By R. W. Mancantelli, J. R. Woodward

IN 1947 a large low grade deposit of uranium was located in the northwest corner of Saskatchewan, in the Beaverlodge property of Eldorado Mining & Refining Ltd. Most of the values occur as thin seams and as coatings on other minerals, and the ore, which is light and friable, is not amenable to the usual gravity methods of concentration. The acid leaching process developed to retreat the company's Port Radium tailings was also impractical, as the percentage of carbonates is high and the percentage of sulphides relatively low. Construction of the mill building and installation of equipment, both scheduled for 1952, awaited selection of a satisfactory ore dressing process on or before Oct. 1, 1951. An extensive research program on dressing of ores from the Ace mine therefore was undertaken by the Mines Branch in Ottawa, a research team at the University of British Columbia, and an ore dressing group at the company's Port Hope refinery. Pilot plant operations were conducted at the Ottawa plant of Sherritt Gordon Mines Ltd. under the general direction of C. S. Parsons, consultant on metallurgy and ore dressing for Eldorado. In mid-September, having compared results of the several research programs, Dr. Parsons recommended a process employing a carbonate or basic leach. He reported that, while the chemistry of the process had been proved, engineering of the flowsheet was incomplete, and he suggested that under normal conditions further pilot plant work at the Ace mine might be profitable. However, since this would involve a delay of 12 to 18 months in bringing the property into operation, he recommended that design of the concentrator proceed immediately. Concentrator capacity was determined by two considerations: 1) the amount of ore then available and 2) the expectation that continued improvements would be made in the ore dressing process as a result of the intensive research being carried out by the Mines Branch of the Department of Mines and Technical Surveys. As these improvements could affect both the chemistry and the en-

Jan 1, 1956

By R. F. Hehemann, D. J. Cometto, G. L. Houze

The w transformation in the Zr-Nb system was studied using X-ray diffraction, dilatometric, re-sistornetric, hardness, and metallographic techniques. w forms in a diffusionless, completely reaersible manner on quenching and in a diffusion-controlled manner- on aging. The temperature at which w begins to form on quenching was determined as a Junction of composition and was found to decrease with increasing solute content. w formed bv aging establishes a metastable equilibrium with an enriched ß phase. The ß/w + ß transus has been determined for this metastable equilibrium and employed to rationalize retrogression and reversion phenomena observed in these alloys. The decomposition mechanism is discussed in terms of a gradual or continuous transformation from ß to the w state. BETA- stabilizing alloying elements lower the MS temperature of the martensitic bcc (ß) to hcp (a') transformation in zirconium and titanium alloys. In certain titanium alloys, a lower symmetry modification of the martensitic structure, termed (a"), also has been reported.1,2 These martensitic transformations are suppressed when the amount of the ß-stabilizing element exceeds a critical level. However, the high-temperature ß phase cannot be quenched to room temperature without change. At alloy contents just above the critical level, |ß trans-forms to the w phase when cooled rapidly.3-6 The amount of w in quenched alloys is reduced by increasing alloy content, and this phase virtually disappears above a critical composition.5 In addition to the transformation during cooling, w also can be formed by aging ß at temperatures below approximately 500°C, and significant alloy enrichment of retained 13 accompanies the isothermal transformation.1-8 The structure of LC is closely related to that of the ß from which it forms.9-15 The bcc (ß) lattice can be generated using a hexagonal cell with three atoms located at (000) and ±(2/3, 1/3, 1/3). This cell has an axial ratio of 0.612 and is oriented with respect to the cubic cell such that (0001)H (111)C and [1120]H [101]C. Consequently, there are four possible orientations of the hexagonal cell, associated with the four (111) planes of the bee lattice. Formally w can be obtained from 0 by allowing the two atoms at the ±(2/3, 1/3, 1/3) positions to approach the coordinates ±(2/3, 1/3, 1/2) and there are four equally probable orientations of w for each 0 grain. In titanium alloys w retains the cubic axial ratio of 0.612" and hence also can be indexed as triply cubic, but this is not the case for aged Zr-Nb alloys where w is clearly hexagonal with an axial ratio of 0.622." The lattice parameters and atomic positions of w depend on thermal history and alloy content. The atomic positions (000), ±(2/3, 1/3, 1/2) provide reasonable agreement between calculated and observed diffracted intensities for w in the fully aged condition.10,14 In the quenched condition, on the other hand, the atoms appear to be displaced from the central plane12,13,15 and assume positions ±(2/3, 1/3, Z = 0.42-0.48) rather than ±(2/3, 1/3, 1/2). This results in a structure with trigonal rather than hexagonal symmetry. The readily detectable parameter and axial-ratio changes of w in Zr-Nb alloys make this system especially attractive for studying the structural changes that occur in the formation and aging of w. Particular attention in this investigation has been directed to the relationship between the structure of w in the quenched and aged conditions, and to certain aspects of the reaction kinetics. MATERIALS AND PROCEDURE Zr-5, 12, 17.5, and 25 pct Nb alloys were prepared by a double arc-melting practice, encased in stainless-steel cans and hot-rolled to 1/8-in.-thick sheet.* Charged weights have been employed for the niobium contents and interstitial analyses are reported in Table I. Dilatometric, X-ray diffraction (filtered CuK, and MoK, radiation), metallographic, and hardness techniques have been employed to follow the transformations during isothermal and quench-aging heat treatments. In quenched specimens, the electrical resistivity also was studied. Betatizing was conducted for 1 hr at 900°C. With the exception of the isothermal dilatometric studies, samples were

