By Horace Pops

Martensitic transformation has been studied during cooling and heating in ß-phase Cu-Zn alloys to which small additions have been made of Ni, Ag, Au, Cd, Ga, In, Si, Ge, Sn, and Sb. The start and finish of the martensitic reaction and the variation of transformation temperature with third-element content were determined by electrical-resistivity measurements from alloys which had either constant zinc contents or constant values of electron concentration. All of the third elements, except nickel, lowered the transformation temperature if the results were plotted along the lines of constant zinc contents in each ternary system. A significant difference in the rate of lowering of the transformation temperature per atomic percent of the third element was observed for elements which had the same nominal valence. No systematic variation of transformation temperature with the valence of the third element was observed. It is suggested that the observed increase in transformation temperature for nickel-bearing alloys is due to the transfer of electrons from the conduction band of the alloy to virtual bound states. However, electron concentration is not the most important factor controlling the instability of the 0 phase. The transformation temperatures of the ternary alloys can be predicted from the following approxilnate expression: Ms (°K) = +3280 - 80 Zn + 8 Ni - 30 Ag - 12 Au - 140 Cd -90 Ga- 145 In - 80 Ge -175 Sn - 120 Si - 150 Sb MOST binary ß -phase alloys based upon the noble metals copper, silver, and gold are unstable at low temperatures and transform spontaneously by a martensitic reaction. This transformation has been studied recently in the ordered bcc ß'-phase Cu-Zn binary al1oys1,2 where the transformation temperature is below the room temperature and decreases with an increase in zinc content. It has been reported that the transformation temperatures can be raised above room temperature by small additions of a third element such as silicon3,5 or gallium,4,5 but no quantitative study has been made. The transformation temperature of different binary alloys can be altered by third-element additions. For example, it was shown that nickel and copper may have a large effect on the Ms temperature of CU-Al6 and Au-cd7 alloys. The present investigation was made to determine systematically the influence of various third elements on the martensite-transformation temperature of Cu-Zn ß-phase alloys. Since these alloys have an electronic origin,' alloy compositions were chosen so that the transformation temperatures could be determined at constant zinc contents or at constant values of electron concentration. I) EXPERIMENTAL PROCEDURE Ten ternary alloy systems were obtained by adding nickel, the noble metals silver and gold, and some B-subgroup elements to a Cu-Zn matrix. These are arranged according to their rows and columns in the Period Table as follows: Each ternary alloy was prepared by melting and casting weighed quantities of high-purity metals (99.99+ pct) in sealed quartz tubes under a partial pressure of helium to make a 4-g ingot. The molten alloys were shaken vigorously and then quenched in water. Since the weight loss was negligible, the compositions of the ingots after casting and annealing were assumed to be the same as the nominal compositions. The ingots were homogenized after casting in helium-filled Vycor tubes for 24 hr at temperatures between 750" and 810 C and quenched into brine. Metallographic examination revealed that all alloys were homogeneous, poly crystalline ß-phase alloys, and that the grain size was in the range 1 to 5 mm. Electrical-resistivity measurements were made to determine transformation temperatures of the ternary alloys during continuous cooling or heating. Transformation temperatures of the ternary alloys can be determined by electrical-resistivity measurements since the resistance of the martensitic phase is much higher than that of the 0' phase. The technique has been described previously in connection with a study of Au-Zn alloys.9 The reproducibility of transformation temperature was approximately ±6°C. II)RESULTS A hysteresis was always observed in electrical-resistivity curves and was usually less than about 12°C.

Jan 1, 1967

By W. L. Phillips

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of' the easy-glide region increased, and the rate of' work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs' studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt's atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.' EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.

Jan 1, 1968

By J. J. Stokes

Literature on the electrolysis of aluminum from cryolite melts and on the structure of these melts is surveyed critically. Data on density, freezing point, and other properties are reviewed. Theories of the electrolysis are examined in the light of these data. Two theories are presented which account equally well for the observations. ALTHOUGH the production of aluminum is a large-scale industrial process, consuming approximately 3 pet of all of the electric current generated in this country, the mechanism of the Hall Process remains a 70-year-old mystery. It is a remarkable fact that the aluminum industry, which was established largely through research and owes much of its growth to research, still employs as its basic process the one developed by Charles Martin Hall while he was still a young man working in a woodshed. There are, of course, modifications in detail and a tremendous expansion of the size of the units used, but basically the process employs carbon anodes and a carbon-lined iron vessel as a cathode for the electrolysis of alumina dissolved in molten salt. Of the almost infinite variety of salts available, the relatively minor Greenland mineral, cryolite, 3NaF.A1F3, is still the only one which gives good performance in the electrolysis. In the early days, the process was thought of as a simple one. The dissolved alumina dissociated and, during the electrolysis, the aluminum was carried to the cathode where it was discharged and collected in a pool of metal. The oxygen was carried to the carbon anode where it reacted to form primarily carbon dioxide together with some carbon monoxide. About the only virtue that can be claimed for this hypothesis is that of simplicity. The actual mechanisms must be tremendously more complex. This paper is devoted to a rather narrow part of the whole subject, namely, what ions are present in the bath, and by what mechanism the current is carried. The complexity of the literature on this system is demonstrated in Table I, which shows the ions postulated as being present during the process. This system is not easy to investigate. Cryolite melts at about 1000°C, so that all the investigations are at relatively high temperatures. Molten cryolite fumes in air, particularly if excess aluminum fluoride is present. The cryolite changes composition on heating at 1000°C, principally by reaction with moisture in the air, but apparently also by reaction with oxygen. Cryolite reacts with most of the customary materials of construction, and those that are not attacked by cryolite seem inevitably to react with molten aluminum. Graphite is the only common material that is inert to the electrolytic bath. Pure cryolite can be held in platinum. There is hope that some of the newer refractories will stand up in bath, and their development for this purpose would be a major advance in the field. The techniques to be discussed, then, are not the most advanced ones. Rather, they are examples of old standardized methods applied under difficult conditions. The principal methods that shed real light on the mechanism are density, electrical conductivity, freezing-point lowering, transport number, viscosity measurements, and reactivity of bath with carbon dioxide. The first measurement to be discussed is density. This procedure is relatively straightforward. A hollow platinum bob is suspended by fine platinum wire from an analytical balance into the melt being investigated. Density1-4 of the system sodium fluoride-aluminum fluoride is shown in Fig. 1. There is a maximum in the density near the cryolite composition, but actually the maximum is on the NaF-rich side of cryolite, close to the composition NaF - Na3AlF8. Density measurements are also useful in giving a clue to the nature of cryolite-alumina melts.1, 4 On the first addition of alumina, density decreases, Fig. 2, although the density of alumina, either solid or liquid, is higher than that of cryolite. These density results indicate that the systems are not simple. A great deal of effort has been spent in measuring the electrical conductivity of molten cryolite and of cryolite with various additives. Conductivity measurements are quite easy for fused salts that can be measured in a dip cell, but no successful dip cell has been made available yet for cryolite. Recourse is had

