By Charles Law McCabe, Lyndon H. Everett, Edna A. Dancy

It has been found that the carbide phase present at equilibrium in the system M-H2-CH4, at about 600°C, is MC for the rare-earth metals Ce and Pr. X-ray diffraction analysis showed that the monocarbides have fcc structures with lattice constants of 5.036 + 0.009Å and 5.131 + 0.001Å for CeC and PrC respectively. Gaseous equilibrium measurements were used to calculate the standard free energy of formation of the monocarbides from the elements. for the formation of (+ 1300) for the formation of PrC. THE rare-earthdicarbides, and their crystal structures, have been known for some years,l but only more recently were the carbides CeC,2,3 Ce2C3 2 and CeCS3 reported. In 1958 to 1959, Spedding et al. published work on the lanthanum-carbon system4 and other rare-earth metal-carbon systems,5 proving the existence of M2C3 and MC2, and measuring the lattice constants. They also demonstrated that tri-rare earth carbides, M3C, exist for the rare-earth metals samarium through ytterbium. However, they concluded that the cerium monocarbide reported by Brewer and Krikorian2 and by Warf,3 and given a fcc structure with a lattice constant of 5.130Å bythe former workers, was, in fact, cerium metal with carbon dissolved in it. They were also unable to find any evidence for the existence of Warf's CeC3, for which no structural details had been given. Even more recently, Palenik22 reported the existence of only M2C3 and MC2, having been unable to find any evidence for the existence of any other rare-earth carbides. There are no published experimentally derived thermodynamic data for the formation of any of these carbides, although Brewer and Krikorian6 have estimated values of for CeC, Ce2C3 and CeC2. The objective of the present investigation was; to determine experimentally the free energy of formation of any of the reported carbides of cerium and praseodymium, through a study of the rare-earth metal-hydrogen equilibrium. EXPERIMENTAL A methane-hydrogen mixture was circulated, in a closed system over previously prepared cerium or praseodymium hydride, and when equilibrium had been attained, the gas mixture was analyzed by selectively oxidizing the hydrogen and condensing out the water formed. The metal hydrides were used as starting material for convenience because, otherwise, the hydrogen in the gas mixture would immediately dissolve in the metals; in addition, the metals would not react with methane alone at the experimental temperature (around 600°C). The circulating system was based on that used by Browning, DeWitt, and Emmett7 for similar studies on iron carbides. It consisted of a quartz reaction vessel, all-glass circulating pump, analysis tube containing copper oxide that could be heated to 300" C by means of a small furnace, a solid CO2-methanol trap, and a double limb absolute manometer, Fig. 1. A cathetometer, capable of reading to 0.005 cm, was used to measure the difference in height between the two columns of mercury. In its final form, the reaction vessel was enclosed in an outer jacket, containing approximately the same pressure of hydrogen as that within, to reduce errors due to diffusion of hydrogen out through the fused silica of the reaction vessel., The circulating system was supplied with

Jan 1, 1962

By R. H. Doremus, E. F. Koch

The first carbide phase that precipitates at 120°C from a iron containing about 0.02 wt pct, C was studied with the electron microscope. In both strained and unstrained material the carbide particles appeared to form on the dislocations in the iron, in agreement with the results of the kinetic study in part II. The structure of the carbide was tentatively identified as an expanded a-iron lattice (body-centered tetragonal) with about 0.7 wt pct C. This phase appeared to be metastable and apparently transformed into cementite or epsilon carbide when the iron was over-aged. WhEN a iron containing less than about 0.025 wt pct C is quenched from 700°C to room temperature the carbon is retained in solid solution and precipitates out slowly with time. The morphology and structure of the precipitating phase are still in doubt, two different carbide phases, epsilon carbide and cementite, have been identified, but there is considerable disagreement about the time and temperature at which they appear.1-4 Epsilon carbide seems to form at lower temperatures than cementite, although one group of investigators4 found only the latter phase over a wide range of aging temperatures. Usually these two phases have been identified after aging times much longer than needed to drain the carbon from supersaturated solution, at least for aging temperatures below 200oC. The precipitated carbides have been observed with the electron microscope,'-5 but again most results have come from samples aged much longer than necessary to reduce the carbon concentration in solution to a low value. In this study the carbide phases were observed in earlier stages of precipitation with the electron microscope, in order to learn more about the shape, size, and distribution of the carbide particles. Samples strained small amounts before aging, as well as unstrained samples, were studied, and the structure of the carbide phase was tentatively identified. EXPERIMENTAL "Ferrovac E" vacuum-melted iron, from which the wires for kinetic studies were also made (Refs. 6 and 7 and the following paper) was used for this work. An analysis of this material is given in Table I; it agrees well with the manufacturer's values. The number of inclusions in the iron was very small, as can be seen in the optical micrograph in the following paper. Pieces of iron about 1 mm thick and 5 to 10 mm in diam were used for all the studies except for those in which the sample was strained before aging; then the specimen was a rod 3 to 6 mm in diam and 20 cm long. The samples were held at about 700°C in wet hydrogen for at least an hour to remove residual carbon and nitrogen, after which they were heated to 950" (in the y region) and cooled to room temperature in the furnace. This treatment gave an average grain diam of more than 1 mm, so that the effect of grain boundaries on the precipitation process was negligible. The samples were carburized at 710°C for about 2 hr in hydrogen that had passed over toluene held at -30°C; then they were rapidly quenched into water. From chemical analysis this treatment gave a carbon concentration of from 0.012 to 0.016 wt pct, which is less than the solubility of carbon at this temperature. After quenching, the samples were aged at 120 "C in an oil bath for vari-

Jan 1, 1961

By Oscar Johnson

The industry has been canvassed for information on methods of handling grinding steel at milling plants, an important subject overlooked in most descriptive articles on milling plant arrangements. The data collected are offered in this paper as a guide to designers and planners who have loading and storage problems to solve. WITH capacities of milling plants expanding from a few hundred tons per day to many thousand, replenishment of grinding media is an important phase of mill operation. Information on this aspect of milling procedure, solicited from several mining companies, is summarized here. At International Nickel's Copper Cliff concentrator the normally strenuous job of changing rods is considerably simplified by the use of the Garrow rod charging machine, Fig. 1. The overhead crane, Fig. 2, brings a bundle of rods, weighing four to a ton, to the loading platform of the machine, positioned in front of the mill. The rods roll one by one down the slight incline of the platform onto a conveyor which sends them into the mill. A modified version of the Garrow machine, Fig. 3, is used at the Federal mill of St. Joseph Lead Co. An overhead crane places the portable steel structure in position in front of the discharge end of any one of the five 9x12-ft rod mills. It then raises a bundle of about twenty 3-in. rods to the discharge platform of the charging machine. The rods are 11 ft 7 in. long and weigh about 278 lb. By tripping a lever the operator allows one rod at a time to roll onto the inclined rollers. A slight push by the operator sends the rod smoothly into the mill. The Union Miniére du Haut Katanga rod charging machine, Fig. 4, is mounted on a pair of wheels at the forward end with swiveling castors at the back for steering it to position for use or storage. Wheels are equipped with locking brakes to maintain the machine in position while it delivers rods to the mill. The device is made in two parts. The first consists of the base, which carries the supporting wheels, grooved rollers, and drive. The other part serves as the rod deck, which can carry up to six 3-in. x 12-ft rods. A short boom built integral with the base reaches through the mill trunnion and delivers the rods into the mill barrel. Three grooved guide rollers ,are provided to receive the rods from the sloping charging deck. One rod at a time is fed to the rollers and thus delivered into the mill. Two of the rollers are driven by 11/2-hp motor through a V-belt drive. The third roller is driven off the first by a single V belt in a groove below the rod groove and on the same center line. Rods are delivered to the charger by an overhead crane in bundles of three to six as needed. The power is supplied by cables plugged into power outlets, suitably located near the rod mill discharge end. The Oliver Iron Mining Co. uses a rod charger, Fig. 5, suspended from a monorail by cables. It is constructed .of structural steel and has two decks, each capable of carrying five rods of 4-in. maximum diameter. The rods ride in grooved free-turning rollers. Legs extending down from the mill end of the mechanism act as supports when the unit is ex-

