Search Documents

By R. M. Brick

THE etched microstructures of cold-worked alpha brasses, after reduc-tions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonomously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {111}, in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson5 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into sym-metry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By W. Rostoker, D. W. Levinson, A. Yamamoto

The influence of carbon on tensile strength, tensile ductility, transformation kinetics, and grain growth characteristics of selected Ti-Mo base alloys was studied. No systematic influence of carbon in tensile strength or significant deleterious effect on tensile ductility was observed. There was a marked increase in transformation rate due to carbon. Dispersed carbides exert a marked inhibiting effect on grain boundary migration, and thus effectively prevent grain coarsening during solution treatment in the ß phase field. AS part of a research program directed toward the illumination of factors governing modes of transformation, transformation kinetics, and mechanical properties obtainable through these transformations by heat treatment, Ti-Mo base alloys were selected for study. The binary system is a characteristic phase diagram type which has been studied in some detail', ' in relation to transformation kinetics and mechanical properties. Although carbon bearing alloys have acquired a bad reputation, the possibilities of melting titanium under conditions which occasion some carbon pickup are very attractive. It is therefore of considerable importance to know whether carbon, present as a dispersed carbide phase, is actually deleterious when all other detrimental factors are minimized. Basic alloy compositions containing nominally 3, 5, 7, and 11 pet Mo were prepared with systematic carbon addition up to 1 pet by weight. Various of these alloys were subjected to a series of critical and definitive experiments to delineate the effect of carbon on the transformation behavior and associated mechanical properties. Experimental Procedure Alloys were prepared from 115 Bhn magnesium-reduced sponge titanium. This sponge analyzed ap- proximately 0.05 pet C. Ti-Mo and Ti-C master alloys were made by arc-melting the sponge with high purity (99.9 + pet) molybdenum and spectro-scopic grade graphite, respectively. Alloys were then prepared from the master alloys and sponge by double are-melting. One kg ingots were prepared by melting in a nonconsumable electrode furnace. These ingots were forged at 1000°C to '/z in. rods, and cleaned and processed into electrodes for the second melting operation. The final ingots were ground to remove surface defects, then forged again to 1/2 in. or 3/8 in. diam rods for processing to test samples. It is significant that all of the alloys at all carbon levels forged satisfactorily. For convenience, the alloys will be referred to throughout the text by their nominal analyses. Samples for the study of transformation rates were prepared from 1/2 in. diam round stock. They were then solution treated in a helium filled tube furnace at 1000°C for 30 min prior to the isothermal transformation treatments in lead bath furnaces. Temperature control in both cases was within ±3oC. Following the isothermal transformation treatments the samples were water quenched. These experiments were carried out before the general adoption of the resistometric procedure for kinetic studies. The data were therefore obtained entirely by metal-lographic analysis. M, temperature was also determined by the metallographic method. Shoulder-type tensile test pieces were machined from heat treated, 1/2 in. diam slugs to provide a 0.252 in. test diam and a 1 in. gage length. The isothermal-type heat treatments were chosen from previous data' to provide three levels of strength and ductility.

Jan 1, 1957

By James Douglas

This sketch of the history, geography and topography of the American transcontinental railways is based upon a paper read many years ago by the author before the American Geographical Society, and now re-cast, with numerous modifications and additions required to bring it up to date. It was intended primarily for the information of members and guests of the Institute from the East attending the California meeting; and, with that purpose in view, the Secretary of the Institute compiled;

Jan 1, 1900

By William I. Watson

Problems encountered in beneficiating mineral raw materials become increasingly difficult as there is a shift to lower grade and more complex raw materials, and because of the economic need to strive for ever higher recoveries, higher grade products, and lower processing costs. Methods of attacking the many problems should include not only the familiar chemical and physical tests and equipment, but such techniques as X-ray analysis, infra-red analysis, differential thermal analysis, and the use of electron and X-ray microscopes. Many people in the mineral-treating field are unfamiliar with these newer methods and techniques. The differential thermal analysis method, in particular, does not seem to be very well known, even though it offers interesting possibilities in the study of many ore treatment problems.

