By J. F. Evers, S. Sadiq, F. W. Preston, G. W. Swift

Proper scaling of unsteady-state flow in laboratory gas reservoir models can be achieved if the permeability/fractional porosity ratio is less than 0.5 md. Porous media meeting this specification can be obtained from mixtures of sand and Portland cement provided (1) the water/cement ratio is in the range of 0.35 to 0.40, (2) the sand/cement ratio is in the range of 1/1 to 2/1, (3) the sand grain size is in the range of 48-100 to 18-28 mesh, (4) the mortar curing time is 7 days or more and (5) the cured mortar is dried under vacuum to reduce the temperature level employed during the drying process. The areal homogeneity of the mortars tested is reasonably good, although significant trends in vertical permeability were noted. The Klinkenberg and non-Darcy coefficients of mortar are such that proper scaling of these effects in the laboratory model could be expected. INTRODUCTION A long term deliverability prediction for a gas well is generally based on data determined from flow tests that are of short duration relative to the producing life of the well. These data, together with an estimate of gas reserves in place, form the basis for establishing the parameters of the mathematical model used to predict performance at future times. Results obtained from a mathematical model represent only an interpretation of the physical process being modeled. Experimental verification of the production process from discovery to abandonment is needed where production occurs under carefully controlled conditions. Ideally, one might consider such an experiment to be conducted in the field. Even if the cost of such an experiment could be justified, the time required would make it impractical to consider. However, if the time scaling problem could be handled properly, an experimental model of the gas reservoir production process could provide the necessary data to study the mechanisms of the production process in a reasonable time period. An experimental model has been designed and constructed using the data of this study as a basis. The model reservoir system consists of one producing well located at the center of a right-circular cylinder of porous material. Ten to 15 observation wells are located at strategic offset positions from the producing well. These wells, and the producing well, are fitted with pressure transducers so that the pressure-time history can be recorded at various radial and azimuthal positions in the drainage area during the entire production life of the system. Time is scaled in the model so that the time required to produce gas from discovery pressure to abandonment pressure is about 2 hours. This compares with a 20-year producing life in the model's field counterpart and gives a time scale factor of approximately 1:100,000. DESIGN CRITERIA To establish design criteria for the experimental model, the reservoir is considered to be a finite right-circular cylinder of radius rr, and height h with a producing well of radius rw located at the center and completed through the producing formation. This reservoir consists of a porous medium which has a uniform permeability k and gas porosity and the gas contained in the reservoir has density p, viscosity µ and molecular weight M. Initially, the pressure at all points within the reservoir is uniform at po. and the reservoir temperature is T. Since the reservoir production process has been demonstrated to occur in two distinct transient modes for either Darcy or non-Darcy flow,l it is

By J. L. Zakin, G. K. Patterson, J. M. Rodriguez

Correlation has been obtained between drag-reducing characteristics for turbulent flow in a pipe and measurable properties of several polymer solutions. Several concentrations of high molecular weight polymethyl methacrylate in toluene, high molecular weight polyisobutylene in both toluene and cyclohexane, medium molecular weight polyisobutylene in cyclohexane and benzene and low molecular weight polystyrene in toluene were studied. Data obtained in these nonpolar solvents and literature data for more polar solvents were successfully correlated as the ratio of measured friction factor to purely viscous friction factor vs the modified Deborah number vrl/D0.2 where 71 is the first-mode relaxation time of the solution estimated by the Zimm theory. A shift factor which is a function of intrinsic viscosity 1/(4[?] - 1) allowed all the data obtained with nonpolar solvents to be correlated as a single function. For these systems, most of the data fit a single curve to within + 5 percent of the average friction factor ratio. The shift factor did not give a unique function of the data for the more polar systems. INTRODUCTION The phenomenon of drag reduction in polymer solutions was first studied by Toms1 in dilute solutions of polymethyl methacrylate in mono-chlorobenzene. The drag ratio for flow through circular tubes has been defined2 as the ratio of the pressure. drop of the solution to the pressure drop of the solvent at the same flow rate. The drag ratio is less than 1.0 for a drag-reducing fluid. Practical use of drag reduction is being made in fracturing operations in the petroleum industry.3 A more fundamental quantity is the friction factor ratio, defined as the ratio of the observed pressure drop to that predicted for a solution of the same viscosity characteristics and density at equal flow rates using the Dodge-Metzner friction factor equation4 Viscous solutions with drag ratios greater than 1.0 can have friction factor ratios less than 1.0. For practical applications, it is drag reduction which is of interest. However, for correlation the fundamental ratio is the friction factor ratio. In recent years, drag reduction has been studied extensively. Recent studies have shown that reasonable predictions of the incipience of drag reduction in polymer solutions can be made from the properties of the solutions and the flow Variables.5 However, it has not been possible to predict accurately the amount of drag reduction to be expected for a given polymer solution without any drag-reducing turbulent flow data on the same solution.6 For flow through circular tubes it is well established that there is a concentration effect and a diameter effect on drag reduction. Toms1 observed that drag reduction increases with an increase in the concentration of the solution up to an optimum concentration beyond which, due to the increased viscosity of the solutions, the drag ratio increased with an increase in concentration. Hershey 7 observed that for dilute Newtonian polymer solutions in nonpolar hydrocarbon solvents, a normal transition region may be obtained followed by a departure from the von Karman equation (on a friction factor-generalized Reynolds number chart). The point of departure is a function of diameter: the smaller tubes depart at the lower Reynolds numbers. Concentrated solutions may show no abrupt transition region, but merely an

