By J. H. Lee

LG Metals Corporation started its second smelter operation at Onsan along with the existing flash smelter on January 31, 1998. Onsan smelter has been producing about 140,000 tons of copper annually from concentrates with the flash smelting line since 1979. In accordance with an increase in domestic copper demand, LG Metals Corporation decided to expand smelting and refining capacity by introducing a second smelter line using the Mitsubishi continuous process and a new tankhouse in 1995. After two years' expansion works consisting of engineering, procurement, construction and a successful commissioning test, the total smelting capacity of Onsan smelter increased to 340,000 ton of copper annually from concentrates. This paper describes the smelting facilities, operation result, problems encountered and improvements during the start-up and early operation of Onsan's new smelter

Jan 1, 1999

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Kexin Jiao, Zhijia Zhang, Jianliang Zhang, Zhengjian Liu

Carburization behavior of molten iron in blast furnace is an essential part of BF long campaign technology. Maintaining carbon content stable is an important prerequisite to ensure the high production of the blast furnace. In this paper, the important aspects of the research progress which mainly including the study of iron carburization at the upper and the lower parts of the blast furnace was reviewed. Indirect carburizing is the main way at the top of the blast furnace. The content of carbon in metallic iron increases with the reducibility of iron ore improved. The thermodynamics and kinetics conditions are good for carburization reaction to take place at the bottom of the blast furnace. Carbon content of molten iron increased by coke carburizing. Meanwhile, the drawbacks of the existing literature on iron carburization behavior were analyzed and new research directions of iron carburization were proposed in the future.

Jan 1, 2015

By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with C02 is expected to occur at as low temperature as possible. In order to get a highly reactive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of C02. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining al\ the obtained data.

Jan 1, 2003

By Fuming Wang, Xin Lu, Hao Bai, Hebin Zhu

"In this study, CO2 emissions and carbon footprint of a typical steel works with integrated process and iron and steel industry in China was calculated and analyzed by a carbon footprint method based on the model of process CO2 emissions in iron and steel making. The carbon footprint of iron and steel industry from 1991 to 2010 in China showed a rapid increasing tendency. In 2008, the CO2 emissions of iron and steel industry in China was 1.289 billion tons, 19.71% of the national total CO2 emissions, and the corresponding carbon footprint was 159.13 million hm2 of green area. Carbon deficit of iron and steel industry also go up gradually if considering the carbon storage by green vegetation. Thus, the internal carbon reduction strategy, such as energy structure optimization and energy saving technology, was mainly encouraged for the sustainable development of iron and steel industry in China.IntroductionThe Global Warming resulting from the increase of Greenhouse Gases (GHGs), in particularly CO2, in the atmosphere has become the main reason of global climate change, and large emission reductions are required for sustainable development [ 1]. The iron and steel industry is the largest energy consuming manufacturing [2] in the world and the largest emitter of CO2 emissions. In 2005, it accounted for about 20% of global industrial energy use and 30% of energy and process CO2 emissions from industry [3]. In China, the crude steel has firmly been ranking at first of the world recent years and kept growing tendency year by year. With the production growth, the CO2 emissions of iron and steel industry also increased significantly and hence the steel industry has become one of the most sources of CO2 emission in China [4], which has attracted more and more attention to seek the carbon reduction strategies.Carbon footprint is an important and useful concept originating from Ecological Footprint, which was used efficiently to quantitatively analyze the impact of the human activities on ecological system, in particularly impact of the human energy activities [5]. In the view of Life Cycle, the carbon footprint is efficient to analyze the direct and indirect CO2 emission in the whole life of various products used in human activities. As to the iron and steel, the important materials and products in the human life, the carbon footprint analysis is quite necessary to evaluate the CO2 emission impact on the corresponding ecological system and global environmental."

