INTRODUCTION BY C. P. SANDBERG. SINCE the discussion On steel rails in America has forcibly drawn attention to the value of chemical analysis, if not as a necessary stipulation, at least as a guide to control the usual mechanical tests, some doubt has been thrown upon the accuracy of the analytical results Obtained by different chemists. To any One having the least acquaintance with chemistry., it is quite clear that if exactly similar results are to be obtained from the same borings of steel, exactly the same methods must be used by the different analysts. Hence the necessity (if complications are to be avoided) of establishing what I may call standard or normal methods, to be used both by the inspectors and by the chemists at the works. Remembering that the application' of chemistry to steel-rail inspection is yet in its infancy, it is of great importance to possess a perfect acquaintance with the best methods in use. Being myself a grateful pupil of Professor Eggertz, of the School of Mines in Sweden, it Occurred to me, two. years ago, that I could not do better than start a laboratory of my. own, and engage One of his pupils, Mr. Troilius, for the purpose of analyzing the steel borings from mechanically-tested rails, so that I might thus Obtain without delay thoroughly accurate determinations. Moreover, in Order to carry on the, operations in perfect accordance with the methods used at the steel works in England and Germany, where I had to control the manufacture, I deemed it desirable to allow Mr. Troilius to go through a course of training at these works; and I gladly seize this opportunity of expressing my grateful acknowledgments to several works in England and in Germany for affording every facility for such an exchange of information as was found necessary in arriving at the best analytical methods to be used.

Jan 1, 1882

By W. A. Backofen, B. C. Wonsiewicz

The Plasticity transition in magnesium was studied by plane-strain compression of single crystals and polycrystalline material at temperatures from about 20" to 307°C. Reduction of single crystals along the c axis was accommodated by twinning on {1011) and retwinning on (10 12}, followed by basal shear in the doubly twinned volume. Deformation in that mode can result in sufficient independent shears for arbitrary shape change. Fracture in c axis compression, below about 100°C, has been related to excessive shear caused by unloading from the stress for {1011} twinning (-50 ksi at 20°C) to that for slip within the twin (-3 ksi); ductility follows from heating because the stress difference is lowered and the twin volume, in which elastic strain energy is dissipated on unloading, is increased. The stress for (1011) twinning is strongly temperature-dependent but not given by a critical resolved shear stress law. The latter is attributed to the influence of stress concentration from prior intersecting shear on nonbasal planes, the former to the temperature dependence of the preliminary slip. THE basic symmetry of hcp crystals has the effect of limiting the number of independent slip systems and making twinning an important deformation mechanism. The general result in wrought polycrystalline aggregates is a more or less sharply developed texture (or preferred orientation) which underlies a strong anisotropy in mechanical behavior. Knowing how the one influences the other is essential background for the use of such materials. Magnesium was of interest in this work because of the unexplained plasticity transition that it undergoes somewhere in the neighborhood of 200°c.''~ At lower temperatures plastic deformation before fracture in polycrystalline material is limited, while at higher temperatures extensive deformation is possible. The transition temperature commonly determines the lower limit of the range in which magnesium is worked. The limited ductility can be traced to a lack of independent crystallographic shears. A minimum of five are required for arbitrary shape change.' Around room temperature, however, slip on all known systems provides only four.' In each case, the slip direction is in the (0001) basal plane so that slip does not allow strain along the c axis. With increasing temperature, more slip occurs on the ( 1011) pyramidal plane and the ( 1010) prism plane but without change in direction.'?' Thus, that development alone cannot explain the transition temperature.

