By Jorge Alberto Soares Tenório, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Franco Alves Lavacchini Ramunno

"The traditional process for recovery of metals from waste electric and electronic equipment (WEEE) usually involves pyrometallurgical processing. However, the application of this technology to processing waste printed circuit boards (WPCBs) might lead to the formation of dioxins and furans, due to thermal degradation of flame-retardants and polymeric resins present in the board substrate. Therefore, this paper proposes a hydrometallurgical route for the recovery of copper. The acid leaching behavior of copper has been investigated at three different temperatures (25°C, 50°C and 75°C) with and without the addition of an oxidizing agent (hydrogen peroxide - H202). The dissolution kinetics for acid copper leaching was calculated based on chemical analysis by ICP-OES (Inductively Coupled Plasma - Optical Emission Spectroscopy). At 50°C with 1 mol/L H2S04 added 10 mL H202 (30%) each half hour under pulp density of 1 g I 10 mL, 100% of copper was extracted after 3 hours. The dissolution kinetics of copper with H2SO4-H2O 2 followed 1 - (1 - X)113 =Ket, i.e. chemically controlled reaction model.IntroductionThe information regarding the generation of waste electric and electronic equipment (WEEE) are still difficult to obtain because the estimates should take into consideration the historical production and sale of various products and the rate at which they reach the end of their life cycle, whose duration depends on the behavior of consumers [1]. Thus, the estimated overall WEEE generation varies between 25 and 50 million tons each year, which corresponds to more than 5% of all municipal waste generated [2], and this amount will increase at a rate of 3 to 5% per year, approximately three times faster than other individual types of waste [3].Printed circuit boards (PCBs) are essential parts of electric and electronic equipment (EEE), being found in virtually all electronic products, as well as in weapons systems [4]. A PCB is a basic component, which consists of a board where copper tracks are deposited. While the board behaves as an electrical insulator, the tracks connect electrically the various components attached to the board [ 5]. In addition to glass fibers, paper and resins, the PCBs contain significant amounts of metals, such as copper, iron, nickel, lead, stain, silver, gold and palladium [6]. In general, the weight fraction of metal is around 28% and the remainder of the boards is composed of plastic (19%), bromine (as flame retardant - 4%) and ceramic material (49%) [7]."

Jan 1, 2014

By Toshio Suzuki, Machiko Ode, Won Tae Kim, Seong Gyoon Kim

"The Ostwald ripening and growth and coarsening of the secondary dendrite arm are studied using a phase-field model. The phase-field parameters are obtained at a thin interface limit proposed by Kim et al. In Ostwald ripening analysis, the difference of the concentration due ·to· the curvature effect is shown. The third power of the average particle radius Rav is proportional to time and the ripening constant shows a good agreement with the value by Deppers et al. The particle radii distribution shows the transition behavior to attain a self-similar stationary shape. The growth and coarsening behavior of the secondary dendrite arm is also analyzed using a phase-field model. The estimated arm spacing and its dependence on time are in good agreements with experimental data.IntroductionThe ripening or coarsening process controls the microstructure during the late stage of solidification. The ripening phenomena are recognized firstly by the Ostwald [1]. The first quantitative analysis for the Ostwald ripening in the limit of vanishing solid fraction was provided by Lifshitz, Slyozov and Wagner (LSW) [2,3]. In their study, that the mean radius grows proportional to the cubic root of time and the size distribution of precipitations shows a ""self-similar"" shape are shown. Most of the studies for the Ostwald ripening confirm or predict these two general rules above. In case of finite solid fraction, the general rules are observed but the ripening constant is larger and the self-similar shape is wider than the LSW prediction respectively [4-6]. To analyze· the high solid fraction system, the theories that consider the solute field correlation are proposed [4,7-8]. In the theory, however, since the particle is treated as the point, the effect of the concentration field deviation from the monopole field should be taken into account. Recently the numerical simulation, in which not only diffusive transportation of solute but also convection effect is considered, has been done using a phase-field model [9]."

