Search Documents

By John C. Bilello

The brittle fracture behavior of cold-worked sintered tungsten was studied over the temperature range 4.2° to 298°K using a high-sensitivity strain measuring system and electronfractography. Similar observations were made on a swaged electron beam zone-refined monocrystal. In sintered tungsten irreversible plastic deformation was observed during cyclic load-unload tests at stress levels well below the fracture stress for all temperatures, but general microyielding could be detected only down to 202°K. For the zone-refined samples macroyielding occurred at all test temperatures with evidence for twinning below -202°K. The fracture stress of the sintered tmgsten was virtually independent of temperature, while the zone-refined crystal showed a 2.3 times increase over the same temperature range. Electronfractography confirmed the presence of numerous rod-shaped and spherical submicroscopic voids which ranged in diameter from 1400 to 4300A in the sintered tungsten; no voids could be found in the zone-refined tungsten. Contrast effects observed on the replicas in the vicinity of certain voids indicated that plastic deformation could be induced by the local stress concentration. It has been suggested that the presence of these voids may be responsible for the low-temperature brittle failure of sintered tungsten. Based m this suggestim und on the evidence obtained here, a dislocatim model is presented to account for the brittle behavior of sintered tungsten. In this model slip, which is induced by the local high stress concentration in the region at the edge of a favorably oriented void, could cause the void to grow to a microcrack of critical size. STUDIES of brittle fracture in bcc metals have led to the well-known experimental relationships between grain size, yield stress, fracture stress, and temperature which have formed the basis for the various dislocation pile-up1-3 or interaction4'= models for slip-induced microcrack nucleation. While microcracks can be nucleated by deformation twins,6,7 there has been no direct evidence furnished by transmission electron microscopy to support conclusively either the Zener pile-up or Cottrell dislocation reaction models for producing micro-cracks in all "brittle" materials. In addition to the "inverse" grain size relationship for yield and fracture stresses the cottrel14 theory predicts that the fracture stress below the transition temperature should behave in a fashion similar to that of the yield stress above this temperature. Such behavior has been verified for several bcc metals.8-10 With reference to both grain size effects and the tem- perature dependence of the fracture stress below the transition temperature, the behavior of sintered tungsten appears anomalous. Early work by Bechtold and Shewrnon 11 showed no apparent temperature dependence of the fracture stress below the ductile-brittle transition temperature (DBTT). They attributed this result to the intergranular nature of the fractures observed. More recent work by Wronski and Four-deux12'13 on considerably purer material did not show any systematic relationship between the fracture stress and temperature below DBTT. The dependence of flow and fracture stresses on grain size is also not clearly established for sintered tungsten. Koo, for example, has shown that the DBTT for sintered tungsten depended chiefly on the annealing temperature and was relatively insensitive to the actual grain size achieved. Using electrofractography and transmission electron microscopy, Wronski and Fourdeuxl3 showed that numerous spherical and rod-shaped submicroscopic voids could be found in sintered tungsten but not in melted tungsten of nominally the same purity. They suggested that these voids could be responsible for the temperature insensitivity of the fracture stress below the DBTT. In the present work the temperature dependence of the fracture stress for high-purity commercially sintered tungsten has been determined. The presence of submicroscopic voids in sintered materials was confirmed, and these were studied in detail to examine the role they could play in nucleating brittle fracture. A dislocation model is suggested which could cause an inherent spherical void to lengthen into a Griffith crack of critical size. EXPERIMENTAL PROCEDURE Commercially sintered tungsten rod was obtained in the as-swaged condition from Sylvania. A zone-refined crystal was obtained from the same source. This crystal was grown by giving three zone passes (at 25.4 cm per hr) to a sintered rod of high-purity tungsten. The rod axis prior to cold working was -15 deg from the [110] direction. Originally the zone-refined rod was -6 mm in diam; it was reduced to -3 mm by eight swaging passes, at high temperatures, with each step having about the same reduction of area. The final swaging step gave a 7.5 pct reduction of area at 1050°C. All swaging operations were performed in a hydrogen atmosphere. For the sintered rod a similar working schedule was employed. Metal-lographic examination of the sintered material revealed that the cold-worked structure had an apparent grain diameter of -25 u transverse to the swaging direction (obtained by the intercept method). In the longitudinal direction cold-worked grains were approximately 1.5 to 2 times their diameter. No distinct fiber structure could be observed optically for the zone-refined rod. The cold-worked structure in the