Jan 1, 1968

By H. L. Couch, J. D. Lubahn

In decarburized mild steel, the strain hardening arising from 1/2 pct strain can he partly recovered by subsequent heating, even though re crystallization or grain growth does not occur. This recovery varies from 5 pct in an hour at room temperature to 70 pct at 800°C. The variation with temperature was qualitatively similar to that reported for copper, but occurred at lower temperatures. Except for the initial portion (Bazdschinger effect), the stress-strain curve following recovery can be superimposed on the original curve by shifting it to the left. In other words, the tensile behavior is essentially the same after straining and heating as if there had been less strain and no heating. The importance of this observation in understanding simultaneous deformation and recouery is explained. AN earlier investigation1 on copper showed that strengthening due to strain hardening was augmented by heating at moderate temperatures, but was diminished by heating at higher temperatures, Fig. 1. Auxiliary experiments1 indicated that recovery and strain aging are independent processes, which may proceed simultaneously, and whose effects are additive as indicated in Fig. 1. In order to study recovery by itself, similar tests were made on decarburized mild steel, where strain-aging effects are known2 to be absent. MATERIAL, TESTING PROCEDURE The specimens were made from rimmed, hot-rolled SAE 1020 steel 0.040 in. thick, by stamping out rectangular blanks and end holes, Fig. 2, and pack milling the reduced section. These were wet-hydrogen treated2 for 16 hr at 720°C to remove carbon and nitrogen completely and then heated 1 hr at 850°C in vacuum to stabilize the grain size. Auxiliary ex- periments showed that heating up to 800°C will not cause grain growth. They were prestrained 5 to 7.5 mils per in. using the special grips shown in Fig. 2. Such small strains are less than the "critical" strain for recrystallization and, therefore, will not cause recrystallization, even at high temperature. The recovery treatment after prestraining and before the retesting consisted of heating for 1 hr in wet hydrogen at the desired temperature. In one test, Huggenberger gages were used to define more accurately the loading and unloading curves. Fig. 3 illustrates the creep during the early stages of unloading, the hysteresis due to cold stretching, and removal of hysteresis by heating.3 RESULTS The load-deflection curves had ratner widely differing shapes for different specimens, both before and after the recovery treatment. Some specimens showed perfectly smooth curves, Fig. 4, while others exhibited an inflection more or less suggestive of a yield point (Fig. 4 shows all extreme case). Some curves were much steeper than others; Fig. 5 shows two extremes. Some additional ex-

Jan 1, 1960

By T. G. Decker, A. F. Witt, A. M. Gaudin

The historical development of the concept of contact angle hysteresis is reviewed. The measurements of contact angles reported in literature have all been made under static conditions. For the measurement of dynamic advancing and receding contact angles, four methods are described together with an evaluation of their precision. Three of these methods were adapted from devices already used for the measurement of static contact angles. The fourth method uses a new principle and apparatus and is the most accurate. While the relationship between surface tensions and the contact angle was extablished as early as 1805 by T. Young,' it was only in 1890 that the existence of contact angle hysteresis was reported by Lord Rayleigh. His observations, however, remained almost unnoticed. With the invention of froth flotation, the contact angle and its behavior became the subject of investigation. In 1907, L. Sulman and collaborators investigated the cause of discrepancies between recorded values of contact angles. They found that certain variations existed in most cases, but that definite maximum and minimum values of contact angles are obtainable. The difference between the maximum and the minimum contact angle in a given system was termed "hysteresis" by Sulman. First attempts to explain hysteresis were made by E. Edser. In the following years extensive studies of contact angles in various three-phase systems

Jan 1, 1963

By H. Conrad, E. Stofel

The fracture behavior of 60-deg-oriented sapphire crystals was investigated for both tension and compression. Plastic flow on the basal plane was found to be a factor in reducing the tensile stress required to produce fracture in the temperature RECENT experiments1-' have shown that single crystals of a alumina (sapphire) can deform plastically, particularly at temperatures greater than 1000°C. The effect of this plastic flow on the fracture behavior of sapphire was not established, but range 1100º to 1500ºC. Mechanical twins, both (0001) and (0111) types, were produced by compression in the temperature range 1100" to 1300°C. Cracks propagated more readily along the twin boundaries than in the nontwinned crystal. experiments with other ceramic crystals4'5 have shown that plastic flow can initiate cracks that lead to catastrophic failure. This suggests by analogy that plastic flow might also be an important factor in the fracture of sapphire crystals. A recent experimental investigationS undertaken to determine the mechanism of plastic flow in sapphire provided an opportunity to study the type of fracture produced after various amounts of plastic shear strain. The results of this study of fracture are reported in the present paper. During the course of

