By Matti J. Saarivirta

The relative machinabilities of the precipitation-hardenable Cu-0.9 pct Cr, Cu-0.25 pct Zr, and Cu-0.9 pct Cr-0.25 pct Zr alloys are improved from 18 to 80 pct by 0.75 to 1.25 pct Pb. The Lead also improves the tensile strength, hardness, ad resistance to softening of the Cu-Cr and Cu-Cr-Zr alloys. When the alloy containing 0.7 to 2.2 pct Cr, 0.10 to 0.25 pct Zr, 0.75 to 1.25 pct Pb, and balance copper is solution-annealed at 1000°C (1830°F) and then aged at 525°C (Y75°F), tensile strength of 65,000 psi, 16 pct elongation, 62Rb hardness, and 84 to 87pct IACS electrical conductivity are obtained. The copper base Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys have high electrical and thermal conductivities, high strength and resistance to softening at elevated temperatures, but their machinability is poor, i.e., close to that of the pure copper. In the manufacture of various components such as welding electrodes or electrical and thermal conductors it is ofter desirable that the alloy have good machinability for high production rates and long tool life. Thus, alloys that combine these properties may be used not only for existing applications, but for new ones where good machinability is a requirement. This investigation was undertaken to improve machinability without impairing other desirable characteristics of the Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys. These commercial alloys contain about 0.4 to 1.2 pct Cr, 0.10 to 0.25 pct Zr, and balance copper. Lead was selected as an element that should improve the machinability and possibly other characteristics of the alloy. WORK PROCEDURE This investigation began with a study of the effect of lead on the hardness, tensile strength, electrical conductivity, and machinability of the binary alloy containing 0.10 to 1.30 pct Cr and balance copper. This was followed by an investigation of the effect of lead on the Cu-0.1 to 0.4 pct Zr and Cu-Cr-Zr alloys. The alloys were made from initially oxygen-free copper and for comparison some castings were made from phosphorus-deoxidized Lake Copper. Commercially pure chromium, zirconium, and lead were used for alloying. In melting the chromium was added to molten copper at 1400°C (2550°F), the heat held for 15 min at temperature, and the temperature then lowered to 1350°C (2460°F) when the other elements were added. The alloys were held for 15 min at this temperature and cast into a cast-iron mold. One-kilogram, 3-in.-diam castings were made. An argon cover was maintained during melting and casting to prevent oxidation. The chemical compositions of the alloys are shown in Table I. The micro structure and properties of the alloys were studied in the cast and wrought conditions prior to and after various solution-annealing and heat-treating cycles. The relative machinability was determined as a function of the lead content and compared with the free-machining Cu-lpct Pb alloy. To determine the machinability, 13/16-in.-diam cast specimens were cut by a machine hack saw using a constant cutting speed of 50 fpm, a fixed feed force, and a new blade for each alloy specimen. Molybdenum highspeed steel saw blades, 0.032 in. thick with 14 teeth per in., were used in all tests. No cutting fluid was used. Five tests were made on each specimen and the average elapsed time per test was taken as a measure of the relative machinability for that alloy. The variation of cutting time for each alloy was less than 110 pct.

Jan 1, 1969

By Edwin F. Brush, John Chipman

Published data on the activity of carbon in binary and ternary austenite at 1000°C are reviewed. The composition variables are . The coefficient, Vj, has the value for substitutional elements but may be assigned a ualue -1 for silicon to effect a simplification on the mathematical treatment. The activity coefficient PC = is obtained from gas equilibrium data. For the ternary systems studied the Henrian activity coefficient is given by the expression: The principle advantage in cornparison with the analogous expression in terms of atom fractions is found in the fact that for most systems the final term and in many the last two terms are zero. Values of the interaction parameters are tabulated and the graphical comparison of the equation with experirt~ental data is sho,wn in several figures. The thermodynamic properties of the solid solution, austenite, are of considerable importance in the heat-treatment of alloy steels and in other aspects of ferrous metallurgy. Early studies embodied in the Fe-C diagram have been extended to include other binary and some ternary diagrams. Our best hope of obtaining a useful thermodynamic treatment of reactions in complex alloy steels will not be found in quaternary and quinternary phase diagrams but in determinations of activities and interaction relations among the several solute elements. The foundation for such a development was laid by smith' in his early studies of the activity of carbon in Fe-C alloys and his subsequent work on Fe-C-Si, Fe-C-Mn, Fe-C-Ni, and Fe-C-Co solid solutions.2"4 Other observers have also made noteworthy contributions and these will be discussed and correlated here in the light of a somewhat simplified mathematical treatment of solute interactions. Fe-C AT 1000°C In a recent review of the thermodynamic properties of binary Fe-C austenite it was shown that the simple mathematical treatment employed by smith' was capable of describing all the published results on this solution. The treatment utilizes the atom ratio, yc = nC/nF,, rather than the atom fraction. The activity of carbon is proportional to the equilibrium gas ratio, either measured on a scalk in which the activity of graphite is taken as unity or, alternatively, aC may be set equal to yc at infinite dilution. In either case the ratio aC/y = (PC, the activity coefficient. It was found that the experimental data of smith1 and those of Diin-wald and wagner; Bungardt, Preisendanz, and Lehn-ert,' and Scheil, Schmidt, and Wiinnings at temperatures of 800" to 1200° C as well as reliable data on the solubilities of graphite and cementite could be represented by the equation for which graphite is the standard state: The data on alloyed austenite have been obtained at 1000°C. For this temperature, the "Henrian" activity coefficient (which is unity at infinite dilution) is: FOr an interstitial solute such as carbon in austenite it has been shown by statistical mechanicsg that the activity in the infinitely dilute solution is proportional to the ratio of the number of lattice sites occupied by carbon to the number of yet unfilled lattice sites. A variable zz proportional to this ratio serves as a useful measure of concentration:" in which b is the number of lattice sites provided by each atom of solvent; in austenite b = 1. The Henrian activity approaches zz at infinite dilution and the ratio a is the activity coefficient. The effect of a change in concentration is then given by: It has been shown further that in some systems the derivative in Eq. [4] remains constant over a wide range of concentrations. In such a case second-order terms become negligible and the Henrian activity coefficients is:

