Search Documents

By R. S. Dean

The commercial production of electrolytic manganese on a small scale commenced in 1939. The writer made a short report on the progress of production and utilization in Mining and Metallurgy for January 1941. Progress during the last two years, naturally, has been more rapid. In June 1940, Congressman (now Senator) Scrugham presented a proposal to Congress for an appropriation authorizing erection of a pilot plant for " the production of metallic manganese by electrolytic or other means." As a result of this, a pilot plant, having a capacity of a few hundred pounds per day was built at Boulder City, Nev. Subsequent appropriations permitted expansion of the plant to about a ton per day. Much has been learned in this plant about electrolytic manganese, and the product even in its small way has found war uses of considerable importance. Meanwhile, the Knoxville plant of the Electro Manganese Corporation, the sole commercial producer, was expanded to about 4 tons per day to supply needed material for the war program. Other proposals for commercial plants have not been favorably received by the War Production Board. The Bureau reported on one such proposal by the American Alloys and Chemical Corporation. Practice at BouldeR City The present practice, as carried out at Boulder City, which is being described in more detail in a current paper by the Bureau staff at Boulder City, starts with a manganese dioxide ore containing about 20 per cent manganese. Currently this ore comes from the Three Kids deposit near Las Vegas. The steps for the production of electrolytic manganese, in general, are as follows: 1. The manganese in the ore is reduced to MnO. 2. The MnO is dissolved from the ore in spent electrolyte, which contains about 38 to 47 grams per liter of free sulphuric acid, 135 grams per liter of ammonium sulphate, and 10 to 12 grams per liter of Mn as sulphate. In the leaching step the manganese is built back up to 32 to 36 grams per liter of Mn as sulphate; the pH is adjusted to neutral by means of gaseous ammonia and passed through thickeners. 3. The electrolyte is purified by adding H2S, which precipitates the heavy metals. After filtering, ferrous sulphate is added to the solution and oxidized with air and the solution is filtered and clarified on a precoat filter. 4. The purified catholyte is electrolyzed in a diaphragm cell using stainless-steel cathodes and lead-silver anodes. The current density is about 45 amp. per sq. ft. Current efficiencies of 60 to 65 per cent are regularly obtained.

Jan 1, 1944

By H. H. Podgurski, F. N. Davis

In silver alloys containing less than 0.2 wt pet Cu. the reaction 9 + 1/2 0, = CuO(s) was found to proceed to equilibrium between 700o and 808oC. From measurements of the equilibrium dissociation pressures of the CuO at several temperatures, the differential heat of solution and the activity coeflicients for copper in silver were calculated. These values were found to be in reasonable agreement with those calculated from data appearing in the literature. A metastable "copper oxide" with an atom ratio of oxygen to copper as high as 1.7 was formed by internal oxidation at 300°C of these same dilute Ag-Cu alloys. No anomalous behavior was noted in the temperature dependence of oxygen solubility in silver. The solubility minima between 300" and 800°C reported several years ago can be accounted for, at least in part, by reactions with trace impurities, such as copper. Cold-worked siloer exhibits an enhanced permeability to oxygen. THIS investigation was undertaken because of our interest in interactions between solute and lattice defects in metals. The reason for the choice of the O-Ag system for study is the anomaly in the solubility of oxygen in silver reported by Steacie and Johnson1 in 1926, specifically that isobars between 100 and 800 Torr show solubility minima at 400°C. It was also claimed that the copper impurity in the silver was not responsible for the minima. Recently, Eichenauer and Müller2 proposed that surface adsorption might have been responsible for this solubility anomaly, but no adsorption isotherms are available to check the pressure and temperature dependence observed at the low temperatures. Surface-tension measurements on silver made by Buttner, Funk, and udin3 suggest that a considerable fraction of a monolayer of oxygen exists on silver at 922°C and at an oxygen pressure of 150 Torr. To account for the pressure sensitivity reported by Steacie and Johnson1 at 300°C, the oxygen bound to the surface at 922°C cannot be considered relevant; the existence of a surface layer at 300°C characterized by a lower energy of binding would be required to explain the effect. All of our attempts to detect an interaction of this type with surface sites have failed. In this investigation we have not been able to associate the dissolution of oxygen in silver with a dislocation interaction. Evidently, severely cold-worked silver does not contain a sufficient number of trapping -sites for oxygen. Indeed, our work shows that oxidation of trace impurities in the silver was probably responsible for Steacie and Johnson's results. In addition, we have been able to establish the nature of the reaction with copper impurity in silver by thermodynamic considerations. EXPERIMENTAL PROCEDURE Measurements of both the internal oxidation rates and the solubility were made volumetric ally in a system equipped with a gas burette, a mercury manometer, a McLeod Gage, and a mass spectrometer. The silver and the silver-alloy samples were protected from contamination by mercury vapor from our pressure gages by suitably placed refrigerated (-78°C) traps. Silica reaction vessels were employed for experiments performed above 500°C. Spectroscopically pure gases were used in this investigation. The highest-purity silver used in the solubility measurements was 99.999 pet. By chemical analysis 2 ppm of Cu were found in this silver. The two Ag-Cu alloys used in this research were made up to 0.14 and 0.15 wt pet Cu starting with 99.999 pet Ag. An unexpected source of error was discovered in the course of the work. At temperatures near 800°C silver distilled from the hot silica reaction tubes into cooler regions of our system. Although the weight loss of silver from the sample was not important in itself, oxygen was being consumed by the silver distilled into the cooler part of the system to form a stable oxide phase from which the oxygen was not recovered. In a separate experiment conducted to determine the necessary correction, losses between 0.2 and 0.3 cu cm (stp) of 0, in 24 hr were measured at 810°C. On the assumption that the flux of silver from the vessel to form Ag2O de-

