By Thomas T., Read

THE decades immediately before and after the end of the nineteenth century (1890-1910) were a period of increased activity in mineral industry education. One reason for ,this, undoubtedly, was the rapid increase in mineral production in the decade 1880-1890; pig iron and copper production tripled; coal, lead, and zinc output more than doubled. Most of the other mineral substances followed the same general trend. Aluminum production began in 1886; petroleum output, which in 1888 was less than it was in 1882, almost doubled in the next three years. Gold alone showed no appreciable change until its discovery at Cripple Creek in 1891, followed by the Klondike in 1896, brought to boiling a public interest in minerals that had been simmering for some years previously. The first cyanide plant in the United States was erected at Bodie in 1893, and the first chlorination plant at Cripple Creek* the next year. Silver- lead smelting had already greatly developed, and the metallurgy of copper was almost transformed. The hearth area and smelting capacity of copper reverberatory furnaces more than quadrupled between 1878 and 1894; matte converters were first erected at Butte in 1884. Copper production of the United States in 1899 was 30 times that of 1872. While it was the increased technology used in mineral production that really made the field attractive for educated young men, undoubtedly they did not realize that, and were impressed mainly by the quantitative increase in output. Another factor was the increased general interest in engineering education; three times as many men took engineering degrees in the United States in 1890 as in 1880; 1893 showed almost a 56 per cent increase over 1890. Industry had come to recognize that technical training was worth while. The mineral industry lagged somewhat at first; the total number of mining degrees

Jan 1, 1941

By G. B. Gould, F. M. Gibson

IN DECEMBER, 1934, the joint Committee on Fuel Values, of the American Institute of Minim and Metallurgical Engineers and the American Society of Mechanical Engineers, submitted a preliminary report, which briefly stated its conclusion that it was not possible to devise any formula for the valuation of coal, based upon the various physical and chemical properties, that would be generally applicable. That report also listed those chemical and physical properties of coal that are generally recognized to have some effect on its use in steam plants, and those physical characteristics of steam plants which affect, in one way or another the relative importance of the properties of coal used in them. Since then, the Committee has considered and discussed in greater detail the interrelationship of the properties of coal and plant characteristics. The conclusions of the Committee are summarized below, with certain recommendations regarding engineering procedure, which will promote the collection of more easily correlated observations with respect to this subject, and thus advance more rapidly the accumulation of data capable of general application.

Jan 1, 1936

By Per Kofstad, Hallstein Kjöllesdal

The oxidation behavior of niobium (columbium) has been studied in the temperature range 500° to 1200°C and at oxygen pressures of 760,100, 10, 1, and 0.1 mm of Hg. The work comprises kinetic studies of the oxidation as well as structural investigations of the oxidized specimens by means of X-ray diffraction, electron diffraclion, electron microscopy, and metal1ographic techniques. The oxidation reaction has a highly irregular temperature dependence and is unusually sensitive to changes in the oxygen pressure. The complex oxidation behavior is suggested to be due to formation of different Nb2O5 modifications in different temperature regions. During oxidation oxygen is also dissolved in the metal. Formation of oxide whiskers take place on the oxide surface at temperatures above approximately 800°C. VARIOUS aspects of the oxidation of niobium have been studied.l-12 The investigations show that niobium has a complex oxidation behavior, and the oxidation

Jan 1, 1962

By WALTER VOIGTLANDER

FOR nearly 100 years wire rope has been fabricated in much the same way. To the great majority of mine superintendents wire rope is just wire rope, little or no semblance of individuality or identifying characteristics. Such an impression was fairly justified until three or four years ago when a practical means was found of performing or preshaping the wires and strands. This discovery permitted a revolutionary change in wire rope manufacture. Instead of merely twisting a number of wires into a strand, then twisting several strands into a complete rope (which twisting would naturally result in great internal strain, thus reducing the resiliency and over-all efficiency of the completed rope), the preformed wires and strands were laid in place without force or twisting. The obvious result was a rope more nearly approximating mechanical perfection. The applied loads are more evenly distributed throughout the component wires and strands, thus reducing unbalanced wire stresses. This results in a higher safety factor. The fact that preformed rope will not unravel when untied at the ends proves the absence of a torsional stress that exists in ordinary rope. A greater useful allowable stress in the wires is therefore possible in actual operating service.

