By Richard H. Olson

"Rarely in our technological society does the discovery of a new class of inorganic materials result in such a wide scientific interest and kaleidoscopic development of applications as has happened with the zeolite molecular sieves." The foregoing, the opening sentence in a landmark volume on zeolite molecular sieves by D. W. Breck (1974), is, if anything, an understatement. Zeolites were recognized as a new group of minerals in the 1750s, but it was not until 1930 that the first analysis of the crystal structure of a zeolite mineral was made. In the late 1940s research workers at Union Carbide Corp. began a program of zeolite synthesis and study which has resulted in one of the major research achievements of all time. Naturally, with the vast research and development efforts devoted to the synthetic molecular sieves, Union Carbide became concerned in the mid-1950s about its position should minable deposits of natural analogues be discovered. Zeolite minerals have diverse origins, and even a brief discussion of these is beyond the scope of this paper. The early work on zeolites was confined to igneous rock occurrences (e.g., amygdules and veins) which were formed by "space-filling;" these crystals tend to be euhedral, thereby rendering them appealing to both mineralogists and collectors. During the first year or so of Union Carbide's exploration (which began in mid-1957) attention was devoted solely to such igneous occurrences. A landmark paper by Bramlette and Posnjak (1933) heralded the potential significance of the occurrence of zeolite minerals as alteration products of vitric ash and similar materials. In the summer of 1958, full attention was directed by Union Carbide to the search for deposits of this type in the western United States. Since then, such exploration has been continu-

Jan 1, 1975

By L. W. McKeehan

THE occurrence of twins in large ferrite crystals, made by a new process, was reported in a recent note. This paper describes a typical case of such twinning and suggests, on the basis of the observed facts, why smooth slip-planes are rarely observed in this metal. METHOD OF PREPARATION The material In which the crystals here dealt with were grown was made from 1/8 -in. Armco iron welding rod containing C, 0.04; S, 0.037; P, 0.003; Si, 0.008, and Mn, 0.02 per cent. This rod was cold drawn into wire about 1 mm. dia. A piece of this wire was supported vertically and was locally heated in hydrogen at atmospheric pressure to about 1400° C. by an alternating current (60 cycles per sec.) of about 35 amp., passed through it between a pair of travelling contacts about 8 cm. apart. The rate of travel for the case in hand was 12 cm. per hr. After some 30 cm. of the length of the wire had been heated and cooled in this manner the whole wire was immersed for a few seconds in dilute nitric acid, not restrained by alcohol. Etching was continued until, as nearly as could be judged by eye, the original smooth cylindrical surface of the wire was no longer capable of specular reflection.