Jan 1, 1964

By Robert Maddin, Neng-Kuan Chen

THE (001) planes have been reported as the cleavage planes in body-centered cubic metals such as alpha-iron and tungsten.' However, in molybdenum, which is also body-centered cubic, experimental X-ray evidence indicating a similar cleavage plane still seems lacking. Tsien and Chow" observed microscopically in the extension at around 1000°C of molybdenum single crystalline wires 0.25 mm in diam that the fracture plane seemed to be parallel to the operative slip plane, which appeared to be (110) at that temperature. Zapffe' pointed out from fractographic study of polycrystalline molybdenum that "although the transgranular pattern is characteristically non-crystallographic, patterns occasionally reveal {100} cleavage." This has been generally assumed to be the case at ordinary temperatures. In the present experiments, a single crystal of Fansteel molybdenum, Vs in. diam x 2 in. long, prepared by the methods described by Chen, Maddin, and Pond" was fractured at room temperature by bending. The fracture surface appeared to be quite similar to the cleavage surface of zinc and was crys-tallographic. A back-reflection Laue photogram was made using 35 kv copper white radiation; the X-ray

Jan 1, 1952

By J. V. Gluck, Ping-Wang Chiang

The tellurium-rich region of the Sb-TI-Te ternary system was investigated by means of DTA, metallo-graphic, X-ray, and electron beam microprobe techniques on the sections Sb2Te3-T12Te3, SbTlTe2-Te, SbT1Te2-Sb2Te3, and SbTlTe2-T12Te3. The phase behavior of this region is summarized in terms of four ternary invariant reactions and a schematic reaction diagram is suggested. Isopleths for the sections SbT1Te2-Sb2Te3, Sb2Te,-T12Te3, and SbTlTe2-Te were constructed, and a schematic diagram of the projections of the liquidus lines and invariant planes is presented. No evidence was found to support the existence of the ternary compound "SbTlTe3", or pseudo-binary behavior of the section T12Te3-Sb2Te3, as reported by Borisova and Efremova. Electrical conductivity, Seebeck coefficient, and thermal conductivity measurements were made at room temperature on fully annealed samples. 1 HE phase relationships in chalcogenides are often complex and difficult to resolve, particularly since the approach to equilibrium is a rather slow process. For example, the phase diagram of the T1-Te binary system was in doubt until clarified by Rabenau et al.,1 the phase fields at compositions near Bi2Te3 in the Bi-Te binary system have only recently been satisfactorily elucidated by Glatz,2 and there may still be some question as to the extent of the Sb2Te3 field in the Sb-Te system.3-5 In ternary systems, the existence of the compound "AgFeTe2" was the subject of a number of conflicting reports6-8 and the stoichiometry of the composition "AgSbTe2" was in doubt for a period of time.9 Recently, questions have arisen regarding the existence of certain compounds in the ternary systems Bi-Tl-Te10-14 and Sb-Tl-Te.15 The impetus for studies of these latter systems stemmed from the report of Borisova et a1.10 of a congruently melting ternary compound, "BiTlTe3", which apparently had extremely favorable thermoelectric properties for room-temperature cooling applications. Attempts by other investigators to produce the compound or confirm the transport properties proved to be unsuccessful.12-14 Recently, Chiang and Gluck14 reported studies of the phase relations in the tellurium-rich region of the Bi-T1-Te system which indicated that the section T12Te3-Bi2Te3 was not pseudobinary as suggested by Borisova et a1.10 The contention of Spitzer and sykes12 was supported that the composition "BiT1Te3" was multiphase, with the primary constituent actually being BiTlTe2, a compound whose existence has been well demonstrated.16,17 The investigation reported in the present paper was prompted by a later report of Borisova and Efremova15 on a similar study of the section T12Te3-Sb2Te3 from the Sb-T1-Te system. They also claimed this section to be pseudobinary, and that a ternary compound "SbTlTe," was formed peritectically. Some "preliminary" crystallographic data were given for the compound and thermoelectric transport properties were presented. In view of the questions concerning the behavior of the Bi-T1-Te system and the existence of the compound "BiT1Te3" it was suspected that the Sb-T1-Te system might behave in a similar fashion, particularly in light of the known existence of a compound SbT1Te2, iso-structural with BiT1Te2.17 Consequently, an investigation was undertaken to clarify the phase relationships in the tellurium-rich region of the Sb-T1-Te system. It is the purpose of this paper to present the results of this study, including a representation of the phase relations, isopleths for various composition sections, and the determination of some phase compositions and transport properties. EXPERIMENTAL PROCEDURES Commercially available high-purity (99.999+ pct) elements, purchased from the American Smelting and Refining Co., were used for the sample preparation. All samples were made from thoroughly mixed powders of previously prepared master alloys: SbTlTe2, Te, Sb2Te3, and T12Te3. Stoichiometric quantities of the constituents for each 10-g sample were weighed into a specially cleaned fused silica tube and sealed under a vacuum of better than 5 x 10-5 torr. The sealed constituents were fused and reacted at 650° to 750°C for at least 4 hr under continuous agitation in a "rocking" furnace, and the resulting product was air-cooled. The tube was opened and the sample was ground to a powder. A portion of the powder was rebottled in a DTA tube under vacuum, and the rest of the material was similarly resealed in a separate tube, re-fused in the rocking furnace, and again cooled to make the ingots for electrical and microstructural studies. All samples were subjected to further heat treatments as discussed in the section on experimental results. Each DTA tube was made of 7-mm-OD fused silica tubing with a concentric 2-mm-ID depression about 4 mm long formed in the bottom to accommodate a thermocouple. The size of a DTA sample was 0.5 to 1.0 g. An Aminco Thermoanalyzer whose accuracy was within 2°C18 was used for the DTA measurements. The metallographic samples were prepared by conventional techniques. A solution of FeCL dissolved in a methanol-HC1 mixture was found to be the most satisfactory etchant. Electron beam microprobe scanning and point-count examinations were made on polished and unetched samples using an ARL Electron Microprobe at an electron beam voltage of 20 kv. The detectors were set to receive characteristic La1 radiation. Calibration standards of the pure elements were incorporated in each sample mount; quantitative point counts were calibrated by a method similar to Ziebold

