Search Documents

By A. E. Back, S. F. Ravitz

When manganese ores are leached with sulphur dioxide, a large part of any zinc in the ore usually is extracted with the manganese.1 In the dithionate process,2,3 in which the manganese ore is leached with dilute sulphur dioxide gas and the manganese is subsequently precipitated by adding lime to the pregnant solution, the zinc is precipitated with the manganese. These facts suggested the possibility of applying the dithionate process to the recovery of zinc from oxidized ores or calcined sulphide concentrates. Accordingly, an investigation was begun, and preliminary tests were made on several ores and concentrates. The results were encouraging, but the need to devote available funds and personnel to other projects made it necessary to drop the work before the various factors involved in the process could be studied in detail. A brief mention of the process,4 however, elicited a number of inquiries, so that it appeared desirable to report the results of the preliminary work. The dithionate process as applied to zinc may be summarized briefly as follows: The ore or calcined concentrate is leached with dilute SO2 gas to dissolve the zinc, largely as zinc sulphate, in accordance with the following equation in which [ZnO] represents the "oxide zinc" in the ore or calcine: [ZnO] + SO2(g) + 1/2 O2 = Zn++SO4— [1] If, in the leaching step, the ore or calcine is suspended in calcium dithionate solution, the sulphate ion, as it is formed, is precipitated immediately as calcium sulphate, which is subsequently filtered off with the insoluble ore residue: Zn++SO4— + Ca++S2O6— = CaSO4(s) + Zn++S2O6- [2] An alternative procedure is to suspend the ore in water, filter off the insoluble ore residue after leaching, add calcium dithionate to the resulting zinc sulphate solution, and then filter off the calcium sulphate precipitate. In either event the zinc is obtained in the form of a pregnant solution of zinc dithionate, from which it can be precipitated as relatively pure zinc hydroxide by adding milk of lime: Zn++S2O6— + Ca(OH), = Zn(OH)2(s) + Ca++S2O6- [3] The zinc hydroxide precipitate is calcined to form the final zinc oxide product: Zn(OH)2 = ZnO(s) + H2O(g) [4] Theoretically the process is completely cyclic with respect to dithionate ion, the calcium dithionate required for reaction 2 being replaced by that formed in reaction 3. In practice, of course, small amounts of dithionate would be lost in the various filter cakes, depending on the economic washing limits. In the leaching step, however, some of the SO2 is oxidized to dithionale instead of sulphate, accord- ing to the following overall reaction: ZnO + 2SO2(g) + 1/2 O2(g) = Zn++S2O6-, [5] so that the dithionate losses are made up, at least in part. Ores and Concentrates Tested The analyses of the ores and concentrates tested are summarized in Table 1, which also includes the analyses of the calcines produced from the concentrates. The concentrates were roasted in a laboratory muffle furnace at the temperatures indicated until evolution of SO2 could no longer be detected; shallow clay dishes ordinarily were used; but calcines 2a and 2c were prepared in iron dishes, with the result that these two calcines were badly contaminated with iron scale. The "complex" concentrate, sample 1, consisted essentially of sphalerite grains containing inclusions of pyrite and other sulphide minerals too minute to be liberated by grinding within economic limits. In the " marmatitic" concentrate, sample 2, the iron was present largely as marmatite (that is, as iron sulphide in solid solution in zinc sulphide) rather than as pyrite inclusions. The zinc was present largely as the carbonate in the two "oxidized" ores, samples 3 and 4, and as the silicate in the "willemite" ore, sample 5. Leaching Tests The leaching cell was a 3-liter glass beaker placed in an electrically heated water bath manually controlled to maintain a temperature of 35°C in the leach slurry. The slurry was agitated by means of a flat paddle-type stirrer