Jan 1, 1927

By R. D. Nelson, S. D. Dahlgren

The conditions of temperature, strain rate, and total strain favoring deformation by grain boundary sliding, slip, or deformation with concurrent recrystallization were evaluated for alpha plutonium. Grain boundary sliding and slip were studied by examining structures formed on polished surfaces with 4.5 pct compressive deformation. The conditions required for recrystallization were determined from compressive deformation us time curves. At 110" C and at a strain rate of 10&apos;per min, deformation was almost exclusively by grain boundary sliding whereas slip was the predominant deformation mode at -10°C and lo-&apos; per min. Defarmation at intermediate tenzperatures and strain rates produced structures showing mixtures of grain boundary sliding and slip. Recrystallization occurred concurrently with deformation only after a critical strain was reached. About 14, 6, and 3 pct strain was required at 105", llO°, and lZO°C, respectively, before recrystallization started, irrespective of the strain rate in the range of lo-&apos;1 to 10&apos;4 per nzin. L HE temperature and strain-rate dependency of the modes of plastic deformation were evaluated for high-purity as-cast alpha plutonium. The techniques used to study slip and grain boundary sliding were similar to those employed previously for alpha plutonium by Bronisz and Gorum,&apos; and spriet.&apos; Recrystallization was investigated using the methods reported by Nelson.3 Bronisz and Gorum&apos; found that slip occurred on more than one slip system at room temperature, and suggested that grain boundary sliding also contributed to the deformation. spriet2 found that deformation was predominantly by slip at room temperature, and observed one to three orientations of slip traces in individual grains. In addition, he deformed polished samples at 10O° C, but concluded that the deformation character of alpha plutonium at 100° C and at room temperature were not essentially different. Several investigators reported that twinning was only occasionally observed.1&apos;2&apos;4 Nelson3 recently found in creep tests that high-purity alpha plutonium would recrystallize concurrently with compressive deformation at temperatures between 25" and 115°C. EXPERIMENTAL PROCEDURE Electrorefined plutonium having less than 300 ppm total impurities was received from Los Alamos Scientific Laboratory in the form of +-in. diarn cast rods. Major impurities were americium, <I00 ppm, and tungsten, (60 ppm. Less than 25 ppm each of other impurities were present. The rods were cut into right half-cylinders 0.35 in. long and 0.25 in. in diam, and the flat faces along the cylinder axes were metal-lographically polished. To avoid loss of the metallo-graphic polish by oxidation, the polished samples were deformed in a silicone fluid heat treating medium contained in a chamber evacuated to a pressure of lo-&apos; torr. Deadweight loading was used to compress the samples between 4.5 and 20 pct at strain rates between 10"4 and lo- &apos; min-&apos;. Strain rates were determined by dividing the total deformation by the elapsed time of the test, even though the strain rate was not constant during deformation. Curves of strain vs time for samples deformed with a constant compressive stress3 show that the strain rate changes by less than a factor of four during the testing of a given sample, which is small compared to the three orders of magnitude change in strain rate investigated. Two samples were loaded into an ordinary metallographic mounting mold and impacted by striking the mold piston with one blow of a 2-lb hammer. Deformation temperatures for the two impact samples were 25" and 90°C. The samples, following deformation, were washed in carbon tetrachloride and their polished and deformed surfaces were immediately inspected metallographi-cally. Subsequently, the deformation structures were replicated with acetate replicating tape for later electron microscope examination, and the samples were then repolished and etched to reveal the microstruc-tures of the deformed metal. Second-stage carbon replicas were prepared from decontaminated acetate replicas using the procedure developed by Miller, Bierlein, and astel.&apos; Additional samples, which were 0.35 in. long by 0.25 in. in diam, were used to obtain constant load deformation vs time curves. These samples were deformed 10 to 20 pct with loads of 15 and 20,000 psi at 120°C; 30, 45, and 55,000 psi at 110°C; and 20 and 30,000 psi at 105°C. Samples were polished and etched to determine whether or not recrystallization or twinning had occurred during deformation. RESULTS AND DISCUSSION The experiments showed that alpha plutonium deforms by grain boundary sliding, slip, and deformation with concurrent recrystallization. Deformation by twinning was insignificant. Metallographic examination of polished and deformed surfaces revealed grain boundary sliding and slip. The start of recrystallization was ascertained from constant load deformation vs time curves. Deformed surface structures of samples compressed 4.5 pct under four different conditions of temperature and strain rate, Fig. 1, show how the deformation mode changes from predominantly grain boundary sliding to predominantly slip with increasing strain rate and decreasing temperature. Deformation at 110°C and 10" 4 min-&apos;, Fig. l(a), was predominantly by grain boundary sliding. Only a few slip traces can be seen in Fig. l(a).

