Search Documents

By F. C. Bond, J. T. Wang

H. J. Kamack (E. I. du Pont de Nemours & Co., Inc., Wilmington, Del.)—Rittinger's law usually is stated to the following effect: "The work (or energy) consumed in particle size reduction is proportional to the new surface area produced." The law has been stated substantially in this way by Taggart20 Berry21 Dalla Valle22 Coghill and DeVaney,23 Richards and Locke," Gross,25 and many others, and, according to Gaudin,26 was originally expressed by Rittinger in the same form. Consequently there can be little doubt that this is the understanding of the law among most workers in the field of particle size reduction. Bond and Wang, however, express the law in the form "the useful work accomplished . . . ." (italics theirs). The distinction is critical, for in the form used by Bond and Wang the law becomes, as they themselves remark "merely a more or less arbitrary definition of useful work," while in its usual sense the law expresses a physical hypothesis which has been verified experimentally within certain limitations. Considering the way the law has been used, it might be stated more explicitly as follows: "In a given machine operating under a given set of constant operating conditions, the work consumed in the particle size reduction of a given material is proportional to the new surface area produced." Or, as Coghill and deVaney have said,27 "the (Rittinger) law holds only when the tests being compared are made under analogous conditions." There are occasions when the law transcends these limitations; for example, the surface area produced per unit energy consumption for a given material in a ball mill does not vary much over a fairly wide range of operating conditions. But by and large, the surface area production per unit energy consumption will vary with the operating conditions, the type of machine, and the material. The essence of Rittinger's law is that the surface area production per unit energy consumption is independent of the particle size, and this has been verified experimentally by numerous workers for numerous materials, within certain limits. An important limitation is that when one grinds to very small particle sizes, agglomerative forces may tend to interfere with size reduction so that the surface area increases less rapidly than Rittinger's law would predict. Within such limitations, Rittinger's law can be regarded as empirically established. The law has, however, certain theoretical implications, and it seems to be chiefly against these that Bond and Wang direct their criticism. Solids are believed to possess surface energy which is proportional to surface area. Thus, Rittinger's law implies a proportionality between surface energy produced and mechanical energy expended (for a particular material in a particular machine). It does not imply that all or most of the mechanical energy is transformed into surface energy; in fact it is known that most of the mechanical energy is transformed into heat. Bond and Wang assert that most of this heat arises from the damping of elastic vibrations of stressed particles. This may possibly be true for crushing (with which they are chiefly concerned), although in grinding it is probable that much of the heat arises from friction between particles. However, the fact that the surface energy is small compared to the heat energy does not invalidate Rittinger's law, which implies merely that they are proportional. The authors also criticize Rittinger's law on the grounds that "this theory cannot be justified mathematically, since work is the product of force times distance, and the distance factor is ignored," and "energy input must be the product of force times distance, and the Rittinger theory completely ignores large variations in the distance (strain dimension or deformation) throughout which a force must act to produce breakage of different materials." However, the quantities force and distance as such are irrelevant to Rittinger's law, which considers energy input as an integral quantity. The fact that different materials require different forces and strains (hence, different amounts of energy) to break them is incontrovertible but again is irrelevant to Rittinger's law, which, as mentioned before, applies -only to a single material. Even in theory, it would not be expected that the surface area produced per unit energy consumption would be the same for different materials, because the surface energy per unit area is presumably specific to each material. Bond and Wang advance another argument of a

Jan 1, 1952

Jan 1, 1931

By Rodney Lawrence, Tim Hackett

INTRODUCTION The western USA contains significant coal reserves in seams 10 feet or more in thickness which lie too deep for surface mining. As part of a demonstration of the use of two legged shield supports in the United States, Kaiser Steel Corporation, under contract to the US government used the longwall method to mine a ten foot thick coal seam in New Mexico. Caliper type shield supports and double drum shearers were used in three longwall panels. During the test, technical, production, and safety data were collected to objectively evaluate the performance of the shields in mining the thick coal seam. This paper presents discussions of practical operating experience and summary statistics to aid the mining industry in planning longwall mines in similar conditions.