By E. A. Elevatorski

Wollastonite, named after William H. Wollaston, an English chemist, is a calcium metasilicate, CaSiO3. It has a short history as an industrial mineral. The earliest production of wollastonite is reported to be from a deposit near Code Siding, located north of Randsburg, Calif. At this locality small tonnages of wollastonite were quarried during 1933-34 and 1938-41, and processed into mineral wool. This operation was largely experimental and virtually no United States production was again reported until the 1950s when a large deposit near Willsboro, N.Y., was developed by the Cabot Corp. A processing plant was placed on-stream in 1953, with nearly continuous production to date, and it is currently operated by Interpace Corp. Since 1958, wollastonite deposits in the Little and Big Maria Mountains of Riverside County, and in the Panamint Range of Inyo County, both in California, have operated intermittently for production of both ornamental and commercial wollastonite. During 1973, the United States was the major producing country, furnishing about 75% of the world's output. Recent production also has come from Finland, Mexico, and Kenya. Small amounts have been shipped intermittently from India, USSR, New Zealand, Republic of the Sudan, Republic of South Africa, and South-West Africa. The principal use of wollastonite is in the manufacture of ceramics, especially wall and floor tiles. Other uses are for paints, fillers, adhesives, reinforcing agents, plastics, fluxes, and glazes. Mineralogy Pure wollastonite, CaSiO3, has the composi¬tion of 48.3 % CaO and 51.7 % SiO,. However, it is seldom found in the pure state due to the ease with which it takes into solution the metasilicates of manganese, magnesium, iron, and strontium. Predominantly, wollastonite occurs as a contact metamorphic deposit forming between limestones and igneous rocks. Commonly associated minerals are garnet, diopside, epidote, calcite, and quartz. It has a specific gravity of 2.8 to 3.0, and hardness of 4.5 to 5 on Mobs' scale. When pure, it has a brilliant white color, but with impurities it may be grayish or brownish. Luster is vitreous to pearly. Melting point of wollastonite is about 1540° C. Wollastonite occurs in coarse-bladed masses, rarely showing good crystal form. It is usually acicular or fibrous, even in the smallest of particles. The most unique property of crushed and ground wollastonite is its cleavage. Fragments of crushed wollastonite tend to be needle-shaped, imparting a high strength, and this property is the basis for many of its uses. The fiber lengths are commonly in the ratio of 7 or 8 to 1, length to diameter. Some crystals of wollastonite fluoresce under short-wave or longwave ultraviolet light, or both; colors ranging from yellow-orange to pink-orange. Specimens may also show phosphorescence. The brightness of wollastonite is a property of considerable importance to the paint industry. Material, 99% pure, with a size of -325 mesh, has a General Electric reflectance rating of 92 to 96%. Chemically, wollastonite is inert and this property makes it useful as a filler and reinforcing agent. There are two polymorphs of calcium silicates: wollastonite, a low temperature form, and pseudowollastonite, a high temperature form. Inversion of wollastonite to pseudowollastonite occurs at about 1120° C, resulting in an increase in the coefficient of expansion and a color change. Pure white wollastonite, on inversion, may change to a cream tint, or various shades of red or brown. The color change is thought to be due to the presence of iron and strontium.

Jan 1, 1975

By D. G. Westlake

Resistance was measured as a function of temperature, 77° to 350°K,for niobium with hydrogen concentrations up to 3.76 at. pct. Cooling curves exhibited a discontinuity in slope that was attributed to the initiation of hydride formation. A thermal hysteresis was explained in terms of diffusion and the effects of mechanical constraint on nucleation and growth. The heat of solution of hydrogen in saturated Nb-H solid solution was 2. 737 * 0.045 kcal per g-atom, including an unknown stress contribution. The critical ternperatures for hydride formation during cooling and for embrittlement are correlated but not coincident. This, too, has been explained in terms of mechanical constraint and stress-itlduced tratzsfomtation. Nb-H alloys undergo a ductile-brittle transition with decreasing temperature.'-3 Similar behavior has been noted for v-H.1,5 For the latter system, there is evi-dence6 suggesting coincidence of the temperature of minimum ductility and the critical temperature T, for initiation of metal hydride precipitation during cooling. A decrease in ductility due to the presence of brittle hydride particles is readily explainable. The fact that ductility begins to decrease at some temperature higher than T,4,5 has led us6 to suggest that precipitation may be strain-induced locally during tensile testing. Wood and Daniels' have reported that a plot of temperatures for 10 pct reduction in ductility vs hydrogen concentration in niobium is not coincident with, but parallels, the solvus.7,8 They believe this indicates a correlation of precipitation and embrittlement. Unfortunately, the two reported solvuses 7,8 to which Wood and Daniels refer are not in agreement with each other. Furthermore, neither solvus was determined experimentally: each was a plot of calculated solubilities. Thus. neither is highly dependable for determining whether embrittlement coincides with initiation of hydride precipitation. Longson 9 studied phase relations in the Nb-H system between 77° and 473°K by dilatometry. Comparison with metallographic observations convinced him that discontinuities in the slopes of his dilatometric plots were coincident with the initiation of hydride precipitation. Plotting the logarithm of the hydrogen concentration vs the reciprocal of the temperature at which precipitation was initiated during cooling, he obtained a straight line shown in Fig. 1. Walter and chandler,'' using X-ray techniques to detect the for mation of a second phase? have obtained three experimental points in the temperature range 295° to 338°K which fall within Longson's experimental error for this plot. A similar plotg of temperatures at which dissolution was completed during heating was a parallel line shifted toward higher temperatures. A straight-line plot was obtained, also, for the temperatures of the ductile-brittle transitions,9 but it was shifted toward still higher temperatures. Longson calculated an activation energy of 2.980 * 0.300 kcal per mole for the hydrogen embrittlement mechanism, compared with 3.180 * 0.400 kcal per mole for hydride formation. Despite this agreement, he concluded, "It seems unlikely that embrittlement results from hydride formation..." because hydrogen embrittlement was observed at temperatures above the solvus. It is our contention that embrittlement is correlated with precipitation of the hydride.6 Because only Longson has investigated Nb-H phase relations at sub-ambient temperatures, we deemed it advisable to re-determine the temperature dependence of the solubility using the resistometric technique already proven successful for the V-H system.6 Coincidence of our solvus with temperatures for embrittlement would

Jan 1, 1970

By R. DiBella, H. Biloni, G. F. Bolling

A study of the detailed relationship between solidification substructure and microsegregation in dilute tin alloys has been continued. New observations reveal that depressions form at the solid-liquid interface not only as an initial form of segregation but throughout the range of increasing constitutional supercooling. In order to show the importance of this node formation it proves convenient to make two simplifications. Although substructure changes continuously as constitutional- supercooling increases,&apos; the following discrete stages may be used for discussion: 1) the planar solid-liquid interface; 2) ordered nodes, or depressions at the interface;&apos; 3) two-dimensional or elongated cells;3 4) regular or hexagonal cells;4 5) distorted cells, or hexagonal cells with branches;4 6) dendrites. It is also convenient to ignore observations made near grain boundaries which interact with the cellular substructure.2-4 And, it should be clearly pointed out that all singular depressions at the solid-liquid interface will be called nodes. Heretofore, the term "node" has been used without clear justification to describe both the truly isolated depression and the junction of cell walls appearing in a later stage of segregation. This usage is continued because it seems proved by the observations. Standard systematic growth of tin crystals was undertaken over a broad range of constitutional supercooling using various added solutes. Except for one or two chance observations, this research failed to reveal any appreciable range of growth conditions over which a disordered array of isolated nodes exists. Even though &apos;some finite range of random instability must exist, it is now concluded that stage one passes very rapidly to stage two. Next, after confirming that stage two passes to stage three by the elongation of isolated nodes: a reexamina-tion of stages three, four, and five followed. Standard metallography showed that pockets of higher solute concentration (for ko < 1) became more numerous in cell walls the more severe the growth conditions. These high-concentration regions must arise from depressions; however, in stage three their segregation is not distinguishable from the segregation of the nodes which join cell walls together. It seems, therefore, that the presence of nodes is causal in the formation of new cell walls, and that the mechanism by which stage three passes to stage four is initiated by nodes. If a similar reasoning is followed, the separation of stage four from stage five appears to be just a convenience that has arisen from the decanted interface observations made in the past. The present observations again show that more severe growth conditions relate directly to an increase in the number of nodes in the hexagonal cell walls. These nodes apparently serve as the origin for lines of segregation extending within the body of a cell, and can thus be assumed to represent the earliest form of branching,* as shown here in Fig. 1. The examination of stage six involved decanted-interface structures as in Fig. 2, which are similar to those considered by Rutter and Chalmers,5 Plaskett and winegard,6 and Hellawell and Herbert,7 and where distinct protrusions are each surrounded by a depressed boundary. The corresponding microsegregation behind the interface, but not far enough behind to allow a smearing of the segregation because of diffusion,4 is shown in Fig. 3. Both the shape of the decanted interface and the segregation pattern behind it

