By M. Soltanieh

The liquidus surface? and tie-lines in the nickel-cobalt-sulphur ternary system have been determined between 1<273-1573 K. The experiments were conducted by equlibrating the liquid sulphide with the metallic alloy phase. The liquid sulphide phase was sampled and chemically analyzed. The alloy was analyzed by electrol} microprobe. Combining the present results with the.avai1abl~ literature data, the thermodynamic properties of this system were calculated.

Jan 1, 1998

By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Yi Wang, Xiaohui Fan

"The mineralization behaviors of typical fluxes are studied by investigating the microstructures with optical microscope. The results show that the reactions begin with between iron ore and lime, limestone with small particle to form primary liquid. Then coarse limestone, dolomite and serpentine take part in reaction under the action of primary liquid. Limestone is the easiest to mineralization, next dolomite, and the last is serpentine. The higher basicity and smaller fluxes size favor the mineralization process of dolomite and serpentine.IntroductionThe purposes of adding fluxes into sintering are that:(1) to increase the basicity of sinter, so as to reduce even eliminate addition fluxes into BF(blast furnace) and decrease the coke ratio of BF[1,2]. (2) to decrease the melting point of sintering mixture to ensure sintering can be carried out at a lower temperature and reduce the energy consumption. (3) to improve the qualities of sinter by forming binding phase with iron ore fines [3].Flux is another significant component for sinter besides iron ore, especially for high basicity sinter[4]. The proportion of flux is usually higher than 10% in sinter mixture(excluding return mine).There were many reports about the influence of the flux types on sintering, such as limestone, dolomite, lime and so on[5-7]. It is very important to choose suitable fluxes for iron ore sintering. Although the effect of flux size on sintering also has been researched, the mineralization behaviors of the fluxes in the sintering process has not been illuminated. The paper will study the mineralization behavior of fluxes in sintering."

Jan 1, 2011

By Donna Guillen, Matthew Lehar, Sebastian Freund, Jennifer Jackson, Helge Klockow

"Research and development is currently underway to design an Organic Rankine Cycle (ORC) system with the evaporator placed directly in the hot exhaust stream produced by a gas turbine (GT). ORCs can be used to generate electricity from heat that would otherwise be wasted, thus producing carbon-free energy. In conventional ORC configurations, an intermediate oil loop is used to separate the hot gas from the flammable working fluid. The goal of this research effort is to improve cycle efficiency and cost by eliminating the pumps, heat exchangers and all other added cost and complexity of the additional heat transfer loop by developing an evaporator that resides in the waste heat stream. Direct evaporation – although simpler and less expensive to implement than indirect evaporation of the working fluid – has historically been avoided due to a number of technical challenges imposed by the limitations of the working fluid. The high temperature of the hot exhaust gas may cause decomposition of the organic working fluid and safety is a major concern due to the high flammability of some of these working fluids. The research team has addressed these challenges and developed a new direct evaporator design that can reduce the ORC system cost by up to 15%, enabling the rapid adoption of ORCs for waste heat recovery. The ORC system is intended to integrate with the GT either as a retrofit or to be marketed as a single package, thus maintaining the manufacturer’s warranty.IntroductionWaste heat from turbines and engines used in industrial applications along with waste heat from industrial processes are exceptionally abundant sources of energy. If even a fraction of this waste heat could be economically converted to useful electricity, it would have a tangible and very positive impact on the economic health, energy consumption, and carbon emissions in the U.S. manufacturing sector. Land-based gas turbines are used in a broad range of applications to produce both shaft and electrical power. Most commonly known for generating electricity either as peaking units or as base load units, they are also used to directly drive pumps, compressors or other machinery requiring shaft power. Simple cycle gas turbines have the advantage of a short startup time relative to coal-fired and nuclear units, however, they incur a significant penalty on their efficiency. Large frame gas turbines usually are combined with bottoming steam-based Rankine cycles to increase the overall efficiency of the system and thereby improve their cost performance. Small-frame gas turbines with exhaust temperatures around 500°C could in principle benefit from steam bottoming cycles, but rarely use them in practice because of the high capital cost of the steam system. Particularly for base load small frame gas turbines, akin to those used in pipeline applications, an increase in efficiency is highly desirable."