Jan 1, 1965

By S. C. Sircar, B. K. Dhindaw

KINETICS and mechanism of sulfation reactions have been studied extensively. Qualitative and quantitative data are reported for the kinetics and mechanism of sulfation reaction of copper oxide pellets;''2 yet it remains a controversial Subject. The mechanism and kinetics of the sulfation of zinc oxide powder (B.D.H. analar quality) were studied by gravimetric technique. A spring of high-carbon steel wire with accuracy well within 0.2 mg was used for measuring weight change. The sample was taken in a Pyrex glass bucket, hanging freely inside a Pyrex glass tube reactor, with a gold wire attached to the spring, the reactor being surrounded by a movable furnace (double wound type) with a temperature control within *5"C. Flow of oxygen, 60 cu cm per min, and sulfur dioxide, 45 cu cm per min, were measured through calibrated flowmeters and the mixture dried over PZ05 before entering the reactor. The experimental results are presented in Figs. 1 and 2. The plot of weight change of zinc oxide, giving the amount of zinc sulfate formed, was found to be linear over the temperature range of 500" to 700° C and up to a conversion of approximately 60 pct, as beyond it they divert from linearity.' The rate of sulfation was found to be affected by total flow rate of gases at a fixed ratio of SO2/O2, up to 60 cu cm per min, and was found to be linearly dependent on quantity of total powdered sample taken. The plot of rate of sulfation of zinc oxide, 70 mg, with varying amounts of vanadium pentoxide, at a constant ratio of gases as mentioned above, and at a constant temperature of 625"C, was also found to be linear as seen in Fig. 2. Extrapolation to zero V2O5 addition gives the same rate of sulfation, as in case of pure zinc oxide, 70 mg. Vz05 was prepared by heating ammonium vanadate at 600°C for 15 min in a muffle furnace. The available literature points out that the theory of sulfation that has received the maximum support postulates the following mechanism for sulfation of ZnS: 2ZnS + 30, = 2Zn0 + 2SOZ; the ZnO formed acts as a catalyst for the reaction, 2 S02 + O2 = 2S03. This SO3 reacts with ZnO to give zinc sulfate. It is suggested here that the above widely supported mechanism is operative in the sulfation reaction and that the rate-controlling step in the sulfation reaction of ZnO is the formation of SO3 from SO, and 0,. The authors are carrying on further work in this line, and the details will be published later. The authors wish to acknowledge the facilities provided and the help extended by Prof. P. R. Dhar, Head, Department of Metallurgical Engineering, and the permission granted to publish this note by the Director, I. I. T., Kharagpur.

Jan 1, 1969

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.' Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler's saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.' A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By Arnold Hoffman

A RESPONSIBLE steel executive recently declared that scrap shortages, despite fantastic prices reaching up to $50 per ton, are responsible for the loss of 140,000 tons of steel a month and that in March 1947 alone 25 more steel furnaces could have been operating were it not for scrap scarcities. His answer to this serious situation was to ask for a speedier flow of scrap and also abolition of Government control over pig iron distribution. It would be more logical, perhaps, if an answer to this growing problem of scrap deficiency were sought within the steel industry itself. As long ago as 1933, L. B. Lindemuth, a consulting steel metallurgist, warned the steel industry that a shortage of scrap was inevitable and that beyond 1938, adequate supplies for open-hearth furnaces could not be expected. The outbreak of war, with consequent phenomenal demands on the industry, accelerated production of steel and further worsened the scrap situation. Today we are suffering from a condition which could have been prevented had the industry been more far-seeing and provided for an inevitable contingency. However, better late than never, and measures can now be taken to alleviate permanently scrap shortages in the future. This can be done by greater utilization of heavy sinter which experience proved is an excellent substitute for scrao and lump ore.

Jan 1, 1947

By AIME AIME

TWO weeks ago the writer was lunching in the Engineers` Club in New York with a man who has perhaps the widest acquaintance among engineers of anyone in the country a member of another of the Founder engineering societies. "By the way," lie asked. "who have they nominated for your next president."' "Doctor Becket," I told him- "Oh. that's line," he replied, in a heartfelt tone that rang with sincerity. "I have come in contact with him occasionally and he is just the right type.' And that is the way Dr. Frederick M. Becket impresses everybody. The right type. Most Institute members of the western group of hard-rock minors do not know him, but then they meet him in his swing around the circle next year they will not require a long acquaintance to sense his kindly and outstanding personality, to realize that he is a gentleman in the bet meaning o1 that word, a man of wide sympathies and interests.