Jan 1, 2013

By F. K. Letowski

Leaching in froth is a particular case of a three phase (liquid-solid-gaseous) process which combines flotation with leaching by using a reactive gaseous reagent as a flotation carrier and a leaching solution as the reactive liquid medium to fonn the foam (froth) in' which the solid particles are suspended. Some physico-chemical and engineering aspects of leaching in froth are discussed and illustrated by its application for cleaning the mineral graphite. Leaching of the graphite concentrate containing 4L4% of the elemental carbon and 3.16% of the sulphidic 'sulphur was canied out in the froth fonned by: (a) a concentrated chloride solution, with a small addition of nitric acid, in the foam state; (b) a mixture of gaseous O2, NO., and H20 encapsulated in the foam; and (c) notable particles of graphite suspended in the foam. The laboratory experiments werecanied out in a "flotation column"-type reactor ala temperature from 80 to !08°C and under total pressure of 100 to 200kPa. In the 3-stage leaching-flotation process, the non-flotable fraction of particles was separated three times from the notable fraction. The concentration of carbon and elemental sulphur in the final flotable fraction was 96% C and 0.38% S respectively. The expected advantages and possible application in hydrometallurgy are suggested.

Jan 1, 1995

Al2O3,-WC Composite powder for cutting tools was synthesized by self-propagating high-temperature synthesis using A1 powder as a reducing agent. WC, W2C and Al2O3 were concurrently formed in WO3Al-C system. It was found that the complete reaction was achieved with excessive addition of carbon and appropriate processing parameters such as degree of dilution, particle size of aluminum, compaction pressures of green pellets and carbon source. The final product which was leached by 50% HN03+HF diluted solution was consisted of Al2O3-55wt% WC having 2-3um of mean particle size.

Jan 1, 1999

By T. Inami

The chlorine leach of the anode slime was studied in order to improve the treatment process at the Niihama Nickel Refinery. The anode slime originates from the nickel matte electrorefining and, contains 3-5% of nickel as sulfides. A comparative study has been conducted on the filter cake resulting from the sulfur filtration of the molten anode slime. The kinetic factors of the chlorine leach such as temperature, grain size were defined. Under the optimized condition, 70-80% of the nickel is recovered from the slime or filter cake. On the basis of these results, the chlorine leach process for the treatment of anode slime has been established. The leaching plant has been installed and successfully operated since 1986.

Jan 1, 1988

By Guo-hua Bai, Hong-jing Yuan, Qian Li, Yong-bin Yang, Tao Jiang, Yan Zhang

"The effect of different additives on the bio-oxidation of arsenic-bearing gold ores has been carried out to solve the problems such as long period of leaching, low oxidation rate. The oxidants strengthen the cathodic reaction and thus improve the leaching rate by the increase of electron transfer. Meanwhile, silver catalysis is also effective for the decomposition of arsenicbearing gold ores due to the strengthening of anode reaction. Co-intensification by oxidants and Ag (I) is more efficient to the bio-leaching and the conversion of As (III) because the anode and cathodic reaction of biological oxidation of sulphide ores were both strengthened. The leaching rate reached to 63.94% after bio-leaching 13days by co-intensification of Ag (I) and Fe(III).IntroductionWith the worsening global ecological problems and the gradual exhaustion of available gold resources, metallurgical technology of refractory gold ore has received more and more attention and become possible due to its good advantage of the economic effects and negative effects to the environment. Refractory gold ore, the direct cyanide leaching rate of that is defined as less than 70%, has become an important raw material in gold extraction industry, in which sulfide bearing gold ore represents a large proportion, pyrite and arsenopyrite (FeAsS) is a common gold-bearing mineral. Since the gold is often encapsulated in the crystal lattice of these minerals, destruction or alteration of the ore to liberate the submicron and/or structurally bond gold is necessary[l]. Even if the ultrafine grinding approach also is generally not sufficient for these refractory ores and additional techniques like roasting, pressure oxidation and bacterial oxidation are used to liberate the gold [2]. In the three pretreatment processes, bacterial oxidation is characterized by its new ideas, low cost, no pollution, simple equipment and operation, high leaching index and become the most promising process which has received much attention over time [3-5]. But its further application is limited by some of its own shortcomings, such as long pretreatment time and the toxic effects of arsenic to bacteria on bio-leaching limit."