Jan 1, 2011

By Lv Guozhi, Niu Liping, Liu Yan, Zhang Zhiqi, He Jicheng, Zhang Ting’an, Dou Zhihe

"CuCr alloy can be extensively used as contact materials in integrated circuit, electrodes, electric contact and high strength conductor. We proposed thermit reduction-electroslag remelting method of preparing the large scale CuCr alloy. But there are pores and oxide inclusions in CuCr alloy prepared by thermit reduction process. This paper studied mainly the effects of ratio of reactant and additive on the inclusion type and their occurrences in CuCr alloy. The slags and CuCr alloy were characterized respectively by XRD and SEM. The results show that when the additive is Na3AlF6, the slag consist of Al2O3 and Cr. When the additive is CaF2, the slag consist of Al2O3, Cr, CaF2 and CaAl4O7. The inclusions in CuCr alloy are mainly Al2O3 and pores which disperse in Cu-rich zone and Cu-Cr phase interface. When 5% CaF2 and 5% KClO3 are added, there are fewer pores and inclusions, and the more better microstructure.1 IntroduceCuCr alloy is the contact terminal material with an eximious properties[1,2], which gradually replaces CuBi alloy becoming the first choice for contact terminal material in the medium and high power vacuum switch after the 1970s. The traditional preparation methods of CuCr alloy mainly contain powder metallurgy, infiltration process and vacuum electric arc melting methods. But the above methods exist some shortcomings, such as poor product quality, high cost of production, processes complex ect[3-9]. CuCr alloy is made by the thermit reduction self-propagating method, which uses CuO, Cr2O3 and Al as raw material to get the high-temperature melt, and then casts to manufacture CuCr alloy ingot, which response equation follows as:"

Jan 1, 2012

By Alwin Frei, Aldo Steinfeld, Peter G. Loutzenhiser, Enrico Guglielmini

"Using concentrated solar radiation as the energy source of high-temperature process heat, the carbothermal reductions of Al2O3 to Al and SiO2 to Si were examined thermodynamically and demonstrated experimentally at vacuum pressures. Reducing the system pressure favors Al(g) and Si(g) formation, enabling their vacuum distillation and avoiding contamination by carbides and/or oxycarbides. Exploratory experimentation in a solar reactor was performed with mixtures of charcoal with alumina and silica in the ranges of 1300-2000 K and 1997–2263 K, respectively, at 10-3 bar by direct exposure to concentrated thermal radiation. Distilled samples contained up to 19 wt% of Al in Al-Al2O3 mixtures and 79 wt% of Si in Si-SiO2 mixtures. When the reducing agent is derived from a biomass source, the solar-driven carbothermal processes are CO2 neutral.IntroductionMetallurgical extractive processes for producing Al1-2 from Al2O3 and Si3-6 from SiO2 are characterized by their high specific energy consumption and concomitant emissions. Alternatively, concentrated solar energy can be used as a high-temperature heat source to drive the carbothermal reductions and, thus, avoid greenhouse gas emissions and other pollutants derived from fossil-fuel-based processes7-12. When the reducing agent is biomass charcoal, the solar-driven carbothermal reduction is CO2 neutral. The carbothermal reductions of Al2O3 and SiO2 are represented by the simplified overall stoichiometric reactions:"

Jan 1, 2011

By V. V. Satya Prasad, A. Sambasiva Rao

Electroslag melting technologies have recently been developed for recycling light scrap of valuable metals and alloys such as superalloys and oxygen free high conductivity (OFHC) copper at Defence Metallurgical Research Laboratory (DMRL), Hyderabad. Conventionally, electroslag melting processes use consumable electrodes. Because of the difficulty in compaction of scrap into a consumable electrode of satisfactory quality, non-consumable electrodes such as graphite and water-cooled copper have been designed. Electroslag remelting using a water-cooled non-consumable electrode was developed to melt scrap of a nickel base superalloy. Sound ingots with smooth surface finish and properties comparable to vacuum melted superalloys could. be obtained from scrap using this process. A modified electroslag crucible melting process using graphite crucible and graphite electrode was developed for recycling OFHC copper scrap. Copper ingots with less than 10 ppm oxygen and electrical conductivity"" 100% IACS could be produced. The same process was also utilized to produce copper-based alloys such as copper-chromium and copper-titanium starting from copper scrap.