Jan 1, 1968

By J. Paces, E. Miller, K. L. Komarek

The resistivity was determined as a function of temperature over the composition range from pure cadmium to 40 at. pct Cd. Melts with cadmium contents less than 85 at. pct had negative temperature coefficients of resistinity. On cooling below a transition temperature close to the liquidus temperature, the slope of the resistivity-temperature curve changed sharply. The activation energy calculated from the slope was 0.07 ev above the transition temperature and 0.14 ev below. The resistivity vs composition curve shows two maxima corresponding in composition approximately to CdSb and Cd3Sb2. THE relationship between the structure of a liquid and that of the crystal formed on solidification is at present not well-under stood. Various experimental determinations of the properties of liquids indicate that deviations from random atomic arrangements in liquids occur and that the properties of a solid and of its melt are closely related. Thermody-namic activities of liquids usually show negative deviations in systems where compound formation occurs in the solid,&apos; and X-ray data indicate that close-packed solids and their melts frequently have nearly the same coordination number. Electrical resistivities and viscosities of liquids frequently exhibit maxima at compositions corresponding to compounds in the solid state. It should be of interest to study systems which have both stable and metastable compounds in the solid, and to determine if the short-range order in the liquid is affected by the existence of the metastable solid phase. The Cd-Sb system exhibits such a metastable phase. The phase diagram is shown in Fig. 1.3 The stable system has one intermetallic compound, CdSb, crystallizing in the orthorhombic crystal structure, with a melting point of 456°C. The metastable system also has one compound, Cd3Sb2, melting at 420°C and crystallizing in the monoclinic structure. Metastable alloys transform to the stable crystal structure in the temperature range from 250o to 350°C. Several distinct indications of very strong short-range order in the liquid phase have been reported in this system, with a close relation between the ordering in the liquid and the existence of both the stable and metastable solid phases. Scheil and Baach4 have observed distinctly different vapor pressures for liquid Cd-Sb alloys depending on whether the liquid solidified to the metastable- or stable-phase configuration. They observed an unusually sharp increase of the activity in a limited temperature interval immediately above the liquidus temperature of stable alloys, followed by a sudden decrease in slope to what they considered normal values. On cooling, the activity data reproduced the values in the normal range but then deviated from the values obtained on heating. They also observed that specimens of the stable phase upon melting and resolidifying always crystallized in the stable crystal structure as long as the melt was not heated to more than 485° to 525°C; otherwise solidification to the metastable phase occurred. However, in a later investigation, these results were not reproduced (13). The resistivity of liquid Cd-Sb alloys has been investigated by Matuyama 5, Oleari and Fioram, 8 and Belaschenko (141, but only above 500°C, the temperature region where Scheil and Baach observed no vapor-pressure anomalies. The data of Matuyama and of Oleari and Fiorani are reproduced in Fig. 5 and show a maximum in resistivity at 50 at. pct Cd. The data of Oleari and Fiorani, however, show the maximum as being rounded, and their values in general are slightly higher than those of Matuyama.

Jan 1, 1964

By R. A. Burton, J. T. Hansford, D. A. T. Donohue

Substantial evidence indicates that many petroleum producing horizons contain naturally occurring, ordered fracture systems and that within a particular geologic zone, vertical fractures induced in wellbores often will be directed along a particular compass direction. Both conditions will seriously alter the fluid displacement behavior within reservoirs. In this study the effect of induced fracture orientation and length on sweep efficiency is determined for a five-spot pattern. In general, it is assumed that all wells are fractured and directed along the same compass direction. Using the electrical analog to steady state, two-dimensional fluid flow in porous media, boundary conditions are obtained from which flood fronts are tracked numerically. The numerical computations require a particle tracking routine for approximating flood front histories. It is shown that recovery is sensitive to the length and orientation of fractures for the pattern studied. with the proper design of fracture-pattern systems, recovery can be enhanced considerably. INTRODUCTION Hydraulic fracturing introduced in 1949l gave the industry a rather inexpensive means of increasing the fluid injection or production capacity of wells. It has been used with particular success to increase the production rate of wells completed in tight formations, such as in western pennsylvania2 where producers have fractured in depleted or near-depleted fields and observed economic responses. Once the natural energy declines in such a reservoir where all wells have been fractured, waterflooding is generally suggested as means of further increasing recovery. Of the dual objective sought in waterflooding — high injectivity and high breakthrough sweep efficiency — the former condition can be obtained if all wells in the flood pattern are fractured; the latter condition should depend on the nature of the fracture system. Considerable theoretical work has been published on the nature of fractures induced in boreholes.3-5 Although discussion persists concerning the possibility of forming a horizontal fracture at a given point within the wellbore, it is generally conceded that only vertical fractures will develop below a given depth, i.e., where the fracturing Pressure is less than the overburden load. Given the fact that fractures will be vertical in most cases of interest, it is also important to know whether there is order to fracture orientations within a given geological region. Kehle has suggested that in tectonically relaxed areas of uncomplicated geology, the stresses are fairly uniform and all fractures in the region should be parallel.5 Dunlap arrived at a similar conclusion in a theoretical investigation of localized stress conditions surrounding the borehole.6 He concluded that most vertical fractures are propagated in a preferred azimuthal direction. Fraser and Pettitt, in extending these theoretical suggestions to a specific field case, used an impression packer to record both a vertical fracture and the orientation of this fracture in the wellbore of a well in the Howard Glasscock field, Tex.7 Use of this information enhanced the waterflood recovery of the field. Anderson and Stahl also used impression packers on three fractured wells in the Allegheny field. N. Y.. and found that the fractures were oriented more or less along the same compass direction.8 Orientation of the fractures in this manner depends on the stress condition within the formation during fracturing. Elkins and Skov have demonstrated that a natural, oriented, vertical fracture system exists within the Spraberry field? Heck suggests

