By Keijiro Nishio

At a time of great antiquity when our Yomato tribe had not yet found its way throughout the country, there lived in Japan barbarous tribes of the stone age, whose dwellings were vertical caves covered with roof's of twigs and weeds. In a cave lately discovered at the village of Morita, 10 miles west from the port of Aomori, there were found pieces of micaceous iron-ore and psilomelane, with oval holes pierced from both sides. Apparently these objects were regarded as ornaments or curios, without being applied to any practical use. Among the traditions given in the Nihonshoki, an ancient history of Japan, there is one relating to the mining industry. According to this tradition, in the mythological age Izanami-no-Mikoto gave birth to Kanayamahiko-no-Mikoto, god of mines, and Amaterasu-Okami (the sun-goddess) was armed with swords. It came to pass at one time that she concealed herself in Ama-no-Iwato ("Heavenly Cave"), and several gods made contrivances to entice her out. Among them, Ishikori-dome, a smith, made a mirror with copper obtained from the Ama-no-Kagoyama, by means of a pair of bellows known as the Ama-no-habuki, which was made of a deer-skin. It is recorded also that Susanb-no-Mikoto, her younger brother, observed the abundance of gold and silver in Korea, where his descendants were to reign, and urged them to provide themselves with boats to convey them across the Sea of Japan. In the course of time he accomplished his object, proceeding to Korea with his son, Isotakeru-no-Mikoto. These accounts

Jan 1, 1913

By H. G. Moulton

THE INCREASING scale of mining operations over the past decade, particularly in connection with the exploitation of large bodies of comparatively low-grade copper ores, has made necessary the study of the behavior of rock under failure. When extractions of as high as 40,000 tons a day are reached in steam-shovel operations and as high as 20,000 tons per day in underground mining operations, it is evident that excavations soon become of such size that the behavior of the rock will often be dependent on fundamental principles applicable to more or less homogeneous materials under stress, rather than on weathering or local planes of weakness. In the ordinary rock excavations encountered in civil-engineering practice, such as excavations for subways, highways, railroads, etc., rock faces are not carried to depths sufficient to develop any pressures, or consequently any failures, except those due to loose masses resulting from local planes of weakness. When, however, orebodies whose tonnage is measured by hundreds of thousands are to be extracted by steam-shovel operations in open pits, it is necessary to determine if possible in advance the slopes that the sides of the pits will assume, for these slopes influence the shape of the excavations and thereby the amount of ore that may be extracted by the open-pit method. When large orebodies are mined underground at depths of 300 to 500 ft. (91 to 152 m.) by caving methods, the surface subsiding as the ore is withdrawn, it is necessary to determine in advance the outermost limits of fracture in the subsiding surface, for on the delineation of these limits depends the location of surface improvements, mills, smelters, etc. and also the location of development work, such as hoisting shafts, main haulage levels, and all other underground openings that must remain undisturbed during the period of ore extraction. Heretofore, in civil-engineering practice, it has been assumed that earth and rock behave differently in failure. For the calculation of earth

Jan 2, 1920

By A. W. Fahrenwald

The physics and chemistry of the flotation process are not well understood. Many papers dealing with the theory of flotation have been published but most have been narrow in their viewpoint. No theory advanced has done more than explain, more or less satisfactorily, various isolated phenomena. Scientists have done little with the problem, doubtless because they have not seen sufficient of the practical side of the subject to have their interest aroused. Any attempt to explain the mechanism of flotation that considers only contact angles, surface tension, adsorption, the floating of needles, flocculation, or any other single and narrow phase of the question is sure to be disappointing. Flotation is a problem of colloid chemistry and must be studied as such. In a broad general way, flotation is a process involving and operating by virtue of surface reactions. The term "surface reactions" may be open to criticisms. Many chemists give the term "reactions" a definite and restricted meaning and to such the term may connote change in atomic grouping in strict stoichiometric ratios. While Langmuir looks upon adsorption as a reaction, and there is much evidence in support of this view, we may look on adsorption as a physcial process as far as this paper is concerned. The term seems well suited to the work in general. Presumably these reactions are reactions between the same kinds of forces (electrical) and differ only in degree and in the surface manifestations produced. This premise seems logical if we accept the theory that the atoms of dl elements are made up of grains of electricity, having mass and charge, called electrons; and that atoms differ from one another only in the number and arrangement of the electrons about a positive nuclear

