By Jo. E. Sheridan

The Dawson coal-mines are owned aid operated by the Stag Canon Fuel Co., of which Dr. James Douglas is President and E. L. Carpenter general manager. The property is situated in Colfax county, N. M., and the openings now in operation are in townships 28 and 29 N R. 20 E., and township 28 N E. 21 E., shown in Fig. I. The mines are part of the southern end of the Raton coal-field, which extends north into Colorado and embraces many coal-camps of the Trinidad section. II. Geology. Geologically, the coal-measures, commonly known as the Laramie series of the Cretaceous system, have x thickness of about 800 ft. in the vicinity of Damson. The coal makes an excellent coke, and, according to some authorities, its coking properties are due to the action of intruded sheets and sills of igneous rock, the sheets occasionally thickening into masses resembling laccoliths, at such places making nearer approach to the coal and sometimes producing small areas of natural coke. There are but few dikes throughout the entire southern portion of the field and little or no faulting along the dikes. In some parts of this great coal-field the intrusive sheets are far removed in the green shales below the coal-measures, and are so much altered as to be difficult of identification. There is but little disturbance of the strata throughout the Raton coal-field in as far as it extends into New Mexico. There are two workable seams in the coal-measures, and two or three smaller coal-seams, ranging from 1 to 2.5 ft. in thick-

Jan 1, 1910

By T. A. Rickard

Freeman, the English historian, said that he had learned from Macaulay "never to be afraid of using the same word or name over and over again if by that means anything could be added to clearness or force. Macaulay never goes on, like some writers, talking about `the former' and `the latter', `he', `she', `it', and `they', through !clause after clause, while his reader has to look back to see which of several persons it is that is so darkly referred to". He might have learned also from Macaulay that a preposition makes a' feeble ending for a serious statement. How often do you hear `the former' and `the latter' in conversation? Good conversation is a guide not to be dis¬dained. When you must use `the latter', do not confuse it with `the last'. Cheap labor, cheap fuel, and cheap transport are essential, the latter [last] being particularly important in base-metal mining. The apparatus may be used to determine such gases as hydrogen sulphide, chlorine, oxides of nitrogen and some others, as well as sulphur dioxide. In the case of the latter two, etc. The two last mentioned are "sulphur dioxide" and "some others". He should have stated which two, and he should have avoided that wretched phrase "in the case of ". Pinning may be partly prevented by use of chalk, oil, or turpentine. The latter [last] is best. I "Partly prevented" is a poor phrase. `Prevented! is a word that does not lend itself readily to modification. He means `checked' or `corrected'.

Jan 1, 1931

By J. B. Cohen, O. F. Kimball

Aging of specimens of Au-20 at. pct Ni and Au-40 at. pct Ni has been followed with electron microscopy, resistance, magnetic measurements, and X-ray diffraction. The periodic structures observed by electron microscopy in Au-Ni alloys by Fisher and Embury are shown to be due to nickel-rich prepre-cipitates. Assuming this alloy system undergoes spinodal decomposition, our observations and available data on thermodynamic properties and elastic constants indicate that the gradient energy coefficient in this system is of the order of 10-5 ergs cm-1 . Shifts of X-ray peaks in this system have been found to be due primarily to residual stresses, not faulting. A large effect of applied stress during aging was detected by X-rays and electron microscopy for the Au-20 at. pct Ni alloy. The presence of a preprecipitation stage during aging of gold-rich Au-Ni alloys for short times below 300°C has been indicated by several previous investigations. Changes in electrical resistivity,1"3 elastic modulus,4 superparamagnetisrn,5 positions of X-ray diffraction peaks,6 and hardness7 have been studied. Electron diffraction and microscopic studies by Fukano8 and Fisher and Embury9 respectively showed that the precipitation process resulted in the formation of periodic composition fluctuations—perhaps spinodal decomposition. MOSS10 detected a satellite with X-rays in quenched specimens, but the wavelength was much smallerthan that found by Fukano. Recently Woodilla and Averbac11 detected a modulation similar to that found by Moss, but with electron diffraction. They suggested that the microstructures observed by Fisher and Embury may be simply due to a Moir'e effect from a back deposit of gold during electropolishing. Satellites in electron diffraction can be enhanced by small bends or tilts of a foil. Even if this were not the case, asymmetric satellites, as are found in Au-Ni are difficult to analyze. They are principally influenced by the large differences in atomic size in this system, and obtaining information on the associated composition fluctuations depends on assumptions as to whether or not there are isolated clusters or composition "waves", and in the latter case whether or not the entire specimen has decomposed. Assuming that decomposition was complete in alloys aged at low temperatures, Woodilla and Averbach suggested that the satellites indicated a composition which varied about the average value by only± 5 pct, much less than that predicted from the phase limits, Fig. 1; they attributed this small variation to a cessation of the reaction caused by the loss of mobile vacancies. In Ref. 12 it was shown that vacancies are trapped by the preprecipitate in this system. Furthermore, after reversion, aging proceeds at a much slower rate than immediately after a quench from the solution temperature,5'11,13 indicating the importance of vacancies in the kinetics. In some senses Au-Ni is a favorable system for studying preprecipitation and reversion mechanisms because of the simplicity of the equilibrium diagram14 and the availability of good thermodynamic15 and diffusion data.16,l7 The calculations necessary to relate the decomposition process to classical nucleation and growth or to spinodal decomposition, as well as those necessary for understanding reversion mechanisms, can, therefore, be made. As an example, the position of the chemical spinodal, calculated from the thermo-dynamic data of Sellars and Maak15 with the method described by Rundman and Hilliard,18 is included in Fig. 1. It is compared to the chemical spinodal calculated from the equilibrium miscibility gap by Cook and Hilliard's method.l9 Included is the coherent spinodal suggested by Golding and MOSS," using measured elastic constants for their calculations and the same ther-modynamic data. The spinodal estimated by Woodilla and Averbach,11 by determining the temperature limits for the observation of the satellites discussed above, is also given. Actually this last curve is open to question on the following grounds: As a phase boundary is approached the spacing of particles or the wavelength

