By Qiang Zhong, Bin Xu, Qian Li, Wei Gao, Yongbin Yang, Yaxuan Wang

Lump coal with high volatility is used for providing heat and reductive gas, and ensuring permeability in COREX. However, it is apt to be pulverized in transport and storage process. Therefore, comprehensive utilization of the pulverized coal to produce coal briquettes with appropriate binders is significant, among which the molasses binder cannot meet the technological requirements. In this paper, coal tar pitch binder and BJ additive were used in briquetting and carbonizing process of coal powder. The results showed that BJ effectively activated cold state cohesiveness of the pitch and make it bond the coke particles to a firm briquette at room temperature .Carbonizations of coal and coal tar pitch achieved obvious constriction and formed a carbonized skeleton. The drop resistance of wet briquettes reached over 50 times/1meter. When cured at 1000 °C for 1h under nitrogen atmosphere, the compressive strength of carbonized briquettes came to 6.43 Mpa.

Jan 1, 2016

By M. Hashimoto

The equilibrium distribution ratios of sulfur between molten copper and CaO-fluxes containing caF2 and caC12 were determined in the range of 1300° to 1400° C under carbon monoxide. The rate of approach to equilibrium is rapid and increases with increasing CaCll concentration. In CaO-CaFl-CaCl2 fluxes, the distribution ratio varies in a complex way with temperature and CaFl concentration. The results are compared with those obtained with the binary fluxes of CaO with BaFZ and MgFl ?

Jan 1, 1983

By Tadashi Aiura, Yasuhiro Miura

"A small amount(0.2mass%) of Scandium(Sc) was added to the 7.NOl and 5083 Al alloys as a refiner and stabilizer of microstructure, and the resulting microstructures were discussed in comparison with the effects of the conventional additives. The followings are summarized: 1) in the as-solidified structure, a ·decreased tendency of constitutional supercooling and increased solubility of Mg were recognized for the Sc-added 5083 alloy. Sc is a -better microstructure refiner for the 7N01 alloy than Zr, in a sense that it does not suppress the favorable effect of· coexisting Ti. 2) Sc effectively suppresses recrystallization both in the 5083 and 7N01 alloys. 3) The rod like primary Al3Sc crystals formed during solidification, as well as the fine dispersion of Al3Sc precipitates formed by subsequent heat treatment, can act as a strong recrystallization suppresser. IntroductionThe 7N01 and 5083 alloys are the most popular industrial Al alloys and they are widely' used for various structures because of their superior properties. Fine macro and micro structures of the materials are required for obtaining acceptable sec resistance,consistent appearance of anodized surface and good weldability, as well as good mechanical properties. In order to produce fine grain structures, transition metals, such as Cr, Zr, and Mn, have been conventionally added.It has been reported that Sc is an efficient refiner [l, 2] and can be an alternative for the conventional and also suppresses recrystallization in Al alloys [3,4]. Scandium is the lightest transition element and forms an equilibrium intermetallic phase. The equilibrium phase, Ll2-Al3Sc, is coherent with the matrix, and of _spherical shape. A fine dispersion of the spherical precipitates is obtained by quenching and aging after solutionizing annealing. The authors have already reported a part of the experimental results on the effect of Sc on the as homogenized microstructure of the 5083 alloy [5]. In the present study, the effects of Sc on the macro and micro structures of the industrial high strength Al alloys(7N01 and 5083) for extrusion are investigated, and the superior role of Sc as a grain refiner is shown"

Jan 1, 2000

By Masatoshi Ogasawara

Saganoseki smelter & refinery operated two flash smelting furnaces, producing a combined 330,000 metric tons per year (hereinafter mtpy) of copper. In 1996, however, it successfully shifted to a single furnace operation while maintaining production at the same level. Since then, the production capacity has been further increased to the present 470,000 mtpy by technological improvements. Also, in order to reduce the converter load which represents a bottleneck in efforts to increase production, the matte grade was gradually increased and currently runs at 65 to 66% attaining the low copper content in the slag (hereinafter slag loss) of 0.7 to 0.8%. This paper introduces some improvements, recent operation results and thermodynamic analyses.