Jan 1, 1969

By H. O. Hofman

With the exception of the exhaustive paper on the Father de Smet mill, by its designer, Mr. A. J. Bowie, Jr. (Bans., x. 87), nothing, so far as the writer is aware, has as yet appeared on the stamp-mills of the Black Hills of Dakota, although they have been steady producers for the last ten years. Within the small area of about 6000 by 1600 feet, $2,271,341.14 was produced in 1887† from rock averaging $4 per ton in free gold. I. The Ores. Character of the Ores.—The gold of the district is found in quartz and pyrites finely distributed through vast bodies of mica- and amphibole-schists, argillites and phyllites, and also impregnating the schists themselves. The " Belt," embracing the section of Lead City, Terraville and Central City, is the only part worked at present. The principal associated mineral is iron pyrites, with some arsenopyrite and chalcopyrite, garnet and asbestos. The ores from open cuts and upper levels are more free-milling. than those from underground workings below water-line. Hence

Jan 1, 1889

By R. G. Gifkins

Mean boundary migration depended linearly upon creep extension under various conditions. Prolonged annealing or air-casting increased the proportion of immobile boundaries at a given stage of tests. Grain growth during annealing followed a power law. The linking of migration and sliding in creep and models for migration are examined; activation energies are calculated from these models. Segregation of oxygen to boundaries appears to be a controlling factor. THE idea that boundary migration and boundary sliding during creep are linked has often been suggested,&apos;-5 especially when evidence has been obtained for an alternation between the two processes. In simple bicrystals sliding can occur without any migration6 but in more complex bicrystals7 it is observed. McLean&apos; and Couling and Roberts 5 made measurements of both sliding and migration; McLean concluded that there was no linking of the two processes whereas Couling and Roberts supported the idea. McLean&apos; also developed a model for migration during creep and annealing. The present work was initiated as part of a study of the recrystallization of lead during creep9 but has been extended to examine some aspects of the mechanism of migration. MATERIALS AND METHODS Specially refined high-purity lead* was used; the total of impurities, excluding oxygen, was 0.0008 wt pct. Oxygen was removed as far as possible by melting in vacuo, treating at 550" to 600°C with hydrogen and then casting at 450°C under a vacuum of 10-2 mm Hg; the oxygen was then believed to be 0.00005 wt pct. Specimens were made from extruded strip and then annealed at the required temperature in an air oven, controlled to 5 lac. They were then polished in a mixture of acetic acid and hydrogen peroxide. At this stage some specimens were etched to give grain contrast and their grain sizes determined by the intercept method. Migration of boundaries during creep was measured on the surface of polished (not etched) specimens, directly loaded at room temperature (22°C) or 50°C (52"C) to initial stresses of 300 to 700 1b per sq in. Twenty six vacuum-cast hydrogen-reduced specimens were used and, in addition, two specimens were from material air cast after hydrogen reduction ("partial" air cast) and two from air-cast material not treated with hydrogen ("full" air cast). Duplicates were made in the majority of tests. At intervals through the creep tests, specimens were unloaded and the migration measured, normal to the direction of migration at the point of measurement, for each boundary along standard traverses. Usually between 110 to 180 boundaries were measured at each of some twelve stages of the tests. Migration was measured on the projected image (X100) using prism illumination. Fig. 1 illustrates the method of measurement and shows the kind of variation of migration found from boundary to boundary and along particular boundaries. Fig. 2 gives an example of more extensive migration. The mean value of distance migrated was generally reproducible to *10 pct but occasional points gave a scatter of *20 pct. The correctibn applied by McLean8 to allow for the contribution sliding makes to the apparent distance of migration could not be used, for the sliding at most boundaries was too small to measure with the equipment available. There were two reasons for supposing the correction unnecessary in the present work;