Jan 1, 1981

By V. R. Degner

The trend in both the metallic and nonmetallic mining industry is toward processing increasingly higher tonnages of lower grade ores, thereby resulting in a growing interest in progressively larger volume individual machines in the flotation circuit. Because of the relatively high cost of large flotation machine development and evaluation, it is important to establish a rational basis by which the existing smaller flotation machine experience can be extrapolated to establish the configuration of the next larger family of flotation machines with a minimum of development modification in the field. This Paper reviews the R&D approach used in translating smaller flotation machine experience to the configuration of a 28.3 m3 (1000 cu ft) induced air machine. Internal cell hydrodynamic principles, which governed this extrapolation, and cell (liquid) surface and froth management considerations will be reviewed, and prototype machine mill tests will be summarized.

Jan 1, 1981

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York LOUIS D. HUNTOON, Chairman. ARTHUR S. DWIGHT, Vice-Chairman. THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. E. MALTBY SHIPP, Treasurer. GEORGE F. KUNZ, W. DE L. BENEDICT. Boston ROBERT H. RICHARDS, Chairman. ALBERT SAUVEUR, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH.

Jan 2, 1914

ALASKA Established November 19, 1947 Meets fourth Monday of each month at Fair¬ banks, Alaska J D CRAWFORD, Chairman BRUCE I, THOMAS, Vice-Chairman C D JERMAIN, Vice-Chairman for Southeastern Alaska EARL H BEISTLINE, Secretary-Treasurer Box 265, College, Alaska

Jan 1, 1952

By EL HANAF

The exploratory program initiated in Egypt in 1937 by four major oil companies was well under way early in 1939. Extensive gravity-meter surveys were carried out in the Sinai Peninsula and the Eastern and Western Deserts. Seismic and magnetometer work vas conducted on a restricted scale. The data collected justified wildcat drilling on structures located geophysically and/or geologically.

Jan 1, 1946

By W. A. Ver Wiebe

The year 1940 was singularly unmarked by sensational developments in Kansas. Routine operations were carried on in a systematic, orderly fashion and the efforts of oil producers were concentrated on extending known fields. In Kansas an arbitrary yardstick for wildcats has been set up. A well drilled mile or more from a known pool or well is now considered a wildcat. A "rank wildcat" is one that is drilled at least 2 miles from any known producer. During 1940, rank wildcats resulted in the completion of 116 test wells, among which 16 were successful in finding new oil pools and the remaining I00 were dry holes. The ratio of successful wells to dry holes, therefore, was approximately I:6. During the year, 1890 wells were completed in eastern and western Kansas. This figure is somewhat lower than that given in several trade journals, because it does not include wells that were deepened or wells that were recompleted in a different geological horizon. About three fourths of these (1423) were completed as commercial oil wells (I220 in western and 203 in eastern Kansas). The commercial gas wells completed number 58 of which 10 are in eastern Kansas and 48 in western Kansas. Of the remzining completions 147 are dry holes in eastern and 262 are dry holes in western Kansas. Based on daily potential capacity, the new discoveries of the year account for a cumulative initial production of 46,000 bbl. in eastern and 2,128,000 bbl. in western Kansas. The state of Kansas attained a new peak in production, with the total of 66,245,000 bbl. for the year 1940, the number of contributing wells being 20,779. Thus the increase over 1939, when about 58 million barrels was produced, is considerable. The previous peak occurred in 1937, when 70,761,000 bbl. was marketed. In another still earlier peak, in 1917, slightly more than 45,000,000 bbl. was produced and sold. The production of gas probably reached a new peak also during 1940, with its total of 85 1/2 billion cubic feet. Between the peak of the year 1908, when over 80 billion cubic feet was produced, and that of 1940, the production dropped to a low point of 16 billion cubic feet in the year 1921. The number of test wells drilled was larger than in 1939; that is, 1890 compared with 1458. The first peak was reached in 1904, when 2782 wells were drilled. The number dropped off rapidly, to 368 three years later, but rose to the second and highest peak in 1918, when 4671 test wells were completed. In the period between 1904 and 1912 more gas wells were completed than oil wells. Between the high peak of completions in 1918 and somewhat lower peak of 1937, the low point was reached during 1931, with the completion of only 470 test wells. In the number of new pools discovered, Kansas again ranks high among the states. The exact number depends somewhat upon the interpretation of a "new" area— whether it should be called a new pool or a long extension of an old pool. Unfortunately, the matter of securing the right kind of production allowable also enters into this question. Often the decision regarding a new pool cannot be made until other wells