Jan 1, 1969

By W. L. Kerlie, J. H. Richards

The variation in hydrogen content of basic open-hearth steels during refining and the effect of changing from steam to air atomization were studied. The water content of the furnace atmosphere, the slag basicity, and the degree of oxidation of the slag-metal system largely control the hydrogen in the steel. SMALL amounts of hydrogen have an adverse effect on the ductility of steel and a wide range of hydrogen contents has an adverse effect on the internal soundness of both ferrous and nonferrous castings. This has been of major concern to the metal industry, both manufacturers and fabricators, for many years. As one of the results of continuing investigations of the hydrogen problem, much has been learned about methods of reducing the hydrogen content of liquid metals below the relatively high levels that are normally associated with such phenomena as rising ingots and excessive porosity in sand casting. However, it was not until a reliable and simple method for sampling and analyzing liquid metal was developed that much progress was possible in quantitatively evaluating the effect of steelmaking practice on hydrogen contents at levels below 6 to 8 ppm. Throughout all the work described in the following presentation the Geffner pintube technique was used to obtain samples of liquid metal1 * and the tin-fusion method, developed at Massachusetts Institute of Technology,2 was used to analyze the samples. Before attempting a systematic experimental program for minimizing the hydrogen content of open-hearth steels, it was necessary to determine the variation in hydrogen in the open-hearth bath during the normal processing of a heat. The logs of ten heats are illustrated in Figs. 1 through 7. The number at each point on the graphs refers to the number of pintube samples analyzed for hydrogen. An increase in the hydrogen content of the liquid metal during the early period of refining is apparent in all heats. There is evidence of a decrease in hydrogen later in the refining period, see Fig. 2, for example. Therefore, the existence of a maximum hydrogen content at some intermediate time during the refining period is anticipated. To test for the existence of a maximum, the data illustrated in Figs. 1 to 5 were grouped together so that they could be examined on a collectively comparable basis. The grouping was effected, as illustrated in Fig. 8, by superimposing Figs. 1 to 5 so that the apparent hydrogen maxima coincided at a fixed position, indicated by the zero on the time axis. Also, by vertical adjustment until the graphs appeared to the eye to be superimposed, the hydrogen scale was made to show the change in hydrogen content. That is, a standard amount was subtracted from the hydrogen values for each heat. Therefore, Fig. 8 represents a generalized presentation of the data and, for this reason, cannot be used to predict the actual hydrogen content of the bath during refining, but rather to show the probable rate of change in hydrogen during refining. Statistical examination of the grouped data in Fi.g. 8 shows that the apparent. increase and suhsequent decrease in hydrogen are real and confirms the existence of a maximum in general. The average increase In hydrogen during the early period of refining is between 0.8 and 1.3 ppm per hr, and the

Jan 1, 1958

By J. W. Whalen

The design, operation and evaluation of an instrumental method for the determination of fluid saturation in porous materials during multiphase flow studies is described. The presence of a magnetic tracer comprising approximately 20 per cent by weight of the aqueous phase is necessary in the utilization of this method. The results of two-phase relative permeability studies on two samples of porous media are presented. The realizable accuracy of the magnetic susceptibility apparatus in fluid saturation determination is estimated to be 2 saturation per cent. The response characteristics of the instrument, together with its simplicity of operation and maintenance are sufficient to recommend its use in routine laboratory studies. INTRODUCTION The problem of fluid saturation determination in laboratory multiphase flow studies characterizing oil recovery processes is one which has been given exhaustive study. Briefly the requirements which are considered essential for a method sewing this purpose are: (1) that the measurement be made external to the porous rock sample under study with no interruption of the fluid flow pattern, (2) the saturation indication must be independent of fluid distribution in the volume scanned by the measuring device, (3) the sensing element should have a small field of definition enabling several independent measurements to be made along the length of a core sample, and (4) the properties of the fluid phases should not be too greatly influenced by required tracer substances. Several methods of saturation determination have found acceptance as meeting most of the above requirements. These include resistivity,1 X-Ray absorption,2,3,4 radiotracers,5,6,7 and neutron8 diffraction The merits of these techniques have been discussed elsewhere in detail and will not be considered here. It may, however. be pointed out that the elaborate instrumentation required by the methods mentioned above, with the exception of the resistivity method (which is undesirable from other standpoints) encourages the development of methods of saturation determination which, while meeting the requirements listed, are simple to operate and maintain. It is the purpose of this paper to describe the instrumentation and evaluation of a technique for the determination of fluid saturation which combines relative simplicity with an accuracy and applicability comparable with methods now in practice. DESCRIPTION OF THE METHOD If the magnetic susceptibility of one of the fluid phases contained within a porous material is sufficiently greater than that of the remaining phases, the fluid content of the material with respect to that phase may be determined by an induction measurement. This may be accomplished by measuring the induced voltage in the secondary of a transformer which contains the porous sample and its interstitial fluids as a portion of the magnetic flux path. Since the fluids used in multiphase flow studies involving petroleum reservoir samples possess uniformly low magnetic susceptibilities, the use of a magnetic tracer in one of the fluid phases is required. In view of the relatively high paramagnetic susceptibility of salts of the transition elements, together with their high water solubility. these compounds become logical choices as tracer materials. Cobaltous chloride, having a specific magnetic susceptibility of 17.5 x 106 cgs electromagnetic units, was used as the tracer material throughout this work, in a concentration of approximately 20 per cent by weight in the aqueous phase. MAGNETIC SUSCEPTIBILITY APPARATUS Basically, the magnetic susceptibility apparatus consists of a transformer serving as the detecting head, a