Jan 1, 1926

By W. R. Hibbard

It has been proposed1 on the basis of slip and flow that the ideal deformation texture of drawn wire for face-centered cubic metals is a (111) direction parallel to the wire axis. Under these considerations, an intermediate [loo] texture is permissible but should eventually change to the stable [Ill] orientation. This theory does not explain why copper and its alloys containing up to about 30 pct nickel, 5 pct zinc and 1 pct aluminum were found to have a double [Ill], [100] texture, while alloys with at least 8 pct zinc and 2 pct aluminum developed essentially a single [Ill] texture.1,2 It does suggest, however, that the [loo] component of the former alloys should disappear with additional deformation.3 Some evidence exists to support this suggestion. Howald4 reported that annealed copper wire previously drawn 93.8 pct and 98.5 pct developed a single [Ill] texture. Since, in wire, the drawn and annealed textures are similar, these wires probably had a single [Ill] deformation texture before annealing. In addition, although cold rolled polycrystalline copper and 80-20 brass were found to form different types of pole figures,5,6 single crystals of these metals when rolled from the stable (110) [112] orientation were found to produce essentially the same polo figure.7.8 It may be, therefore, that while the addition of solute elements changes the path by which the final texture is obtained, the final texture is not changed. Experimental Results The wires remaining from the previous investigation1 already drawn about 50 pct reduction in diameter were further drawn to 86 pct and then to 96.4 pct total reduction in diameter. The textures were determined after these stages by transmission X ray photograms taken with a copper K-alpha beam rotated 0 degrees toward the wire axis. It was found that the ratio of the [111].] and [100] intensities of the double texture in copper and its alloys containing 0.94 pct aluminum, 30.70 pct nickel, 2.61 pct zinc and 4.99 pct zinc increased from about 3:l for the 50 pct reduction to about 9:l for the 86 pct reduction. After 96.4 pct reduction, these wires exhibited essentially a single [lll] texture. Summary Thus, the drawn wire deformation texture of copper and its alpha solid solution alloys containing aluminum, nickel or zinc is essentially a single [Ill] texture as predicted by theoretical considerations of slip and flow.' For copper and its alloys containing up to about 1 pct aluminum, 5 pct zinc and at least 30 pct nickel, an intermediate [loo] component is found after about 50 pct reduction in diameter, but disappears after about 95 pct reduction in diameter. For alpha solid solution alloys containing at least about 2 pct aluminum and 8 pct zinc the single [Ill] texture is developed considerably more easily and is found after about 50 pct reduction in diameter. No explanation of this compositional effect is apparent. Similar work is contemplated for cold rolled and cold compressed alloys. References 1. w. R. Hibbard, Jr. and M. K. Yen: Trans. AIME 175, 126. Metals Tech., Feb. 1948, TP 2334. 2. W. R. Hibbard, Jr. and D. E. Trout, 11: Trans. AIME 185, 620. Jnl. of Melals, Sept. 1949, TN 18. 3. W. R. Hibbard. Jr.: Disc. of R. M. Brick's paper on Deformation Textures, ASM Symp. on Cold Working of Metals, Oct. 1948. 4. T. S. Howald: Disc. of Ref. 1. Trans. AIME, 175, 126. Melals Tech. Aug. 1948, TP 2449. 5. R. M. Brick, D. L. Martin and R. P. Angier: Trans. ASM (1943) 31, 675. 6. 0. Dahl and F. Pawlek: Zlsch. Melall. (1936) 28, 266. 7. C. S. Barrett and F. W. Steadman: Trans. AIME (1942) 147, 57. 8. J. E. Burke and C. S. Barrett: Trans. AIME 175, 106. Melals Tech., Feb. 1948. TP 2327.

Jan 1, 1950

By K. Fallenius

Since 1970 a new series of pneumo-mechanical flotation machines has been developed by Outokumpu Oy. The cells have a completely new type of mechanism based on a recently-developed theory of conditions necessary for dispersion of large amounts of air. The mechanism was developed in 3 cu m cells and scaled to 16 cu m cells. Rotor and stator description, scale-up theory, and practical experience with the 16 cu m cell are presented.