Jan 1, 2000

By R. Cavanagh

Studies relating to the fixation of sulfur by reaction of 4 to 8 mm diameter cylinders of calcined limestone or dolomite with high strength sulfur dioxide in the temperature range 880°C to 1020°C were undertaken. Dolomites are far superior in sulfate capacity and reactivity than dense limestones even at high strength SO2. The sulfation reaction was first order with respect to SO2 concentration below 100 percent. Zero reaction rate at 100 percent SO2 concentration indicates that sulfate was the exclusive reaction product and that sulfite had no role in the reaction. At relatively low SO2 concentrations gaseous diffusion through the reaction product layer has a marked effect on the rate. As SO2 concentrations were increased up to 100 percent more complex rate controlling mechanisms unfold. By sectioning partially reacted dolomitic limestone pellets a moving interface was observed. Reaction ceased because of pore plugging for dense non-porous limestones at 30% conversion. With dolomitic material virtually complete sulfation of the calcium was observed. S.E.M. analysis showed that the average atom ratio Ca:S was 1.01, thus supporting the argument that little if any of the magnesium was sulfated.

Jan 1, 1996

By Batric Pesic

Reactions of metallic iron were studied in several different aqueous solution systems: water, medium salt solution used for the growth of T ferrooxidans, ferric iron solution and solution containing T ferrooxidans. Each system was studied under abiotic and biotic conditions in the presence of T ferrooxidans and as a function of pH, particle size of iron powder, temperature, ferrous and ferric iron concentrations. It was found that metallic iron reacts with water differently than does with ferric iron in water. Surprisingly, T ferrooxidans were non-functional in the dissolution of metallic iron. Also, the reactions of metallic iron with pure water were indistinguishable from the reactions with water containing medium salts for bacterial growth. The reactions with ferric iron were also independent of medium culture compounds. The mechanisms of metallic iron reactions with ferric ions are different from the mechanisms of metallic iron reactions with water.

Jan 1, 2001

By R. P. King

The essential features of an image analysis system for the measurement of mineral liberation are described. Good procedures for image acquisition and image processing prior to image analysis are defined. The basic stereological methods for the measurement of volume fraction, surface area per unit volume, particle size distribution and liberation spectra are given. The appropriate methods for fractal correction when measuring perimeters of irregular features and for frame correction when measuring linear intercepts are developed. Practically useful and accurate procedures for the stereological correction of particle size and liberation distribution methods are given.

Jan 1, 1995

By Debbie Marshall

Nickel and cobalt in lateritic ores can be extracted by either a hydrometallurgical or a pyrometallurgical route. The high-iron limonitic fraction of a deposit is best processed&apos; hydrometallurgically while the magnesium-rich transitional and saprolitic fractions are more suited for pyrometallurgical processing. During hydrometallurgical processing, it may be attractive, for economic reasons, to blend the limonitic component with transitional and saprolitic ores, which contain higher nickel levels. However, blending increases the concentration of magnesium in the feed, leading to increased acid demands. The decision on how much ore to process then becomes an economic one. Ore samples with different magnesium contents were prepared for the leach test program by blending limonitic and transitional ores. The ore samples were slurried in seawater and tested in the Falconbridge Hydrometallurgical Pilot Plant. As expected, acid consumption increased with increasing magnesium content of the ore. For target extractions of 95% nickel and 92% cobalt, the required residual free acid concentration increased from 30 g/L at 1.7% magnesium to 50 g/L at 2.7% magnesium. When the magnesium content was raised to 3.8% and 4.6% in subsequent pilot plant testing, the final free acid requirements did not increase beyond what was observed at 2.7% magnesium. Thus, the cut-off ore composition to maximize nickel units and minimize acid requirements is between 1.7- 2.7% magnesium. Keywords: high pressure acid leaching, laterites, magnesium

Jan 1, 2004

By Anna Wasilkowska

The study concentrates on the effects exerted by microstructure, deformation history and uniaxial stress conditions (temperature, stress state, strain rate) on the mechanical properties offerritic TRIP-aided steels for automotive applications. In low-alloyed TRIP-steels it is quite difficult to separate the effect of the austenite to martensite phase transformation from the influence of the ferritic matrix contributing to the yield stress and uniform elongation. Investigation of transformation kinetics of retained austenite as a function of the deformation temperature show that using the parameter k to characterize the retained austenite stability allows to identify regious of different temperature sensitivity separated by a transition temperature of 10±5°C. The observed low strain-rate sensitivity of the flow stress is an intrinsic property of the ferritix matrix and points to defomtation governed by slip. The ultimate tensile strength is much stronger affected by temperature than the yield stress. The influence of the temperature on the elongation is complex, because of the heating of the specimens by 60-l20°C at moderate and high strain rates. The increase of the total strain can be understood in terms of thermal softening of the ferrite. On the other hand, the steep increase of the stress during dynamic testing is an effect of accommodated elastic and plastic strains in the matrix. The strain- hardening exponent is dependent on the conditions imposed during testing. The martensite transfomtation rate is lower and the critical stress for martensite nucleation is much higher under compression compared to tensile loading. In secondary tensile tests, the yield stress increases steeply, and the ultimate tensile strength and the total elongation depend linearly on the amount of pre-straining. The results confirm that in the range of 8=10-4 s-l the TRIP-effect governs room temperature plasticity. Keywords: TRIP-steels, mechanical properties, strain rate sensitivity, temperature sensitivity, austenite stability