Jan 1, 1959

By G. E. Keller, G. D. Coe

Several methods have been devised for rapid determination of sulfur in coal using a high-temperature combustion furnace. The fundamental principles of the various methods are similar but the techniques vary widely. The method described herein is no different in principle from some of its predecessors but varies considerably in technique. Originally devised to overcome the low-accuracy criticism leveled against the others, the tube-furnace method has proved successful for limited applications. Work is being done to widen the applicability of the technique. Subsequent to the work of A. Vita1 in 1920, a number of investigators have published data dealing with the rapid determination of sulfur in coal using a high-temperature combustion furnace.2-5 These, together with several unpublished methods, involve wide differences in technique although they are all similar in principle. Investigation of typical details of procedure showed that poor precision or accuracy could be attributed to one or more of the following: 1) inadequate quantity of sample to be representative, 2) a delivery tube temperature too low to confine condensation to a washable area of the tube, 3) no provision for back washing the delivery tube, 4) incomplete absorption of the sulfur compounds due to inadequate bubbler, and 5) the false assumption that all of the sulfur is evolved as sulfur dixoide. The method herein discussed is no different in principle from some of its predecessors; the differences are in technique. Although the method is rapid—a determination can be completed in 5 min— accuracy has riot been sacrificed in order to achieve speed. MATERIALS AND EXPERIMENTAL WORK Fig. 1 shows the arrangement of the equipment. A metered volume of oxygen is passed through calcium chloride for removal of moisture, then through Ascarite for removal of carbon dioxide, and thence through a glass tee to the feed end of the combustion tube. Connected to the side arm of the glass tee is a rubber tube that is closed with a pinch clamp during combustion of a sample. The products of combustion are expelled through a Vycor bubbler, the end of which is submerged 3 cm below the surface of a 1 pct hydrogen peroxide solution contained in a 300 ml high-form beaker. At the completion of the 4-min combustion period the contents of the beaker are titrated to a yellow end point, using a methyl red indicator, with 0.05 N sodium hydroxide (or sodium tetraborate). The pinch clamp on the tube leading from the tee in the oxygen line is then opened and mouth suction applied to draw the hydrogen peroxide up into the bubbler past the ell, almost to the rubber tube connecting the bubbler to the combustion tube. This washing of the bubbler is repeated until no further acid reaction with the indicator is obtained. The hydrogen peroxide-sul-furic acid solution is then titrated to the final yellow end point. Test work conducted at the Robena Laboratory disclosed the following critical conditions that had important bearing on the precision of the method: Weight of Sample: Several series of tests wherein the sample weight ranged from 0.1 to 0.5 g of -60 mesh coal showed that the lowest variance (standard deviation squared) resulted from the use of 0.5-g samples; the variance was slightly greater when 0.3-g samples were used, and with less than a 0.3-g sample weight the variance increased rapidly with decrease in weight. Although the use of a 0.5-g sample invariably resulted in a very slight explosion as soon as the sample entered the hot zone of the combustion tube, this did not detract from the precision of the method. Temperatures: Mott and Wilkinson5 found that a combination of low temperature (1250°C) and low oxygen flow rate (less than 700 ml per min) tended to give high results due to formation of oxides of nitrogen. Although the method herein employs a much higher oxygen rate than 700 ml per min, as an additional precaution to assure accurate results, 1315°C (2400° F) is recommended as the most desirable furnace temperature. The temperature of the elbow of the bubbler should be at least 75°C to minimize condensation

Jan 1, 1961

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, ' AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.' The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By Elmer Weber, W. M. Baldwin