Jan 1, 1969

By Philip H. Nelson, Richard Lingle

Vibrating wire stressmeters (VWS's) and borehole deformation gages (BDG) were deployed in two in-situ heater experiments at Stripa, Sweden to determine the thermally induced stress changes in the rock mass. The heater experiments ran for 18 months, including a six- month cool-down period after the heaters were turned off. Gages were installed in both horizontal and vertical boreholes and were subjected to temperatures ranging from 10°C to 120°C, depending upon the distance of a gage from the central heater. Most gages operated in a moist environment because groundwater flowed into many of the instrument boreholes during the experiments Of the 36 VWS's installed, six failed. Failures were attributed to corrosion of the vibrating wire due to moisture entering the gage body. Of the 30 BDG's installed at the beginning of the experiments, 22 failed, also as the result of water entering the gage body. Modification and reinstallation of the gages eliminated the problem of water infiltration, but much data from early stages of the experiments was lost due to gage failures. Calibration of the VWS in blocks of Stripa granite showed a lack of repeatability. Variability in calibration results are attributed to seating effects, to variations in the elastic modulus of the rock, and to changes in temperature. These three effects combined to produce an error judged to be approximately ±33% of the stress changes measured at Stripa. In contrast, the major source of error in determining stress with the BDG appears to be the uncertainty in rock modulus and thermal expansion coefficient. Sample calculations based on data acquired near the end of the experiments (during cool-down)

Jan 1, 1982

By Charles E. Mann, Douglas J. Lootens, Rufino B. Bomasang

INTRODUCTION The economy of the Philippines, like that of many other developing nations, has been severely strained by the rapid escalation of imported crude oil prices over the past decade. In an effort to reduce its dependence on imported crude, significantly increased emphasis, both in the public and private sectors, is being placed on the rapid development of Philippine coal resources. This paper is designed to present an overview of the Philippine coal industry, its historical development, present status, and future potential. COAL RESOURCES AND RESERVES In 1977, a British consulting firm collated all available data on Philippine coal resources and estimated the total coals potential at about 0.9 to 1.4 billion metric tons (mt). In 1981, using more recent data the Philippine Bureau of Energy Development (BED) estimated the potential at 1.7 billion mt. The BED estimated the proven coal reserves at 257 million mt. These coal resources are scattered throughout the major islands comprising the Philippine archipelago. However, about 52 percent of the currently proven reserves are located in the tiny island of Semirara between the islands of Mindoro and Panay. About 25 percent is located in the Cagayan Valley in northeastern Luzon while 13 percent is located in Mindanao. The remaining 10 percent is scattered in the islands of Cebu, Samar, Mindoro, Negros, Polillo, Batan, and Catanduanes. The bulk of Philippine coal is sub-bituminous in rank. Some bituminous coal with coking properties has been reported in Malangas, Zamboanga del Sur in western Mindanao, and in Catanduanes, but the exact tonnages have not been accurately established. It is believed, however, to be at most 5 million tons. A little semi-anthracite coal exists in Malangas with the remaining unmined reserves estimated at a little more than one million tons. Table 1 shows the quality ranges of Philippine coal deposits.. Figure 1 shows the distribution of known Philippine coal resources PHILIPPINE COAL PRODUCTION In 1981, total coal production was 330,720 mt. Though modest by world standards, this was the highest production figure in Philippine coal mining history. This came from 25 mines, mainly small scale underground mines of capacities varying from 10 to 100 tons per day (tpd). The actual production capability was about 800,000 mt in 1981, but the producers had to scale down production to the level of local demand. Even then, some 50,000 tons of coal remained unused by year-end. The 1981 production came from the following areas: Cebu 224,751 mt (68%) Zamboanga del Sur 57,095 mt (17%) Semirara 13,222 mt (4%) Polillo 17,132 mt (5%) Cebu has always been the main source of Philippine coal production. Coal mining has been carried out in Cebu for the last 50 years, although it has been characterized by a very crude mining technology. Due to the limited size of coal deposits and complicated geology, however, Cebu's share of the total national production is expected to go down to only 10 percent by 1985. Except for Semirara's open-pit production, the balance of Philippine coal production comes from underground mines. These underground mines generally use room-and-pillar methods, except for those at Zamboanga del Sur and Polillo which use modified longwall methods patterned after those used in Taiwan. Due to the much higher mining recovery, most underground mines are now planning on switching to longwall. At Semirara, an open pit mine is now being developed for a one million ton per year capacity by 1984, and will then be the largest Philippine coal mine. While present earthmoving work is done with bulldozers, loaders, and trucks, the main coal extraction equipment will be bucket wheel excavators imported from Austria. PRESENT COAL UTILIZATION Existing coal production is sold mainly to coal- fired cement plants and power plants. The balance is sold to a sugar central, a coconut oil mill, a food processing plant, and two plants producing carbide and ferro-silicon alloys.