Jan 1, 1955

By R. H. Hiltz

Three titanium alloys, known to provide a mechanically unstable p structure after quenching, were selected as material for a study of the Origin and nature of stress-induced transformation. Data from hardness and tensile tests were used to study the initiation of marten site and the effect of the transfornation and transformation products on the mechanical properties of B titanium, particularly the stress-strain relationships. With the exception that the materials investigated showed a natural aging reaction in the P condition, their behavior is analogous to that of&apos; stress-transforming stainless steels. The transformation starts after initial yielding and is essentially complete just prior to .maximum loading. Once initiated, the martensite itself is capable of propagating the transformation. The deforn-ing materials show low strength, high ductility, and a high strain-hardening exponent. In metallic systems which undergo a diffusionless transformation on cooling, it is possible to produce a similar transformatiorl by plastic deformation under special conditions. Dewez&apos; in delineating Ms temperatures for the titanium-rich end of most titanium binary systems:, established the point of intersection of Ms with room temperature for those particular alloys. Alloy compositions which would quench to mechanically unstable p were established from these data. The first investigation into the possibility of stress-induced transformation occurring in titanium met with little success. It was concluded that such a transformation in titanium was possible only under very special conditions. Continued effort in this direction, however, showed certain Ti-Mo binaries to be highly susceptible to this phenomenon. This fact was utilized by Liu to study the habit planes of martensite and by Machlin and wenig5 to study the effects of stress and plastic deformation on the P to a prime transformation in titanium alloys. The first investigation of the mechanical properties of these alloys was conducted by Holden and his coworkers at Battelle Memorial Institute.&apos; The potentiality of the alloys i3s sheet-forming material was recognized, and the data reappeared in a survey of this type of titanium material.? The initial optimism was tempered by the difficulties in obtaining homogeneous 2i-Mo alloys in commercial-size ingots. The increasing need for good sheet-forming material kept investigation in this direction active, resulting in the development of a commercial alloy of this type.&apos; This study was undertaken to obtain a clearer picture of the mechanism of stress-induced transformation in titanium. MATERIALS AND TEST PROCEDURE Three alloys were selected for this investigation: one a Ti-Mo alloy; another a Ti-Cr-Mo alloy, known to deform martensitically; and the third, a Ti-V alloy with an Ms below room temperature and an Md above room temperature, but known to contain w phase in the quenched condition. The compositions of these alloys are given in Table I. These alloys were cast as 5-lb experimental ingots, employing skull melting. The ingots were hot-forged into 1-in.-round bars. Two 72-in.-thick slices were cut from each bar for hardness testing; the remainder was cut into 0.252-in. tensile blanks. The tensile blanks and one hardness disc from each bar were heated in salt to a temperature 100°F above the 0 transus, held 2/2 hr, and brine quenched. X-ray analysis showed the pieces to be 100 pct 8.* *Omega cannot be distinguished from p by the technique employed. Tensile blanks were machined to size after this treatment. TO prevent transformation due to machining stresses, the shoulders and gage length were ground. True stress-true strain curves were

Jan 1, 1960

By S. L. Couling, D. J-P. Adenis

i2) twinning in poly crystalline magnesium does not usually occur homogeneously but is concentrated in localized regions or bands inclined at about 45 deg to the stress axis. These bands of twinning are in many ways similar to the Luders bands seen in mild steel alzd Al-Mg alloys. Within a hand the percentage of the volume twinned may approach 100 with no twinning outside the band. Bands are not produced in specimens of grain size a3 x 10-= in. or in samples deformed at temperatures 300°F. Annealing of heavily twinned regions leads to re crystallization textures markedly different from those found in the starting material. The exact preferred orientation appears to depend on the starting grain size, the amount of compres-sive strain and the manner in which it is introduced. MAGNESIUM, with its hexagonal crystal structure, deforms plastically at room temperature by a variety of deformation mechanisms, one of the most important of which is (1012) twinning. In single crystals such twinning occurs on compression parallel to the basal plane or tension perpendicular to it. In wrought polycrystalline magnesium, such as rolled sheet, the preferred orientation is such that almost all the grains have their basal planes nearly parallel to the sheet surface. Therefore, if sheet material is deformed by cold rolling or by tension in the plane of the sheet, deformation of the grains by (1012) twinning is not favored. On the other hand, twins form readily on compression parallel to the plane of the sheet as in a compression test, on the compression side of a bent sample, or at the outer rim of a drawn cup. The first part of this paper deals with the morphology of (1012) twinning in polycrystalline magnesium. Some aspects of this subject were covered by Barrett and ~aller.&apos; Of direct bearing on the work to be reported here are the comments of Jetter&apos; in discussion to Ref. 1. He shows that Mg + 1.5 pct Mn alloy sheet when bent about a transverse axis develops a pattern of transverse bands on the surface of compression. A longitudinal section through the sheet shows that the bands are wedge-shaped and inclined to the rolling direction. The bands were identified as "outcrops of regions in which deformation is localized as the result of the reorientation brought about by (1012) twinning". The second part of the paper treats the recrys-tallization texture of the specimens twinned by compression. Magnesium deformed and then annealed generally recrystallizes with no change in orientation.1&apos;3&apos;4 This statement is true provided that the amount of (1012) twinning occurring during deformation is small. In an isolated observation, Anse15 has shown that, when deformation produces much (1072) twinning, annealing causes new maxima to appear in the pole figure. The second part of the paper elaborates on this point. I) MATERIALS AND PROCEDURES All of the experimental work to be reported was done using the commercial sheet and plate alloy AZ31B (nominal composition: 3 pct Al, 1 pct Zn, 0.4 pct Mn, balance magnesium). This alloy is available commercially in two tempers, -0 (fully annealed) and -H24 (partially annealed), and specimens of both tempers were used in various experiments. The average grain. diameter (AGD) for -0 temper 0.125-in. sheet is about 0.5 x 10- in.; where material of larger grain size was desired, anneals at elevated temperature were used to grow the grains. compression tests were made on a screw-driven "hard" machine. The specimens were clamped in a

Jan 1, 1964

By M. B. Bever, A. K. Jena

Equations for the heat effects of additions of mixtures of multicomponent phases to a solution have been derived in terms of the enthalpy interaction coefficients. By these equations and the measured composition dependence of the heat effects on addition of mixtures of Ag-Cd solid solutions and elemental gold to liquid tin-rich solutions, values of the enthalpy in-teraction coefficients in tin-rich solutions at 541°K have been obtained. Analysis of these results in terms of the regular solution theory and the quasichemical theory suggests that near the melting point of the solvent association in the solution becomes important. SEVERAL recent papers have discussed the nature of dilute solutions on the basis of measured enthalpy interaction coefficients. l-3 These coefficients contribute to the understanding of the constitution of solutions and can be used for the evaluation of thermo-dynamic data of multicomponent systems. Their experimental determination, however, is laborious. This communication reports values of the enthalpy interaction coefficients of silver, cadmium, and gold in liquid tin-rich solutions obtained from the measured heat effects of additions of mixtures of Ag-Cd solid solutions and elemental gold to liquid tin-rich solutions. These measurements were made in the course of the determination of the heats of formation of Ag-Cd solid solutions reported in a concurrent publication.4 THE HEAT EFFECT OF AN ADDITION TO A SOLVENT This analysis is concerned with the addition of a mixture of multicomponent phases from the temperature To to a solvent of known composition at temperature T. If Nmixture << Nsolvent, where N designates the gram-atoms involved, the heat effect per g-atom of mixture added can be expressed as (HT - HT )i = difference in heat contents of component element i in the mixture at T and To Q = heat effect on solution of the mixture at temperature T Also1 Q = S Xi [2] where ?Hi ,T,x = relative partial enthalpy per g-atom of i in solution at temperature T and composition of the solution x x = average of the atom fractions of the added material in solution before and after the addition The relative partial enthalpy ?Hi per g-atom of an element i in a dilute solution composed of a solvent 1 and the solutes j = 2, ... m is related to the interaction coefficients by the following equation5 ?Hi - ?Hi-?Hi,x1-1 + S n1ixj+ . . . +S...S...S nrixn2... Xnji...Xnmm+... [3] vhere Xj = atom fraction of solute j in the solution nri = the rth order enthalpy interaction coefficients, which can also be represented by the more general designation5 L(i)n2,n3...nm and nj may have any positive integral value or zero. For identification of various rth order interaction coefficients, nri is written as nn2i2,...nij,...nmm. Eqs. [1], [2], and [3] combine to give the following general equation for the heat effect on addition of a small quantity of a mixture to a large quantity of a dilute solution n = _?ga ?Ha,To + ? Xi(HT - HT o)i a. i + ?xi?Hi,X,i?1 + ??xnjixj + . . . + ???. . .?. . .?xinrix2n2. . . xnji. . . xnmm+ . . . [4] The first term on the right-hand side of this equation is the heat of decomposition at the addition temperature of the phases present in the mixture, the second term is the heat required to raise the temperature of