Jan 1, 1963

By Edward Jeffrey

THE use of coke in metallurgy, to any important degree, dates from the middle of the 18th century. Its utilization came most opportunely for European civilization. The forests of Europe, except in the most remote and inaccessible regions, had been largely fed, in the form of charcoal, into the smelting furnaces. For a hundred years-the middle of the 17th to the middle of the 18th century-there was a stationary condition of population corresponding to the exhaustion of European forests. This situation, which was particularly evident in Great Britain, was due to the fact that the forests had been depleted and the practical utilization of coke had not begun. The coking industry is essential for our metallurgical industries, which in turn are basal to healthy economic progress. But coke is of great importance, not only on its own account, but for its byproducts, which enter fundamentally into all the arts of peace and war. The dyestuff industry and the manufacture of explosives are intimately connected with one another, as was shown by the recent war. The subject of coking coal, therefore, is well worthy the serious attention both of practical industry and the scientific investigator. The most valuable coking coals, from the metallurgical standpoint, are derived from the coals of highest ranks. Coals, for example, that have a carbon ratio of from 70 to 80 per cent. yield the most valuable coke for the blast furnace. The difficulty of investigating these coals, however, is great, for they are rather friable and delicate and possess a high carbon content, which makes them difficult to manipulate. They present, on account of their high carbon content, a considerable degree of opacity when examined, in thin sections, under the microscope. The tenderness of structure and blackness of such high-grade coking coals as those of Connellsville and the Pocahontas region make them extremely difficult to investigate.

Jan 1, 1925

By Frederic Carter

THERE have been many attempts to prove that platinum was known to the ancients, but since no traces of the metal have been found in the relics of early times, it must be concluded that it had not been known to them. As far as records go, it was actually first discovered in the 16th century in a Spanish mine on the Pinto River in South America; from which source it received its name of Platina del Pinto (little silver from the Pinto). It was more or less of a rarity and was a subject of interest to a few chemists only, until the year 1822 when the metal was first discovered in Russia. In 1819 there had been noticed in the washings of the gold sands of the southern part of the Ural Mountains, grains of a heavy white substance, but it was not until three years later that this substance was found to contain platinum. While at first the amounts of platinum brought from the Urals had been meager, prospecting soon disclosed rich deposits extending over a considerable area, and nuggets from 10 to 20. lb. were by no means rare. This discovery assured to chemists an ample supply of platinum for their crucibles, etc. The ore is now found in various parts of the world but the richest deposits are still found in the Ural Mountains. The platinum of commerce is obtained entirely from alluvial deposits at depths varying from 6 to 40 ft. The sand and gravel of former river beds are subjected to a series of screenings and washings to effect the separation of the ore. Actually, probably all gold-bearing gravel beds of the world contain platinum, and it is more than likely that large quantities of platinum ore have been thrown away with the black sand washings from gold placer deposits. This is especially true of the alluvial deposits of the Pacific Coast in California and Oregon. Platinum ore is usually found in the form of rounded or, flattened grains of "sand," and occasionally in irregular lumps of the size of peas. Large nuggets are very rare. The ore has a metallic luster and is distinguished by its steel gray color, but shows light gray streak when rubbed on a hard white surface; it has a high specific gravity, 16 to 19; is infusible in the hottest blast furnaces, and insoluble in any single acid. Platinum ore is a complex body consisting of the metal in combination with varying proportions of the other members of the platinum group; iridium,

Jan 1, 1928

Total U.S. mineral production reached an estimated $17.8 billion for 1960, 4 pct above 1959 and second only to the record high of $18.1 billion established in 1957. As a group, metals achieved a rise from $1.6 billion in 1959 to $2.0 billion this year, an increase of 28 pct. Similarly the value of nonmetallic production including fuels (i.e., natural gas, petroleum, natural-gas liquids, asphalt and related bitumens, carbon dioxide. anthracite. bituminous and lignite coal, peat, and helium) rose from $15.5 billion in 1959 to approximately $15.8 billion in 1960. However, this 2 pct increase in the total value of non-metallic production was due to an increase in the value of the fuels ($11.8 billion in 1959 to $12.2 billion in 1960) which offset a drop in value of the other nonmetallic minerals ($3.7 billion in 1959 to $3.6 billion in 1960).