Jan 1, 1982

By G. T. Smith, R. C. Moyer

Cadmium, along with other impurities such as lead, gallium, germanium and indium, is characteristically found associated with zinc ores, the average ratio of zinc to cadmium being about 200 to 1. The increasing demand for cadmium has led most zinc producers to develop a means for its recovery. The separation and recovery of this byproduct constitutes an important development in the metallurgical field. Zinc sulphide concentrates, principally from domestic sources, are processed at Donora Zinc Works and they assay approximately 60 pct zinc, 30 pct sulphur, 0.37 pct cadmium, and 0.8 pct lead. Concentrates are roasted to convert zinc sulphide to zinc oxide. Sulphur evolved as sulphur dioxide is used to manufacture 60º Baume sulphuric acid by the lead chamber process. The roasted calcine is sintered to remove the remaining sulphur and volatile impurities. Fume from the sintering machines is collected by Cottrell pre-cipitators and sent to the Cadmium Department for cadmium removal. The sintered product, a crude zinc oxide, is then mixed with coke and salt and charged into horizontal retorts for reduction to zinc metal. Furnace residues are then passed through a Waelz kiln which recovers practically all of the remaining zinc as an oxide. This oxide is collected by Cottrell precipi-tators and returned to the sintering plant for further processing. The following discussion covers operating procedure, and equipment used in the Cadmium Department for the manufacture of cadmium and its byproducts. (See attached Flow Sheet, Fig 1.) The production of cadmium may be divided into several steps, each of which will be discussed separately. These steps are as follows: 1. Raw Materials—Sinter Plant Cottrell dust, acid sludge and sulphuric acid. 2. Sulphating—Separation of lead. 3. Purification—Separation of impurities other than zinc. 4. Precipitation—Separation of cadmium from zinc. 5. Briquetting—Preparation of sponge for charging to furnace. 6. Smelting—Distillation of cadmium metal. 7. Remelting—Casting into commercial shapes. 8. Recovery of Rare Metals—Separation of germanium, gallium and indium. Raw Materials The raw material, or Sinter Plant Cottrell dust, from which the cadmium is manufactured, is recovered by Cottrell units collecting fume from two Dwight-Lloyd sintering machines. An average analysis of this dust is 36 pct zinc, 1.5 pct sulphur, 17 pct lead, and 5.5 pct cadmium, with associated elements in smaller amounts. A lesser tonnage of material removed from the sintering machine fans, and called fan cleanings, is also treated for cadmium. It is lower grade material and analyzes approximately 41 pct zinc, 1.2 pct sulphur, 14 pct lead, and 4 pct cadmium. Cottrell dust and fan cleanings are delivered to the Cadmium Department by monorail crane in bell-bottomed dump buckets. Acid sludge and 60" Bauine sulphuric acid are received from the Acid Department. The acid sludge is a mixture of lead sulphate, sulphuric acid and zinc sulphate, and is recovered mainly from the floors of the acid chambers or storage tanks. The acid sludge is delivered to the Cadmium Plant in a lead lined bucket. The 60º Baume sulphuric acid is delivered through a lead pipe to a lead lined storage tank. Sulphating Four well ventilated lead lined sulphating tanks, 8 1/2 ft in diam by 12 ft deep, are used. These are steel tanks lined with 20 lb lead on the bottom and 16 lb lead on the ides, equipped with Hastelloy side agitators. 15 hp motors drive 24 in. propellers at 450 rpm. There are water connections to stuffing boxes to keep sludge from entering the bearings. The tanks are covered with removable wooden lids and are connected to marine plywood

Jan 1, 1950

By R. A. Graham, R. W. Rohde, J. R. Holland

In a shock wave compression study of a martensitic Fe-30 pct Ni alloy, Graham, Anderson, and Holland' found a region of unusual compressibility extending from a few kilobars up to about 20 kbars. This region was characterized by a continuously decreasing shock wave velocity with increasing stress. In this note, we report the results of a study initiated to determine the source of this unusual compressibility. In earlier shock-loading experiments on martensitic Fe-30 pct Ni, Loree et a1.' determined that a phase change occurred at about 80 kbars. Subsequently, Bowden and elly found that samples of a similar material shock-loaded at about 100 kbars experienced a martensite-to-austenite transition. Their crystal-lographic analysis showed the transition was a direct reversal of the established martensite system to the austenite phase. The shock loading in the present experiments was accomplished by precisely controlled plane impact between two discs of the sample material. This configuration created a state of uniaxial strain in the two the front of a projectile which was accelerated to various velocities. Planarity between the impacting discs was controlled to 5 x 10-4 rad, and impact velocities were measured to 0.5 pct. From a knowledge of the Hugoniot relationships of the material and the impact velocity, the shock-wave stress can be calculated. Samples were shocked at 18, 50, 70, and 100 kbars. The specimen discs shocked at 18 and 50 kbars were instrumented with quartz gages to observe the stress time profile. A more detailed description of the experiment has been given previously.4 The shock-loaded specimens were recovered intact by decelerating them in a catcher filled with soft wood. Discs of Fe-30 pct Ni nominally 12.7 mm thick and 64 mm in diam were cut from bar stock. Chemical analysis of the material provided the following composition in weight percents: 29.5 Ni, 0.50 Mn, 0.21 Si, and 0.10 C, with traces of Cr, Cu, Mo, Al, and Co. The discs were austenitized at 650° C for 2 hr at a pressure of less than l0-' torr, and furnace-cooled. Martensite was then produced by quenching the discs at -196" and holding 168 hr. The initial martensitic structure formed is shown in Fig. l(a). Typical microstructures of samples shock-loaded at 18 and 100 kbars are shown in Figs. l(b) and l(c). The banded structure with the austenite regions running parallel to the shock propagation direction was characteristic of samples shock-loaded at all stresses. No such banding was found in samples that were not shock-loaded. Comparison of Figs. l(b) and l(c) shows that, although under the optical microscope the two microstructures are quite similar, the martensite plates of the specimen shocked at 100 kbars etched in a distinctly different manner. This unique etching behavior of martensite in samples shock-loaded above the 80 kbar transition point has also been observed by Leslie el al.' These investigators determined from X-ray and electron microscope studies that fcc martensite, similar in appearance to normal bcc martensite, had been formed under shock loading. A quantitative determination of the amount of austenite present after shock loading was made by X-ray techniques. Both the methods of Lindren' and Miller' were utilized. The results are shown in Table I. The error limits are those experimentally observed from two independent analyses of each sample and represent the precision of the experiment. The absolute error, which should be similar for each sample, is believed to be about 10 pct. It is seen that as the shock stress increases the amount of austenite present also increases. On the basis of the X-ray and microscopic observations, we conclude that shock loading below the 80 kbar ersal will initiate a martensitic reversal: the amount of reversal that occurs increases with in-

Jan 1, 1969

By Milan Matula

One of the main characteristics of the development of rock mechanics in some countries is a close cooperation between experts in rock mechanics and workers in related fields, including soil mechanics and engineering geology. The purpose of this chapter is to outline the contribution that engineering geology can make to rock mechanics and to present a few examples of engineering geology studies that have been used in solving some practical rock mechanics problems. Engineering geology investigations dealing with the influence of geological factors on the physical properties of rock materials and rock masses fall into three main categories : 1) Systematic study and correlation of the physical properties of the main rock types with the petrogenetic evolution that caused the differences in the properties of these various rock types. 2) Study of the heterogeneity and anisotropy of both rock materials and rock masses. 3) Delimitation of rock masses which are approximately uniform in physical properties (quasihomogeneous units). Delimiting of the quasihomogeneous rock masses is the main contribution that the engineering geologist can make to rock mechanics. This delimiting is based on the evaluation of many complex geologic factors, not on test results alone, and therefore is most effectively done by trained engineering geologists. The foregoing types of studies are being used in Czechoslovakia for several purposes, including : 1) the compilation of regional engineering petrologic data-that is, the systematic definition of the main rock types of the country in terms of their representative physical characteristics;