Jan 1, 1924

J. L. CHRISTIE, Chairman T. S. FULLER, Past-chairman W. M. PEIRCE, Vice-chairman W. A. SCHEUCH, Vice-chairman E. M. WISE, Secretary International Nickel Co., Bayonne, N. J. W. M. CORSE, Treasurer Executive Committee H. A. BEDWORTH G. O. HIERS D. K. CRAMPTON R. H. LEACH E. H. DIX, JR. R. F. MEHL J. A. GANN J. WALTER SCOTT' JEROME STRAUSS Finance Committee T. S. FULLER, Chairman W. M. CORSE H. S. RAWDON C. H. MATHEWSON SAM TOUR

Jan 1, 1934

W. H. BASSETT, * Waterbury, Conn.-Manganese should not be expected to remedy all the defects that are due to poor melting practice. It is undoubtedly valuable in helping to eliminate porosity in many of the alloys. In the copper-nickel alloys, its use is becoming almost universal, for, beside helping to make sound castings, it tends to hold the carbon in solution in the solidified alloy. GWILLIAM H. CLAMER,? Philadelphia, Pa.-I have found that manganese copper is satisfactory for eliminating sulfur and that it works very well in the crucible and when you have reducing conditions; but in a large reverberatory charge, where the conditions are oxidizing, we were not able to eliminate the sulfur.

Jan 1, 1919

By W. Joseph Schlitt

The types of copper leaching and recovery operations in the United States are reviewed, along with characteristics and trends in the industry. The contribution of the various leach operations to total mine output is discussed in order to provide a perspective on the relative importance of copper leaching as a method of production.

Jan 1, 1980

By Wayne C. Hazen, James K. Kindig

As the complexity of hydrometallurgical systems increases, it offers new opportunity for applications of solvent extraction. However, the high capital cost of mixer-settlers for large flow rates is a drawback to wide application in base metal recovery. This paper presents information on the use of cyclone separators in place of settlers with attendant significant reduction in capital cost. Various flowsheet possibilities for this development are discussed.

Jan 1, 1972

By E. V. Crane

A tremendous volume of the metal rolled annually into sheets strips and coil stock finds its way to a host of stamping and manufacturing plants which are the quantity production units of the country. Considerable in volume, too, are the rolled and extruded rods which go into forging and manufacturing plants for conversion into the same general line: those widely sold metallic necessities and luxuries of the household, the office, transportation, farming and building construction. Yet, in spite of its age and its importance, the stamping trade has been doing its "engineering" largely by trial and error. Its distinctive method is shearing out and plastically working metal to finished shape in a few quick strokes with high loads and expensive tools which are warranted only by large quantities to be produced. The principal operations have many features In common with rolling and wire-drawing methods. Combinations of stresses are diffcrent, however, and details of operations are infinite in variety. An engineering study of the subject begins with stress analysis, but must go back to metallurgy for its foundation. A grouping of pressed-metal working operations according to whether the metal is (1) sheared, (2) bent, (3) drawn or (4) squeezed has proved useful. All of these groups include instances of both hot and cold operations. For discussions of metal working properties, the division between hot and cold working is taken as the recrystallization range of temperature. This, of course, brings tin, lead and often zinc into the hot-work range at or near room temperature. The outstanding hot-working press field is in forging: particularly of brass; all of which is included in the squeezing group. Shearing Operations The shearing group of operations, including blanking, piercing, trimming, shaving, slitting, shearing, notching, parting and numerous variations and combinations of these enters once or more into the production schedule of practically every stamped or forged article. The transverse stress, set up in shearing, as shown in Fig. 1A, is a combination of an angular compressive thrust and a tensile stress which is also at an