Jan 2, 1961

By Charles A. Ashburner

The manufacturing and domestic consumers of anthracite are beginning to realize the fact more fully, that the coal purchased for any one year does not seem to burn so freely, does not fire with so little trouble, and does not last so long as that purchased during other years, or vice versa. Where coals of different sizes, or from different districts, are offered to the trade by the same or competing salesmen, the question suggests itself, which shall we buy ? Among housekeepers, who are the most numerous class of consumers, though on the smallest scale, distinction is seldom recognized among these anthracites. By other consumers the coals are grouped into those which, when burned, will produce either a white or a red ash, special qualities being arbitrarily attached to each. Others, again, know only of three varieties : (1) Those from the WYoming and LacKawanna fields, or the coals shipped from the northernmost basins over the railroads running through northeastern Pennsylvania direct to New York—notably, the Delaware. Lackawanna and Western, Delaware and Hudson, and Erie railways; (2) those shipped by the Lehigh Valley Railroad and the Lehigh and Susqaehanna division of the Philadelphia and Reading Railroad down the Lehigh Valley ; and (3) those shipped over the main line of the Philadelphia and Reading Railroad down the Schuylkill Valley. In special localities, where a favorite coal is largely used, the consumer will speak of one class, composed of his favorite coal, which possibly comes from two or three collieries, with a total aggregate annual production of less than a million tons; and of a second class, composed of the coals from all the other collieries in the anthracite

Jan 1, 1886

By F. R. Hensel

PURE silver and silver-lead alloys have been studied as to their suitability for bearings.1-8 A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materials.† The silver-rich end of the diagram as reported in the literature9-11 was found to be sketchy and it was necessary to carry out considerable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. TEST MATERIALS In the beginning of the work, only fused alloys were investigated. Later, research [TABLE I. Composition of Fused Silver thallium Alloys Tested for Antifriction Properties PERCENTAGE ALLOY No.OF THALLIUM 15330.48 153406 231 HT2.04 2312.10 232 HT3.83Balance 2324.07Silver 233 HT5.86 2336.38 2349.84 234 HT10.07] was carried out on electroplating methods and diffusion processes. In preparing the fused alloys, care was taken to exhaust the toxic fumes caused by the thallium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in. diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr2O7, 8 c.c. H2SO4, and 100 c.c. H2O. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C. show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475°C. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not result in complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1945

By Marcus A. Grossmann

This paper offers for consideration certain somewhat radical modifications in the iron-carbon diagram, these modifications being the result of the presence of notable amounts of alloying elements. When only small amounts of alloys are present, the standard iron-carbon diagram (Fig. 1) can be used with but insignificant changes; when larger amounts of alloys are present, however, it assumes a distinctly altered appearance. No comment is offered for the present except to call attention to the delta area, A4BM, which represents a region of mixtures of austenite and delta iron, just as area A3SP represents mixtures of austenite and alpha iron. Absence of Carbon We may turn at once to the effect of the presence of alloys. It has been found that in the complete absence of carbon, the gamma change will sometimes disappear entirely when sufficient alloying element is

Jan 1, 1927

By Francis J. Dennis

(San Francisco Meeting, October, 1911.) MANY factors govern the value of dredging-ground, and much capital can be wasted by the mistaken policy of contracting for the purchase of property and the installation of machinery before a thorough, examination has been made. To the uninitiated investor the presence of gold is generally the criterion,, and very superficial evidence is necessary to satisfy him as to this point. He considers the comprehensive report of a competent engineer as a wasteful extravagance and cannot understand why the engineer requires so much time and money to ascertain the information on which to base his conclusions, when the promoter can furnish him such pleasing and satisfactory data with but little expenditure of time and money. The uninitiated investor will often optimistically risk capital for purchase and equipment, and not until the venture comes to grief does he learn that the conditions are wholly unsuited for dredging. In many instances, a short preliminary examination by a competent engineer would have disclosed these facts. The mere presence of gold is by no means sufficient; some of the other factors necessary to be ascertained in determining the value of placer-ground for dredging-purposes are : (1) character and distribution of gold, and how much can economically be recovered; (2) character of bedding underlying the gravel, its contour, and whether its gold can be recovered by ordinary dredging-operations; (3) area and depths of gravel, surface contour, over-burden, water-level, proportion of fine material and boulders, and the presence of any material which might interfere with the dredging-operations and the recovery of the gold; (4) water-supply, power available, labor, transportation, and supplies, and cost of these ; (5) climatic condi-tions; (6) title to property, cost and royalties, and legal obstacles to carrying on dredging-operations. A brief reconnaissance may be sufficient to determine that some of the essential conditions for successful dredging are

