By D. B. Hunter, H. W. Rosenberg

The titanium-rich portion of the Ti-Pd system was investigated from 0 to 75 wt pct Pd by metallo-graphic and X-ray techniques. A 0 eutectoid occurs at 24 wt pct Pd and 1190°F. Two compoutzds are indicated in the region below 75 wt pct Pd, Ti,Pd and Ti2Pd3. The solubility of palladium its a titanium is low, probably less than 1 pct. In 1960 Rudnitskii and Birunl published a complete version of the Ti-Pd phase diagram. However, their work was in disagreement with the earlier literature in that they reported only one inter metallic compound, whereas three had been reported earlier. In view of these discrepancies, it was therefore necessary to redetermine those portions of the diagram of immediate interest. The following account describes our work on the system over the range of 0 to 75 wt pct Pd. MATERIALS AND METHODS Distilled titanium sponge and elemental palladium were used in the formulation of the alloys; the chemistry of these materials is detailed in Table I. The alloys were prepared as 10 to 50 g blended compacts that were melted into buttons by arc melting under gettered argon on a water-cooled copper hearth. Weighing of the ingredients before and after melting showed that negligible weight changes occurred. Therefore, no analyses were undertaken and the compositions of all alloys are nominal. All alloys were fabricated by hot rolling at 1700°F to 0.070-in.-thick sheet. Scale was removed by sandblasting and pickling in a 5 pct HF-35 pct HNO,, balance H20 solution. For metallographic examination, specimens were mounted after heat treatment transverse to the rolling direction, ground on silicon carbide papers of increasing fineness to 600 grit, and then electro-polished using a solution containing 600 ml me-thanol, 60 ml perchloric acid, 360 ml butyl cello-solve, and 2 ml "Solvent X". Unless otherwise specified, etching of alloys containing up to 42 pct Pd was carried out by swabbing with a 12 pct HN03-1 pct HF aqueous etch where a bright etch was required, or by a 1 pct hydrofluoric in saturated oxalic acid solution where contrast between phases was required. The Ti-52.8 Pd alloy was etched with a solution of 25 ml HF, 40 ml glycerine, 35 ml methanol, and 18 g benzalkonium chloride. For X-ray examination, 1/2-in.-square speci- mens of sheet were mounted flat in a standard 1-in. metallographic mount and ground and polished as above. X-ray diffraction was performed using a Norelco type 12045 Diffractometer, employing CuKa radiation with a nickel filter at 40 kv and 20 ma. Specimens were rotated about the sheet normal during exposure. Although this procedure did not remove the effects of sheet texture from the relative intensities, it had the advantage that oxidation or contaminants entering during preparation of powder samples could not confuse the patterns obtained. RESULTS AND DISCUSSION Fig. 1 illustrates the Ti-Pd phase diagram according to Rudnitskii and Birunl with the work of the present authors superimposed. Both interpretations agree that the system is of the 0 -eutectoid type with an extensive 0-phase field, and that the eutectoid temperature is just below 1200°F. There is also agreement that the solubility of palladium in a titanium is restricted. Our work would indicate that the a solubility of palladium is low, probably less than 1 pct. However, whereas Rudnitskii and Birunl place the eutectoid composition at 41 wt pct Pd, this investigation shows it to be at about 24 wt pct Pd. Moreover, this investigation confirms the existence of compounds at Ti2Pd and Ti2Pd3, whereas Rudnitskii and Birun report only a single Berthol-lide phase covering the TiPd to TiPd, range. Laves et a1.' and Wallbaum, whose work was summarized by Maykuth , reported the existence of Ti2Pd3 and TiPd, in addition to Ti2Pd. More recently, Nevitt and Downe~' have reported the structure of