Jan 1, 2000

By Malti Goel

"Ferrous and non-ferrous metals industries are source of both direct and indirect greenhouse gas (GHG) emissions. Metal industry accounted for 29.7% of the total GHG emitted from the Indian industry sector in 2007. Aluminum is second largest contributor after steel. Indian Aluminum industry has been growing and is adopting several effective measures for better efficiencies through process change and waste utilization. Improvement in the energy efficiency can form the basis of monitoring reduction in emissions. Under the National Action Plan on Climate Change 2008, National Mission for Enhanced Energy Efficiency (NMEEE) aims to upscale the efforts to unlock the market for energy efficiency improvement on a public private partnership (PPP) basis. For a transition to low carbon economy industry is undertaking voluntary measures through scientific and technological innovations both in upstream and downstream sectors. In this paper an attempt is made to overview recent developments in Indian Aluminum industry as well as summarize scientific & technological challenges and prospects.IntroductionAluminum plays a vital role in industrial development. It is a substitute for different type of materials ranging from wood to copper and steel. The aluminum industry has high energy consumption and high contribution to greenhouse gases from carbon dioxide and perfluorocarbons (PFCs) emissions. It is estimated that CO2 equivalent burden of aluminum industry is about 1% of total anthropogenic emissions. The anticipated world growth rate is 3.5% for aluminum demand. Through measures to reduce both direct and indirect CO2 emissions, electricity consumption was reduced from 25 kWh / kg of Aluminum in 1998 to 15 kWh / kg of Aluminum produced in 2008. It is targeted to further reduce it to 10.8 kWh. Aluminum industry is also responsible to about 60% of all PFC emissions. The PFC emissions are harmful to environment, accumulate in surrounding vegetation and contaminate. Efforts to reduce PFC emissions from aluminum industry started early and reduced to 0.5-1 kg / tonne in 1990 [1] from 12-15 kg / tonne in 1940. Since 1990s to 2000 it further reduced to 0.2 -0.4 kg / tonne as seen in Fig. 1. The Global Aluminum Sustainable Development Initiative (GADSI), targets perfluorocarbon (PFC) specific emissions reduction of 80% for 2010 relative to 1990."

Jan 1, 2011

By Zhigang Liang

A carbon free precast block was prepared by using high-alumina fused corundum as aggregate and fused magnesia, and ultra-fine Al2O3 and ultra-fine SiO2 powders as matrix materials. A small linear expansion for the precast block was achieved through spinel formation from the reaction of MgO with Al2O3. The precast block showed a lower apparent porosity, higher hot modulus of rupture and better slag corrosion resistance compared to the traditional Al2O3-MgO-C brick. Moreover, the practical application of the precast block to the ladle lining proved it to possess a better thermal insulation which could effectively prevent the temperature drop of molten steel during the refining process. It can be predicted that the carbon free precast block could possibly be accepted as a new type of ladle lining material for the production of low-carbon and ultra-low-carbon steel.

Jan 1, 2009

By Naiyi Li, Henry Hu, Alfred Yu

"In the past few years, various squeeze cast aluminum components have been developed and successfully implemented in various vehicles by the automotive industry because of their superior engineering performance. However, fundamental understanding of the formation of air gap during squeeze casting processes is still very limited despite of its significant influence on the extent of heat transfer between the casting and mould. In this paper, a mathematical model has been developed to simulate phenomena of air gap between the casting and mold' during squeeze casting of aluminum alloys. The model considers the effect of process parameters such as applied pressures and mold temperatures on the events of air gap formation. The predication indicates that the occurrence of highly enhanced heat transfer in squeeze casting of aluminum alloys primarily results from the presence of excess applied pressures.IntroductionA number of squeeze cast Al components has been developed and used in mass-produced vehicles in the past few years, such as steering knuckles, Road wheel, Engine Block etc. This is attributed to their superior engineering performance. In squeeze casting, the cooling rate can be increased by applying high pressure during solidification which results in the noted refinement in the micro structure scale leading to better casting properties. However, the excessive pressure increased interfacial heat transfer coefficient is affected during the solidification by air gap formation and die surface condition etc., which is believed to increase thermal resistance at the casting/die interface [l - 4]."