Jan 1, 1970

By Maurice Ewing, L. Don Leet

The most important quantitative method in seismic prospecting by refraction shooting is the method of profiles. A profile is established by firing a series of charges at various points along a straight line which terminates at the seismograph. The same data are obtained by repeatedly firing charges at one place and recording at a series of stations along the line of the profile. The quantities which are measured are the distance x from each firing position to the seismograph and the time t required for the first disturbance from each explosion to travel to the seismograph. These data are used in plotting the familiar time-distance graph. The only time-distance graphs that will be considered here are those obtained in localities where the velocity of propagation depends solely on the depth beneath the surface; that is, where there is no slope in the subsurface. The essential calculation to be made from such a time-distance graph is the determination of P(x), the maximum depth of penetration of a disturbance coming to the seismograph from a firing point at the distance x from the instrument. If the time-distance graph consists of a series of straight lines, as is often the case, the penetration P(x) can be calculated by means of formulas which appear in almost every description of seismic prospecting.' Until the present, however, the only formula that has been available for calculating P(x) for time-distance graphs which are smooth curves is one which requires an arbitrary assumption regarding the law of velocity increase with depth.2 The practice in these cases has been to approximate the curve by means of a number of straight lines and then to apply the ordinary straight-line formulas. This method clearly can yield accurate results only when a sufficiently large number of straight lines is used. The labor of computation increases rapidly when the number of lines is increased, so too few lines often are used. Further than that, there is a strong tendency to overlook the approximate nature

Jan 1, 1932

By J. A. Pusateri, M. A. Orehoski, N. R. Arant

Plant studies on commercial-size ingots and laboratory experiments with induction furnace heats have demonstrated that the major source of ingot cracks is associated with two conditions arising during top-pouring practice: 1—solidification during pouring, and 2—turbulence created by the impact of the stream. Methods of controlling the two factors were effective in eliminating or significantly reducing ingot cracks. BECAUSE the process of removing surface defects from hot-rolled product is so costly, the steel industry is striving constantly to develop methods of preventing, or at least decreasing, the occurrence of surface defects. Investigations have revealed steel-making and processing variables related to major surface defects, and controlling these variables has led to improvements in surface quality. However, the fundamental causes of major surface defects, such as ingot cracks, have not been determined; consequently such defects persist. At the Research and Development Laboratory of the United States Steel Corp. in Pittsburgh, a seam research program was initiated to determine the fundamental causes of certain major defects. As a part of the program, ingot cracks in killed, finegrained C1020 steel were selected for study. A cost survey indicated that, of the steels produced in sizable tonnages, carbon steels in the range of 0.18 to 0.23 pct C content require the most conditioning. Since this is particularly true of C1020, any im-provement of surface quality that might be effected from the study would be beneficial. Also, since the frequency of ingot cracks is exceedingly high for this grade, the steel would provide an excellent opportunity for a thorough study of the ingot-crack-ing problem. Why steels in this carbon range tend to exhibit more ingot cracks than do other steels was not considered in the investigation; the mechanism of ingot-crack formation was of paramount importance. Also, only the top-pouring practice was considered in the investigation, because this pouring procedure is used more extensively than others. In this study, ingot cracks are defined. as deep surface defects that sometimes are observed in an ingot prior to rolling but usually are observed during the initial stages of rolling on the primary mills. These defects may occur at any angle to the rolling direction but are most prominent in the transverse or nearly transverse direction. The appearance of ingot cracks on the rolled product varies with respect to their angle of formation and with the extent of rolling after their first occurrence. Ingot cracks are also termed "deep seams," "arrowheads," "irregular cracks," and "transverse cracks." Fig. 1 shows ingot cracks in a rolled bloom. This report summarizes: l—the exploratory investigation of commercial-size ingots; 2—the labor-atory investigations related to determining the source of ingot cracks and developing corrective methods; and 3—the plant evaluations of laboratory methods of decreasing ingot cracks. Exploration of lngot Cracks in Commercial Ingots Materials and Experimental Work: At the Du-quesne Works of the United States Steel Corp., five heats of killed, fine-grained C1020 steel were selected for the exploratory phase of the seam-research program. The heats were made by open-hearth practices that are considered most conducive to good surface quality. They were top-poured into 22x25 in. big-end-up hot-topped molds. One as-cast ingot and four other ingots rolled to the following cross-sectional sizes were set aside from each heat: 16x20 in.; 9 1/2x10 in.; 5x5 in.; and 2x2 in. The processing of the heats, from the time of charging in the open hearth furnaces to the end of the rolling operation on the primary mill, was observed carefully and recorded. The cast ingot and the four rolled ingots from each heat were examined for surface defects. The cast ingots were split longitudinally near the vertical center plane to expose the ingot structure beneath badly cracked regions. Also, a series of transverse sections was cut at about 1 in. intervals in a badly cracked area of one ingot. All sections were ground, polished, examined by sulphur printing and deep etching, and photographed. The rolled ingots