Jan 1, 1965

By A. R. Troiano, R. F. Hehemann

The influence of partial decomposition to high temperature bainite on reaction kinetics at a lower temperature has been studied in two alloy steels. Reaction at the lower temperature is retarded by the prior treatment, and the extent of decomposition may be reduced. Interpretation of these results is based on a mechanism involving a limitation in the nucleation and growth of bainite plates. OF the major transformations in steel, the characteristics and general behavior of the bainite reaction are probably the least understood and appreciated. Limitations of space preclude a critical evaluation of the present status of the bainite transformation in this presentation; however, such a treatment will shortly appear elsewhere. Only the salient features pertinent to the present investigation will be introduced briefly here. Although the reaction curve for the formation of bainite is similar to that for a nucleation and growth process, other kinetic features are more in keeping with the martensitic mode of transformation. A definite temperature exists above which austenite will not transform to bainite.1-5 his temperature, which has been designated B., is determined by the composition of the austenite. Unlike other nucleation and growth processes, the amount of austenite transformed to .bainite is a function of reaction temperature. The extent of decomposition increases from 0 at H. to 100 pct at some lower temperature.' , This lower temperature will be designated B1 and appears to be relatively insensitive to austenite composition.% 5 The similarity in the effect of reaction temperature on the bainite and martensite transformations serves to emphasize the close connection between these two decomposition processes. Austenite decomposition in the bainite range proceeds without partition of the alloying elements.8-11 Partition of carbon has been proposed" primarily on the basis that partial transformation to bainite lowers M, and increases the amount of austenite retained at room temperature. Carbon enrichment resuslting from such partition has been employed to explain the influence of reaction temperature on the extent of decomposition.'" It should be noted, however, that no enrichment has been detected experimentally in high carbon steels.1,14,15 Lattice-parameter measurements of retained austenite in steels containing 0.3 to 0.4 pct C have indicated carbon enrichment, 3,10-18 although the split indicative of a high carbon martensite has not been reported. Carbon enrichment, if it does occur, must be highly localized around the bainite plates. Therefore, carbon enrichment does not account for the influence of temperature on the progress of the bainite reaction."' Thermal history is known to influence the martensite transformation through stabilization.20,21 No similar phenomenon in the bainite transformation has been reported. Materials and Procedure Two triple-alloy steels were chosen for this investigation. Their compositions were as given in Table I. These steels were chosen because the pearlite reaction did not interfere with the bainite reaction. Steel K was received in the cast condition and forged from 2 in. square bars to 1/2 x1 3/4 in. plates. The 4340 was received as 11/4 in. hot-rolled rounds. Both steels were homogenized in vacuum for one week at 2300°F in order to minimize segregation. A quenching dilatometer similar to that described by Flinn, Cook, and Fellows" was employed for the kinetic measurements. Dimensional changes were detected by a differential transformer coupled with a high speed recorder. The dilatometer was mounted so that it could be transferred to any one of three furnaces: a nitrogen-atmosphere austenitiz-ing furnace and two salt-bath furnaces for isothermal transformation. Dilatometer specimens were 1/32 x 1/4x 1/2 in. with a gage length of 1.4 in. All specimens were nickel plated in order to minimize decarburization during austenitizing. The austenitiz-ing conditions consisted of 10 min at the temperatures given above. Austenitizing temperatures were controlled to 210°F and transformation temperatures to ±3ºF. The precision of the dimensional measurements was estimated to be ± 5 x105 in. per in. Results and Discussion Isothermal Transformation: The characteristics of the isothermal bainite reaction will be described

Jan 1, 1955

By W. C. Leslie, R. M. Fisher, K. G. Carroll

A nitride, believed to be Si3N, has been separated from three nitrided silicon steels. Germanium nitride, Ge3N4, has been prepared from pure germanium. Comparison of the diffraction patterns indicates that the two nitrides are isomorphous; on orthorhombic structure is suggested in place of the rhombohedral structure previously reported for Ge3N4. THE possibility that a nitride of silicon may, under appropriate conditions, precipitate in silicon steels or in steels killed with silicon makes it desirable to have some positive means of identifying such a compound. One such means is the X-ray or electron diffraction pattern of the nitride. A review of the meager data in the literature indicates that the nitride most likely to form is Si3N4, a conclusion supported by the results of a study of nitrided silicon steels to be published shortly by L. S. Darken and R. P. Smith, of this Laboratory. Unfortunately, there is available no diffraction pattern for this nitride. Data have been reported, however, for Ge3N4 which, judging from the similarity between germanium and silicon, might be expected to be isomorphous with Si3N4. An effort was made, therefore, to form such a silicon nitride, to determine its composition and diffraction pattern and, if possible, its structure. To this end a series of three silicon steels was nitrided under controlled conditions with the resultant formation of nitride particles which yielded an electron diffraction pattern in situ. The particles were then extracted from the steel and an attempt was made to determine their chemical composition. X-ray and electron diffraction patterns were also obtained from the extracted particles, which indicate that the nitride is isomorphous with Ge3N4, although a complete determination of the structure has not been possible. These results show that a silicon nitride with a well-defined diffraction pattern can form in silicon steels, and they suggest that this nitride is Si3N4. Materials and Procedures The sillicon steels investigated were In the form of thin sheet or strip and had the composition shown in Table I. The 0.58 and 1.21 pct Si steels were nitrided by holding them at 1110°F in an H2-NH3 atmosphere containing 3 pct ammonia for 48 hr. The nitride particle size was increased by subsequent heating at 1500°F for 13 1/2 hr in helium. The resulting microstructure is shown in Fig. 1. The steel containing 3.20 pct Si was nitrided at 1200°F for 16 1/2 hr after which it was held in helium at 1500°F for 4 hr. Its structure as seen under the electron microscope is illustrated by Fig. 2. As would be expected from the higher silicon content and the shorter holding time at 1500 °F, the nitride particles are smaller and more numerous than those in the 1.21 pct Si steel. The ammonia-hydrogen treatment reduced the carbon content of the steels to a very low level, so no interference was encountered from carbon or carbides. In the case of the 3.2 pct Si steel, the carbon was reduced to 0.003 pct before nitriding by heating in dry hydrogen. Attempts to obtain an X-ray diffraction pattern from polished and etched surfaces of the 1.21 and the 3.20 pct Si steels were unsuccessful. However, an electron diffraction pattern was obtained from the surface of the steels. The interplanar spacings obtained from these patterns arc shown in Table 11, col. 5. The nitride particles were then extracted from all three steels by dissolving the ferrite matrix in bromine-methyl acetate, the solution used in the Beeghly method for the extraction of aluminum nitride from steel. X-ray diffraction patterns of these residues, obtained by means of a spectrometer and by a 57 mm Debye-Scherrer powder camera using filtered cobalt or chromium radiation, are given in Table II along with the pattern obtained by