Jan 1, 1950

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid iron alloys containing chromium and nickel has been measured in the temperature range 1550° to 1700°C at nitrogen pressures to 1 ah. The solubility surface has been determined for the iron corner of the liquid metallic ternary to 21 pct Cr and 11 pct Ni. The nitrogen solubility increases markedly with increasing chromium concentration. The effect of nickel and the bilinear effect of chromium and nickel are less pronounced. The solubility data are presented, and interaction coefficients are determined from them. THE solubility of nitrogen has been determined in liquid Fe-Cr-Ni binary and ternary alloys. The work in this laboratory has been directed toward a relatively limited composition range, that is to 20 pct Cr and 10 pct Ni. Humbert and Elliott1 studied the entire ternary; but their investigation was, understandably, limited in this region. The region considered here is of the greatest commercial interest. Knowledge of the solubility in these alloys is important for accurate control of the nitrogen levels in various stainless alloys. Also, the solution behavior is of theoretical interest because of its deviations from ideal dilute solution rules at moderate chromium levels. The nitrogen solubility in the iron binaries has been reviewed extensively by Pehlke and Elliott,2 particularly with respect to the dilute solution interaction parameters. More recently, there has been some interest in accurate descriptions of solute interactions in non-dilute solutions. Most of the investigators have adopted a power series fit to accommodate any non-linearity of the data. The Taylor series expansion is adopted here, using Scimar's notation3 for the interaction coefficients. An alternate method, instead of requiring higher-order expansions, is to restrict the range of the composition variables. A planar solubility surface may be fitted to the data and its range of validity determined. If the axes of this region are displaced from the usual origin—the solvent pure iron—a change in standard state is required for the solution reaction. The standard state for nitrogen in iron is commonly taken as the hypothetical 1 wt pct solution of nitrogen in pure iron. However, for an alloy of appreciable solute concentration, e.g., 13 pct Cr or 18 pct Cr-8 pct Ni, it would be convenient to use that base composition as the solvent and redefine the solution reaction in terms of that particular solvent. A brief derivation follows, defining the free energy of solution in an alloy solvent. Following the treatment by Darken and Gurry,4 for a nitrogen pressure of 1 atm: N (pure component) = N (1 wt pct in solvent) [l] AG=RT ln100/ wt pct N in solvent Taking this reaction for an alloy solvent less the same reaction for a pure iron solvent the relation between nitrogen in pure iron and an alloy is: N (1 wt pct in Fe) = N (1 wt pct in alloy) [2] AG = RT[ln(wt pct N in Fe) - ln(wt pct N in alloy)] Adding ½ N2(g) to each side and subtracting N (1 wt pct in Fe) = ½N2(g), the total free energy for solution of nitrogen in an alloy, referred to nitrogen at infinite dilution, is given by: ½N2 (g) = N (wt pct in alloy) L3] AG°3 = -RT ln(wt pct N in alloy )PN =1 atm Interaction parameters have their usual meaning when ?G°/RT is differentiated with respect to the proper composition coordinate. If desired, the dilute alloy treatment may be utilized with the new reference composition as the solvent. This has. indeed, been done by Small and pehlke5 in their analysis of nitrogen solution in liquid 18-8 alloys. The Sieverts' technique was used for this investigation on an apparatus previously described.6 The materials used in this program were: Ferrovac-E iron, 99.95 pct, Crucible Steel Co.: chromium, 99.95 pct, Union Carbide Metals Co.; nickel, 99.9 pct, International Nickel Co. Recrystallized alumina crucibles were used with no evidence of crucible-melt reaction. RESULTS The locations of the ternary compositions investigated are shown in Fig. 1. The data of Turnock7 and small8 have been alluded to in other papers.5'6 There were no departures from Sieverts' law observed for