Jan 1, 1969

By Roy A. Lindgren

SINCE the year 1643, when the first blast furnace in America for treating iron ore was built at Saugus, Mass., out of mica schist quarried in the neighboring district, the procurement of a suitable refractory for furnace lining has been a problem of concern to the operators of furnaces. The stacks built of mica schist continued to smelt iron ore until about 1836, when, according to F. H. Norton, the first firebrick were produced', at Queens Run, Pa. Other writers speak of brick having been molded and burned in Massachusetts about the year 1834. In 1841, Andrew Russell began to produce medium refractory plastic clay brick near East Liverpool, Ohio, that were used for lining blast furnaces'. The well-known Kentucky clay-producing district was not opened up until the year 1871, but since then it has produced a large percentage of the linings for iron blast furnaces. While some strides have been made by the refractories industry during the 100 years that have passed since the first firebrick were produced, it has been only during the last two decades that any real progress has been made towards bettering the product, even though the method of production had improved. Perhaps the fault lies with the user of the brick rather than with the producer, for not sooner demanding a supe¬rior product. During the past 15 years the tonnage produced per lining has increased from 500,000 gross tons to 1,000,000 gross tons, and now some furnaces are producing 1,600,000 gross tons and better on a single lining. It is true that enlarged capacity of furnaces and improved practice have accounted for some of this increase in tonnage, nevertheless better quality in firebrick must be given credit for its share. However, we are not yet ready to say that we have reached a maximum life of furnace lining. We believe that a better product can be produced and that the refractories industries of America will, through their extensive research depart-

Jan 1, 1937

By Cyril Wells, Robert F. Mehl

The two earlier papers in this series1,2 presented data on the rate of diffusion of carbon and of manganese in gamma iron. Apart from their scientific interest, these data are needed chiefly in order to treat data on carburization, on rate of formation of pearlite, and on rate of austenit-izing in a quantitative way.1'2'9'10 In the present investigation rates of diffusion of nickel in ?-Fe over wide temperature and concentration ranges have been determined, and the effects of carbon, of im- purities, and of grain size on these rates have been studied. Claussen,3 using the data of Fry,4 has calculated the diffusion coefficient of nickel in y-Fe as 9.2 X 10-11 sq. cm. per sec. at 1200ºC., but had no data from which to calculate the variation of D with concentration, temperature, and percentage of carbon. Method and Materials Method.—Nickel was diffused along the axis of a cylindrical specimen across a concentration gradient, concentration-penetration curves were determined and D values calculated from Grube or Matano solutions.5 Details of the method are given