Jan 1, 2013

By Liang Yu, Yuhua Li, Yuanchi Dong

"High alumina slag, with alumina normally more than 15 pct, is encountered with blast furnaces in China because of high alumina/silica ratio in iron ore as well as sinter and high ash content in coke for cost reason. High alumina slag with high viscosity and high liquidus temperature would lead to higher slag volume and thereby, furnace productivity. In the present work, liquidus temperature of high alumina slag, based on Meishan factory, Baosteel China, were investigated. A liquidus temperature model was introduced in the present work based on basic physical chemistry theory and focused on the chemical composition area used in Meishan factory(pct): Al2O3 from 14 to 17.5 and MgO from 8 to 12, so that the blast furnace slag could be designed for optimum blast furnace performance.IntroductionBlast furnace slag composition[1] has very important bearing on its physicochemical characteristics which affects smoothness of operation, slag handling, coke consumption, the degree of desulphurization, hot metal productivity and its quality etc. The slag properties which affect most are liquidus temperature, viscosity, sulphide capacity and alkali capacity. Variation of these slag characteristics with composition and temperature has been a field of active researches as these its great influence on the blast furnace operation. In the early years, most of these studies were carried out over low alumina blast furnace slags with alumina normally less than 15 pct. High alumina slag was first introduced in India because of its high alumina/silica ratio iron ore as well as sinter and high ash content in coke[2]. And then this problem becomes common as higher alumina/silica ratio iron ore imported and used [2-5]. The most important problem caused by high alumina content is liquidus temperature and then viscosity of the slag.Generally speaking those reported works [2-5] investigated a pretty wide range of chemical compositions and then obtained complex model, respectively. In fact, every factory has its own interest because of different resources. For example, the Al2O3 content from 20% to 30% pct was studied in Tata Steel India [2], but it is too high for Baosteel Meishan. A very lower percentage of alumina content, 14-18 % pct, was mainly used."

Jan 1, 2008

By R. L. Player

"The Copper Isasmelt process has been developed over the past 15 years by Mount Isa Mines Limited (MIM) and the Commonwealth Scientific and Industrial Research Organisation (CSIRO). The first two commercial plants were commissioned in mid 1992.The results of four heat balances on the Mount Isa plant are presented. At a smelting rate of 98 t/hr of chalcopyrite concentrate plus 14 t/hr reverts, the total heat generated was -91MW. Approximately 39% of this energy came from coal, while 50% of the energy reported to the process waste gas. To a first approximation the furnace is near chemical equilibrium.The impurity distribution in the Mount Isa plant was presented. Approximately 91 % As, 85% Cd, 75% Bi, 68% Zn, 60% Sb and Tl, 45% Pb and 30% Te in concentrate was eliminated from the matte.The ""bubble"" frequency of the gas cavity below the foot of the lance was measured at -2. 1Hz. Side bands displaced by -l.lHz modulated the bubble frequency. This was consistent with radial gravity wave motion in the slag bath. The two processes, gas bubbling and wave motion appeared to be coupled together; the bubble frequency was twice the slop wave frequency. IntroductionCopper Isasmelt has been developed over the past 15 years by Mount Isa Mines Limited and the Commonwealth Scientific and Industrial Research Organisation. The process is based on the Sirosmelt lance, invented by researchers at the then Division of Mineral"" and ProcessEngineering ofCSIRO in 1973.The first two commercial scale copper furnaces were commissioned at Mount Isa and the Cyprus Miami Mining Corporation smelter at Miami, Arizona in August and June 1992 respectively.The process concept, the history of the development, and the Mount Isa plant have been described (1, 2, 3).This paper sununarises heat balances obtained on the furnace, the impurity distribution among the output streams and lance injection characteristics."