Jan 1, 1955

By Frank M. Monroe, James R. Cost

The solubility of nitrogen in vanadium is determined from 275" to 575°C by measuring the height of the nitrogen internal friction peak of equilibrated V-N alloys. The proportionality constant at 275°C between the internal friction peak height (Q- 1) and the atom percent nitrogen in solution is found to be 0.095 per at. pct for nitrogen concentrations up to 0.8 at. pct. The heat of solution of the nitride in vanadium is 5500 cal per mole. The solubility of nitrogen in the Group V metals is discussed. LITTLE work has been performed on the vanadium-nitrogen terminal solid solution. Hahn1 found the solubility for nitrogen to be very small and reported the existence of a hexagonal phase of composition near that of V2N at the solubility limit. Rostoker and Yamarnoto2 reported the solubility to be at least 3.5 at. pct at the melting point and to be less than this value at 900°C. In addition, they reported from X-ray diffraction studies that nitrogen in solution produces tetragonality in the vanadium lattice. An X-ray study by Schonberg3 has confirmed the results of Hahn but indicated that the tetragonality observed by Rostoker and Yamamoto was due to the presence of oxygen in their specimens. Beatty4 has performed lattice parameter and hardness measurements on terminal solid solutions and found the upper limit of the solubility to be at least 0.66 at. pct N. No measurements have been made of the pressure-temperature-composition relationships (P-T-X) for the terminal solid solution. As a part of a research program on gas-metal equilibrium, an attempt was made to study the P-T-X relationships in the V-N system using both the internal friction and the gas equilibration methods which have been successful with the Nb(Cb)-N and Ta-N systems (see Ref. 5 for a review of this work). Extensive investigation, using the gas equilibration methods, showed this method not to be applicable with vanadium This was presumably due to the gettering action of vanadium sublimed on the walls of the Sieverts apparatus. Thus, the nitrogen pressure relationships with temperature and composition were not obtained. The internal friction methods were, however, found to be applicable, and the temperature-composition relationships are reported in this paper and compared with similar results for the Nb-N6 and Ta-N7 systems. The existence of a Snoek internal friction peak due to nitrogen in solution in vanadium has been clearly demonstrated. 8-10 Powers and Doyle found the peak to be at approximately 275°C for frequencies near 1 cps.8 In a subsequent paper10 they reported the proportionality constant at 275°C between the internal friction peak height (Q-1) and the concentration of ni- trogen in solution (in atom percent) as 0.06 per at. pct. The studies of Stanley and wert9 indicated qualitatively that the height of the Snoek peak decreased with aging at the peak temperature and thus suggested that internal friction methods were suitable for study of the solubility. EXPERIMENTAL METHOD The vanadium for this investigation was of particularly high purity. It was obtained from the Ames Laboratory of the U.S. Atomic Energy Commission, Ames, Iowa in the form of a 1/2-in. diam, three pass zone-refined ingot. The electrical resistivity ratio (p300ºk/p4ºk) was 160. The initial composition was determined as follows: Carbon 200 ppm Oxygen 150 ppm Chromium <50 pprn Iron 125 ppm Silicon <50 ppm Other metallic 100 pprn The initial vanadium ingot was fabricated to 30-mil wire by swaging and wire drawing without the need of intermediate annealing. Lengths of this wire were then further purified (particularly for oxygen) by outgassing at 10-6 torr at 1400°C for 4 hr. The outgassing treatment resulted in specimens with a bamboo grain structure and a lustrous appearance. Desired amounts of nitrogen were added to the outgassed wires in a Sieverts apparatus in which known amounts of nitrogen were equilibrated with the wire at 1300°C. Nitrogen concentrations were produced in the desired range from less than 1 to 10 at. pct N. Monitoring of the partial pressure of nitrogen in the Sieverts apparatus indicated that at 1300°C equilibrium between the nitrogen gas and the vanadium was obtained within 10 min. Relatively rapid cooling from the nitrogen addition temperature was obtained simply by turning off the specimen heating current and cooling to room temperature in the partial pressure of nitrogen. Internal friction measurements of wire specimens were made under forepump vacuum in a torsional pendulum at frequencies near 1 cps. The torsional pendulum was of low thermal inertia and was designed so that specimens could be heated both by a conventional tube furnace and by the joule heating of a separate current through the wire specimen." Use of a static atmosphere of helium gas as a quenching medium made it possible to cut the specimen current, rapidly cool the specimen to the measurement temperature, and make a measurement of the internal friction in less than 1 min. Because of the large solubility of vanadium for nitrogen, the internal friction peak heights were in some cases greater than Q-1 = 0.1. This high damping resulted in an estimated relative uncertainty in the damping measurements of approximately 10 pct. X-ray analyses made to identify the precipitated ni-