Jan 1, 1970

By H. H. Rachford, D. W. Peaceman

A system of partial differential equations describing miscible displacement of fluids in porous media is derived The system takes into account the influence of gravity, the spatial distribution of permeability, diffusion, and fluid viscosities and densities. A numerical procedure for approximating solutions to the differential systems has been tested for a horizontal two-dimensional geometry. In end-to-end displacements of oil with less-viscous solvents, the numerical solutions exhibited fingering qualitatively similar to that observed in laboratory models. Small random spatial variations in permeability about the mean value are sufficient to initiate fingering. Quantitative comparisons of computed results with laboratory data show good agreement. INTRODUCTION Miscible flooding of oil by solvent is receiving increasing consideration for field use.1-4 Unfortunately, such floods potentially present severe problems in loss of recovery through the by-passing of oil by expensive solvent. Consequently, their economic evaluation requires sound techniques for predicting recovery. The purposes of this work are to present a finite-difference method for calculating the multidimensional displacement of oil by solvent and to investigate the validity of the method by comparing results of calculations with data from displacements in laboratory models.5 The formulation of the method to simulate the model experiments treats a case of limited scope in the description of solvent flooding in the reservoir. The model experiments were carried out with fluids that were assumed to form an incompressible, ideal, two-component system with constant diffusivity. Establishing the validity of the method even in its present form provides a major step toward the goal of quantitatively evaluating individual solvent flooding projects. First, it demonstrates the fea- sibility of calculating the course of displacements which are dominated by an inherent macroscopic instability, i.e., viscous fingering. In addition, the method provides almost the only practical means of examining the effect of the size and extent of reservoir inhomogeneities on the development and propagation of the fingers, taking into account the important influences of diffusion and gravitational segregation. It might be inferred that such studies cannot yield results of practical value because in displacements dominated by macroscopic instability the pattern of finger development and the resulting performance should depend critically on small variations in the geometric distribution of reservoir inhomogeneities. The present method offers the capability inherent in computational techniques of predicting performance reproducibly with any arbitrary distribution of reservoir properties and, as such, provides a means of evaluating the sensitivity of behavior to uncertainties in reservoir definition and, thus, assessing the reliability of prediction of performance. THE PHYSICAL PROBLEM DATA USED FOR QUANTITATIVE TESTS OF CALCULATIONS In this work, a calculation for treating the miscible-displacement process is tested by comparing calculated results with experimental data. The experiments chosen for comparison have been described in detail,5 and the quantitative features are summarized in a later section. Briefly, oil was flooded by solvent of equal density from a thin rectangular channel in Lucite packed with uniform Ottawa sand. Under these conditions, two-dimensional geometry is considered adequate to represent the process. Inasmuch as the present work is concerned with testing of the method by comparison with specific two-dimensional data, the system of equations presented in the succeeding section will be oriented to defining the physical system specifically. THE DIFFERENTIAL EQUATIONS Suppose x, y to be a Cartesian co-ordinate system and define h(x, y) to be the height of a point above a horizontal reference plane. It will be assumed

By W. A. Backofen, D. Lee

Titanium of commercial purity (RC-70) and two all-a (hcp) alloys (4Al-1/4O2 and 5Al-2.5Sn) were tested in sheet form under conditions of combined-stress loading. Plane-strain compression and plane -strain tension together with uniaxial compression and tension provided information for constructing the tension-tension and compression-compression quadvants of the plane-stress yield locus. Coordinate values were obtained from yield-strength measurements; the slope at each point was based on a plastic-strain ratio. The materials represented a wide range of plastic anisotropy, which was reflected in correspondingly varied departures of the yield locus from that for iso-tropy. The tension-tension and compression-compression quadrants were not identical. If the uniaxial yield strength is insensitive to direction and the sign of the applied stress, the Mises or perhaps the Tresca criterion is adequate for predicting the onset of yielding under combined-stress loading. The prediction is not so straightforward in plastically anisotropic material. Depending upon details of texture, combined-stress yielding resistance may be substantially different from that indicated by the usual criteria.&apos; However. a continuum theory of yielding under such conditions is available for reasonably direct application.2,3 Whether or not it can be used successfully must, of course, depend upon how closely the conditions of the theory are satisfied in the material in question. In its present form the theory contains no provision for Bauschinger-type effects, nor does it allow for the consequences that might grow out of deformation by more than one mechanism, e.g., by slip and twinning.4 With those limitations, more importance must be attached to experimental information about the yield surface for anisotropic materials. Studies of the yield surface have generally been confined to states of plane stress (tension-tension and tension-compression) established in thin-wall tubes by externally applied forces and internal pressure. That approach would be entirely suitable for anisotropic materials if they were available in tube form or in sufficient bulk to be machined into test specimens. 6-9 It would not serve for the textured and anisotropic sheets of much current engineering interest, unless sheet could be formed into high-pressure tubing without structural change. Since there would seem to be little chance of the latter, practical alternatives are needed. One such alternative is the subject of this paper. It involves the use of a few selected but relatively simple uniaxial loading tests on sheet specimens. The underlying idea is presented here with some details relating to application and a few results bearing on how well it has worked. THE BASIS OF TESTING Conventional Measurements. Yielding for a general case of anisotropy is described by the plane-stress locus in Fig. 1. Reference directions in the sheet specimen are related to the stress coordinates as shown with the insert: x is the rolling direction, y the transverse direction, and z the through-thickness direction. The four reference-direction yield strengths (t, tension; c, compression), Xt, Xc, Yt, and Yc, are all different. Nine paths that can be followed in uniaxial loading experiments are identified. Paths 1, 2, 3, and 4 represent conventional tension and compression testing to establish Xt, Yt,.Xc, and Yc. Useful information also comes from the ratio of the transverse plastic-strain components associated with yielding and flow in conventional tension or compression. A condition to be satisfied in locus construction is that the plastic-strain vector be everywhere normal to the locus.10 The projection of the vector which would