Jan 1, 1970

By Thomas A. Edison, John Birkinbine

The Transactions already contain many valuable papers on the subject of ore-concentration, but with reference more to the treatment of other ores than those of iron. In this country much money, labor and thought have been devoted to the enrichment of iron-ores by roasting to drive off sulphur and carbonic acid, eliminate water, or make the ore more friable, and by washing and screening to remove the clay and sand from earthy ores. In concentrating magnetites and hematites more has been done than is generally believed; but, unfortunately, the results up to the present time have not been encouraging. On the contrary, so many attempts have proved unsatisfactory that any system of concentration is now unjustly looked upon with doubt, and the problem presented to individual mines must therefore be approached with caution. For many years the magnetites of the Adirondack region of New York State have been roasted, reduced to proper size by means of gang-stamps, and jigged on screens in water. Latterly plunger-jigs and rotary-jigs have been introduced, and in some places crushers and rolls have taken the place of stamps. In one instance in that region a plant for reducing the ore by crushers and rolls and separating it by magnetism was put up to treat a titaniferous ore; but, the titanium occurring as ilmenite, the result was unsatisfactory, and the plant is now being reconstructed at another mine, where apatite and silica are to be separated from the magnetite. A large concentrating works was erected at Negaunee, Michigan, in the Marquette region, Lake Superior, to enrich the leaner specular ores. This consisted of crushers, Cornish rolls and rotary-jigs. The results ohtained weye not satisfactory, and it has been abandoned. Another plan to treat the lean magnetites from a large dump-pile at Republic, Michigan, by means of pulverizers and water-jigs also

Jan 1, 1889

By G. S. Derrickson, R. A. Golobic

Any type of agitation within a confined vessel is primarily concerned with two parameters: a level of agitation describing the homogeneity of the constituents (whether it be suspension or mixing), and the energy efficiency with which this level of agitation is accomplished. The following is an attempt to present a solution to the problem of adequately defining and optimizing these properties. A discussion is included of the application of good design practices to the determination of a mechanically efficient shape to the blade elements of the propeller. These practices, excluding several appropriate modifications, have been known, but not well understood, in aircraft fluid mechanics for a number of years. Having optimized the direct impartation of energy to the medium being agitated, attention is turned to one of the more perplexing phenomena of multi-phase systems - definition and prediction of agitation levels. The result of recent study and testing is a method of scaling that the authors believe provides a lucid understanding of governing physical parameters within the agitator itself, allowing one to scale up and down with confidence.

Jan 1, 1985

By R. M. Rose, D. P. Ferriss, J. Wulff

Single crystals of tantalum, tungsten, and the binary alloys thereof were grown by electron-beam zone melting and tested in tension between 77° and 373°K. The ductile-to-brittle transition temperature increased sharply with solute concentration, for both tungsten-rich and tantalum-rich alloys; apparently, the maximum transition temperature exists near the 50 pet concentration. Twinning was observed to be a consequence of cleavage-crack propagation. Cleavage occurred on(100)planes, and extensive tearing and "river markings" were present. The onset of brittleness could not be associated with any change in deformation mode, the yield point phenomenon, or the large rise in yield stress with decreasing temperature. Cleavage was observed to initiate at either the specimen surface, or subgrain boundaries. The observation was made that the grain boundaries of Polycrystalline materials are probably even better as nucleation sites for fracture, and are responsible for brittleness at high temperatures and lower solute concentrations than those of the corresponding single crystals. TUNGSTEN and tantalum, the two high-melting neighbors in the third transition period of the periodic table, present striking contrasts. Although both are bee, tungsten has far higher elastic moduli, and the highest ductile-to-brittle transition (DBT) of all the pure metals.' Tantalum, however, is ductile at liquid helium temperatures. Large strain aging and yield point phenomena are observed in tantalum,2,3 but only to a lesser extent in tungsten.4 Tungsten work-hardens at a high rate,5 whereas this effect is negligible in tantalum.' Since the mutual solid solubility of these two metals is complete,7 and no ordering has yet been reported in the binary system, the possibility of depressing tungsten's DBT by tantalum additions was considered. Also, tungsten additions to tantalum could produce hard, high-melting alloys which might be ductile at room temperature. Such alloys offered excellent bases for complex alloy development, particularly with regard to the effect of rhenium on Group VI metals.8"10 In addition, there was the opportunity to examine flow and fracture modes in the vicinity of the DBT, with particular emphasis on the correlation between brittleness and fundamental deformation mechanisms. Myers11 has reported that recrystallized alloys with up to 10 pet W in tantalum are ductile at room temperature, but alloys with 20 pct W could not be swaged at temperatures as high as 500°C. The whole spectrum of Ta-W alloys has been surveyed by Braun, Sedlatschek, and Kiefferl2 using sintered powder compacts. In addition to some physical properties they reported a maximum hardness at about 50 at. pet W, dropping to much lower hardness levels for the pure components. They were able to cold work tantalum-base alloys with as much as 30 pet W and to warm work tungsten-base alloys with up to 20 pet Ta by procedures similar to those used for pure tungsten. EXPERIMENTAL In order to study deformation modes and to keep the impurity concentrations at a minimum, electron-beam zone melting was used to prepare single crystals of high purity. The electron-beam zone melting apparatus is similar to that described by Calverley, Davis, and ever" and incorporates a grid control rectifier to maintain control of emission current. Pure metals were refined by making three zone passes at 4 mm per min up the rod. Alloys were prepared by melting together wire of one constituent on a previously melted rod of the major constituent. Subsequently, two zone passes were made in opposite directions to level the composition after the manner suggested by pfann.14 Purification of the starting materials was accomplished by evaporation of the several impurities, and the degree to which this was accomplished is indicated in the chemical analyses of Table I. The uniformity of composition along a zone levelled rod was within the i 1 pet accuracy of the fluorescent X-ray technique used to determine composition. Crystallographic orientation of the

