By Wayne Bell, Matthew Andriese, Shuqian Xie, Jiann-Yang Hwang, Zhiwei Peng

"Pyrolyzed carbons are generally known as good microwave absorbers and their dielectric properties still remain to be fully explored. In the present study the dielectric properties and dielectric polarization-relaxation phenomenon of a typical activated carbon was investigated. The experimental results indicate the complex permittivity is highly dependent on temperature and frequency. The decrease of permittivity with increasing temperature from room temperature to ~100 °C is probably ascribed to the release of the water vapor adsorbed on the surface of activated carbon, and the variations of permittivity with temperatures between 100 °C and 450 °C in the frequency range of 300 MHz to 3000 MHz are mainly attributed to the decreased relaxation time of dielectric polarization.IntroductionPyrolyzed carbons have been identified as excellent microwave absorbers owing to their high dielectric and electrical loss under microwave irradiations. Among them, activated carbon continues to attract more and more attention from researchers. Due to its special physical properties, the production, modification and regeneration of activated carbon with the assistance of microwave have been widely studied over the last few decades [1-6]. However, only few attempts have been applied to explore the dielectric properties of such materials due to the complexity and variability of their organic precursors and activation processes [7,8]. In order to shed a light on this problem, a typical sample, Norit® A Supra USP powdered activated carbon, was adopted to perform dielectric characterization, which may provide useful information for its wide application in the fields of purification, energy (hydrogen) storage and so on."

Jan 1, 2011

By Samson Adeosun, Sanmbo Balogun, David Esezobor

"Iron and steel making processes give rise to large amounts of usable and unusable materials, the latter generally being termed wastes. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. This paper defines the concept of “waste-free technology”, discusses its development in the steel industry and highlights the benefits of the technology to the manufacturing sector and the environment. The paper also articulates how the “waste-free” technology could be applied in the proposed Ajaokuta integrated steel plant in Nigeria.IntroductionIn the past, nature was considered an inexhaustible store. Its resources were consequently exploited and waste products therefrom were discarded. Today, attitudes have not changed appreciably even as raw materials cost rise by the year to pose a series of socio-economic problems, which, among others, may include the rational and optimum utilization of resources, environmental protection and reduction of waste formation. Consequently, industrialists now face unexpected regulatory pressure in areas of pollution prevention, waste minimization and hazardous waste disposal.Iron and steel making processes give rise to significant amounts of usable and un-usable materials, the latter generally being termed waste. It is sometimes difficult to distinguish between re-usable by-products and wastes which cannot be sold or land-filled. Much depends on circumstances such as the local market for the material. This can itself vary from time to time with by-products which cannot be used or sold becoming wastes and vice versa. In this paper, the term waste refers to those materials that are either irrationally utilized or, land-filled and part of the byproducts that are not utilized. It includes that part of used materials which is not incorporated into the products manufactured during a process stage and which in contrast to reuseable materials, is considered not suitable for any further use, owing to technical or economic factors. In general, these materials are inorganic and parts of them are either utilized or passed to the other processes; the other part should be disposed of using well-established waste disposal practices to avoid any environmental threat.Thus, creative methods must be developed to modify the manufacturing processes to reduce emissions and process wastes by fully utilizing all resources. One method of eliminating the negative effect of waste formation is the use of purification and cleaning structures (pollution control system, PCS). These are, however, quite expensive."

Jan 1, 2008

By G. Lissens

In this work the electrochemical combustion of dissolved organic species in a single compartment cell containing a titanium mesh cathode and a boron doped diamond anode has been studied, The organic molecules involved were complexing agents such as EDTA (ethylenediaminetetraacetic acid) or NTA (nitrilotriacetic acid) used in metal plating shops and bright nickel plating bath additives, From batch experiments, it is shown that complete decomplexing of EDTA and NIA is feasible. Complete TOC (Total Organic Carbon) removal from solutions containing 0.01 M EDTA, 0.02 M NTA and bright nickel plating bath additives could also be achieved. Recycling experiments show that decomplexing of EDTA and NTA solutions can be obtained at an average electrical energy input of ~20kWh.kg-1 of complexing agent. Decomplexing rates of respectively 3.l3 mmol.Ah-1 for EDTA and NTA have been obtained, The Instantaneous Current Efficiency (ICE) was 71% for EDTA and 95% by NTA, Simultaneous recovery of Cu from a 0.01 M Cu-EDTA solution has also been evaluated. A solution (1.8 dm3) containing 0.01 M EDTA and 528 ppm of Cu was treated in a single compartment cell at a current density of 2 A.dm-2. 73% of the TOC could be removed and a final copper concentration of 8 ppm was obtained.