Jan 7, 1959

By David R. Mitchell, B. M. Bird

DENSE-MEDIA processes utilize the familiar laboratory float-and-sink procedure on a commercial scale. Just as wood chips float on water and sand sinks, so coal floats and refuse sinks when placed in a medium intermediate in specific gravity between the coal and refuse. Liquids intermediate in specific gravity between coal and refuse used in commercial plants are of four types: (1) organic liquids of high specific gravity-halogenated hydrocarbons; (2) dissolved salts in water; (3) pseudo liquids obtained by suspending solids, such as sand or magnetite, in water, and, (4) fluidizing a mass of sand or other solids by air currents. Those most widely used for cleaning coal are solutions of calcium chloride in water and a suspended sand or magnetite pseudo liquid. Laboratory float-and-sink testing is an intermittent operation during which every opportunity is given for particles lighter than the medium to float and particles heavier to sink. Commercial processes are continuous; vertical and horizontal currents of the separating medium occur as either part of the process or unavoidedly produced by the introduction of feed and withdrawal of products, 'so that the exact separation of the laboratory technique is not duplicated by commercial processes. However, separations close to the theoretical are obtained in commercial machines by careful technical control of the process. Most machines in commercial installations are crowded to get as much out of the equipment as possible, so that careful technical control is necessary is get the recoveries and grade of product desired. Sizes usually cleaned are plus ¼ in. or plus 1/8 -in. in the United States and plus 1/16-in. in Great Britain. Coal as small as 1 mm. has been cleaned in some experimental installations. The separation of coal from refuse in sizes finer than about 1/8-in. is made difficult by viscosity effects and hence at the present time cleaning is confined to the coarser sizes. Technical advances in the art of cleaning coal by dense-media processes is progressing rapidly and it is likely that equipment, media, and procedures will be developed to clean sizes down to 0.5 mm. efficiently and at low cost.

Jan 1, 1950

By H. G. Doll

THIS paper discusses a method and apparatus for determining the dip of formations traversed by a drill hole, by means of electrical measurements in the hole. The process consists in recording the Spontaneous Potentials present along three oriented generatrices in the hole. By comparison of the three curves thus obtained, after application of a correction factor to compensate for any deviations of the hole, the dip angle and the dip direction are determined. Excellent accuracy is obtained for dip angles over 10°. Because the method is simple and the apparatus rugged, the measurements are rapid and reliable; consequently, they can be made at all the levels that are of interest at any time after the well has been drilled. Mechanical cores are not needed to evaluate the dips. A convenient, timesaving procedure is to perform the dipmeter survey at the time the electrical log is taken, using for both operations the same cable and truck. Actual examples of results obtained in wells of the Gulf Coast area are given.

Jan 1, 1944

By H. D. Newell

THERE has been much research and commercial development in recent years in the use of chromium and nickel in steels of various types, including those intended for high-temperature service. By "high-tem-perature steels" are meant those specifically designed for service at ele-vated temperatures in steam plants, oil refineries and other industries where high-temperature operations are conducted. This paper is devoted to some preliminary data on the effect of silicon on certain of the most popular chromium-molybdenum steels now being used in quantity by the refining industry and includes a short statement on the influence of copper in steels intended for high-temperature service.

Jan 1, 1937

By R. Woods

INTRODUCTION Gaudin (1), considered that "the mechanism of mineral collection is the central problem of flotation theory". From their work on adsorption phenomena in flotation for more than fifty years (2), Gaudin and his co-workers have made major contributions to the elucidation of this mechanism, a fact acknowledged by their contemporaries in the field (e.g. (3)). Their investigations in a number of areas, e. g. demonstrating that submonolayer quantities of adsorbed collector species can induce flotation, or identifying the influence of substances which can activate or depress (1), have helped to provide the basis for and the development of a theory to account for the interaction between mineral and collector. It was established in the late fifties (4) that the presence of oxygen is a prerequisite for the flotation of metal sulfides with thiol collectors. This fact rendered inadequate the concept of simple ion adsorption being responsible for rendering these minerals hydrophobic. The requirement for oxygen has been explained (1) in terms of this species being a component in chemical reactions between the sulfide surface and the collector. Gaudin has been instrumental in identifying the products of chemical reactions at sulfide minerals (1, 5), a line of work which has been continued particularly by Finkelstein and co-workers in South Africa (6). In presenting a detailed mechanism of the mineral-collector- oxygen interaction, it has often been considered that the mineral surface [must] first be oxidized to a metal oxy-sulfur species which