Jan 1, 1969

By Gearge C. Wallick

This paper describes experimental procedures for the calibration of capillary tubes to be employed as comparison standards in gas flow-rate measurements and considers several types of flow which were observed in the calibration of seven capillaries of varying diameter. It is shown that under certain experimental conditions deviations from Poiseuille flow are observed which may not be attributed to turbulence, and that this flow behavior may be described empirically by introducing the classical kinetic energy correction into the Poiseuille equation. INTRODUCTION Techniques have been developed for the measurement of the volume rate of flow of nitrogen through glass capillary tubes as a function both of the differential pressure applied and of the absolute gas pressure. Capillary tubes thus calibrated are frequently used to determine the rate of gas flow through a porous sample in the measurement of slip-corrected permeability. The purpose of this note is to describe the calibration procedure and to discuss some observed deviations from the ideal flow behavior predicted by the Poiseuille equation. EXPERIMENTAL PROCEDURE The volume flow rate of nitrogen as a function of the differential pressure was determined experimentally for a series of seven glass capillary tubes of varying diameter. As is shown in Table 1, the capillary radii in the series ranged from 0.004 cm for K1 to 0.07 cm for K7. The capillary tubes were cut from capillary tubing purchased on special order from several manufacturers and the bore radii were determined by microscopic measurement. The gas volume flow rate was measured for each capillary tube at a series of differential pressures in the range from 0 to 3 cm of mercury and at average absolute pressures of 1.0, 2.5, 4.0, and 6.0 atm. Experimental Procedure for Small Capillaries A schematic diagram of the apparatus used to calibrate the three smallest capillaries, Kl, K2, and K3, is shown in Fig. 1. By means of a standard Ruska Instrument Corp. volumetric pump (equipped with a synchronous motor drive, two stages of gear reduction, and a quick-change lathe gear box), nitrogen was displaced by mercury from a metal cell immersed in a constant-temperature bath. The pump, the line to the cell, and a part of the cell were filled with mercury. As mercury was forced into the cell, it displaced nitrogen which passed through the capillary tube being calibrated and into a large container with a volume of approximately 30 liters. Since the volume of this container was very large compared to the total volume change of the gas resulting from the action of the displacement pump, the absolute pressure of the system was essentially constant throughout any one run. Prior to any determination this pressure could be set at any desired level by means of an auxiliary nitrogen cylinder. The differential pressure across the capillary was measured with a Meriam Red Oil manometer and recorded together with the corresponding pump displacement rate which was equal to the gas flow rate. By repeating this process for a series of different displacement rates at each of the absolute pressures of interest, the data necessary for plotting the calibration curves for capillaries K1, K2, and K3 were obtained. All calibration measurements were made in a constant temperature room to minimize errors due to temperature fluctuations. In each run. the flow was maintained until equilibrium was established. Experimental Procedures for Large Capillaries The flow rates through Capillaries K4, K5, K6, and K7 required to obtain the pressure drops desired were larger than could be obtained from available constant displacement pumps, and it was thus necessary to employ an alternative calibration procedure. The arrangement of apparatus used in calibrating these capillaries at an average pressure of one atmosphere is shown in Fig. 2. Each capillary was calibrated by flowing nitrogen through the capillary and recording the differential pressure as a function of the flow rate. 'The differential pressure was measured with a Meriam Red Oil manometer and the flow rate was determined by collecting the effluent gas over water at constant pressure and recording the increase in volume per unit time after an equilibrium had been established. Appropriate corrections were made for the

Jan 1, 1953

By Wm Price

THE object of this paper is to present a survey of some of the physical properties of sheet nickel silver when subjected to cold rolling and when annealed at temperatures extending from 350° C. throughout the commercial annealing range. A number of alloys were taken from stock and analyzed. Four of these, representing low nickel and high nickel both with and without lead, were chosen for the tests. The analyses were as follows: ALLOY COPPER, LEAD, IRON, NICKEL, MANGANESE, ZINC, PER CENT. PER CENT. PER CENT. PER CENT. PER CENT. PER CENT A 64.68 Trace 0.194 - 6.73 0.06 remainder B 65.82 1.27 0.227 6.17 0.06 remainder C 65.44 Trace 0.345 17.83 0.08 remainder D 65.60 1.08 0.238 17.77 0.06 remainder These alloys were rolled in accordance with regular mill practice to approximately No. 6 B. & S. gage. The bars (which were then coiled) were annealed together in a mill muffle and afterwards pickled in a 10 per cent. sulfuric-acid solution and cold rolled in stages of approximately .one number (B. & S.) at a time to No. 18 B. & S. gage. After each stage, suitable samples were set aside for physical tests. Additional samples were chosen for tests after the bars were rolled to Nos. 8, 10, 12, and 14 gage. These samples were annealed together in the mill muffle and, after pickling, were finished on 0.050-in. gage, yielding a series of specimens 2, 4, 6, and 8 numbers hard for the subsequent annealing tests. Tensile test pieces 9 by 1 in. (22.9 by 2.5 cm.) were cut from both lots and the central portion was milled to give a test section 2 ½ in. long by ;Z in. wide. A distance of 2 in. was marked off on the edge of each specimen with light punch marks. In the case of the annealed alloys, Erichsen test pieces 4 by 2 1/2 in. were also taken.