Jan 1, 1931

By S. R. Goodman, Hsun Hu

The formation of secondary - recrystallization tex-tlires in cube-textured 18-8 stain less steel (Type 304) Ilas been studied at three temperatures. Prolonged annealing at 100°'C protluces a PredoninanGly (520) [OOZJ-type texture, which is related to the cube te.ture of the primary lnatrix by a rotation of approxivzately 22 deg around the [001] axis in the rolling direction. Annealing at 1200 or 1300°C facers the formation of the (123)[272/-type texture, which is related to the matrix texture by a [111] rotation of app.voxiniately 40 deg. These observations suggest that in the secondary recrystallization of cube-texlut-ed stainless steel an apparent actilation energy for growth is higher for grains related to the tncrtuix Og [111] rotations thun those reloted by [100] rotations. THE formation of secondary-recrystallization textures in cube-textured primary matrices of fcc metals has been studied widely by various investigators. For Fe-40 pct Ni alloys, Pawlek' and wassermann2 reported that the orientations of secondary grains were related to the cube texture by rotations of 30 and 38 deg around [001] in the rolling direction. However, Rathenau and custers3 found that, while in one Fe-48 pct Ni alloy, most of the secondary grains were oriented with respect to the cube-textured matrix by rotations around [001] of 26.5 deg, in another alloy of a different origin, the orientations of secondary grains were related to the cube texture by rotations of approximately 35 deg around a [lll] axis. Similar orientation relationships were also observed between the secondary grains and the cube-textured primary matrices of copper.4"a No attempt was made to differentiate these two types of orientation relationships; reorientation by either a [111] or a [100] rotation was considered to be equally favored. The present investigation consisted of a study of the secondary recrystallization textures in cube-textured stainless steel. It was noted that the secondary grains formed in stainless steel were considerably smaller than those of Fe-Ni alloys or copper. This offered the advantage that the secondary recrystallization texture could be determined by the texture-goniometer technique, and a more detailed study of the textural development during the course of secondary recrystallization could be made. The effect of annealing temperature on the formation of secondary-recrystallization textures was also investigated. MATERLAL AND METHOD It was shown earlier"-" that a strong cube texture can be obtained in 18-8 stainless steels by rolling at 800°C to produce the copper-type deformation texture, followed by annealing at 800" to 1000°C for recrystallization. To improve the cube texture for the present study, a commercial-grade 18-8 stainless steel (Type 304) was rolled at 800°C first to 5 mm (0.2 in.) thick plates. Three of these plates were then stacked and welded together along the edges into a sandwich assembly. After annealing at 900°C for 20 min: the assembly was finally rolled at 800'C to 90 pct reduction in thickness with reheats and end-for-end reversals after each pass. Only the central strip, which was reduced from 5.0 to 0.50 mm (0.7 in. to 0.020 in.) thick, was used. The chemical composition of the steel in weight percent was as follows: C, 0.06; Mn, 0.38: Cr, 18.71; Ni, 9.56: P, 0.011; S, 0.009; and Si, 0.39. The purpose of rolling the strip in a sandwich assembly was to prevent direct contact between the central strip and the rolls. It was observed earlier" that, when the strip was rolled at 800°C without being enclosed in a sandwich assembly, the cube texture obtained by subsequent annealing at 900" or 1000° C for recrystallization was largely confined to the central section of the strip, while most of the recrystallized grains formed in the surface section of the strip were not cube-textured. This was obviously due to the fact that the actual temperature at the strip surface during rolling, as a result of direct contact between the strip and the cold and massive rolls, was considerably lower than 800°C. By using a sandwich assembly for hot rolling, the cube texture obtained upon subsequent annealing for recrystallization was found to extend through the entire thickness of the strip. After rolling, the central strip was taken from the sandwich assembly. and cut into specimens. Prior to annealing. the specimens were etched to 0.25 mm (0.010 in.) thick. A tube furnace provided with a purified, dry argon atmosphere was used for annealing. Textures were determined by the reflection technique. using a Siemens automatic texture-goniometer and ZrOz-filtered MoKa radiation. With a time constant of 4 sec. the preferred orientation of the secondary grains could be measured satisfactorily by the integrated intensities. Both (111) and (200) reflections were measured, and corresponding pole figures were constructed according to the techniques described previously.10 The agreement between results deduced from these two reflections was excellent. RESULTS AND DISCUSSION Secondary-Recrystallization Texture due to Prolonged Annealing at 1000°C. Fig. 1 shows the primary-recrystallization texture of a specimen annealed at 1000°C for 30 min. A substantial improvement in both sharpness and intensity of the cube texture, owing to the present processing method, can be noted readily by comparing Fig. 1 with similar pole figures shown earlier in Refs. 9 and 11. Secondary recrystallization