Jan 1, 2003

By M. T. Thomas

Sufficient development of the X-Ray Photoelectron Spectroscopy (XPS), the Auger Electron Spectroscopy (AES), and the Secondary Ion Mass pectroscopy (SIMS) has made these instruments ideal for solving problems related to mineral processing -particularly gold ore processing. XPS can determine both the surface composition and chemistry of ores and tailings, and the various phases within either of them. AES can also determine surface composition with the further advantage of having greater spatial resolution so the surface chemistry associated with specific minerals in the ore can be identified. This identification helps to clarify why some minerals pass through a chemical process unaffected, while others can be successfully treated. SIMS has an elemental sensitivity from one to four orders of magnitude greater than XPS or AES which makes it useful for detecting the presence of some elements in very low concentration (parts per million).

Jan 1, 1981

By Zhucheng Huang, Yuanbo Zhang, Kecheng Zhang, Guanghui Li, Tao Jiang

"With rapid development of Iron and Steel industry, plenty of metallurgical dusts and sludges are generated, which have not been effectively utilized because of their poor hydrophilicity and bad ballability. Agglomeration and roasting of metallurgical dusts & sludges with a new-type composite binder are studied in this paper. The results indicate that the dosage of the new binders can be decreased to 2.5 wt% from 3.5 wt% when using the wet-grinding process. Under the optimal conditions of briquetting pressure 2070 N/cm2, briquetting moisture content 13 wt%, roasting temperature 1000 °C and roasting time 40 min, the qualities of the green, dry and roasted briquettes meet the requirements of the industry production. The finished products have the compression strength of more than 2000 N/cm2, which can be used as high-quality burdens for blast furnaces.IntroductionWith rapid development of Chinese Iron & Steel industry, there are more and more serious resource shortage and environmental pollution existing. Converter sludges, containing 30% ~ 40 wt% moistures, are typically difficult for recycling [1]. Foreign processing technologies for sludges treatment are relatively advanced including cold-bonded agglomerates for blast furnace, RHF reduction for the dusts and sludges with high content of Zn and Pb, smelting and reduction. Domestic iron and steel companies use a small amount of sludges in sintering. However, the sludges have the characteristics of high moisture and containing harmful impurities, which directly affect the sintering mixture permeability and product quality [2-5]. There are also other technologies such as production of metallized pellets, cooling agents for steelmaking, etc [6]. All of these deficiencies and applied are not in large-scale."

Jan 1, 2011

By Zhucheng Huang, Ronghai ZHONG, Tao Jiang, Jun ZOU

The method of reduction roasting and magnetic separation of low-grade, micro- fine disseminated refractory iron ore following granulation with coal produced unexpected success. Pellets of iron ore with diameter between 3 and 8mm were granulated with coal, bentonite and water. The raw pellets and reduction products were analyzed by scanning electron microscopy and x-ray diffraction. Results show uniformly distributed coal powders inside the pellets improved the kinetics of the reduction process and accelerated the reduction rate. Reduction time was higher at temperatures below 890℃, which resulted in the formation of substantial amounts of fayalite. When temperature was increased, micro- fine hematite was then quickly reduced to iron metal and the amount of fayalite decreased sharply. When pellets were reduced at 950℃ for 25min, reduction products with 56.73% metallization rate were obtained. After grinding and magnetic separation, a concentrate with 72.18% Fetot was obtained.

Jan 1, 2015

By W. Kunda

A laboratory study was carried out on the treatment of sulphidic copper concentrates in aqueous chloride systems under elevated temperatures and oxygen overpressure. Exploratory tests showed that chalcopyriteoxidizes with various chloride salts to form, depending upon the pH of the system, soluble copper chloride or insoluble copper oxychloride salts; the copper can then readily be recovered from the solution or residues respectively. During the leaching, iron was oxidized to iron oxide and remained in the leach residue while the bulk of the sulphide sulphur was oxidized to the elemental form with a minor portion oxidized further to sulphate. The presence of metal chloride salts in the system increased the oxidation rates of chalcopyrite and depressed the solubilization of iron in the system. A systematic oxidation leach study carried out in (1) ammonium chloride and (2) sodium chloride systems showed that the former system required little or no HC1 addition while the latter required 2 mol of HC1 per mol of dissolved copper (plus zinc). The copper was recovered from the cuprous or cupric chloride leach solutions by cementation with iron. Extractions of 99% copper and zinc, 97% silver, and negligible iron were obtained. Sulphur was oxidized to the elemental or sulphate form; the relative proportions of the total sulphur were 60 and 30% for system (1) and 80 and 10% for system (2). A flowsheet for a conceptual process with minimal reagent requirements was proposed.