Jan 10, 1920

By Cyril Smith

A STUDY of the mechanical properties of the alloys of copper and silver led to the discovery that the solubility of silver in copper was greatly different from that generally supposed, therefore some work was done to determine the solubility with greater accuracy than had previously been achieved. After the work had been completed, two papers were published1 giving solubility figures which agreed closely with one another and with the work described herein. A detailed comparison of that work with the present will be given later. PREPARATION OF ALLOYS The copper used in making the alloys was electrolytic ingot of high purity. The silver was prepared by precipitation as chloride from nitric acid solution, followed by fusion of the washed precipitate with sodium carbonate and potassium nitrate. This method gives metal containing at least 99.99 per cent silver. The copper was first melted under charcoal in a small electric resistance furnace and the silver added as pure silver, it being unnecessary to make any intermediate alloys. After thorough stirring the metal was poured into a mold of suitable form. The alloys contained between 0.008 and 0.015 percent of oxygen. Small amounts of oxide were visible under the microscope, but it is not believed this would have much effect on the results. Copper-silver alloys are notorious for segregation, consequently a few experiments were carried out to find a form of casting with as little segregation as possible. A mold 6 in. long and 1/2-in. dia. was first used, and an alloy nominally containing 5 per cent silver was cast in it, while some of the same alloy was poured directly into water to obtain the maximum rate of cooling possible. Analyses were made both on this sample and on turnings from the top and bottom of the 1/2-in. dia. casting, the turnings being separated into three parts according to the position

Jan 1, 1931

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By R. W. Moore, A. B. Kinzel

Although the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approximately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cenlentite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consideration of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:' C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown In Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850" C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the sample after 5 min. at 850" C. is shown in Figs. 3 and 4, and the nest of pearlite surrounding the graphite nodules is most satisfactory evidence of the character of the nodules. As the length of time of heating at this temperature increases, the pearlitic zone increases, with final restoration

Jan 1, 1935

By A. R. T. Denues

LIQUID-OXYGEN explosives commonly consist of a carbonaceous absorbent enclosed in a canvas wrapper and soaked with a liquid con-taining more than 90 mol per cent of oxygen. Investigation of these explosives in this country was initiated in 1917 by George S. Rice, then Chief Mining Engineer of the Bureau of Mines. The early development is summarized in two papers.1,2 Their characteristics, advantages and disadvantages were considered in a recent bulletin of the Bureau of Mines.3 Other publications of this Bureau4,5 treat the technology of these explosives and contain adequate references to pertinent literature. These investigations defined the properties of liquid-oxygen explosives and improved them greatly; however, an outstanding disadvantage is their high inflammability, a property of critical practical importance. These explosives as hitherto prepared are easily inflamed; the combustion resulting from an accidental ignition is particularly dangerous because of the ease with which it passes into detonation. For this reason the Bureau of Mines undertook a cooperative investigation, which has resulted in the development of fire-retardant treatment for the minimiza-tion or elimination of this hazard without materially impairing the explosive properties, including the ease of detonation. This presentation will offer a general description of the investigation and the outstanding results. Further phases will appear in subsequent short papers, and the entire investigation including the results of detailed experiments will be available in a forthcoming bulletin of the Bureau of Mines (Bull. 429). The effects produced by fire-retardant treatments of the carbonaceous absorbent and of the canvas wrappers were investigated separately, and the efficacy of combinations of these treatments with particular reference to the possibility of inflammation and to the development of detonation from inflammation was studied. The experimental explosive was pre-pared from a granular carbonaceous absorbent and the results described may be more or less unique for such a material. An extensive preliminary