Jan 1, 1962

By J. L. Moriarty, Irving Johnson, H. M. Feder

The crystallization of ternary alloys has been studied as a coprecipitation phenomenon by measuring the substitutional carrying of trace metals with CeCd11 precipitating from liquid cadmium. The Doerner-Hoskins logarithmic distribution law has been found to apply in all cases; the coprecipitation coefficients obtained were: 1.48 (La), 1.06 (Th), 0.63 (Pr), 0.24 (Gd), 0.17 (Sm), 0.13 (U), 0.10 (Er), 0.09 (Sr). Li, Na, K, Ba, Y, Sc, and Zr were not measurably carried. It has been observed that coprecipitation was most extensive for those tracers which form with cadmium an intermetallic compmdnd isostructural with CeCd11 or closely related thereto. For these tracers an inverse relation between Solubility in cadmium and coprecipitation coefficient was noted. THE partition of impurities between the liquid and solid phases of a metal or a congruently melting intermetallic compound has been extensively studied by the methods of zone melting.' However, when the composition of a liquid alloy and of the solid phase crystallizing from it differ grossly, partition of an impurity cannot be investigated in this manner. Partition of the impurity under equilibrium conditions may be studied by investigation of the appropriate phase diagram and partition under nonequi-librium conditions may be studied by observation of coring in the solidified alloys.2 The nonequilibrium case is of special interest in metallurgical practice because many complex alloys are cooled too rapidly to permit the uniform diffusion of impurities throughout the crystallizing phase(s). With this in mind, the present study was undertaken to obtain quantitative data on the phenomenon of coprecipitation via substitutional solid solution in certain metallic systems. It will be noticed that rather than adopting metallurgical ter- minology we have chosen to refer to the partition of impurities during alloy crystallization as coprecipitation.3 In the terminology of coprecipitation the impurity is referred to as the tracer and the precipitating phase as the carrier. From aqueous solution, coprecipitation may occur as a result of adsorption on the surface of the carrier, by occlusion of the liquid within the crystals, or by solid solution of the tracer in the carrier. By slow cooling of liquid metallic solutions it is relatively easy to form large, regular crystals of the carrier; the effects of adsorption and occlusion may be minimized and the influence of substitutional solid-solution formation may be made to predominate. Previous studies of the crystallization of some intermetallic compounds4 and of copper, silver, and gold5 have shown that the coprecipitation or partition behavior of trace metals is entirely analogous to that observed in aqueous systems when ionic substitution occurs, e.g., coprecipitation of Ra++ with BaSo4. The precipitation of CeCd11 from liquid cadmium was chosen for study. This choice was influenced by the following consideration. If the relative atomic sizes of the tracer atom and the atom for which it substitutes determine the tendency to coprecipi-tate, then a lattice having a substitutional site of well-defined size would be desirable. In CeCd116 (structure type cubic BaHg117) the cerium atom is completely surrounded by a cage of twelve nearly equidistant cadmium atoms. Thus, atoms much larger or much smaller than cerium should be poorly accommodated in this cage. The choice of a lanthanide central atom allowed the testing of the size hypothesis with a number of lanthanide tracers which differed in size but not in valence or electro-negativity. EXPERIMENTAL The general technique of this investigation was to prepare a slightly undersaturated solution of carrier in liquid cadmium to which a tracer was added. The concentration of tracer was always so low that saturation over the entire temperature range investigated was never exceeded. The solution was cooled in a stepwise fashion. After each step a por-

Jan 1, 1964

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By R. D. Daniels, T. W. Wood

The tensile properties of columbium and Cb-H alloys containing up to 455 ppm H were studied as a function of temperature and strain rate. Hydrogen, introduced into columbium at elevated temperatures, using a thermal -equilibrium technique, embrittled columbium most severely at about —77°C. This elnbrittle ment occurred even at hydrogen concentrations of an order of 20 ppm. At higher temperatures, the hydrogen tolerance of columbium increased in relation to the increased solubility of hydrogen in tile metal. Below this temperature hydrogen tolerance, as determined by ductility and fracture stress, increased slightly. Strain rate had little effect on the tensile results for cross-head speeds over the range 0.002 to 2.0 in. per min. Strain aging during the tensile test appears to explain the ductility mininmum at —77°C. The apparent increase in hydrogen tolerance at lower temperatures is attributed to the low mobility of hyhogen. Experiments were performed in which samples were prestrained in tension at room temperature and tested to failure at —196°C. Results suggest that hydrogetz segregation to preformed crack nuclei can cause subsequent embrittlement even at temperatures where hydrogen mobility is too low to cause embrittlement in a normal tensile test. COLUMBIUM is an example of the class of bcc metals with ductile-brittle transition temperatures sensitive to the presence of interstitial atom contaminants. Hydrogen is one of these embrittling contaminants. The embrittling effect of hydrogen is less potent, perhaps, in columbium than in some of the other bcc refractory metals, but it is still a problem of both theoretical and practical interest. Unlike hydrogen in iron and steels, hydrogen in columbium is exothermically rather than endo-thermically occluded. The embrittlement process in exothermic systems has not been studied as extensively as that in endothermic systems, especially at hydrogen concentrations below the limit of solubility. The purpose of this investigation was to evaluate the embrittlement process in initially pure columbium as a function of hydrogen content, temperature, and strain rate. The Cb-H phase diagram, according to Albrecht et al.,1 is shown in Fig. 1. Columbium reacts exothermically with hydrogen producing a solid solution at concentrations of less than about 250 ppm (parts per million by weight) H at room temperature. At concentrations above the highly temperature-dependent solvus a second phase is formed. Like many similar hydrogen-metal systems,2 his system exhibits a miscibility gap with respect to hydrogen solution. Albrecht found the critical temperature of the miscibility gap to be about 140°C, the critical concentration to be 0.23 atom fraction hydrogen, and the critical pressure to be 0.01 mm Hg. Above 140°C there is a solid solution of increasing lattice constant extending across the phase diagram. Hydrogen concentrations of particular interest in this investigation were those below the limit of solubility in columbium. At hydrogen concentrations above the limit of solubility, columbium will contain the hydrogen-rich second phase and will be brittle under most testing conditions because the hydride generally precipitates as platelets with coincident matrix lattice strains.1'3 At hydrogen concentrations below the limit of solubility, the tensile behavior of columbium is expected to be more sensitive to the interrelationships between hydrogen concentration and mobility and the testing variables such as temperature and strain rate. Literature references to the hydrogen embrittlement of metals, especially ferrous alloys and titanium alloys, are too voluminous to mention. It is only recently, however, that detailed studies of the hydrogen embrittlement of columbium have been undertaken. Wilcox et a1.4 studied the strain rate and temperature dependences of the low-temperature deformation behavior of fine-grained are-melted columbium (1 ppm H) and the effect of hydrogen content (1,9, and 30 ppm H) on the mechanical behavior of columbium at a series of temperatures for a single strain rate. A strain-aging peak was ob-served at about -50°C which was attributed to the presence of hydrogen in the metal. Eustice and carlson5 studied the effect of hydrogen on the ductility of V-Cb alloys at a series of temperatures over the range -196° to 25°C. Pure columbium was embrittled by 20 ppm H which produced a ductility transition at approximately -70°C. Ingram et al.6 studied the effect of oxygen and hydrogen on the tensile properties of columbium and tantalum. A minimum in the notched-to-unnotched tensile ratio of hydrogenated columbium was obtained at about -75°C, but because of the relatively large hydrogen content employed (200 and 390 ppm) the ductility