Solid lead obeys a single parabolic weight increase vs. time law. In contrast, liquid lead undergoes three successive parabolic weight increases vs. time laws, the first of which has a low constant relative to the latter two. The conversion times for the change from one parabola to the next decrease with increasing temperature. IN recent reports on the subject,1,2 it was noted that zirconium and titanium scale in air by a complex mechanism. The scale first forming on the metal is protective to the extent that it gives a low constant, K, for Tammann's, and Pilling and Bedworth's parabolic equation: w² = Kt [1] relating weight increase, w, due to chemical reaction of the metal with the air, and time, t. After hundreds of hours of apparent stability in some cases the first scale yields to another that offers little protection to the metal. This transition from one scale to another, from a slow parabolic oxidation reaction to a fast one, was not due to impurities in the atmosphere or incidental effects (changing environment, etc.) but was a specific behavior of the metal itself, the transition occurring at definite times (dependent on temperature) and showing other reproducible traits. In view of this behavior how can long-time service behavior be predicted from short-time laboratory tests, not only in the case of these metals, but in any case? Certainly a systematic study of the type of scaling behavior described above—wherever it is found—would help to answer this question. The present paper is a report on the behavior as it is found in lead—the only metal to the authors' knowledge for which the behavior has been described at all, if inadequately, for our present purpose.* At least four oxides of lead are known, of which one occurs in two allotropic forms. They are ß (red) tetragonal PbO stable up to 486°C;8 a (yellow) orthorhombic PbO stable from 486°C up to its dissociation temperature in air at about 2300°C;9 minium or Pb3O4 which from the dissociation pressure data given in Fig. 1 decomposes to PbO at 540°C in air; lead sesquioxide or Pb2O3,; and lead dioxide or PbO2 which, according to Fig. 1, decomposes in air at 400°C to minium. In view of the high dissociation temperature of PbO, lead will scale up to at least its boiling point. Further, it is known that oxygen is almost insoluble in liquid lead.'V his implies a fair probability that an oxide scale would not dissolve in the molten metal and would afford the same protection to lead in the liquid state as in the solid. All of the oxides of lead for which specific gravity data are available are more voluminous than an equivalent weight of metal or a lower oxide from which they might form, hence the scales will be in compression. Lead oxides are known to be ductile, so it would be anticipated that they would form coherent nonporous scales. It is not surprising to learn, then, that both solid and liquid lead scale according to the Tammann, and Pilling and Bed-worth law.14,15 (Gruhl states that at 600°C and above lead oxidizes linearly with time because of "spitting" of the scale.) The parabolic constants K reported by various investigators3,14-16 are badly scattered, however, as shown in Fig. 2. The oxides formed on solid lead were described as being reddish-brown but were not chemically identified by Pilling and Bedworth.15 Gruhl's descripdin³ of the appearance of the scales On his liquid samples indicates that a (yellow orthorhombic) PbO is formed initially on the specimens but gives Way eventually—at least at temperatures below 486 °C— to .ß (red tetraunal) PbO, and that below 540°C minium—Pb3O4 :is firmed at an even later time as an overlay on either the red or yellow PbO. Fig. 3 is a graphical interpretation of Gruhl's description. Gruhl does not indicate any change in the parabolic scaling rate as yellow PbO converts to red. He does indicate that minium reduces the scaling rate, al-

Jan 1, 1953

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,' whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham's work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy' found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By D. P. Kedzie, R. A. Dodd

The fatigue strength, fatigue hardening, and effect of fatigue deformation on subsequent age hardening of supersaturated Al(Cu) solid solutions have been determined as functions of alloy composition and temperature. The fatigue strength/tensile strength ratios, determined at 150°, 25°, and -195°C, decreased with increase in alloy content for all temperatures, but the F.S./U.T.S. ratios at -195°C decreased much more rapidly than did the ratios for 150" and 25°C. This suggested that strain aging and/or age hardening occurred during tests at higher temperatures. Additionally, the F.S./U.T.S. ratios at 150°C exceeded those at 25°C for all compositions, indicating greater strengthening during fatigue at 150°C. The effect of fatigue or tensile deformation at 150°, 25°, and -195°C on subsequent age hardening showed that the deformatzon increased the rate of precipitation and indicated that mechanically produced vacancies were probably formed during deformation. Fatigue hardening was studied at 150°, 25°, and -195°C, and the effect of room-temperature rests after 10 and 100 cycles was examined. The results confirmed that strain aging occurred at the higher temperatures . DURING the last 15 years various mechanisms of fatigue crack nucleation and growth based on dislocation and vacancy interactions, operating singly or collectively, have been proposed. The probable consensus of present opinion is that the fatigue process in pure metals essentially involves dislocation interactions, and that vacancies formed by such interactions play a minor or inconsequential role. However, there is some evidence that age-hardened alloys tend to overage during fatigue, probably by local vacancy-enhanced diffusion, and strain aging also might be important in selected cases. Furthermore, it has been established that the behavior of quenched-in vacancies in Al(Cu) and other solid solutions is composition-sensitive. Therefore, it seemed worthwhile to investigate various aspects of the fatigue behavior of supersaturated Al(Cu) alloys and to examine the results in terms of vacancy-enhanced effects. EXPERIMENTAL The alloys used in this investigation were prepared from 99.994 wt pet A1 and OFHC copper, the latter containing 0.04 pet 0 as the principal impurity. Six alloys were made, containing, by actual analysis, 0.58, 0.96, 1.96, 2.85, 4.45, and 5.51 wt pet Cu. They were induction-melted in air in graphite crucibles, cast as 7-in. by 7/8-in.-diam rods in graphite molds, and hot-rolled to 5/8 in. diam. The experimental work was a three-part program involving the determination of a) 10' cycle fatigue stresses as a function of alloy composition and temperature; b) the effect of fatigue deformation on subsequent aging of the supersaturated alloys; and c) fatigue hardening as a function of alloy composition and temperature. For determining the 105 cycle fatigue stresses, a portion of the 5/8-in. stock was machined into Krouse rotating cantilever beam fatigue specimens, 2 in. in length by 1/4 in. minimum diameter. These were tested at +150°, 25°, and -195°C (liquid nitrogen) on a Krouse high-speed machine, with special weights to provide lower -than-normal loading ranges, this being necessitated by the small load requirements of those alloys of lower copper content. For the high-temperature tests a small resistance heater was designed to clear the collets and fit in between the chucks, while for the low-temperature tests a hollow nylon cylinder was used, having closed ends drilled to pass a fatigue specimen, and positioned similarly to the heater. A plexiglass container completely enclosed the fatigue machine; rubber gloves fixed to ports in the walls enabled the machine to be operated from outside the box. A tray of magnesium perchlorate dried the air in the container and prevented both atmospheric corrosion fatigue at room and elevated temperatures and troublesome ice build-up at low temperatures. A total of ten to fifteen specimens was used for each combination of alloy composition and temperature. The result of each test was plotted on a standard S-N diagram, and the next stress was selected on the basis of the trends indicated by previous specimens. In this manner a small portion of the S-N diagram was constructed, and the 105 cycle fatigue stress obtained. Small Krouse fatigue specimens were also used to study the effect of cyclic prestrain on subsequent