Jan 1, 1940

By C. S. Barrett

IT has been observed that deformation in iron takes place by slip on {110} + {112} + {123} planes1,2 but in silicon ferrite with low deforma-tion temperatures or high silicon contents (exceeding 4 per cent) the authors have found that slip is confined wholly to {110} planes, at least with small amounts of deformation. The purpose of the present inves-tigation was to determine the effect of this alteration of slip mechanism on preferred orientations in cold-rolled and recrystallized strips. Inci-dental observations on the effect of the recrystallization temperature were also made. The numerous determinations of the texture of cold-rolled iron and steel have been in satisfactory agreement as to the principal features of the texture. (with the exception of a few conclusions that apparently have been based on insufficient data). The texture is chiefly one in which [110] directions of the grains lie along tile direction of rolling, with a deviation of a few degrees, and in which the (100) planes lie in the plane of the rolled sheet, with a deviation from this position chiefly about the rolling direc-tion as all axis 3-9. This deviation about the rolling direction as an axis has been measured by different observers and lies between about 45° and 50° or 60° for iron5,6,9 and is usually in the neighborhood of 50° for mild steel6,7,8. The range of this deviation is a function of the percentage of total reduction 8, 10. Post' reported that it decreases with increasing percentage reduction, but apparently he .studied only the surface material, which Gensamer and Mehl7 found to be somewhat differently oriented from the material in the inside of the sheet. McLachlan and Davey10 found that the deviation also decreases with increasing percentage of total reduction for the material in the interior of the sheet and is independent of the percentage of reduction per pass.

Jan 1, 1937

By P. W. Bakarian, C. H. Mathewson

THE greater part of the literature on the plastic behavior of magnesium dates back to that active period of research in crystal mechanics immediately following the widespread preparation of isolated metallic crystals large enough for the application of conventional methods of mechanical testing. These investigations, performed on single crystals, revealed an analogy between zinc and magnesium with respect to their fundamental mode of deformation, in the operation of glide and twinning, respectively, on crystallographically similar planes. Mathewson and Phillips (1928)1 by geometrical analysis identified the {102} ? plane in magnesium as the twinning plane, Schiebold and Siebel (1931)2 confirmed this twinning plane, established the basal plane as the plane of slip, and a digonal axis I as the slip direction. They also reported twin formation in a secondary role on the {101} plane. Schmid (1931)3 summarized and discussed the earlier evidence and presented the results of his own experiments on the effect of temperature and small amounts of soluble elements. From X-ray studies on extended wire single crystals, he concluded that slip along the basal plane in the direction of the digonal axis I closest to the stress direction was the sole slip system operating at atmospheric temperature. This conclusion was based on experiments with crystals of many different orientations relative to the stress axis. Special attention was directed to the basal plane and the digonal axis I, as the plane and direction of greatest atomic density. Determinations of resolved shear stress at the onset of plastic yielding-i.e., the critical resolved shear stress-were also made; the average of these calculations showing 82.9 grams per sq. mm. This value varied only slightly up to 300°C., at which temperature it was found to decrease to 70.5 grams per sq. mm. The extension of his crystals at temperatures above 225°C. further disclosed the presence of new slip systems. After the original specimens of circular section had been

Jan 1, 1943

By Arthur S. Dwight

From the latest and best literature on lead-smelting, little can be learned concerning the present state of the art of mechanical feeding in the United States. H. O. Hofman, in his Metallurgy of Lead (5th ed., 1899), briefly describes the main features of the system in use at Pueblo, Colo., and later (p. 235) says " the only successful mechanical feeding, as far as the writer is aware, is that found at the works of the Pueblo Smelting and Refining Co." H. F. Collins, in his Metallurgy of Lead and Silver (London, 1899), covers American practice pretty thoroughly; but as to mechanical charging, he says: "The German plan of taking off the gases by means of a small iron pipe suspended in the center, and the plan of charging by means of cup and cone, as in iron blast-furnaces, have both been tried, but have not found favor, chiefly on account of the difficulty of obtaining free access to the furnace-shaft for barring, etc., with such devices."' . H. W. Hixon, in his Notes on Lead and Copper Smelting (3d ed., New York, 1900), gives a description and drawing of the Hixon feeding device, as originally installed at East Helena. Evidence that this system of feeding has passed its experimental stage, and deserves more serious consideration than it has heretofore received, is furnished by two large plants—the Pueblo and the East Helena—of the American Smelting and Refining Co., where mechanical feeding has been in continuous and successful operation for a considerable period; one new plant now erecting at Salt Lake City, Utah, and one old one belonging to the same company, the El Paso works, now being rebuilt after a disastrous fire, in both of which mechanical feeding is to be a prominent feature ; one new plant of an independent concern at Torreon, Mexico, which will adopt mechanical feeding; and a number of other smaller plants, among