Jan 1, 1941

By W. A. Ver Wiebe

The year 1940 was singularly unmarked by sensational developments in Kansas. Routine operations were carried on in a systematic, orderly fashion and the efforts of oil producers were concentrated on extending known fields. In Kansas an arbitrary yardstick for wildcats has been set up. A well drilled mile or more from a known pool or well is now considered a wildcat. A "rank wildcat" is one that is drilled at least 2 miles from any known producer. During 1940, rank wildcats resulted in the completion of 116 test wells, among which 16 were successful in finding new oil pools and the remaining I00 were dry holes. The ratio of successful wells to dry holes, therefore, was approximately I:6. During the year, 1890 wells were completed in eastern and western Kansas. This figure is somewhat lower than that given in several trade journals, because it does not include wells that were deepened or wells that were recompleted in a different geological horizon. About three fourths of these (1423) were completed as commercial oil wells (I220 in western and 203 in eastern Kansas). The commercial gas wells completed number 58 of which 10 are in eastern Kansas and 48 in western Kansas. Of the remzining completions 147 are dry holes in eastern and 262 are dry holes in western Kansas. Based on daily potential capacity, the new discoveries of the year account for a cumulative initial production of 46,000 bbl. in eastern and 2,128,000 bbl. in western Kansas. The state of Kansas attained a new peak in production, with the total of 66,245,000 bbl. for the year 1940, the number of contributing wells being 20,779. Thus the increase over 1939, when about 58 million barrels was produced, is considerable. The previous peak occurred in 1937, when 70,761,000 bbl. was marketed. In another still earlier peak, in 1917, slightly more than 45,000,000 bbl. was produced and sold. The production of gas probably reached a new peak also during 1940, with its total of 85 1/2 billion cubic feet. Between the peak of the year 1908, when over 80 billion cubic feet was produced, and that of 1940, the production dropped to a low point of 16 billion cubic feet in the year 1921. The number of test wells drilled was larger than in 1939; that is, 1890 compared with 1458. The first peak was reached in 1904, when 2782 wells were drilled. The number dropped off rapidly, to 368 three years later, but rose to the second and highest peak in 1918, when 4671 test wells were completed. In the period between 1904 and 1912 more gas wells were completed than oil wells. Between the high peak of completions in 1918 and somewhat lower peak of 1937, the low point was reached during 1931, with the completion of only 470 test wells. In the number of new pools discovered, Kansas again ranks high among the states. The exact number depends somewhat upon the interpretation of a "new" area— whether it should be called a new pool or a long extension of an old pool. Unfortunately, the matter of securing the right kind of production allowable also enters into this question. Often the decision regarding a new pool cannot be made until other wells

Jan 1, 1941

By AIME AIME

INSTITUTE members attending the Annual Meeting in New York who want to see one of the mining engineers' newest aids, photoelastic stress analysis, are due for an interesting afternoon on Thursday, Feb. 15, when open house: will be held at the Columbia University mining laboratory. Information as to the direction and distribution off stresses in mine structures, which has been developed by Professor Bucky, associate professor at the Columbia School of Mines, and David Sinclair, research assistant, is useful in the design of pillars and in the placing of openings relative to working places such as gangways and haulage levels.: This work has been sponsored during the last ten years by the Engineering Foundation.. It is fully reported in T. P. No. 1140.