Jan 1, 1967

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.' Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler's saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.' A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By Albert Sauveur

This paper explains the possibility of using advantageously a boiling solution of sodium picrate to reveal dendritic segregation in steel. The mechanism of the action of the reagent is described. The failure of manganese alone to produce persistent dendritic segregation is also considered. IRON, like other metals, solidifies through the formation of dendritic crystals; iron alloys forming solid solutions, like other solid solutions, solidify likewise through the formation of dendritic crystals. The alloying elements or impurities as well as the inclusions segregate generally in the interstices, or "fillings," between the axes and branches of the dendrites; that is, in the portions last to solidify. This results in dendritic segregation or heterogeneity, which is generally persistent and makes possible the revelation of the dendritic crystallization of the metal through the selective action of a suitable etching reagent.1 For this purpose, a cupric solution, such as Le Chatelier's, is generally used, copper being deposited on the pure, or relatively pure, ferrite present in the axes while the fillings remain free, or relatively free., from copper deposition. The dendritic structure, formed on solidification in a steel containing 0.50 per cent. carbon, 0.37 per cent. manganese, 0.12 per cent. silicon, 0.07 per cent. sulfur, and 0.035 per cent. phosphorus is shown, after treatment with Le Chatelier reagent, in Fig. 1 under a magnification of 8 diameters. Commercial steel always contains inclusions of manganese sulfide, which are located in the fillings of the dendrites. Comstock has shown that boiling sodium picrate imparts a dark coloration to these inclusions. We find that this reagent likewise reveals dendritic segregations in commercial steel, as shown in Fig. 2, under a magnification of 8 diameters, which represents the same spot as that shown in Fig. 1. The fillings

Jan 2, 1924

By A. G. Spillette, R. L. Nielsen

The purpose of this paper is to further the understanding of reservoir response to hot-water injection by desuribing a two-dimensional, mathematical model of the process. Key assumptions are that no gas phase is present, and that the injected fluid reaches thermal equilibrium instantaneously with the reservoir fluids and sand. The resulting system of three partial differential equations is solved simultaneously through the use of a "leap-frog" application of standard alternating direction implicit methods for the solution of the mass-balance equations and the method of characteristics for solution of the energy-balance equation. The utility of the mathematical model is demonstrated by comparing numerical and analytic temperature distributions for hot-water bank injection and by comparing calculated with observed field behavior. Additional calculations show that hot waterfioding can recover significantly more oil than cold waterflooding, and that a hot-water bank recovers, with less energy input, nearly as much oil us continuous injection. Introduction Consistent field success with hot fluid injection processes requires good reservoir description and a thorough understanding of recovery mechanisms. The latter is fostered by a combination of well designed experimental studies and physically sound mathematical modeling. The purpose of this paper is to further the understanding of reservoir response to hot-water injection by describing a two-dimensional mathematical technique, indicating its validity, and demonstrating its utility for studying the effects of reservoir and operating parameters. Published experimental studies of hot fluid injection processes are few." Even if extensive data were available, two considerations discourage exclusive reliance on laboratory or field work. First, because of the severity of scaling requirements," laboratory results must be interpreted with care. Second, because of the one-shot nature of field experiments — injectivity/productivity tests and pilot floods—results seldom are available over the desired range of operating conditions. These factors emphasize the need for devoting attention to mathematical modeling to complement laboratory and field work. Through the use of mathematical models, scaling uncertainties can be bridged and response can be predicted for unique combinations of reservoir and operating conditions. Numerous mathematical models developed during recent years enable us to calculate temperature distributions, thermal efficiency (or conversely, fraction of heat lost), and oil recovery behavior for hot fluid injection. Ramey" and Spillette' recently have provided reviews of these methods. Most models have concentrated on predicting temperature distributions and thermal efficiency; few have been directed at predicting oil recovery.'."1° Although these techniques are useful for estimating effects of reservoir parameters and operating conditions on process performance, results are limited by the assumptions made and by the methods of coupling independently solved fluid-flow and energy-balance equations. A computer-based method is presented for predicting total reservoir response to hot-water injection that obviates most simplifying assumptions. The model simulates fluid flow and heat transfer in two dimensions within a vertical cross-section spanning the oil sand and adjacent unproductive strata. Known numerical procedures are used to solve the governing partial differential equations. The mathematical model handles the effects of reservoir heterogeneity, gravity, capillarity, relative permeability and temperature-dependent fluid properties. In addition, a wide range of operating conditions can be modeled, including hot-water followed by cold-water injection. Mathematical Description of Hot-Water Injection Key assumptions in the mathematical model for hot-water injection are that (1) no gas phase is present and (2) the injected fluid reaches thermal equilibrium instantaneously with the reservoir fluids and sand. Relative permeability and capillary pressure are assumed independent of temperature. Darcy's law for multiphase fluid flow relates the velocities of the oil and water phases to the phase pressure gradients by the following relations:

Jan 1, 1969

By B. M. Larsen, W. E. Shenk

This paper describes a method of reversal control of the open-hearth furnace that obtains in practice those effects considered below as essential to a completely automatic control, without appreciable interference with the natural rise and fall in temperature of the regenerative portions of the furnace system. Growing out of some studies of radiation pyrometry in open-hearth regenerators, it was developed during 1934-1938, and has been successfully applied to a number of commercial furnaces. The goal of open-hearth furnace operation is the highest rate of production of steel of proper quality consistent with good refractory life and fuel economy. This requires rapid heat transfer from furnace to charge, which in turn is dependent upon heating the furnace refractories to the highest safe operating temperature. The greater the heat input to the melting chamber, the sooner this limiting temperature will be reached, so that control methods in general that are designed to protect against overheating of refractories should help to maintain maximum fuel input and production rate. For the typical open-hearth system, with fixed regenerator capacity and with rate of fuel input usually restricted in its range of variation, our basic assumption is the idea that the only other important variable —that is, the time interval between successive reversals—should also be held constant or within a small range. The present reversal control was designed therefore so that, under normal operating conditions, no arbitrary limitation is imposed other than to keep the reversal interval within the optimum time range. However, since a near approach to completely automatic operation involves protection of refractories through the balancing of furnace end temperatures as well as emergency protection against temperature peaks above some upper limit, it was also felt essential to employ, as an integral part of the control unit, a temperature-measuring instrument to register the true temperature of the refractory surfaces at some critical region in the hot ends of the regenerative zones. As the basic elements of the control, we thus have one "maximum" and one lLminimum" time relay and a potentiometer recorder-controller, combined with switches and relays to operate as follows: I. Reversal normally occurs within an optimum range limited by the maximum and minimum settings to about 4 to 6 min. variation, but the actual interval usually is less variable and closer to the minimum setting. 2. The margin between minimum and maximum time is utilized, together with a "floating temperature limit" in the potenti-ometric control instrument, to correct any tendency toward temperature unbalance between ends of the furnace. 3. A second "maximum temperature