Jan 1, 1970

By F. Lynwood Garrison

Except in the old Catalan forge, or its modifications, attempts to make iron and steel directly from ore in a practical and economical manner have failed so frequently and completely that such schemes are looked upon with justifiable distrust. Without exception, all have failed from one cause or another, although in some instances every indication of a practical success was manifest in the beginning. It is, therefore, necessary to carefully examine and consider every detail affecting the process, or more properly, furnace, under consideration. This I have done to the best of my ability during a long visit to Russia last summer, and after satisfactorily observing the practical success of the furnace in the iron works of Count Stroganoff at Dobriansky in the Government of Perm, I decided to investigate as completely as possible the history of similar furnaces in Finland and Russia. These data, sifted and verified with the greatest possible care, form the substance of the present paper.* An illustration on page 321 of Percy&apos;s Iron and Steel shows the old type of Osmundssmide or harkugnar, which has been in use in Northern Europe since pagan times. Fig. 1 shows a furnace of this kind. It should, perhaps, more properly be called a high-bloomary furnace or forge, the Swedish word hark meaning bloom or loupe. It was with this type of furnace that Mr. Husgafvel began his experiments at Porsaskoski in 1875. Attempts to obtain better results with larger furnaces of this type were failures, as every bloom or loupe obtained necessitated blowing out the furnace with a consequent large waste of fuel. A larger furnace of course increased this waste with no corresponding advantage. A movable hearth of threeeighth inch iron, lined with a mixture of clay, quartz and lime, was next tried, but in consequence of the frequent repairs of this lining,

Jan 1, 1888

By W. A. Backofen, D. Lee

Titanium of commercial purity (RC-70) and two all-a (hcp) alloys (4Al-1/4O2 and 5Al-2.5Sn) were tested in sheet form under conditions of combined-stress loading. Plane-strain compression and plane -strain tension together with uniaxial compression and tension provided information for constructing the tension-tension and compression-compression quadvants of the plane-stress yield locus. Coordinate values were obtained from yield-strength measurements; the slope at each point was based on a plastic-strain ratio. The materials represented a wide range of plastic anisotropy, which was reflected in correspondingly varied departures of the yield locus from that for iso-tropy. The tension-tension and compression-compression quadrants were not identical. If the uniaxial yield strength is insensitive to direction and the sign of the applied stress, the Mises or perhaps the Tresca criterion is adequate for predicting the onset of yielding under combined-stress loading. The prediction is not so straightforward in plastically anisotropic material. Depending upon details of texture, combined-stress yielding resistance may be substantially different from that indicated by the usual criteria.&apos; However. a continuum theory of yielding under such conditions is available for reasonably direct application.2,3 Whether or not it can be used successfully must, of course, depend upon how closely the conditions of the theory are satisfied in the material in question. In its present form the theory contains no provision for Bauschinger-type effects, nor does it allow for the consequences that might grow out of deformation by more than one mechanism, e.g., by slip and twinning.4 With those limitations, more importance must be attached to experimental information about the yield surface for anisotropic materials. Studies of the yield surface have generally been confined to states of plane stress (tension-tension and tension-compression) established in thin-wall tubes by externally applied forces and internal pressure. That approach would be entirely suitable for anisotropic materials if they were available in tube form or in sufficient bulk to be machined into test specimens. 6-9 It would not serve for the textured and anisotropic sheets of much current engineering interest, unless sheet could be formed into high-pressure tubing without structural change. Since there would seem to be little chance of the latter, practical alternatives are needed. One such alternative is the subject of this paper. It involves the use of a few selected but relatively simple uniaxial loading tests on sheet specimens. The underlying idea is presented here with some details relating to application and a few results bearing on how well it has worked. THE BASIS OF TESTING Conventional Measurements. Yielding for a general case of anisotropy is described by the plane-stress locus in Fig. 1. Reference directions in the sheet specimen are related to the stress coordinates as shown with the insert: x is the rolling direction, y the transverse direction, and z the through-thickness direction. The four reference-direction yield strengths (t, tension; c, compression), Xt, Xc, Yt, and Yc, are all different. Nine paths that can be followed in uniaxial loading experiments are identified. Paths 1, 2, 3, and 4 represent conventional tension and compression testing to establish Xt, Yt,.Xc, and Yc. Useful information also comes from the ratio of the transverse plastic-strain components associated with yielding and flow in conventional tension or compression. A condition to be satisfied in locus construction is that the plastic-strain vector be everywhere normal to the locus.10 The projection of the vector which would