Jan 1, 2004

By He De-wen

Based on the principle of life cycle assessment (LCA), municipal solid waste management (MSWM) was analyzed by life cycle inventory method. According to the system expansion and substitution method, the content and frame of life cycle analysis is summarized and applied to municipal solid waste. On the basic of feasibility research of life cycle analysis on MSWM, the paper put forwards complete and concrete ?three changes? measures under life cycle analysis on MSWM. Some aims of MSWM can be achieved under above conditions of LCA on MSWM: to improve the current system efficiency of MSWM; to enhance the serve quality of MSWM, to increase recycle garbage from MSW; to reduce waste amount and reach minimization and innocuity aim of MSWM; to help the departments of MSWM to get over all difficulties to realize their ideal goals.

Jan 1, 2009

By Bin Du

In recent years, concurrent product design and process is gaining popularity and will become a norm of the industry of the future. Forging has been a critical manufacturing process for production of components with superior tensile strength, toughness and grain flow. This paper describes an expen system which is being developed for forging die design and forging process analysis in concurrent engineering environment. Rules and guidelines pertaining to forgeability are formulated and incorporated into the knowledge-base in building the system. The system is built using an object-oriented paradigm. The object-oriented approach and hierarchical rule structure paradigm are briefly discussed. Finite element analysis packages (ALPID-2D) were incorporated into the program to give the simulation result of the forging process. The system can automatically produce a competent design and recommend a set of processing parameters for a given product. The designer can modify the design according to the result of the simulation.

Jan 1, 1992

By Xiangwen Wang

Electrochemical measurements associated with the electrowinning of lead metal from concentrated brine (NaCI) - lead chloride (PbCI,) electrolytes at temperatures in the range 328 to 353°K (55 - 80°C) were conducted. The electrodeposition of lead metal onto a lead rotating-disk electrode may be described by the electrodic reaction: {PbCl 4 2 + 2e- = Pb° + 4Cl-} The deposition-overpotential requirements are low (approximately 41mV per decade of current density - Am+), with a corresponding high exchange current (approximately 0.018 A.cm2). The diffusion coefficient of the electroactive PbC142- species in a 3.5 NaCl electrolyte at 353°K was insensitive to the total PbCI, concentration (0.01 to 0.1M), and its value was found to be (1.21*0.1)~10-5 cm2Is with a temperature-sensitivity coefficient (E,/R) of approximately 1.98x103K-1 (328OK(T<353OK).

Jan 1, 1993

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

By Ivan Imris

The common problem of new and conventional technology of copper production is the copper losses in the slags, which may be divided into mechanical and physico-chemical losses. In the first group can be included particles of mechanically entrained or floated unsedimented matte particles which coexist with slag. On the other hand, the physico-chemical losses are caused by solubility of copper in the slag in the form of sulphide and oxide. The copper losses in the slags from different processes has been predicted by calculation from thermodynamic data and compared with those determined by microscopic examination and quantitative electron microprobe analysis. Depending on the forms of copper losses in the slag the reduction of copper losses in the slag or the slag cleaning process could be suggested.

Jan 1, 2003

By Manjie Li, Mingrui Yang, Haijun Peng, Shuxing Qiu, Wei Liu, Shengfu Zhang

It is important to produce and utilize highly reactive coke in order to reduce the energy consumption and CO2 emissions through improving shaft efficiency in blast furnace. The present study aimed to investigate the transformation of iron minerals and properties of iron coke (the coke mixed iron ore fines). Along with the increase of iron ore fines, cold strength displayed a slight downtrend and the pore structure wasn’t inferred to be a major factor affected the properties of iron coke. During carbonization, the majority of mixed iron oxides were reduced to metallic iron by CO and H2 and the degree of metallization achieved to approximately 75%. Nevertheless, produced metallic iron was oxidized by pure CO2 during gasification. Iron coke reactivity index (ICRI) was obviously enhanced and the iron coke strength after reaction (ICSR) drastically decreases, which were also significantly influenced by crystal structure of carbon.