Jan 1, 2003

By Guo Xian Jian

In this paper, the effects of matte grade, flux grain size, blast flowrate and blast O2 content on the process of silica flux melting in a copper converter were investigated. The results showed that the blast flowrate and the blast 02 content were not significant factors in the melting process. However, with an increase in grain size of flux and grade of matte, the amount of the flux molten decreased. The data on the melt rate of process correspond well with the mathematical model which simulates the chemical reactions occurring at the interface. The kinetic equations of melting are as follow:

Jan 1, 1996

By Zdzislaw Miczkowski

At KGHM Polska Miedz S.A, a direct flash smelting process is used for smelting of chalcocite concentrate for the production of blister copper. The paper presents a model of complex oxidation process of single concentrate grains smelted at KGHM. The description covers main chemical reactions, phenomena of heat and mass exchange inside the grains and between a grain and the surrounding space. In the model, two zones describing the course of process inside the grain were distinguished: ? The first one, which moves faster towards the centre of a grain, both organic and carbonate carbon are freed, The process takes place without the presence of oxygen and results in an increase of the temperature in the core of the particle. ?The second zone moves slower into the grain and the rate of the movement is determined by the presence of oxygen, In that zone the sulphur is eliminated and the oxidation of the organic compounds vapours moving from deeper layers of a grain takes place. Based on the results of laboratory tests, the coefficients that describe the oxygen transportation into the grain and decide the progress in the chemical reaction were determined, The paper contains the results of model calculations for single grains reacting in environment of various content of oxygen as well as the results of model calculations for the laboratory reactor system.

Jan 1, 2003

By Charles H. Bucknam

A gold sampling optimization study was carried out in support of open pit gold mining operations for the Newmont Gold Company Bootstrap-Capstone deposits in Northeastern Nevada. Six bulk samples were tested using fire refining techniques at field particle size, to determine coarse particle heterogeneity of the ores, and by gravity .concentration methods at 10 mesh particle size, to observe any particulate gold liberation. An overall sampling model is presented for the deposit based on the pooled test information, to reconcile the results of coarse particle heterogeneity testing and the fine particle 'liberation testing. The sampling model is used to recommend procedures to control the variability of gold grade estimation due to the fundamental error (nugget effect) during sampling, sample preparation and assaying of the ores and other fundamental variances. The technique of simplified quantitative risk analysis (SQRA) is used to provide an economic justification for implementation of. recommended improvements to field sampling practices.

Jan 1, 1999

By Robert D. Pehlke

"Current continuous casting processes are going through a rapid evolution of advances and new developments. At the same time, intense efforts are being directed to the development of radical new technologies such as continuous casting of thin slabs and strip steel.Traditionally, the casting processes for steel have been anticipated by the development and implementation of processes in the non-ferrous industry. This trend is reviewed and what it may portend for steel is described.IntroductionThe continuous casting of steel has been a widely adopted process in the production of steel. The concepts for this processing go back into the early and mid 1800's; however, commerical development was delayed for a variety of reasons until the mid twentieth century.Beginning in the early 1960's, adoption of continuous casting was initiated and continues at this point in time to be accelerated. In Japan, more than 90% of the steel produced is continuously cast (1). More than 50% of the steel produced in the United States is continuously cast and this fraction continues to rise (2). Numerous examples can be cited of installations costing well over $200,000,000 which have provided a payoff in less than a year and a half. As this process has continued to be applied and its technology to increase, computer control systems have been installed. In particular, in the larger plants producing slabs, sophisticated computer systems involving the integration and networking of mini-computers, micro-computers, and mainframe including back-up systems at all levels are being utilized. Pehlke (3), and Harabuchi and Pehlke (4) have described the structure of these systems."

Jan 1, 1988

By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems are necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed by the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-1 to 102 Pa) at 1573K. The effect of Fe3+/Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By Preben Ingerslev

Control of the reheating of ingots is based either on surface temperature measurements using optical pyrometers or on furnace set points and reheat time determined empirically. This paper presents a real-time mathematical heat flow model, named BESTT, which calculates the temperature distribution in an ingot cross section when reheated or cooled. The model runs on a 486 PC in less than one minute for a variety of ingot cross sectional shapes such as circular, square and with some considerations octagonal and heavy-cornered square. Initial temperatures can either be uniform or nonuniform while accounting for temperature dependent thermophysical properties. The model was developed and verified using 718 alloy ingots in box type furnaces. When integrated with on-line pyrometric measurements, BESTT can provide for improved feed back in the reheating control loop. The use of BESlT will assist in reducing energy costs, and improving product quality and consistency. EPD Congress 1994 Edited by C. Warren The Minerals, Metals k Materials Sodety, 1993