Apr 1, 1912

By T. Egleston

THE materials containing copper which are refined in the United States, are, for the most part, the native, coppers of Lake Superior. Until quite recently but little pig copper was made for sale, and that came principally from the pure sulphurous ores of New England and the South, and was generally sold to refineries not far from the ore furnaces. A small amount found its way into the market which was produced either as the by-product of the treatment of gold and silver ores, or as the result of the treatment of impure copper ores; but both these grades, on account of the impurities they contained, were looked on with suspicion, and were not sought for. All the grapes of pig copper are sold by the unit of copper contents, a great reduction being made in the price when impurities are present. There are at the present time only three works which treat native copper, the two of the Detroit and Lake Superior Copper Company, and the works of C. G. Hussey & Co., in Pittsburgh. There are a few works which smelt sulphurous ores and refine their pig; besides these there are a few small works where pig copper is refined only. Some of these purchase black copper, refine scrap, or simply refine such grades of ingot copper as are found in the market, but mostly that from Lake; Superior, for the purpose of getting it into such shapes that can be handled commercially to advantage, such as in making large plates or high grades of wire for electrical purposes. A number of such works are situated in the Naugatuek Valley and elsewhere in New England. The recent discovery, of valuable ores in Arizona makes it probable that within a few years the refining of copper in the United States will make great developments. Up to the time of the discovery of the mines on Lake Superior, only a very small quantity of native copper had ever been found, not sufficient to justify the erection of works for its special treatment. It had, besides, never been found in very Large masses, so that the discovery of great-blocks of it presented serious difficulties, not only in mining it,† but in bringing it into a merchantable condition. It seemed a very simple process to melt these large masses, * Road at the Lake Superior Meeting, August, 1880. †Transactions American Institute Mining Engineers, vol. vi, page 2S2.

Jan 1, 1881

By E. P. Abrahamson II

The effect of transition element binary solid-solution additions upon the recrystallization temperature of vanadium has been investigated. Cr, Fe, Co, Ni, Mo, Ru, Rh, Os, and IY lower the recrystallization temperature, while Ti, Mn, Zr, Cb, Pd, Hf, Ta, W, Re, and Pt raise it. The majority of elements have their greatest effect in less than 0.15 at. pet. Both the rate of change of recrystallization temperature with atomic percent solute and the limit of initial linearity are found to Correlate with the free atom grozdnd state outer electron configuration of the sollte element. THE work of Abrahamson and Grant1 and Abraham-son and Blakeney2 has shown that the solute's elec- tron configuration appears to be a prime determinant of both brittle-to-ductile transition and recrystallization temperature in dilute binary alloys. It has also been shown by Abrahamson3 that the limit of linearity, i.e., the limit of initial linear change of recrystallization temperature with atomic percent solute, is also a function of the electron configuration of the solute in iron base alloys. Because of the systematic nature of the solute electron configuration correlation, it is to be expected that some systematic variation might be observed upon changing the solvent. Thus, this study of recrystallization in vanadium base alloys is the first of a series aimed at defining the role played by the electron configuration of solute in determining the recrystallization characteristics of dilute transitional alloys. PROCEDURE All alloys were made using 99.8 pct V containing 0.011 C, 0.024 N, 0.08 0, 0.006 H, 0.035 Ta, and

Jan 1, 1962

By H. A. Bright, H. C. Vacher, J. G. Thompson

The methods employed for the determination of oxides and oxygen in ferrous materials may be roughly classed in two groups, "wet" methods and "hot" methods, the first group including the iodine, electrolytic, mercuric chloride, hydrochloric acid, nitric acid, and chlorine methods; the second group including the vacuum-fusion and hydrogen-reduction methods. The wet methods depend upon preferential solubility in a selected medium to separate the metallic portion of the sample from the oxygen-containing constituents. Subsequent analysis of the insoluble residue permits the isolation and separate determination of individual oxides and compounds. The hot methods depend upon the reduction of the oxide constituents of the sample by means of carbon or hydrogen at elevated temperatures. With the exception of the recently developed fractional vacuum-fusion method, the hot methods do not identify individual oxides and compounds but yield only a single value representing the sum of the oxygen contents of several or all of the oxide constituents present. With such diversity in the principles and aims of the different groups, it is not surprising that concordance of results by different methods has usually been difficult to obtain. The present cooperative attempt to define more rigorously than has been possible heretofore the accuracy and limits of usefulness of the various methods, originated in correspondence between Dr. John Johnston, Director of Research of the United States Steel Corporation, and other interested metallurgists. The plan was, briefly, to submit identical samples to a number of laboratories for analysis by different methods and to collate the results of these analyses. The project was endorsed by the Iron and Steel Division of the American Institute of Mining and Metallurgical Engineers at the annual meeting in February, 1933, and has been conducted under the joint sponsorship of the Iron and Steel Division and the National Bureau of Standards. The latter organization undertook