Jan 1, 1932

By Harvey Cline, Donald P. Ferriss

THE violent outgassing of commercial tungsten and other refractory metals when melted in an electron beam zone refining apparatus1"3 is dealt with experimentally by one or both of two approaches. One is to provide a suitable emission current control1,2 the other is to purify the metal in the solid state before melting.4 The first of these is usually sufficient, but the authors chose also to investigate the source of the troublesome gases and to devise means of solid-state purification. Some further insights into the use of tungsten as a structural material at temperatures near its melting point were also revealed in the course of the work. One may speculate on the causes of gas formation in tungsten at high temperature by inferences from the literature and an examination of the impurities in commercial wire. Davenport5 observed microporosity in both tungsten and molybdenum filaments heated to several hundred degrees below their melting points. Studying the function of oxygen in molybdenum welds, Perry, Spacil, and wulff8 attributed similar porosity to the disproportionation of Moo2 to molybdenum metal and Moo3. Tungsten dioxide also disproportionates7 above 2000oC to yield WO3 vapor at considerable pressure. Commercial tungsten contains some 5 to 20 wt ppm O and a similar concentration of carbon depending on the details and precautions of processing. Therefore, evolution of CO is also a strong possibility as a source of gas at high temperatures. Furthermore, even for activities in the order of 0.01, it may be calculated that the pressure of CO at 3000°C would be over 4000 psi, which is in excess of the tensile strength of tungsten at this temperature.9,10 Powder metallurgy tungsten contains some 0.02 pet Fe and 0.002 to 0.005 pet of the elements Ni, Si, Al, Ca, Mn, Mg, and Mo; at temperatures over 2800°c, therefore, these elements will exhibit appreciable vapor pressure, though small compared to that of WO3 and CO. Some of these impurities may react to form high-pressure monoxides such as SiO and A10. Finally, dissolved and occluded nitrogen is an ever-present source of high-pressure gas. Commercial Type 218, General Electric filament wires, 0.025 in. diam, were heated by resistance in 10 -4 mm of Hg and in argon or hydrogen at pressures from 50 µ to atmospheric. For temperature determinations in vacuo, the Jones - Langmuir8 current-temperature relationship was employed. For gaseous atmospheres, the burn-out temperature was assumed to be the same as in vacuo so that a small, constant correction could be made for temperatures below burn-out conditions (i.e., local heating to failure). Several dozen experiments may be summarized by pointing out some structural observations. At 3050oC in 1 atm of A, porosity is very evident after 30 min, as shown in Fig. 1. For the section in Fig. 2, failure occurred 200°C below the melting point and many voids have grown in the grain bound-

Jan 1, 1962

By C. H. Mathewson

BERYLLIUM, magnesium, zinc and cadmium, together with mercury, constitute a coherent sub-group of the periodic system and these metals, excepting mercury; have been studied in sufficient detail by the new X-ray diffraction methods to prove their common adherence to the hexagonal close-packed type of crystal structure with a progressive increase in axial ratio as we pass through the group from beryllium to cadmium. The first four columns of Table 1 summarize the data on crystal structure of these metals reported in the International Critical Tables.1 The last two columns are based on results obtained in the present investigation. TABLE 1.-Lattice Constants and Twinning Law of the Be-Cd Group of Hexagonal Metals Dimensions of Unit Axial Cell, A Ratio Description of Twinning Element a° c° (c°/a°) Composition Axis Plane Beryllium 2.28(3) 3.60(7) 1.58 {1012} Probably 1 {1012} Magnesium 3.22 5.23 1.621 ,1 {1012} Zinc 2.65(7) 4.94(8 1.86(2) 11012 } 1 {1012) Cadmium 2.98 5.63 1.88(5) {1012} Probably 1 {1012} Twinning has often been observed in zinc and cadmium. The general aspects of this twinning are abundantly illustrated by photomicrographs, diagrams, etc., in the papers by Romig, and Mathewson and Phillips reported to this Institute in 1927.2. A determination of the composition