Jan 1, 1941

By Cyril Wells, Robert F. Mehl

The two earlier papers in this series1,2 presented data on the rate of diffusion of carbon and of manganese in gamma iron. Apart from their scientific interest, these data are needed chiefly in order to treat data on carburization, on rate of formation of pearlite, and on rate of austenit-izing in a quantitative way.1'2'9'10 In the present investigation rates of diffusion of nickel in ?-Fe over wide temperature and concentration ranges have been determined, and the effects of carbon, of im- purities, and of grain size on these rates have been studied. Claussen,3 using the data of Fry,4 has calculated the diffusion coefficient of nickel in y-Fe as 9.2 X 10-11 sq. cm. per sec. at 1200ºC., but had no data from which to calculate the variation of D with concentration, temperature, and percentage of carbon. Method and Materials Method.—Nickel was diffused along the axis of a cylindrical specimen across a concentration gradient, concentration-penetration curves were determined and D values calculated from Grube or Matano solutions.5 Details of the method are given

Jan 1, 1941

By J. O. Lewis

Oil wells usually reach their maximum daily output shortly after they are completed. From that time they decline in-production, the rapidity of decline depending on the output of the wells and on other' factors governing their productivity. The production curve of a well shows the mount of oil produced per unit of time for several consecutive periods; if the conditions affecting the rate of production are not changed by outside influences, the curve will be fairly regular, and, if projected, mill furnish useful knowledge as to the future production of the well. By the aid of this knowledge the value of a property may he judged, and proper depletion and depreciation charges may be made on the books of the

Jan 2, 1918

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice-chairman for Production of the Petroleum Division: Generally in Table 1 the unit for presentation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions-—several units of continuous productive reservoirs of distinctly different structure and of distinctly dzerent stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and/or commercial value. As to each space in the tabulation, it is either (1) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert x; in spaces where the proper entries are determinable but not determinable from data available to the author, the author will please insert y; in spaces where the proper entries are determinable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use 2. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report l,8x,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations

Jan 1, 1937

By Enrique Touceda

For a number of years prior to the world war, the firm of Geo. H. Thacher & Co., of Albany, N. Y., was engaged in the manufacture of marine and other gray-iron castings. At the outbreak of the war the firm decided to specialize in the manufacture of propeller wheels. It attacked the problem, therefore, from a foundry point of view, seeking to produce a casting that would be so accurate that no subsequent machining would be required on the blades, also from the point of view of the ship builder. There were two general methods of manufacture, the shortcomings of which have been freely acknowledged. In the sweep method, the nowel, or bottom half-mold, for each blade is swept up by a spindle beam and pitch race, while the top half-mold for each blade is built up individually. In the pattern method one individual blade, with the hub or hub portion, is mounted on a spindle and the individual blade mold formed, the pattern is then rotated on the spindle to the position for the next blade, etc. In rare cases wheels were made from a solid pattern. Owing to the cost of the pattern, its failure in many instances to be correctly made, and (when made of wood) its early and sure distortion the disadvantage of this pratctice is obvious, while metal patterns in most instances were prohibitive in cost. In these methods both green-sand and loam molding was practiced. The casting produced by either method can be considered only as a blank from which the propeller must be machined. The back surface of each blade must be chipped to the templet and through this procedure chipped to such accuracy as will be required for a static balance. Inasmuch as the work done by the machine tool is confined to the driving face of the blades, not only is perfection most difficult, but corrosion will be greater because of the removal of the dense skin of the casting and the local strains set up by the pneumatic tool in chipping. To produce a finished 9-ft. propeller for a Navy destroyer required from 8 to 21 days of foundry work and about the same length of time for the machining. Through the use of the Thacher process, only as many hours are required, besides it is possible to produce a finished casting in perfect conformity with any particular propeller-wheel design.