Jan 1, 1955

By Charles W. Chesterman

Perlite is a glassy volcanic rock which will, upon rapid controlled heating, expand or "pop" into a frothy material of low bulk density, valued as a lightweight aggregate. The term perlite also is applied to the expanded product. The chemical composition of perlite ranges from that of rhyolite to that of andesite; the water content ranges from 2 to 5%. Most perlite is pale gray, but some is black, brown, or even green. Inclusions in perlite are common and include phenocrysts of quartz, feldspar, biotite, and hornblende, and miscellaneous rock fragments. Occurrences of perlite are restricted to areas of Tertiary and Quaternary volcanic rocks. Perlite occurs as flows associated with thick accumulations of pyroclastic debris and other flow rocks, as dikes, sills, domes, and as selvages of intrusive bodies of volcanic rock. Individual flows of perlite range in thickness from a few feet to as much as 100 ft and commonly cover several square miles. Dikes and sills of perlite generally are small, but domes generally are substantial in size and may be as much as several miles in diameter. Most perlite deposits are large enough and topographically situated so as to lend themselves to low-cost open pit mining methods. Conventional equipment is employed in the mining of perlite. Although milling procedures may appear to be simple, care is exercised in order to produce a carefully sized product and to minimize the production of excessive quantities of fine materials, which have limited use and are considered as waste. Perlite is processed, or "popped," in one of two basic types of furnaces: horizontal rotary or vertical stationary. Both types of furnaces include product collection and dust control systems. Many commercial deposits of perlite are known to occur throughout the world, and although no exact estimate of reserves is available, there appears to be an adequate supply to meet current and future worldwide requirements. End Uses The uses of expanded perlite are many and varied and are based primarily upon its physical and chemical properties. Because of its (1) low bulk density, which generally ranges between 2 and 20 lb per cu ft; (2) low thermal conductivity "K" factor (Btu per hr per sq ft per OF per in, of thickness), which ranges between 0.267 for loosely packed perlite (bulk density of 4.48 lb per cu ft) to 1.25 for perlite gypsum plaster; (3) high resistance to fire; and (4) low sound transmission, expanded perlite is used to a great advantage as aggregate and insulating material in the construction industry. Early uses of perlite were related exclusively to the construction industry, which now consumes about 60% of the domestic production. The primary use of perlite now is as aggregate in insulation boards. Other uses of perlite in 1971 were as aggregate for plaster, horticultural aggregate, low-temperature insulation (cryogenics), and concrete. Because of its low thermal conductivity ("K" factor), high adsorption of sound, low bulk density, and fire resistance, perlite aggregate plasters hold many advantages over conventional plaster. Perlite aggregate plaster lends itself to machine applications, dries quickly, and has relatively high elasticity which reduces cracking after drying. These same features make perlite useful as aggregate in portland cement concrete and asphalt concrete for construction wherever weight reduction, insulation, and acoustics are of prime importance. Perlite-portland cement concrete offers up to 20 times more thermal insulation than conventional concrete, and because of this it finds wide application in roof decks and floor fill in multistory buildings, in

Jan 1, 1975

By G. R. Speich, Morris Cohen

The growth rate of bainite has been determined by hot-stage metallography in five hypereutectoid high-purity iron-carbon, iron-carbon-chromium, and iron-carbon-nickel alloys. The studies have been confined essentially to lower bainite. The growth rate is independent of time at constant temperature, but both the edgewise and sidewise growth rates increase with increasing temperature. Increasing the carbon content, or adding chromium or nickel, decreases the growth rate without greatly affecting the temperature dependence. The results lead to separate diffusion-controlled models for the edgewise and sidewise growth rates. ALTHOUGH bainite has been subject of many detailed investigations,1,2 the growth mechanism of this intermediate transformation product of steel remains unclear. One difficulty has been that practically all the kinetic measurements have been restricted to studies of the overall reaction rate. Only a limited amount of information3, 4-6 is available on the growth process itself. The purpose of the present work was to investigate the effect of time, temperature and composition on the growth rate of bainite using hot-stage metallography. This method makes it possible to observe continuously the isothermal growth of individual bainitic units because of the surface upheavals accompanying their formation.3 This information is needed to test the existing growth models and to obtain a better understanding of the factors controlling the bainitic transformation. EXPERIMENTAL PROCEDURE Alloys—The compositions of the alloys used in the present work are shown in Table I. The five alloys were vacuum-melted and cast, and were prepared from high-purity materials. The three iron-carbon alloys were available from the work of Roberts et al.7 in the form of 3/8-in. diam rods.* To facilitate machining, the rods were ing. The rods were then tempered for 3 hr at 650°C to allow machining. The iron-carbon alloys in Table I were selected for investigating the effect of carbon on the bainitic growth rate. Due to the rapidity of the transformations involved, it was not feasible to measure the growth rates in iron-carbon alloys having carbon contents much less than 0.9 pct C. The iron-carbon-chromium and iron-carbon-nickel alloys were selected to study the influence of chromium and nickel on the growth rate at a carbon level of about 1.1 pct C, since this carbon content was intermediate among the iron-carbon alloys. The concentrations of chromium and nickel were chosen to match isothermal trans formation diagrams in the literature.8'9 Hot-Stage—Since the iron-carbon alloys had such low hardenabilities, it was necessary to quench the hot-stage specimens drastically from the austentiz-ing temperature to the isothermal transformation temperature to prevent the formation of pearlite or proeutectoid constituents. A rapid-quenching metal-lographic hot-stage was built for this purpose. A maximum temperature of about 1100°C and quenching rates up to 500°C per sec could be attained with this equipment. The details of the apparatus are described in a recent publication. After being polished and mounted on the hot-stage, the specimen (0.020 in. thick) was protected from oxidation and decarburization during austenitizing by a vacuum of 10-4 to 10-5 mm. The quench to the reaction temperature was accomplished with a helium blast, and the isothermal run at this temperature was conducted in a helium atmosphere. A fine-wire thermocouple spot-welded to the sample and a high-speed