Jan 1, 1965

By Henry Leidheiser, Melvin C. Jr. Hobson

The rate of formation of the intermetallic compound, indium antimonide, at the interface between iudium and antimony at 100°C is greatly increased when a composite electrode of indium electrode -posited on antimony is made the cathode in an electrolytic cell. The amount of indium antimonide formed during electrolytic treatment at constant potential appeared to he proportional to the square root of time, but the scatter of the data, particularly at long times, makes it impossible to state this conclzlsi1:ely. The rate constant for the electrochemical synthesis was estimated to he 1.5 x 10-12 sq cm per sec. A similar- set of experiments was conducted in the absence of an applied potential but under otherwise similar conditions. The rate constant lor the thermal synthesis was less than 2 x 10-14 sq cm per, sec, at least two orders of magnitude less than obtained during electrolytic treatment. In a series of electrochemical studies it was observed that intermetallic compounds formed on the surface of polarized electrodes.1'2 The possibility of using this technique for the electrochemical preparation of intermetallic compounds was investigated and subsequently applied to the synthesis of the semiconducting III-V compounds. Gallium antimonide, indium arsenide. indium antimonide, and indium bismuthide were successfully formed by electrodepositing the Group III element from a boiling acid solution onto an electrode made of the Group V element. The following kinetic studies were undertaken on indium antimonide to obtain quantitative information on the rate of formation of this representative III-V compound under a potential gradient. EXPERIMENTAL The electrolytic cell for these experiments was a modified, three-neck, round-bottom, 500-ml distillation flask. Sealed into the side of the flask was a Luggin probe which monitored the surface of the working electrode and extended out of the flask to a small reservoir containing a saturated calomel electrode. The counter electrode was platinum. The three electrodes were connected to a Wenking po-tentiostat which maintained a preselected constant potential near the surface of the working electrode with reference to a saturated calomel electrode. All potentials noted in this paper are with reference to a saturated calomel electrode at 45° ± 5°C. The potential and the current were both monitored using Sargent Model MR recorders. The antimony electrodes were cast in graphite molds to form spheres about 15 mm in diameter with a shank 6 mm in diameter and 10 mm long. A heavy copper wire (12B & S gage) was soldered to this shank. Collodion was applied for protection to the shank and the connecting part of the copper lead. A snug-fitting O-ring was slipped over the shank and the electrode was then fitted into a teflon holder such that only the spherical portion was exposed. The electrode surfaces were cleaned and chemically polished prior to assembly and introduction into the electrolyte by etching in a modified CP-4 solution (50 parts glacial acetic acid, 10 parts concentrated nitric acid, 2 parts 48 pct hydrofluoric acid). The electrolyte was 10-2 M In+3 in 1 MH2So4 and its temperature was held constant by refluxing. The reflux condenser was open to the atmosphere and no temperature correction was made for changes in barometric pressure. The indium concentration in the electrolyte was checked from time to time by the analytical method outlined below for the determination of the amount of indium antimonide formed electrochemically. A schematic of the recorded potential is shown in Fig. 1. At point A the antimony electrode was introduced into the cell and the open-circuit potential recorded. At point B the potentiostat, preset at the desired potential, was switched on. It was switched off at point C and the potential fell to the open-circuit value of the electrodeposited indium. The

Jan 1, 1965

By R. A. Conkling

DORSET HAGER, Tulsa, Okla. Recently we have, been doing a little work along the same lines Mr. Conkling has outlined iii his paper. I am not prepared to say that Mr. Conkling is not correct but our results do not agree with his. I think it is a question of difference in correlation and interpretation of the well records. Our cross-section of the Cushing pool does not agree with that of Mr. Conkling and we find instead of the beds thickening in the syncline, there is a tendency to thicken on top of the anticline. We took the north dome of the Cushing field, and are now trying to get all the records. It will probably be another month before we have all the data complete but our results at present do o not agree with those of Mr. Conkling at all.