Jan 1, 1928

By Frank E. Neil, O&apos

The formation tester, as the name implies, is a tool built for testing the contents of sands encountered in drilling Wells Without actually cementing casing on the sand. The tester was developed in the Mid-Continent and has been in use commercially there since about 1926. However, some two dozen patents have been issued on formation testers dating back to the seventies. The method apparently was an outgrowth of the old Mother Hubbard grain or bean packer, used around casing before the days of cementing casing. These packers were also seated in a tapered hole and if the formation tested was not satisfactory the casing was pulled loose and the hole taken down to another formation. A great deal of experimental work has been done in its development, and as a result of this work the formation tester became an accepted integral part of the petroleum development in California. The formation tester was introduced into California some three years ago by M. 0. Johnston. Months of discouraging and expensive work followed its introduction into this state, but one organization after another tried the tool and its use is now fairly general. Shortly after Johnston began testing in California, the Halliburton tester was also introduced into the state and now another tool is being introduced, the Shaffer-Roles tester. Principle and Operation of Testers The principle employed in all formation testers is that of packing off the fluid in the hole above the formation to be tested and thereby prevent,ing it from having access to the testing tool. This permits the fluid contained in the given formation to have unrestricted access to the tool. It is accomplished by running the tool and packer on the bottom of the drill pipe; the valves in the tool being closed while going into the hole to prevent fluid from entering the drill pipe. The packer is then seated at the desired point, trapping the drilling fluid above it. When this has been done, the valves in the tool are opened and the fluid from the formation is allowed to enter the empty pipe through the tool. If the

Jan 1, 1934

By W. A. Binsacca

The concentrator treats sulfide ore containing lead, copper, zinc, gold and silver, at the rate of 850 tons per 24 hr., and produces lead, copper, zinc and iron concentrates by selective flotation methods. The ore occurs below the oxidized zone along a main fracture, the wall rock of which is either greywacke or calcareous shale. The predominating sulfide minerals are galena, sphalerite, pyrite and chalcopyrite; the others are quartz and calcite. In minor amounts, arsenopyrite, pyrrhotite and hematite occur, and such secondary minerals as smithsonite, chalcocite, covellite, bornite, cerussite and anglesite are detected in the ore, the last two named occurring principally as surface alterations of the galena. The ore is hauled from the mine bins in 10-ton cars which pass over the track scales before entering the car dumper ahead of the crusher plant.' A conveyor belt delivers the crushed ore to the sulfide bin, which has a capacity of 2800 tons. The primary grinding unit consists of two 6 by 12-ft. Marcy rod mills operating in parallel and in open circuit, each taking 425 tons per day. One rod mill discharges into an 8 by 25-ft. Dorr classifier with a 12-ft. bowl and the other into a 6 by 25-ft. Dorr duplex classifier. These classifiers are arranged so that each unit rakes the sands into a 6 by 14-ft. Traylor ball mill, which discharges to the bowl classifier only. The duplex classifier therefore operates in open circuit and the bowl classifier in closed circuit, the overflow of both classifiers furnishing the feed for the flotation section. Other groupings have been tried, but this has been found the most satisfactory. The Marcy mills are driven by 150-hp. slip-ring induction motors with speed reducers to give 17 r.p.m. The Traylor mill operates at a speed of 24 r.p.m. and is driven by a 200-hp. slip-ring induction motor, direct connected to pinion and gear. The bowl classifier operates at a speed of 22 r.p.m., with the bowl rake making 4.5 r.p.m. and the duplex classifier at 31 r.p.m. High-carbon steel rods of Mexican manufacture, 12 ft. long by 3-in. diameter, are used in the Marcy mills, with a resulting consumption of 1.52 Ib. per ton ore. The Traylor mill is fed 3-in. cast-iron balls cast in