Jan 1, 1961

By F. W. Warnaars

The Los Bronces copper deposit is located on the west side of the Andes Mountains in central Chile about 54 km (34 miles) northeast of Santiago. The deposit consists of a hydrothermal breccia complex that was emplaced in the western part of an earlier porphyry copper mineral system. This system exhibits propylitic, sericitic, silicic to potassic hydrothermal alteration with disseminated and stockwork copper-molybdenum sulfide mineralization over an area of about 12 km2 (5 sq. miles). The Rio Blanco Mine, about 800 m (0.5 miles) east of Los Bronces, is an underground block caving mine located in the central part of this system. The mineralization at Rio Blanco is characterized by one of the highest primary copper grades known for porphyry copper systems. Present mining at Los Bronces is from an open pit located in the northern part of a hydrothermal complex that is composed of at least seven different copper-bearing tourmaline breccia pipes. Together these pipe form one large contiguous body about 2 km (1.2 miles) long and 0.7 km (0.4 miles) wide at the surface. This body crops out at elevations of between 3.5 and 4.1 km (2 and 2.5 miles) above sea level. Each breccia pipe has a characteristic shape, matrix, type and degree of mineralization and alteration. Quartz, tourmaline, specularite, anhydrite, pyrite, chalcopyrite, sericite, chlorite, and rock flour are present in significant quantities in most breccia matrices. The clasts consist mainly of quartz monzonite, andesite, and minor amounts of quartz latite porphyry. The seven different breccia pipes are identified, from oldest to youngest, as Ghost, Central, Western, Infiernillo, Fine Gray, Anhydrite, and Donoso. The breccias coalesce, interfinger, or display gradational contacts. In places they form sharp contacts with each other and with the surrounding intrusive or volcanic host rocks. Early breccias are disrupted or cut by subsequent breccia events. Explosive emplacement was followed by collapse after the release of hydrothermal pressures. The Los Bronces breccia complex has sharp contacts with the surrounding intrusive stock and andesites. These contacts dip inward on the north, west, and south margins. The eastern contact is nearly vertical and/or dips slightly outward and suggests a westward tilting of the body of about 15° after emplacement. The breccia complex is not fully explored at depth, but is known to extend at least below the 3 km (2 mile) elevation in its central eastern part, about 1 km (0.6 miles) below the highest breccia outcrop. Primary copper sulfide minerals are most abundant in the Donoso and Infiernillo breccias where the matrix consists mostly of tourmaline, quartz, sulfides, specularite, and/or chlorite with minor amounts of rock flour, sericite, and clay. The volume of the matrix material is mostly smaller than in the other breccias. Secondary enrichment enhanced the primary copper grade in the southern two-thirds of the Los Bronces breccia complex and in much of the surrounding porphyry system. Primary grades of 0.3% to 0.5% copper have been enriched to approximately 0.9%. This enrichment may extend from surface outcrops to a depth of more than 500 m (1, 640 ft) in more permeable parts of the breccia complex. A leached and oxidized capping of variable thickness covers a large part of the enriched layer and exceeds 300 m (984 ft) at one location. The shape and depth of the enrichment blanket and the capping suggest that the enrichment process is still active.

Jan 1, 1983

By B. A. Shaw

Historically, microwave tubes have been fabricated from massive metal and ceramic components. The current trend is to lighten tibes for airborne applications. The reqciiremenls of light weight and also reduced cost have created a novel approach to tube structure in which thin-film technology plays a major role. Although the electrical requirements of thin-film circuits in microwave tubes differ from those required or se,niconductor integrated circuits. the technology is basically similar. The stringent requirements of the micvowave tube have created sophisticaled thin-film techniques thut are of interest to the integrated-circuit industry in general. This paper describes a nunzber of thin-jilm techniques recently developed and discusses in detail the application of the technology in microwave tubes. The particular areas of interest are: 1) ceramic mounted thin-film slow-wave structures; 2) thin-film secondary emitters; 3) suppression of tube environnental multipactor by semiconducting' thin films; and 4) age-hardenable and dispersion-hardened thin metal films. SEVERAL thin-film techniques specifically applied to microwave power tubes are discussed in this report. There are two reasons for this work. One is the necessity of reducing weight and cost of microwave tubes and the other is related to overcoming problems in the tube operation by the use of applied thin-film technology. The major emphasis of this work has been on tube slow-wave structures. Other work in the area of secondary emission, either its suppression or its enhancement, is continuing; the most satisfactory results to date have been by utilization of thin-film technology. The requirements of high thermal and electrical conduction together with greater strength than normally obtained with elemental materials have led to the development of dispersion-hardened films. The paper will discuss: 1) ceramic-mounted delay-line microwave tubes; 2) multipactor and secondary emission; 3) hardened films. I) CERAMIC-MOUNTED THIN-FILM SLOW-WAVE STRUCTURES In a conventional crossed-field microwave tube, the slow-wave or delay-line structure is produced from two carefully machined components. One half of the structure is shown in Fig. 1. The other half is the mirror image of the first but is rotationally offset by a half a period. The combined structure now forms an interdigital type of slow-wave structure and is the anode of the tube as shown in Fig. 2. The period and finger length of an interdigital slow-wave structure are prescribed by the desired dispersion characteristics. The typical design is as shown in the first figure; it can be noticed that the finger width is several times greater than the finger thickness. Even assuming that it were mechanically possible to produce free-standing fingers of extremely small cross-sectional dimension, for example, 0.002 in. thick by 0.005 in. wide by 0.500 in. long, decreasing this finger width would increase the tube efficiency but would also decrease the thermal-conduction path, causing an increased temperature rise from intercepted rf current which in its extreme could easily cause finger melting. Hence, for free-standing lines of this type, the design is a compromise between mechanical capabilities, tube efficiency, and thermal dissipation. These structures are also expensive and tend to be heavier than purely electrical considerations would demand. In the present approach, we have transposed the three-dimensional structure previously shown into an essentially two-dimensional structure as shown in Fig. 3. The linear structure is used here for clarity of detail. The support member is a ceramic material and the line is deposited copper. The final tube design is shown in Fig. 4. Because of the backwall sup-