Jan 1, 2015

By Y. K. Rao

Relatively pure crystalline lead sulfate (PbSO4) can be produced by chemical vapor transport from an impure source such as the lead-acid battery paste or the roast-ore-leach-residue from a hy¬drometallurgical process-route. In a closed-reactor, transport of matter is induced by a tempera¬ture-gradient and the steady-state transfer rate can be calculated using the data on the standard free energies of formation for the species present and the pertinent binary diffusion coefficients. The present work focusses on chemical vapor transport in a tubular reactor (1.4-cm inner diameter x 10-cm long) with the source- and deposition-ends held at 850°C (T,) and 750°C (Td), respectively; PbC12(g) is the &apos;solvent&apos; or &apos;transport agent&apos; and NiSO4(s) placed in the source-zone -serves to maintain a sufficiently high S0,-potential such that the stability of the lead sulfate species is ensured. For the purposes of analysis, the gas-phase in the reactor is assumed to consist of eight species: H2O, PbC12, SO3, SO2. O2 HO, C12, and PbC14. The reaction between C12(g) and PbSO4(s) in the high-temperature source-zone produces PbCl2, SO2, and 02; four more reaction-equilibria in the same zone yield other species. In the low-temperature deposition-zone, reaction equilibrium involving PbC12, H2O, and SO, leads to the nucleation and growth of PbSO4 crystals; three other reaction-equilibria occur in this zone. By employing the virtual equilibrium state for the end-zones and coupling it to the Stefan-Maxwell diffusion equations for each of the gas species, the respective partial pressures for these, in the source- and deposition-zones, are computed at steady-state. From these data, the molar fluxes of PbCl2. PbCl4, and so forth, are determined. Allowing for the transport-enhancing effects of thermal convection, the net transport rate of lead (or PbSO4) is duly calculated for specified initial conditions. The predicted rates show very good agreement with measured rate data reported in the literature [ V. Plies, T. Kohlmann and R. Gruehn: Z. anorg. allg. Chem, 568, 62 (1989)

Jan 1, 1995

"Mechanical alloying (MA) synthesizing technology and thennohydrogen processing (THP) were utilized to produce nanocrystalline Ti-MMC's reinforced by TiB intermetallic compound by using TiH2-B powder mixtures. Powders MA'ed up to 8 hours were examined by X-ray diffraction and SEM study. All MA'ed powders afterwards were HIP'ed at 700, 800 and 950EC for 1 hour. Detailed XRD, SEM and TEM study of the samples were carried out to determine the structure and micrography of the Ti-TiB MMC material processed by MA+THP approach followed by HIP'ing at high temperatures.IntroductionThe fiber reinforced titanium base composites [1,2] which possess a great resistance to high temperature have been investigated. In these studies fibers of C and SiC were used as reinforcing materials. However, these fibers react with Ti-matrix at elevated temperature resulting in product formation at the interface between the matrix and the fiber. Because of the chemical reactions, strength of the product MMC material diminishes.In conventional techniques of whisker reinforced composite material production, the mixtures of matrix metal powders and dispersed fibers are consolidated by hot pressing, HIP and/or hot extrusion. These techniques, however, have some shortcomings. Hard and brittle fibers could be broken during mixing cycle of the processing. Consolidation techniques could also be the cause for fiber breakdown. Attaining of the uniform dispersion of fibers into the metal matrix is not an easy process. The chemical reactions at elevated temperature exposures in the interface between the matrix material and fiber reinforcement cause product formations leading to poor mechanical properties."