Jan 1, 1969

By T. L. MacKay

Oxidation rates of single-crystal and poly crystalline zirconium in oxygen at temperatures from 307° to 815°C obey the parabolic rate law for short ex-posure time, 4 to 6 hr. The activation energy for the oxidation of single-crystal zirconium between 420° and 790°C is 42.6 ± 0.7 kcal per mole, and in the temperature range 307" to 600°C the activation energy for oxidation of poly crystalline zirconium is approximately the same. The high-activation energy is indicative that diffusion through the bulk oxide film is the primary mode of mass transport for both types of metal. The higher oxidation rates for poly -crystalline zirconium in this temperature range were attributed to differences in the orientation of the grains in the metal with respect to the oxidizing surfaces. Above 600°C, vain growth was observed in polycrystalline zirconium, and the oxidation rates approached those of single-crystal zirconium. ThE kinetic data of previous oxidation studies1-' of zirconium in oxygen have been interpreted by both parabolic and cubic rate laws. There is some evidence that there is a transition from the parabolic to the cubic rate law at prolonged exposures, but the question is still controversial. For the parabolic rate law activation energies are reported in the range 18.6 to 35 kcal per mole, and for the cubic rate law in the range 38 to 47 kcal per mole. So far as the mechanism of zirconium oxidation is concerned, inert marker studies10,11 have indicated that the oxidation proceeds by oxygen (anion) diffusion through the oxide film toward the metal-metal oxide interface. Pemslerl2 observed that the orientation of the grains in the zirconium metal substrate affected the rate of formation of the oxide film on the surfaces of the grains and that the orientation dependence of the corrosion rate persisted beyond the initial stages of reaction. The rate of oxidation was a minimum when the c axis of the grain was parallel to the surface of the sample, and rose to a maximum when the c axis was inclined at about 20 deg to the plane of sample surface, and decreased again at higher inclinations. cox13 observed that in 300°C steam a thin oxide film was formed initially on zirconium and that this oxide film, which exhibited interference colors, became dark first along the grain boundaries and then over the whole surface in an inhomogeneous manner as the film thickened. Cox proposed a mechanism in which oxygen diffused along preferred paths created by grain boundaries in the metal and formed a much thicker film at or near the grain boundary than on the central zone of the grain. In the present study, the oxidation rates of single crystals of zirconium were measured in oxygen and compared with the oxidation rates of polycrystalline zirconium of the same bar stock. It was felt that such a comparison would elucidate the role of grain boundaries in the metal substrate. SAMPLE PREPARATION Single crystals of zirconium were prepared by following the procedure of I3apperport,14 starting with 1/4-in. rod purchased as crystal-bar zirconium. Zirconium rods 2 in. long were wrapped in tungsten foil and sealed in quartz tubes at pressures of less than 10-6 mm of mercury. Large single crystals were grown by thermal cycling above and below the a-/3 transformation temperature, 862°C. Several specimens were simultaneously subjected to the same cycling procedure, heating to 1200°C, holding for 4 hr, then cooling in the furnace and holding at a temperature of 840°C for 5 to 10 days. This cycle was repeated five or six times for each set of specimens. The grain size of the crystal-bar zirconium before thermal cycling was between 10 and 30 p. Fig. 1 shows the microstructure of an end section of as-received crystal-bar zirconium. A longitudinal section of each zirconium rod after thermal cycling was polished and examined under polarized light, see Fig. 2, and the largest single crystals were selected for this study. Zirconium rods 1/8 in. in diameter and 1/2 in. long with spherical ends were machined from the single crystals and from the as-received bar stock. An X-ray examination showed that the c axis of the single crystals made either a 34-deg or an 89-deg angle with the rod axis. The specimens were chemically etched for 2 min in solution consisting of 15 parts hydrofluoric acid (48 pct), 80 parts nitric acid, and 80 parts water. The chemical polish removed 1 to 2 mils from the surface. EXPERIMENTAL The Sartorius vacuum microbalance used in this study has a sensitivity of 0.5 pg and a capacity of