Jan 1, 1940

By F. I. Grace, L. E. Murr

The mechanical responses and residual defect structures in 70/30 brass and type 304 stainless steel following explosive shock loading and cold reduction by rolling have been studied. A distinct relationship was observed to exist between the residual mechanical properties and micro structures observed by transmission electron microscopy. Shock-loaded brass deformed primarily by the formation of coplanar arrays of dislocations and stacking faults at lower pressures, and twin-faults (deformation twins and €-martensite bundles) at higher pressures (> 200 kbar). The micro -structures of cold-rolled brass were characterized by dense dislocation fields elongated in the rolling direction. Stainless steel was observed to deform by the formation of dense arrays of stacking faults at lower shock pressures and twin-faults at high shock pressures (>200 kbar). Lightly cold-rolled stainless steel deformed similar to low Pressure shock-loaded stainless steel, but transformed to a' martensite in heavily cold-rolled stainless steel. Discontinuous yielding was observed for the heavily cold-rolled stainless steel, and stress reluxution in the weyield region for cold-rolled and shock -loaded stainless steel was interpreted as an indication of the ability of twin-faults and stacking faults to act as effective barriers to dislocation motion. A simple model for the formation of the planar defects and a' martetnsite is presented based on the propagating of Shochley partial and half-partial dislocations. A considerable effort has been expended over the past decade in an attempt to elucidate the response of metallic-crystalline solids to the passage of a high velocity shock wave (e.g., smith,' Dieter,2 and zukas3). While it has been possible to obtain relevant information pertaining to the residual defect structures and mechanical properties, there have been few rigorous attempts to draw a direct comparison between these structures and properties. In addition, numerous investigators have recently observed the occurrence of deformation twinning in shock deformed fcc metals (e.g., Nolder and Thomas,4 and Johari and Thomas5), but little attempt has been made to elucidate the mechanisms of formation of these defects. Comparative data for metals deformed by shock-loading and the same metals deformed by more conventional modes of deformation such as cold-reduction by rolling is also generally lacking. The present investigation therefore has the following objectives: 1) to examine the mechanical properties of some explosively shock loaded and cold-rolled fcc metals of low stacking-fault energy as a function of their residual substructures; 2) to present a simple model for the formation twin-faults and related defect structures in the low stack-ing-fault energy materials of interest (70/30 brass, ySFg= 14 ergs per sq cm; and 304 stainless steel, ySF = 21 ergs per sq cm); 3) to make some deductions with regard to the residual characteristics of dislocation and planar defect substructures in cold rolled and shock loaded 70/30 brass and type 304 stainless steel. In particular, it was desirable to characterize the residual hardening effects of particular deformation substructures. I) EXPERIMENTAL PROCEDURE Sheet samples of 70/30 brass (0.005 and 0.15 in. thick; annealed at 659°C for 2 hr) and type 304 stainless steel (0.007 in. thick; annealed 0.25 hr at 1060°C) of nominal compositions shown in Table I were cold-rolled in one direction only to produce reductions in thickness of 15, 30, 45, 60, and 75 pct in the brass; and 5, 15, 25, 35, and 45 pct in the stainless steel. Identical sheet samples in the annealed (unrolled) state were subjected to plane compressive shock waves to various peak pressures ranging from 0 to 400 kbar in the brass and 0 to 425 kbar in the stainless steel; and with a constant peak pressure duration of approximately 2 microseconds. A detailed description of the shock loading technique has been given previously.6 Tensile specimens 1.0 in. in length and 0.125 in. in width were cut from the cold-rolled sheets (tensile axis parallel to the rolling direction), and the shock-loaded sheet specimens. Stress (load)-strain (elongation) measurements on the tensile specimens were made on a Tinius-Olsen load-compensating tensile tester using a strain rate of 2.7 x 10-3 sec-1. Tensile tests were repeated at least twice, giving essentially the same results. Stress relaxation measurements in the preyield region were also made using an initial strain rate of 5.4 x 10-4 sec-1. In addition to tensile and stress relaxation measurements, Vickers microhardness measurements were made on all samples. A total of 100 microhard-ness readings were obtained for each specimen following a light electropolish to ensure uniform surface conditions for all tests. The hardness averages ob-

Jan 1, 1970

By Norman L. Wimmler, H. G. Iverson, S. Ricker, P. E. Oscarson, S. H. Lorain

THIS paper has been prepared with the principal objective of recording the results of the Bureau of Mines exploration of five major clay deposits in the Western Region. It is based mainly on data contained in unpublished Bureau of Mines reports. Acknowledgment is made to the Federal Geological Survey for its cooperative work with the Bureau of Mines, to the various State geological and mining departments, and other State and local agencies. CLAY EXPLORATION BY THE BUREAU OF MINES Much has been written and published on clays and clay deposits relating to their refractory, ceramic, and other qualities but such literature is lacking in analyses of the available alumina content of the clays and provides little indication of their possibilities as a source of alumina. With this new objective in view, a great many of the known clay deposits were reexamined and new ones discovered. The Bureau of Mines made preliminary examination of numerous areas in the western United States. Five of those most favorably indicated were systematically drilled, and in each a large amount of high-alumina clay has been found. These five major projects are Molalla and Hobart Butte, in western Oregon; Cowlitz-Castle Rock, in southwestern Washington; Lone, in California; and the Olson-Troy area in Idaho (Fig. I). Preliminary scout drilling was done in the Stockton deposit at Coeur d'Alene, Idaho; the Whiteware deposit near Lewistown, Mont.; and 13 areas in the Spokane or eastern Washington region, where the most favorably indicated area, known as the Excelsior, is now being drilled more systematically. Preliminary drilling was undertaken in numerous areas adjacent to the major deposits and others more remote. As a result, large additional clay possibilities were found. THE CLAY DEPOSITS The clay deposits under consideration are of the sedimentary or transported types, parts of which have been altered further by the agencies of weathering, ground water, or hydrothermal action. There are extensive deposits of residual clays in northern Idaho and in eastern Washington, but they have been found to be low in the available alumina and to contain much free quartz, mica, and unaltered feldspar. To be of value, they must first be subjected to beneficiation to remove these gangue minerals. The sedimentary clays have been derived largely from the decomposition, erosion, and transportation of granites, gneisses, schists, and basalts. At Molalla, some