Jan 1, 1976

By H. R. Deeth, C. J. Koenig

About ten years ago nepheline syenite was introduced to the ceramic industry and the material has now found application in the various branches of the industry, namely, as a vitrifying agent in white-wares and as a source of alumina and alkalies in glasses, glazes, and porcelain enamels. Spencel described the early mining and processing developments regarding this material. Since the time of his article many research papers have appeared relating to the usage of nepheline syenite but little has been published relative to subsequent mining and processing methods. A complete indexed review of the literature was issued recently by Ohio State University.2 Since "Lakefield" nepheline syenite from Blue Mountain, Ontario (Fig I); is the only commercial ceramic-grade nepheline syenite now being marketed on this continent, discussion is limited to this operation carried on by American Nepheline Limited, Lakefield, Ont., and its subsidiary in the United States, American Nepheline Cory. at Rochester, N. Y. The Deposit Blue Mountain is a long ridge rising to an elevation of about 350 ft at its highest point above the surrounding country and extending for about six miles in a northeasterly direction across Methuen township, Peterborough County. The rock of the Blue Mountain central alkaline intrusive is fine grained, light colored and of even granitic texture. The solidified mass consists predominately of the minerals albite, nepheline and microcline in order of abundance. The average mineralogical composition for the deposit obtained by a study of 112 samples taken regularly over the whole formation is as follows:3 Volumetric Mineral Per Cent Albite.................... 54 Microcline................ 20 Nepheline................ 22 Muscovite................ 2 Mafics.................... 2 (Biotite, hastingsite, magnetite) Total................... loo The mineral nepheline (or nephelite) belongs to the feldspathoid group but is lower in silica content than are the feldspars. It is a silicate of soda, potash, and alumina (NaKAl2O32SiO2). Its presence with albite (Na2oA12O3 6SiO2) and microcline (K2O A12O3 6SiO2) gives the Blue Mountain deposit an alkali content of 15 pct and an alumina content of approximately 24 pct. While this huge alkaline mass is somewhat variable mineralogically, it has a uniform chemical composition. When the iron, mostly in the form of magnetite, is removed during processing, a remarkably uniform finished product is obtained. Geological surveying has disclosed many million tons of nepheline syenite in the Blue Mountain deposit. Diamond drilling in the area where mining is now being carried out indicates a block of about one million tons.

Jan 1, 1949

By Lendall P. Warriner, Blandford C. Burgess

Jasper County lies just north of the geographical center of Georgia, bounded on the west and north by the Ocmulgee River. The county seat, Monticello, is approximately 65 miles east-southeast of Atlanta and 40 miles north of Macon. It is served by the Macon-Athens branch of the Central of Georgia Railway Co. and by five paved highways converging from adjoining county seats. Farming and lumbering are the principal local occupations. About half the county is covered with pine and mixed hardwoods; a large part of the forested land is owned by the Soil Conservation Service of the Department of Agriculture in its Piedmont Land Utilization Project. The topography is one of gently rolling field and forest with occasional hills rising 100 ft or: more above the creek beds. Though annual rainfall is in the neighborhood of 60 in., most of it falls in torrential downpours of short duration which tend rapidly to erode the red soil and convert the country roads to greasy tracks of red mud.