Jan 1, 1967

By O. N. Carlson, W. M. Paulson

A phase diagram is proposed for the Y-C system based on the vesults of thermal analyses, microscopic obsevvations, and X-ray diffraction studies. Three intermediate phases occur in the system: a congru-ently melting fcc phase with a wide range of homogeneity about the composition Y2C, an intermediate solid-solution region between 55 and 58 at. pct C, and a bct dicarbide melting congruently at 2415°C. All three compounds undergo a phase transformation at elezlated temperatures. A continuous serzes of solzd solutions exists between the fcc phase and the high-temperature form of YC2 with a maximum in the solidus at 2000°C and 30 at. pct C and a minimum at 1805°C and 54 at. pct C. THIS investigation of the Y-C system was undertaken as part of a nuclear materials development program. Yttrium-base alloys are of interest as possible containers for liquid metals, and carbides are currently receiving increased attention as high-temperature materials for advanced reactors and other applications. Previous work on this system was limited in scope, and the results were somewhat inconclusive and at times contradictory. Spedding et al.&apos; reported the existence of a triyttrium carbide having an fcc structure with a wide range of homogeneity and Dean et a1.2 reported the existence of a rhombohedra1 phase having the stoichiometry of Y2C. Bachella et a1.3 observed that the latter was the result of ordering of carbon atoms in the fcc solid solution. The ordering range was placed at 800" to 1000°C. Vickery et a1.4 reported a high-melting compound which they identified as yttrium dicarbide, and Spedding and coworkers1 determined the structure of this phase as bct with lattice parameters a = 3.66 and c = 6.17A. Samsonov et al.5 reported the melting point of YC2 as 2300" * 50°C. Recently Bowman et a1.6 found a transformation in the dicarbide from the tetragonal to an fcc form at 1320 20°C. Samsonov and coworkers7 reported a monocarbide of yttrium melting at 1950" * 20°C and also a sesqui-carbide melting at 1800" * 50°C. The existence of the latter has also been indicated by others,1&apos;8 but neither compound has been definitely established. The Y-C phase diagram shown in Fig. 1 was proposed by Chubb and Keller8 in 1964 based on the data available at that time. The tentative nature of this diagram together with the uncertain status of the compounds indicated that additional work on this system was needed. EXPERIMENTAL PROCEDURE Yttrium metal of 99.9 pct purity was prepared for use in this study by the reduction of YCl, with calcium to form a sponge product.9 The major impurities in this material were as follows: 100 ppm C, 150 pprn H, 20 ppm N, 300 to 1000 ppm O, <20 ppm Ca, <100 ppm Cr, <80 ppm Cu, 150 ppm Fe, <30 pprn Mg, <400 ppm Ta, and <100 ppm Ti. Alloys were prepared by arc melting yttrium sponge together with pieces of high-purity graphite rod in a purified argon atmosphere. Homogeneity was insured by repeated melting, inverting the ingot between melts.

Jan 1, 1969

By R. L. Smith, I. G. Greenfield

The binary system Ga-Sb has been investigated by thermal, X-ray, and metallo-graphic methods. &apos;The intermetallic compound GaSb melts at 705.9OC and forms a eutectic with antimony at 11.8 atomic pct Ga. This eutectic melts at 589.8OC. A eutectic appears to be formed at 29.8°C but is too close to the composition of pure gallium to be detected. IN the course of an investigation of the semiconducting properties of the intermetallic compound, GaSb, the phase equilibrium between gallium and antimony has been investigated. Recently, the phase diagram of similar systems, such as In-Sb,&apos; In-AS,&apos; and Bi-As3 have been determined. These diagrams have the same general appearance in that an intermetallic compound is formed at 50 atomic pct and a eutectic is formed on both sides of the intermetallic compound. Jenny,& who has been investigating the semiconducting properties of intermetallic compounds, has concluded from thermal data of several alloys that the phase diagram of the Ga-Sb system resembles those mentioned previously. This paper represents a more detailed study of the Ga-Sb equilibrium. Experimental Procedure The gallium that was used to prepare the alloys was obtained from A. D. Mackay Inc. and the Aluminum Co. of America; the latter reported the purity as 99.95 pct. The antimony was obtained from Bradley Mining Corp. who specified a purity of 99.997 pct. Since the intermetallic compound of GaSb was prepared primarily to be used for further studies of the semiconducting properties, additional purification by a standard zone-melting technique under an atmosphere of hydrogen was performed. Hall-effect measurements on this material indicated an impurity content of less than 3 ppm.5 The antimony also was purified by zone melting and used in conjunction with the compound GaSb to make the necessary alloys for the determinations of the antimony-rich side of the phase diagram. The antimony-rich alloys were chill cast in Vycor tubes which were evacuated to a pressure of less than one micron. Since these alloys expand on freezing, precautions were taken to prevent oxidation of the ingot in the event the tube fractured. To insure homogeneity, the brittle alloys were ground and then placed in the furnace for the thermal-arrest determinations. Since the cost of gallium is high, the experimental procedure was complicated somewhat because of the necessarily limited sizes of the melts. In order to economize, the gallium-rich side of the diagram was determined by using a 35 g ingot of pure gallium initially and adding increasing amounts of antimony in order to obtain additional alloys. The furnace used in the determination of the cooling curves is illustrated in Fig. 1. A 2¼ in. quartz tube, sealed at one end, was fitted with a brass flange which was attached with DeKhotinsky cement. The brass collar was water cooled to prevent the cement from softening. An "0" ring was used to provide a seal between the brass collar and the furnace cover. Nichrome ribbon was wound around a 2 ½ in. asbestos-covered copper core which was used to reduce the thermal gradient in the furnace. The insulation consisted of alternate layers of asbestos and aluminum foil surrounded by sil-o-cel refractory and