Jan 1, 1944

By H. C. Gatos, J. T. A. Pollock

It is well known that the superconducting critical current densities of many alloy superconductors may be increased by cold working and in some cases further enhanced by a short heat treatment. This latter enhancement has been attributed to the redistribution of dislocations into cell-like networks' and to the precipitation of second phase particles,2'3 which act as flux pinning centers. In a manner analogous to dislocation pinning in precipitation hardening alloys,4 it is expected that here also a critical distribution of the pinning centers should result in maximum pinning effect. Concentration inhomogeneities exist in most or all commercial alloys yet there have been only a few attempts made to determine their effect on critical current capacity in the absence of cold working. Sutton and Baker,5 and Kramer and Rhodes6 have found that the complex precipitation processes occurring during the aging of Ti-Nb alloys can result in critical current density enhancement. Livingston7-10 has clearly shown, for lead and indium based alloys, that the distribution of precipitated second phase particles is of critical importance in determining magnetization characteristics. However, these '(soft" alloys age at room temperature and the time involved in specimen preparation prevents metallographic examination in the state in which the superconducting measurements are made. Thus results with such alloys are expected to be biased towards larger precipitates and interpar-ticle spacing. The present study of Ta-Zr alloys was undertaken to examine the influence of second phase precipitation, as controlled by heat treatment, on the critical current capacity of well annealed polycrystalline material. A study of the published phase diagram11 indicated that annealing supersaturated samples containing up to 9 at. pct Zr at suitable temperatures would result in the precipitation of a zirconium-rich second phase. It was MATERIALS AND PROCEDURE The alloys were prepared from spectrochemically pure tantalum and zirconium. Analysis was carried out by the supplier. Major impurities in the tantalum were: 12 pprn of 02, 17 pprn of N2, 19 pprn of C, and less than 10 ppm each of Mo, Nb, Al, Cr, Ni, Si, Ti. The crystal bar zirconium was pure except for the following concentrations: 15 pprn of 02, 17 ppm of C, 23 ppm of Fe, 11 ppm of Cu, and less than 10 pprn each of Al, Ca, N2, Ti, and Sn. Samples were prepared in the form of 8 to 10 g but-tons by arc melting using a nonconsumable electrode on a water-cooled copper hearth in a high purity ar-gon atmosphere. Each button was inverted and re-melted three times to ensure an even distribution of the component elements. The samples were then homogenized at temperatures close to their melting points for 3 days in a vacuum furnace maintained at 5 x 10-7 mm Hg. After this treatment the buttons were cold rolled to sheets approximately 0.020 in. thick from which specimens were cut, 0.040 in, wide and 1 in. long suitable for critical current density (J,) and critical temperature (T,) measurements. These strips were then recrystallized and further grain growth was allowed by an additional vacuum heat treatment at 1800°C for 60 hr. Some second phase precipitation occurred during cooling of the furnace and a solution treatment was necessary to produce single phase supersaturated samples. This treatment was successfully carried out by sealing the samples together with some zirconium chips in quartz tubes under a vacuum of 5 x 10-7 mm Hg, heating at 1000°C for 5 hr and then quenching into water or liquid nitrogen. The samples were then heat treated at either 350" or 550°C and quenched into water or liquid nitrogen. All samples which were heat treated at 350°C were quenched in both cases by cracking the capsules in liquid nitrogen. The samples treated at 550°C were quenched by dropping the capsules into water. Analysis for oxygen in randomly selected samples indicated that the oxygen content was in the range of 175 to 225 ppm. Values of Tc were determined by employing a self-inductance technique. Jc measurements were made at 4.2oK by increasing the direct current through the wire in a perpendicularly applied field until a voltage of 1 pv was detected with a null meter. The risk of resistive heating at the soldered joints during these latter measurements was reduced by first plating the ends of the wires with indium and then soldering to the copper current leads using tin. Metallographic examinations were performed after mechanical polishing of the same samples and etching in a 4H20:3HN03 (conc):lHF(conc) solution.