Jan 1, 1960

By J. Gordon Parr, D. H. Polonis

The formation and subsequent decomposition of metastable phases in Ti-Ni alloys containing up to 11 pet (atomic) Ni have been studied. The decomposition of a completely retained ß phase and of a completely transformed 8 phase in a 6 pet alloy has been followed by X-ray diffraction and metallographic methods and by hardness determinations made during the process. The possible mechanisms of the reactions are discussed. PREVIOUS investigations of the Ti-Ni system have usually been limited to phase diagram studies; but little attention has been given to metastable phases and tempering processes. These are important, however, since equilibrium conditions are rarely achieved—nor, perhaps, are they desired—in practice. Up to the present time the available transformation data for titanium alloys appear to be restricted to isothermal transformation curves for selected binary and ternary systems. No quantitative studies have been made of the mechanism by which equilibrium is approached. Several independent investigations have been carried out to determine the Ti-Ni phase diagram. Early work by Wallbaum&apos; and later by Long et al.&apos; produced tentative phase diagrams which were not representative of true binary conditions, since the alloys were contaminated with oxygen and nitrogen. The most recent diagram (Fig. 1) is due to Margolin et al.," and a slight modification of the a + ß/ß boundary (shown dotted) has been proposed by McQuillan.&apos; The structure of the phase Ti,Ni was shown by Duwez and Taylor" to be face-centered-cubic, with 96 atoms per structure cell. The formation of a martensitic ß phase (close-packed-hexagonal) in Ti-Ni alloys has generally been observed when specimens of low nickel content are rapidly cooled from the 0 (body-centered-cubic) range. Margolin et al. reported an increasing tendency for P to be retained in lump specimens as the nickel content increases. McQuillan&apos; has studied the effect on the microstructure of delay time in quenching, and has reported the formation of pro- eutectoid a precipitate in a quenched hypoeutectoid alloy. In a previous study of Ti-Fe alloys," experiments were made on powder specimens produced by filing alloy ingots. Techniques were devised for the preparation and heat treatment of alloys, and X-ray diffraction methods were used both for structure determinations and phase ratio estimations. A similar approach has been made in this study of Ti-Ni alloys. Experimental Methods Ten alloys ranging from 0.25 pet to 18 pet Ni* * All compositions are in atomic percentages unless otherwise stated. were prepared from iodide titanium bar stock (hardness Rf 72) and Johnson-Matthey spectrographic standard nickel by levitation melting.&apos; As a check

Jan 1, 1957

By John A. Church

Jan 1, 1903

Jan 1, 1901

By Ralph W. Smith

DEVELOPMENT of the lime industry- in Ste. Genevieve County began in a crude way in 1840. According to information furnished by the Missouri Bureau of Geology, in the early days small vertical kilns built of stone were used, and wood was the fuel. Modern development began in 1904 when one company introduced steel shells lined with firebrick. Within a few years two more companies erected similar plants, and in 1925 a fourth company began operations. Thus there are today four lime companies at Ste. Genevieve, all operating at high capacity and with a gradually increasing production. GEOLOGY The limestone of Ste. Genevieve County, which has the chemical composition and purity required for lime burning, is the upper 80 or 90 ft. of Spergen formation. The Missouri Bureau of Geology, in its geological map of Ste. Genevieve County, gives the Spergen formation a total thickness of 160 ft., but only the upper portion is pure enough for lime burning, with an average raw-stone analysis of 98.7 per cent CaC03; 0.35 Si02; 0.3 R203; 0.35 MgCO3; 0.3 S03. The Spergen, one member of the Meramac group, Iowa series, of the Mississippian system, underlies an area approximately 12 miles long north and south, by 5 miles wide east and west (Fig. 1) in Ste. Genevieve County. The entire eastern two-thirds of Ste. Genevieve County is sedimentary, the formations dipping gently toward the east on an average grade of about 4 per cent, or 2 ½ º. Thus the outcrops of the various sedimentaries run approximately north and south. A line running west from Ste. Genevieve crosses the outcrops of the sedimentaries, ranging from the top of the Mississippian to the Ozarkian geological system in a space of 12 miles. Thus with the gentle dip of 2 ½ º the 160-ft. thickness of the Spergen formation stretches out in its outcrop so that it is approximately one mile

