By Yavuz Ali Topkaya

Rare earth ferrosilicide is a versatile alloy mainly used to control the detrimental effects of sulfur in steel and to modify graphite structures in cast iron. The aim of this study was to determine the optimum conditions to make rare earth ferrosilicon alloy using a preconcentrate produced from a bastnasite type of ore present in the Beylikahir-Eskisehir region of Turkey. This concentrate contained 23.5%REO, 41.37% CaF2, 10.69% BaSO4, 8.50% CaCO3, 4.18%Fe2O3, 2.83% Al2O3, 2.74% SiO2, 1.20% P2O5 and small amount of other oxides. The initial metallothermic reduction of this concentrate using ferrosilicon and aluminum in a graphite crucible placed in a muffle furnace gave very low recoveries due to the difficulties encountered in adjusting the slag composition, temperature and amount of additives. Therefore, two batches of rare earth oxide concentrate containing 61.1% and 81.7% cerium oxide, respectively, that were procured from a Turkish glass producer, were used to optimize with respect to temperature, duration, slag-making additives and amount of reducers. In these experiments, smelting and reduction was done in an induction furnace with graphite crucible, and, ferrosilicon and aluminum were added after melting the charge. As a result, there was no difficulty in obtaining a rare earth ferrosilicon alloy containing 35-55% RE, 5-25% Fe and 20-40% Si, with about 80% metal recovery. When the optimum conditions were applied to the preconcentrate, alloys of similar compositions were obtained with 70-80% recovery. Experiments were also done with mixtures of preconcentrate and rich concentrate, and, recoveries as high as 95% were obtained. Only in this case, to increase the recovery, mixtures had to be charged to the empty graphite crucible after heating the crucible to the required temperature.

Jan 1, 2006

By William K. Connor, O&apos

The U.S. Bureau of Mines (USBM), in cooperation with the American Society of Mechanical Engineers (ASME), conducted over 200 hours of melting tests to vitrify residues from five municipal waste combustion facilities. Combined residues (grate residue and f1yash) from three municipal waste combustors, a waste water treatment sludge combustor, and flyash from a refuse-derived-fuel (RDF) boiler, were sequentially melted in a I-metric-ton (mt) water-cooled-wall electric arc furnace. Each of the residues underwent magnetic separation, screen size analysis, and bulk chemical analysis prior to melting. The furnace products were examined by optical and electron microscopy and by X-ray diffraction. Bulk chemical analyses were acquired for the metal, fume, and vitrified furnace products. The material balance for the furnace operation indicates that from 69 to 86 pct of the feed reported to the vitrified furnace product, which had leaching potentials well below the EPA limit for each metal, as determined by the EPA TCLP. The electric arc melting furnace currently is being utilized in a cooperative research project between the USBM and the Idaho National Engineering 'Laboratory (INEL) for melting tests on simulated low-level radioactive wastes,