Jan 1, 1970

By Walter R. Hibbard, Walter L. Finlay

INTRODUCTION THE key feature of the lattice coherency theory of precipitation hardening1-6 is the forced coherence between matrix and precipitate which elastically strains both lattices and is believed to be the major source of strengthening in precipitation hardening. In systems exhibiting age hardening, the atom movements leading to precipitation are not at all extensive and are such as to require the minimum amount of energy to produce the interface; that is, the new lattice forms in such a way as to be as nearly as possible a continuation of the old with a matched, coherent plane at the interface at least during the initiation of the precipitation. The crystallographic sequence whereby regions of the matrix change to the precipitate lattice usually can be resolved into a set of shearing operations.5,6 Conversely, the perhaps novel speculation is made that solution of a second phase is accompanied by shearing movements which are possibly the reverse of the precipitation shearing movements. A basic premise of the investigation reported in this paper is that precipitation and solution shearing movements constitute structural weaknesses which might cooperate with applied stresses to facilitate plastic deformation. Another basic premise of the investigation is that the application of hydrostatic pressure to a precipitation hardening system will significantly alter the degree of disregistry across the matrix-precipitate interface and thereby significantly affect the course of age hardening. Two binary precipitation hardening systems were investigated: 12 pct zinc in aluminum which undergoes transformations, both precipitation and solution, by a simple crystallographic mechanism; and 4 pct copper in aluminum which undergoes a complex transformation in precipitating and dissolving a second phase. The effects of the application of uniaxial tensile creep stress during elevated temperature aging of both systems and of hydrostatic pressure during the elevated temperature aging of 12 pct aluminum-zinc were then investigated. Previous Investigations Van Wert in 1935,7 studied the effect of hydrostatic pressure on the room temperature age hardening of a few precipitation hardening systems. The latter were rather unfortunately selected since none is known to exhibit any marked volume change on aging and the majority were complex commercial alloys the precipitation mechanisms of which are not known. Jenkins, Bucknall and Jenkinson,8 in 1944, applied tensile creep stresses to a complex coppernickel-silicon alloy at various temperatures. The complexity of the alloy and the industrial objective of the work did not permit an appreciable addition to the theoretical understanding of either deformation or precipitation hardening.

Jan 1, 1948

W. H. BASSETT,* Waterbury, Conn. (written discussion ?).-The effect of reducing gases on hot solid copper has been known for many years in the copper industry, and precautions taken to guard against it in the general practice in copper heating and annealing. In view of the statement that Bengough and Hill, in 1910, were the first to suggest the possibility of the formation of gas within the copper itself, it is interesting to note that in Harper's Magazine for April, 1904, an article, "Life and Diseases of Metals," by Professor Heyn, illustrated the effect of reducing gases on copper by a photograph, which is shown in Fig. 1. This he entitled "Copper burst asunder by disease." After referring to the effect of hydrogen on steel, he makes the following remark: "Similar symptoms of poisoning, caused by hydrogen or gases containing hydrogen (as gas for lighting purposes), are apparent in copper when exposed to red heat. Not every kind of .copper is susceptible to this poisoning in equal degree. Copper per-fectly free of cuprous oxide is entirely exempt from poisoning. Most of the various coppers of commerce, however, contain cuprous oxide, formed during the smelting process while exposed to atmospheric influences. In such coppers, containing cuprous oxide, hydrogen causes a terrible disease on the copper being heated red hot. The copper bursts asunder and is permeated by cracks. This disease is practically incurable and can be eradicated by resmelting only. The results work destructively according to the amount of cuprous oxide contained in the copper." It must have been evident to Professor Heyn, as it was to us on reading this article, that the bursting asunder of the copper was clue to the formation of steam. Practical copper heaters have known for many years that it was quite possible to produce blisters, or large gas holes, in the interior of copper plates or bars by heating to a high temperature in reducing gases. These facts, of course, do not detract from the value of the study of the action of hydrogen gas that has been made by Mr. Pilling, but simply illustrate that the practical effect of reducing gases on furnace-refined copper has long been a troublesome factor in the heating or annealing of that metal.