Jan 1, 1994

By C. Damiani

The Chuquicamata smelter, operating since 1952, has gone through several developing stages which have been characterized by the addition of peak technology for copper concentrate smelting (Teniente converter and Outokumpu flash furnace) with an intensive use of technical oxygen, which has permit-ted to partially discontinue the reverberatory furnace utilization. This paper shows the main indicators and operational practices at present, as well as those concerning maintenance aspects. Finally, the most relevant topics related to the future development of the smelter are mentioned with special remarks on the Decontamination Plan, which allows US to keep the high level of production, reducing the emission of contaminants according to the legal requirements in force.

Jan 1, 1993

By Bao Xiancheng

Jinlong's copper flash smelting process started up in April 1997. In the early days of production, lots of equipment and process problems were encountered. But, through continuous improvements in equipment and operation, the designed productivity was reached two years later and the smelting operation has been greatly upgraded since then. After more than 4 yew of production, we have made great achievements, such as increasing the flash furnace availability, significant improvements in operation control, optimization of concentrate burner's structure and operation, and smooth operation of the whole smelter. This paper outlines Jinlong's operational achievements made after commissioning, and discusses problems that were encountered and their countermeasures. Operational experience is also summarized

Jan 1, 2002

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3-PbZrO3-Pb(Mg1/3Nb2/3)O3) system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densifieation by the normal sintering was slow even at high temperatures. When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.

Jan 1, 2003

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3 PbZrO3-Pb(Mgl/3Nb2/3)O3 system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densification by the normal sintering was slow even at high temperatures, When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.-

Jan 1, 2003

By Edward Rosenberg

The synthesis and characterization of silica polyamine composites modified with a variety of sulfur containing ligands is described. The two most successful ligands in terms of sulfur in-corporation and mercury capture are ethylene sulfide and carbon disulfide. The ethylene sulfide forms either an amino mercaptane or a polysulfide upon reaction with amino groups on the composite. The carbon disulfide undoubtedly forms a dithiocarbamate functional group upon reaction of the amino group under basic conditions. Both materials posses excellent capture kinetics and capacities for mercury, Once captured, the mercury is extremely difficult to remove from the composite materials, even with concentrated acids, and they easily pass the TCLP test. The materials are compared with related thioether modified silica polyamine composites and appropriate potential applications are discussed.

Jan 1, 2003

By Patrick R. Taylor

Ilmenite concentrate and methane are fed to a non-transferred arc thermal plasma reactor to produce a powder that is primarily TiC and Fe. This material has promising characteristics for powder metallurgy applications. Free energy minimization plots were used to predict the feasibility of the reaction. An estimate of the optimum molar ratio between the ilmenite concentrate and methane was made based on the mineral composition. Argon-helium mixtures were used as plasma gases. The effects of power input level, carrier gas flow rate, powder feeding rate, and methane-ilmenite molar ratio were studied and the behavior of the system characterized. Two different powder injection angles were tried. A mathematical model to describe the temperature profiles in the reactor was formulated and solved. The product has been characterized by x-ray diffraction and atomic absorption. A conversion of 97 % of Ti to TiC was achieved. It was found that minor amounts of titanium oxides, iron carbide and free carbon are also present. TEM and SEM were used to study the morphology.

Jan 1, 1996

The effect of change in slag composition upon metal losses to the slag and the relationship between slag composition and slag matte separation was investigated at 1400°C. The synthetic slags containing CaO, MgO, SiO2,, A1,0, and FeO were similar to those employed in the electric furnace smelting of sulphide Cu-Ni concentrates containing PGM (Precious Group Metals) from the Merensky Reef of South Africa. The matte with a grade of 9.3% Cu and 16.0% Ni was a typical electric furnace product. The results indicated that the Cu and Ni solubility in the slag increases with the increase of the basicity ratio and CaO and MgO contents of the slag. At constant CaO/MgO ratios the rise in basicity decreases the metal losses. When FeO and SiO2 contents of the slag are kept constant, the substitution of MgO with CaO decreases the metal losses. The relationship between slag composition and matte-slag separation was found to depend primarily on the basicity ratio and the FeO content of the slag. The net effect comes from a strong interaction of the two in such a way that increasing basicity and decreasing FeO contents deteriorate the clean separation of the two phases.