Jan 1, 1902

By Ralph D. Parker

The Frood mine (Fig. 1) is 2½ miles north of Sudbury, at a general elevation of 1000 ft. above sea level. It includes the original Frood location, which was the No. 3 mine of the Canadian Copper Co., and the adjoining Frood Extension, which until 1929 belonged to the Mond Nickel Co. Mine Openings The mine is operated from two vertical shafts and one underground incline shaft. No. 3, for men, supplies and ore, is a vertical six-compartment shaft in the footwall of the south mining area and extends froin surface to a depth of 3045 ft. No. 4 is a vertical three-compartment shaft, 2500 ft. north of No. 3 and adjacent to the north mining area. It extends from surface to a depth of 3345 ft., and is used exclusively for hoisting ore. No. 5 shaft, inclined at 65' to the horizontal and of three compartments, is near No. 4 and extends from the 2600-ft. level to 77 ft. below the 3100 level. It is used for development below the 2800 level. The ventilation shaft, No. 1, with which this paper is directly concerned, will be described fully in the following pages. Mining Methods The orcbody is laid out in 80-ft. sections at right angles to the gcneral strike and numerically indicated from the southern extremity toward the north. Each section consists of a 45-ft. stope and a 35-ft. pillar, extending the full width of the orebody. Pillars and stopes are superimposed from level to level. The present mining territory is divided into two vertical areas, a north and a south area. Both areas have the same number of stopes on each level, the two areas being separated by 10 sections to be mined later. In a few instances, at the ends of the south area, where the orebody has narrowed, longitudinal stopes are used, of more than the usual 45-ft. width. It will thus be seen that mining operations hare been concentrated in two relatively small areas, offering

Jan 1, 1934

By Earl S. Greiner, Bradley Stoughton

As a part of the systematic study of the alloys of iron under the auspices of the Engineering Foundation, and preliminary to the commencement of comprehensive work on this larger subject, the authors have undertaken an investigation of the available literature dealing with the alloys of iron and silicon. The purpose is to collect all the data in English and foreign languages and present them in two monographs, one of a more scientific and the second of a more industrially useful nature. Of course, a great deal of information upon the constitution of the iron-silicon alloys was found specificially upon the changes of phase in the equilibrium diagram and the different phases present, such as solid solution, chemical compounds (iron silicides), etc. While no extended research was contemplated in the particular study undertaken, nevertheless the data collected proved to be so contradictory in many respects that a simple study of some of the outstanding problems involved in the constitution and equilibrium diagram was undertaken. Because research was not a primary object of the work, and also because of the extreme industrial importance of the silicon alloys between 0.80 and 14 per cent. silicon, and finally because of the unsatisfactory state of knowledge existing as to these alloys, the experimental investigation was limited entirely to alloys with less than 10 per cent. silicon. Discussion oF Continuous Series It has often been said in print that the iron-silicon alloys form a continuous series of solid solutions from 0 to 15 per cent. silicon. This claim the authors are inclined to doubt: first, because the alloys from 0 to 4.25 per cent. silicon are ductile and malleable at atmospheric temperature, while those with 5 per cent. or more of silicon are comparatively hard and brittle. Furthermore, the alloys with more than 4.25 per cent. silicon are comparatively hard and low in ductility at atmospheric temperature, but become much more ductile when heated slightly. It is well known, for example, that the alloy containing 4.75