Jan 1, 1996

By Zhucheng Huang, Ronghai ZHONG, Liangming Wen, Tao Jiang

The reduction roasting-magnetic separation and its strengthening of high silicon coal-containing mini-pellets by sodium additives were researched. The results show that the carbon gasification reaction and reduction of fine hematite in high silicon coal-containing mini-pellets with 3% sodium additives were enhanced. Comparing with no sodium additives, the gasification rate of carbon with 3% sodium additives reacting with CO2 for 40 minutes at 950 and the metallization rate of reduced pellets with 3% sodium additives after roasting for 35 minutes at 960 increased from 35.15% and 58.72% to 86.98% and 86.15%, respectively. The analysis of SEM equipped with EDS demonstrates that the inner pore of reduced pellets with 3% sodium additives was more developed and the iron grains size significantly enlarged, meanwhile, the iron grade of concentrate increased from 60.45% to 80.23% and the iron recovery rate decreased from 84.67% to 80.78% after grinding-magnetic separation.

Jan 1, 2016

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By Laurentiu Nastac

"The importance of investigating solute redistribution during the unidirectional solidification of multi-component alloys is broadly discussed in the literature. A previously developed analytical model that was experimentally validated for Al-Cu, Sn- Bi and Fe-Si dilute binary alloy systems is used in this article to study in detail the solute redistribution, the liquid/solid interface stability based on an extended transient constitutional undercooling criterion and the size of the initial transient region during the unidirectional solidification of Ti-6-4 and Ti-17 alloys. A comparison between Ti-6-4 and Ti-17 alloy systems with respect to interface stability and the size of the initial transient region is also provided. The effective partition coefficients of the alloying elements in these alloys were determined based on specially designed experimental measurements.IntroductionThe importance of investigating solute redistribution during alloy solidification is broadly discussed in the literature [1-5]. One of the relevant applications of this study would be the mathematical modeling of equiaxed and columnar solidification of multicomponent alloys. This includes the instability of the solid/liquid interface. There are several mass and heat transfer processes that involve the calculation of solute redistribution during directional solidification such as industrial directional solidification processes, continuous casting, remelting processes, Czochralski crystal growth technique, floating zone techniques, etc."

Jan 1, 2012

By M. Urda-Kiel

Stainless steel is increasingly used as a cathode starting sheet. It was shown earlier that even when depositing copper on copper, a substrate-influenced zone appears in the deposit structure, followed by a transition zone and finally by the electrolysis-influenced structure. On copper, the substrate-influenced zone has a thickness of twenty micrometers and on titanium, eventually more than fifty micrometers. Initial nucleation and growth have a considerable influence. In this paper, copper was deposited in a channel cell on four different 304 stainless steel substrates: mechanically polished and anodized, respectively, at 0, +400 and +800 mV/SHE in 1M H2SO4 at 20°C. Copper was deposited under electrowinning conditions after solvent extraction (SX) (40 g/l Cu++, 180 gh/l, H2SO4, 20 or 60°C). The results showed that, although Auger surface analyses of the substrates were only slightly different one from another including the oxide thickness, nucleation and initial stages of growth were very sensitive to the surface treatment of the substrate. Potential step and current step methods gave similar results : progressive nucleation followed by 3D diffusion controlled growth. The highest nucleation frequency was observed on stainless steel anodized at 0 mV/SHE, under various electrolysis conditions. The potential influence of these findings on industrial practice is discussed.

Jan 1, 1999

By Y. Ikeda

Typical electric appliances were dismantled into component pieces to study the recyclability of these discarded goods. Types and weight ratios of these component materials were investigated and characterized. The results showed that if they are dismantled properly, these goods could be classified into several groups of similar materials and/or structures, namely those consisting of single materials, metal-plastic combinations, metal-metal combinations and complex combinations of many different materials. By separating each combination into recyclable materials and isolating hazardous materials, it was found that the final waste for disposal could be reduced and the recycling efficiency could be improved markedly as compared to the conventional shredding method. The metal-metal combinations account for 60% by weight of the total metal contents in electric appliances, and therefore, it becomes important to segregate these metals. For the complex combinations, a process consisting of pyrolytic decomposition of plastic contaminants followed by smelting of the residue is proposed. It is anticipated that nearly zero-emission recycling of electric appliances will be achieved by applying this treatment process.