Jan 1, 1935

By David Moskowitz, Ira Binder, Robert Steinitz

THE hard refractory borides of the transition elements of the 4th, 5th, and 6th groups of the Periodic System have been the subject of a number of recent investigations.'-' It is well known now that most of these elements form several different borides, and Kiessling8 has summarized the rules which govern to some extent the arrangements of the boron atoms in the various structures. Melting points of a few borides have been published." The systems Fe-B, Ni-B, and Co-B have been reported," but, as these borides are rather low melting, they are outside of the groups of boron compounds considered here. Brewer' has tested the stability of various borides and estimated a number of eutectic temperatures between different borides, but in no case was the complete system of a transition metal and boron investigated. The phase diagram becomes of special importance if the preparation of the borides from the elements in powdered form is considered; the lowest eutectic temperature will determine the first appearance of a liquid phase. Also, the knowledge of high temperature phases, if they exist, is important for the preparation of bodies from these borides by hot pressing or sintering. During the investigation of various metal borides,7 it was found that there were more boride phases existing in the Mo-B system than reported by Kiessling." They occur, however, only at temperatures above 1500°C and were, therefore, not found by him. This led to a study of the equilibrium diagram of the Mo-B system. ranging from 0 to 25 pct B and from room temperature to the liquidus. Part of this investigation was reported during the "Research in Progress" session at the 1952 Annual Meeting of the AIME.11 Raw Materials and Preparation of the Borides The raw materials used were commercial molybdenum and boron powder, both supplied by the Molybdenum Corp. of America. The molybdenum powder was 99+ pct pure? while the boron powder contained about 83 to 85 pct B. A large percentage of the impurities in this powder was oxygen, with the rest formed by iron, calcium, and unknown substances. The low purity of the boron used was, however, not considered detrimental to the final product, as most of the impurities evaporated at the high temperatures at which the borides were formed. The final product always had a minimum purity of 96 to 98 pct (figured as molybdenum and boron), with carbon, iron, and probably oxygen being the remaining products. Carbon is usually present as graphite. The chemical analyses always confirmed the compositions which corresponded to the crystallographic structures as determined by X-ray diffraction, and the boron content of the finished product agreed closely with that of the starting mixture; no boron was lost during the boride preparation. The chemical analysis methods employed for molybdenum and boron were previously described by Blumenthal.12,13 The powders were mixed by hand in the desired proportions, compressed at room temperature under low pressure, and then heated under hydrogen to about 1500" to 1700°C in a graphite crucible to form the borides. Usually, the three well-known borides Mo,B, MOB, and Mo,B,, which are stable at room temperatures, were prepared in this way, and all other compositions were made by mixing these borides in various ratios or by the addition of molybdenum or boron powders for the very low or very high boron contents. Preparation of two-phase compositions directly from the elemental powders was tried only occasionally to check whether equilibrium could be reached in this way. Experimental Procedures The stable borides were mixed in the desired ratios and heated under hydrogen in graphite crucibles to various temperatures. The well insulated crucibles were heated in a high frequency induction furnace. Special care was taken to obtain exact temperature measurement, which proved much more difficult than originally anticipated. It is believed that individual temperature measurements have an error of less than ±25ºC, while melting or transformation temperatures are accurate within ±50°C. The temperatures were measured with an optical pyrometer which was aimed at the closed end of a graphite tube extending down into the crucible. close to the samples. Attempts to measure directly through the hydrogen exit stack failed. The crucible arrangement is shown in Fig. 1. Heating was done at a slow rate to be sure that the temperature inside the crucible was uniform. The specimens were kept at the final temperature for about 30 min. For the investigation of high temperature phases, some samples were quenched. They were heated, without atmosphere protection, in a very small graphite crucible which could be rapidly removed from the high frequency coil, and dropped into water. These quenched samples were afterwards annealed to establish the equilibrium at lower temperatures. The melting points or the positions of the solidus and liquidus lines were determined by heating the specimens to various temperatures and examining them at room temperature for evidence of a liquid phase. These results were checked later on by thermal arrest curves, especially to determine the exact position of the eutectic temperature line. For this purpose about 200 g of the boride were melted in a graphite crucible, in an arrangement similar to Fig. 1. Slow cooling was assured by very good

Jan 1, 1953

By H. Kenworthy, R. B. Fisher, R. G. Knicherbocker, M. M. Fine

The progress made to date in the mineral dressing of complex Arkansas titanium ores is reported in this paper. Concentrates of rutile, a dioxide of titanium, were produced by treating a submarginal ore from the Magnet Cove Rutile Co., Inc., Magnet, Ark. The rutile recovery at present is 45 to 50 pct of the total TiO2, with the possibility of increased recovery with additional research. The work reported herein is part of a general study which will later include results of investigation of other titanium ore bodies in the Magnet, Ark., area. The fragile character of the rutile minerals, the softness of the gangue, the occurrence of pyrite and leucoxene, and the considerable proportion of extremely small size rutile in the presence of montmorillonite- and illite-type clays in the Magnet Cove open-pit mine are the important factors in the mineral dressing of this submarginal rutile ore. History The occurrence of titanium minerals in the Magnet Cove area of Arkansas was recognized as early as 1890, but it was not until about 1912 that any appreciable prospecting for the minerals was undertaken. At that time drilling was begun, a shaft was sunk, and several drifts were driven, but beneficiation to recover the titanium minerals was not attempted. The only successful mining and milling operation of the Magnet Cove rutile deposit was begun in 1932 by the Titanium Corp. of America and continued until 1942. The ore was washed by means of a rotary scrubber and then deslimed in a drag classifier. The discharge was ground in a rod mill, classified, and tabled to recover a rougher rutile concentrate, which was screen-sized and retabled on cleaner tables. The cleaner concentrates were given a reducing roast, screen-sized, and magnetically separated to produce a finished rutile concentrate. Most of the rutile produced during this period was sold abroad. In 1942, the Titanium Alloy Corp. of Arkansas (a subsidiary of the Titanium Alloy Manufacturing Co. of New York) purchased the property and rebuilt the mill. Subsequently, the plant and property were acquired by the Magnet Cove Rutile Co., Inc., of Little Rock, Ark., the present owners. Very little titanium has been produced since 1942. Although the Titanium Corp. activities yielded enough returns to allow continued operation for approximately 10 years, certain factors must be recognized. These are: (1) production of rutile in that period was during a low in the economic cycle which permitted low-cost operation on a small scale, and (2) a considerable portion of the production was above the water level and no drainage problems existed. Prior to this paper there has been no published report of any mineral-dressing investigation of the lower levels of the ore body. Reference is made in another paper1 to an earlier investigation of Magnet Cove rutile by the Rolla laboratory, in which it is stated that recoveries of 12 to 17 pct of the rutile were obtained. The present investigation was undertaken to improve the known milling processes and to provide adequate metallurgical information about the ore treatment. Titanium Technology The titanium mineral of primary interest in the present investigation was the titanium dioxide, rutile. Rutile is one of the industrial minerals whose annual consumption is relatively small but strategically important. The domestic production of rutile was 7100 tons in 1948. The imports of rutile in the same year were approximately 8000 tons.2 A major use of rutile is in the production of welding-rod coatings, for which a product containing a minimum of 92 pct titanic oxide is desired. Other constituents, such as lime, silica, and sulphur, must be held to a minimum, but hard-and-fast specifications for these elements cannot be drawn. It is necessary to incorporate the rutile in a welding-rod coating, make a sufficient number of test welds, and then determine the tensile strength of the weld metal in the as-welded and stress-relieved conditions. Such a test gives