Jan 1, 1964

By T. V. Moore, H. D. Wilde

In many of the important problems of the petroleum engineer, it is necessary to know accurately the laws governing the flow of gas and liquid mixtures in vertical pipes. Although much work has been done along these lines, no satisfactory solution to the problem has been found. A good theoretical discussion of the energy balance in a gas-lift has been published by Versluys.1 One of the most important factors affecting the efficiency of the flow of oil and gas mixtures is slippage, and in most of the experimental work that has been done no provision has been made for the measurement of this quantity. As Versluys pointed out, since there is no method now known to estimate it from the data usually taken, slippage must be determined empirically. This paper presents the results of some work carried on to measure slippage in short experimental gas-lifts. As shown herein, slippage can be easily calculated in a vertical pipe carrying a mixture of oil and gas if the fractions of the pipe occupied by liquid and gas respectively are known. In this work, the fraction of the pipe occupied by the liquid was measured under a wide variety of conditions and the relationship between this fraction and other quantities, which are easily measured in ordinary work, was determined. It was hoped that the quantitative relationship obtained from this work could be used for making accurate calculations in flowing or gas-lift wells, but unfortunately it did not check satisfactorily when applied to actual wells. Apparently flow in long flow pipes is more efficient than in the short ones used for the experimental work. Nevertheless, it is felt that the data themselves arc of interest; that the method of attack may be of value in future work and that the relationship derived between slip and the relative velocities is a contribution toward the solution of the gas-lift problem.

Jan 1, 1931

Discussion of the paper of Godfrey T. Vivian, presented at the Cleveland meeting, October, 1912, and published in Bulletin No. 76, October, 1912, pp. 1103 to 1109. COURTENAY DEKALB, Tucson, Ariz. (communication to the Secretary*) :--Mr. Vivian's paper is interesting as an evidence of renewed attempts to solve the problem of adapting the centrifugal machine to the uses of the metallurgist. It would not seem that the Gee machine has solved the problem, because it is manifestly of use only with quite high-grade material, since low-grade pulp could not stand the cost of treatment by a discontinuous process. The mechanism, however, would seen to accomplish grading more perfectly than the ordinary centrifugal basket. This is an entirely different thing from concentration, which is intended to yield a finished marketable product. The real problem is to design a successful continuous centrifugal machine. Ten years or snore ago a machine, which might be described as having an inverted step-basket, offered much promise, and was constructed and tested at considerable cost, but it presented insuperable difficulties. The construction of a successful continuous centrifugal would be welcomed by the whole industrial world, since its uses would be most extensive. Mr. Vivian suggests the utilization of the centrifugal machine as a substitute for slime filters in the cyanide process, but he, has apparently not tried the experiment. I tested the efficiency of centrifugal machines for this purpose in 1897-8, having to extract the cyanide solution from a highly argillaceous slime of the sticky kind which the Mexican call ?lama." Our filter-presses yielded cakes containing usually :30 per cent. of moisture, and so dense as to preclude washing. The centrifugal machine readily Brought the moisture content down to 9 per cent. and permitted fairly successful washing. Despite these advantages, the cost of power, labor, and repairs, and the loss of time in discharging the cake, exceeded the costs and