Jan 1, 1956

By J. A. Berger, R. J. Towner

A method for determining the disorientation between sub-grains that .share a common tilt or twist boundary from measurements on X-ray micrographs is described. The method may be applied to subgrains of almost any orientation having boundary angles in the range from about 1 min to 1 deg of arc. An adaption of the Berg-Barretl method has been made to allow calculation of small angles of about 1 min to 1 deg of arc: between adjacent subgrains from the relative displacement of their images on X-ray micrographs. schulz4 gave equations for determining subgrain disorientation where the axis of subgrain rotation and the reflecting crystal planes were parallel to the specimen surface. In our method, however, they need not be parallel and, indeed, may have va:rious orientations. His camera setup, involving a fine-focus X-ray tube for obtaining high resolution with continuous radiation, was different from the one used in the present investigation (a 1.2 x 1.2 mm effective source and characteristic radiation). The X-rays produced a slight magnification in the subgrain images in the Schulz method, but not in the present method. The commonly available type of X-ray tube used permitted relatively short exposure times with a fine-grained photographic plate, which could be magnified optically many times for the examination of small subgrains. The method is illustrated by results obtained on {110} tilt boundaries in a polygonized aluminum single crystal of 99.994 pct purity. The flat crystal was stretched 6 pct in tension and then heated at 500°C for a cumulative time of 5 hr. Earlier, cahn5 studied subgrains formed by polygonization in stretched and heated aluminum crystals. He observed kink bands to have well defined boundaries lying in (110) planes, at least in the early stages of deformation. Cahn found that the (110) tilt boundaries formed by polygonization were directly related to the lattice bending about the <211> axis which lay in the (111) slip plane perpendicular to the <110> slip direction. DESCRIPTION OF THE CAMERA Our camera was similar in detail to Honey-combe&apos;s.6 Unfiltered copper radiation was used at 35 kv, and 20 ma. With the particular specimen used here to illustrate the method, a 1.2 by 1.2 mm effective source and a distance of 780 mm from target to specimen were employed, giving a convergence of 5 min of arc in the primary beam. The distance was 9.5 mm from the specimen to film. The upper 1/2- by 1-in. portion of the front surface of the specimen was irradiated with the film in parallel position. Since the specimen had been inhomogeneously deformed, many regions were in a position to reflect characteristic radiation at the Bragg Angle. Five minute exposures were satisfactory with Kodak Single Coated X-ray Film, 1 1/2 hr

Jan 1, 1961

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.&apos; In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator&apos;s Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.&apos; Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

By V. N. Krivobor

The study and use of low-carbon manganese steels have been curiously neglected in the general history of developments in alloy steels. Hadfield1 made an extensive study of manganese-iron-carbon alloys about 1886, which culminated in the wide application and use of Hadfield austenitic manganese steel. His alloys were nearly all high in carbon, as compared with the steels discussed in this paper, and he found a marked tendency toward brittleness in the alloys of medium and low manganese content, that is, below 7 per cent. manganese. As a result, there has been a widespread prejudice against the use of manganese steels containing between 1.0 to 3.5 per cent. manganese with comparatively low carbon. Steels of this composition have never been studied adequately in comparison with other alloy steels, and have had litttle use in practice. In a very recent paper by Sir Robert Hadfield2 the following statement appears: 6L... manganese-iron alloys with little or no carbon do not seem to offer any practical employment; they only become valuable in the presence of quite high percentages of carbon, 0.90 to 1.50 percent." The results of the present investigation are so contrary to the findings of Hadfield that the writers feel fully justified in presenting the preliminary report incorporated in this paper. Previous Investigations As early as 1886 the Terre Noire CO.3 in France produced alloys containing up to 2.5 per cent. of manganese, using ordinary low-grade

Jan 1, 1927

By Donald A. Brobst

The minerals barite (BaSO4) and witherite (BaCO3) are the chief sources of the element barium and its compounds needed for many industrial processes and products. Barite, the principal ore mineral, is found the world over and is abundant and widely distributed throughout the United States.3 Witherite is much less common than barite, though more desirable in many ways as a raw material for the production of barium chemicals. England is the chief producer of witherite. Witherite is not mined in the United States at the present time, but it has been mined with barite from a deposit at El Portal, California. Barite is also called barytes, tiff, cawk, or heavy spar. Ordinarily it is a heavy mineral that crystallizes in the orthorhombic system. It is colorless, white, or gray, and transparent to opaque. In some deposits barite is black, yellow, brown, red, green, or blue because of included impurities. The streak is white and the luster vitreous to resinous or pearly. The specific gravity of pure barite (65.7 pct BaO and 34.3 pct SO3) is calculated to be 4.5, but inclusions and impurities in natural barite may reduce this value considerably. Well-formed crystals are generally tabular and have three cleavages. The barite of many deposits, however, has an uneven fracture and an apparent cleavage caused by separation along planes between successively deposited layers. The hardness is 2.5 to 3.5 on Mohs&apos; scale. Commercially the terms "hard" and "soft" are used to refer to ease of grinding. Barite is relatively insoluble in water and acid, and thus can be used as a chemically inert material. Witherite, the natural carbonate of barium (77.7 pct BaO and 22.3 pct CO2), crystallizes in the orthorhombic system. The fracture is uneven and the luster is vitreous to resinous. The hardness is 3 to 3.5. The specific gravity of the pure mineral is calculated to be 4.29. It is transparent to opaque. The color is ordinarily white, gray, yellow, brown, or green. Geology and Distribution of Deposits Workable deposits of barite are widely distributed throughout the world in many geologic environments in sedimentary, igneous, and metamorphic rocks. Most deposits can be classified into three main types: (1) vein and cavityfilling deposits; (2) bedded deposits; and (3) residual deposits. 1. Vein and cavity-filling deposits are those in which barite and associated minerals occur along faults, gashes, joints, and bedding planes, and in breccia zones and solution channels. They also occur in various collapse and sink structures in limestone. Sharp contacts of the veins and cavity fillings with wall rocks are common. Barite cements fault and collapse breccia by replacement of the matrix or by filling voids. Large-scale replacement of the wall rocks beyond ore-controlling structures is rare. Barite in vein and cavity filling deposits is generally dense, "hard," and white to gray. Associated minerals are fluorite, calcite, ankerite, dolomite, quartz, and many sulfide minerals, especially pyrite, chalcopyrite, galena, and sphalerite. Gold, silver, and rare earth minerals occur with barite in some deposits in the western United States. Barite is also a gangue mineral in metallic ore deposits but production as a byproduct from such deposits will be affected by many economic factors. The host rocks are igneous, sedimentary, and metamorphic rocks of pre-Cambrian to