Jan 1, 1953

By H. E. Cline, E. F. Koch, J. L. Walter

It has been postulated and, in a few instances shown, that some kind of dislocation structure will be present at semicoherent interfaces to accommodate small lattice mismatches. In the present study of the NiAl-Cr eutectic, regular arrays of interface dislocations are observed at the boundary between the chromium-rich rods and the NiAl-rich matrix. The networks were examined by transmission electron microscopy and selected area diffraction. The rods and the matrix have a crystallographic relationship in which all directions and planes of the two phases are parallel. The dislocation networks are cmposed of a<100> dislocations lying on the intersections of the cylinders with (100) planes. Dislocations forming hexagonal rather than square arrays are also observed at certain areas of the network. The morphology of the network is consistent with the interpretation of mismatch being accommodated by interface dislocations in the cylindrical geometry. The measured spacing between dislocations was used to calculate an apparent lattice mismatch between the phases (˜0.35 PCt)interface network energy (-140 ergs per sq cm), and network strengthening (-10,000 psi). It has been proposed by Frank and Van der Merwe1 that dislocations should be present at the boundary between two semicoherent crystallographically related phases. The role of the interface dislocations would be to reduce the internal stresses, caused by the mismatch in atomic spacing across the interface. Such dislocations have been observed at the interface between expitaxially grown films and Substrates.2-4 Interfacial dislocations have also been observed at precipitate-matrix interfaces.&apos;-&apos; Directionally solidified eutectics have been shown to have semicoherent phases1&apos; and would, therefore, be expected to have interfacial dislocations as found by Weatherly at a lamellar fault in A1-A12Cu.11 The NiAl-Cr eutectic appeared to be a promising system to examine because both phases are cubic, the lattice mismatch is small, and the phases are crys-tallographically related. Furthermore, the eutectic is easily thinned for transmission microscopy. Indeed, interfacial dislocations were observed and this report describes the nature of the dislocation networks in the boundary between the NiAl-rich ma-trix-phase and the fine chromium-rich rods.21 I) EXPERIMENTAL PROCEDURE Ingots, 3/4 in. in diam and 6 in. long were made by melting in vacuum and casting under argon using 99.9 pct pure material. The composition, in at. pct, was 33 pct Ni, 33 pct Al, and 34 pct Cr. The ingots were then placed in A1203 crucibles on a water-cooled base, melted by means of induction, and withdrawn from the hot zone at the rate of 1 in per hr under argon.* * T his material was first directionally solidified in this laboratory by E. R. Stover Slices were taken perpendicular to the growth direction of the directionally solidified ingot for metallography and for transmission electron microscopy. The electron transmission samples were thinned mechanically, then thinned electrolytically in A-2 electrolyte* *A-2 electrolyte: 62 ml perchloric acid, 700 ml ethanol, 100 ml butylcellosolve, 137 ml distilled H20. until a hole appeared in the foil. 11) EXPERIMENTAL RESULTS A) Optical Microscopy. The microstructure, viewed on a plane perpendicular to the growth direction, is shown in Fig. 1. The structure consists of cells or colonies of parallel chromium-rich rods in the NiAl matrix. The cells occur when there are impurities present12 or, in a ternary eutectic, if the composition is slightly off the eutectic composition. The axis of the chromium-rich rods is parallel to the growth direction except near the cell boundaries. Here the rods may assume angles to the growth direction; however, examination shows that the crystallographic relationship between the rod and the matrix remains the same. Fig. 1 includes cell boundaries where the rods formed at a large angle to the growth direction. The variation of rod position across the cells made it possible to Fig. 1-Structure on plane perpendicular to growth direction. Rods near cell walls are at large angle to growth direction. Magnification 315 times.

Jan 1, 1970

By L. E. Murr, P. J. Smith

A study has been made by transmission electron microscopy of thin foils of 304 stainless steel fatigued external to the electron microscope in reversed bending, and of thin foils fatigued directly within the microscope in alternating tension. The build-up of stacking faults in the thin foils during fatigue zoas correlated with the dislocatirm structures found in thin films prepared fror fatigued bulk specimens. The performance of the special devices designed for fatigue of thin foils so outlined and the importance of alternative methods of preparation of more uniform fatigue specimens bY vapor deposition are emphasized. INVESTIGATIONS on fatigued bulk aluminum1,&apos; and stainless stee13j4 have revealed the existence of dislocation substructure on examination by transmission electron microscopy of electrolytically thinned foils representative of these bulk specimens. While this technique has proved extremely valuable, it has several shortcomings. First, the method of fatiguing bulk specimens and then thinning to foil for electron-transmission observation allows only one observation of internal structure at any one portion of the fatigue life. Second, thinning the bulk fatigued specimens to foil results in the loss of at least one original surface. Thus, what one sees in the remaining electron-transparent sections is an internal dislocation or fault structure which in many cases cannot be correlated with the original surface markings. This is an undesirable feature, since it is well-known that metal surfaces play an important part in the fatigue process.5 An obvious third undesirable feature of the thinning-from-bulk technique is the fact that static observations have difficulty (in the case of fatigue) explaining the mechanism of a dynamic process. What is required then is a method whereby a selected thin area can be continuously observed either while undergoing cyclic deformation or at various fixed stages of fatigue deformation. While Murr and wilkov6 have reported some success with an apparatus designed to fatigue thin metal foils directly within the electron microscope, the nature of the specimen-mounting procedure and the mechanical features involved in the adaptation of the fatigue device to the electron microscope make this method difficult to operate. It was not possible, for example, to make frequent observations of a selected area because of difficulty in maintaining a chosen area in a stable viewing position inside the electron microscope. Except for the build-up of a dislocation substructure and what are commonly referred to as "slip striations", little else has been reported from observations on thin-foil sections prepared from bulk fatigue specimens. segal17 has found "slip striations" in stainless-steel fatigued specimens which were electropolished from both sides, but gave no explanation as to their origin or identity in terms of lattice imperfections. The research to be reported in this paper was undertaken with the following objectives in mind. First, an attempt was made to devise a technique or techniques whereby thin metal foils could be fatigued and repeatedly observed by transmission electron microscopy. Second, it was hoped that some correlation could be made between deformation striations found in fatigued thin transmission specimens and thin foils prepared from bulk fatigued specimens. These investigations illustrate quite convincingly that a feasible method is available for the direct study of the fatigue mechanism and similar dynamic phenomena in thin transmission specimens inside the electron microscope. I) EXPERIMENTAL METHODS Three modes of specimen fatigue and observation of fatigue damage were used. These involved fatigue of thin-foil specimens in a special arrangement external to the electron microscope and observation of a selected area at various stages in the fatigue life, the fatigue of thin-foil transmission specimens inside the electron microscope, and the fatigue of bulk specimens external to the electron microscope followed by thin-foil preparation for direct observation at predetermined stages. Design of the External Fatigue Clip and Specimen Holder for the Hitachi H.U.11 Electron Micro-scope. The purpose of the fatigue clip was to provide a reversed bending fatigue stress to a thin-foil transmission specimen outside the electron microscope. In order to accomplish this, a flat-bottomed, U-shaped brass clip was made as shown