Jan 1, 1991

By Ryo Sasai, Takeshi Itakura, Haruki Imaizumi, Hideaki Itoh

"Emission of industrial wastewater containing harmful oxoanions is one of the serious problems on account of its toxicity and the environmental pollution, especially caused by boric, phosphinic, arsenic and antimonic species. In this study, we developed a novel treatment technique of such polluted-water by hydrothermal mineralization. The treatment is “Geomimetic” method for precipitating oxoanions in aqueous media as natural ore resources by using hydrothermal treatment with calcium salts mineralizer. The treatment made it possible not only to detoxify the polluted-water, but also to recover the calcium minerals such as Ca2B2O5·H2O, Ca5(AsO4)3(OH), etc. Concentration of each ion in treated-water was lower than that of effluent standard in Japan. Moreover, the residual concentration of each ion was independent of the initial concentration, but it depends only on the solubility of the formed mineral under hydrothermal condition. Therefore, the hydrothermal treatment could be recommended as one of the treatment techniques of polluted-water.IntroductionVarious oxoanions such as boron and arsenic oxo-anions have high toxicity against human health and the environment. They are important resources, however, for plating or advanced material manufacturing industries[1-3], from which the wastewater containing these oxoanions is generated every day. An appropriate treatment is often required for industrial wastewaters to attain national effluent standards of Japan (NESJ, B: 10 mg/dm3, As: 0.1 mg/dm3). On the other hand, there is no production of arsenic and boric resources in Japan, and they are expected to be recycled. Therefore, the establishment of a system for the removal and recycling of arsenic and boron from wastewaters is of global significance.Several methods to remove them from aqueous media have been already reported by using adsorption[4], electro-coagulation[5], membrane separation[6-8] and biological techniques[9]. However, these methods have the following problems because of their stability in water. (1) Removal yield is low, especially for tri-valent arsenite ion (AsIIIO3 3-) and borate ion. (2) The applicable concentration range is narrow. In addition, the used adsorbents or collected residues after treatments are sill hazardous wastes, so that they must be treated by a proper method. But, it is very difficult to convert them to recyclable resources at most industrial plants. These problems are caused by the difficulty to recover these oxoanions as stable solid precipitates with low solubility in water. The establishment of recycling system of these hazardous compounds will be one of the world-important issues, especially, in Japan, which is poor in natural resources. On the other hand, compounds that contain high arsenic concentrations and are insoluble in water, are often found in natural minerals, for example, as haidinglite (Ca(AsO3OH)·(H2O) or Johnbaumite (Ca5(AsO4)3(OH)). This fact suggests that nature has an ability to produce insoluble As-bearing minerals. Similar phenomena can be found in case of boron, antimony, etc."

Jan 1, 2008

By Wen-Ming Chien

Keywords: AN-KN Phase Transition, Lattice Parameters of AN-KN, X-ray Diffraction The lattice parameters of the low and high temperature phase of KNO3-rich (in NH4NO3) solid solutions have been determined by the X-ray diffraction method. The low temperature single KNO3 phase (KN II) are from 92%-100% KNO3 in NH4NO3 composition range and from room temperature to 393 K showing in X-ray diffraction patterns. The high temperature KNO3 phase (KN I) showed very broad composition range between 20% to 100% KNO3. The lattice parameters of KNO3-rich (KN II and KN I) solid solutions have been calculated at different temperature range. The volumes of orthorhombic KN II phase decrease from 0.3208(3) to 0.3195(3) nm³ at the room temperature as the compositions increase from 95% to 100% KNO3. The lattice constants of the hexagonal KN I phase show that there is no significant change in a-direction when the temperature increases. Details X-ray results and lattice expansion equations during heating will be presented.

Jan 1, 2005

By M. A. Barakat

"Adsorption of heavy metal ions specifically, Cu(II), Zn(II), Mn(II), and Cr(VI) from aqueous solution on synthetic 4A Zeolite was evaluated. The 4A zeolite was synthesized previously by dehydroxylation of low grade Kalabsha Kaolin at 800 °C, and reacted hydrothermally with 2-4 M NaOH solution at 100 °C for 2h. The adsorption capacity of the metal ions were found to be strongly dependent on pH and initial metal ion concentration. At the optimium conditions the adsorption capacity decreased in the order Cu(II) > Zn(II) > Mn(II) > Cr(VI) ions. Almost complete adsorption was achieved for both of Cu(II) and Zn(II) ions at pH > 6, while the adsorption capacity for both Mn(II) and Cr(VI) was 96, and 55.3 % at pH 11 and pH 3, respectively. The results also showed that the grain size of the 4A zeolite has a little effect on the adsorption capacity. The experimental data was compared with two adsorption isotherms, Langmuir and Freundlich isotheroms. The results showed a good agreement of the Langmuir plots with the experimental data.1. IntroductionSeveral industrial wastewater streams may contain heavy metals such as Cr, Cu, Pb, Zn, Co, Ni, Mn, etc. including the waste liquids generated by metal finishing or the mineral processing industries. Heavy metals are considered hazardous pollutants due to their toxicity, even at low concentration, and nonbiodegradability. Increasing level of heavy metals in natural water bodies poses a serious threat to all living species including humans. It is, therefore, essential to reduce the heavy metal concentration in effluents/wastewater before it is discharged into the water bodies [1]."