Jan 1, 1967

By George P. Chapman

Mica is a platy mineral occurring in a variety of complex hydrous aluminosilicate forms with differing chemical composition and physical properties. Principal minerals in the mica group include: Muscovite-potassium mica (colorless or pale green/ ruby) Phlogopite-magnesium mica (dark brown or amber) Biotite-magnesium-iron mica (black or dark green) Lepidolite-lithium mica (lilac) Selected properties are given in Table 1. Muscovite is most important commercially with phlogopite of lesser use. The laminated structure of mica enables it to be split into very thin films which are transparent and tough as well as having outstanding dielectric and insulating properties. Commercially, mica is used in a number of forms (Chowdbury, 1941; Rajgarhia, 1951; Skow, 1962). Sheet mica consists of flat sheets mined from naturally occurring books of mica, free from defects and capable of being punched or stamped into required shapes. Sheet mica is separately classified into blocks, films, or splittings according to thickness. Built-up mica, or micanite, is made by arranging overlapping splittings in layers , cemented with a binder and pressed together at high temperature. Reconstituted mica, or mica paper, is made by depositing fine flakes of high-quality scrap mica in a continuous film impregnated with binder. Scrap and flake mica are normally unsuitable in quality or size for making sheet mica. Originally the term scrap mica referred to the waste byproduct of mining and fabricating sheet mica, and distinct uses were developed for this material. Subsequently it became economically feasible to mine lower quality mica for these uses, and the term flake mica was introduced. Although the two terms are still used somewhat synonymously, it is considered better, at least in the United States, to use the term flake mica in referring to mica mined for uses other than as sheet mica; and to restrict the term scrap mica to mica mined for or with sheet mica, but which will not meet the specifications. Synthetic mica, such as fluorophlogopite, is produced by slow crystallization of a melted blend of pure raw materials. Mineralogy In the true sense the term mica does not relate to, a particular mineral, but to a group or family of minerals of similar chemical composition and to some extent similar physical properties. These minerals are predominantly potassium aluminum silicates with varying amounts of magnesium, iron, and lithium. The precise formulas and isomorphic relationships of the various group members have been studied, but general agreement has not been reached (Grimshaw, 1971; Hurlbut, 1952; Skow, 1962). The general formula describing the chemical composition of micas is [X2Y4-6Z8020(OH, F)4, where X is mainly K, Na, or Ca; Y is mainly Al, Mg, or Fe; Z is mainly Si or Al (Deer, et al., 1962).] These minerals have an internal structure of the layered lattice type where the silicon atoms are in the center of a tetrahedral grouping of oxygen atoms. The groups are linked together in a single plane by three oxygen atoms that lie within the common plane. Each of these oxygen atoms is shared by two tetrahedra. These linked tetrahedral groups, when continually extended, produce a hexagonal network within the plane. This internal structure of the mica has been used to explain the ex-

Jan 1, 1983

By R. Fawley, M. A. Quader, R. A. Dodd

Stacking fault energies and annealing twin frequencies have been measured for austenitic stainless steels having a) constant 20 wt pct Cr and varying nickel contents, and b) constant 20 wt pct Ni and varying chromium contents. The effect of nitrogen has also been studied and, to a lesser extent, so has the effect of carbon. All measured stacking fault energies plot linearly against the corresponding annealing twin frequencies, suggesting that, for constant prior deformation and grain size, twinning frequency can be used to estimate stacking fault energy. Compositions low in nickel possess the lowest fault energy, while the maximum fault energy within the investigated composition range occurs mound 20 pct Cr-20 pct Ni. Nitrogen has practically no effect on stacking fault energy when increased from 0.005 to 0.05 wt pct, although Planar dislocation glide is associated with higher nitrogen contents; this may be a short-range order effect. Carbon may raise the stacking fault energy a little, and causes pronounced dislocation tangling in deformed alloys. The basically different dislocation structures promoted by nitrogen and carbon, respectively, are not associated with large variations in stacking fault energy, and the reason for the difference remains unknown. INTEREST in the dislocation configurations developed in plastically deformed alloys arises principally from a desire for an understanding of mechanisms of plastic deformation and fracture. Comparatively little basic work has been concerned with austenitic stainless steels, although considerable interest has developed in the fundamental aspects of deformation of these alloys since the suggestion that those compositions deforming essentially by planar glide are particularly prone to transgranular stress corrosion cracking.' Certain facts are well-established. An 18 Cr-8 Ni steel (type 304) has a low stacking fault energy which is increased by higher nickel contents, and the structure of these steels when moderately plastically deformed changes concomitantly from planar to less planar to distinctly tangled dislocation configurations. These changes are thought to relate to changes in stacking fault energy, and considerable effort has been expended in measuring stacking fault energies of austenitic stainless steels through the determination of node curvatures2"4 even though the method has limitations due to formula approximations,5 an upper limit of measurement of 50 erg cm-2 at the most,5 and the necessity of an extremely meticulous experimental technique. Therefore, it is not surprising that only qualitative agreement between different investigators is generally to be found.'-' At high energies where node radius measurements are inappropriate, some use has been made of annealing twin frequencies to estimate relative stacking fault energies, although a recent critical evaluation of the method suggests that it should be used cautionsly with due regard to effects of grain size and prior deformation.6 Finally, there is a question as to whether the structures of some deformed steels are due to ordering effects. In particular, the role of nitrogen in promoting planar dislocation motion has been suggested to be due to ordering,' but similar suggestions have been made for steels having low interstitial contents.4 EXPERIMENTAL Small ingots of austenitic stainless steels (-50 g) were prepared from components exceeding 99.99 pct purity, the nickel and chromium being Johnson Matthey "Specpure" metals. Carbon was added as pure graphite, and nitrogen as CrN. The components were accurately weighed, and it was assumed that the final composition was the same as the nominal composition

Jan 1, 1969

By R. Maddin, C. H. Mathewson, W. R. Hibbard

According to conventional crystal mechanics, a face-centered cubic single crystal slips on the system {111} <110> which receives the highest shear stress in terms of the stated orientation of the stress axis of the crystal.l However, in brass, the slip process is never as simple as this conventional analysis indicates. There is always a second cooperating plane which contains the same slip direction as the primary plane.2&apos;3 There is still another cooperating slip system commonly called the conjugate system3 previously observed to function with considerable lag only after the rotation due to the action of the first plane had produced a symmetrical condition of equal shear stress on the two systems. In the 1943 Campbell Lecture,4 a slip mechanism was outlined in which the {111) planes moved step-wise in two adjacent <112> directions integrating into the <110> slip direction. "... the slipping process would be visualized as a succession of steps 30" to the right and left of the resultant, microscopically observed, slip direction; a first step setting up the twinned configuration in the single spacing involved and an ensuing slip returning the atoms to the untwinned configuration while completing a fully integrated <110> movement."4 This process is shown diagrammatically in Fig 1 which shows two close packed layers of atoms at a slip site. A movement of the full circles through the "valleys" into the adjacent sites would produce a twin configuration with respect to the open circles. The term, "twin fault," seems most appropriate to define this faulted condition of the lattice. Annealing twins in face-centered cubic metals may arise from preformed nucleii which could be described as twin faults produced by the first movement of this two stage slip process. However, it is clear that this kind of slip does not take place so as to embrace a measurable number of adjacent planes because careful X ray examination has not conclusively shown the existence of ponderable twin lamellae (as in the case of Neumann bands in the body-centered ferrite). In view of the imponderable character of these hypothetical twin faults, the search for evidence of their existence seems restricted to indirect methods. The most obvious experimental technique serving this purpose is the determination by micrographic and X ray methods of the alignment of the composition planes of annealing twins with the former slip planes in axially strained and recrystallized single crystals. In previous attempts of this sort not all of the annealing twins could be traced to slip planes known to be operative in the conventional sense and hence evidence appeared negative or inconclusive. With the discovery of additional slip systems2&apos;3 operating in conjunction with&apos; the major system of highest resolved shear stress in axially strained brass it became apparent that the simple technique outlined above might be re-employed with more gratifying results. If, on annealing single crystals of alpha brass previously strained in tension, twins are found with their composition planes parallel to all three operative slip planes and with no participation of the fourth plane there is good evidence in favor of the existence of twin faults and of the two stage slip process. Experimental Procedure and Resuits Single crystals of alpha brass of the 70-30 composition were grown by solidification from the molten state.