Jan 1, 1965

Pursuant to notice duly given in accordance with law and the constitution, a special business meeting of the members of the Institute was held at the office of the Institute on June 27, 1919, at 8.30 P.M., 1573 members were present in person or by proxy. On resolution duly made and seconded, the change of name to American Institute of Mining and Metallurgical Engineers, Incorporated, was authorized and the officers of the corporation were instructed to take the necessary steps to accomplish this result. The votes were 1565 in favor of the resolution and 7 against. It was then moved and seconded that the certificate of incorporation be amended to define the purposes for which the corporation was formed as follows: "To promote the arts and sciences connected with the economic production of the useful minerals and metals, and the welfare of those employed in the industries by all lawful means, " etc., etc.-the remainder of the article reading the same. The purpose of this change was to allow the Institute to take any legal means it desires to accomplish the objects mentioned above instead of restricting it within narrow limits. The vote was 1573 in favor of the resolution and none against.

Jan 8, 1919

By Frank C. Greene

Drilling in Missouri in 1944 was nearly treble the rate of 1943 because of continued development of the Tarkio pool in Atchison County and the preparation of a pool in Jackson County for a water-injection project. The pipe line from the Prairie Point gas pool in Platte County was in operation throughout the year of 1944, but several of the shallow oil pools in Cass and Jackson Counties were off production during much of 1944 because of a shortage of help. Table I gives a summary of activities by counties. The total footage drilled was 41,475 .ft., of which 21,187 ft. was by rotary tools and 20,268 ft. by cable tools.

Jan 1, 1945

CLARENCE N. FENNER.-Mr. Gelstharp, chief chemist of the Pitts-burgh Plate Glass Co., has directed my attention to the fact that that company was using optical pyrometers obtained from the Leeds & Northrup Co. several months before the members of the Geophysical Laboratory arrived at Charleroi. I am glad to make this correction. The chief object of my paper was to emphasize the necessity of careful temperature control in the making of optical glass and to describe the kind of tests to which an optical pyrometer should be subjected at a glass plant in order to obtain information regarding the closeness with which its readings correspond with true temperatures under the condi-tions which prevail in each particular case.

Jan 12, 1919

By W. L. Doyle

SLAG weights were taken on a series of twenty-eight 6-ton bottom-pour heats. These weights varied from 573 to 1050 lb. Of these, four were chosen for study of the effect of cleaned and uncleaned foundry scrap on the variations of slag weights. Data regarding the make-up and results of the heats are given in Table I. For heat No. 3 the actual slag weight was checked, using the Mn-MnO calculation method-weight 1050 lb. [5,600 X 0.0055 = 30.80 heads and gates 6,000 X 0.004 = 27.00 plate scrap 800 X 0.0083 = 6.64 pig iron 450 X 0.0034 = 1.53 iron ore]

Jan 1, 1947

POSITIONS VACANT Position as superintendent of all-sliming cyanide plant in Montana will he open in spring. Thoroughly experienced man wanted. No. 6. Position as engineer for iron-mining company in Virginia is open. Single man with experience in underground surveying preferred. No. 7. ENGINEERS AVAILABLE (Under this heading will be published notes sent to the Secretary of the Institute. by members or other persons.) Member, 34 years old, married, nine years responsible position in South America, excellent knowledge of Spanish, Latin-American people and customs, with present employer seven years, six years as manager and legal representative of a mining company, desires to make a change April, 1914. Prefers position requiring energy, executive ability, business tact and practical knowledge dealing with political and legal authorities, rather than strictly technical position. No. 35. Technical graduate, married, with four years&apos; experience in assaying, surveying, sampling,. and mine supervision in Utah and Mexico, open for engagement. No. 37. Member, aged 28, desires opening on engineering or sales force of machinery house, or manufacturing concern. Twelve years&apos; experience, in smelters, cyanide plants, concentrators and gold dredges, steam, gas and electric machinery and mechanical drafting. At present foreman for a silver-lead company. No. 40.