Jan 1, 1967

By M. C. Smith, W. V. Green, D. M. Olsen

The creep-rupture behavior of commercial powder-metallurgy molybdenum rod is reported in the temperature range 1600" to 250O°C, at stresses up to 9000 psi and times up to 1 month. The effects of temperature, stress, and grain growth are discussed. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher-stress results reported by pugh.1 BECAUSE of its high melting point, molybdenum should retain useful strength to relatively high temperatures. Combined with its ready availability in the United States, this makes it attractive for many applications in missiles, rockets, and so forth—wherever its susceptibility to oxidation can be tolerated or overcome. The mechanical properties of molybdenum rod in the temperature range —200" to 1540°C have been reported by pugh,&apos; Bechtold,&apos; Parke,3 and Carriker and Guard.4 Madden and chen5 have measured the tensile properties of molybdenum single crystals in vacuum up to about 2500°C. As one further step in evaluating its mechanical usefulness, the constant-load creep-rupture properties of commercial powder-metallurgy molybdenum rod have been investigated in the range 1600" to 2500°C. MATERIAL TESTED Creep specimens were machined from 1/2-in. round commercial molybdenum rod, manufactured from powder by pressing, sintering, and swaging. Spectrochemical analysis of the rod showed "traces" (less than 0.01 pct) of silicon, aluminum, chromium, iron, and zirconium, and "faint traces" (less than 0.001 pct) of manganese, magnesium, cobalt, and nickel. Carbon content was 130 to 200 ppm, nitrogen was 110 to 180 ppm, and oxygen 30 to 35 ppm. A typical microstructure of the as-received rod is shown in Fig. 1. Room temperature tensile properties for five specimens strained at about 0.015 in. per in. per min are shown in Table I. CREEP SPECIMENS USED The specimens used for creep-rupture testing are illustrated in Fig. 2. The 1/4-in.-diam gage section was 3/4 in. long, and terminated at shoulders 5 mils high. These shoulders served as fiducial marks for optical strain measurements. Surface finish on the gage section was 16pin. r.m.s. One specimen, for a "long-time" test described below, was modified by dividing the 3/4-in. gage length into three 1/4-in. long sections with individual diameters of 0.250, 0.230, and 0.210 in., each terminating in a pair of fiducial shoulders. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.6 In it the specimen is held vertically on the axis of a cylindrical tantalum or tungsten heater tube by threaded molybdenum or tungsten grips. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. The bottom specimen grip is held at its lower end by a clevis pin. The testing load is applied to the specimen through the upper grip by means of hanging weights, a constant force-multiplication lever system, and a pull rod sealed to the chamber lid by a bellows. The incandescent specimen is viewed by an external optical system through slots in the heater-tube and radiation shielding, and an enlarged image of it is projected on a ground-glass screen. Gage-length measurements are made on this image with a pair of cathetometers. Thorium oxide coatings were applied to the threaded ends of most specimens, to prevent diffusion-welding of specimens to grips during testing. Without such a coating welding usually occurred, and grips were often broken by subsequent efforts to remove the tested specimens.

Jan 1, 1960

By F. D. Rosi, C. A. Dube, B. H. Alexander

WHEN a deformed polpcrystalline metal is heated to a sufficiently high temperature, a recrystallized structure develops which consists of small, essentially stress-free grains. This transformation is referred to as primary recrystallization. Under certain conditions, on prolonged annealing of the specimens, a type of grain coarsening occurs in which a small number of grains commence to grow at various points by devouring the neighboring finegrained primary structure, which, in itself, exhibits a marked stability toward normal grain growth. This grain coarsening process has been referred to by Burgers&apos; as "secondary recrystallization" or "exaggerated grain growth." Although much work has been done on recrystallization and growth processes, present knowledge of the factors which determine the occurrence and growth of secondary grains is inadequate for the advancement of a theory which accounts for the observed characteristics of this recrystallization phenomenon. In this respect, it would be important to make measurements of the velocity of growth of these large secondary grains. The early work of Feitnecht2 on aluminum showed that the size of secondary grains increased with temperature and time, suggesting that such measurements would be possible. More recently, Burgers1 found that the growth velocity of these grains in aluminum was constant over a large time interval, as is generally found for the growth velocity of primary grains in a uniformly deformed test piece.3-5 It is reasonable to expect that the determination of the activation energy of the secondary growth process might lead to a better understanding of the underlying atomic mechanism. This investigation, therefore, is one of a series primarily designed to measure the growth velocity of secondary grains at various temperatures for silver, copper, and aluminum. It is hoped that these studies along with those of orientation relationships, will establish a sound basis for theorizing as to the origin and nature of the secondary transformation. Experimental Procedure The metal used in the present investigation was high-purity silver (999.9 fine), which was supplied in the form of cold-rolled plates 0.250 in. thick. These plates were annealed at 500°C for 1 hr and then straight-rolled to a thickness of 0.04 in. in three reductions of approximately 45 pct, followed in each case by an anneal at 450°C for 1/2 hr. The 0.04 in. sheets were given a final reduction of approximately 50 pct, which resulted in a thickness of 0.02 in., thereby insuring two-dimensional crystal growth. Individual specimens of this material about 1x3 cm were used for all heat treatments, unless otherwise noted. The annealing was carried out under an atmosphere of argon in an Inconel tube furnace whose temperature was controlled to within -+2°C. Metallographic examination of the secondary transformation was accomplished by mechanically polishing the specimens on one side to approximately one half their thickness through 2/0 metallographic emery paper, and then electrolytically polishing in a solution of potassium ferrocyanide and sodium cyanide. With a current density of approximately 20 amp per sq dm, the time required to obtain a satisfactory surface varied from 3 to 5 min. Standard potassium bichromate was used to etch the electrolytically polished surfaces. A heavy etch with this solution produced a sharp contrast between the secondary grains and the fine-grained primary structure, darkening the latter while leaving the large secondary grains bright. All area measurements of the secondary crystals were made with a planimeter on enlarged tracings of the grains.