Jan 5, 1913

By Shozo Saito, P. A. Beck

Mettrllographic and X-ray diffraction study of Cb-Co alloys in the Composition range of 7 to 33 nt. pct Cb, after annealing at 1175 °', showed that near 25 al. pct Cb on MgNi,-lype hexagonal Laves Phaseexists in a narrow composition range, and that an MgCl- type cubic Laves Phase occurs between approximately 27 and 32.6 ut. pd Cb. Lattice parameter and density measures indicated that, in both phases. the deviations from proper Loves sloichimetry result from the substitution of cobalt atoms for some 0f the columbium atoms. Tlle same phases occurant 1000'C, together with an additional phase of unknown structure, which appears between the hexagonal Laves phase and the cobalt-bose terminal solid solutions KOSTER and Schmid' identified a phase corresponding to the composition VCo,, and more recently the crystal structure of this phase has been determined.' In the Ta-Co system Korchynsky and Fountain recently found two intermediate phases at the composition Taco,, one of them metastable. In contrast to the V-Co and the Ta-Co systems, in the Cb-Co system no intermediate phase has been found4 at the composition CbCo,. The present investigation was undertaken in order to reexamine the question of the existence of such a phase. EXPERIMENTAL PROCEDURE Twelve alloys were prepared by arc-melting in a water-cooled copper crucible under helium atmosphere. Electrolytic cobalt and 99.9 pct pure colum-bium powder have been used as starting materials. It was found that melting losses can be reduced by compressing the colunlbium powder in the form of thin pellets before melting. For the alloys used the melting losses were not higher than 1 pct. The intended compositions of all alloys and the chemical analyses of three of them are given in Table I. Specimens from all alloys were annealed in evac- uated fused silica tubes at 1175°C for 3 days and quenched in cold water. A second set of specimens of most alloys was annealed at 1000°C for 7 days and then quenched in cold water. The annealed and quenched specimens were examined metallographically, using the following etchant: 60 pct glycerine +20 pct H,NO, + 10 pct HF + 10 pct water. Powder specimens for X-ray diffraction were prepared by crushing annealed solid specimens in a mortar. Alloys containing 27.3, 28, 29.7, and 32.6 at. pct Cb annealed at either 1175" or 1000°C were very brittle and it was found unnecessary to reanneal the powders. However, alloys containing 24.8 at. pct Cb, or less, especially those annealed at 1000°C, were much less brittle and re-annealing was required to remove the strains present in the crushed powders. In each case reannealing was done at the same temperature at which the corresponding solid specimens were annealed and it, too, was followed by quenching in cold water. In many instances X-ray diffraction patterns were also taken of the polished and etched solid specimens and compared with the corresponding X-ray diffraction patterns obtained with powders. The X-ray diffraction patterns were taken with an asymmetrical focusing camera, using CrK radiation. For precision lattice parameter measurements some X-ray diffraction patterns were taken with a symmetrical focusing camera, again using CrK radiation. EXPERIMENTAL RESULTS A microscopic examination of the alloys annealed at 1175°C revealed that the alloy containing 25.5 at. pct Cb was composed of a single phase, but that the 24.8 at. pct Cb alloy did contain a small amount of a second phase, identified by means of X-ray diffraction as having a fcc structure, undoubtedly the terminal solid solution based on cobalt. Apart from the few very weak lines corresponding to this minor phase, the X-ray diffraction patterns of these alloys could be well interpreted in terms of a MgNi,-type hexagonal Laves phase structure. The indexing of the X-ray diffraction pattern, Table 11, yas based on the lattice parameter values a, = 4.740A and c,

Jan 1, 1961

By J. O. Brittain, N. R. Adsit

A number of zinc bicrystal specimens with the grain boundary loaded in simple shear were plustically deformed in creep in a vacuum at 200°C and under an argon atmosphere at 350°C. The results indicated that the amount of grain boundary sliding at a given time was controlled by the slip in the grains and was proportional to the resolved shear stress on the slip plane. Curves of grain boundary sliding vs time were found to be cyclic with no regular periodicity. ALTHOUGH grain boundary sliding (G.B.S.) has been investigated in a number of different types of tests on various materials there is substantial disagreement on the interpretation of the various observations. Gifkins1 has presented a comprehensive review of the subject of G.B.S. and fracture. He reports that the activation energy for high-temperature creep is equal to that for volume self-diffusion and that pure metals show less tendency towards intercrystalline fracture than alloys. Pure metals show appreciably greater grain boundary migration than alloys, and both grain boundary migration and grain boundary sliding follow the same general trend in time as plastic deformation during creep.' While there have been a number of different mechanisms proposed to account for G.B.S., none of the models explains all the results. Since zinc has only one prominent slip system, it was hoped that experiments on G.B.S. in zinc bicrystals might enable us to separate the effect of grain boundary angle and the effect of matrix slip and thereby resolve at least one part of this complex phenomenon. EXPERIMENTAL PROCEDURE Bicrystals of pure zinc (99.99 pct) were grown by a Bridgeman technique in a furnace having a gradient of 20°C per in. The bicrystals were seeded to a desired orientation and grown in a split graphite mold which was 3/4 by 5/8 by 8 in. The mold was enclosed in a Pyrex tube and the tube was evacuated and then filled with a small amount of argon before it was placed in the furnace. The growth rates were 1/2 to I in. per hr for the bicrystals and 1/2 to 3 in. per hr for the single-crystal seeds. The longitudinal V notches served to hold the grain boundary in position during the growth process. A schematic rep- resentation of a specimen which had been cut with a jewelers saw from the bicrystals is shown in Fig. 1. All specimens of a series were cut from the same crystal, some of which were 7 in. in length. After specimen preparation the boundary was approximately 5/16 in. long and the V notches had a radius of 1/16 in. The boundaries were straight at a magnification of X100 with the exception of a few which had a gradual radius of curvature of greater than 3.2 in.-1. Laue back-reflection photograms were taken on the specimens to check the orientation of grains in the bicrystals. The method of relating the orientation of the two lattices is shown in Fig. 1, where 0 is the angle between normal to the boundary and the trace of the basal plane, is the angle in the boundary between the trace of the basal plane and a line parallel to the V notch, and x is the angle in the basal plane between the Burgers vector and the perpendicular to the grain boundary. After mechanical polishing the specimens were chemically polished.2 Subsequent to the polishing operation the specimens were encapsuled under a vacuum of better than 25 annealed at 340°C for 1 hr to remove the effects of this handling, and again chemically polished. Finally, fiduciary marks were scribed on the specimen using a micromanipulator. Creep tests, which were conducted in a modified Bausch apparatusS with the boundary loaded in simple shear, were run at a constant load (since the boundary area remained essentially constant this is approximately constant grain boundary stress). The temperature was controlled to ±1/4°C as measured on a semiprecision potentiometer with a calibrated thermocouple. The specimens were tested in a vacuum of better than 0.5 at 200°C and in purified argon at a pressure of 1/2 atm at 350°C. The op-