Jan 1, 1950

By F. G. ROCKWELL

ALTHOUGH the diamond as a gem stone dates back many hundreds of years its use industrially, at least to any extend is recent. The old adage: "Use a diamond to cut a diamond" indicates that some industrial use was made of this material in cutting and polishing many years ago. It also put to various other industrial by the Romans. General industrial use however was never developed to any considerable extent until about the time of the first World War. It is definiely known however, that a Swiss watchmaker, M. Leschot by name, invented a diamond drill in or about the year 1862, Today, some 75 or 80 per cent of the total didamods produced are used in industry. There are two main classifications of diamonds : (1) carbonados or "black diamonmds," and (2) diamonds proper.

Jan 1, 1944

By Edgar M. Dunn

Part I. Determination oF Gases in Smelter Flues. General considerations. Regular methods for carbon monoxide, oxygen, nitrogen, moisture. Sulphur oxides-—Methods of Lunge and Hempel tried, and either modified or discarded, with reasons therefor. Gravimetric method developed at Anaconda. Description of apparatus used. Brief notes on Richter and Hawley methods for the direct cietermination of sulphur trioxide. Carbon dioxide, with complete notes on same. Arsenic trioxide. Table of percentages of flue gas constituents found at a Western smelter. Some final notations as to the value of flue gas analysis, in connection with an intelligent log of furnace operations. Part II. Notes on the Determination oF Dust Losses at the Washoe Reduction Works, Anaconda, Mont. Discussion of problem, with description of flue system. Various places and methods for determinations of velocity. Instruments used. Procedure in making determinations for velocity. Soundings of cross-section for depths of dust. Calculation of velocities and areas. Daily volume of gas, and plant operations during tests. Place for dust determinations. Apparatus and methods of 'sampling. Results obtained, with table of daily amount of dust losses. Analysis of dusts for values, from various sampling stations. Complete analysis of composite sample of stack emanation. Last analysis totaled to show form in which present. Discussion of recovery as a commercial proposition. References on Pitot tube and calculations.

Jan 1, 1914

By J. Gordon Parr, G. R. Purdy

The phase boundaries of "TiNi" have been accurately determined by high-tewperature X-ray diffraction and metallo-graphic techniques. The phase (centered at 51 pct Ni) has a restricted range of homogeneity at 500°C, and a much greater range at 800°C. "TiNi" in all alloys containing less than 51 pct Ni decomposes rapidly and reversibly at 36°C to form a previously unreported phase. ThE region of the titanium nickel system corresponding to the phase "TiNi" has been the subject of several investigations.1,2,4-7 Laves and wallbaum1 reported "TiNi" as a body-centered cubic (a2) Phase, and Duwez and Taylor2 determined its para- meter to be 2.986. Duwez and Taylor also reported that "TiNi" decomposed into "Ti2Ni" and "TiNi3" on prolonged heating at 650" and 800°C, which led McQuillan3 to suggest a sluggish eutectoid reaction between "TiNis" and "Ti2Ni". Margolin, Ence, and Nielsen,' working with higher purity alloys, found no evidence of this decomposition. They showed the "TiNi" phase region extending from 49 to 54 pct*

Jan 1, 1962

By F. R. Hensel

Up to the present time few attempts have been made to produce hard nonmagnetic materials by heat treatment of austenitic steels. The usual result has been to cause them to pass into the martensitic stage, thus destroying to a great extent the typical austenitic properties, since this involves a transition of a portion of the iron from a face-centered to a body-centered type of atomic arrangement. High-strength nonmagnetic materials such as might be provided by properly hardening austenite are required in the electrical industry for different machine parts. In Europe nonmagnetic retainer rings for restraining the end-turns of the rotor windings in turbo-alternators have been developed as a special application of high-strength austenite. In testing1 a 28,000-kva. three-phase Siemens turbo generator running at 3000 r.p.m. at full load current, the losses in the short-circuit test were 450 kw. for the magnetic ring and 286 kw. for the nonmagnetic, and the difference should be attributable to the magnetic ring. The differences in temperatures during the same test are given in Table 1 and these show the advantage of a nonmagnetic over a magnetic retainer ring.

