Search Documents

By Frank C. Aplleyard

The two calcium sulfate minerals-gypsum and anhydrite-occur in many parts of the world, and gypsum has long been of economic importance in the family of industrial minerals. Gypsum, the dihydrate form of calcium sulfate (CaSO4•2H2O) and anhydrite, the anhydrous form (CaSO4) are frequently found in close association, and it is seldom that a calcium sulfate deposit will consist exclusively of one mineral or the other. Although known gypsum deposits are extensive, anhydrite makes up the largest part of total calcium sulfate reserves. However, it has very minor economic use, and most of the following discussion will be devoted to gypsum. Calcium sulfate is one of the principal constituents of evaporite deposits, and when pure, has the following composition: [Sulfur Combined Lime Trioxide Water (CaO) (SO,) (H2O) Gypsum 32.6% 46.5% 20.9% Anhydrite 41.2% 58.8% -] Deposits of pure gypsum or of pure anhydrite which are large enough to be considered commercial have never been found because of both the metastable relationship between the two minerals, and the presence of impurities such as calcium or magnesium carbonates, chlorides, other sulfate minerals, clay minerals, or silica. As a result most mine production of gypsum will range between 85 and 95% pure. Often it is used as mined, although in certain cases, one or more forms of mineral beneficiation are employed to upgrade the product. End Uses The largest use for gypsum is based upon the unique property which calcium sulfate has of readily giving up, or taking on, water of crystallization. With the application of a moderate amount of heat in a process known as calcining, gypsum is converted to plaster of paris (the hemihydrate of calcium sulfate, CaSO4 ½ H2O) which when mixed with water will set or harden as the calcium sulfate returns to the dihydrate form. This semifinished product, usually called stucco, is then manufactured into a large variety of plasters, wallboard, and block for construction use, or into plasters for industrial applications. About 75% of the gypsum used in the United States is calcined for these purposes. Uncalcined uses of gypsum are principally as a retarder for portland cement, as a soil conditioner, as a mineral filler, and other minor industrial applications. About 25% of the gypsum mined in the United States goes into these markets; however, in less developed countries where construction and other industrial uses may be quite limited, the use of uncalcined gypsum for portland cement retarder may well be the dominant-if not the only-market for the mineral. It has often been noted that calcium sulfate constitutes the world's largest reserve of sulfur, and minor use of both anhydrite and gypsum has been made to produce sulfuric acid or other sulfur compounds such as ammonium sulfate. However, because sulfur is readily available at lower cost from other sources, use of calcium sulfate has been limited to only a few locations where it could compete economically. No such use is reported in the United States at this time. Mineralogy Anhydrite, CaSO4 because of its geologically rapid conversion to gypsum, and relatively high solubility (about 0.2 g per 100 g H2O) is not often found outcropping in climates wet enough to support abundant vegetation except on steeply dipping slopes or other places where hydrated material is continuously removed. Anhydrite rock is most often light to bluish gray in color, and under the microscope, varies

Jan 1, 1983

By John Chipman, Carl F. Floe

The system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or CO2 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modern metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100" to 1500ºC., and pressures from about 20 mm. of mercury to somewhat above atmospheric. Review of Previous Work The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as O2, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: 2M+G2=2MG K=(MG)2 /M2 X PG2 [I] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: MG = K1 vPG2 [2 Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: 6Cu + SO2 = Cu2S + 2Cu2O [3] K= Cu2S X (Cu2O)2 i - (Cu)6(Pso2) [4] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: K1 =V3SO2 /Pso2 or

Jan 1, 1941

By Carl F. Floe, John Chipman

The system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or CO2 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modern metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100" to 1500ºC., and pressures from about 20 mm. of mercury to somewhat above atmospheric. Review of Previous Work The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as O2, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: 2M+G2=2MG K=(MG)2 /M2 X PG2 [I] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: MG = K1 vPG2 [2 Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: 6Cu + SO2 = Cu2S + 2Cu2O [3] K= Cu2S X (Cu2O)2 i - (Cu)6(Pso2) [4] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: K1 =V3SO2 /Pso2 or

Jan 1, 1941

By Paul T. Allsman, E. W. Newman

TRENCHING, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively.

Jan 1, 1944

By E. A. Gulbransen, J. W. Hickman

IN a previous paper1 the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300° to 700°C. except for copper, where the range selected was 100° to 500°C. The results of these studies were presented in graphical form as existence diagram, of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviations in lattice parameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: I The existence diagrams of various alloys. [2.] The effect of the structure of the [ying] metal on the existence diagram of Iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body- centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K42B1 Nichrome V, Hipernik, Inconel, Stellite " 21," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1946

By Roger Holmberg, Kenneth Mäki

This paper describe; open pit studies where blasting damage introduced in the remaining rock has been investigated. Results from two open pit mines are described and discussed. Parallel performed laboratory experiments, where simulated blasting damage has been introduced into samples before shear strength testing took place, are also reviewed. These studies are tied together in order to throw some light upon how the blasting damage influences the slope stability. A mathematical model is also described which will make it possible to optimize the blast design for a specified damage zone in the rock mass.