Jan 1, 1976

By Rui Mao, Ke-Xin Nao, Jian-Liang Zhang, Xiang-Nan Xu, Meng-Fang Wei

"In this research, fundamental characteristics of dust and sludge containing iron from the dusting system of sintering process, blast furnace, oxygen converter and rolling process in steel enterprise were studied by chemical analysis, X-ray diffraction analysis, optical microscope analysis, scanning electron microscopy analysis, particle size analysis and other analysis means. Development direction of resource utilization for dust and sludge containing iron from steel enterprise was put forward on the basis of above study.IntroductionDust and sludge containing iron for steel enterprise mainly come from the dusting system of sintering process, pelletizing process, blast furnace, oxygen converter, rolling process and other related process. Iron content of dust and sludge is between 30% and 70%, and they also contain certain content of carbon, calcium oxide, magnesium oxide and harmful elements [1-3]. Output of dust and sludge is determined by raw materials conditions, technological processes, equipment configuration and management level. Dust output in sintering process accounts for about 2% to 3% of the sinter production, while dust and sludge from iron making and steel making process respectively take up 3% to 4% of hot metal and crude steel production, and the solid waste from rolling process accounts for about 0.8% to 1.5% of the output of rolled products [4,5]. Dust and sludge contains Fe, CaO, MgO, C and other valuable resources, it will not only result in the waste of resources, but also cause serious pollution to environment ifthe dust and sludge are not recycled. China's crude steel production in 2012 is about 700 million tons and output of dust and sludge containing iron is nearly 60 million tons, so, it is of great significance to have a resource recycling for dust and sludge containing iron from steel enterprise."

Jan 1, 2014

By QinGuo, Shenghui Guo, Lei Li, Jinhui Peng, Linqing Dai, Libo Zhang

The ferrous removal process after carbothermic reduction of chromite fines with microwave heating combined with leaching was investigated. Under the following conditions: Reaction temperature: 1150 , Reaction time : 40min, Semi coke ratio: 12% , the iron content of the reduction product : 13.05% . Metallization achieved was 52.7%. Reduced chromite was leached with 8% of H2SO4 and FeCl3 aqueous solution. The results show that: the recovery rate of chromium can reach 88.06%, the mass ratio of chromium to iron is 3.5:1 for leaching 30 minutes with 8% of H2SO4; the recovery rate of chromium can reach 88.91%, the mass ratio of chromium and iron is 2.56:1 for leaching 4h at room temperature with FeCl3 aqueous solution (100g/L). The leaching time of latter is longer but can realize the circulation effectively and reduce the waste liquid processing problem.1

Jan 1, 2016

By Bruce H. Baker

Studies of used or unused refractory materials are excellent examples of applied mineralogy in industry. Refractory materials are mineral substances containing ceramic or chemical bonding systems. Knowledge of the mineral composition, bonding, and textural relationships often explains the resulting physical property values of a refractory and contributes to the interpretation of refractory wear mechanisms occurring in steel plant service.

Jan 1, 1982

By E. Charles Abbey

Manganese in electrolyte has both beneficial and detrimental effects in Zn electrowinning. Mn oxidizes to form MnO2 on Pb–Ag anodes, cell walls and pipes. MnO2 reduces anode corrosion but also leads to short circuiting and maintenance issues. MnO2 is thought to interact with chloride ions and produce oxidized chlorine species. The interactions between Mn and Cl are not well understood. Therefore, two sets of 45+ day bench scale experiments were conducted to investigate the effects of the manganese to chloride ratio on anode corrosion rate and electrolyte chemistry using rolled Pb–Ag anodes. Daily manganese and chloride losses from the electrolyte appeared to be correlated. Increasing the average Mn/Cl− ratio from ∼7:1 to ∼11:1 reduced the anode corrosion rate. Increasing the ratio above 11 did not reduce the corrosion rate further. Anode scales produced with Mn/Cl− ratios at and above 11:1 contained some γ–MnO2 while scales formed with ratios less than 11:1 did not.

By Brian P. Atkin

The NISOMI-81 opaque mineral searcil and identification system uses quantitative color values (Pe, dA, y) and VHN as its determinative para-meters. The system is designed to operate on a Radio-Shack TRS-80 micro-computer which is interfaced to a motorised diffraction grating mono-chromator (WILSCAN). Using an interfaced monochromator/photometer combination a typical identification including the measurement of the photometer data on both specimen and standard, calculation of color values and a computer search takes about 6 minutes. The data file contains 240 minerals at present but can easily be expanded as reliable new data become available.