Jan 1, 2003

By G. B. Harris

Much has been written over the past decade concerning the disposal of arsenic from metallurgical processes. In Canada, there are proposed regulations which would classify arsenic in the Primary Group of twenty one persistent, toxic pollutants to be banned or phased out. Since many nickel and cobalt ores, not to mention those of copper, gold and uranium, contain significant amounts of arsenic, it is pertinent to assess the current state-of-the-art of its disposal. The literature is reviewed, and it is demonstrated that from a purely chemical point of view, the family of ferric arsenates largely immobilize arsenic. There is clear evidence from laboratory studies that both crystalline ferric arsenate (scorodite) and amorphous ferric arsenates in which the molar Fe/As ratio is at least three (Fe/As = 3) have very low arsenic solubility; plant data are given to support this. The debate over the long term stability of these compounds continues however; the evidence presented for long term stability and for compound breakdown is critically reviewed in the light? of the recent structural studies, and the role of base metals in these compounds evaluated. Finally, conclusions are drawn as to the viability of a purely chemical process for the long term disposal of arsenic from metallurgical processes.

Jan 1, 1993

By Mokka Rao, Asdrubal Serrano

"A mathematical model is developed which describes the movement of the minerals present where the vertical and angular velocities are related with the different operative parameters involved in the process of separation of silica from iron ore, which permit maximise the capacity of the spirals to obtain major productivity. The process is realised in two steps, of the rough dressing and other cleaning. Through the results obtained for chemical analysis of the final products of each spiral and the equation of movement of particles, it is proved the applicatibility and efficiency of mathematical model to operating parameters of the spiral. Moreover, it is determined though the recuperation of the final products of quality in the use spiral HC 1870 and HG 8/7. INTRODUCTIONThere is prospetive of increasing the production the iron ore in agreement with the demand of siderurgical proyects united with the external demand of quality 40 million tons per year. The Ferrominera de Orinoco Company is experimenting two types of modem spirals, Humprey (HC 1870) and Reichart (HG 8/7) which have limited capacity. For this reason this investigation designed a mathematical model with which larger units can be designed for increasing the capacity of the spiral."

Jan 1, 1999

By J. van Driel

NOx is a growing concern for acid plant operators due to recent legislation reducing the allowable stack limits, as well as continually more stringent requirements for product acid quality. NOx also causes a major problem during maintenance as NOx rich acid residues fume following exposure to moisture in the air. Until recently, the solution for NOx related issues was to treat the symptom, rather than the cause. NOx in product acid was treated using chemicals and the NOx in the plant stack was generally left untreated. As part of an environmentally driven change in concentrates, Budel Zink installed the first gas phase NOx destruction process to be incorporated into a commercial scale acid plant. Nitrogen oxides contained in the process gas are reduced selectively with ammonia over a catalyst to form nitrogen and water. As a result, the NOx reduction is in agreement with the permit requirements.