Jan 1, 1945

By Leendert de Witte, Fred J. Radd

In many areas caring failures can be directly related to electrical currents observed in the casings. It is the thesis of this paper that the observed casing currents are mainly due to electrochemical potentials of the type in evidence on spontaneous potential curves of electrical logs. The general nature of these potentials are discussed and an equivalent circuit is given for current and potential distributions around open holes. The casing forms a short circuit to these potentials and tends to average the effects of local cells. The case of casing corrosion opposite the Dakota water sands in the salt-mud area of Kansas is discussed anil used us a qualitative, illustration of the relation between SP's and casing currents. A method of quantitative derivation of casing current distribution frorn electric log SP curves, using linear transform theory, is described and results are compared with a measured current profile. The effects of hydrogen over-potentials at the cathodic portions of the pipe are considered and some laboratory data are given in support of conclusions regarding the over-1.01tuge.s. INTRODUCTION To date an appreciable amount of work has been done on the measurement of oil well casing currents and on the correlation of the anodic portions of the current profiles with corrosive casing failures. Speculations on the origin of the casing currents have, however, remained rather vague; and although almost every plausible cause has been mentioned, there is to the writers' knowledge no clear-cut expose' on the details of the causes of the corrosive currents in the literature. A study of current surveys and casing failures in the N.W. Burnett field, Ellis County. Kan.. indicated the probability that concentration cell emf's between the Wellington salt section and the relatively fresh waters in the Dakota sands were a major cause of the corrosion currents. A more general concept evolved upon analysis of the severe corrosive conditions in the Pleistocene sands in the Ventura Avenue and San Miguelito fields in California. In this area no major variations in the salt content of the formation waters occur and yet large casing currents are observed. An explanation is found in the fact that the local spontaneous potentials which are set up due to concentration contrast between the drilling fluid and the connate water are short circuited when casing is set. The very conductive path through the casing increases the magnitude of the currents and has the tendency to average local sources over fairly large intervals. Current will flow between the sections that are predominently shaly and the sections that are mostly sandy. At the places where the current leaves the pipe, corrosive attack will occur. This same phenomenon will be present wherever unprotected pipe is set through sections that show large SP kicks on the electric logs over reasonably thick interval~. GENERAL- NATURE OF THE SPONTANEOUS POTENTIALS When a sequence of sedimentary rocks is penetrated by a drill hole filled with a mud which has a different salt concentration from that in the formation waters, various types of electrochemical potentials are established between the formations and different parts of the mud column. Opposite clean sand sections. a simple liquid-liquid junction potential will be observed; while opposite argillaccous formations, a membrane potential, often referred to as shale potential, will be established. The first quantitative analysis of these emf's in terms of liquid junction and membrane potentials is due to Wyllie.1

Jan 1, 1956

By J. P. Pritchard, J. T. Pierce, O. G. Slay

This paper discusses the results of a technology-evaluation program to ascertain the feasibility of a piotornask-photoresist technology developed for fabrication of multiple-layer thin-film superconductive circuitry. The uehicle selected for this evaluation was a 120-bil associative data processor requiring a set of nine photomasks to define a similar number of patterned material layers of lead, tin, and polymer insulation. A total circuit area of 4 sq in. involved 2500 actitle and 12,000 passive crossings. Several short-free, electrically continuous specimens were satisfactorily completed under this program. Problems encountered in the preparation and use of the requi-ed set of Photomasks are discussed, as also are the problets of providing suitable external connections. A major retarding factor in the development of the superconducting thin-film cryotron technology for many years was the absence of batch fabrication means yielding necessary device density and count per substrate for practical applications. Early workers in the field desired only limited numbers of devices to permit careful study of discrete devices and representative circuitry integrating logic and memory capabilities. For these purposes mask stencils could be formed to selectively control the placement of materials, sequentially vapor-deposited in vacuum, to form the multilayer structure. In general a distinct pattern was required for each material layer; therefore, mechanical provisions were required to change not only the material source, but the patterning mask as well, before each deposition. All deposition steps were preferably performed in a single evacuation of the deposition chamber. Thus the means for storing, transporting, and registering masks and sources with respect to the substrate existed and were operated within the vacuum environment. In the authors' experience, the approach was and remains serviceable for preliminary device study, but was not extensible to an economical manufacturing method by virtue of the difficulties inherent in mask stencil preparation and use, and the capital investment implicit in the mechanization requirements. Since the commercial attraction of the cryotron technology stems principally from its potential for economical batch fabrication, the authors' program has placed major emphasis on fabrication methods. A highly useful method has evolved through adaptation