Jan 1, 1982

By Manju Gurung, Birendra Babu Adhikari, Keisuke Ohto, Hidetaka Kawakita, Katsutoshi Inoue, Shafiq Alam

Novel bio-adsorbent gel was prepared by immobilizing functional groups of glycidyltrimethyl ammonium chloride, a kind of quaternary ammonium chloride, onto polymer matrices of persimmon extract for the recovery of precious metals such as palladium(II) and platinum(IV) from chloride media. It was found that this adsorption gel exhibits high selectivity to gold(III), palladium(II) and platinum(IV) over base metals such as copper(II) and iron(III) while crude persimmon extract, the feed material, exhibits high selectivity only for gold(III). From the adsorption isotherms study, the maximum adsorption capacities for gold(III), palladium(II) and platinum(IV) were evaluated as 3.30, 1.67 and 1.00 mol/kg, respectively. Those for palladium(II) and platinum(IV) are higher than those of simple quaternary ammonium chloride type of chemically modified persimmon tannin gel and commercially available anion exchange resin.

Jan 1, 2016

By R. Singh, C. Gong, J. Chaudhry

"Metalorganic chemical vapor deposition (MOCVD) is an ideal technique for the deposition of conducting and non-conducting oxide based thin film materials. In this paper we have presented a study of photo assisted MOCVD for the low temperature deposition of a number of oxide based advanced materials. We have used incoherent light sources as the source of optical and thermal energy in our MOCVD system. The vacuum ultraviolet (VUV) and ultraviolet (UV) photons can enhance the surface reaction of the absorbed molecules through the perturbation of the electronic state of binding between the absorbed molecules and the solid surface. Unlike plasma process, no surface damage is expected and high quality materials have been deposited. At a given substrate temperature, the performance of deposited film depends on the lamp configuration.INTRODUCTIONMetalorganic chemical vapor deposition (MOCVD) has become the standard manufacturing technique for the deposition of large area thin films of compound semiconductors. l.(.w-cost, high crystalline quality, atomically clean and sharp interfaces, atomic layer epitaxy, high throughput rates and potential for direct writing are some attractive features of MOCVD. Due to a number of potential advantages mentioned above, MOCVD is considered as an ideal technique for the deposition of various electronic and optical materials for a wide variety of applications. Rapid isothermal processing based on incoherent radiation as the source of optical and thermal energy is emerging as the key low thermal budget (integral of processing time and temperature) processing technique for the fabrication of current and next generation of microelectronic and optoelectronic devices and circuits [1]. In this paper we have demonstrated that the design of the lamp assembly plays an important role in determining the properties of the materials deposited by RIP assisted MOCVD. We have studied the growth rates, structural properties and electrical properties of Y2O3/Si structure. At a given substrate temperature, best results are obtained for the lamp assembly that provides maximum number of VUV and UV photons."

Jan 1, 1994

By K. Verbeken, E. Wettinck, M. Verhaege

Iron (III) can easily and selectively be removed from acidic sulphate solutions with organo-phosphoric acids like Di-2-Ethyl-Hexyl-Phosphoric Acid [D2EHPA]. Stripping of the iron (III) loaded organic, however, is difficult unless highly concentrated inorganic acid solutions are used. In this paper results are shown for the enhanced stripping of iron from loaded D2EHPA by electro-reduction. The loaded solvent is contacted with a 2 M H2SO4 solution, which is continuously recycled in an electrochemical reactor where iron (III) is reduced to iron(II). As iron (II) is not extracted by D2EHPA, the equilibrium for iron (III)- D2EHPA is shifted towards the aqueous iron (Il)-sulphuric acid solution. The electro-reduction unit is a vessel with separated catholyte and anolyte chambers. The catholyte is the actual stripping solution where iron (III) is reduced to iron (II) on a stainless steel electrode. The anolyte is a 2 M H2SO4 solution where oxygen is evolved on a lead alloy electrode. A sintered glass plug separates the compartments. With this unit, enhanced stripping of iron from the solvent is possible under mild acid conditions [2 M H2SO4], and a concentrated ferrous sulphate solution can be obtained. The results shown have mainly been obtained by studying the parameters affecting the electro-reductive stripping of a D2EHPA loaded organic phase in a batch reactor. From an iron (IH)-saturated 20 vol. % D2EHPA solvent containing ~ 12.5 g/1 Fe (III) over 90% of the iron can be stripped in one stage with a 2 M H2SO4 solution at 50°C. It is shown that in this way it should be possible to obtain a concentrated ferrous sulphate solution which can be processed downstream to recover a pure iron product.