Jan 1, 1931

By Tomoyuki Moritani, Atsuyuki Mizuno

A concentration of manganese nodule varies areally from 0 to 30 kg/m2 in the central-eastern deep sea bottom of Central Pacific Basin with depth of 5,600-5,900m, but generally it is low, mostly of the abundance order from 0 to less than some kilograms per square metres through the bottom. A high concentration over about l0kg/m is localized to the northwestern basin, besides "St. 414 Deep Sea Hill" and “GH 76-1 Trought”, and also it is likely related with the substratum of deep sea clay. Nodules are tentatively classified into nine types of Sr, SPr, SEr, Db, Ss/SPs, ISs, IDPs and V, in terms of morphology and surface feature. The types may be related with internal structure, nuculeus, mineral composition, chemical composition, occurrence and areal distribution, and might have resulted from various environmental factors of nodule genesis. The abundance of nodule at each station shows the interesting relation with acoustic records by 3.5KHz and seismic reflection profilings. In both the records, thick transparent layer over about 45m thick yield neither any nor significant amount of nodule. The layer less than 45m relates with abundant nodules up to 30kg/m2, though it yield also very little nodule in some cases. The relation suggests that the formation of nodule most likely could be related with the accumulation rate of the post-middle Eocene sedimentary sequence to some extent and also with other controlling factors. The relation can lead us to the tentative delineation of distribution of nodule deposits in the area. The comparative-consideration with the deposits in GH 74-5 area, just east- ward of the present area, shows the areal peculiarity of nodule genesis in deep sea bottom. The results of chemical analyses will be discussed elsewhere.

Jan 1, 1976

By A. Kaufmann, B. Cullity, G. Bitsianes

T0 determine the bulk of the phase diagram, techniques for melting, thermal analysis, heat treatment, metallography, and X-ray diffraction that have already been described were used.' It proved difficult to get definitive results for most of the alloy system because of the large number of compounds, their high melting points, and their extreme brittle-ness which made metallography difficult. The final phase diagram, essentially as shown in Fig. 1, was issued with considerable trepidation.' The phase relationships at the two ends of the system were defined with satisfactory accuracy. In the central region between U,Si, and USi, there was great uncertainty concerning the melting points and even the composition of the compounds. At the uranium end of the system, it is quite clear that a eutectic exists at about 985 °C and approximately 8 or 9 atomic pct Si. The a-to-8 transformation is not appreciably altered by silicon, but the 8-to-y transformation is raised to about 795°C. There is appreciable solid solubility in y-uranium, as demonstrated by the micrographs of Fig. 2. The occurrence of the E phase was not suspected at first, since the alloys as melted and furnace cooled gave no X-ray diffraction or thermal arrest indication of it. However, suitable metallography revealed a rim around each of the compound particles as shown in Fig. 3. Heat treatment above 600°C revealed that the rim was another phase which formed by peritectoid reaction between uranium and U,Si,. This reaction proceeds slowly and it is difficult to get it to go to completion. Consequently, there is some uncertainty concerning the exact composition of P and the exact peritectoid temperature. On the basis of various metallurgical studies, it was decided that the most probable composition for t was about 23 atomic pct Si. Metallographic examination shows the closest approach to a single phase at this composition. Likewise, density and hardness measurements of heat-treated alloys shown in Figs. 9 and 10 show a change in slope at 23 pct Si. This is revealed most clearly by plotting the difference in hardness or density between chill-cast and heat- treated alloys as shown in Fig. 4. Zachariasen2 was able to index the diffraction lines of P and to determine the arrangement of the atoms in the unit cell. He concluded that the composition must be US. However, it is felt that the metallurgical studies are reliable and that Zachariasen's X-ray work does not furnish positive proof that the P phase exists exactly at the stoichiometric composition U3Si. There are many instances in alloy systems where a phase does not occur at the composition dictated by the molecular structure. It is possible that the chemical analyses used in the present work were subject to some systematic error. This seems unlikely, however, since recent work in several laboratories seems to show excess compound at 25 atomic pct Si.