Jan 1, 1998

By Sasa Djokic

In developed countries, the difference between demanded and produced quantities of non-ferrous and rare metals are compensated by secondary raw materials recycling and reprocessing of by-products from both ferrous and non-ferrous extractive metallurgy. Utilization of non-ferrous and rare metals from the metallic secondary raw materials is very significant, both for recovery of the metal value and contribution to the environment protection. Similar to all non-developed countries, the extractive metallurgy in Serbia was based on available natural resources and not so strict environment protection regulations, which was either insufficient or completely absent. Today, Serbia is at the beginning of development of efficient and economical technical and technological solutions in order to ?ecologize? technogenic systems by waste materials, secondary raw materials and degraded soils regeneration (by recycling and revitalization). Several metallurgical technogenic systems in Serbia, together with secondary raw materials classification according to their potentiality for metal extraction by using the existing technologies and expected economical and ecological effects of recycling, are discussed in this paper.

Jan 1, 2005

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Yoichi Takeda

Copper solubility in Si02-CaO-FeOx slag equilibrated with copper matte in 10% S02 atmosphere at 1573K was estimated. Essential parameters are activity coefficients of copper oxide and sulfide, oxygen and sulfur potentials and activity of copper in the slag-matte system. A large number of experiments provide proper parameters to calculate copper solubility in slag. A classical thermodynamic model postulating CUOO.5 and CuSo.; molecules assists in estimating copper solubility in slag. Additions of Si02 and CaO reduce copper solubility almost in any condition. Copper loss, that is function copper solubility and slag volume, in the silica saturated Si02-FeOx binary slag is minimally equilibrated with less than 66% copper matte while copper loss in the 50% FeOx-SiOrCaO ternary slag saturated with 2CaOSi02 is minimally equilibrated with over 66% copper matte. This slag composition has potential for continuous copper converting, direct copper production or high-grade matte production.

Jan 1, 2003

By William Petruk

"Heap leaching is a developing technology for recovering native gold and electrum from low grade deposits and from tailings. Recovery depends on permeability of the rock and ore minerals, size of particles in the heap, and ore textures that influence exposure of gold grains to cyanide solutions. These ore textures include gold-bearing veinlets and microveinlets along fractures and microfractures, gold grains in porous minerals and rocks, and gold graim. occurring along grain boundaries of other minerals. On the other hand, small encapsulated gold grains arc not likely tote exposed even with fine grinding. Most gold grains that occtir along grain boundaries of other minerals can be exposed with a moderate to fine grind, but the. resulting material will be too fine-grained to be permeable in a heap. Such finely ground ore, as well as tailings from flotation operations, can however be prepared for heap leaching by agglomerating the material into porous briquettes. Oxidized and weathered zones above. orebodies are frequently amenable to heap leaching because the gold-bearing pyrite and arsenopyrite have become permeable by conversion to porous iron oxides and ferric oxyhydroxides. A review of ore textures in several types of gold deposits suggests that:(1) the gold in vein deposits would gtmerally be amenable to heap leaching of both oxidized ores and fresh non-refractory ores,(2) the gold in Carlin-type deposits and in volcanogenic massive sulfide deposits is not likely to be amenable to heap leaching fresh ore, but oxidized zones above the orebodies are generally amenable to cyanidation, and(3) the gold in porphyry copper-gold deposits and in Witwatersrand-type deposits would likely be amenable to heap leaching of both fresh and oxidized ores but with high cyanide consumption."