Jan 1, 1930

By J. E. Burke, C. S. Barrett

THE fine lines shown in Fig 1 are typical of markings that may be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied to them, such as deformation lines or strain markings, indicate this uncertainty. In this paper which reports the results of a further investigation of their nature, they will be called strain markings. INTRODUCTION Matthewson and Phillips1 in 1916 concluded that strain markings appeared only after deformations that exceeded 20 pct. They objected to the markings being called slip lines believing this term should be reserved for surface markings produced by plastic deformation. In 1921, Vogel2 described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallographic in nature, and since they resemble Neumann bands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matthewson3 reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as evidence that the markings coalesce into annealing twins, and hence that they themselves are mechanical twins. Many attempts have been made to [ ] demonstrate directly that the markings are mechanical twins. In 1934, Samans4 described the results of X ray studies of two deformed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings are mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5,6,7 although in no case was the original method of Samans employed. An

Jan 1, 1948

By Philip Davidson, Wm. B. Price

The object of this paper is to present, a survey of some of the physical properties of sheet nickel silver when subjected to cold rolling and when annealed at temperatures extending from 350" C. throughout the coininercial annealing range.. A number of alloys were taken from stock and analyzed. Four of these, representing low nickel and high nickel both with and without lead, were chosen for the tests. The analyses were as follows: Alloy Copper, Lead. Iron. Nickel, ManGanese, Zinc, PeR Cent. Per Cent. Per Cent. Per Cent. Per Cent. PEr Cent. A................ 64.68 Trace 0.194 6.73 0.06 remainder B................ 65.82 1.27 0.227 6.17 0.06 remainder C................ 65.44 Trace 0.345 17.83 0.08 remainder D................ 65.60 1.08 0.238 17.77 0.06 remainder These alloys were lolled in accordance with regular mill practice to approximately No. 6 R. & 6. gage. The bars (which were then coiled) were annealed together in a mill muffle and afterwards pickled in a 10 per cent. sulfuric-acid solution and cold rolled in stages of approximately one number (B. & S.) at a time to No. 18 B. & S. gage. After each stage, suitable samples were set aside for physical tests. Additional samples were chosen for tests after the bars were rolled to Nos. 8, 10, 12, and 14 gage. These samples were annealed together in the mill muffle and, after pickling, were finished on 0.050-in. gage, yielding a series of specimens 2, 4, 6, and 8 numbers hard for the subsequent annealing tests. Tensile test pieces 9 by 1 in. (22.9 by 2.5 cm.) were cut from both lots and the central portion was milled to give a test section 2 1/2 in. long by 1/2 in. wide. A distance of 2 in. was marked off on the edge of each specimen with light punch marks. In the case of the annealed alloys, Erichsen test pieces 4 by 235 in. were also taken.

Jan 1, 1921

By M. W. Fabjanczyk, E. G. Alexander

INTRODUCTION The purpose of this paper is to summarise development of design processes used in the 1100 oreoody as a result of experience encountered. Design methods have been developed as a result of the history of ground behaviour, free-standing qualities of cemented back fill and mass blasting techniques. This paper contains an historical review of design methods previously described by Matthews ( 1972 ) , Hornsby and Sullivan (1977 and 19781, Kirkby, Blair and Hutton (19781, and Stewart (1980). The reasoning behind design philosphy changes are discussed and placed into context with methods now adopted. The 1100 orebody is Mount Isa's main producer of copper ore (5 million tonnes per year ) . Proven reserves are 120 million tonnes at 3.2% Cu. Location of the 1100 orebody in relation to overall mine geometry was well described by Dayton (1976). Geology The orebody is located in a series of massive brecciated shale lenses, in either a siliceous or dolomitic matrix, surrounded and separated by a uniform shale sequence. The whole formation is truncated at depth by a faulted contact with a greenschist facies metamorphic sequence below (Figure 1 and Figure 2) Mathias and Clark (1976). The breccia is known locally as silica dolomite and contains nearly all the economic mineralisation. Interfingering of shale and breccia often results in irregular boundaries to the silica dolomite and the ore limits. Geometry The geometry of the orebodies is shown by Figures 1, 2 and 3. Figure 3 also shows the location of the copper orebodies in relation to the lead orebodies. Structure Although the orebody is contained within the massive breccia (u.c.s. 150-250 MPa), it is cut by shear zones sub-parallel to the regional bedding (north-south striking, dipping approximately 60o to the west), and diagonally by major transverse faults (Figure A). These major faults have continuity in excess of 300 metres, with varying amounts of displacement up to 200 metres, and are zones of potential movement.