Jan 1, 1976

By John D. Roach

DURING an investigation of the yttrium-hydrogen system aimed at producing solid yttrium hydride specimens containing various amounts of hydrogen, it was observed that yttrium containing approximately 2 wt pct H exhibited a tendency to crack and crumble to a powder on standing in air at room temperature. It was also observed that longer hydriding times, at a given temperature, increased this susceptibility to powdering without an increase in hydrogen content, also that moisture in the air is necessary for the observed effects to occur. Even if cracking did not occur, there was a continual formation of a light gray powder on the as-treated surface of the hydrided yttrium and this reaction continues until the entire hydrided piece has been reduced to a powder. Storing the hydrided specimens in the absence of air or removing the surface either by machining or grinding were effective means of preventing this disintegration of hydrided yttrium. In an attempt to determine the reason for this powdering phenomenon, the surfaces of a number of as-hydrided yttrium specimens were examined by X-ray techniques. In all cases the X-ray pattern obtained showed the major phase to be yttrium hydride (YH2) as would be expected since the specimens contained 2 to 2.2 wt pct H. In some cases a trace of yttrium oxide was observed. There was also a third phase present on the surface of these hydrided specimens which could not immediately be identified. This unknown phase was a face-centered cubic material, NaC1-type structure, with a lattice parameter of 4.855 and a calculated density of 5.914 g per cc. Very slight hand polishing of the surface of the hydrided yttrium specimens completely removed both the unknown phase and the traces of oxide so that only the yttrium hydride pattern remained. Based on the X-ray patterns the quantity of the unknown phase on the surface of the hydrided yttrium appeared to be directly related to the susceptibility of the material to powdering. Work at the Denver Research Institute on the yttrium-nitrogen binary system showed that yttrium nitride (YN) is a face-centered cubic material with a lattice parameter of 4.878A and a density of 5.890 g per cc. They also noted that this compound rapidly disintegrated to a powder on standing in air. The unknown pattern observed in the above specimens corresponds very closely to that of the nitride—fcc structure, 4.885 parameter, and density of 5.914 g per cc. The presence of this thin film of nitride on the surface of the hydrided specimens probably accounts for the observed powder formation and crumbling. The nitride reacts with the water vapor in the air (verified by private communication from Dr. C. Huffine, General Electric Co.) to yield yttrium oxide and ammonia. Ammonia is readily detected when hydrided yttrium specimens were allowed to stand in bottled moist air. The powder formed on the surface of the hydrided specimens was shown by X-ray analysis to be yttrium oxide. This reaction appears to occur primarily at the grain boundaries since discrete particles of yttrium hydride separate from the specimens during this powdering process. The reaction of yttrium nitride with water vapor is believed to be as follows: 2YN + 3H2O - Y203 + 2NH3. Despite the fact that this nitride is present only as an extremely thin surface film, if the above reaction is not prevented by removing this film from the surface either by machining or grinding, the reaction continues until the entire hydrided piece has been reduced to a powder. To account for this continuation of the reaction, it is believed that the following reactionalsooccurs: 2YH2 + 2NH3 -2YN + 5H2. The nitride produced by the latter reaction reacts in turn with water vapor. The reaction therefore becomes autocatalytic and continues until the hydride has been consumed and the entire piece reduced to oxide powder. The amount of nitride required to initiate this reaction is quite small and this nitrogen contamination can occur from a number of sources—hydrogen gas employed, minute leak in the hydriding apparatus or even from degassing of the reaction vessel itself. Longer hydriding times increase the possibility of nitrogen contamination and this is especially true when a dynamic gas system is employed in the hydriding process. The production of stable, solid hydrided yttrium is dependent on the complete absence of nitrogen contamination during processing. If such contamination does occur, powdering of the hydrided product can be prevented by removing the nitride from the surface e.g. grinding or by preventing access of air to the pieces e.g. sealing in wax or plastic. The author wishes to express his appreciation to General Electric Co. for sponsoring this research and for permission to publish the results of work under Subcontract AT-93.

Jan 1, 1962

Jan 1, 1952

By M. S. Smani, P. Blazy, J. M. Cases

Investigations on the beneficiation of sedimentary Moroccan phosphate ores are reported in four separate parts. The first discusses electrochemical phenomena at the solid-aqueous solution interface for minerals of the apatite group. In the second part, the electrochemical properties of the calcareous gangue associated with the phosphate ore are investigated. The flotation of calcite and phosphate oölites, using both anionic and cationic collectors, is discussed in the third part. It is shown that selective recovery could be obtained for precise concentrations of collectors and pH ranges. Results of work aimed at optimizing depression of phosphate oölites during inverse flotation of the carbonate gangue with sodium oleate are reported in Part 4.