Jan 1, 1997

By M. Neises, M. Roeb, C. Sattler, S. Stenger

"A two-step thermo-chemical cycle process has been developed and investigated. It is based on metal oxide redox pair systems, which can split carbon dioxide as well as water molecules by extracting oxygen atoms and reversibly incorporating them into their lattice. If concentrated solar radiation is used as the heat source, a promising method exists to produce synthesis gas from water and CO2. An easy way of operation is gained by the combination of a ceramic substrate as the absorber structure, which can be heated to high temperatures with concentrated solar radiation, and of a metal oxide coating which is capable to carry out the redox reactions. The performance and kinetics of a ferrite based redox material coated on ceramic substrates were investigated in a laboratory set-up. CO2 could be reduced with significant conversions. In addition, several side reactions were observed like the formation of carbon and like the Boudouard reaction.IntroductionThe search for alternative energy carriers and for processes able to reuse carbon dioxide stimulates the research for sustainable routes of alternative fuel production. In the scope of this search thermo-chemical processes combined with sources of concentrated solar energy have become more and more attractive. Ideally, the only raw materials for such processes are water (H2O) and carbon dioxide (CO2) enabling not only a process free of emissions, but also allow to reduce emissions of other processes by reusing CO2 to provide synthesis gas, which itself can be applied to produce chemical commodities or even better synthetic fuels like methanol or petrol.In contrast to the direct splitting of those raw materials, thermochemical cycles split water and CO2 in several steps and enable hydrogen (H2) and carbon monoxide (CO) generation at temperatures controllable by today’s technical equipment. One of the most interesting thermochemical cycles is a two-step process using metal oxide based redox systems. During the first step of this cycle (the regeneration step) the metal oxide is reduced setting some of its lattice oxygen free according to reaction (1). In the next step (the splitting) the reduced and activated material is oxidised by withdrawing oxygen from water and CO2 and at the same time hydrogen and CO is set free according to reactions (2a) and (2b) respectively."

Jan 1, 2011

By Florian Aurelian, Mihai Popescu

"It will be tested four types of “geochemical barriers”. All those mixtures were contacted with mine waters containing uranium, radium and heavy metals. The loading capacity was determined. The optimum mixture was determined and its efficiency was tested within an uranium areal, where the activity was stopped. It was determined the possibility to recover the radioactive elements and the heavy metals from the investigated barriers.IntroductionThe paper presents the results concerning the performances of some “geochemical barriers” used for the decontamination of mine waters from uranium mining sites, which were tested in lab and in situ.ExperimentalThe research activity was carried out in lab and on the site.In the lab a module was constructed in order to follow up the uptake capacity of the “permeable reactive geochemical barriers” used to remove the radiolelements from the contaminated waters originated from the uranium mining industry. The barriers, which were used, are made of cheap natural materials, which can be easily got (wood chips, peat coal, sawdust, iron span, steel and zeolitic tuff). The following types of barriers were tested:•, 1st barrier: peat coal, sawdust, zeolite on weight ratio of 1/1/1;•, 2nd barrier: bentonite, sand, wood chips, peat coal on weight ratio of 1/1/1/1;•, 3rd barrier: iron span, steel, sawdust, peat coal on weight ratio of 2/1/1;•, 4th barrier: iron span, steel, sand, firry wood chips on weight ratio of 1/1/1.Lab researches concerning the uranium uptake capacity of the above described “reactive barriers” pointed out that the 3rd mixture (iron span, steel, sawdust, peat coal on a ratio of 2/1/1) didn’t reach the maximum uranium uptake capacity not even after eleven contact stages (the uptake capacity being of 70.6 mg U/ kg of mixture) and the mixture of peat coal, sawdust and zeolite has an uranium uptake capacity of 26.6 mg U/kg of mixture and becomes saturated after four contact stages.Each one of the components involved in physical-chemical processes of sorption, reduction and precipitation, will determine the diminution of uranium and other metals contents upstream the permeable reactive barrier."

Jan 1, 2008

By J. Y. Hwang

The relationship between coal characterization and physical cleaning has not been well understood due to the complex nature of coal. Therefore, it is difficult to apply the results of coal characterization to predict and evaluate the performance of a physical separation (e.g. flotation). Eight U.S. bituminous coals were analyzed and studied petrographically in conjunction with washability and flotation tests. The results show that grindability correlates to ash and fixed carbon contents; liberation determined directly by petrographic techniques is close to liberation determined indirectly by washability; and an ideal separation efficiency can be determined by measuring the inertinite content and the washability separation efficiency using a heavy liquid with a density of 1.4. The ideal separation efficiency was attained for most coals by packed column flotation. The ideal separation efficiency can be used for comparing process technologies and process parameters.

Jan 1, 1988