Jan 1, 1937

By D. J. Jr. McAdam

RESULTS of investigation of corrosion-fatigue of metals at the U. S. Naval Engineering Experiment Station have been presented by the author in four papers. 1,2,3,4 In those papers references were given to the work of Haigh in 1917.5 The investigation at Annapolis included a variety of ferrous and non-ferrous alloys. The experiments showed that even slight corrosion simultaneous with fatigue may cause failure at stresses far below the ordinary endurance limit. The experiments also showed that, for most metals, severe stressless corrosion prior to fatigue is much less damaging than even slight corrosion simultaneous with fatigue. The term "corrosion-fatigue" was restricted to mean the simultaneous action of corrosion and fatigue. The combined effect of corrosion followed by fatigue was called "prior-corrosion fatigue." A stress-cycle graph representing corrosion-fatigue is a curve approaching a horizontal asymptote, the ordinate of which may be called a "corrosion-fatigue limit." To avoid confusion in later discussion, the term "endurance limit" will be restricted to mean the fatigue limit obtained by tests in air with specimens as free as possible from stress concentration and from corrosion. The endurance limit as thus obtained presumably represents an inherent property of the metal.

Jan 1, 1929

By William D. Klopp

A study was conducted of the tensile and creep properties of are-melted and electron-beam-melted tungsten over the temperature range 2250° to 4140°F. The tensile and creep strengths vary with pain size, the finer -grained materials being stronger. The activation energy for transient creep at 2250° to 3500°F is 95,000 cal per (g)(mole), while that for steady creep at 3300o to 4000°F is 141,000 cal per (g)(mole). At 2875o to 3300°F the apparent activation energy for steady creep decreased with decreasing temperature. It is suggested that cross slip is rate controlling during transient creep, while dislocation climb is rate controlling during steady creep above 3300° F. ALTHOUGH considerable data have been generated on the high-temperature tensile properties of powder-metallurgy tungsten,1 relative few data have been published on the properties of are-melted2 or electron-beam melted tungsten.3 Furthermore, the available data show a fairly large amount of scatter at high temperatures. The effects of structure and purity have not yet been defined, aside from observations that high-purity electron-beam (EB)-melted tungsten3 and single-crystal-plasma-flame tungsten4 are weaker than less pure powder-metallurgy tungsten. The creep behavior of powder-metallurgy tungsten has been studied, but no data are available on the creep behavior of tungsten consolidated by melting. Green5 found that powder-metallurgy tungsten exhibited linear creep at 4082° to 5072°F with an activation energy of 160,000 cal per (g) (mole). The similarity of this activation energy to that of 153,000 cal per (g)(mole) for volume self-diffusion6 suggests that recovery of strain hardening by dislocation climb is rate controlling in this temperature range. In studies at 4800°F, Sutherland and Klopp7 concluded that grain size significantly affected the creep behavior of commercial powder-metallurgy materials. This grain-size effect was suggested by sherby,8 although the opposite relation had been reported for aluminum.' The purpose of the present study was twofold: first, to provide baseline data on high-temperature tensile and creep properties of are-melted and EB-melted tungsten for concurrent tungsten alloy studies, and, second, to determine the phenomenolo-gical effects of structural and purity variables on the high - temperature mechanical properties of tungsten. EXPERIMENTAL The are-melted tungsten materials were prepared by melting sintered 1-1/4-in.-diam electrodes into 2-1/2-in.-diam by 5-in.-long ingots. The are-melting facility has been described previously.' Eight ingots were melted, machined, and hot-extruded at

Jan 1, 1965

By William Kelly

THE objeet of this paper is to describe the electric equipment at the iron-ore mines of Penn Iron Mining Co., Vulcan, Mich. and of Republic Iron Co., Republic, Mich.; to give the result's of tests; and to discuss the methods in use from an operating as well as from an efficiency standpoint. Electricity was introduced at the Penn mines for pumping, hoisting, and compressing air in the spring of 1907, upon the completion of a hydro-electric plant built by that company on the Menominee river about 4 miles from the mines. This plant was described in a paper1 presented before the Lake Superior Mining Institute. A paper2 presented at a meeting of the same Institute describes some of the operating features, and the safety devices of the electric hoist at the Curry shaft were briefly described in the Proceedings of the First Co-operative Safety Congress held under the auspices of the Association of Iron and Steel Electrical Engineers at Milwaukee, Wis., Sept. 30 to Oct. 5, 1912.