Jan 1, 1963

By David J. Mack

THE structures and properties of the copper-aluminum alloys have been the subject of much study since the classic investigation of Carpenter and Edwards1 focused attention on the engineering utility of these alloys. It was recognized at an early date that the metallographic structures developed in the aluminum bronzes were similar to those developed in steels, both in the annealed and the rapidly cooled state. Most investigators have been concerned with the acicular, martensitic-like structure formed from the ß solid solution upon rapid quenching; the transformation of the ß under equilibrium cooling to a lamellar eutectoid having been relatively neglected. With the introduction in 1930 by Davenport and Bain2 of the isothermal transformation technique for studying eutectoidal decompositions, a new field was opened. Although an enormous amount of work has since been done on the isothermal transformation of steel, study of structurally analogous systems has been almost totally overlooked. The outstanding exception was the prize-winning paper† of Smith and Lindlief3 who investigated the decomposition of the ß phase in copper-aluminum alloys by isothermal methods. This was followed in 1934 by Wasserman's reviews of available information on analogous transformations in eutectoid alloys. Since that time no comprehensive study of isothermally transformed eutectoids analogous to steel has appeared, although many valuable contributions have been made to an understanding of the structures developed in such systems. Important papers have been published by Kurdjumow, Gridnew and co-workers, 5-17 Obinata,18,19 Greninger,20,21 and others .22.28 The work to be described in this paper was an out-growth of preliminary studies on the isothermal transformation of a eutectoid aluminum bronze, after it became apparent that the alloy under study was reacting somewhat differently than the similar alloy used by Smith and Lindlief. PRELIMINARY EXPERIMENTS The material used in this study was a high purity aluminum bronze especially prepared by Ampco Metal, Inc. It analyzed: Copper-88.o7 pct, Aluminum-11.89 Oct, Iron-0.02 pct, Manganese-0.01 pct, Others-Balance. Although some disagreement exists on the exact composition of the eutectoid, this alloy was believed to be of essentially eutectoid composition even though some pro-eutectoid* delta particles existed in the microstructure of furnace cooled specimens. Specimens transformed isothermally at temperatures slightly below the eutectoid showed relatively large amounts of pre-eutectoid delta, but as will be shown later, this results

Jan 1, 1947

By K. J. Rosengren

INTRODUCTION Mount Isa Mines Limited operates a major mining complex at Mount Isa in northwest Queensland, Australia. The location is arid and remote, some 600 miles distant from the nearest port of Townsville on the eastern coast (Fig. I). Current mine production is 6 million long tons per annum comprising 3.8 million tons of copper ore and 2.2 million tons of silver-lead-zinc ore. Copper ore production is scheduled to increase to 5.8 million long tons per annum by 1973 and a new silver-lead-zinc mine is being developed at Hilton, 13 miles north of Mount Isa. The Mount Isa and Hilton orebodies occur in a single stratigraphic member, termed the Urquhart Shale. This shale is conformable with several other sedimentary formations striking north-south and dipping approximately 65º west. The silver-lead-zinc orebodies occur in bands conformable with the shale bedding and tend to be of tabular shape, varying in width from a few feet to nearly 200 ft. The copper orebodies occur in breccia bodies, locally known as "silica-dolomite", within the Urquhart Shale and tend to be more irregular and massive with widths up to several hundred feet. The detailed geology is described by Bennett (1 2). At present, production comes almost entirely from underground operations with only about 25,000 tons per year of carbonate ore from open pit operations. The mining method used in the copper orebodies is sublevel open stoping with pillar recovery by pillar blast before stope filling or by sublevel caving after stope filling. A large primary sublevel caving operation was also carried out until recently in one of the orebodies. The wider lead orebodies are mined by sublevel open stoping, with or without pillar recovery, while cut and fill stoping is used in the narrower orebodies. Details of the mining methods are given by Davies (3). The company's interest in open pit mining stems from a large open pit which was mined out in 1965 and a further large open pit planned for future production. In addition, the company is currently evaluating several large ore deposits in Australia and New Guinea. All of these orebodies would be mined by open pit methods and rock mechanics studies of slope stability are now a standard feature of all open pit evaluations.