Jan 1, 1938

Jan 1, 1915

By Alan Morris

Brass rod for use in automatic screw machines is one of the major products of the brass mills. A large tonnage is consumed each year in the manufacture of an endless variety of finished articles and parts for assembly into other products. The machines that do this work have been developed to a high degree of efficiency, and their manufacturers are still striving for higher production speeds. This development has brought with it a demand for brass rod to meet the increasingly difficult machining conditions. This paper is a report of the results of tests undertaken in an effort to obtain a measure of the effects of such variables as lead content, microstructure and cold work on the machinability of brass rod. It is realized that the term "machinability" has never been well defined. Power, finish and tool life all should have a place in such a definition. In practice it is sometimes found necessary to sacrifice some of these in order to obtain a rod that will not tend to throw up a burr, or will give a burr which is easily tumbled off. Again a specially stiff rod may be necessary because of long overhang from the chuck or a rod of special characteristics is needed to take a given broaching operation without chattering. It is only through an understanding of the effect of basic mill operations on the machinability of the rod that such problems as these may be solved most economically. It is hoped that this paper, together with the discussion it may evoke, will prove to be a basis for such an understanding. Testing Apparatus The testing apparatus used was of the single-tooth milling cutter type, in all respects sirnilar to that first used and described by Airey and Oxford1 and again by Boston. The machine used in the present test is shown in Fig. 1. It is an ordinary milling machine in which a heavy pendulum has been substituted for the pulley on the arbor. If the pendulum is raised

Jan 1, 1932

By M. R. Geer, J. D. Davis, H. F. Yancey

ALTHOUGH the mechanical cleaning of coal is carried out at plants on the surface, preparation is actually begun at the face in the mine. Here the character of the coal and the amount, character, and distribution of the impurities within the bed may be seen. Blasting methods, dust-allaying procedures, location of mining cut with respect to bands of impurity, and the practice of discarding segregated impurities underground, all have an important bearing on the successful operation of surface cleaning units. The most important single characteristic of both coal and its associated impurities from the standpoint of cleaning is specific gravity. Other characteristics related in one way or another to the preparation , of coal are rank, petrographic composition, structure and hardness, and friability. These and still other coal properties are discussed in the first section of this chapter and impurity characteristics in the second. COAL CHARACTERISTICS RELATED TO PREPARATION Rank As a result of work done over a period of several years by committees of the American Society for Testing Materials and the American Standards Association, standard specifications are now available showing the &apos;classification of coals according to rank and quality of grade.&apos; The term "rank" expresses the degree to which the original coal-forming material has been changed by metamorphism through successive stages from peat to anthracite. Table 1 shows the classification of coals according to rank as devised by the committees of the organizations mentioned. The basic scheme of classification for the higher-rank coals is according to

Jan 1, 1943

By John H. Bassarear, A. A. Dor

INTRODUCTION Primary grinding mills as defined in this paper, are autogenous or semi-autogenous rotating, tumbling mills having a coarse feed with a top size usually varying from 150 to 300 mm (6 to 12 inches). Most frequently, the feed to these mills is the product of primary crushing plants but in some cases run of mine ore is used as feed such as at Benguet, McDermitt, L-Bar Sohio, Bear Creek and others. The size of the largest lumps in the mill feed is principally determined by limits set by the mill feed trunnion diameter and by the type and size of conveying equipment used for handling and of bins and stockpiles used for storage. The use of primary mills in mineral processing plants has expanded very significantly in the last twenty years, and they have been successfully applied to the treatment of a wide variety of ores in both wet and dry grinding applications. In the present state of technological development for primary grinding mills, there is a wide choice of acceptable options with respect to type and size, grinding flowsheet and grinding media. The choice of the optimum combination which would result in the most satisfactory condition of operation, from the standpoint of both metallurgical results and costs, depends on the nature of the ore, the required characteristics of the grinding products and on various geographic and economic circumstances. The effects of such factors and considerations on the choice and sizing of primary grinding mills and flowsheets are reviewed and discussed in the following pages. PRIMARY MILLS SELECTION Inherent Characteristics of Primary Grinding Primary grinding is complex because it involves several comminution mechanisms which occur simultaneously and to some degree interfere with one another. These mechanisms of impact, attrition and abrasion have been described earlier. The relative importance of these three main grinding actions and their mutual balance resulting in a continuous uniform operation of the mill depend to a very large extent on the nature of the ore and its physical properties. Homogenous, single mineral ores will behave quite differently from heterogenous ores consisting of different minerals bound together along defined