Jan 1, 1919

By G. E. Anderson

The Asientos-Tepezala district is in the north of the State of Aguasca-lientes, about 30 miles north of the city of Aguascalientes, the capital. The district is reached by a standard-gage railway on the west side through the junction, Rincon de Romos, which is on the main line of the National Railways of Mexico from El Paso to Aguscalientes. The terminal is Tepezala. On the east side a narrow gage connects Asientos with the junction, San Gil, on the main line, Asientos to San Luis Potosi. Tepezala on the west side of the Asientos hills is about 2 miles from Asientos on the east side. The area between the two mining centers is separated by a low subdued divide which forms the central part of the hills. The district is in a group of isolated hills surrounded by characteristic bolsón plains. The hills rise above the surrounding plains about 6500 to 10,000 ft.; the highest peak is Alta Mira. The two mining districts lie somewhat upon the flanks of the hills at about the same elevation, 7200 ft. The district is an old one and has been known since early in the 17th Century when the mines were worked by the Franciscan Monks. Their mining operations, which were limited to the oxidized ore above the water level, consisted chiefly in extracting silver from the Santa Francisca vein. To judge from the old workings and the remains of surface plant, the operations were on a large scale. By modern mining operations since about 1900, the various mines of the district have been one of the principal sourees of ore for the smelter located at Aguascalientes. Topography The topographic features of the Asientos hills are largely controlled by the character of the underlying rocks. During the Tertiary period, the entire group of hills was probably covered by extrusive volcanic material in the form of cones and lava flows. The central part of these have since been carried away by erosion, so that remnants have been left along the borders of the hills. These remnants form rather conspicuous peaks,

Jan 1, 1927

The following list comprises the names of those persons who became members during the period May 10, 1916, to June 10, 1916: ARCHIBALD, JOHN CHRISTIE, Min. Engr., Supt. of Cyanide Plant, Guanajuato Reduction Mines, Guanajuato, Mex. BRUNEL, FRANK P., Cons. Min. Engr Mitchell & Brunel, Ajo, Ariz. CALVERT, WILLIAM ROBERT, Cons. Geol. ...225 Kearns Bldg., Salt Lake City, Utah. CHAMPION, J. R., Supt The Yak Mining, Milling & Tunnel Co., Leadville, Colo. CHARLES, LAVERN JOHN, Construction Engr., Elephant Butte Dam, Elephant Butte, N. M. CHASTEL, ANDRE, Min. Engr., Societe Miniere & Metallurgique de Penarroya, 12, Place Vendome, Paris, France. CHRISTIE, WALLACE H., Vice-Pres. and Mgr., Alt. Bert Gold Dredging Co., 604 Mission St., San Francisco, Cal. CLARK, RONALD ..Hardinge Conical Mill Co., 120 Broadway, New York, N. Y.

Jan 7, 1916

By J. Campbell

The hydrostatic tensions in pure metals and long freezing range alloys are evaluated theoretically considering the viscous flow of residual liquid and the general plastic collapse of the casting. The former mechanism operates until the radii of the remaining liquid channels are of the order of 10-3 cm radius, after which the second process limits the attainable negative pressures which range from —1500 to -4200 atm for nickel, aluminum, copper, and iron. In previous reports1'2 the maximum possible hydrostatic tensions developed during solidification have been evaluated employing spherical symmetry. This inevitably involves the concept of totally confined liquid regions, the reality of which has recently been brought into serious doubt3 following observations of the freezing of various transparent materials. Regions of interdendritic liquid which are apparently about to be isolated by the growth of dendrite arms are observed not to be cut off because the advance of the dendrite tips is arrested until the region has completely solidified. Although this may be the result of the very low melting point liquid available at this late stage in freezing, or the result of a higher rate of heat transfer to the dendrite tips because of the acceleration in liquid flow rate near the completion of solidification, this point need not concern us. In this paper an attempt is made to approximate more closely to real conditions; thus the assumption of confined liquid regions is abandoned and cylindrical symmetry adopted. It has also been necessary, therefore, to consider the viscous flow of residual liquid through the remaining channels in the pasty zone. Furthermore, the rather special conditions of spherically symmetric solidification led to extremely high solidification rates and hence unusually high tensile stresses as solidification neared completion; the cylindrical Symmetry appears to yield solidification rates and stresses which are more typical of real castings. The rate of solidification is first considered since this critically affects both the flow of the liquid and the creep of the solid.