Jan 1, 2002

By Wayne Bell, Matthew Andriese, Shuqian Xie, Jiann-Yang Hwang, Zhiwei Peng

"Pyrolyzed carbons are generally known as good microwave absorbers and their dielectric properties still remain to be fully explored. In the present study the dielectric properties and dielectric polarization-relaxation phenomenon of a typical activated carbon was investigated. The experimental results indicate the complex permittivity is highly dependent on temperature and frequency. The decrease of permittivity with increasing temperature from room temperature to ~100 °C is probably ascribed to the release of the water vapor adsorbed on the surface of activated carbon, and the variations of permittivity with temperatures between 100 °C and 450 °C in the frequency range of 300 MHz to 3000 MHz are mainly attributed to the decreased relaxation time of dielectric polarization.IntroductionPyrolyzed carbons have been identified as excellent microwave absorbers owing to their high dielectric and electrical loss under microwave irradiations. Among them, activated carbon continues to attract more and more attention from researchers. Due to its special physical properties, the production, modification and regeneration of activated carbon with the assistance of microwave have been widely studied over the last few decades [1-6]. However, only few attempts have been applied to explore the dielectric properties of such materials due to the complexity and variability of their organic precursors and activation processes [7,8]. In order to shed a light on this problem, a typical sample, Norit® A Supra USP powdered activated carbon, was adopted to perform dielectric characterization, which may provide useful information for its wide application in the fields of purification, energy (hydrogen) storage and so on."

Jan 1, 2011

By Cesar Garban

The samples of the washings are characterized of the ore for physical, chemical and metalurgical properties for representivity. the optimum values are determined for the recuperation of gold of the washings of the gold ore from the zone El Callao, Venezuela by acidic solutions of thiourea of the following parameters: Ph , contact time, composition of the liquid mixture, ratio of solid to liquid, grade of liberation, in an apparatus designed for contacting solid powder of the mineral with liquid solution of thiourea mantained in suspension by bubles of compressed air. The experimental results showed that the velocity of lixivation in primier time of (20) minutes is rapid and practically 2/3 part of the reaction is completed. For experimental design of parameters, the optimum conditions of recuperation of gold determind in this experimental investigation are:

Jan 1, 1999

By Chang-Young Choi

Korea Zinc commenced zinc production in 1978 with a capacity of 50,000 tpa. Since then, continuous investments have been made and resulted in Korea Zinc now being the biggest zinc and lead producer in the world. In the course of increasing zinc production capacity, the company management realized that the company needed a lead smelter to prevent the solid waste disposal problems by treating the lead containing solid waste. This paper begins by briefly stating the objectives and the roles of the lead smelter at Onsan. It describes the QSL process and the TSL process, and further extends the description of the TSL process, through which harmless inert solid waste could be produced for secure final disposal. It is also mentioned that the TSL process plays an important role in the integration of zinc and lead production. Throughout the paper, a positive attitude in handling the environmental issues in the non-ferrous smelting industry is emphasized. Finally, a solution for the solid waste disposal problem in the zinc and lead industry is proposed, with which the environmental issues can be an opportunity rather than a crisis. The current operation at Ousan suggests the future direction of the non-ferrous smelting technology that all of the zinc and lead producers should pursue.

Jan 1, 2003

By Bao Xiancheng

Jinlong&apos;s copper flash smelting process started up in April 1997. In the early days of production, lots of equipment and process problems were encountered. But, through continuous improvements in equipment and operation, the designed productivity was reached two years later and the smelting operation has been greatly upgraded since then. After more than 4 yew of production, we have made great achievements, such as increasing the flash furnace availability, significant improvements in operation control, optimization of concentrate burner&apos;s structure and operation, and smooth operation of the whole smelter. This paper outlines Jinlong&apos;s operational achievements made after commissioning, and discusses problems that were encountered and their countermeasures. Operational experience is also summarized

Jan 1, 2002

The direct removal of lead ions from D2EHPA-kerosene using metallic zinc as the reducing agent was evaluated. The electrochemical process, called galvanic stripping, is a potential alternative stripping technique when standard chemical methods are not adequate. Four parameters found to be important in the rate of lead removal were studied in a factorially designed experiment. The variable evaluated included D2EHPA concentration, temperature, zinc surface area and solution agitation. Temperature and surface area were found to be the most significant, while agitation and D2EHPA concentration had less influence on the reaction. An activation energy of 22.5 Kcal/mole was calculated indicating a chemically-controlled process. The reaction was also sensitive to the concentration of oxygen in the system. The zinc required was considerably in excess of stoichiometry, possibly due to the dissolution and redeposition of lead: In general, the results were encouraging and demonstrated that lead impurities could be removed from D2EHPA using cementation type reactions.

Jan 1, 1995

By G. Cifuentes

The kinetics of the electrolytic oxidation of cyanide to cyanate on PbO2-coated stainless steel anodes have been studied by both experimental and theoretical means. The anodes were based on 316 steel and performed in a satisfactory fashion. The pH of the studied KCN solutions exhibited a constant value about 11. Values for all the kinetic parameters have been determined and a mechanism for the studied reaction is proposed.

Jan 1, 1999