Jan 1, 1922

By Enrique Touceda

For a number of years prior to the world war, the firm of Geo. H. Thacher & Co., of Albany, N. Y., was engaged in the manufacture of marine and other gray-iron castings. At the outbreak of the war the firm decided to specialize in the manufacture of propeller wheels. It attacked the problem, therefore, from a foundry point of view, seeking to produce a casting that would be so accurate that no subsequent machining would be required on the blades, also from the point of view of the ship builder. There were two general methods of manufacture, the shortcomings of which have been freely acknowledged. In the sweep method, the nowel, or bottom half-mold, for each blade is swept up by a spindle beam and pitch race, while the top half-mold for each blade is built up individually. In the pattern method one individual blade, with the hub or hub portion, is mounted on a spindle and the individual blade mold formed, the pattern is then rotated on the spindle to the position for the next blade, etc. In rare cases wheels were made from a solid pattern. Owing to the cost of the pattern, its failure in many instances to be correctly made, and (when made of wood) its early and sure distortion the disadvantage of this pratctice is obvious, while metal patterns in most instances were prohibitive in cost. In these methods both green-sand and loam molding was practiced. The casting produced by either method can be considered only as a blank from which the propeller must be machined. The back surface of each blade must be chipped to the templet and through this procedure chipped to such accuracy as will be required for a static balance. Inasmuch as the work done by the machine tool is confined to the driving face of the blades, not only is perfection most difficult, but corrosion will be greater because of the removal of the dense skin of the casting and the local strains set up by the pneumatic tool in chipping. To produce a finished 9-ft. propeller for a Navy destroyer required from 8 to 21 days of foundry work and about the same length of time for the machining. Through the use of the Thacher process, only as many hours are required, besides it is possible to produce a finished casting in perfect conformity with any particular propeller-wheel design.

Jan 1, 1922

By D. G. Wilder

D.G. Wilder I found the suggestion that the amount of displacement of a fault can be numerically related to the thickness of gouge or breccia to be both intuitively satisfying and intriguing. I have long agreed that there is some type of relationship between the amount of gouge and the amount of displacement of faults. I congratulate the author for developing a numerical relationship between them. However, I am concerned that the limits for applying this relationship be fully understood. An underlying assumption in this approach is that there is either a uniform thickness of gouge or breccia along a given fault or the thickness does not vary widely. Since it is not always possible to confirm this, the displacements derived by this method should be viewed with caution unless significant fault extent can be observed. At the Nevada Test Site, in drifts constructed in granite for test emplacement of spent nuclear reactor fuel, we found a fault with 0.3 to 0.4 m (12 to 16 in.) of clay gouge. Within a few meters of this location, the fault had no clay gouge, but rather consisted of a highly fractured zone with significantly altered rock and some slickensides. Based on Fig. 1, the 0.3 to 0.4 m (12 to 16 in.) thickness of gouge would indicate a displacement in excess of 30 m (98 ft). However, no gouge thickness would indicate essentially no displacement. Based on a quartz vein that terminated on the fault, and is not identified nearby, an estimated displacement of more than a few meters was made. This estimate is consistent with that obtained using the regression line proposed in the paper if the 0.3 to 0.4 m (12 to 16 in.) thickness for the gouge is used. However, using the regression curves with zero thickness would not yield results consistent with what was observed in the field. Therefore, it is important to recognize that the suggested procedure would properly yield a range of probable displacements. ? *Work performed under the auspices of the US Department of Energy by the Lawrence Livermore National Laboratory under Contract W-7405-Eng-48. Reply by E.C. Robertson It is certainly true that the t (thickness) of gg-bx (gouge and breccia) on a fault does vary along the fault. My observations have been that near the termination of a fault, the displacement d is small and the t is also small, whereas the maximum d and t will usually be found in the central part of the fault. The information on gg-bx and t of the fault found in granite in the NTS tunnel by Mr. Wilder could be interpreted somewhat differently than he does. He speaks of the fault changing within a few meters from 0.3 to 0.4 m (12 to 16 in.) of clay gg to "a highly fractured zone with significantly altered rock and some slickensides," but no gg. The highly fractured rock may be taken to be bx, rock not so finely ground as gg but still crushed by the fault movement, equivalent to the gg in my usage, and probably occupying about the same t. Mr. Wilder's estimates for the fault in the NTS tunnel for t of 0.3 to 0.4 m (12 to 16 in.) and for d of a quartz vein, in excess of "a few meters," would place the point on the low side of the central trend line in my Fig. 1, at the lower limit. There is, of course, a problem with determining d using displacement of only one planar surface. It would be greater or lesser depending on the rake of the movement. Finally, estimating the d of a fault from its t should be made with awareness of our present uncertainties, as pointed out by Mr. Wilder. Although the central trend line in my Fig. 1 has a ratio of d/t of 100, I have put the limiting ratios at 10 and 1000. Understanding of the values of the ratio will be improved only with collection of more data, for which the discussion of Mr. Wilder is much appreciated. ? G.C. Waterman E.C. Robertson's paper provides significant information to a geologist attempting to deduce fault offset by noting the products of structural dislocation. However, considerable mapping in underground and open-pit mines, and examination of structures produced in different geological settings, have convinced me that gouge and breccia thickness are controlled by geological conditions and fault movement. The following paragraphs suggest geological variables that control them. 1. Depth of Loading A near-surface fault resulting from tensional stress has more breccia/gouge than is produced by a similar stress at considerable depth. A deep-loaded compressional stress may produce a linear zone of schist, or structural dislocation may occur along an earlier formed belt of schist. Such "shear zones" are common in Canadian mines in precambrian rocks. In neither case can offset be directly deduced by an analysis of the minimal gouge/breccia in the shistose rocks. At greater depth, stress may be partially to wholly relieved by flowage. I vividly recall first noting the regional "Midas Thrust" in the Lark mine, Bingham Mining District, UT (where we called the structure the North Fault). My recorded notes, as I remember them, showed a narrow gouge streak separated the "Jordan" and "Commercial" limestone units from impure, muddy limestone beds of uncertain stratigraphic position. The visible structure did not indicate the great importance of this premineral fault