Jan 2, 1914

By O. C. Ralston, William C. Hunter

DUring experimental study on the separation of a zinc concentrate from the heavy sulfide ores of Jerome, Ariz., a great deal of attention has been given to proper activation of the sphalerite content of the ore. The sphalerite at Jerome contains enough iron to class it as a marmatite, as picked specimens have only about 60 per cent. zinc, whereas pure zinc sulfide contains 67 per cent. zinc. This marmatite in large pieces is black in color, but in dry powdered state is brown. A flotation froth made from it has a silvery black luster in comparison with a brassy luster caused by chalcopyrite which occurs in the same ores. The sample used in most of the experiments described below consisted of about 3000 Ib. of diamond-drill core from the zinc-bearing orebodies of the United Verde mine, and had the following analysis: Per Cent. Per Cent. Oz. peR Ton Cu............... 0.695 Al2O3............ 0.83 Ag................. 1.30 Zn............... 6.17 S................ 43.35 Au................ 0.02 Fe...............36.23 CaO............. 0.46 SiO2............. 9.27 Mineralogically, this analysis is calculated to the following, which is in agreement with the microscopic examination: Per Cent. Per Cent. Chalcopyrite................... 2.0 Schist........................... 3.2 Marmatite..................... 10.32 Quartz........................... 8.2 Pyrite........................ 73.0 Calcite.......................... 0.9 All samples were ground in a laboratory ball mill in order to leave about 3 per cent. on a 200-mesh sieve, fine grinding being essential to liberate the minerals in the ore. Most of the Jerome ores are so intimately crystallized that reasonably complete unlocking by grinding does not take place until 800 mesh is approached. Therefore, the 200-mesh grind adopted contains a considerable amount of locked mineral grains, but not so much as to render impossible the preparation of commercial grades of concentrate.

Jan 1, 1930

By R. Woodward Moore

A graphical method of analyzing the data obtained from shallow earth-resistivity depth tests is presented. The method is based upon empirical results and has no theoretical basis. The usual apparent resistivity-electrode spacing curve is used together with a cumulative resistivity-electrode spacing curve plotted on the same sheet. The greatly reduced scale required for plotting the cumulative values of resistivity together with the effect of the summation of the individual resistivity values serves to minimize the effect of purely local surface anomalies and inadvertent errors of measurement. The point of intersection of tangents or straight lines drawn to intersect at zones of maximum curvature in the cumulative curve indicates the depth to the underlying material. Numerous figures are presented in which data from published reports and from recent field studies are analyzed and the results compared with actual depths established by borings or with depth values obtained by the use of theoretical methods of analysis. Smoothly rounded curves of apparent resistivity such as are often obtained in the field, and which have been a serious drawback to attempts to analyze the data empirically heretofore, appear to be susceptible to rather accurate analysis by the method described. The method is best suited to analyses involving shallow two-layer formations. It has been applied successfully, however, in analyzing the data obtained from tests made over shallow three-layer formations. As with most empirical methods, its chief advantage is its simplicity and ease of application. There have been published many papers that discuss the interpretation of data obtained from earth-resistivity tests when using the four-terminal method of electrode spacing developed by Wenner.' The majority of these have dealt with theoretical analyses for two-layer and three-layer formations. Some sets of "master curves" have been presented for use in analyzing field data to determine the depth to the first and possibly the second horizon below the earth's surface. Although practically all of these theoretical methods of analysis have appeared to have particular merit and some have been used successfully in practice, they have been found to be of little value where the local conditions surrounding the test failed to conform to those assumed in the theory. In certain fields, particularly in civil engineering, relatively shallow explorations are often involved and geophysical methods of test must compete with the direct methods of exploration ordinarily used. Only when it can be demonstrated that geophysical methods of test can materially reduce the time and cost of a given exploration project will the civil engineer abandon direct methods in favor of the interpretations of geophysical exploration data. Empirical methods of analyzing earth-resistivity data have been used in many instances in the past. Such methods have been employed for a number of years by the Public Roads Administration in research work relative to the application of

Jan 1, 1946