Jan 1, 1976

The following list comprises the names of those persons who became members during the period May 10, 1916, to June 10, 1916: ARCHIBALD, JOHN CHRISTIE, Min. Engr., Supt. of Cyanide Plant, Guanajuato Reduction Mines, Guanajuato, Mex. BRUNEL, FRANK P., Cons. Min. Engr Mitchell & Brunel, Ajo, Ariz. CALVERT, WILLIAM ROBERT, Cons. Geol. ...225 Kearns Bldg., Salt Lake City, Utah. CHAMPION, J. R., Supt The Yak Mining, Milling & Tunnel Co., Leadville, Colo. CHARLES, LAVERN JOHN, Construction Engr., Elephant Butte Dam, Elephant Butte, N. M. CHASTEL, ANDRE, Min. Engr., Societe Miniere & Metallurgique de Penarroya, 12, Place Vendome, Paris, France. CHRISTIE, WALLACE H., Vice-Pres. and Mgr., Alt. Bert Gold Dredging Co., 604 Mission St., San Francisco, Cal. CLARK, RONALD ..Hardinge Conical Mill Co., 120 Broadway, New York, N. Y.

Jan 7, 1916

By William E. Ford, Edward Salisbury Dana

A. Anhydrous Carbonates The Anhydrous Carbonates include two distinct isomorphous groups, the CALCITE GROUP and the ARAGONITE GROUP. The metallic elements

Jan 1, 1922

Jan 1, 1891

Oct. 8-13, 1917 COMMITTEE ON ARRANGEMENTS H. A. BUEHLER, Chairman, W. E. McCOURT, Secretary, C. J. ADAMI, Southeastern, J. A. CASELTON, Entertainment, F. W. DEWOLF, Book, , E. F. GOLTRA, Finance, L. L. HUTCHISON, Tulsa, E. McAULIFFE, Transportation, P. N. MOORS, Reception, MRS. P. N. MOORE, Ladies, J. D. ROBERTSON, Publicity, VICTOR RAKOWSKI, Joplin., H. A. WHEELER, Excursions, A. THACHER.

Jan 7, 1917

By Y. G. Shiau, J. E. Burke

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

By J. E. Burke, Y. G. Shiau

Several attempts have been made to account for the fact that grains in a fully recrystallized metal will coarsen on annealmg. Two fundamentally different hypotheses have been advanced, with several variations of each. One school considers that the cause of grain growth is the surface energy of the grain boundary. The theory of Jeffriesl that grain size and grain size contrast control growth is an example. The second school considers the primary cause to be a difference in the lattice energy on either side of the grain boundary. The more perfect grains are considered to grow at the expense of their less perfect neighbors, with a decrease in free energy, and a consequent increase in the stability of the system. Burgers2 presents the case for the strain or lattice imperfection theory of grain growth quite completely. The latter theory is attractive, since there is no doubt that differences in lattice energy or lattice perfection can cause grain boundary migration. A recrystallization nucleus grows for this reason as was beautifully demonstrated by van Arkel and Ploos van Amstel.³ Although it is generally stated that grain growth does not precede recrystallization, several workers4-5 have shown that small strains may induce a single crystal in an aggregate to grow, or at least may cause some grain boundary migration. The origin and nature of the imperfections that are considered to be responsible for normal grain growth have never been clearly described, but it is generally agreed that they are a consequence of the difficulty of atomic reorientation in the solid state, and that they do not seriously differ from the type of imperfection that can be introduced by mechanical deformation. An object of the present work was to determine whether the introduction of mechanical deformation would cause grain growth in a specimen which would not otherwise show it under the conditions used. It was also planned to determine the effect of such deformation on the rate of growth in a specimen which would show growth in the unstrained condition. Recently Maddigan and Blank6 have indicated that slightly strained specimens of alpha brass can undergo considerable growth prior to recrystallization if annealed at low temperatures. French7 has reported that at deformations less than 17 pet it is very difficult to detect the beginning of recrystallization in the same material. It was therefore planned to broaden this work to include a complete study of the microscopic behavior of alpha brass under condition~ of temperature, time, grain size and deformation such that recrystallization would not occur or would occur to only a Small extent. Experimental Procedure The brass was prepared by melting cathode copper and commercially pure zinc

Jan 1, 1949

For the seventh consecutive year, the value of nonfuel mineral raw ma¬terials produced in the US set a new record, reaching almost $20 billion-up 12.7% from the previous year, according to the US Bureau of Mines. The Bureau reported that this mineral production was the basis for about $200 billion worth of processed materials of mineral origin.