Jan 1, 1950

By L. A. Panek

Research on roof bolting has developed significant information with respect to the functions that can be performed by properly installed bolts and the methods that can be used to ensure that effective installation has been achieved. The present paper brings together results that are pertinent to the design of a bolting system for reinforcing horizontally stratified mine roof with vertical bolts. The design approach is based on the use of bolts to decrease the maximum bending stress within an arbitrary sequence of roof strata (see Fig. 2) in which the only loads are the weights of the individual beds. The use of rock bolts to achieve other objectives, such as to stabilize a fractured rock mass on the periphery of a mine opening,3 is excluded from consideration herein. Reinforcing effect of bolts consists of a friction effect and a suspension effect in combination. "Friction effect" refers to reduction of bending in a stratified roof due to clamping action of tensioned bolts, which compress the strata, thereby creating frictional resistance to displacement along planes of stratification. (The flexure of a sequence of strata is necessarily accompanied by horizontal displacement of each bed with respect to its neighbor, along mutual surfaces of contact.) Although the sliding of the beds tends to exert a shearing effect on the bolts, tests show that this has negligible influence on the bending stresses, probably because the bolts are so far apart. "Suspension effect" refers to the transfer of part of the weight of the weaker or thinner strata to one or more thick strata, which occurs when strata with differing tendencies to deflect are constrained to have equal deflection. The term "suspension" is used irrespective of whether the thin strata are above or below the thick strata, because tests show that the supporting effect of the flexurally more rigid roof strata is for practical purposes independent of their position in a bolted sequence of strata. An earlier paper4 dealt with a bolted unit in which all strata had equal flexural rigidity; bolting could develop a friction effect but no suspension effect. The present paper deals primarily with a bolted unit in which all strata do not have equal flexural rigidity, so that bolting can develop both a friction effect and a suspension effect. The reinforcing effect of the bolts was determined by a combination of experimental and theoretical stress analysis.4&apos;6&apos;7 The experimental method consisted of loading a model by rotating it in a centrifuge to simulate the gravity forces exerted about an underground excavation. Models were made from two different limestones, although the results are independent of the material because the elastic constants were taken into account in the data analysis. Electric resistance strain gages were bonded to the highest and lowest members of the bolted unit to determine the outer-fiber bending strains at the center and at the supports. The quantitative results presented herein are based on tests of 56 different models, which included a range of values for the structural parameters. Each model was tested several times, with different combinations of spacing and tension of the bolts. DESIGN EQUATIONS The effects of friction and suspension on the flexure of a bolted stratified roof can be expressed by the following equations, which give the maximum bending stress, the deflection, the friction effect, the suspension effect and the transferred load for any (the i-th) member of the bolted unit in terms of the structural parameters:

Jan 1, 1964

By H. C. Chang, N. J. Grant

REEP studies and measurements in most in-V> stances are based on a relatively gross gage length. Even in some recent theoretical studies on the mechanism of creep, changes were followed by means of X-rays and metallography without regard for the behavior of the individual grains and grain boundaries.&apos;" Analytical studies of creep have frequently indicated that more than one competing process is operative and that the ultimate creep performance depends on the effects of temperature, time, and strain rate as well as grain size.&apos;-" he grains and grain boundaries are known to respond differently to these variables but the extent of the response is still little known, especially in poly-crystalline materials where the relative orientations of grains and grain boundaries are important. This paper reports some experimental observations of the behavior of the grain boundaries and their effect on the deformation in the grains. High purity aluminum was used to avoid complications of aging reactions, second phase, inclusions, etc. Experimental Procedure A small vertical nichrome wound furnace was built to permit direct loading on the test specimen. This furnace is capable of operating up to about 1300°F with reasonable temperature distribution. A ground rectangular quartz window, 1.25x0.5 in., is imbedded in the external stainless steel tube to permit observations of the creep process with a microscope. An argon atmosphere ,was provided to prevent oxidation. The quartz window caused a temperature gradient between the back and front surfaces of the specimen of 15" at 700°F. The temperature gradient could be cut down to 3°F along the length of the specimen by adjusting shunts across the furnace windings. An ordinary metallurgical microscope with a working distance of 14 mm was rebuilt so that it could be moved in three mutual perpendicular directions. Visual examination could be made with either a 30X eyepiece or a 15X filar eyepiece. Using an objective of focal length 24.3 mm and a numerical aperture 0.20 a total magnification of 120X or 240X could be obtained. High purity aluminum rated at 99.995 pct was supplied by the Aluminum Co. of America as % in. then the gage portion was further machined to 3/16 in. diam. The ends were Y4 in. diam and threaded to fit available specimen holders. Two opposite flat surfaces of the gage portion were obtained by milling, giving final dimensions of the gage portion of 3/4x3/16x3/32 in. Machined specimens were first electropolished in Jacquet&apos;s solution.&apos; Reference marks were produced by pressing a thin sewing needle into the surface of the specimen. The specimen was then annealed at 900°F for 24 hr and at 1150°F for 12 hr. Typical macrostructures of specimens treated in this manner are shown in Fig. 1. The range of the grain size was 1 to 5.5 mm (see Fig. l), but most of the grains were of 2.5 mm and went through the whole thickness of the specimen. The specimen was re-electropolished and etched electrolytically to reveal the grain boundaries. In order to reveal the orientation difference of the grains, etch pits were produced on the surface of the grains by etching in a mixture of hydrochloric and nitric acids (HC1, 45 pct; HNO,, 10 pct; H,O, 45 , by volume). The specimens were very carefully put into the holders and furnace; yet even with this care, fine slip lines were developed on the specimen surface.

