many industries but this paper is confined to their use in the oil industry. The centrifugal machine is found at the well where "cut oil" is dehydrated for acceptance by pipe lines; and in the refinery and byproduct plant. In fact, wherever finely divided suspended particles should be removed from an oil, there is a possible use for a centrifugal machine, if the particles have, or can be made to have, a specific gravity different from that of the oil. Centrifugal machines are also used for cleaning fuel and lubricating oils and dehydrating transformer oils. Applications and Results When oil comes from the well mixed with water, it is spoken of as cut oil. Settling often does not remove sufficient water for the oil to be accepted by pipe lines, thus necessitating chemical or other treatment. Centrifuging alone, or following chemical treatment, effectively prepares such oil for pipe lines, as is shown by the following data: WateR, Etc. Wat~R. Etc. Temperature, Oil to Pipe Line, aT StUt at Finish Degrees F. Bel. Per HouR PIE Cent. PEECent Oklahoma lease.... 160 10 10 0.25 Kansas lease....... 125 4 20 0.25 to 2 On the Oklahoma lease, the machine was cleaned of solid material once in 12 hr. At first, it was thought that chemical treatment was necessary to start separation and 1 qt. of prepared compound was added to each 100 bbl. of the cut oil before centrifuging. Later it was found that

Jan 1, 1924

By Francis M. Rice

Before the world-wide depression, the primary purpose of most blast-furnace operators was to produce a maximum tonnage of pig iron per day for each furnace in blast. Some attention was paid to the conservation of labor and raw materials, but the idea was well established that low-cost pig iron was attainable only when each furnace was producing a high tonnage. After the depression had set in, the picture changed considerably. Each blast-furnace operator was forced to run his plant in a manner that best fitted the economical set-up of his company. A great deal of thought was expended on the different methods of operation, always with the idea of making each product in a way that would best serve his company financially. Because of this abnormal condition, the blast-furnace man was compelled to indulge in various practices of which many had been believed to be next to impossible up to that time. The ultimate purpose of these innovations was either one or a combination of the following: 1. To produce only enough pig iron for immediate consumption at a minimum cost. 2. To produce gas for boiler or mill use to supplant some higher priced fuel. 3. To consume the coke produced at the coke plant, which was often viewed as a byproduct. 4. To protect the cash position of the company. These conditions were met by diverse methods, some of which were: 1. Slow or decreased wind. In some instances the blast blown was held as low as 25 per cent of the normal volume. 2. Intermittent operation, in which the furnaces were shut down or "fanned" at frequent intervals.

Jan 1, 1935

By Francis M. Rice

Before the world-wide depression, the primary purpose of most blast-furnace operators was to produce a maximum tonnage of pig iron per day for each furnace in blast. Some attention was paid to the conservation of labor and raw materials, but the idea was well established that low-cost pig iron was attainable only when each furnace was producing a high tonnage. After the depression had set in, the picture changed considerably. Each blast-furnace operator was forced to run his plant in a manner that best fitted the economical set-up of his company. A great deal of thought was expended on the different methods of operation, always with the idea of making each product in a way that would best serve his company financially. Because of this abnormal condition, the blast-furnace man was compelled to indulge in various practices of which many had been believed to be next to impossible up to that time. The ultimate purpose of these innovations was either one or a combination of the following: 1. To produce only enough pig iron for immediate consumption at a minimum cost. 2. To produce gas for boiler or mill use to supplant some higher priced fuel. 3. To consume the coke produced at the coke plant, which was often viewed as a byproduct. 4. To protect the cash position of the company. These conditions were met by diverse methods, some of which were: 1. Slow or decreased wind. In some instances the blast blown was held as low as 25 per cent of the normal volume. 2. Intermittent operation, in which the furnaces were shut down or "fanned" at frequent intervals.

Jan 1, 1935