Jan 1, 1949

By F. N. Rhines, W. S. Pellini

In many of the otherwise well established alloy phase diagrams the solidus curves (temperatures at which liquid first appears upon melting) have not been located accurately, chiefly because the experimental techniques that have been most popular for determining solidus temperatures have been both cumbersome and subject to large errors. C. E. Homer and H. Plummerl have described a sensitive and at the same time a very simple technique for locating the solidus curves in a number of alloys of tin. Their method consists simply in noting the temperature at which a specimen of the alloy ruptures under the influence of a light bending force. Although this method is not new, it has been little used for this purpose in the past; nevertheless, it appears so attractive in its possibilities of speed, simplicity, and precision that the investigations presently to be described were undertaken to verify its merits. The redetermination of the solidus and eutectic temperatures of the lead-antimony system was employed as a medium of experimentation. New values obtained in this way are believcd to be sufficiently precise to warrant a revision of the currently accepted lead-antimony phase diagram (Fig. I). Determinations of the solidus of the lead-rich lead-antimony alloy series have been published by X. S. Dean2 and by E. E. Schumacher and F. C. Nix. Their points are represented in Fig. I. In their work the solidus was not located at antimony collcentrations greater than 2 per cent; the curve was presumed to meet the eutectic horizontal at an antimony concentration of about 2.5 per cent. In the present studies the solidus has been traced to 3.5 per cent, where the eutectic horizontal is intersected (Table I and Fig. I). Within the range investigated by Dean and by Schumacher and Nix the agreement with their values is good. H. Seltz and B. De Witt,4 on the basis of activity measurements, have calculated that the intersection of the solidus and the eutectic reaction horizontal should lie at 3.86 per cent of antimony. The following determinations of the eutectic temperature have been reported: Roland-Gosselin,5 228°C.; Ewen,6 228OC.; J. E. Stead,7 24g°C.; Campbell,8 228°C.; W. Gontermann,9 245' to 252°C.; R. Loebe,lo 245°C.; E. Heyn and 0. Bauer,ll 245°C.; H. Endo,12 250°C.; R. S. Dean,= 247' to 258°C.; E. Abel, O. Redlich, and J. Adier,13 245°C.; W. Broniewski and L. Sliwowski,14 250' to 252°C.; H. Seltz and B. De Witt,4 25o°C. A temperature of 247°C. appears to have been generally accepted in recent years; it is the value most frequently obtained by the method of cooling curves. Values below 247°C. have usually been obtained by inferior cooling-curve techniques; those above 250°C., by the method of heating

Jan 1, 1943

By W. S. Pellini, F. N. Rhines

In many of the otherwise well established alloy phase diagrams the solidus curves (temperatures at which liquid first appears upon melting) have not been located accurately, chiefly because the experimental techniques that have been most popular for determining solidus temperatures have been both cumbersome and subject to large errors. C. E. Homer and H. Plummerl have described a sensitive and at the same time a very simple technique for locating the solidus curves in a number of alloys of tin. Their method consists simply in noting the temperature at which a specimen of the alloy ruptures under the influence of a light bending force. Although this method is not new, it has been little used for this purpose in the past; nevertheless, it appears so attractive in its possibilities of speed, simplicity, and precision that the investigations presently to be described were undertaken to verify its merits. The redetermination of the solidus and eutectic temperatures of the lead-antimony system was employed as a medium of experimentation. New values obtained in this way are believcd to be sufficiently precise to warrant a revision of the currently accepted lead-antimony phase diagram (Fig. I). Determinations of the solidus of the lead-rich lead-antimony alloy series have been published by X. S. Dean2 and by E. E. Schumacher and F. C. Nix. Their points are represented in Fig. I. In their work the solidus was not located at antimony collcentrations greater than 2 per cent; the curve was presumed to meet the eutectic horizontal at an antimony concentration of about 2.5 per cent. In the present studies the solidus has been traced to 3.5 per cent, where the eutectic horizontal is intersected (Table I and Fig. I). Within the range investigated by Dean and by Schumacher and Nix the agreement with their values is good. H. Seltz and B. De Witt,4 on the basis of activity measurements, have calculated that the intersection of the solidus and the eutectic reaction horizontal should lie at 3.86 per cent of antimony. The following determinations of the eutectic temperature have been reported: Roland-Gosselin,5 228°C.; Ewen,6 228OC.; J. E. Stead,7 24g°C.; Campbell,8 228°C.; W. Gontermann,9 245' to 252°C.; R. Loebe,lo 245°C.; E. Heyn and 0. Bauer,ll 245°C.; H. Endo,12 250°C.; R. S. Dean,= 247' to 258°C.; E. Abel, O. Redlich, and J. Adier,13 245°C.; W. Broniewski and L. Sliwowski,14 250' to 252°C.; H. Seltz and B. De Witt,4 25o°C. A temperature of 247°C. appears to have been generally accepted in recent years; it is the value most frequently obtained by the method of cooling curves. Values below 247°C. have usually been obtained by inferior cooling-curve techniques; those above 250°C., by the method of heating