Jan 1, 1982

By Kenneth R. Hancock

Iron oxides are unique in that they are the only significant colored mineral found in a natural state suitable for use as a pigment after being pulverized to pigmentary size. The current world production of iron oxide pigments is estimated by the author to be between 499 and 590 kt (550,000 and 650,000 st) based on 1979 data. The fact that highly colored natural deposits of iron ore are found throughout the world accounts for its use in prehistoric man&apos;s artistic cave paintings. These early artists did not realize that they had established man&apos;s first paint test fence which now has some 20,000 years of exposure. In addition to abundance, constituting about 7 % of the earth&apos;s crust, iron oxides have the advantages of low cost, permanency, and are not toxic. Through the centuries, succeeding civilizations have utilized iron oxides as a major source for decoration and protection when coloring was desired. In the last century the chemical industry has improved on nature by developing a complete range of synthetic iron oxide pigments which surpass the pigments produced from natural iron ores in uniformity, color quality, and chemical purity. In the United States alone, the combined production of natural and synthetic iron oxides produced sales of over $28,000,000 in 1970 (Stipp, 1970) and increasing to $97 million by 1980 (Spinrad, 1980). Nomenclature With the increasing importance of the synthetic iron oxides it is necessary to make a distinction between the natural or mineral pigments and the synthetic pigments. Natural pigments are those products which are derived from selected ores and should not be confused with iron ores mined for steel production. Iron ores that are mined for steel must be capable of being mined and reduced to iron on a commercial basis. These ores are selected on the basis of iron content and processing economics. It is therefore unusual when iron ores for steel production are suitable for use as mineral pigments. Natural pigment ore sources are selected for their special physical-chemical properties and can command a premium price. Synthetic pigments, and in this instance iron oxides, are those pigments produced from basic chemicals. Through chemical synthesis pigmentary sized particles are produced as opposed to comminution, the major procedure common to all natural iron oxide pigments. Classification An important characteristic of a pigment is its color and, therefore, a logical separation can be made on this basis. A. Yellow Iron Oxide Pigments 1. Natural mineral origin a) Goethite b) Lepidocrocite c) Ochres d) Siennas e) Limonite 2. Synthetic pigments a) Goethite B. Red Iron Oxide Pigments 1. Natural mineral origin a) Hematite b) Siderite (calcined) c) Pyrites (calcined) 2. Synthetic pigments a) Hematite C. Brown Iron Oxide Pigments 1. Natural mineral origin a) Umbers b) Limonite (calcined) c) Siderite (calcined) d) Goethite (bog ore or sulfur mud) 2. Synthetic pigments a) Blends of hematite, goethite, and magnetite

Jan 1, 1983

THE decades immediately before and after the end of the nineteenth century (1890-1910) were a period of increased activity in mineral industry education. One reason for this, undoubtedly, was the rapid increase in mineral production in the decade 1880-1890; pig iron and copper production tripled; coal, lead, and zinc output more than doubled. Most of the other mineral substances followed the same general trend. Aluminum production began in 1886; petroleum output, which in 1888 was less than it was in 1882, almost doubled in the next three years. Gold alone showed no appreciable change until its discovery at Cripple Creek in 1891, followed by the Klondike in 1896, brought to boiling a public interest in minerals that had been simmering for some years previously. The first cyanide plant in the United States was erected at Bodie in 1892, and the first chlorination plant at Cripple Creek* the next year. Silver- lead smelting had already greatly developed, and the metallurgy of copper was almost transformed. The hearth area and smelting capacity of copper reverberatory furnaces more than quadrupled between 1878 and 1894; matte converters were first erected at Butte in 1884. Copper production of the United States in 1899 was 20 times that of 1872. While it was the increased technology used in mineral production that really made the field attractive for educated young men, undoubtedly they did not realize that, and were impressed mainly by the quantitative increase in output. Another factor was the increased general interest in engineering education; three times as many men took engineering degrees in the United States in 1890 as in 1880; 1892 showed almost a 56 per cent increase over 1890. Industry had come to recognize that technical training was worth while. The mineral industry lagged somewhat at first; the total number of mining degrees