Jan 1, 1965

By H. K. Birnbaum

The effect of 1ow-temperature stabilization anneals on the structure of the 0 phase Au-Cd alloys and on the diffusionless transformations observed in these alloys was examined by X-yay diffraction techniques. A phase separation in the ß-phase region was proposed to account for the experimenta1 results. The effects of quenching from elevated temperatures on the transformation behavior of these alloys were shown to be consistent with the proposed mechanism. IT has been shown that the high-temperature ß phase (CsCl structure) of the Au-Cd alloy system transforms to a phase having an orthorhombic (D2) ß&apos; structurel1-3 for compositions near 47.5 at. pct Cd and a tetragonal (4/m, m, m) ß" structure* in the vicinity of 50.0 at. pct Cd. Both transformations are diffusionless, crystallographically reversible, and occur on cooling at about 60° and 30°C respectively. The temperature interval from the beginning to the end of the transformation is of the order of 5°C in each case. Although the transformations are normally athermal, some of them have been reported to occur isothermally.= wechsler6,7 has shown that the effects of quenching a 49.0 at. pct Cd alloy from elevated temperatures are consistent with the retention of a nonequilibrium number of lattice vacancies. Annealing of these quench effects results in a broadening of the X-ray reflections.8 After a suitable quench, the 47.5 at. pct Cd alloy transforms to a phase having not the p&apos; orthorhombic structure but another structure which has properties similar to that of the ß" tetragonal structure.5.9 This change in the type of transformation has also been obtained after long anneals in the ß-phase region at about 70oC10 The present investigation was primarily concerned with the structural changes accompanying the above transformation phenomena. The change in transformation product and accompanying physical changes during an anneal in the ß phase have been termed stabilization effects. Experimental Procedure —The results reported in this investigation were obtained with the use of a Norelco diffractometer fitted with a temperature-controlled cryostat. The specimen temperature was controlled to better than ± 0.l°C during the measurements. CrKa radiation monochromated electronically with the use of a scintillation counter and pulse height analyzer was utilized. Specimens containing 47.5 and 50.0 at. pct Cd were prepared by sintering filings obtained from homogenized ingots of the proper alloy composition. (Gold of 99.999 pct purity and cadmium of 99.98 pct purity were used). All heat treatments were carried out with the specimens capsulated in vacuum ( < 10 % mm Hg) or in a He-H gas mixture. The quenching technique used in these experiments was to drop the pyrex capsule which contained the specimen from the annealing furnace into water, the temperature of which was controlled. The pyrex capsule shattered on contacting the water resulting in a relatively rapid quench. After the heat treatment, the specimens were mounted in the diffractometer and were left undisturbed in the diffractometer specimen holder during each sequence of measurements. EXPERIMENTAL RESULTS A) Low-Temperature Annealing—The transformations which were considered "normal" for these alloys were those obtained athermally during furnace cooling at approximately 50°C per hr after an elevated temperature anneal. Under these experimental conditions, the specimens were observed to transform to phases having structures whose diffraction patterns could be indexed as the ß&apos; orthorhombic structure for the 47.5 at. pct Cd and as the 0" tetragonal structure for the 50.0 at. pct Cd alloys. The transformation temperatures on cooling were approximately 60" and 30°C, respectively. Under the "normal" conditions both transformations were observed to go to completion, i.e., the entire volume of the ß phase was transformed to the product phase. In some specimens an extremely weak ß 110 reflection was observed at 20°C indicating that a small amount of retained ß was present. The effect of low-temperature annealing on the nature of the diffusionless transformations was examined for the 47.5 and 50.0 at, pct Cd alloy. The specimens were annealed in evacuated capsules at temperatures in the vicinity of 600°C (as specified in Table I) for 24 hr and were then cooled to 100°C at a rate of 50°C per hr. The specimens were then removed from the capsules and mounted in the diffractometer without allowing the specimen temperature to drop below 80°C. Annealing at the low temperatures was accomplished in the diffractometer by means of the cryostat which was mounted around the specimen. During the low-temperature anneals the lattice parameter, integral breadth of the reflections, and ratios of the integrated intensities of the fundamental and super lattice reflections for the 0 cubic phase were periodically determined. After annealing for the required time, the specimens were slowly cooled in the diffractometer and the diffraction patterns were recorded as a function of temperature. The specimens were cooled until the phase transformations were completed, following which the specimens were heated and diffraction