Jan 1, 1972

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress .4,5† The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed .27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By Charles H. Fulton

Experimental work on the process was begun on a laboratory scale at Cleveland, Ohio, in 1914, and transferred to East St. Louis, Ill. in 1916, where a commercial sized furnace was in technical operation until January, 1918. The essential steps of the process are as follows: Oxidized zinc ore or roasted zinc concentrate is mixed with crushed coke and coal-tar pitch and formed into briquets 9.25 in. (23.5 cm.) in diameter and 21 in. (53 cm.) long in a manner similar to that used in the manufacture of graphite or carbon electrodes, except that much less care and time are required. The composition varies with the nature of the ore; in one case, the composition was 100 parts ore, 70 parts coke, and 18 to 20 parts pitch. These briquets maintain their form and volume during and after the distillation of the zinc. This object is gained by using coke as the matrix and coal-tar pitch as the binder; this pitch becomes coke on heating and unites the ore particle and the original coke particle into a continuous mass. The briquet is an electrical conductor but only to such a degree that it can be used as a resistor. The size of the ore, as in the present practice of zinc metallurgy, ranges from fine material, such as flotation concentrate, to coarse table and fine jig concentrate. The process is not restricted to any particular kind of ore, but is applicable to pure high-grade ores, ores high in iron, and complex zinc-lead ores, since the residue from the distillation IS held immovably in place within the briquet. In the case of complex zinc-lead ores, the distillation is conducted with a carefully regulated temperature so that a high percentage of lead is retained in the distilled briquet, which may then be smelted for its lead content. In present zinc smelting practice, the reduction fuel is from 40 to 50 per cent. of the weight of the ore. In the briquet, it is from 60 to 85 per cent. of the ore; but unless the ore is exceptionally high in residue, the distilled briquet may be used over again as coke, or as a high ash coke for fuel purposes in power production. Baked briquets are hard and tough and may be handled roughly

Jan 1, 1921

By Gregory M. Dexter

Recent litigation in Pennsylvania between three coal-mining companies and a private water company resulted in the payment by the coal companies of the equivalent of about $500,000 to buy a new water supply to replace that which had been damaged by acid drainage from strip mining. An investigation of the relevant facts indicates that the water could have been treated by spending about $40,000 on equipment and $15,000 yearly for chemicals, labor, and power until the contarnination could be reduced about 80 pct. The water company's supply, furthermore, had deteriorated largely by reason of dry weather before stripping was begun by the coal companies. Payment to the water company should not have exceeded $300,000 and could have been as low as $100,000. Strip mining of coal is common in Pennsylvania. The most important objection to it in Pennsylvania is generally acid pollution of runoff water. An outline of the methods, therefore, that could be used to reduce such pollution, to compare acid-contaminated waters. and to treat such waters to make them satisfactory for public and industrial use is worth-while. The watershed of the West Penn Water Co. covers about 4.5 square miles, 20 miles west of Pittsburgh, and has two 90,000,000 gal reservoirs supplying about 1,300,000 gal daily for public and industrial use of which 450,000 gal daily are for two railroads. The pollution arises from weathered derivatives of typical'" Coal Measures"' rocks, the principal source being pyrite (and marcasite) in Pittsburgh and Rooster coals. Springs and seeps on hillsides issue from sandstone and limestone formations intersecting shale or clay land surfaces, or from perched water tables. The two reservoirs create an artificial permanent water table. Soap-hardness tests on three seepage samples taken in a dry summer ranged from 150 to 500 ppm. Water sampled came from aquifers above Pittsburgh and Rooster coals, obviating the possibility of contact with pyrite-containing coal. Since acid contamination of mine waters is the result of chemical reactions of oxygen and water with pyrite, it will be reduced by the exclusion of either air or water. The Sunnyhill Coal Co. has applied this principle in its "contouring" method of strip mining by burying contaminated coal-waste material under a compact, smoothed-up surface of top-soil, gravel, clay, and sand at a cost