Jan 1, 1967

By Michael J. Callow

THE PROPERTY of Mount Isa Mines, Ltd., is located at Mount Isa, Northern Queensland, Australia, at roughly 20" south latitude. It is 600 miles from Townsville on the east coast, the port for Mount Isa, 1200 miles from Brisbane and approximately 1600 miles from Sydney in New South Wales. Living conditions in the camp, though wild and crude at the commencement of building, are now excellent and little has been left undone to provide comfort and attractiveness. The climate being warm and dry, many of the buildings are built on posts, 8 to 10 ft. off the ground, with spacious screened-in verandas. Club houses, stores, school, hospital and ice plant have all been provided by the company as well as modern conveniences, such as running water, shower baths, electric lights, septic tank arrangements, tennis courts and amusement grounds.

Jan 1, 1932

By E. P. Polushkin, Henry L. Shuldener

THIS paper describes the results of microscopic examination of a series of brass pipes removed from apartment and office buildings in New York City, adjacent localities on Long Island, and Philadelphia. They were selected as typical of approximately four hundred pipe specimens obtained over a period of five years during an investigation of corrosion in hot-water installations. A part of the investigation is reported in this paper and includes a brief history of the pipes, a description of their inside surface and microstructure, and a study of the effects of corrosion, with particular reference to the structural aspects of local and selective dezincification. Although the bibliography on the corrosion of brass pipes is quite extensive, it refers almost entirely to corrosion in sea water. The authors believe that their examination of this series of pipes, which had been subjected to the corrosive action of fresh water for various lengths of time, may throw some additional light on the problem of corrosion. PIPES EXAMINED The pipes were made by different manufacturers and their sizes range from ¾ in. to 4 in. nominal inside diameter, the majority being within I to 2 in. They can be divided into two groups according to chemical composition: (I) with a copper content of 60 to 62 per cent and (2) with a copper content of 65 to 68 per cent. The first group (pipes made of Muntz metal) comprises 22 pipes and the second (pipes made of high brass) comprises 18 pipes. The pipes had been in service in various locations in the hot-water systems of the buildings involved. Some were taken from horizontal lines in the basement, some from overhead distributors and some from vertical risers. The distance, in terms of feet of pipe, of the specimens from the hot-water generator was no less than 75 ft. and often 100 to 300 ft. In the majority of cases the water-heating equipment was provided with a regulator to limit the temperature of the hot water supply. The normal range of temperature in pipe systems of this kind is 100° to 160°F. WATER SUPPLIES The average chemical composition of the water supplies carried by the pipes is shown in Table I. In evaluating the corrosiveness of a natural water, four factors are considered of prime importance: namely, hardness, alkalinity, pH and silica content. The waters listed in Table I are characterized by relatively low hardness, low alkalinity, low pH and low silica content. The waters of lower pH and higher CO2 content are more corrosive. A characteristic of all of these waters is that they do not deposit a protective mineral coating as do waters with high bicarbonate of lime content, which would be reflected

Jan 1, 1944

By Thomas F. McLoughlin, David K. Hylbert

A new method of satellite imagery analysis has been developed during underground mine roof research. Landsat positive film transparencies were projected onto topographic base maps to scale and lineaments enhanced with a Ronchi grating (method A). Thirty-five millimeter slides of video-enhanced scenes were also projected onto base maps (method B). Both methods permit direct plotting of lineaments to scale and direct correlation with surface and subsurface data wing transparent overlays.

Jan 1, 1981

By J. F. Stiehr, R. L. Sanford, T. L. Myers

This paper summarizes the development of a Directory of Computer Programs Applicable to US Mining Practices and Problems. The directory is funded by the US Bureau of Mines and includes a sampling of computer usage in operating and manufacturing companies, consulting firms, computer companies, research organizations, universities, and various US government agencies. General references to computer applications throughout the mining industry are discussed as well as the availability of programs to interested organizations or individuals.

Jan 9, 1979

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W. FRANCIS, Chairman, WILLARD S. MORSE, Vice-Chairman. THOMAS -T. READ, Secretary, Woolworth Bldg., New York: N. Y. P. A. MOSMAN, Treasurer. LOUIS D: HUNTOON. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W. RODDEWIG, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 10, 1914