Jan 1, 1943

By J. Chipman, N. J. Grant, H. L. Bishop, H. N. Lander

Data of several studies on the equilibrium between molten iron and open hearth-type slags have been combined to determine some of the chemical reactions involved in steel-making. Effects of slag composition and temperature on the iron oxide activity, distribution of sulfur between slag and metal, and the carbon content of the metal are discussed. Also, an overall reaction for the equilibrium between sulfur and oxygen is presented. DURING the past 15 years, a number of significant equilibrium studies have been carried out between liquid iron and simple basic and acid slags in an effort to throw light on the chemical reactions involved in steelmaking. This paper is a summary of the experimental reports on investigations which have been conducted at the Massachusetts Institute of Technology, and of related work in other laboratories. The investigations summarized in this paper include the works of Fetters and Chipman1 and Taylor and Chipman,' which dealt with simple slags that are similar to those found in the open hearth. The sulfur determinations of the slag-metal tests of Fetters and Chipman as reported by Grant and Chip-man" are included. Also, the investigations by Win-kler and Chipman' and Grant and ChipmanQ f more complex slag systems are included in this summary. The experimental procedure is described in detail in each of these papers and will not be discussed. Since the previous reports have been somewhat independent, it is desirable to review and combine the data of the various investigations to determine, as accurately as possible, the reactions in the slag-metal systems of the open hearth. It is the object of this report to present the combined data in such a way as to enhance their utility and applicability. Oxidizing Power of Slags of the System (CaO+MgO)-Si0,-FeO in Equilibrium with Carbon-Free lron The slags selected to determine the iron oxide activity in equilibrium with pure liquid iron were those containing less than 2 pct each of P,O,, MnO, or A1,0, on a weight percentage basis. The method used to calculate activities of iron oxide in liquid slags was that developed by Taylor and Chipman.' The solubility of oxygen in molten carbon-free iron under pure iron oxide slags can be expressed by the following eauation —6320 log (pctO)-------------— + 2.734 [1] where T is the absolute temperature. The oxygen solubility values as determined from Eq. 1 were used throughout this study to calculate the iron oxide activity. The iron oxide activities of slags of various iron oxide contents are plotted in Fig. 1 as a function of the basicity, which is defined as the ratio (pct CaO + pct MgO)/pct SiO,, and are based on molecular percentage values of the components. The percent (FeO), is the total iron content in the slag calculated to FeO. Fig. 1 shows that as the basicity increases at constant mol pct (FeO),, the iron oxide activity increases rapidly and reaches a plateau which extends on the basicity scale from about 1.3 to 2.3; the iron oxide activity then decreases rapidly until a basicity of about 3.0 is reached, where it tends to level off. The solid portions of the curves represent the experimental data of Fetters and Chipman and Win-kler and Chipman. Their experimental heats were made in magnesia crucibles, and hence the slags were saturated with magnesia. The broken lines on the left represent the experimental data of Taylor and Chipman, who used a rotating crucible. In general, these slags contained less than 3 pct MgO. The absence of data for slags containing less than about 40 mol pct (FeO), and basicity ratios greater than about 2.5 made it necessary to calculate curves using ionic concepts of slags. The broken lines on the right, which disregard the solubility limits of di and tricalcium silicate and lime, were obtained by following the treatment of Flood and Grjotheim,"

Jan 1, 1957

By W. F. Holbrook

IN a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 pen cent MgO slags over the range 1475° to 1525° C is included The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple Twelve-gram charges of 0 8 per cent sulphur-metal and 5-gram charge-, of slag were subjected to heating for 30 nun at a prescribed temperature The charges were analyzed for sulphur content For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal Six slag and metal charges were made coincidentally in 5/8-in holes in a section of an electrode graphite rod One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO SLAGS WITH MAGNESIUM OXIDE CONSTANT 15 Per cent MgO -The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SI02, 5 to 27 per cent A1203 and 24 to 53 per cent CaO Variation in composition has been in steps of 2 per cent over much of the area Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered m steps of 4I per cent and even