Jan 1, 1953

By G. C. Weaver, G. T. Harley

Beds or lenses of potash and magnesium salts are found in a thick salt section (Salado) overlain by Rustler Red Beds in several members of which water is present and from one of which the rehery process water used by International is obtained. Most of the holes drilled are less than 1000 ft. deep, but some wildcat holes have exceeded 3- ft. cable or rotary tools are used to drill down to the salt. when samples of water are desired the cable rig is used, but when this is not necessary, and where caving material is present, the rotary rig has an advantage. The rotary rig has a further advantage in that only one machine is required to drill and core the entire hole, whereas the cable rig must be moved off to make way for the core drill. Casing is placed in the upper section of the hole as required to shut off water, and a 5 3/16 in. string is set in the top of the salt before coring starts. With the rotary rig drilling is often carried to the salt with no casing, as drilling mud seals off caving ground and water-bearing strata, and a string of 4-in. line pipe or 4-in. flush-joint casing is landed on top of salt. Several types of gasoline-powered core rigs have been used in the field and all recover a 2 1/2-in. core. More recently the Sullivan Model 37 rotary rig has been tried, and a Sullivan Model N has been adapted to use a rotary bit in the upper section. Core is recovered in 20 ft. sections with a double-tube core barrel, and the bit used is a bottom-discharge type set with diamonds. The drilling fluid must be a saturated brine to prevent solution and etching of the minerals present. Blowouts are apt to Occur from nitrogen gas trapped under the several polybalite beds, and some have been strong enough to blow the tools out of the hole. Core recovery is practically loo per cent. All holes are plugged after drilling, with cement through the salt section and opposite each water horizon* and mud through the remainder of the hole. Cores are carefully logged and preserved, and in sections containing potash and magnesium minerals they are quartered and analyzed. The correlation of Ore beds between drill holes is briefly described. Introduction Beds Or lenses of potash and magnesium salts are found at varying depths in a thick deposit of salt (Salado formation) in what is known as the Permian Basin, in southeast New Mexico and West Texas. The Salado formation is Composed chiefly of common salt (halite) with numerous beds of anhydrite, polyhalite, and the soluble potash minerals carnallite, sylvite and langbeinite. Many other minerals are present in small amounts but their Presence has no bearing On the coring technique. Before starting to core the salt section it is necessary to penetrate 300 to 600 ft. of unconformably overlying Permian sediments (Rustler formation) which are composed of red and gray clay, sand, anhydrite, dolomitic limestone and occasional lenses of salt. The upper part of the formation is predominantly anhydrite, and the lower part predominantly clastic. A thin bed of dolomitic limestone, known

Jan 1, 1948

By G. C. Weaver, G. T. Harley

Beds or lenses of potash and magnesium salts are found in a thick salt section (Salado) overlain by Rustler Red Beds in several members of which water is present and from one of which the rehery process water used by International is obtained. Most of the holes drilled are less than 1000 ft. deep, but some wildcat holes have exceeded 3- ft. cable or rotary tools are used to drill down to the salt. when samples of water are desired the cable rig is used, but when this is not necessary, and where caving material is present, the rotary rig has an advantage. The rotary rig has a further advantage in that only one machine is required to drill and core the entire hole, whereas the cable rig must be moved off to make way for the core drill. Casing is placed in the upper section of the hole as required to shut off water, and a 5 3/16 in. string is set in the top of the salt before coring starts. With the rotary rig drilling is often carried to the salt with no casing, as drilling mud seals off caving ground and water-bearing strata, and a string of 4-in. line pipe or 4-in. flush-joint casing is landed on top of salt. Several types of gasoline-powered core rigs have been used in the field and all recover a 2 1/2-in. core. More recently the Sullivan Model 37 rotary rig has been tried, and a Sullivan Model N has been adapted to use a rotary bit in the upper section. Core is recovered in 20 ft. sections with a double-tube core barrel, and the bit used is a bottom-discharge type set with diamonds. The drilling fluid must be a saturated brine to prevent solution and etching of the minerals present. Blowouts are apt to Occur from nitrogen gas trapped under the several polybalite beds, and some have been strong enough to blow the tools out of the hole. Core recovery is practically loo per cent. All holes are plugged after drilling, with cement through the salt section and opposite each water horizon* and mud through the remainder of the hole. Cores are carefully logged and preserved, and in sections containing potash and magnesium minerals they are quartered and analyzed. The correlation of Ore beds between drill holes is briefly described. Introduction Beds Or lenses of potash and magnesium salts are found at varying depths in a thick deposit of salt (Salado formation) in what is known as the Permian Basin, in southeast New Mexico and West Texas. The Salado formation is Composed chiefly of common salt (halite) with numerous beds of anhydrite, polyhalite, and the soluble potash minerals carnallite, sylvite and langbeinite. Many other minerals are present in small amounts but their Presence has no bearing On the coring technique. Before starting to core the salt section it is necessary to penetrate 300 to 600 ft. of unconformably overlying Permian sediments (Rustler formation) which are composed of red and gray clay, sand, anhydrite, dolomitic limestone and occasional lenses of salt. The upper part of the formation is predominantly anhydrite, and the lower part predominantly clastic. A thin bed of dolomitic limestone, known

Jan 1, 1948

By R. M. Waterstrat, B. N. Das, Paul A. Beck

The central region of the Ti-Mn system was studied by means of x-ray diffraction and metallography. The following intermediate phases were found: an MgZn2-type Laves phase having a wide range of homogeneity, the p-phase of unknozvn structure, and the + -phase with a large tetragonal unit cell, stable at 930°C and lower temperatuves. MaYKUTH, Ogden, and jaffee1 determined the soh-inh bility limits of manganese in and titanium. They also confirmed the structure of the intermediate phase TiMn2 which was previously identified as a Laves phase of the MgZn2 type.2 In the equiatomic region they found an additional intermediate phase, y, which presumably formed by a peritectic reaction at approximately 1200°C. This last observation was disputed by Rostoker, Elliott, and McPhers0n,3 who reported the formation of TiMn by a peritectoid reaction between 900" and 1000° C, but found no evidence of any intermediate phase other than the Laves phase at higher temperatures. Elliott and Rostoker4 reported furthermore that the X-ray diffraction pattern of TiMn could be identified as that of a o phase, although their data were not consistent with this inter~retation. Margolin and Ence6 presented X-ray diffraction data for the and TiMn, phases, and obtained metallographic indications for the existence of additional intermediate phases. They concluded from metallographic observations that two Laves phases are formed, separated by another phase, designated as &. A phase diagram for the Mn-Ti system has recently been published by Savitskii and Kopetskii,&apos; which shows considerable disagreement with the work of Hellawell and Hume-Rothery,&apos; in particular with regard to the terminal solid solutions based on the allotropes of manganese. The present investigation was undertaken primarily to clarify the phase relationships in the equiatomic region of the Ti-Mn system. The metals used in preparing the alloy specimens Were iodide titanium and electrolytic manganese, the latter having a nominal purity of approximately 99.9 pet. The electrolytic manganese was covered with a thick coating of a brown manganese oxide which was reduced by heating the manganese flakes for several hours at a temperature of 1100°C in an atmosphere of dry hydrogen. Three alloys, see Table I, were made using sponge titanium and manganese not treated in hydrogen. The alloys were prepared by arc-melting in an atmosphere of helium or argon. The composition of each alloy was calculated by assuming that the entire weight loss during melting was due to evaporation of manganese. Subsequent chemical analysis of certain alloys indicated that the compositions calculated in this manner were usually correct within 1.4 pct, as shown in Table I. All alloy specimens were wrapped in molybdenum foil before sealing them in silica tubes containing argon at a pressure of 1 atm at the annealing temperature. After quenching in cold water, the alloy specimens were bright and clean, with no evidence of any surface reaction. The alloys listed in Table I were examined metallographically, using an etchant consisting of 20 pet HNO3, 20 pet HF, and 60 pet Glycerine. powder for X-ray diffraction examination was prepared by crushing a portion of each annealed alloy