Jan 1, 1953

By T. G. Digges, M. R. Achter

ALTHOUGH zone melting has found favor in recent years because of its convenience and its faster rate of production of single crystals, the older technique of strain annealing still has a number of advantages. It has been reported1 that the lattice of a crystal prepared in this manner has fewer defects than one grown from the melt and, of course, the control of the external geometry is easier. Also, the diameter of the crystal which can be grown by zone melting has a theoretical limit determined by the surface tension, thermal conductivity, and specific gravity of the material, while the size of that which can be grown in the solid state is limited only by practical considerations. In a program for the study of the structure-sensitive properties of niobium and its alloys it was desirable, for ease of handling, to have available single crystals of large diameter. This requirement dictated the choice of the strain-anneal technique. Induction heating was chosen in the present work in preference to other methods because of its deep penetration of large-diameter sections. A five-turn coil, powered by a motor generator operating at 10,000 cps, is contained in a vacuum chamber. The work is lowered through the coil for both the recrystallization and the crystal-growth steps. Starting with electron-beam melted material, the bars are cold-swaged, recrystallized, strained in a tensile machine, and then subjected to the growth step. Single crystals have been grown under the following conditions: Reduction in area during swaging— 79 to 99 pct, recrystallization temperature—1500o to 1667°C at the rate of 1.25 in. per hr, strain—1.0 to 2.5 pct, growth temperature—1600o to 2400°C at rates from 0.15 to 1.25 in. per hr. Starting grain sizes achieved after the recrystallization step varied from 0.6 to 1.55 mm. The starting grain size was found to be critical; if it is too fine and has any residual cold work, as shown by the presence of a fiberlike texture, a single crystal cannot be grown. Using this technique niobium single crystals have been grown from 0.250 in. diameter and 12 in. long to 1.00 in. diameter and 5 in. long as shown in Fig. 1. The 1-in. crystal is the largest to be reported for a refractory metal as compared to 0.500 in. for molybdenum grown by zone melting.2 As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and Smallman,3 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point ahead of the interface between the single and polycrystalline portions. Finally, it is returned to the chamber and growth is continued "around the corner". The amount of bending which can be imparted to the rod is limited by coil geometry which up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. The perfection of these single-crystal specimens as a function of process variables is being measured by X-ray and metallographic techniques and the results will be reported in a forthcoming paper. This work was partially supported by the Advanced Research Projects Agency.

Jan 1, 1964

By U. F. Kocks

SINGLE slip and a single parallel array of edge dislocations have been obtained in silicon single crystals by homogeneously bending them in a four-point dead-loading device at 1000°C around the [211] axis with [253.] as the tensile axis which encloses an angle of 40° with the glide plane. Other orientations or lower temperatures proved unsuitable. The homogeneity of the bending was checked by the method shown in Fig. 1. The chemically polished specimen was exposed to parallel light from a microscope-stage lamp. The sharpness of the focus of the reflected light is an approximate measure of the circularity of the sample. This method permitted the determination of the actual radius of bent specimens within 10 pct accuracy. The etching solution developed to show up dislocations consisted of the following volume parts: 2 HF, 1 HNO,, 2 CH,COOH, 1 a solution of 5 wt pct of CuNO, in water (Rosi&apos;). The acetic-acid content was adjusted to produce fine well-defined etch-pits in about 2 min at room temperature. The effectiveness of the etch did not depend on the crystal-lographic orientation of the face etched. The number of etch pits produced after a given deformation was checked in the usual way against the Cahn formula&apos; and showed good agreement. As it is to be expected from the orientation of the primary system there are slip steps on the top and bottom faces but not on the side faces (perpendicular to the bending axis), whereas etch pits appear on the side faces but not on the top and bottom faces. This is different only for occasional dislocations of a secondary glide system. All the micrographs included have been taken in places where the most of secondary glide could be seen. From this it is evident that in the homegeneously deformed region the number of secondary dislocations was less than 1 in 1000 of the primary type. Dislocation Distribution—A series of tests with varying amounts of deformation is shown in Figs. 2(a-c). An observation that can readily be made from these pictures is that the linear density of dislocations within slip lines is relatively constant and independent of the amount of deformation. "Slip line" in this context is understood to mean a line that is a straight connection of individual etch pits. The heavily pitted bands which can be seen in each of these three pictures may be resolved fairly definitely, at higher magnifications, into many "slip lines" the distance between them being of the order of 0.5p The distance between dislocations in slip lines is of the order of 2p and it is also fairly constant in going from the neutral zone outward. The higher over-all dislocation density in the outer regions of any sample and the higher total number in a more heavily deformed sample, are effected by a larger number of "slip lines." The relative constancy of the dislocation distance within an individual slip line is surprising. The absence of pile-ups" may imply, if there is no rear- rangement on unloading," that there are no substantial obstacles to slip in this case. It seems that the equilibrium distribution of the dislocations in each active slip plane under the higher external stress on

Jan 1, 1959

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970

By P. R. Sperry, P. A. Beck, Hsun Hu

As described by means of quantitative pole figures, the inside texture of highly rolled aluminum and copper strips may be approximately described by four equivalent ideal orientations near (123) [121]. If rolled in reversed passes, the surface texture of copper is also near (123) [121], that of aluminum is (100) [011]. The inside texture of highly rolled brass is (110) [112]. The surface texture is the same, if rolled in reversed passes. The surface texture of all three metals is related to the inside texture, but asymmetrical, if rolled without reversal between passes. MANY previous investigations dealing with the subject of the present work were reviewed by Wassermann.1 Barrett,2 Brick,3 and Richards.&apos; The recent introduction of quantitative methods for pole figure determination by Decker, Asp, and Harker,5 Schulz5 and others made it possible to reinvestigate some of the finer points which the earlier more qualitative photographic methods left undecided. The rolling textures of silver and of 70-30 cartridge brass have been quite consistently characterized by the ideal orientation of (110) parallel to the plane of rolling and [112] parallel to the rolling direction. On the other hand, it has been recognized by several investigators that certain other face-centered cubic metals, such as copper and aluminum, developed rolling textures rather different from that of brass. These textures have been variously described by the following ideal orientations, singly or in combinations with each other: (110 [112]: (112) [111]; (135) [335]; (135) [211], etc. The discrepancies usually have been attributed to the lack of sharpness in the textures and to the attendant difficulty of associating "ideal orientations" with pole figures showing great scatter of orientations. It seemed desirable to investigate by the new quantitative methods to what extent the apparent lack of sharpness may have been brought about by the qualitative methods used previously, rather than by the textures themselves, and to decide, if possible. between the various ideal orientations which have been proposed. Another problem, not satisfactorily settled by earlier investigations. concerns surface textures in rolled metals. For instance, in rolled aluminum the surface texture in some cases appeared to be similar to the texture inside the sheet, whereas in other cases it was reported to be entirely different.&apos; The conditions under which such differences may have arisen, and the possibility of the occurrence of different surface textures in other face-centered cubic metals do not appear to have been examined in detail. The present work was undertaken to investigate the above questions. Some of the results obtained have been described- riefly. Experimental Procedure Specimen Preparation: In the present investigation 2s aluminum, electrolytic tough-pitch copper, and commercial 70-30 brass were used. These materials were available in the form of cold-drawn rods. 1 in. diam for tough-pitch copper and commercial 70-30 brass and 11/2 in. diam for 2s aluminum. The cold-drawn bars were alternately annealed and rolled 30 pct lengthwise in several cycles until a penultimate thickness of 0.500 in. was reached. The intermediate and the penultimate anneals were carried out for 30 min at 380°C with 2s aluminum, and for 30 min at 550°C with 70-30 brass. For tough-pitch copper, the intermediate anneals were 30 min

Jan 1, 1953