Jan 1, 1969

By G. B. Misra

Though resistance to flow offered by mine airways supported with timber sets has been an object of study over the last half century, no accurate relation has yet been established from which prediction of the resistance coefficient of a projected timbered airway can be made. Zenofontowa et al. developed an empirical relation, but this relation has not been found to satisfactorily correlate experimental data obtained by Sales and Hinsley. This led the author to develop a set of simple theoretical relations between the resistance coefficient of timbered airways and the various parameters affecting it, such as the type and spacing of sets as well as the shape and size of members forming the set. Experiments were designed with the help of a laboratory model airway to verify the validity of the relations developed. With the experiments conducted so far with 4, 3 and 1-piece sets of 3.4 x 3.4, 2..5 x 2.5, and 4.5 X 4.5-cm square-section timbers in a 45.8 x 38-cm model airway, the theoretical relations have been shown to hold.

Jan 1, 1972

By W. G. Pfann

Under certain conditions, a molten zone can be made to move through a solid by impressing a stationary temperature gradient across the solid. This phenomenon can be utilized in fabricating semiconductive devices, growing single crystals, joining, boring fine holes in solids, measuring diffusivities in liquids, small scale alloying, and purification. Fundamentals and exemplary applications are outlined. ANEW aspect of the travel of a molten zone through a solid is considered in this paper. Whereas, in previously described zone melting techniques,'-' zones were usually caused to move by changing the position or temperature of a heat source, in the present technique a zone is made to move by impressing a temperature gradient across it. For example, a thin layer of molten A1-Si alloy, sandwiched between two silicon slabs having a temperature gradient normal to the layer, will travel through the hotter slab. One feature of temperature gradient zone melting, as this technique will be called here, is that zones of unusually small dimensions can be maintained. This leads to such diverse uses as have been listed in the abstract. In this paper fundamentals of the movement of a molten zone in a temperature gradient, and some practical applications thereof, are outlined. Assumptions The movement of a molten zone through a solid body of solvent substance in which a temperature gradient exists will be discussed. The length of the zone will be its dimension in the direction of motion. The direction of the temperature gradient will be toward the region of higher temperature. To be considered is a binary or higher order solute-solvent system in which the concentration of solute in the molten zone is sufficient to produce a lowering of the freezing temperature of the solvent which is at least of the order of the temperature range impressed on the charge. While we discuss primarily molten zones in a solid matrix, the principles are applicable to solid or vaporous zones in a solid matrix, a requirement being that the diffusivity in the zone be substantially greater than in the matrix. Diffusion of solute into the surrounding solid will be assumed negligible. In general, its presence will not basically alter the conclusions to be drawn. For illustration, a system represented by the partial constitutional diagram of Fig. la will be discussed, in which k, the distribution coefficient defined in the figure, is constant and less than unity. However, the technique is applicable to any solute- solvent system in which one component lowers the melting point of another component. Movement of a Molten Zone in a Temperature Gradient Consider, in the system AB of Fig. 1, where B is designated the solute and A the solvent, the effect of sandwiching a thin layer of solid B between blocks of solid A and placing the whole in a temperature gradient such that the temperature of the layer is above the lowest melting temperature of the system. Surrounded by an excess of A, the layer will dissolve A, becoming molten, and expand in length." As so- lution of A continues, at both interfaces, the mean solute concentration in the zone will move to the right in Fig. la, until at temperature T, the liquid at the cooler interface reaches the liquidus concentration C,. Solution of A thereupon ceases because the liquid T1 is saturated with A. The liquid at the hotter end of the zone, being at temperature T2, is not saturated with A at concentration C1. Hence solution of A continues there and concentration C2 is approached. A concentration gradient therefore is set up in the zone, causing A to diffuse toward the cool end and B toward the hot end. As a result, the liquid at the cool interface becomes supersaturated and a layer of crystalline A containing concentration kc, of B in solid solution freezes. Since a source of A

Jan 1, 1956