Jan 1, 1985

Jan 1, 1890

By J. D. Prater, H. R. Spedden, E. E. Malouf

With the expansion of copper leaching of the various mine wastes at the Kennecott properties, additional copper recovery facilities have been required. A research and development program has been pursued to determine a suitable economic approach to the processing of the additional leach solutions contemplated. lnvestigations on laboratory and pilot plant scales covered electrowinning, solvent extraction, launder and vat type cells, activated launders, precipitation drums, and precipitation cones. This paper contains information on the development and use of a new precipitation-cone-type copper recovery plant, which provides many advantages over older systems. The application of research findings to the old art of leaching copper from copper-bearing mine waste has resulted in a significant contribution of copper to over-all copper production. For example, at the completion of the current expansion program at the Kennecott properties in the United States, copper produced from waste dump leaching will amount to about 25% of the total production. Formerly only 2% was derived from this source. This planned expansion of copper leaching focused attention on the problem of developing more efficient methods for the recovery of copper from greatly increased volumes of copper-bearing solutions.1 The detailed investigations which have been made in laboratory pilot plant and plant tests for the recovery of copper from copper-bearing solutions have included electrowinning, solvent extraction, ion exchange and cementation with iron in launders, precipitation drums, activated launders, and precipitation cones. The results of these investigations have led to the development of a new precipitation cone-type copper recovery system providing many advantages over older methods. ELECTROWINNING OF COPPER FROM COPPER-BEARING SOLUTIONS The direct electrowinning of copper from relatively dilute solutions of copper-bearing mine water, namely solutions containing 10 to 20 lbs of copper per 1000 gal, has always been an attractive possibility.2,3 By this method, high-purity copper powder can be recovered with a power consumption of 3.5 kwh per Ib of copper. However, once the solution strength de-

Jan 1, 1967

By James Terry Duce

In order to facilitate interpretation of the data in this chapter, we print the following excerpts from circulars to authors, compiled by Mr. Frank A. Herald when he was Vice-chairman for Production of the Petroleum Division: Generally in Table 1 the unit for presentation of data is a field. For our purposes a field is defined as the whole of a surface area wherein productive locations are continuous. Such unit commonly includes and surrounds nonproductive areas. Such unit commonly includes a great variety of geologic conditions-several units of continuous productive reservoirs of distinctly different structure and of distinctly different stratigraphy. Therefore it is hoped that our authors will subdivide "field" so as to enable students to make analyses that may have scientific and/or commercial value. As to each space in the tabulation, it is either (I) not applicable, (2) the proper entry is not determinable, (3) the proper entry is determinable, but not determinable from data available to the author, (4) the proper entry is determinable by the author. In spaces not applicable, the author will please draw horizontal lines; in spaces where the proper entries are not determinable, the author will please insert x; in spaces where the proper entries are determinable but not determinable from data available to the author, the author will please insert y; in spaces where the proper entries are determinable by the author he will, of course, make such entries. Generally, y implies a hope that in some future year a definite figure will be available. Inability to determine precisely the correct entry for a particular space should not lead the author to insert merely y. Contributions of great value may be made by the author in many cases where entries are not subject to precise determination. In such cases the author should use his good judgment and make the best entry possible under the circumstances. For many spaces, the correct entries represent the opinion of the author (for example, "Area Proved") and in such cases the entries need not be hedged to such extent as in cases where the quantities are definite yet can be ascertained only approximately by the author. In cases under definite headings but where figures are only approximate, the author may use x. For example, if the total production of a field is known to be between 1,800,000 and 1,850,000, the author may report 1,8xx,xxx; or if the production is between 1,850,000 and 1,900,000, the author may report 1,9xx,xxx. Where a numeral is immediately to the left of x or y, such numeral represents the nearest known number in that position. As to quantity of gas produced from many fields the question will arise as to whether the figures should include merely the gas marketed or should include also estimates of gas used in operations and gas wasted. Although rough approximations