Jan 1, 1938

By Walter R. Hibbard, Cyril Stanley Smith

IN 1929 one of the authors1 determined the constitution of copper-silicon-manganese alloys contailling over go per cent copper. Through a combination of circumstances the presence of the copper-silicon kappa phase was overlooked in both binary and ternary systems. In the binary system the omission has already been rectified.2,3 To establish the limits of this phase in the ternary system, the samples that had been heat-treated at the time of the original research have now been re-examined, using more careful technique. Full details of the compositions used and the temperatures and times of heat-treatment are to be found in the earlier paper.2 The etching reagent now used to distinguish the kappa phase had the following composition: hydrogen peroxide (30 vol.), 2o c.c.; water, 25 c.c.; 20 per cent potassium hydroxide solution, 5 c.c.; ammonium hydroxide (0.90 sp. gr.), 50 c.c. 'I'able I lists the newly observed structures. In virtually every case the constituents are the same as those previously recorded, except where kappa is now shown to be present as a result of the improved etching technique. X few other changes will be noted (No. 138 at 450°C., No. 147 at 550°C., Nos. 153 and 149 at 75o°C.). The change from liquid to beta in equilibrium with kappa in No. 137 at 800°C. is based upon newly heat-treated samples. The alloy is very near the solidus at 800°C. and probably there was a slight error in the old heat-treatment temperature. The isothermal phase diagrams shown in Figs. I to 6 were reconstructed on the basis of the new studies. The presence of manganese does not greatly change the composition limits of the kappa phase or cause the K-a + Y change to occur at a markedly different temperature. There is some uncertainty regarding the range of existence of beta, for alloys were not spaced very closely in composition. The proposed diagrams, however, are in accordance with the available experimental data and with the dictates of the phase rule. Theoretically necessary fields with no experimental points are delineated by dotted lines. The alpha boundaries at all temperatures are shown together in Fig. 7. This includes also some additional points on the alpha boundary at 300' and 350°C., which were obtained as a result of electrical-conductivity measurements. Two series of seven alloys with increasing manganese content but with silicon constant at 1.90 + 0.03 per cent or 2.42 ±. 0.05 per cent were cast in ingots of 3-in: diameter. These were hot-rolled, homogenized and drawn to wire, finished at 0.08-in. diameter with a 61 per cent reduction of area following annealing at 700°C. Conductivity determinations were made before and after annealing for 30 days at 300°C. or 21 days at 350°C. Figs. 8 and 9 show the change of conductivity produced by this annealing, plotted against manganese

Jan 1, 1942

By Walter R. Hibbard, Cyril Stanley Smith

IN 1929 one of the authors1 determined the constitution of copper-silicon-manganese alloys contailling over go per cent copper. Through a combination of circumstances the presence of the copper-silicon kappa phase was overlooked in both binary and ternary systems. In the binary system the omission has already been rectified.2,3 To establish the limits of this phase in the ternary system, the samples that had been heat-treated at the time of the original research have now been re-examined, using more careful technique. Full details of the compositions used and the temperatures and times of heat-treatment are to be found in the earlier paper.2 The etching reagent now used to distinguish the kappa phase had the following composition: hydrogen peroxide (30 vol.), 2o c.c.; water, 25 c.c.; 20 per cent potassium hydroxide solution, 5 c.c.; ammonium hydroxide (0.90 sp. gr.), 50 c.c. 'I'able I lists the newly observed structures. In virtually every case the constituents are the same as those previously recorded, except where kappa is now shown to be present as a result of the improved etching technique. X few other changes will be noted (No. 138 at 450°C., No. 147 at 550°C., Nos. 153 and 149 at 75o°C.). The change from liquid to beta in equilibrium with kappa in No. 137 at 800°C. is based upon newly heat-treated samples. The alloy is very near the solidus at 800°C. and probably there was a slight error in the old heat-treatment temperature. The isothermal phase diagrams shown in Figs. I to 6 were reconstructed on the basis of the new studies. The presence of manganese does not greatly change the composition limits of the kappa phase or cause the K-a + Y change to occur at a markedly different temperature. There is some uncertainty regarding the range of existence of beta, for alloys were not spaced very closely in composition. The proposed diagrams, however, are in accordance with the available experimental data and with the dictates of the phase rule. Theoretically necessary fields with no experimental points are delineated by dotted lines. The alpha boundaries at all temperatures are shown together in Fig. 7. This includes also some additional points on the alpha boundary at 300' and 350°C., which were obtained as a result of electrical-conductivity measurements. Two series of seven alloys with increasing manganese content but with silicon constant at 1.90 + 0.03 per cent or 2.42 ±. 0.05 per cent were cast in ingots of 3-in: diameter. These were hot-rolled, homogenized and drawn to wire, finished at 0.08-in. diameter with a 61 per cent reduction of area following annealing at 700°C. Conductivity determinations were made before and after annealing for 30 days at 300°C. or 21 days at 350°C. Figs. 8 and 9 show the change of conductivity produced by this annealing, plotted against manganese