Jan 1, 2008

By S. C. Sharma, M. Krishna, N. Sanmukha

"The oxidation behavior of an aluminium composite with 0, 2, 4, and 6% by weight of hematite at 200 to 500 °C has been investigated. Within the experimental temperature ranges a parabolic weight gain was observed. The, weight gain as a function of oxidation time becomes linear after an initial period on oxidation formation, an oxide scale was found whose morphology depends on temperature, cooling rate and sub-scale formation at the interface between the matrix and reinforcement. The presence of hematite particulate reinforcement has very little effect on the oxidation behavior. The interface oxidization rate was found to be higher than that of other regions. The, oxidation products were either metallic oxides or ceramic oxides. The exposure time of specimens to oxidation was 1000 minutes at various temperatures. In the present work key principles of alloy oxidation were discussed. Also the paper emphasizes various reactions taking ' place and the activation energies involved in the oxidation reactions.IntroductionMetal matrix composites (MMCs) reinforced with ceramic particulate, whiskers, or fibers have received increasing attention due to their potentially high fracture toughness and strength 1-5. Particle reinforced Aluminium MMCs find potential application in several thermal environment, especially in the automobile engine parts, space applications, such as drive shafts, cylinders, pistons, and brake rotors6.With the exception of gold, no metal or alloy is stable at room temperature, they tend to form their respective oxides. Most of the metals in the solid or liquid state are morphologically unstable when exposed to air at higher temperatures. An investigation relating to the temperature profiles of the piston area in a diesel engine has shown that the temperature can reach as high as 500¬800 K in certain regions of the piston. As the piston and cylinder areas are exposed to high temperature environment, the MMCs should have sufficient stability on both mechanical and chemical strength (oxidation). Oxidation occurs at grain boundaries in alloys and at the interface of the particulate and matrix in MMCs, which usually enhances intergranular fracture, resulting in premature failure and severe brittleness 8-10. Therefore for high-temperature applications, it is essential to have a thorough understanding of the oxidation behavior of aluminium MMCs."

Jan 1, 2000

By Pengfu Tan

Converter slag chemistry control has played an important role in optimizing converter operations. A thermodynamic model of copper P-S converter has been developed to predict the behavior of magnetite in the converter slag. Predictions of bath temperature, slag and matte compositions, and magnetite content in the slag have been validated by industrial data. The effects of fluxing strategy, returns and skim charges, oxygen enrichment, and temperature on the magnetite formation in the slag have been predicted and discussed. Some improvements of the industrial operations have been presented.

Jan 1, 2005

By Wang Shulan

The synthesis process of BaTiO3 from TiO2 and BaCO3 in the molten NaOH-KOH at 350oC was studied by the A.C impedance technique. The A.C. impedance of molten NaOH-KOH (xNaOH = 0.36) and the variation of the conductivity of the salt with time during the synthesized process were measured. The synthesized reaction of the BaTiO3 and the decomposition reaction of BaCO3 are fast and were finished in 10min. The interaction between TiO2, BaO and BaTiO3 and the molten salt was confirmed by the variation of the conductivity.

Jan 1, 2005

By P. N. Anyalebechi

The effects of Si (0.19-0.52 wI. %), Fe (0.20 wI. %-0.44 wI. %), and Cr (0-0.10 wI.%) on the response of ingots of aluminum alloy 3004 solidified at different rates (O.IO°C/s to 30°C/s), to homogenization heat treatment have been investigated. Response to homogenization was determined by quantifying the following microstructural parameters: (i) amount of Mn retained in solid solution; (ii) types, relative amounts, sizes, size distributions, shapes, and chemical compositions of second phases; (iii) extent of the alpha-transformation (i.e., AI6(Fe,Mn) --7 (XAI12( Fe,MnhSi) reaction; (iv) dispersoid formation; and (v) alleviation of dendritic microsegregation. Of the three alloying elements investigated, Si had the greatest effect on the response of aluminum alloy 3004 to heat treatment. Increase in Si content, fineness of cast microstructure, and homogenization temperature facilitated alpha-transformation reaction, dissolution of Mg2Si, loss of Mn supersaturation, and formation of AldFe,Mn)3Si and Mg2Si dispersoids.

Jan 1, 2008

By Wenshan Zhang

Three important methods of removing Fe in hydrometallurgy of zinc, manganese, copper, nickel, cobalt and etc are described, including neutralized hydrolysis method, jarosite method and goethite method. The reactions, technical requirements and thermodynamic analysis during Fe removal process are also discussed in this paper.