Jan 1, 1960

By C. Kremer Bain

DURING the past several years of diamond drilling in Washington County, Mo., the St. Joseph Lead Co. has discovered a concentration of commercial lead-zinc ore at four different points within an area of 36 square miles. The largest and to date the most promising group of these orebodies is located in the Indian Creek area. It was considered to be of sufficient value to warrant development. The Indian Creek area is in the center of the northern half of Washington County, 11 miles northwest of Potosi, Mo., the county seat. The location is readily accessible from Potosi by car or truck over the all-weather Missouri State Highway No. 114. The topography is one of rolling relief, varying from an elevation of 700 ft above sea level on Mineral Fork and Indian Creek to a maximum of 1176 ft at High Point Tower. It is divided in equal halves between the drainage to Mineral Fork and to Indian Creek. The shaft site at 1060 elevation is on the divide between the two drainage areas. The Indian Creek side is rough and heavily wooded, with only a few cultivated clearings. The slopes to Mineral Fork are more gentle and rounded, with much of the area cleared for farm land. Most of the surface is covered with Potosi and Eminence formations, which show little evidence of any structure. Ore structure was worked out by extensive diamond core drilling, with holes varying in depth from about 700 to 1300 ft. As of Oct. 1, 1950, 218 prospect holes had been drilled within the 36-square mile area. The ore is disseminated galena with considerable accompanying sphalerite in the Bonne Terre forma-tion in the shape of irregular blanket-type deposits. The main controlling structural feature of the outlined mineral zone is a buried pre-Cambrian rhy-olite-porphyry ridge extending partly through the Bonne Terre formation, which laps against the por phyry and also covers it. The mineralized zone parallels and forms an irregular halo around the porphyry ridge and is concentrated in the Bonne Terre formation where the La Motte sandstone is cut out by the porphyry ridge. This is a very common mineral occurrence in the southeastern Missouri lead belt district. The La Motte sandstone, which normally underlies the Bonne Terre formation, is thus cut out entirely. In this area the Bonne Terre is usually about 275 to 320 ft thick, the La Motte varying in thickness from zero up to 400 ft. Commercial concentrations of ore are indicated at several places, the most notable being at the shaft site where an orebody at least 4000 ft long with widths of 500 to 600 ft has been outlined. The total thickness of mineralized rock reaches 150 ft in some holes, although total ore thickness runs from 8 ft to about 60 ft, often in more than one layer. Preliminary Planning Ore reserves as outlined lend themselves to open-stope mining with trackless haulage and mobile loading machines and drilling equipment. This type of equipment has proved to be very efficient during recent years in the company&apos;s lead belt operations. After a study of bids for shaft sinking and an estimation of comparative costs, it was decided that the shaft would be sunk by St. Joseph Lead Co. personnel using company equipment. Since the plant site is about 26 miles from the company&apos;s nearest lead belt operations, it was necessary to plan a complete surface plant, including mill, shops, office, change room, and warehousing facilities. Immediately following the filing of an application for a certificate of necessity, a headframe was selected for which detailed drawings were already available. The order was placed for fabrication so that it could be delivered and erected in time to serve for sinking the shaft. This eliminated the expense of a temporary headframe. Drilling was started on two churn drill holes near shaft location, and two 1000-gpm deep well pumps