Jan 5, 1979

By J. E. Korski

Quebec Cartier Mining Co. operates a low-grade iron ore deposit at Lac Jeannine, Que., which is located at the extreme southwestern end of the Quebec-Labrador Trough (Fig. 1). The facilities there include one of the world's largest concentrators, a hydroelectric plant of 60,000 hp, and the modern town of Gagnon. A 191-mile railway connects the mine to the seaport situated at Port Cartier on the St. Lawrence River. The harbor in Port Cartier can accommodate both lake and large ocean- going vessels and is also the site of a major grain terminal. The concentrator in Lac Jeannine is designed to produce some 8 million tpy (tons per year) of specular hematite concentrate, containing 66% Fe, from approximately 20 million tons of crude ore. An annual stripping program of 5 to 8 million cu yd of waste rock uncovers the required ore. Approximately 100,000 tons of ore and waste are removed daily on a year-round, 24-hr-per-day basis. The open pit covers an area with maximum dimensions of 8,000 x 2,600 ft (Fig. 2). Present mining plans call for an ultimate depth of approximately 1,000 ft below original ground level. The rocks in the pit area are typical of this portion of the Grenville geological province. They consist largely of marble, quartz rock, pegmatite, iron formation, and stratigraphically older gneisses. The iron-ore formation consists of medium to coarse-grained specular hematite in a quartz host rock. The formation occurs locally in a plunging, anticlinal form. The topography in the vicinity of the mine is rolling, with maximum variations in elevation of about 400 ft. The hills are thickly wooded with birch, black spruce, and some tamarack. Lakes and muskeg areas are plentiful. Precipitation and temperature records have been kept since 1959. The annual rainfall has ranged between a low of 23 in. and a high of 42 in.

Jan 1, 1969

By T. E. Leontis

The importance of magnesium alloys in the manufacture of aircraft engines has been realized for many years. A concentrated effort has been exerted in the laboratories of the Dow Chemical Co. to develop magnesium-base alloys with improved properties at elevated temperatures whereby greater advantage can be taken of the inherent lightness of these materials. In an earlier publication, attention was called to the superior tensile properties and resistance to creep of cerium-containing magnesium alloys at temperatures up to 700°F. More recently, additional data on magnesium-cerium alloys have been furnished by Murphy and Payne. The present paper deals with the mechanical properties of sand-cast magnesium alloys containing zinc, at temperatures up to 500°F. The study includes binary Mg-Znt alloys containing up to 10 pct zinc and several ternary and some polynary alloys based on the Mg-~Zn,f Mg-jZn, Mg-4.4211, Mg-6Zn, and Mg-roZn binaries. The compositional variation in the tensile properties, hardness, and creep at room and elevated temperatures, and in the electrical conductivity at room temperature has been determined. The results of these tests show that many zinc-containing magnesium alloys exhibit resistance to creep at elevated temperatures significantly higher than that of present commercial magnesium alloys, but lower than that of alloys of the magnesium-cerium type. In addition, they have high tensile properties at room and elevated temperatures and high conductivity. This combination of mechanical properties and conductivity indicates that these alloys should be given serious consideration for commercial applications involving exposure to temperatures higher than those to which present commercial magnesium alloys can be taken safely. Literature The properties of sand-cast magnesium alloys containing zinc as a principal alloying element have not been investigated very extensively, especially at elevated temperatures. The following remarks, which are confined to sand-cast alloys, will serve as a summary of the most important references on this phase of magnesium metallurgy. The first recorded determination of the tensile strength of binary Mg-Zn alloys as a function of zinc content was reported by Aitchison. Similar studies, including the measurement of elongation and hardness, have been performed by Gann and Winston,' Dumas and Rockaert, Haugh-ton and Prytherch,6 and by Spitaler, the last being reported by Beck.' A slight superiority in the tensile strength of chill-cent Mg + 8 es alloy Over the sand-cast alloy was noted by Maybrey.8 That alloys of magnesium containing 5 to 12 pct zinc

Jan 1, 1949