Jan 1, 1981

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

1. How Does One Determine Whether an Ore Body Will Block-cave? Page Mark A. Smith......... 122 Harry A. Leidich........ 122 McHenry Mosier ...,.. 22 R. W. Hughes ........ 122 Sherman R. Burdick ....... 123 R. T. Gallagher........I 23 Benjamin F. Tillson...... 123 Lucien Eaton...........123 C. F. Jackson..... . .. 123 Philip B. Bucky........... 126 2. How Does One Determine the Block Dimensions and the Development Work Necessary to Make an Ore Body Cave? Mark A. Smith... 125, 127, 129 Harry A. Leidich..........126 McHenry Mosier......126, 127, 132 R. W. Hughes...........126 Sherman R. Burdick.........127 R. T. Gallagher...........127 Benjamin F. Tillson......127,131 L. E. Young............127 Robert D. Hoffman.......128, 132 Gerald Sherman..........128 Philip B. Bucky......130, 131, 132 K. S. McClellan..........132 Tell Ertl.............132 3. How Do the Forces Act and What Are the Stresses Developed in a Block That Cause It to Block-cave? Mark A. Smith.........132, 135 Harry A. Leidich........133 McHenry Mosier . .. 133 R. W. Hughes ....... 133 Sherman R. Burdick..... . 133 R. T. Gallagher..........134 C. F. . Price, Jr. ........134 Benjamin F. Tillson.........134 C. F. Jackson......134, 135,137 R. Taborelli...........135 Frank A. Ayer ... .....136 Philip B. Bucky . .........136 Rollin Farmin . . .......136 . . . Weysser.....135, 136, 137 George S. Rice...........137 4. What Determines the Procedure in Removing Caved Ore? Harry A Leidich...........137 McHenry Mosier........137,141 R. W. Hughes...........137 Sherman R. Burdick........138 R. T. Gallagher...........138 Mark . Smith...........138 Philip B. Bucky......140,141,143 C. F. B. Price, Jr..........140 R. H. Bennett...........141 C. F. Jackson..........141, 143 Gerald Sherman..........141 Tell Ertl.............141 .. .. ..................143 C. H. Shoemaker..........143 5. What Are the Criteria for Determining the Efficiency of a Block-caving Operation? Harry A. Leidich.......... 143 McHenry Mosier......... 144 R. W. Hughes........... 144 Sherman R. Burdick.......144 R. T. Gallagher . ......... 144

Jan 1, 1946

By Alden Greninger

IN a recent study1 of the deformation of metastable beta copper-zinc and beta copper-tin crystals, it was established that the parallel markings that appear on the surface of these crystals after slight deformation represent lattice transformations. Stereographic analysis showed that in beta copper-tin, the poles of these markings deviated one or two degrees from poles of the form { 133 } . In beta copper-zinc the plane delineated by the markings corresponded to no one crystallographic plane of the matrix lattice; the marking poles deviated from 5° to 11° from poles of the form {110}, and were displaced only a few degrees from (110) zones. Inasmuch as the new transition lattices produced as the result of the deformation are different for each alloy, it was thought at first that the habits of the markings might be the result of a cooperation between matrix lattice and transformed lattice. (Both matrix lattices are body-centered cubic.) Such a cooperative effect is thought to obtain in the formation of Widmanstätten figures, for it is well known that the matrix lattice alone does not determine the habit assumed by a segregate phase. On the other hand, it is not inconceivable that the dissimilarity in mark-ing habit might be due to differences in deformation characteristics of beta brass and beta bronze. Barrett and co-workers2 have shown that slip-line habits in pure iron are markedly different from those in high-silicon ferrite; and although it has been repeatedly demonstrated that plates of a segregate phase do not necessarily form on the slip planes of the matrix lattice, deformation characteristics may be more intimately allied with plate formation when a transformation is made to occur as a result of plastic deformation. However, there is the fact that the orienta-tion of markings in metastable beta copper-zinc is the same whether the markings be produced by quenching, deformation, or liquid-air cooling; likewise, quenching and deformation markings in metastable beta copper-tin are oriented in the same way with respect to the beta matrix.

Jan 1, 1938