Jan 1, 1950

By T. E. Leontis, F. N. Rhines

THE oxide scale that forms upon magnesium at elevated temperatures is nonprotective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth1 and has been verified by Suzuki2 and by Scheil.3 Pilling and Bedworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki,2 the product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavault5 observed that excrescences form upon liquid magnesium and alloys in the course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium7and calcium8 minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.9 Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Scheil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. EXPERIMENTAL PROCEDURE AND RESULTS The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the

Jan 1, 1946

By Kenneth A. Gutschick, Robert S. Boynton

Lime has become a very general loosely used term that includes virtually all finely divided types of limestone as well as burned forms of lime. However, actually (and according to Webster) lime is only calcined limestone (known as quicklime, calcium oxide, or calcia). It also embraces the secondary product of quicklime-namely hydrated lime or slaked lime (calcium hydroxide). Fundamentally there are two basic types of limestone-high calcium and high magnesium (dolomitic). The dolomitic quicklimes and hydrated limes correspond to their "high calcium" counterparts in terminology. The only difference is that the dolomitic types are a combination of the elements, calcium and magnesium, whereas high calcium limes contain only 0.5 to 2 pct of magnesium. Both types, which are made through calcination at high temperatures, are shown chemically as follows: [ ] In the above reactions either type of limestone is burned (calcined) in furnaces known as lime kilns so that the carbon dioxide content of the stone is expelled as a gas. With high calcium limestone 44 pct of the weight of the stone is lost; with dolomitic limestone the loss is 48 pct. Also, both reactions are chemically reversible since quicklime absorbs carbon dioxide readily and in so doing transforms itself back to the original carbonate form. Most quicklimes correspond in size to the original rock, which varies from one to eight inches, depending upon the type of kiln employed. Slight shrinkage occurs during calcination. A few limestones when calcined will decrepitate (break down) into a fine powdery form; however, chemically it is the same as the pebble or lump-sized material. For some uses the lumps of quicklime are pulverized and packaged. Since quicklime has great affinity for moisture and carbon dioxide, it is perishable. When it absorbs moisture and CO2 slowly from the atmosphere, the resulting product is "airslaked." Consequently, it must be stored in dry, moisture-proof areas that are free from CO2. Because of its fugitive nature, it is usually consumed within a few weeks after manufacture. A more stable form of lime is hydrated lime-commercially made by adding water to the quicklime until the lumps break down into a fine, white powder. This product, which is usually packaged, can be stored more safely; and many of its uses are interchangeable with quicklime. The irreversible chemical reactions of hydrated lime for both high calcium and dolomitic types are: [ ]

Jan 1, 1960

By J. K. Stanley, R. F. Meel

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

By R. F. Meel, J. K. Stanley

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

By Franklyn W. Oatman

In order that the conditions which obtain in an oil well may be readily understood, a brief description of a typical California well and a number of the phenomena accompanying same will be given. That the necessity for the exclusion of water be realized, the effects of water intrusion, a description of methods of prevention, .and a discussion of causes of failure will be presented, followed by a summary and recommendations. Fig. 1 shows a section of a typical well which illustrates the relation of oil sands to overlying strata. It indicates a deep water sand separated from the oil sand by shale, and the proper place for the final shutting off of water. In this well a comparatively thick stratum of compact shale protected the oil from overlying water so that the operation of landing the water string was a simple matter. In some wells the protecting stratum may be only from 3 to 5 ft. thick and very careful operation is necessary in order to land the water string of casing properly and not puncture through to the oil sand. The cases just cited are common, but occasionally, after excluding overlying water, productive oil sands are drilled through in the expectation of finding more productive underlying sand, and a water-bearing stratum is tapped. In this case the problem is the reverse of the normal; water must be prevented from ascending rather than descending. A discussion of well-drilling methods is not within the scope of this paper, except such operations as pertain to shutting off of water. A brief outline of the several conditions which may accompany drilling follows. Some or all may be present in any particular case. The direct relation of these to prevention of intrusion will be discussed in detail further on. In drilling, the hole becomes more or less irregular in shape, and rough, and as the casing follows the bit into the well it does not fit snugly against the walls. As a result, water may descend between the casing and walls of the well. If a circulation pump is not used during drilling, the hole is simply punched through and the pulverized material removed from the well by means of a bailer. If circulation is maintained there is a continual flow of water down inside the casing and up around the outside between the pipe and the walls of hole. This keeps an open space around the pipe.