Jan 1, 1942

By John B. Mertie

MONAZITE formerly was described as moribund, but, in the light of recent developments, it is no longer so. It is the common source of the rare earths and thorium, both of which are becoming progressively important in industrial and other applications. Moreover, by the action of foreign governments, the sources on which the United States has depended for its supply are now either restricted or cut off entirely. Monazite has thus become a scarce mineral and processors in this country are endeavoring to acquire it from all available sources. RARE EARTHS AND THORIUM The rare earths proper, as defined by spectroscopists, are the oxides of cerium, praseodymium, neodymium, prometheum, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium and lutecium, with atomic numbers ranging respectively from 58 to 71. Chemists include with the rare earths scandium, yttrium, and lanthanum, with atomic numbers respectively of 21, 39, and 57. Thorium, with an atomic number of 90, is analogous to lanthanum, in that it precedes a second group of elements, whose oxides constitute the "rare earths of higher order." These are protactinium, uranium, neptunium, plutonium, americium and curium, with atomic numbers ranging respectively from 91 to 96. The last four mentioned are artificially prepared elements that so far have not been detected in nature. The rare earths with odd atomic numbers, except europium and lutecium, have no natural isotopes; and the two exceptions have only two isotopic forms. Those with even atomic numbers have from 4 to 7 natural isotopes. Samarium148 is radioactive, disintegrating over a half- life of 1.4 X 10 11 years with the emission of alpha rays. Lutecium176 is weakly radioactive, disintegrating over a half-life of 2.4 X 1010 years, with the emission of beta and gamma rays. At least 64 radioactive isotopes of the rare earths proper have been artificially prepared. Thorium is a strongly radioactive element, with a half-life of 1.39 x 1O10 years, which disintegrates through a series of 14 isotopes of 10 elements. The two longest lived and most important of these are

Jan 1, 1949

By P. R. Sperry

In an investigation of the decomposition of the solid solution in a cold worked high-purity aluminum alloy containing 7 pct Mg, aged at temperatures from 30o to 82°C, the nucleating sites at the earliest stages of precipitation were observed to be of two types. Nucleation occurred at the high angle grain boundaries both when the alloy was initially cold worked and when solution annealed. Nucleation also occurred at certain unique deformation markings which began to appear in abundance at approximately 30 pct reduction in thickness by cold rolling. These deformation markings were identified as deformation (kink) bands rather than as the usually assumed "slip planes." Zn material that was cold rolled 15 pct, only the grain boundary Fig. 2—A1-7 pct Mg alloy, cold worked 60 pct and heated at 230° C for 5 min. Etched with Perryman's reagent. X500. Reduced approximately 25 pct for reproduction. (a) Bright field illumination, precipitate deeply pitted. (b) Phase contrast, showing slip markings.

Jan 1, 1962

By J. L. Rodda, M. L. Fuller

In connection with an investigation in this laboratory on the high-zinc side of the copper-zinc system, it was observed that well developed segregate structures of the Widmansttten type were formed when a secondary phase precipitated from the solid solution of copper in zinc. This paper presents an analysis of the crystallographic relationship between the segregate and the solid solution matrix. The data to be presented are an interesting addition to the literature on segregate structures in that the plane of segregation is one of the less densely populated planes. In agreement with the generalization of C. H. Mathewson and D. W. Smith' the plane of segregation in the matrix contains the direction of closest atomic packing of the lattice. Furthermore, the matrix and the segregate are both hexagonal close-packed, which has not been reported hitherto in the 1iternture.l The increasing commercial importance of zinc alloys containing copper makes this fundamental study of value to the metallography of zinc alloys. Zinoeich Copper-zinc Alloys Copper enters into solid solution with zinc to at least 1.8 per cent at 400" C., according to W. M. Peirce.3 The solubility is less at lower temperatures. Thus a solid solution of copper in zinc, saturated at an elevated temperature, will precipitate the excess copper in a separate phase at a lower temperature, conditions of concentration, time, and temperature being suitable. The nature of these two phases has been established by the X-ray method of crystal analysis. Westgren and Phmgmén4 and also Owen and Preston5 have shown that the solid solution eta (7) is of the substitu-tional type with copper atoms replacing zinc atoms on the hexagonal