Jan 1, 1994

By Manuel Pérez-Tello

An experimental study on the oxidation of chalcopyrite (CuFeS2), pyrite (FeS2), covellite (CuS) and chalcocite (Cu2S) particles was conducted by means of differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) techniques. Oxygen concentration in the process gas was set to 40 and 70% by vol. and a heating rate of 40 °C/min was used. Response variables included: the temperature of incipient reaction, the total exothermic heat of reaction, particle mass, morphology, and mineralogy of the reacted particles. Based on the experimental data and phase stability calculations, reaction mechanisms were proposed to represent the behavior of the particles during oxidation. The reaction mechanisms were verified by X-ray diffraction (XRD) analyses of the oxidized particles, and by thermochemical and mass balance calculations to reproduce the DSC and TGA thermograms. Overall kinetic models were developed to represent the evolution of the exothermic heat of reaction for each mineral as a function of time. Experiments conducted with copper concentrate particles containing the minerals studied suggest that the reaction mechanisms for the individual minerals can be used to represent the oxidation behavior of the copper concentrate particles.

Jan 1, 2006

By Baojun Zhao, Zhixiang Cui, Zhi Wang

"Bottom blown oxygen copper smelting process has been developed in Dongying, China by Dongying Fangyuan Nonferrous Metals Co., Ltd. in commercial scale. This is the first modem copper smelting technology developed in China with the advantages of high oxygen enrichment, low temperature and autothermal operation. Production capacity of more than 100,000 tonnes per year of copper has been achieved through a single bottom blown oxygen furnace with instantaneous feed rates reaching up to 90 t/h. The main features of the bottom blowing smelting process are that high grade matte (up to 72 wt% Cu) can be produced at relatively low temperatures with 2-3 wt% Cu remaining in the smelting slag. Analyses of quenched smelting slag show that significant amount of magnetite crystals are present in the slags at operating temperature which indicates that the operating temperature was much lower than the liquidus temperature of the slag. After four years operation this new technology has shown great potential for expanding production capability and energy saving. Process development continues on the first commercial scale bottom blown furnace at Dongying Fangyuan Nonferrous Metals and a larger bottom blown smelting furnace is under construction.IntroductionFlash and bath smelting technologies are the major processes used in modem copper making industry [l]. Ausmelt/Isasmelt using top blown and Noranda/Teniente using side blown are typical and common bath smelting technologies. In 1980s-1990s Hunan Shuikoshan Mineral Bureau, jointly with China Nonferrous Engineering and Research Institute (now China Enfi Engineering Corp.), developed the concepts of the bottom blown oxygen processes for both lead and copper smelting [2]. After the pilot test on 3000 ton copper per year scale in 1991, it was not progressed to industrial scope."

Jan 1, 2013

By D. P. Cook, M. I. Bloch, J. A. Dantzig

"In this article, we describe a combined experimental and computational program to study the filling of automotive wheels during low pressure die casting. Experiments are performed by placing thermocouples into the mold walls of a production caster for the Ford F 113 wheel to measure the temperature profiles in the die during processing, and to infer the filling pattern. Computational models are also developed using a 36° section of the wheel pattern, taken directly from CAD data files. We use these models to simulate the filling and heat transfer processes. Comparison between experimental and computational results are presented, demonstrating the viability of this procedure.IntroductionAutomotive companies are using increasing amounts of aluminum in production vehicles: While the main driving force is improved fuel economy through weight reduction, replacing steel wheels by aluminum also offers the potential for improved vehicle performance by reducing unsprung mass. For these reasons, many new vehicles are now supplied with cast aluminum alloy wheels, and the aftermarket for these wheels continues to grow.The most common production process for these wheels is low pressure die casting. The process is subject to numerous defects, including microporosity, cold shuts, cold folds, misruns and inclusions. Scrap rates at the caster of the order of 10% are not uncommon. Many wheels also have large production runs, into the hundreds of thousands of wheels per year. Thus, the cost savings from even small reductions in scrap rate have the potential to be quite significant.Most of the defects are associated with the filling and solidification processes in the mold. The molds are air cooled, and the placement and sizing of cooling passages is currently as much art as science. The ultimate goal of this project is to improve that situation, by implementing simulation procedures that enable engineering design methods to be used in die and process specification."

Jan 1, 2000