Jan 1, 1954

By E. A. Hopkin

Laboratory tests conducted by the author. together with actual field experience in Canada. have indicated the magnitudc of some of the factors affecting ability of drilling mud to clean the hole. A correlation was observed between funnel viscosity and particle slip velocity. A relationship was also observed between the Bingham yield value of the mud and the particle .slip velocity. Laburatury tests indicated little change in slip velocity with funnel viscosities up to ahout 80 sec/qt or to yield values of aboul 15 lb/100 .sq ft. The lip velocity of the partic1e.s. studied vuried from 160 ft/min with water to neerly zero for high mud viscositie. lncreasing the mud density, creating laminar annular mud flow or rotating the drill pipe Mlay also improve the carrying capacity of mud. Field tests indicated that during fast upper-hole drilling, the rate of cutting removal must he sufficien to maintain the concentration of cuttings in the annulus at less than 5 percent by volume to prevernt balled-up drill collars and .stuck drill pipe. INTRODUCTION In the Mid-Continent area, hole cleaning during rotary drilling normally involves the use of low-density drilling muds with funnel viscosities varying from 26 to 80 sec/qt. However, frequently it is necessary to raise the mud viscosity in excess of 200 sec/qt to clean the hole. In addition, field experience has indicated that during very fast upper-hole drilling, annular mud velocities considerably in excess of the maximum slip velocity of the cuttings (normally considered to be 120 to 150 ft/min) are necessary to prevent balling the bit and drill collars. In view of these variations in mud properties and circulation rates necessary to clean the wellbore, a study of factors affecting hole cleaning and the relative magnitude of each was undertaken. The study was also prompted by the knowledge that a drilling mud with properties close to those of water would drill at rates several times that of a viscous mud. The carrying capacity of these near-water muds was not clearly understood, however, and many drillers were reluctant to use them. DISCUSSION EFFECT OF MUD PROPERTIES ON DRILLING RATE The effect of mud properties on drilling rate has been studied by a number of investigators. 1t is clear from their work that mud properties close to those of water will significantly improve drilling rate and bit life. If the water-type mud will also effectively clean the hole and cause no logging or formation impairment problems, the choice of an appropriate drilling fluid is clear—use water. Often, however, a water-type drilling fluid is not capable of effectively cleaning the hole. THEORY OF PARTICLE SETTLING The forces acting on a particle that is allowed to settle through a fluid quickly reach equilibrium, and the particle settles at some constant velocity referred to as the slip velocity. The slip velocity of any particle depends upon a number of factors such as density and viscosity of the fluid, the volume, specific gravity, shape and roughness of the particle, and upon the shape and area of the projected face of the particle at right angles to the direction of relative fluid solid movement. Brown&apos; expressed this relationship for spheres in Newtonian fluids in the following equation. where v, = slip velocity D, — diameter of sphere p, = density of spheye p, = density of liquid /a = friction factor g = constant. The friction factor f, varies as the size, shape, surface roughness and slip velocity of the body, and as the density and viscosity of the fluid varies. WaddelV ound experimentally that where dynamic similarity exists. f, was a function of the particle Reynolds number (NRe) of the sphere (Fig. 1). Fig. 1 shows that f, for spheres varies from over 10 for low NKe numbers to 0.44 for N,,. over 600.

By J. A. Heskett

NEW ZEALAND is dependent on the outside world for its ferro goods, yet it can boast of at least two well-defined iron-ore deposits; namely, Para Para limonite, 3 Fe203 + 21120 also found as lower hydrated oxides, and Taranaki iron-sand, a combined magnetite and ilmenite, 2FeO + 2Fe203 + FeO + Ti02. The former is of massive variety and the FIG. 1.-VIEW OF WORKS SHOWING IRON-SAND DEPOSITS, ALSO WHARF AND BREAK¬WATER IN THE DISTANCE. latter granular and mixed with various proportions of fine shell and siliceous sand well water-worn. This latter deposit forms the greater portion of the beach sands of the west coast of the North Island of New Zealand. It is so fine that the whole of a sample passed through a sieve of 40 meshes to the inch. The ilmenite cannot be detected by the microscope, as in the titaniferous ores of the Adirondacks, nor can it be magnetically separated, as in the titaniferous ore of Natashkwan, Canada. To all appearances it is a chemical compound of the double oxides of iron and titanium and not a mechanical mixture, as is the ore of the Adirondack deposits.

Jan 8, 1920

By Herbert Ives

THE incandescent gas mantle is of considerable interest from the standpoint of temperature measurement because it presents a series of apparent contradictions to the established laws of radiation on which are based some of our best methods of temperature determination. One of these contradictions is that the mantle of least brightness (of the commercial thoria-ceria group) is the one having the highest temperature; this, though explicable without any violation of radiation laws, was long a stumbling block to the understanding of the performance of the mantle. Another anomaly is that the energy radiated by the mantle decreases with the rise of temperature, thus apparently invalidating total radiation methods of pyrometry, based on the fourth-power law. The discussion of methods of measuring mantle temperature which follows, is largely taken from an extensive study of the physics of the Welsbach mantle. 1 The incandescent gas mantle consists of a skeleton of refractory oxide of very light weight and open structure, formed by the ignition of a cotton or silk "stocking" previously thoroughly impregnated with salts of certain rare earths. The mantle of commerce is a mixture of approximately 99 parts of thorium oxide with 1 part of cerium oxide. This mixture, discovered largely by accident, gives luminous radiation many times greater than that from either of the constituents taken alone. It is customary to speak of the thoria as the "base" and the ceria as the "colorant," and the commercial mantle represents one of a family in which an oxide of low emissive power is employed as a base, which will assume a high temperature, while a small amount of some other oxide of high visible emissive power is added, which will reduce the temperature of the mantle but little. This is, in general, the most efficient- way, from the standpoint of visible emission, to utilize a substance of high emissive power in the visible spectrum. But it is not necessary. that two substances should be employed to produce a radiator

Jan 9, 1919

By V. R. Degner

The trend in both the metallic and nonmetallic mining industry is toward processing increasingly higher tonnages of lower grade ores, thereby resulting in a growing interest in progressively larger volume individual machines in the flotation circuit. Because of the relatively high cost of large flotation machine development and evaluation, it is important to establish a rational basis by which the existing smaller flotation machine experience can be extrapolated to establish the configuration of the next larger family of flotation machines with a minimum of development modification in the field. This Paper reviews the R&D approach used in translating smaller flotation machine experience to the configuration of a 28.3 m3 (1000 cu ft) induced air machine. Internal cell hydrodynamic principles, which governed this extrapolation, and cell (liquid) surface and froth management considerations will be reviewed, and prototype machine mill tests will be summarized.

Jan 1, 1981