Jan 1, 1960

By R. D. Schoone, J. T. Michalak

Recovery, recrystallization, and texture development of a cold-rolled aluminum-killed steel have been studied during simulated box annealing. Two different initial conditions existed prior to cold rolling: 1) essentially all of the nitrogen in solid solution and 2) most of the nitrogen precipitated as AlN. The combined effect of nitrogen and aluminum in solid solution before annealing was to inhibit recovery and sub-grain growth at temperatures above about 1000°F and to raise the recrystallization temperature range on continuous heating at 40°F per hr from 1000"-1050°F to 1065"-1085°F. For the material with nitrogen and aluminum initially in solution there was an inhibition in the nucleation of the (001) [110] texture component and an enhancement of the (111) [110] texture component. The differences in annealing behavior mzd texture development are attributed to preprecipitation clustering of aluminum and nitrogen at subboundary sites developed by prior cold working. THE annealing of cold-worked aluminum-killed steels has been the subject of numerous investigations.&apos;-&apos;2 These studies have been concerned with kinetics of recrystallization, with microstructure and texture development, and with the individual and combined effects of composition, thermal history prior to cold rolling, and heating rates during subsequent annealing. It has been shown that the inhibition of recrystallization, and the development of the pancake-shaped grain and recrystallization texture characteristic of aluminum-killed steels, can be associated with the precipitation of A1N particles during a recrystallization anneal involving heating rates in the range 20" to 80°F per hr. If the AIN is precipitated before cold rolling or if more rapid heating rates are employed, the cold-rolled steels recrystallize more rapidly to an equiaxed grain structure and texture comparable to that of rimmed low-carbon steel. The retardation of recrystallization, the development of the elongated grain structure, and the pronounced (111) texture have been attributed to: 1) precipitation of A1N at prior cold-worked grain boundaries to form a mechanical barrier to grain boundary migration;&apos; 2) precipitation on the boundaries of the growing recrystal-lizing grains as well as on cold-worked grain boundaries;&apos;" and 3) preprecipitation clustering or precipitation on subboundaries to retard recovery, nucleation, and growth. The present study was undertaken to study in more detail recrystallization and texture development during commercial box annealing of cold-rolled aluminum-killed steels. Comparison of the annealing be- havior after cold rolling, for two different conditions prior to cold rolling, was made in an attempt to define more clearly the role of aluminum and nitrogen in forming the recrystallization texture. A) MATERIAL AND PROCEDURE The material used in this investigation was a commercial low-carbon aluminum-killed steel which was hot-rolled with a finishing temperature of about 1565"F, then coiled at about 1020°F. The composition, in wt pct, was: 0.050 C, 0.30 Mn, 0.007 P, 0.019 Si, 0.03 Cu, 0.02 Ni, 0.02 Cr, 0.045 Al, and 0.004 N. Two 4.5 by 13 by 0.078 in. sections were cut from the center section of a hot-rolled panel and one of these was reheated to provide two different conditions prior to cold rolling: low AlN: as commercially hot-rolled, with aluminum and nitrogen in solid solution; and high AlN: as commercially hot-rolled, then reheated at 1300°F for 3.5 hr to precipitate most of the nitrogen as AlN. ~etallc&a~hic examination indicated that the reheating did not change grain size nor carbide distribution (some spheroidization of pearlite was noted). Texture analysis at half-thickness level showed that both sections had the same substantially random as-hot-rolled texture. The results of check chemical analysis of each sample are given in Table I. Both sections were cold-reduced 65 pct on a laboratory rolling mill to a final thickness of 0.027 in. Cold rolling, in one direction only, was in the direction of the prior hot rolling. Specimens 1.0 by 1.25 in. were cut from the cold-rolled sheets and given a simulated box anneal in an atmosphere of 2 pct HZ-98 pct He. Specimens were heated at a constant rate of 40°F per hr from room temperature to various temperatures in the range 750" to 1300°F and cooled immediately by withdrawal to the water-cooled end of a tube furnace. The temperature in the 6-in. uniform hot zone of the furnace was controlled within 3"F. Selection of the individual specimens was made to give a random distribution of annealing temperatures with respect to location in the cold-rolled sheet. At least two specimens of each condition were annealed to the same temperature and smaller specimens for light microscopy, transmission electron microscopy, and X-ray studies were prepared from each of these. Rolling-plane sections for each of these studies were taken at half thickness. Light microscopy and transmission electron micro-

Jan 1, 1969

By Thomas A. Simpson

THE Birmingham red iron ore district in Jeffer-son County, north central Alabama, Fig. 1, is bounded on the northwest by the Warrior and Plateau coal fields and on the southeast by the Cahaba and Coosa coal fields. The area of study includes the ridge and valley between Red Mountain and Shades Mountain, Fig. 2, approximately 70 square miles extending from Homewood in the northeast to Greenwood in the southwest. The district is one of the most important producers of hematite in the United States, with an annual production of about 7 million tons.&apos; The amount of hematite mined between 1870 and 1950 ranged from 6 to 16 pct of the nation&apos;s total annual production,&apos; and the iron and steel products from blast furnaces in the Birmingham district supply the entire southeastern section of the country. Most of the mining in the Birmingham district is from slope mines along the outcrop of the ore on Red Mountain, such as Red Ore, Muscoda, Spaul- ding, and Sloss. The Pyne and the Shannon are the shaft mines of the area. The Shannon mine of Republic Steel Corp., in the central part of the area under study, is in Shades Valley at the foot of Shades Mountain. The Pyne mine of Woodward Iron Co. is 2 miles east of Readers Gap in Shades Valley. The hydrology problem has become more prevalent as mining in the area has progressed downdip. An extensive exploratory diamond drilling program is necessary to determine areas where water pressures and abnormal flows are excessive. This operation, added to higher pumpage rates, has greatly increased the costs of ore extraction. In November 1952 the U. S. Geological Survey began a detailed study of occurrence and movement of ground water in the iron mining areas of the Birmingham district. The study is a part of a small-scale but nationwide program to develop data that will be of help to the mining industry in solving mine water problems. The area of the study, in the Ridge and Valley province of the Appalachian system, Fig. 1, is a series of alternate ridges and valleys trending northeast. The principal ridges are Red Mountain, altitude about 1000 ft, and Shades Mountain, about 1100 ft. Shades Valley is between these two ridges, and its lowest point is about 480 ft. Shades Moun-

Jan 1, 1956

By K. B. McQuillin

The volume of data resulting from an intensive search for new coalfields necessitated the establishment of a computer based processing system for coalfield data. The development of this system over the past seven years is described, with particular reference to the problems encountered in both the design and operation of the data base.