Jan 1, 1962

SEC. 1. The membership of the Institute shall comprise seven classes, namely: 1. Members; 2. Honorary Members; 3. Senior Members; 4. Associates; 5. Junior Members; 6. Rocky Mountain Members; 7. Junior Foreign Affiliates. All shall be equally entitled to the privileges of membership, excepting that no member of any class whose residence shall be outside of the United States of America, except those residing in Mexico and Canada, shall be entitled to vote. SEC. 2. Members: A person to be eligible for election or transfer into the class of Member must be at least 27 years of age and must have had at least six years&apos; employ¬ment in the practice of engineering, mining, geology, metallurgy, or chemistry, during at least three years of which he must have held positions of responsibility in one or more of these fields. This shall not apply to Rocky Mountain members. SEC. 3. Honorary Members: Each candidate for Honorary Membership must be recommended by at least ten Members and must be elected by ballot at a meeting of the Board of Directors by the unanimous vote of the Directors present; provided, how¬ever, that the number of Honorary Members shall at no time exceed twenty. Such election shall automatically act as a transfer of such member from any other class of membership to which he may belong. SEC. 4. -Senior Members: The Directors may in their discretion place on the Honor Roll of Senior Members and transfer from any other class of membership other than Honorary Membership the name of any Member or Associate who has reached the age of seventy years and who has paid dues for thirty years, and for good reasons in special cases may vary the age or number of years. SEC. 5. Junior Members: A person to be eligible for election to the class of Junior Member must be qualified through education or experience to hold a subordinate position in engineering, mining, metallurgical, geological or chemical work. He shall be not more than 33 years of age at the time of election. SEC. 6. Associates: A person eligible for election or transfer into the class of Associate shall be one, who, in the opinion of the Committee on Admissions and the Board of Directors, is suitable for such election or transfer by reason of his interest in or connection with mining, geology, metallurgy, or chemistry. SEC. 7. Rocky Mountain Members: Membership in a special class of life member¬ships without annual or other dues and without right to receive the printed literature distributed to other members or the right and privilege of wearing the official badge of technical members, is given to all members of the Rocky Mountain Club at the time of consolidation. These special Rocky Mountain memberships shall be claimable by any member of the Rocky Mountain Club, not already a member of the Institute, availing himself of the privilege within ninety days after mailing of notice to him, by the Secretary of the Institute. SEC. 8. Junior Foreign Afliate: Upon appropriate action by the Board of Direc¬tors and with its approval, members in good standing of any technical society having its headquarters outside of the United States of America, Canada, or Mexico,

Jan 1, 1937

By R. E. Robbins, H. R. Brager

THIS note describes an unusual result obtained in an electron microscope investigation of cavities produced in commercial type 304 stainless steel irradiated in a thermal reactor (ETR) at 290°C to a high neutron flu-ence, 6 x loz1 n per sq cm. The analysis of the steel used is given in Table I. The unusual result is that the calculated quantity of helium gas produced by transmutation during the irradiation, 12 ppm, is less than one-tenth the amount of gas necessary to balance the surface tension of the observed cavities produced in the steel during ETR irradiation. Therefore, the cavities would be expected to behave like voids; however, they behave like "gas filled" bubbles. The maximum quantity of helium produced in the steel by B" transmutation was 8 ppm. In addition, the amount of helium formed by (n, (1) fast neutron reactions with the major alloy constituents and nitrogen was calculated to be 4 ppm based on the tabulated differential or effective fission-averaged cross sections of elements in type 304 stainless steel irradiated in typical thermal reactors.&apos;, In previous investigations concerning commercial austenitic stainless steel irradiated in a thermal reactor, the amount of helium gas calculated to be produced by transmutation has always been significantly greater than the amount calculated on the basis that the bubbles were gas filled, PPs= 2y/R. The balance of the gas was assumed to be in bubbles smaller than could be detected on the electron micrographs. Accordingly, the bubbles were attributed to helium produced from transmutation of impurity boron by thermal neutrons. These bubbles were not uniformly dispersed in the matrix but were located principally at grain boundaries, or were radially positioned around a few precipitates located in the matrix and at the grain bundaries., 4 Voids have also been observed in austenitic stainless steel irradiated at high temperature to high neutron fluences in the EBR-I1 and Dounreay Fast Reactors. The voids were uniformly distributed throughout the matrix. The amounts of helium gas produced by transmutation during these irradiations were less than one-tenth the amounts needed to balance the surface tension of the voids formed by the fast reactor irradiation. The fast reactor results are quite analogous to those reported here for the ETR irradiated steel. Electron microscope examination of the fast reactor irradiated material after a 1 hr postirradiation annealing at 900°C disclosed that essentially all the voids had been eliminated. The authors stated that the voids had developed due to the high concentration of vacancies produced during irradiatin., 6, &apos; The microstructure of the ETR irradiated material as-tested at 75O°C, Fig. 1, contained about 2 X lot5 cavities per cm3 with an average diameter of 110A. With the Van der Waals b correction and y = 1500 ergs per cm2, 300 ppm He would balance the surface tension of the observed cavities. Stereoscopic examination of the electron micrographs showed that the cavities were neither preferentially located near the grain boundaries nor highly concentrated at specific regions or precipitates. The cavities were nearly uniformly distributed throughout the matrix, on dislocations and at grain boundaries. These observations imply that the cavities were not the sole results of B&apos;O

Jan 1, 1969

By A. G. Metcalfe

Observations at temperature are used to investigate the phase changes in alloys containing more than 50 pct Co and above 1000°C. The nonsuppressible transformations in cobalt above 1120°C and in the intermetallic compound Co2Cr3 are studied. The liquidus and solidus surfaces are determined. Insufficient data is obtained to complete the constitution diagram. A REVIEW of some of the earlier work on cobalt&apos; and on the binary systems with chromium2-4 and with molybdenum,5 showed that one likely source of differences might be attributed to the presence of phases at high temperatures which could not be retained by quenching. Consequently, the decision was made that only methods of examination at temperature should be used in this work. The correctness of this decision was confirmed during the course of the work by the investigation of the martensitic nature of the transformation in cobalt- and by the decomposition of the high temperature form of the phase Co2Cr3 on quenching.&apos; The use of high temperature methods, including dilatometry and thermal etching led to the postula-tion of the existence of a high temperature form of cobalt with a probable hexagonal close-packed structure, transforming from cubic cobalt over a range of temperature from 1119° to 1145°C.8 One of the important pieces of evidence for this transformation was that it was observed in alloys with chromium and molybdenum which were nonmagnetic at this temperature so that confusion with magnetostriction effects was impossible. These results were not reported in this earlier paper, so that the data given here supply further evidence for the existence of a second allotropic transformation in cobalt. High temperature observations are necessarily much slower in producing results than the examination of quenched specimens at room temperature by conventional means such as X-ray diffraction or microexamination. The investigation has only covered a limited part of the field, as a result, extending from the liquidus down to about 1050°C and from the cobalt corner up to 50 pct alloying elements. The differences between the various reported diagrams for the constitution of the Co-Mo and Co-Cr systems have already been mentioned. The best available diagram in the first system is due to Sykes and Graff&apos; which is shown in Fig. 1. Fig. 2 shows the latest Co-Cr diagram due to Elsea, Westerman, and Manning.&apos; A comparison reveals that these are incompatible because of the disagreement with regard to the number of allotropes of cobalt. Elsea, Westerman and Manning took their liquidus and solidus curves from Wever and Haschimoto.2 The temperature horizontal in the two-phase field beneath the eutectic was placed 35" to 39°C higher than in earlier work2,4 with a new interpretation of the nature of this transformation. This interpretation also required a peritectic horizontal at about 1470°C, which has been confirmed here for an alloy with 53 pct Cr. No investigation had been made of the ternary system until after this work had been terminated, when a section at 1200°C was published." In this work a ternary compound was found by the X-ray diffraction examination of quenched alloys. This compound contained less than 50 pct Co, and was thus outside the field investigated here. However, some reactions were found dilatometrically which could not be fitted on the diagram and are now believed