Jan 4, 1917

By W. O. Philbrook, H. E. Burner, F. S. Manning

The equation of continuity for the hydrogen reduction of hematite in a fixed bed of closely-sized particles is solved assuming a flat velocity profile, negligible temperature gradients, md negligible axial diffusion. A kinetic expression from the literature is used which assumes the reduction process is controlled at the oxide-metal interface. The integral fractional conversion is computed, and the importance of particle diameter, flow mte, temperature, bulk axial diffusion, and inter- and intra-particle mass trarnsfer is predicted. Comparison with experimental data suggests one or more additional undefined variable(s) is significant. Equipment modifications are suggested for fidture experimentcll work. WITH the increasing desire to "design" the ore feed of a blast furnace, it has become necessary to define more quantitatively the process variables and to evaluate the extent of their control upon the reduction process. The bulk of the work reported in the literature has centered about the reduction of single particles; however, the blast furnace process more closely resembles reduction of a fixed bed than that of single particles. To simplify this analysis, the isothermal reduction by hydrogen of a natural hematite in a fixed bed of closely-sized particles is examined. With appropriate modifications in the kinetic and flow rate expressions, the approach employed should be extensible to mixtures of carbon monoxide, hydrogen, and inert nitrogen, and to adi-abatic conditions, thus approaching the blast furnace process more closely. The fixed bed variables which are investigated in this study are particle diameter, flow rate, temperature, and bulk axial diffusion, as well as inter-and intra-particle mass transfer. Of particular interest is the effect of particle size upon fractional conversion for a bed operating under constant pressure drop. The constant pressure drop concept bears a close resemblance to the blast furnace process, where regions of larger particles may provide a greater permeability to divert most of the reducing gas flow from the regions of smaller ore particles. Under such conditions one would expect qualitatively that, for sufficiently small particle sizes where the flow rate is small and the total surface area is large, the reduction rate would be limited by the gas flow rate. Initially the gas entering the bed reacts very rapidly and the composition approaches the equilibrium conversion value a short distance from the reactor inlet. This concentration "wave-front" then moves up the bed as the flow of reducing gas is continued, leaving in its wake an ever increasing layer of reduced particles. Providing that the reducing gas leaves the bed at equilibrium concentrations, conversion is expected to increase with an increase in flow rate, and hence with an increase in particle diemater. Conversely, for sufficiently large particles the flow rate will be high but the surface area available for reaction will limit the reduction rate. Since the total surface area decreases with an increase in particle size, conversion, in this case, is expected to decrease as the particle diameter is increased. It is clear then that between these two extremes an optimum particle diameter must exist. THEORETICAL DEVELOPMENT Above the temperature where wiistite is stable (about 560°C) the reduction of hematite proceeds through the series Fe2O3/Fe3O4/FeO/Fe. On the basis of microstructural studies and earlier work, Edström1 has postulated a mechanism for the reduction of an ideal hematite lattice: 1) Iron phase formation at the boundary between wiistite, iron, and gas (for sufficiently porous iron). 2) Diffusion of iron across a wustite layer. 3) Phase boundary reaction of Fe3O4 to FeO. 4) Diffusion across a dense magnetite layer. 5) Phase-boundary reaction of Fe2O3 to Fe3O4. According to the mechanism postulated, gaseous reaction product has to be removed only at the boundaries between wüstite and iron or gas, the only possible exception being enveloped Fe3O4 specks. On this basis McKewan2,3 has proposed that one may consider the hematite reduction process as a simple two-phase system of oxide/metal. If, for FeO and Fe3O4 layers of negligible thickness, the hypothesis is made that the rate of formation of a

Jan 1, 1963

By Walter Rose, W. A. Bruce

Improved apparatus, methods, and experimental techniques for determining the capillary pressure-saturation relation are described in detail. In this connection a new multi-core procedure has been developed which simplifies the experimental work in the study of relatively homogeneous reservoirs. The basic theory concerning the Leverett capillary pressure function has been extended and has been given some practical application. Some discussion is presented to indicate the relationship of relative permeability to capillary pressure, and to provide a new description of capillary pressure phenomena by introducing the concept of the psi function. INTRODUCTION For the purposes of this paper the capillary character of a porous medium will be defined to express the basic properties of the system, which produce observed results of fluid behavior. These basic properties may be classified in the following manner, according to their relationship to: (a) The geometrical configuration of the interstitial spaces. This involves consideration of the packing of the particles, producing points of grain contact, and variations in pore size distribution. The packing itself is often modified by the secondary processes of mineralization which introduces factors of cementation, and of solution action which causes alteration of pore structure. (b) The physical and chemical nature of the interstitial surfaces. This involves consideration of the presence of interstitial clay coatings, the existence of non-uniform wetting surfaces; or, more generally, a consideration of the tendency towards variable interaction between the interstitial surfaces and the fluid phases saturating the interstitial spaces. (c) The physical and chemical properties of the fluid phases in contact with the interstitial surfaces. This involves consideration of the factors of surface, interfacial and adhesion tensions; contact angles; viscosity; density difference between immiscible fluid phases; and other fluid properties. Fine grained, granular, porous materials such as found in petroleum reser~oir rock possess characteristics which are expressible by (1) permeability, (2) porosity, and (3) the capillary pressure-saturation behavior of immiscible fluids in this medium. These three measurable macroscopic properties depend upon the microscopic properties enumerated above in a manner which defines the capillary character. Systems of capillary tubes or regularly packed spheres may be thought of as ideal and numerous references can be cited in which exact mathematical formulations are developed to show the relationships governing the static distribution and dynamic motion of fluids in their interstitial spaces. The capillary character of non-ideal porous systems such as reservoir rock also is basic in determining the behavior of fluids contained therein; although, in general, the connection is not mathematically derivable but must be approached through indirect experimental measurement. This paper gives consideration to the evaluation of petroleum reservoir rock capillary character. The methods employed may be applied to the solution of problems in other fields, and the conclusions reached should contribute to the basic capillary theory of any porous system containing fluid phases. In this paper, a modification of the core analysis method of capillary pressure is employed and it is intended to show that the capillary character of reservoir rock can be expressed in terms of experimental quantities. A very general method of interpretation correlating the capillary pressure tests with fundamental characteristics such as rock texture, surface areas, permeability, occasionally clay content and cementation is introduced. Eventually an attempt is made for establishing a method of deriving relative permeability to the wetting phase from capillary pressure data. The experimental evaluation of capillary character must be approached in a statistical manner if reservoir properties are to be inferred from data on small cores. This is implied by the heterogeneous character of most petroleum reservoirs, and suggests that considerable intelligence should be applied in core sampling. Finally, this paper supports the view that once the capillary character of a given type of reservoir rock has been established by core analysis, fluid behavior can then be inferred in other similar rock. Although no great progress has been made in establishing what variation can be tolerated without altering the basic fluid behavior properties, evidence will be presented to indicate that certain reservoir formations are sufficiently homogenous with respect to capillary character that the data obtained on one core will be useful in predicting the properties of other cores of similar origin. Tests have shown that cores under consideration can vary widely with respect to porosity and permeability and still be considered similar in capillary character. EXPERIMENTAL METHODS AND TECHNIQUES Various types of displacement cell apparatus for capillary pressure experiments have been described in the literature. Bruce and Welge; Thornton and Marshall; McCullough, Albaugh and Jones3; Hassler and Brunner; Lever-