Jan 1, 2006

By Sayavur Bakhtiyarov

Keywords: Rheology, Viscoelastic, Oil In this paper we present the results of the rheological property measurements on viscoelastic composite materials used in oil industry. Laboratory experiments were carried out to determine important thermophysical, rheological and mechanical properties of the test materials using both the standard commercial and in-house made equipment. The composites with the paramagnetic particles (?-iron oxide) are exhibited a significant magnetic memory after magnetic treatment. The measured value of the yield stress after the magnetic treatment increased almost twice in comparison with the yield stress value of the magnetically untreated composite. The yield stress of the composite material exponentially decreases with time and reaches its magnetically untreated value after 15 hours. The yield stress also increases with the amount of the paramagnetic powder additive, and it reaches a maximum value at 8 wt-% of this additive. The obtained results provide valuable information for computer modeling of the viscoelastic fluid flow in pipes of complex geometry.

Jan 1, 2005

By María Eugenia Castro, Silvia Galasso, Jorge Duca, Claudia Osuna, Ernesto Esparza

"We present a procedure for treatment of non-active solutions equivalent to the solutions obtained from dissolution of ionic exchange resins used in purification of a nuclear reactor primary cooling system containing Co, Ni, Cs and its isotropic varieties as main radioactivity source. Finally it is immobilized into a ferritic matrix by calcination which avoids its future leaching into environment.In order to achieve the objective of this treatment, a bivalent and a trivalent iron salt is added to the solution. Then, either a base or an acid is added, depending on the initial pH of the treated solution, with a Cs precipitating additive in order to reduce Co and Cs by precipitation, flocculation and adsorption. Controlling the amount of precipitating reactives it is possible to modify the activity/volume rate becoming a medium into a low radioactivity waste.The leaching test result applied over the ferritic sample is lower than the minimum limit established by law. Therefore, it can be kept safely in a interim storage."

Jan 1, 2008

By Ryan Walton

The Flash Converting Furnace at Kennecott Utah Copper converted over 465kmt of high-grade matte in 2002 but was restricted due to low matte production to 395kmt in 2003. This paper presents updated operational performance data and describes improvements implemented since the mid 2001 rebuild. Matte burner feed distribution, silica and arsenic impacts on settler lime-based slag operability, blister laundering, uptake/boiler accretion control, and dust sulfation will be discussed, as well as current development requirements dictated by operational imperatives and furnace modification plans.

Jan 1, 2005

By Ji-He Wei

Keywords: stainless steel, AOD refining, side and top combined blowing, mixing characteristics, water modeling The fluid mixing characteristics in the bath during the side and top combined blowing AOD (argon-oxygen decarburization) refining process of stainless steel have preliminarily been investigated on a water model unit of a 120 t AOD converter. The geometric similarity ratio between the model and its prototype (including the side tuyeres and the top lances) was 1:4. On the basis of the theoretical calculations for the parameters of the gas streams in the side tuyeres and the top lances, the gas blowing rates used for the model have more reasonably been determined. The influence of the tuyere number and position arrangement, and the gas flow rates for side and top blowing on the characteristics has been examined. The results demonstrated that the liquid in the bath underwent vigorous circulatory motion during gas blowing, without obvious dead zone in the bath, resulting in a well mixing effectiveness. The gas flow rate of the main tuyere had a governing role on the characteristics, a suitable increase in the gas flow rate of the subtuyere could improve mixing efficiency, and the gas jet from top lance could make the mixing time prolong. Corresponding to the oxygen top blowing rate specified by the technology, a roughly equivalent and good mixing effectiveness could be reached by using six side tuyeres with an angle of 27 degrees between each tuyere, and five side tuyeres with an angular separation of 22.5 or 27 degrees between each tuyere. The relationships of the mixing time with the gas blowing rates of main-tuyeres and sub-tuyeres and top lance, the angle between each tuyere, and the tuyere number have been obtained.