Jan 1, 1954

By Harold Margalin, Elmars Ence

M. H. Mueller, M. V. Nevitt, and H. W. Knott (Argonne National Laboratory)—We have reported1 the crystal structure of Ti2CU as body centered tetragonal with a. = 2.944A and co = 10.786A, six atoms per unit cell, and space groupl4/mmm(MoSi2 type). This cell is larger but definitely related to the unit cell reported by the authors. It permits definite positions for the titanium and copper atoms in the cell located as follows: 2 Cu (a) 0 0 0; 1/2 1/2 1/2 4 Ti (e) 0 0 z; 1/2 1/2 1/2 + z; 0 0z; 1/2 1/2 1/2- z where z = 0.341 The face centered tetragonal cell reported by the authors can be transformed to a small body centered tetragonal cell with flo (small bet) = ao(fct)v2 Both unit cells have the same CO. Neither the face centered tetragonal cell with four atoms per unit cell nor the small body centered tetragonal cell with its two atoms per unit cell lend themselves conveniently to an orderly arrangment of the 2 to 1 ratio of titanium to copper atoms. When the co of this small body centered cell is tripled, however, a large body centered tetragonal cell results with six atoms per unit cell as described above. We had also noted that the X-ray patterns of Ti2Cu indicated that the structure could be approximately described by the face centered tetragonal cell as reported by the authors; how- ever, there was evidence for a few additional very weak lines whose positions indicated a larger unit cell. Since the X-ray scattering amplitudes of titanium and copper are nearly equal, it is evident that it is difficult to distinguish their positions especially from X-ray powder patterns. It was therefore decided to look at a powder pattern obtained by neutron diffraction since the scattering amplitudes of the two elements are considerably different in magnitude and opposite in sign. The sample used for neutron diffraction was selected from a group of three alloys prepared by arc melting using crystal bar titanium of 99.92 pet nominal purity and 99.999 pet pure Cu. The alloys designated as A, B, and C had the following respective compositions: Ti-32.8 at. pet Cu, Ti-33.3 at. pet Cu, and Ti-33.8 at. pet Cu. On the basis of the melting losses incurred, it was established that the actual concentration of either component in any of the alloys probably did not deviate from the intended value by as much as 0.1 at. pet. The alloys were annealed for 5 days at 700°C in evacuated Vycor capsules and quenched in tap water. The metallographic structures of these alloys are shown in Fig. 1. None of the alloys contained sufficient second phase to permit its positive identification. Since alloy B contained the least amount of second phase and since its composition placed it closest to the ideal stoichiometry, it was chosen for the neutron diffraction study. The oxygen content of alloy B was found by chemical analysis to be 0.06 at. pet. This particular intermetallic compound is especially suitable for investigation with neutron diffraction since if the titanium and copper atoms have a random statistical distribution, a near null-matrix would result in which there would be practically no coherent scattering of neutrons, and hence no Bragg diffraction peaks. Such a condition could come

Jan 1, 1962

By S. C. Sircar, D. R. Wiles

The rate has been studied of the hydrogen reduction of nickel ions in acetate -buffered solutions, using a nickel catalyst. At temperatures between 130°and 160°C, the rate is found to be proportional to the catalyst area, the nickel ion concentration, and the hydrogen pressure. The effect of hydrogen ions is to reduce the observed rate, likely by causing the reverse reaction (dissolution) to proceed. The experimental activation energy was found to be 25 kcal per mole. THE precipitation of metals and lower oxides from solution by hydrogen reduction has been quite actively investigated during the past few years.1 In the case of nickel, the kinetics of the precipitation have been studied in ammonia solution2 but extension of this study to acid solutions has not attracted much interest, largely because of the unfavorable thermodynamics at all but the lowest acidities. For example, Schaufelberger foundg that only 10 pct reduction of nickel could be effected in sulphate solutions. One kinetic study of the reduction of Ni++ has been reported by Knacke, Pawlek, and Sussmuth,4 in which the order of the reaction was found to be one in nickel ion and one-half in hydrogen pressure. No mention was made as to the part played by the nickel catalyst, or by the pH of the solution. Moreover, the activation energy reported (4 .12 kcal per mole) is so low as to lead to some question as to whether diffusion might be playing a major role in determining the kinetics. We have recently completed a study5 of the kinetics of the hydrogen precipitation of nickel from acetate-buffered acidic solutions whose results confirm and amplify those of Knacke et al. EXPERIMENTAL PROCEDURES The work was done in a high-pressure autoclavee by the usual technique of removing small samples of the solution for analysis. Nickel analysis was done colorimetrically by the dimethylglyoxime method.&apos; The catalyst used was carbonyl nickel powder (Standard A powder of the Mond Nickel Co., Ltd.) which was found to be composed of spheres of less than 350 mesh. The surface area of the powder was determined in this laboratory by the B. E. T. method to be 1.85 sq m (m2) per g. The catalyst was added to the solution only after the proper temperature and pressure had been reached. Agitation of the baffled system was by a turbine-type impeller, rotated at speeds between 400 and 750 rpm. The reduction rate was found to be independent of the stirring rate, so it was assumed that diffusion in the liquid does not limit the rate. In typical experiments, the nickel concentration was unchanged during an induction period of variable length. The concentration then decreased sharply, and gradually levelled off to approach the final equilibrium value. In some cases, notably at high stirring rates, the nickel concentration was found to increase considerably during the induction period, and then to decrease. In all cases, the rate was determined from the slope of the tangent to the rate curve as the concentration first decreased below the initial value. This is seen in Fig. 1. The rate measurements were found to be reproducible to within about 5 and to be quite independent of the nature or duration of the induction period. The range of conditions used is given in Table I.

Jan 1, 1961