Jan 1, 1914

By Robert E. Tally

The ore reserves of the United Verde Copper Co. in 1907 were estimated at 4,500,000 tons, averaging about 7 per cent copper. Seventy-five per cent of this tonnage was confined to the so-called fire stopes and the remainder was virgin ore. The fire area was being operated at a maximum capacity of 150 tons per day, and the other workings furnished the remainder of the ore, approximately 600 tons per day. The mine was developed to a depth of 900 ft. and the lower levels were considered lean and unpromising. The smelter had been built directly over the ore-bodies. Its site was congested, the ground was settling and maintenance costs were excessive. The major needs of the United Verde obviously were 1. Additional ore reserves. 2. A new and modern smeltery. 3. A method for the mining of the fire-stope ores commensurate with the tonnage and values involved. It is the method specified in point, 3 with which this paper is chiefly concerned. Such a method required the removal of the old smelter, and additional ore reserves were essential not only for the maintenance of production but for the investment necessary for the building of a new smelter.

Jan 1, 1932

By Yu A. Chernegov

Building up the USSR&apos;s economic strength was the result of all the achievements and successes of our economy. The Soviet Union was the first to begin planned guidance of the economy. The mining industry of the USSR, which holds the first place in the world output of mining production, has always been considered as the main raw materials basis of the country&apos;s economy. High and stable development rates are a feature of planned economic management, based on the social ownership of the means of production. During the past ten years from 1965 to 1875 the national income used for consumption and accumulation increased practically by 1.9 times. There has been no inflation, no unemployment in the Soviet Union for about forty years already. High and stable growth rates of the production of mining industries and that of the branches, which are their direct consumers are characterized by the data in table I. The achievements and successes of the economy&apos;s development are to a great extent determined by the three planning components, which are as follows:

Jan 1, 1977

By L. Stone, H. Margolin

The Ti-C-N and Ti-C-O systems were investigated in the temperature range from 500° to 1400°C and in the composition range up to 2 pct C and 5 pct N or 0. Characteristic isothermal sections at 800°, 900°, 1000°, and 1300°C are presented. The Ti-N-0 system was studied in the temperature range from 900&apos; to 1400°C with alloys containing up to 6 pct total alloying content. Characteristic isothermal sections at 1000° and 140O°C are presented. Melting-point data for all three systems are also included. THIS paper reports on one of a series of investi-gations which have been conducted on the phase diagrams resulting from interstitial alloying with iodide titanium. The other investigations involved delineation of the binary systems with carbon,&apos; nitrogen and boron,h and oxygen. The Ti-0 binary system has also been investigated by Bumps et al.&apos; In varying degrees, each of these interstitial elements has been shown to stabilize the low temperature a modification of titanium1-5 and each forms a face-centered cubic TiX compound (henceforth designated 6). In addition, the Ti-N and Ti-0 systems reveal a low temperature tetragonal phase (6) formed by a peritectoid reaction between a and TiX Experimental Procedure The development of experimental techniques for the study of titanium alloy systems has, to a large extent, become standardized. In this investigation, the equipment and procedures described in detail by Cadoff and Nielsenl have been used. Arc Melting: In general, binary alloys with carbon, nitrogen, and oxygen, prepared in the composition range of interest in this investigation, show negligible composition changes during arc melting. However, the possibility of the formation of some gaseous combination of alloying elements such as CO, CN, or NO during the preparation of these ternary alloys was considered. Calculations showed that the evolution of only 0.05 gram of such a gas would be detectable as a pressure change in the closed system used during preparation of these alloys. Such pressure changes were not observed. Consequently, nominal compositions have been used in plotting the data. The compositions of the materials used in the preparation of the alloys are shown in Table I. After melting for 3 to 5 min at 275 to 350 amp, the alloys were checked for homogeneity by microstruc-tural examination. Alloys containing up to 1 pct C were homogeneous in the presence of less than 3 pct N or 0. At higher alloying contents, some inhomo-geneities in the carbon distribution became evident. Alteration of the melting procedure toward longer times and higher currents did not improve the homogeneity of these alloys. Ti-N-0 alloys were homogeneous in the range to about 3 or 4 pct total alloying addition. Beyond this, almost all of the specimens showed as-cast microstructures consisting only of the phase. Consequently, inhomogene-ities could not be detected by examination of micro-structures. Ten alloys from each of the systems were analyzed for two of the elements present (oxygen being omitted in all cases and titanium being omitted in the Ti-C-N alloys). In all cases the analyses were found not to be sufficiently precise to serve as criteria for the total composition of these alloys. On the basis of phase distribution in heat-treated alloys, however, it appears that carbon is distributed throughout the alloys most uniformly, with oxygen and nitrogen following in that order. Heat Treatment: Specimens for heat treatment were wrapped in titanium sheet before sealing in the argon-filled quartz capsules. Heat-treatment times varied from 100 hr at 800°C to 0.5 hr at 1400 °C. After heat treatment the specimens were quenched by breaking the capsule in water. With the exception of alloys in the low composition region, heat treatment did not have an appreciable effect on the as-cast microstructures. Metallography: Following heat treatment, the specimens were prepared for metallographic examination by grinding on emery paper and electrolytic polishing. For the majority of the specimens a 10-sec etch with Remington "A" agent (25 pct HNO3, 25 pct Hf, and 50 pct glycerin) adequately