Jan 1, 2005

By N. L. Piret

In copper smelting minimization of solid waste generation is receiving increased attention with more stringent environmental legislation and lower disposal space availability. Copper smelting slags generally being valorizable, solid waste generation is attributed to the presence in the feed of unvalorizable impurities which do not report to the slag and to the unavoidable formation of contaminated dilute acid solutions which need neutralization. As to unvalorizable impurities, solid waste minimization is achieved by rejecting them in the highest possible concentration. Dilute acid is mainly due to the formation of SO3 in the smelter gases and to the discard of decopperized bleed-off electrolyte. Its generation is substantially lowered by preventing SO3 formation, by converting the dilute acid to a valorizable product, e.g., by thermal decomposition for H2S04 recovery or by precipitation as chemical gypsum, and by suitable treatment of the bleed-off electrolyte for impurity removal. Industrial processes are evaluated and alternatives are discussed.

Jan 1, 1994

By Elli Nurminen

Keywords: Thermal conductivity of sulphates, flash smelting, heat recovery boiler, flue dust Accretions and build-ups in metallurgical heat recovery boilers decrease the efficiency of the heat transfer and may cause process shut downs. Transient plane source method (Hot Disk) has been applied to measure the thermal conductivities of the Copper Flash Smelting flue dusts. Thermal conductivities of copper, iron and zinc sulphates, and process flue dusts were measured. The results indicate that all the components are effective thermal insulators, having a thermal conductivity of less than 1 W/mK. Decreasing dust layer porosity has an increasing effect on thermal conductivity. Insulating layers on the boiler walls decrease greatly the heat transfer efficiency of the boiler. The gathered information will be used in CFD-modelling of the process, and in the process control.

Jan 1, 2005

By Courtney A. Young

Cyanide is a critically important chemical to the mining and metallurgical industry. It has a strong affinity for metals making it favorable as an agent for metal finishing and treatment as well as a lixiviant for metal leaching, particularly gold. These technologies are environmentally sound but, because cyanide is very toxic, safeguards are required to prevent accidental spills and treat effluents before being discharged. Various methods of cyanide remediation by separation and destruction for cyanide management purposes are therefore reviewed. The methods have been broadly categorized as physical, -adsorption. complexation and oxidation methods including photolysis and other advanced-oxidation processes. Reaction mechanisms for these methods are presented throughout this paper, Finally, the methods are compared in regards to their effectiveness in treating various cyanide species: free cyanide, thiocyanate, weak-acid dissociables, and strong-acid dissociables.

Jan 1, 1998

By Andrew Wessman

Keywords: Recycling, Electrodeposition, Recovery, Dilute, Dissolved Metal Ions In order to facilitate the recovery of pure metals from solutions containing a mixture of dissolved metal ions, a pulsed electrodeposition method was developed. Using this method, it is possible to selectively remove metal ions from solution based upon the electrochemical potential of the particular ion desired. The use of pulsed electrodeposition rather than direct current electrodeposition creates an electrodeposited material with better morphology, increases electrical efficiency of the process, and avoids problems with short circuiting between electrodes. Using this method, it is possible to recover dissolved metal ions in a purified form in one simple step, and therefore maximizes recovery of the metal ions while obtaining them in a saleable form. This method is likely to be useful in improving the recycling process for numerous complex metal mixtures and alloys.

Jan 1, 2005

By Valery M. Paretsky

The effect of the degree of nickel oxide reduction and the reaction gas composition on the furnace productivity has been estimated by computations and the established relationship is in good agreement with the practical data obtained in the process of electric smelting at the Severonickel smelter. An increase in the reduction degree within a range of =0.65 - 0.9 results in an increase in the furnace productivity by 19% to 37% and in a decrease in the unit electric power requirement by 16% to 27% depending on the reaction gas composition. The agreement between the computed and practical data has confirmed that the decisive factor for the process of treatment of reduced nickel oxide in an electric-arc furnace under the given conditions is the specific heat absorption, which is dependent on the nickel oxide reduction degree and the reaction gas composition.

Jan 1, 2005

By Melissa L. Trapani

Keywords: Copper, Taphole, Flow Instability. ?Blister spitting? is a flow irregularity where the molten blister copper stream ? or part thereof ? sprays from the taphole exit rather than following a regular flow profile to the collection box. As well as being a general ?housekeeping? issue, the unpredictable nature of the flow is a threat to operator safety. Also, the aggressive flow pattern may contribute to the mechanical wear of the taphole refractory, compromising the integrity of the taphole. This paper brings together a collection of first-hand observations and reports from process personnel, and suggests some theories as to the causes of blister spitting.

Jan 1, 2005