Jan 1, 1915

By C. H. Mathewson, Robert Maddin, W. R. Hibbard

A SATISFACTORY mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.1 Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.3 EXPERIMENTAL PROCEDURE Half inch rods of alpha brass (nominally 70 pct Cu, 30 pct Zn) * were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.' In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pct nitric acid solution. The back-reflection Laue technique as described by Greninger5 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buerger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1948

By S. M. Parmley

Experience has shown that there are some factors connected with the drying of fine washed coal that are not present in drying of slack coal as normally practiced at cement kilns or pulverized coal plants. It is the purpose of this paper to show some of these variations as they have been encountered under actual operation. The Champion No. 1 cleaning plant of the Pittsburgh Coal Co. uses the wet system of cleaning coal. The plant is equipped to produce commercial sizes or mixtures, the primary sizes being plus 6 in. and 4 by 6 in., which are hand-picked. Minus 4-in. sizes are all cleaned by the wet process. To produce a commercial product as free of moisture as possible, the washed coal is first passed over sizing and dewatering screens, then each size except the — ?-in. coal is conveyed to loading booms by slow-moving draining conveyors. As the +?-in. sizes are not heat-dried, no data will be given, as it is the purpose of this paper to describe the heat drying of — ?-in. coal as practiced at the Champion No. 1 plant of the Pittsburgh Coal Company. To fully appreciate the conditions, it must be remembered that the — ?-in. product is now shipped at a lower moisture content than when received from the mine. The incoming coal in the — ?-in. size will average 5 per cent. moisture and the shipped product 3 per cent. moisture. This is a case where a wet process gives a reduction of both ash and moisture in the fine sizes. The shipped product, therefore, is more uniform in all characteristics, and uniformity of product is the most important single factor in coal preparation. The 0 by ?-in. coal is first dewatered on slow-moving continuous bucket dewatering elevators, running at the rate of 40 ft. per minute, with 48-in. perforated buckets with ¼ by 1½-in. slots, spaced ? by 2?-in. centers staggered. The moisture in the coal discharged from the elevators runs 20 to 28 per cent., depending on the fineness of the product. The discharge from the dewatering elevator is further drained on a drag-type conveyor equipped with ½-mm. wedge wire screen. The conveyor discharges coal with an 18 to 25 per cent. moisture to three centrifugal dryers of the Carpenter type. The Carpenter dryers

Jan 1, 1931

By C. H. Aldrich

For many years the City of Prescot, about 8 miles northeast of Liverpool, has been the home of British Insulated Cables, Ltd., one of the largest wire mills and manufacturers of electrical equipment in England. Since this location is close to the industrial center of the country and the seaboard, with good railroad transportation facilities, it was a logical site for the new refinery. Early in April, 1932, the writer was called upon to prepare a preliminary layout and estimate of cost of the proposed plant, and shortly afterward, following a discussion of these figures with officials of British Insulated Cables, in England, the decision was reached to proceed immediately with construction of the plant. The refinery was built by British Insulated Cables, Ltd. Designing of the plant was started early in May, 1932, orders for equipment being placed as rapidly as possible. On July 18 the first steel was erected and the first charge was cast on Jan. 5, 1933. No difficulties of any consequence were experienced in starting the plant and the grade of copper produced was quite satisfactory after the first charge. The initial capacity desired was 2500 tons of refined copper per month. Since only one furnace was to be built, it was necessary that it should have sufficient reserve capacity to catch up after unavoidable shutdowns. It was also necessary to lay out the plant so that it would operate efficiently at this tonnage and at the same time permit expansion in the future, if necessary, to several times its original capacity. In order to meet these conditions and also to take full advantage of the space available, the layout shown in Fig. 1 was adopted. The principal plant structures are a blister storage aisle, casting building, wire-bar storage building and a coal-pulverizing building. Additional smaller structures include a brick and charcoal shed, pumphouse, drill room, water-cooling tower, clay-preparation shed, substation and plant office. Incoming blister is received in either broad-gage railway cars or steam motor lorries in the blister storage aisle, unloaded by overhead electric crane to narrow-gage cars, weighed and sampled, then either sent directly to the furnace or placed in storage. After refining, the copper is cast on the wheel, passes through the cooling bosh and is