Jan 1, 1954

By J. T. Mackenzie

Henry Marion Howe, in whose memory we are gathered together, was one of the great thinkers who develop from time to time to whom is given the rare gift of synthesis. Analysis is given to few, but synthesis, the ability to show the relation of all parts to each other and thus to give a clear picture of the whole, is reserved for the very few. Analysis can be achieved by honesty, intelligence, and industry, but synthesis is only given to genius. Professor Howe&apos;s crowning achievement is the picture of the whole iron-carbon series shown in Fig. I, which places steel, malleable, gray iron, mottled and chilled irons in their proper relation to each other and shows the essential unity of the series. Perhaps his best statement of the case is found on page go of the Metallography of Steel and Cast Iron in these words: " Each member of the gray cast-iron series consists of the metallic matrix approximately equivalent to that member of the steel-white-cast-iron series to which it corresponds in percentage of combined carbon with its continuity broken up—by masses of graphite ..." Apparently he had taken considerable interest in this idea around the turn of the century, for he refers to a discussion at the Franklin Institute in I900 in which he said: "Though many others had probably conceived this relation between the steels and cast irons, it was here enunciated for the first time, so far as I know. It was received with great incredulity." The concept was explained in some detail in a paper on "The Constitution of Cast Iron" presented before the A.S.T.M. in 1902 when Professor Howe was retiring president of that young society. In the discussion Dr. Sauveur stated that he was "very well acquainted with Professor Howe&apos;s theory of the constitution of cast iron," and went on to say that while he "shared it to the fullest extent, some foundrymen . . . claim cast iron is a metal entirely different from steel . . . that steel and cast iron have very little in common, and that therefore the knowledge gained in the study of steel is of little or no value in the study of cast iron." Dr. Moldenke, in discussing the same paper, said he had been working on the same theory for 12 years but he laid no claim to publication. Discussing the difference in the micro-structure of the metallic matrix, Professor Howe pointed out that "such minor structural differences are indeed to be expected, because of the difference in the conditions under which these constituents are generated. "One difference in these conditions is that the steel of most micrographs has been either forged or at least treated thermally in such a way as to give a new structure radically different from that which formed during the initial solidification, whereas the cast irons have not. Hence what we see in the steels is a transformation structure, but in the cast irons a solidification structure. By giving the cast

Jan 1, 1944

By J. T. Mackenzie

Henry Marion Howe, in whose memory we are gathered together, was one of the great thinkers who develop from time to time to whom is given the rare gift of synthesis. Analysis is given to few, but synthesis, the ability to show the relation of all parts to each other and thus to give a clear picture of the whole, is reserved for the very few. Analysis can be achieved by honesty, intelligence, and industry, but synthesis is only given to genius. Professor Howe&apos;s crowning achievement is the picture of the whole iron-carbon series shown in Fig. I, which places steel, malleable, gray iron, mottled and chilled irons in their proper relation to each other and shows the essential unity of the series. Perhaps his best statement of the case is found on page go of the Metallography of Steel and Cast Iron in these words: " Each member of the gray cast-iron series consists of the metallic matrix approximately equivalent to that member of the steel-white-cast-iron series to which it corresponds in percentage of combined carbon with its continuity broken up—by masses of graphite ..." Apparently he had taken considerable interest in this idea around the turn of the century, for he refers to a discussion at the Franklin Institute in I900 in which he said: "Though many others had probably conceived this relation between the steels and cast irons, it was here enunciated for the first time, so far as I know. It was received with great incredulity." The concept was explained in some detail in a paper on "The Constitution of Cast Iron" presented before the A.S.T.M. in 1902 when Professor Howe was retiring president of that young society. In the discussion Dr. Sauveur stated that he was "very well acquainted with Professor Howe&apos;s theory of the constitution of cast iron," and went on to say that while he "shared it to the fullest extent, some foundrymen . . . claim cast iron is a metal entirely different from steel . . . that steel and cast iron have very little in common, and that therefore the knowledge gained in the study of steel is of little or no value in the study of cast iron." Dr. Moldenke, in discussing the same paper, said he had been working on the same theory for 12 years but he laid no claim to publication. Discussing the difference in the micro-structure of the metallic matrix, Professor Howe pointed out that "such minor structural differences are indeed to be expected, because of the difference in the conditions under which these constituents are generated. "One difference in these conditions is that the steel of most micrographs has been either forged or at least treated thermally in such a way as to give a new structure radically different from that which formed during the initial solidification, whereas the cast irons have not. Hence what we see in the steels is a transformation structure, but in the cast irons a solidification structure. By giving the cast