Jan 1, 1958

Abbey, Robert Graham, District Mgr.. The W. W. Sly Mfg. Co., 50 Church St.. New York, N. Y. '21 Abbott, A. N., Mines Supt., Mazapil Copper Co., LtdConcepcion del Oro, Zac., Mexico. '28 *Abbott, Argyle Campbell, Dev. Dept., E. I. du Pont de Nemours & Co., Wilmington, Del. '29 Abbott, Clarence E., V.P., Charge of Raw Materials, Tenn. Coal, Iron & R. R. Co., 1242 Brown-Marx Bldg.. Birmingham, Ala. '04 Abbott, Louis Benjamin, Chief Engr., Elkhorn Div., Consolidation Coal Co., Jenkins, Ky. '16 Abeel, George H., Jr., Cons. Min. Engr Box 427, Santa Monica, Cal. '18 Abel, Albert E., Asst. to Pres., Valley Mould & Iron Corp Hubbard, Ohio. '19 Abel, Raymond L., Asst. Prof., Dept. of Pet. Refin., Univ. of Pittsburgh Pittsburgh. Pa. '28 Abeel, Leo M., Research Engr., Sullivan Concentrator Chapman Camp, B. C., Canada. '31

Jan 1, 1929

By E. Teghtsoonian, E. M. Schulson

The tensile behavior of bcc ordered P' AuZn single crystals (CsCl structure) has been investigated under varying conditions of temperature, composition, and orientation. Between -0.2 and 0.4 T, multi-stage hardening occurs fm stoichiometric and nonstoichio-metric crystals oriented near the middle of the primary stereographic triangle. At higher and lower temperatures, parabolic type hardening occurs, followed by work - softening at the higher temperatwes. Deviations from stoichiometry give rise to increased flow stresses. Multi-stage hardening was observed for most orientations, except along the [loll-[lll] boundary and near the [001] corner of the stereo -graphic triangle, where parabolic type hardening occurs. Along two slip systems, (hk0)[001] and (, operate simultaneously while in the [001] comer, slip occurs mainly on the system. Electron microscopy of deformed crystals revealed bundles of edge dislocations forming walls approximately Perpendicular to the glide plane. In general the plasticity of 4' AuZn closely resembles the plasticity of bcc crystals. In recent years, considerable interest has arisen concerning the mechanical properties of the CsCl type intermetallic compounds Ag Mg,'- Fe co,' and Ni Al.'-' The compound P'AuZn is structurally similar. It has a low and congruent melting point of 725"~,'" remains ordered up to the melting point,16 and pos-esses a range of solid solubility from 47.5 to 52.0 at. pct Au at room temperature.15 The present paper reports the results of an investigation on the general tensile behavior of material in single crystal form. Some dislocation configurations characteristic of the deformed state are also reported. The results of a detailed study of the slip geometry in AuZn are presented in a separate paper.17 PROCEDURE Alloy preparation, crystal growing techniques, and the procedure followed in selecting specimens of minimum composition variation are reported elsewhere.17 Dumb-bell shaped tensile specimens were prepared by carefully machining single crystals in a jewellers' lathe to a gage length of 0.80 in. and diam of 0.090 in. Back-reflection Laue X-ray patterns and room temperature tensile tests revealed that machining damage could be eliminated by electrochemically polishing 0.005 in. from the machined surface followed by annealing at 300°C for 1 hr. Specimens were polished in fresh 5 pct KCN solution (40°C, 12 v). Experiments were performed by gripping specimens in a self-aligning pin-chuck and threaded collet system, then straining in a floor model Instron tensile machine. All tests were performed in duplicate. Experimental variables included temperature, composition, and orientation. Unless otherwise stated the strain rate was 2.5 x 10"3 per sec. Liquid testing environments included nitrogen (WOK), nitrogen cooled petroleum ether (133" to 293"K), and silicone oil (293" to 488°K). Resolved shear stress-shear strain curves were electronically computed from autographically recorded load-elongation curves. Stress and strain were resolved on the macroscopic noncrystallographic (hkO) [001] system operative under the specific test conditions of temperature, strain rate, and orientation reported earlier.17 RESULTS The temperature dependence of the work-hardening curves is shown in Fig. 1 for gold-rich crystals of 51.0 at. pct Au oriented near the center of the stereo-graphic triangle. Over the range of intermediate temperatures from -200" to 400°K, they are very similar to those classically observed for fcc metals (reviewed by Nabarro et al.).'' The beginning of deformation is characterized by a region of decreasing hardening rate, stage 0, which is followed by a region of low linear hardening, stage I, and then a region of higher linear hardening, stage 11. At the higher temperatures, stage 111 is observed, a region of decreasing hardening rate. Over the intermediate temperature range, the extent of stage 0 and of the slow transition between stages I and I1 decreases with increasing temperature. Total ductility is large, often greater than 300 pct shear. As the temperature is either increased or decreased, the extent of stage I is decreased, giving rise to parabolic type flow and reduced ductility. Similar temperature effects have been reported for bcc ~r~stals.~~-~~ Below -14O°K, hardening is terminated in brittle fracture while above -400°K. initial hardening is followed first by work-softening and then by chisel-edge type ductile fracture. Stoichiometric (50.0 at. pct Au) and Zn-rich (51.0 at. pct Zn) crystals were also tested from 77" to -500°K. The effect of composition on the flow behavior is illus-

Jan 1, 1970