Jan 1, 1941

By Arthur West

It is the purpose of this paper to describe briefly some recent large power stations for blast furnaces, where the blast is exclusively supplied by gas engines using furnace gas. The stations are given in the chronological order in which they were designed, in order to indicate the various improvements suggested by experience. Fig. 1 shows the blowing-engine station of the Bethlehem Steel Co. at Bethlehem. Although the picture shows only five blowing engines, the house now contains 11 engines. In the diagrammatic plan the arrow shows the position and direction of camera. This station handles five modern blast furnaces of 450 to 500 ions capacity each. In this, as in all the other stations described in this paper, each furnace is blown by two single tandem gas engines. Ten engines are thus required for five furnaces, leaving one single tandem spare engine. This spare capacity has been shown by several years&apos; experience at Bethlehem to be adequate to insure continuous operation. The engines in the Bethlehem station are right hand and left hand, arranged in pairs. The outboard bearings of each pair are close together so that there is not room for passageway between them. On the right of the picture are shown the inclined drums communicating with the cold-blast lines outside of building, so that any engine may be operated on any furnace. The illustration shows four cold-blast gate valves with pipes passing through wall, but since the photograph was taken the drums have been extended to take care of a fifth valve for a fifth furnace. At the extreme back of the picture can be seen the tubs of three twin vertical-horizontal Southwark steam blowing engines, which, although of modern design and as good as new, are not operated because of the greatly reduced blowing cost shown by the gas blowing engines. The next station built is shown in Fig. 2. This is the plant of the Minnesota Steel Co. at Duluth, Minn., and is at present constructed for five engines, to handle two furnaces, with one spare engine. The engines are of practically the same size as those at Bethlehem. Instead of being arranged in right-hand and left-hand pairs, as at Bethlehem, all the engines are of the same hand; this arrangement has some ad-

Jan 1, 1915

By Walter S. White

The Michigan native-copper district has produced about 5,400,000 tons of copper since mining began in 1845. The copper occurs primarily as open-space fillings and replacements in amygdaloidal flow tops and conglomerate beds of the Portage Lake Lava Series, of middle Keweenawan age. Secondary minerals with which the copper is associated include microcline, chlorite, epidote, pumpellyite, prehnite, quartz, and calcite; zeolites, other than laumontite, are not abundant. A zonal pattern of the secondary minerals transects bedding and suggests regional metamorphism mainly to the grade of the prehnite-pumpellyite graywacke facies of Coombs. Most of the major copper deposits are near the upper limit of abundant quartz in this zonal pattern. The distribution of copper in both amygdaloid and conglomerate deposits is controlled partly by primary permeability of the rocks and partly by later tectonic fracturing that was concentrated in the mechanically weak flow tops and sedimentary beds. Ore shoots and deposits are therefore controlled partly by primary structural features, such as areas of thick and thin fragmental amygdaloid or the boundaries of conglomerate lenses, and partly by regional structure: a number of ore deposits are in synclinal downwarps. The copper-bearing solutions that formed the deposits were ascending. They may have come from a large concealed intrusive, or may have been driven out of the porous tops of lava flows when the rocks were compacted and metamorphosed at great depth in the central part of the Lake Superior syncline. The second hypothesis seems more consistent with the widespread distribution of the copper, its relation to mineral zoning that represents truly regional metamorphism, its native state, and the likelihood that copper deposition was later than most or all of Keweenawan volcanism.