Jan 1, 1934

IN A broad sense, the subject of slag control includes not only the adjustment of the composition of the slag but also of its relative weight in terms of percentage of the metal-bath weight. The slag is made up essentially of (1) oxides formed by oxidation of silicon, manganese, phosphorus, and iron in the charge, (2) SiO2, MnO, and other oxides charged as such, and (3) lime charged or fed to the heat to neutralize the “acidic”: oxides present (Si02 and P2O5). Obviously, if practically perfect control were possible over the composition of the charge as well as over the oxidation process during the melting period, both slag weight and composition would be very nearly predetermined, and the control problem would be solved. Unfortunately, we have only a somewhat. imperfect control over these factors, so that beginning at about the lime-boil period in the heat, and later in the early refining period, it becomes necessary for the first helper, as the heat progresses, to make quick estimates of the composition and physical state of development of the slag (as well as of the amounts of phosphorus, sulphur, and carbon in the metal) from which he can judge how much extra lime, roll scale, fluorspar, and other additions will be needed not only to give the desired final slag composition, but also to hasten the complete fusion or shaping to a desired viscosity in the liquid state. The discussion in this chapter is limited essentially to those more or less practical rapid methods of slag estimation that have been used, or at least tried, for these purposes under actual open-hearth shop conditions. Another aspect of importance here is the extent to which the freedom of choice to the operator is limited by available charge materials, product specifications, and the oxidation and other chemical- reaction effects which inevitably occur under the conditions of this furnace process. For a better understanding of these control limitations and of the chemical and physical background of the subject, the reader is urged to read at least part of the discussion in Chapters XVII and XIX. Charge materials are discussed in Chapter IV, and many of the details of charging, melting, and refining practice closely related to slag control are given in Chapters VI and VII.

Jan 1, 1944

By L. E. Young

The purpose of this paper is to start a discussion on: (I) methods of supporting the immediate roof, particularly of local areas of poor roof, during the mechanical loading of coal; (2) methods of increasing the rapidity of the movement of the mining faces so that, without the use of cribs, jacks, park walls, and filling, there will be no danger to men, equipment, and working places from the subsidence of the overlying strata. In the Pittsburgh district the application of mechanical loading devices in mines working in the Pittsburgh seam has been retarded by the difficulties of holding and handling the draw slate. Normally the thickness of this slate averages about 8 in. but the hardness varies, and a cut of coal cannot always be loaded without placing posts or crossbars to support the slate. Locally, the slate may be thicker and special methods of support may be required. If crossbars are placed to hold the slate when the coal averages 5 ft. in thickness, the standard methods of transporting the coal cannot be followed, and the use of conveyors may be desirable. Very little information is available on the effect of increasing the rate of movement of advancing or retreating break lines or longwall faces. A few British publications have presented some data but all such data relate to longwall faces that have moved not more than 6 ft. a day. The most rapid rate of movemerit of longwall faces in Germany is 6 ft. per day. In the ordinary hand-loading mine in western Pennsylvania break lines on full retreat will move about 2 ft. per day. If loading machines are used under similar conditions the rate of retreat may reach 4 ft. per day. In a mine where coal is loaded by hand on conveyors three shifts per day, the rate of retreat has ranged from 11 to 16 ft. per day, with an average of 13 ft. If mobile loading machines could be used to load on conveyors on break lines, the rate of retreat should be increased substantially During 1935 and 1936, the United States Bureau of Mines, under a cooperative agreement with the Pittsburgh Coal Co., carried on studies of roof movement at Montour To. 10 mine. The work war done urider the direction of Mr. H. P. Greenwald, Supervising En neer, Experi-