Jan 1, 1995

By Tian Sugui

By means of the long-term aging treated, creep properties measuring and microstructure observation, an investigation has been made into the microstructure and creep behavior of the casting and rolling GH4169 superalloy after long-term aged. Results show that, after the casting and rolling GH4169 superalloy treated by long-term aged, significant amount of " phase are dispersedly precipitated within the grains of the alloy, and some of the NbC, Cr7C3 carbide are distributed along the grain boundaries. In the range of the applied stresses and temperatures, the creep activation energies and stress exponents of LTA GH4169 alloy during steady state creep are calculated to be Q=541.1kJ/mol and n=16.2, respectively. During creep, the deformation mechanism of LTA GH4169 is thought to be the twinning and dislocation slipping within the twinning regions, and the damaging mode of the alloy is the intergranular fracture, and the non-smooth crystal surface is displayed in the fracture regions of the alloy. Thereinto, the carbides film formed along the grain boundaies has a few effect on the strength between the boundaries, which is a main reason of resulting in the alloy possessing a longer creep lifetimes.

Jan 1, 2009

By Filiz Sahin

This paper presents a synthesis of TiB2 via carbothermal reduction method using a mixture of TiO2, B4C and C prepared in molar ratio of 2:1:3. Reduction experiments were carried out in a high temperature graphite furnace in a graphite crucible under argon atmosphere at different time (0, 15, 30 and 60 min.) and temperatures (1400, 1500 and 1600 °C). The products obtained were investigated using XRD technique.

Jan 1, 2008

By Animesh Jha

"Fine ceramic powders (<500 nm) exhibit exceptional physical and mechanical properties in engineered structural ceramics. The production of fine powders, in particular the non-oxide ceramics, via a cheaper route than the organic solvent route has been rather elusive. This paper examines the physical chemistry of sub-oxide vapour-phase reduction reaction for the nucleation of non-oxide ceramic phase. Well known vapour species eg SiO and BO in the production of technical ceramic powders (SiC, BN) are particularly discussed for understanding the nucleation process of SiC and BN ceramic phases respectively. The regimes of partial pressures and temperatures are particularly 'identified. The calculated nucleation rate as a function of the temperature is compared with the experimental results on powder morphology. The production of amorphous and nanocrystalline h-BN powders is discussed in the context of substrate structure and thermodynamic parameters.IntroductionThe physical and mechanical properties of ceramic components are strongly dependent on the powder particle size and morphology used for their fabrication. For example the strength (Os) of the structural ceramic components increases with decreasing average grain-size (d) in accordance with the Hall-Petch relationship: Os = 0""0 + k/(d)1/2. Here k is an empirical constant which can be established from the graphical relationship. However as the particle size approaches submicrometer-size range, the dependence of strength on the particle size becomes more complex [1]. The design of ceramic components based on nanometer-size particles have recently become an important field which can offer ceramic materials with properties comparable to their metal counterparts. Several materials based on these concepts have been developed and reported by Niihara [2]. For example, the Al2O 3-SiC nanocomposite, having average B-SiC grain size 0.3-2um with intragranular SiC particulates of 5-10 nm has unusually high strengths (1100 MN/m2) at low and elevated temperatures combined with enhanced fracture toughness (> 4 MN-ml.5) which is an unusual combination in structural ceramics. Besides mechanical properties, as the particle size of ceramic powders approaches the nanometer-size range, the charge transport properties also improve by many times. The effect of particle size on the electrical conductivity of Si3N4-TiN composites has been well documented [3.4]. The size of ceramic particulates without doubt plays a pivotal role in determining the properties of ceramic components."

Jan 1, 1996

By Zachery Zanetell

Flotation circuit performance has become increasingly more challenging due to the complexity of available ore sources. To optimize value mineral recovery, the mineralogical composition of the ore should be evaluated and understood. Utilizing a variety of mineralogical and analytical tools, flotation processing challenges can be overcome and potential limitations understood. In this paper, several case studies will be discussed in terms of the value that has been provided through the use of mineralogical analysis to optimize flotation performance.