Jan 1, 2000

By Huimin Lu, Zegao Sun, Zhijiang Gao

The traditional Ti6Al4V alloys were obtained by the smelting reduction of V-Ti bearing beach placer by rotary hearth furnace and aluminothermic reaction in laboratory. First, it gets he lp from combined rotary hearth furnace and grinding magnetic separation process to prepare titanium slag containing vanadium. In this study, a neural network model was used. The comparisons between experiment results and neural network simulation results show that genetic algorithm (GA)-based on back propagation (BP) method can predict the degree of reduction and separation of iron and slag with higher prediction accuracy. Then by aluminothermic reaction process, the optimized process parameters for Ti-V-Al alloys were searched. Al can deoxidize metal V and Ti from the metal oxides of artificial rutile containing vanadium. Finally, traditional Ti6Al4V alloy can be obtained by remelt and adjust the constituents.

Jan 1, 2016

By Allan MacRae

Freeport-McMoRan Inc. operates an ISASMELTTM furnace for the smelting of copper concentrate at the Miami Smelter in Claypool, Arizona. In May 2017, the furnace was restarted after incorporating newly designed copper cooling elements from just above the tap hole to the underside of the roof. The objective of the improved cooling design was to extend campaign life by eliminating existing failure mechanisms with the wall refractory. In addition to upgraded bathline coolers and complete coverage of the gas offtake transition, or ‘kettle’, with plate coolers, a novel arrangement of coolers was installed in the remaining freeboard area. The shell required significant cutting and re-stiffening, as well as extensive modification of the cooling water piping. Based on performance observed to date, it is expected that smelter throughput will be increased due to extended ISASMELTTM refractory campaign life.

By R. Hurman Eric

The flow of molten slag and matte and the estimation of the mass of settled matte in electric furnaces is discussed and the action of the electric furnace as a settler is considered. Particle size of the concentrate and its grade are major contributors to settler dimensions. Discussion on the production capacity of the electric furnace with reference to operating current, power input, furnace dimensions such as width and length and electrode diameter are given. These discussions are based on considerations derived mainly from experimentally determined properties of the slag such as its resistivity, viscosity and liquidus temperature. Extension of the design and operating considerations to circular furnace symmetry is also discussed.

Jan 1, 1995

By Douglas K. Modrow

In the fall of 1993, construction was completed on a state of the art industrial waste water treatment plant at Asarco's East Helena Lead Smelter. Purpose of the plant was to remove arsenic and metals using hydroxide precipitation. Completing of the plant culminated a lengthy process of laboratory bench-scale test work, engineering, construction, and Environmental Protection Agency (EPA) oversight. Unfortunately, the effiuent requirements for the plant were made significantly more stringent as construction was rearing completion. As a result, optimization activities were initiated to determine and implement measures to substantially improve effiuent quality so the new discharge limits could be met. These activities consisted of acquiring a thorough understanding of process chemistry and plant operations, and developing simple, practical methods of automating unit operations associated with the treatment plant. Implementation of these modifications in the second half of 1996 will not only significantly improve the constancy and reliability of treatment plant operations, but also result in operating cost savings and reduced need for increased operator attention at capacity flows, plus allow the treatment plant to meet the new discharge limits.

Jan 1, 1996

By Wenzhou Yu, Cong Zhang, Wenhui Ma, Gang Wang, Kuixian Wei

"A novel technique was successfully developed for nickel further purification by vacuum directional solidification. The removal effect of impurities in nickel was studied based on theoretical analysis and experiments. High removal efficiency of impurities in nickel can be realized according to theoretical analysis. The experimental results show that the vacuum directional solidification treatment could increase the nickel purity from 99.96% to 99.996%. Since vacuum directional solidification could effectively remove the impurities from nickel with low contamination and low cost, it is a potential route to obtain high-purity nickel for commercial application.IntroductionNickel is widely used in metallurgy, machinery, petroleum industry, chemical industry, construction industry, light industry, and other industries for its ductility, medium hardness, ferromagnetism and high chemical activity. Nickel-based alloy is an important material for the key parts of aircraft, tanks, submarines, radars, nuclear reactors and aerospace fields [1-5]. Generally, nickel contains Si, P, S, Fe, Cu, Zn, As, Cd, Sn, Sb, Pb, Bi, Al, Mn, Mg and other impurity elements, which may hinder the commercial application of nickel. Therefore, it is necessary to refine the crude nickel for the high purity nickel."

Jan 1, 2014