Jan 1, 1949

By Walter Rose, W. A. Bruce

Improved apparatus, methods, and experimental techniques for determining the capillary pressure-saturation relation are described in detail. In this connection a new multi-core procedure has been developed which simplifies the experimental work in the study of relatively homogeneous reservoirs. The basic theory concerning the Leverett capillary pressure function has been extended and has been given some practical application. Some discussion is presented to indicate the relationship of relative permeability to capillary pressure, and to provide a new description of capillary pressure phenomena by introducing the concept of the psi function. INTRODUCTION For the purposes of this paper the capillary character of a porous medium will be defined to express the basic properties of the system, which produce observed results of fluid behavior. These basic properties may be classified in the following manner, according to their relationship to: (a) The geometrical configuration of the interstitial spaces. This involves consideration of the packing of the particles, producing points of grain contact, and variations in pore size distribution. The packing itself is often modified by the secondary processes of mineralization which introduces factors of cementation, and of solution action which causes alteration of pore structure. (b) The physical and chemical nature of the interstitial surfaces. This involves consideration of the presence of interstitial clay coatings, the existence of non-uniform wetting surfaces; or, more generally, a consideration of the tendency towards variable interaction between the interstitial surfaces and the fluid phases saturating the interstitial spaces. (c) The physical and chemical properties of the fluid phases in contact with the interstitial surfaces. This involves consideration of the factors of surface, interfacial and adhesion tensions; contact angles; viscosity; density difference between immiscible fluid phases; and other fluid properties. Fine grained, granular, porous materials such as found in petroleum reser~oir rock possess characteristics which are expressible by (1) permeability, (2) porosity, and (3) the capillary pressure-saturation behavior of immiscible fluids in this medium. These three measurable macroscopic properties depend upon the microscopic properties enumerated above in a manner which defines the capillary character. Systems of capillary tubes or regularly packed spheres may be thought of as ideal and numerous references can be cited in which exact mathematical formulations are developed to show the relationships governing the static distribution and dynamic motion of fluids in their interstitial spaces. The capillary character of non-ideal porous systems such as reservoir rock also is basic in determining the behavior of fluids contained therein; although, in general, the connection is not mathematically derivable but must be approached through indirect experimental measurement. This paper gives consideration to the evaluation of petroleum reservoir rock capillary character. The methods employed may be applied to the solution of problems in other fields, and the conclusions reached should contribute to the basic capillary theory of any porous system containing fluid phases. In this paper, a modification of the core analysis method of capillary pressure is employed and it is intended to show that the capillary character of reservoir rock can be expressed in terms of experimental quantities. A very general method of interpretation correlating the capillary pressure tests with fundamental characteristics such as rock texture, surface areas, permeability, occasionally clay content and cementation is introduced. Eventually an attempt is made for establishing a method of deriving relative permeability to the wetting phase from capillary pressure data. The experimental evaluation of capillary character must be approached in a statistical manner if reservoir properties are to be inferred from data on small cores. This is implied by the heterogeneous character of most petroleum reservoirs, and suggests that considerable intelligence should be applied in core sampling. Finally, this paper supports the view that once the capillary character of a given type of reservoir rock has been established by core analysis, fluid behavior can then be inferred in other similar rock. Although no great progress has been made in establishing what variation can be tolerated without altering the basic fluid behavior properties, evidence will be presented to indicate that certain reservoir formations are sufficiently homogenous with respect to capillary character that the data obtained on one core will be useful in predicting the properties of other cores of similar origin. Tests have shown that cores under consideration can vary widely with respect to porosity and permeability and still be considered similar in capillary character. EXPERIMENTAL METHODS AND TECHNIQUES Various types of displacement cell apparatus for capillary pressure experiments have been described in the literature. Bruce and Welge; Thornton and Marshall; McCullough, Albaugh and Jones3; Hassler and Brunner; Lever-

Jan 1, 1949

Earth Sciences: The standard of living of the world's people depends upon human initiative, investigation, and know-how in exploiting the earth's resources. The Earth Sciences-geology, mineralogy, geophysics and geochemistry, meteorology, geography-are basic sciences dealing with those problems concerning the origin, constitution, and utilization of the earth's materials. The development of these fields in one department provides the greatest opportunity for direct contact and stimulus for scientists and teachers working in related fields. In the Earth Sciences, geology and mineralogy are obviously closely related. As rocks are the materials of which the earth is made, so in turn minerals are the constituents of the rocks. Conversely, a study of earth structures and the interplay of physical and chemical forces in the earth is necessary in order to understand the origin and source of minerals. Building on the basic core of knowledge of earth processes, earth structures, and earth history, the geologist will continue to push out the frontiers of stratigraphy, structural geology, pale-biology and petrology with growing insight into principles that control surface and subsurface rock conditions. As the field of geology has advanced, several lines of specialization have developed. The economic geologist

Jan 1, 1950

By W. S. Ayres

[Secretary's Note.—At the Spokane meeting of the Institute, in discussion of President Brunton's address on "Modern Progress in Mining and Metallurgy in the Western United States," and at the request of members present, Mr. Ayres gave an oral account of his new separator, which is here published as an independent paper, partly because of its inherent importance and partly because it describes an improvement which did not originate in the Western United States, and therefore does not fall, strictly speaking, under the title of President Urunton's address.—R. W. R.] A brief history of the growth of the anthracite-coal preparation will give a better view-point from which to judge the present problem of separating slate from coal. At the beginning of the commercial value of anthracite, 70 years ago, only the pure portions, or " splits," of the veins were mined and shipped to market, and without any preparation or screening other than the selection, while loading, of the glassy lumps, and the rejection of the fine material and the slate that had strayed accidentally into the coal. The next step was the crushing or breaking of the coal (hence the name "breaker" as applied to the preparation-building), and the sizing of it by means of bars or revolving screens. This stage of its development marked the advent of the " breaker-boy " as a slate-picker, with his ever-increasing capriciousness. As the richer veins or a splits " became exhausted and the market demanded a still greater output, the less-pure " splits " and the thinner veins were utilized to produce the coal. Carrying as they do a far greater percentage of impurities, particularly when removing the pillars, it became necessary to build new and better equipped preparation-plants. Finally, we are now at the highest stage of complicatioii yet known to the art of coal-preparation. We are dealing with varying specific gravities, frictional difference, hardness, structure, and form in the pieces of coal and slate coming from many different veins, and

Jan 1, 1910