Jan 1, 1968

By James M. Barker

Sulfur is a nonmetallic element of great physical and economic importance to the world. It is widely but sparingly distributed throughout the hydrosphere, lithosphere, and biosphere. Sulfur is the tenth most abundant element in the universe and eighth most abundant in the sun. In the earth&apos;s crust, which is mainly igneous, it ranks 14th, but is eighth or ninth in sediments (Kaplan, 1972; Stanton, 1972). It apparently is very abundant in the core of the earth, because it is a strong chalcophile, and it is fifth in abundance in stony and iron meteorites (Field, 1972) where it occurs as trolite (FeS). In ancient times sulfur was called brimstone, literally "burning stone." Today the term brimstone is used interchangeably with the term elemental sulfur. Shelton (1979) summarized most of the common definitions of terms, grades, and specifications for the sulfur industry as follows (with minor additions): Sources of Sulfur: Combined sulfur-Sulfur that occurs in nature combined with other elements. Cupriferous pyrites-Pyrite containing relatively minor amounts of copper sulfide minerals. Hydrogen sulfide-A toxic gas (H2S) occurring in natural gas and petroleum. Involuntary sulfur-Sulfur produced primarily as a result of legislative or process mandates. Native sulfur-Sulfur that occurs in nature in the elemental (uncombined) form. Nonferrous metal sulfides-Copper, lead, zinc, nickel, and molybdenum sulfides that are processed for their metal content. Organic sulfurs-Complex organic sulfur compounds occurring in petroleum, coal, oil shale, and tar sands. Pyrites-Iron sulfide minerals that include pyrite, marcasite, and pyrrhotite. Sulfate sulfurs-Sulfur in anhydrite and gypsum. Voluntary sulfur-Sulfur produced in response to market forces. Basic Sulfur Products Produced and Marketed: Acid sludge-Contaminated sulfuric acid usually returned to acid plants for reconstitution. Brimstone-Synonymous with crude sulfur. Bright sulfur-Crude sulfur free of discoloring impurities and bright yellow in color. Broken sulfur-Solid crude sulfur crushed to -8 in. Byproduct sulfuric acid--Sulfuric acid produced as a byproduct of a metallurgical or industrial process, generally relating to combined sulfur sources. Crude sulfur-Commercial nomenclature for elemental sulfur. Dark sulfur-Crude sulfur discolored by minor quantities of hydrocarbons ranging up to 0.3 % carbon content. Elemental sulfur-Processed sulfur in the elemental form produced from native sulfur or combined sulfur sources, generally with a minimum sulfur content of 99.5%. Formed sulfur-Elemental sulfur cast or pressed into particular shapes to enhance handling and to suppress dust generation and moisture retention. Frasch sulfur-Elemental sulfur produced from native sulfur sources by the Frasch mining process. Hydrogen sulfide-Associated with natural gas or petroleum and produced at refineries and coke oven plants; used to make sulfuric acid or recovered sulfur. Liquid sulfur-Synonymous with molten sulfur. Liquid sulfur dioxide-Purified sulfur dioxide compressed to the liquid phase. Molten sulfur-Crude sulfur in the molten phase.

Jan 1, 1983

By G. B. Sazuyer

DEVELOPMENTS respecting beryllium during the past year have been sufficient to center attention on it as likely to be the most important of any of the chemical elements that have recently found a place for themselves in technical industry. This importance is only potential, however, largely because adequate supplies of beryllium ore will be necessary. The beryllium industry will be only as great as the mines which support it. To find and develop large mines will be the problem. Chief of the immediate commercial developments in the United States is beryllium-copper and its espousal by Anaconda and Riverside even at present high prices. According to the pamphlets of these companies, it ap¬pears that beryllium is to copper nearly what carbon is to iron. When one considers that the tensile strength of pure copper is about 33,000 lb. per sq. in., but that the addition of 1.5 to 2.5 per cent of beryllium produces a heat-treatable alloy with a maximum tensile strength of 220,000 lb. or over, the analogy to carbon and iron is made strikingly, clear. Striking among the properties of beryllium-copper is its resistance to fatigue, claimed to be equal or superior to that of spring steel. It needs little imagination to foresee a great industry for this alloy alone.

Jan 1, 1934

Jan 1, 1968