Jan 1, 1944

By M. E. de Morton

Recovery and early recrystallization of heavily deformed, 99.98 pct Cr was investigated by studying metallographic structure. X-ray line sharpening, electrical resistivity, plastic properties, internal friction, and shear modulus. Appreciable recovery of resistivity, internal friction, and shear modulus together with some hardening and relief of internal strains occurred before the visible growth of a textured substructure above 350°C (recrystallization in situ). The complex behavior of shear modulus, internal friction, and its strain amplitude dependence during annealing are discussed qualitatively in terms of the relative mobility of dislocations. BY plastically deforming fully recrystallized 99.98 pct Cr above the brittle to ductile transition temperature, at -350°C. as in wire drawing, chromium can be made very ductile at room temperature. However, this ductility is lost on annealing at high temperatures when recrystallization takes place.&apos; The present investigation was made to determine the general pattern of the changes in a number of physical and mechanical properties during recovery and recrystallization of heavily deformed chromium as part of an effort to elucidate the reasons for lack of ductility in the fully recrystallized condition. PREPARATION OF MATERIAL Wire specimens 0.027 in. in diam were prepared from arc-melted, electrolytic chromium by extruding, hot swaging and finally wire drawing at 300" to 350°C, i.e. above the brittle-to-ductile transition temperature. The total reduction in area of the wire was 98 pct and the last 3 pct of reduction was made at 100" to 150°C before cooling to room temperature. The impurity content of the material is shown in Table I. Internal friction and modulus measurements were made on a single specimen after annealing in situ at successively higher temperatures. For all other measurements, a fresh specimen was used for each temperature and annealing of these specimens was done in evacuated (0.001 mm Hg) and sealed silica tubes for 1 hr at the various temperatures up to 700°C. EXPERIMENTAL METHODS AND RESULTS The occurrence of a. transition in some physical properties of chromium at - 40°C2 imposed limitations on the temperature region where some of the measurements could be made. The reason for this transition in chromium is at present unknown but is probably associated with an antiferromagnetic state observed below - 40°C.* Heavy deformation produces an anomalous decrease in resistivity when measured at temperatures below -40°C4 though a normal increase is observed above this temperature. On the other hand internal friction in heavily deformed chromium5 over the temperature range 40" to 50°C is invariant with temperature. Above and below this range internal friction is strongly temperature dependent, increasing with increasing temperature. A temperature in this range was therefore convenient for both resistivity and internal friction measurements and for consistency the measurements of the mechanical properties were also made at about this temperature. No structural change has, however, been observed in careful X-ray measurements6 between -195" and 50°C, i.e. departure from cubic symmetry was not greater than 3:10,000; X-ray line sharpening measurements were therefore more conveniently made at room temperature.

Jan 1, 1962

In 1846 a bill was pending in Congress to reduce, or eliminate, the tariff on coal; the debate caused the same writer to visit the mines on the north side of the James River and to write a letter about them to the same paper.&apos; Omitting the political arguments, his account follows: "July 13, 1846. "Early in the morning we rose, washed, combed, and ate a first-rate breakfast, and then went to the Tuckahoe, mined by Messrs. Sneed and Dietrock. Coal was first discovered here sixty years ago, and mined by Colonel Thomas Randolph, the proprietor of the land. They were worked by him for his smith-shops. Since which time they have been worked periodically, up to the war of 1812, when they were abandoned; and recommenced in 1837 under the management of Dr. W. T.- Scott. Subsequently a Company was formed called Tuckahoe Coal Mining Company, which purchased the whole track at a cost of $30,000. They commenced the sinking of a shaft and went as far as 412 feet, and then pitched the fat all into the fire by hauling off altogether in despair. In 1843 Major Sneed went to work at it, and succeeded. I may here remark that Major Sneed has been the pioneer in this business on the North side of the River, and has sunk more shafts than any other man who has pursued this vocation in Eastern Virginia. The difficulties and expense in sinking these shafts are sometimes immense. The coal on the outcrop or surface is not always a guide to where it may be found imbedded many hundred feet under earth and rock. "The Tuckahoe Pits are on the Eastern end of the coal field, within twelve hundred yards of the Canal, and about twelve miles from Richmond. They employ fifty hands and raise some three hundred thousand bushels of coal per year. It is highly bituminous and excellent for the manufacture of iron. The Tredegar and Belle Isle Rolling Mills are supplied with it. It must be good and of the right kind&apos;, or they would not use it. These pits are the only. ones on this side troubled-with gas-of course ventillation is necessary. There is not as much water in this Pit as I have found generally in many others, although they have extended their operations to a considerable distance under ground. I have observed in examining the coal mines, that, where they are sunk over four or five hundred feet, they are annoyed by gas, and where there is a less depth they are troubled with water. It is evident, therefore, that water, in the region of these coal fields, does not run through the earth to any extent, even five hundred feet deep, and the farther you go below that the greater the increase of gas. "We next visited William Cottrell&apos;s Pits, situated one mile and a half north of this. He employs some thirty hands, and raises from 4 to 500 bushels per day. "T. & R. Crouch&apos;s Pits are one hundred yards north of Cottrell&apos;s. This firm employ from 80 to 90 hands, and raise from 8 to 900 bushels per day. They are now

Jan 1, 1942

By Jacques B. Wertz

Among the parameters to be considered in the continuous search for new base-metal deposits, there often is a stratigraphic controlling factor that seems instrumental in the localization of ore. In British Columbia, for instance, the Upper Triassic as well as Lower Jurassic volcanics mixed with sediments are a useful indication in the search for copper while, in some parts of Australia, rhyolite bodies seem to be the favorable indicator, and this always within the geosynclinal environment. In Arizona, this stratigraphic factor becomes highly significant and it will be shown here that a large number of ore deposits are to be located around the flanks of ancient calcareous basins or depressions, preferentially corresponding to a certain optimum thickness as revealed by isopachs. The Martin limestone, of Devonian age, is already known for its basal O&apos;Carroll bed which coincides with mineralization at places, and this is a relatively minor control. However, several limestone basins outlined by isopachs are in reality of greater importance as they localize mining districts. Indeed, most mines are found to coincide with a specific thickness of limestone while occurring simultaneously close to major, regional fracture intersections. The regional fractures in question were interpolated and extrapolated from known, important fault expressions, integrating quite well with the existing geology and further confirmed by minor criteria such as contacts, igneous plugs, axes of elongation of batholiths, dikes, etc. Although elements of subjectivity remain, this grid of fractures can be used quite successfully as a working hypothesis in the search for ore. Results of the present study which superposes major structural