Jan 1, 1938

By N. F. Mott

Jan 1, 1961

By K. K. Clark, W. H. Somerton

The feasibility of reducing pressures needed to fracture formations by heating the borehole intensively has been investigated on a laboratory scale. Reductions in fracture pressures of heated Bandera, Berea and Boise sandstone cores were observed at various confining pressures, simulating reservoir stress conditions to a depth of 5,000 ft. Both permeable and impermeable borehole boundary conditions were tested. Three heating conditions were used in the tests. One group of samples was heated in a furnace to a temperature of 600C, cooled to room temperature., and then tested for fracture pressures. Two other groups of samples were heated with a borehole heater to maximum borehole wall temperatures of 625 and 792C, then cooled and tested. In all cases, heated samples showed substantial reductions in fracture pressures compared to unheated samples. The higher temperature borehole heated samples showed the greatest reduction, amounting to 70 per cent in the extreme case. In actual application to wells, it was concluded that fracture pressures may be reduced by 20 to 50 per cent by intensive borehole heating before fracturing. INTRODUCTION Hydraulic fracturing of oil and gas wells is an accepted and effective technique for increasing well productivity in many areas, but is notoriously unsuccessful in other areas. The technique becomes less interesting for production stimulation purposes when excessive fracture pressures are necessary. Formations which do fracture but require high pressures, probably form horizontal fractures. There is good evidence to indicate that some formations do not fracture at all, but yield plastically under high pressure. Thus, any technique which will make formations easier to fracture or will reduce fracture pressures is potentially interesting to petroleum producers. Horizontal fractures generally occur in planes of weakness, such as bedding planes, and at pressures equaling or exceeding the effective overburden stress. In the unusual case where planes of weakness do not exist, a slightly higher pressure must be applied to overcome the tensile strength of the rock. In general, high fluid-loss fracturing fluids are conducive to the formation of horizontal fractures.1 Vertical fractures, when they do occur, are initiated at pressures generally lower than overburden pressure and are favored by low fluid-loss fracturing fluids or impermeable boreholes. The pressure necessary to create a vertical fracture in an impermeable, elastic medium can be predicted from the so-called "thick-walled cylinder" equation: Pf = 2 or+ st.............(1) where pf = fracture pressure or = radial stress st = tensile strength of medium. This equation indicates that to fracture it is necessary to overcome a tangential compressive stress, induced by and equal to two times the radial confining stress, plus the tensile strength of the medium. If the above equation held strictly true for rocks, very little could be done to reduce fracture pressure. The tensile strength of the rock might be reduced somewhat, but any change in st would be small compared to the magnitude of the tangential stress at reasonable subsurface depths. Laboratory tests have shown that actual fracture pressures exceed values predicted from Eq. 1 by factors of 1.4 to 28.6.1,2 Eq. 1 thus does not properly describe the

Jan 1, 1966

By Eugene N. Cameron

Pegmatites of these areas have become important sources of beryl and lepidolite and have yielded cassiterite, columbite-tantalite, and other minerals. Examination of about 60 of these pegmatites leads the author to question the opinion of earlier investigators that the concentrations of beryl, lepidolite, and columbite-tantalite found have mostly formed by hydrothermal or pneumatolytic replacement of previously formed quartz-feldspar pegmatites. The author concludes, on the contrary, that present knowledge of the occurrence of minerals in zoned pegmatites can be applied to prospecting and mining of pegmatite deposits in these two areas of South West Africa. PEGMATITES occur in abundance in certain areas of South West Africa and in adjacent parts of northern Cape Province in the Union of South Africa. Some of the pegmatite deposits were prospected before World War I, and intermittent mining was done during the period between the two World Wars. The deposits of the Jooste lithium mines became an important source of lepidolite, and beryl, columbite-tantalite, wolframite, and other minerals were produced. Since World War II prospecting and mining have been carried on vigorously, with the result that South West Africa produced nearly 3000 tons of beryl during 1949 through 1953, together with more than 40,000 tons of lithium minerals, chiefly lepidolite and petalite. Small amounts of tantalite, columbite, and other minerals have also been produced during the postwar period. Most of this mineral production has come from two pegmatite areas roughly outlined in Fig. 1. One is the Karibib-Omaruru area of north central South West Africa. The second is the northeastern part of the Orange River pegmatite area, which extends into adjacent parts of Namaqualand, in northern Cape Province of the Union of South Africa. The writer visited the two pegmatite areas in July 1951. The visit was brief. but it gave an opportunity to compare some of the' pegmatites of these areas with those studied and described in detail by many investigators in the U. S., Brazil, and Canada during and since World War 11.'-l' The writer has attempted to determine, in a preliminary way, whether the concepts of internal structure and distribution of minerals in pegmatite bodies developed out of these studies are applicable to prospecting and exploration of pegmatites in South West Africa. Previous Work In an important series of papers (1929 to 1942) T. W. Gevers, H. I?. Frommurze, S. H. Haughton, G. K. Joubert, and other geologists of the Geological Survey of South Africa described and discussed the pegmatites of the two areas.*-" These works are the principal sources of information on the pegmatite mineral deposits of South West Africa. The investigations showed that in the two areas pegmatites are profusely distributed in pre-Cambrian rocks. These rocks are meta-igneous and metasedimentary units that have been folded and subsequently invaded by younger pre-Cambrian granites and by other igneous rocks. The pegmatites are considered to be genetically related to the pre-Cambrian granites. Pegmatites occur in the granite bodies themselves but are most abundant in the surrounding metamor-phic rocks, a pattern repeated in many pegmatite districts of the world. The origin of the pegmatites and the factors controlling the occurrence of mineral deposits in them were discussed at length by Gevers and Frommurze (1929)" and later by Gevers 14, 15 pp. 41-51, Ref.