Jan 1, 1977

By J. F. Poland

Annual pumpage of ground water from the alluvial valleys of California now is about 10 million acre-feet. This heavy pumpage has created problems of over-draft and ocean-water encroachment in many valleys. Steps are being taken to protect and increase the available supply but much additional basic study is needed.

Jan 2, 1950

By A. G. Roach

THIS paper deals with a plant built under joint agreement between the Canadian and United States Governments to supply the strategic mineral, corundum, at a time when African production was dwindling and war demands still increasing. The operation began in September 1944, retreating the tailings from a former mill by gravity methods, and is still in production (Sept. 1946). In 1942, when it became apparent that South African production would be insufficient to meet mounting wartime requirements of corundum, a survey was made of Canadian sources of the mineral, at the request of the Foreign Economic Administration of the U. S. Government. The investigation1 indicated that the quickest and cheapest supply would be obtained by reworking the tailings deposit at Craigmont, Ontario. Sampling of the dump by Canadian Government engineers revealed that 125,000 tons of tailings, averaging 2.96 pct corundum, was available for retreatment. Ore-dressing tests on representative samples of the deposit were conducted by the writer in the laboratories of the Industrial Minerals Section of the Department of Mines and Resources at Ottawa; and gravity concentration on tables was indicated as the most suitable method of treatment. Decision to proceed with the project was deferred until May 9, construction was begun on May 18, and tune-up operation of the plant begun on Sept. 15, 1944. CORUNDUM-ITS PROPERTIES AND USES Corundum is an oxide of aluminum having the formula A1203. Its outstanding characteristic is its great hardness; 9 in the Mohs scale. In this respect it is second only to the diamond. It usually occurs in barrel-shaped crystals in nepheline syenites and other feldspathic rocks deficient in silica. It has a specific gravity of 3.95 to 4.1 and is insoluble and infusible. In color it ranges from white, through red and green, to black. Ruby and sapphire are gem varieties of corundum. Corundum is supplied to industry as closely graded grain.2 The coarser products (10 to 24-mesh) are used largely for snagging wheels in the steel-castings industry, while the finer grades (from 70-mesh down to flours) find a wide application in the polishing of lenses and for other uses in the optical trade. All sizes of corundum grain are in close competition with synthetic abrasives such as carborundum and alundum. In some fields of application the artificial product is superior to the natural grain but not in all. The shape of the particle and its behavior under conditions of actual use determine its sphere of employment. The United States is the largest consumer of corundum, annual consumption in peacetime approaching 3000 tons; during the war this figure was roughly doubled. During the years 1902 to 1913, the bulk

Jan 1, 1946

By B. M. Larsen, L. S. Darken

SOME years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general. our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2-by a high concentration of active (or "free") lime and of manganese oxide dis) solved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. DISTRIBUTION OF MANGANESE BETWEEN SLAG AND METAL AT EQUILIBRIUM On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction [FeO + Mn ;7± MnO + Fe [A] slag metal slag metal] the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as [K" aFPI OFeO ? aMn] where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term aFe may he combined with K" to give a new constant K&apos;. Making these changes.

Jan 1, 1942

By Walter Knox, Charles H. Sawyer

All of the coals commonly used in domestic bituminous stokers form coke, and satisfactory operation depends upon the fact that the coke formed is so weakly bound together that it breaks readily in the normal operation of the stoker and automatically maintains a good fuel bed. Some coals, because of their tendency to form solid, blocky coke, are practically excluded from use in small domestic stokers as now built. Other coals, some among the best stoker coals available, can form this troublesome coke under certain conditions. Many contradictory methods have been offered as cures for coke formation. Generally the procedure has been to try various adjustments until a combination was found that seemed to give better results. Such random methods of treatment have not provided any reliable information as to causes. The present paper covers a comprehensive test program undertaken by the Koppers Company&apos;s Stoker Coal Research Laboratory at Kearny, N. J. The program had two main objectives; first, to discover what factors affected coke formation, and second; to define corrective steps that could be applied in stoker service work. Conclusions and Results i. The design of the stoker outweighs in importance all other factors capable of improving coke formation. 2. Insufficient air supply aggravates the formation of large blocky coke, although raising the air above 30 to 40 per cent excess (as determined during steady running) does not further improve the character of the coke formed and only reduces its accumulation at the expense of efficiency, increased fly ash, poorer clinker-ing, and other disadvantages. 3. Increasing the coal feed results in a somewhat more friable coke structure and is recommended for persistently troublesome jobs. 4. Increasing over-fire draft improves the character of the coke formed and reduces troublesome accumulations by accelerating off-period burning, although at some expense in efficiency and some increase in fly-ash accumulation. 5. Coke structure was not substantially improved by blocking some of &apos;the retort tuyeres, although the blocking of tuyeres at the feed-screw end of a rectangular retort did lead to somewhat improved performance, possibly because of considerably better distribution of coke in the fuel bed. 6. With the equipment tested no difference was shown between installation of the same stoker in a steam boiler and a warm-air furnace, or between a sand-filled and a ventilated type of hearth. 7. The following design features had no noticeable effect on coke formation: a. Presence or absence of coal-tube air as provided by many manufacturers to eliminate smoke-back. B. Presence or absence of a flap damper ill the air duct to minimize off-period burning. c. Continuous or intermittent (ratchet and pawl driven) movement of fuel feed screw.

Jan 1, 1944