Jan 1, 1971

By B. M. Larsen, T. E. Brower

In two previous paperslJ dealing with the carbon-oxygcn reaction, and the simultaneous content of each, in liquid steel in the furnace, we have made use of the quantity A[O], defined as the excess oxygen beyond what would be in equilibrium with carbon then present if the pressure of carbon monoxide were I atm.; that is, if [C] X [O] is taken as 0.00222, A[O] = [O] - 0.0022[C] where [O] is the percentage of oxygen by weight as measured by the method described earlier.3 This quantity ?[O] proves to be substantially independent of carbon content over the range 0.08 to I,z per cent, as well as of the basicity of the slag, and is nearly always within the limits o.o15 to o.oz5 per cent when the bath is boiling normally and is in what we have termed a steady state, Apparently it must be at least about 0.014 per cent before boiling occurs; but this threshold value seems to depend upon the ease of bubble formation at the metal-hearth interface, hence upon the condition of the surface of the hearth. In any case, ~(01, on the average, changes considerably following any disturbance of the bath, as by addition of ore. The present paper deals with the average changes in A[O] level following addition of spiegel or crop ends, or after procedures to promote stirring, or by tapping of the steel from the furnace. The observations were made on a large number of commercial heats, and consequently are subject to the influence of various disturbing factors; the results have the compensating merit of showing the consistency obtainable under the limitations imposed by practical operation. Variability of Excess Oxygen in Normal Open-hearth Operation The preceding genera&apos; statements refer to the average value of A[0] particularly in heats that are boiling actively; on individual heats, which are less active, there may be a variable time lag between the disturbance and its effect, which complicates the interpretation of what is going on. For instance, if in the normal refining process boiling is sluggish, the slag usually is gaining Oxygen from the gas phase above it, Or from added Ore$ faster than it is losing oxygen to the metal; Yet when the bath starts to boil vigorously, the opposite condition may prevail for Some time. The consequence of this lag is a variation of A[o], the interpretation of which in a sing1e heat may not be immediately obvious. This condition is illustrated in Figs. I and 2. In Fig. 1, A[0] at the beginning of the test period was near the lower limit of its usual range (dashed lines) in the steady state as a consequence of the lime boil, which had ended about as indicated. The bath is now cold, carbon drop is slow, and the first small orc feed causes only a small rise in A[O]; as the temperature rises and as lime dissolves in the slag, and the bath becomes more active, the

Jan 1, 1948

By B. M. Larsen, T. E. Brower

In two previous paperslJ dealing with the carbon-oxygcn reaction, and the simultaneous content of each, in liquid steel in the furnace, we have made use of the quantity A[O], defined as the excess oxygen beyond what would be in equilibrium with carbon then present if the pressure of carbon monoxide were I atm.; that is, if [C] X [O] is taken as 0.00222, A[O] = [O] - 0.0022[C] where [O] is the percentage of oxygen by weight as measured by the method described earlier.3 This quantity ?[O] proves to be substantially independent of carbon content over the range 0.08 to I,z per cent, as well as of the basicity of the slag, and is nearly always within the limits o.o15 to o.oz5 per cent when the bath is boiling normally and is in what we have termed a steady state, Apparently it must be at least about 0.014 per cent before boiling occurs; but this threshold value seems to depend upon the ease of bubble formation at the metal-hearth interface, hence upon the condition of the surface of the hearth. In any case, ~(01, on the average, changes considerably following any disturbance of the bath, as by addition of ore. The present paper deals with the average changes in A[O] level following addition of spiegel or crop ends, or after procedures to promote stirring, or by tapping of the steel from the furnace. The observations were made on a large number of commercial heats, and consequently are subject to the influence of various disturbing factors; the results have the compensating merit of showing the consistency obtainable under the limitations imposed by practical operation. Variability of Excess Oxygen in Normal Open-hearth Operation The preceding genera&apos; statements refer to the average value of A[0] particularly in heats that are boiling actively; on individual heats, which are less active, there may be a variable time lag between the disturbance and its effect, which complicates the interpretation of what is going on. For instance, if in the normal refining process boiling is sluggish, the slag usually is gaining Oxygen from the gas phase above it, Or from added Ore$ faster than it is losing oxygen to the metal; Yet when the bath starts to boil vigorously, the opposite condition may prevail for Some time. The consequence of this lag is a variation of A[o], the interpretation of which in a sing1e heat may not be immediately obvious. This condition is illustrated in Figs. I and 2. In Fig. 1, A[0] at the beginning of the test period was near the lower limit of its usual range (dashed lines) in the steady state as a consequence of the lime boil, which had ended about as indicated. The bath is now cold, carbon drop is slow, and the first small orc feed causes only a small rise in A[O]; as the temperature rises and as lime dissolves in the slag, and the bath becomes more active, the

Jan 1, 1948