Jan 1, 1956

By S. H. Moll, R. E. Ogilvie

The investigation of solid-state diffusion phenomena may lead to much information concerning binary alloys. In particular, a study of the concentration gradients present in multiphase diffusion couples can lead to the determination of the solubility limits of the single-phase fields in the phase diagram. The specific concentration gradient which results from the heat treatment of a diffusion couple depends not only upon the time and temperature of diffusion, but also upon the number of phases existing in equilibrium at the diffusion temperature. Such concentration gradients possess sharp discontinuities whose terminal points correspond to the solubilities existing at the limits of the two-phase field in the phase diagram at the diffusion temperature. In general, there will be a discontinuity in the concentration curve for each two-phase field which exists in the phase diagram between the concentration limits of the couple. A number of investigators have analyzed the gradients present in multiphase diffusion couples. 1-8 The iron-titanium phase diagram exhibits a y loop in the temperature range from 900" to 1400°C, and the limit of the a + y field lies at some composition which is less than 1 wt pct Ti for any temperature. It was felt that a diffusion study could yield values not only for the diffusion coefficients involved, but also for the chemical solubilities in the phase diagram. The concentration gradients were analyzed by an X-ray absorption technique developed by Ogilvie.6 The absorption of a monochromatic X-ray beam is measured in steps parallel to the diffusion direction and the resulting intensity gradients are transformed into concentration gradients by applying the laws of X-ray absorption in a binary system. This technique has been applied by ogilvie6 to the systems Ni-Au, Cu-Au, Fe-Cr, and Ni-Cr; by Gelles7 to the systems Be-Fe, and Be-Ni and by Hilliarde to the system Al-Zn. Linear X-Ray Absorption Analysis—The use of X-ray absorption analysis as a tool for determining concentration gradients arises from the fact that the beam is absorbed according to the quantity and species of elements present in the sample and not according to their state of aggregation. This method is more advantageous than the chemical analysis of machined layers since it is less time consuming and less expensive and can analyze a very small area. IF a homogeneous binary alloy (A + B) is analyzed with two different monochromatic X-ray beams I0(2) and lo(2) the following relation between the transmitted intensities, the intrinsic absorption coefficients of A and B for the two different radiations and the weight fraction of each element may be derived.' In (I/Io) (a+b) xa(u/p)a(2) + xb(u/p)8(2) Eq. [1] is independent of specimen thickness and density, but requires that either element A or B possess an absorption edge between the wavelength limits of the two monochromatic beams. I, is evaluated for each radiation by measuring the transmitted intensity through a varying number of foils of a suitable absorber. A plot of the natural logarithm of the transmitted intensity as a function of the number of foils, when extrapolated to zero foils, yields the value of I,. If a plot of the ratio in Eq. [ I] is calculated as a function of xA, then a master curve results. From

Jan 1, 1960

By J. L. Jernegan

IN a former paper laid before the Institute, entitled Lead and Silver Smelting in Chicago, I endeavored to give a description of the manner in which argentiferous lead ores from the far West were treated in that city, and also described the method employed in the desilverization of the silver-lead produced from the ores. It will perhaps be remembered, that very siliceous ores, principally from the Emma mine, Utah, containing over 40 per cent. of silicic acid, were then being treated at the works of the Chicago Silver Smelting and Refining Company in the reverberatory furnace, with the use of metallic iron, in the form of borings, as a precipitating medium for the lead ; and that the extraction of the silver from the resulting bullion was effected by the Balbach process. The Swansea Works, also the works at Brighton, just outside of this city, and those of S. P. Lunt, were at that time treating ore of a similar character by the same method. The inadequacy of the process for the ores then under treatment was, in a manner, pointed out by me in the paper above referred to. Since the time of its writing, many and important improvements have been made in the metallurgical treatment of Western ores in Chicago. Most ores are now roasted previous to reduction, and the latter operation is conducted in the shaft-furnace instead of the reverberatory. Such is the fact at least at the Swansea Works, the largest in the city, and here it was where the first steps were taken in this direction. In selecting these works as the subject of this paper, I am in hopes that the description given of the various metallurgical operations, as they are there now conducted, will serve to give an idea of the improvements introduced

Jan 1, 1876