Jan 1, 1938

By L. E. Young

The purpose of this paper is to start a discussion on: (I) methods of supporting the immediate roof, particularly of local areas of poor roof, during the mechanical loading of coal; (2) methods of increasing the rapidity of the movement of the mining faces so that, without the use of cribs, jacks, park walls, and filling, there will be no danger to men, equipment, and working places from the subsidence of the overlying strata. In the Pittsburgh district the application of mechanical loading devices in mines working in the Pittsburgh seam has been retarded by the difficulties of holding and handling the draw slate. Normally the thickness of this slate averages about 8 in. but the hardness varies, and a cut of coal cannot always be loaded without placing posts or crossbars to support the slate. Locally, the slate may be thicker and special methods of support may be required. If crossbars are placed to hold the slate when the coal averages 5 ft. in thickness, the standard methods of transporting the coal cannot be followed, and the use of conveyors may be desirable. Very little information is available on the effect of increasing the rate of movement of advancing or retreating break lines or longwall faces. A few British publications have presented some data but all such data relate to longwall faces that have moved not more than 6 ft. a day. The most rapid rate of movemerit of longwall faces in Germany is 6 ft. per day. In the ordinary hand-loading mine in western Pennsylvania break lines on full retreat will move about 2 ft. per day. If loading machines are used under similar conditions the rate of retreat may reach 4 ft. per day. In a mine where coal is loaded by hand on conveyors three shifts per day, the rate of retreat has ranged from 11 to 16 ft. per day, with an average of 13 ft. If mobile loading machines could be used to load on conveyors on break lines, the rate of retreat should be increased substantially During 1935 and 1936, the United States Bureau of Mines, under a cooperative agreement with the Pittsburgh Coal Co., carried on studies of roof movement at Montour To. 10 mine. The work war done urider the direction of Mr. H. P. Greenwald, Supervising En neer, Experi-

Jan 1, 1938

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction .within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress.4,5? The theory of recrystallization is not in advanced state; if recrystallization data were obtained, in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By Ralph Hultgren, Louis A. Carapella

When F. Heuslerl found in 1898 that certain alloys containing only copper, manganese, and tin were ferromagnetic, the discovery excited a great deal of interest and led to numerous investigations. It was early found that tin could be replaced by aluminum, arsenic, antimony, bismuth, or boron without destroying the ferromagnetic nature of the alloys.2 Copper may also be replaced by silver.% All these alloys have come to be known as "Heusler alloys." The aluminum alloys apparently were the most magnetic and have been most extensively investigated. However, no agreement has yet been reached as to the source of the ferromagnetism arising from these nonferromagnetic elements. Absence of reliable quantitative data makes speculation hazardous. The value of much of the earlier work was vitiated by lack of necessary precautions against contamination, and by lack of close control of heat-treatment. It was only recently established that in aluminum Heusler alloys4 the ferromagnetism arose from a single phase, an ordered body-centered-cubic structure. With modern methods of preparation, heat-treatment, and X-ray examination, it is possible to prepare these alloys without contamination, to heat-treat them intellgently, and to determine what phase or phases are present in the finished sample. In the present investigation, a series of pure alloys in the comparatively neglected copper-manganese-tin system have been prepared, which consist of a single, body-centered-cubic structure (the beta phase) and whose compositions vary within wide limits. The magnetic saturation values of these single-phase alloys have been quantitatively determined, so that considerable data on the effect of composition on the ferromagnetism have been made available. In the course of the investigation some information on the extent of the stability of the beta phase and the nature of phases in adjacent regions of the ternary diagram has been accumulated. Anomalies in earlier data. have been explained, and alloys have been prepared that are much more strongly magnetic than any previous Heusler alloys. Previous Work In the original work of F. Heuslerl and coworkers,2 a maximum magnetic saturation value of I = 107 was found at the composition Cu6Mn3Sn, while a value for CusMnAl of I = 443 was early measured. Ross and Gray5 found a second maximum at the composition Cu2MnSn, which was much more magnetic than Heusler's original alloy. F. Heusler6 hen reinvesti-gated the system, confirmed their results,

Jan 1, 1942