Jan 1, 1933

By G. B. WATERHOUSE

THE year 1929 was exceedingly busy and prosperous for the iron and steel industry in the United States. The lake shipments of ore were approximately 65,000,000 tons, steel ingots produced were about 57,000,000 tons. Plants were very active. operating for many months well over their rated capacity, slowing down during the last quarter following the severe break in the stock market. The ore tonnage mentioned above was the greatest ever shipped by lake from the Lake Superior region. The trend at the ore mines has been to supplement manual labor by mechanical appliances as much as possible. Mining methods have been greatly improved along the lines of safety as well as to increase the percentage of ore recovery. Crushing and grading of iron ores continued to gain in popularity inasmuch as remarkable blast-furnace operations and records were obtained with sizing and uniformity of raw materials. Progress was made along other lines. The Bradley process for the separation of manganese osicle and iron oside from siliceous manganiferous iron ore was cleuelopecl; also considerable work was clone on a process for the beneficiation of the Cuban laterite ores. Sintering of ores and concentrates increased in popularity. A new analytical method for the deter- mination of sulfur in iron ore was worked out which reduced the time required appreciably. The ore re- serves of the Lake Superior district continued to receive considerable attention and played an important part in the recent mergers which have taken place in the iron ancl steel industry.

Jan 1, 1930

By Luther Wagoner

Having given in a former paper1 the results of assays of sea-water, bay-mud, dredgings from San Francisco bay, etc., and believing it might be interesting to extend the work to include some deep-sea dredgings, I procured from the Smithsonian Institution six samples taken by the U. S. steamer Albatross, and marked as follows: Depth in No. station. Locality. Latitude. Longitude. Fathoms. 1. 2103. Off Delaware bay. 38' 47' 20" N., 72o 37' W., 1,091. 2. 2265 to Between Chesapeake 35° 37' N., 74O to 75O W., 49 to 70. 2297. bay and Hatteras. 3. 2420. Off Chesapeake bay. 37' 03' 20" N., 74O 31' 40" W., 104. 4. 2528. East of Georges 41° 47' N., 65o 37' 30" W., 677. bank. 5. 2572. SE. of Georges bank. 40° 29' N., 66O 041 W., 1,769. 6. 2681 South of Nantucket. 39' 43' N., 70' 29' W., 990. The above samples were assayed by the cyanide-method, described in my former paper (p. 807), about 30 g. of sample being used, and the following results were obtained: Value in Milligrams Per Metric Ton. No. Station. Gold. Silver. 1. 2103. 145 1,014 2. 2265 to 2297. 44 304 3. 2420. 15 353 4. 2628. 267 1,963 5. 2572. 125 377 6. 2681. 66 414 No. 4, Station 2528, consisting of red clay and volcanic ash, mas re-assayed ; 35 g. was roasted at a low heat for one hour and weighed 34.05 g. after roasting; the color was changed to a deep brick-red; and when assayed by the cyanide-method

Jan 1, 1908

By E. I. Larsen, F. R. Hensel

According to statements by Guertler1 Smith and Hamilton were the first to study the copper-titanium alloys, but owing to the presence of large amounts of impurities their data are inconclusive. M. A. Hunter and I. W. Bacon later investigated the electrical conductivity and the temperature coefficients at room temperature. The present writers reported their results2 in November, 1930. Recently Kroll published data on copper-titanium alloys3 which agree closely with those obtained by the authors. Material Tested The titanium used was in the form of square sintered rods, the analysis of which runs as follows: titanium, 95.4 per cent; silicon, 0.7; iron,l.8; aluminum, 1.4; copper, 0.1; manganese, 0.05. The ingots were prepared in a high-frequency induction furnace in air atmosphere. Their analyses are given in Table 1. Up to 5 per cent titanium the alloys could be forged. Above that amount they were red short and broke up easily. Owing to their rapid absorption of nitrogen and oxygen from the air, the alloys with the higher amounts of titanium tend to form surface films which greatly increase the casting difficulties, especially when small masses of metal are handled. It was, however, possible to prepare sound ingots up to 25 per cent titanium. Thermal and X-ray Investigation The cooling curves of some of the alloys are plotted in Fig. 1, and R tentative diagram constructed from these data is given in Fig. 2. From this it is evident that the solid solubility of copper for titanium is approxi-mately 4 to 5 weight per cent titanium at 878" C., which is the eutectic temperature. The melting point of copper is lowered gradually by adding

Jan 1, 1932