Jan 1, 1983

By C. M. Brown

Selection criteria for the instrumentation employed in semi-autogenous grinding circuits are reviewed. Instruments in use for grinding mill and related process equipment start- up, shutdown, protection, monitoring, control, and performance reporting functions are discussed with examples given of current industry practice. The quantity and type of instrumentation used vary from operation to operation, but today many semi- autogenous circuits are highly instrumentated, and employ automatic process control for both circuit stabilization and optimization of economic performance. Examples of analog and digital based control systems exist, and are described.

Jan 1, 1982

By S. L. Lopata, E. B. Kula

A variation of yield and tensile strength with direction has been noted in heat-treated 4340 steel which had been warn-worked by rolling in the austenitic condition prior to quenching. Measurements by X-rays showed a preferred orientation of martensite crystals. Various ideal preferred orientations of martensite were calculated by assuming a preferred orientation for austenite and transforming this to martensite by the Kurdjumov -Sachs and Nishiyama relationships. Comparison with the measured preferred orientation showed that the ideal rolling texture for austenite in 4340 steel could be expressed as a (112) [111] texture with a component of (110) [112]. No evidence was found for any fiber axis in the rolling direction, or fop- a (123) [412] texture. The observed martensite pole figures can be adequately accounted for by these ideal austenite textures and by the Kurdjumou-Sachs or Nishiyama transformation relationships between austenite and martensite. ALTHOUGH preferred orientations are found in cold-rolled steel sheet and in many nonferrous metals, they are not generally encountered in wrought, heat-treated high-strength steels, since such steels are generally not cold worked sufficiently to develop a strong texture, and any texture that is present is removed during heat treatment by the phase transformations taking place. This report gives details on a preferred orientation found in warm-rolled and hardened 4340 steel. In a recent study, a special combination heat-treating and working technique was used in which 4340 steel was deformed in the austenitic condition, and before re crystallization of the austenite could occur, quenched to form martensite.' Since the austenite was unrecrystallized, it was cold worked and hence could have contained a preferred orientation which could be transmitted to the martensite on quenching, and this in turn could be manifested as a directionality of mechanical properties. Such a directionality of properties was found as a result of working, and this prompted an X-ray study of the preferred orientation. Literature Survey— Rolling Texture in Face-Cen-tered-Cubic Austenite—M a preferred orientation is found in a rolled and hardened steel, it is first appropriate to consider what texture existed in the austenite as a result of the rolling but prior to the transformation to martensite. The changes taking place as a result of the austenite-martensite transformation are then considered. In view of the instability of austenite in 4340 steel at low temperatures, no direct determination of the austenite texture was made. However, an estimate of the texture for austenite in 4340 steel may be made by considering the textures found for other face-centered-cubic metals. Barrett' has reviewed the rolling textures for many materials. The most common orientation in face-centered-cubic metals has the (110) planes parallel to the rolling plane and the [112] directions parallel to the rolling direction, or (110) [112]. Other orientations found are (112) [111], as well as (100) [001], (110) [001], and others. Beck and his co-workers, using quantitative pole figures, report that (123) [121],3 later corrected to (123) [412],4 better describes the ideal orientation. smallman5 reported that the ideal preferred orientation for high-purity face-centered-cubic metals is (123) [121], but that there is a transition to (110) [112] as solid solution elements are added. The latter texture tends to occur more readily at lower temperatures. This transition between the two textures was explained by differences in the slip characteristics with concentration or temperature. More recently, Jones and Fell6 concluded that the (123) [412] texture for face-centered-cubic metals could equally well be represented by a mixture of (110) [112] and (112) [111] textures, and hence it had no physical reality. From the above results it can be seen that there is no agreement on the "ideal" texture for fcc metals and, hence, no firm basis for assuming a texture for austenite in 4340 steel. Therefore, the orientations (110) [112], (123) [412], and (112) [111] have been considered in the following.* *The (123) [4121 is identical to the (123) [121] rotated 90 deg. Orientation Relationship between Austenite and Martensite—When martensite forms from austenite, certain crystallographic planes of the martensite are parallel to planes in the austenite. This orientation relationship was first determined by Kurdjumov and

Jan 1, 1960

THE following employment items are made available to AIME members on a nonprofit basis by the Engineering Societies Personnel Service, Inc., operating in cooperation with the Four Founder Societies. Local offices of the Personnel Service are at 8 W. 40th St., New York 18; 100 Farnsworth Ave., Detroit; 57 Post St., San Francisco; 84 E. Randolph St., Chicago 1. Applicants should address all mail to the proper key numbers in care of the New York office and include 6c in stamps for forwarding and returning application. The applicant agrees, if placed in a position by means of the Service, to pay the placement fee listed by the Service. AIME members may secure a weekly bulletin of positions available for $3.50 a quarter, $12 a year. MEN AVAILABLE Project Manager or Construction Engineer, 48, married. Twenty-five years' experience on mine, mill and smelter construction work, design and operation, U. S. and Mexico. Speak Spanish. Now employed; available 30 days notice. Prefer U. S. or Mexico. M-698-489-E-1-San Francisco. Mining Geologist, 53, single. Eleven years' intensive field experience giving a completely practical competence for the smallest or largest of areas; plus the highest possible grade of academic background and independent research qualifying for top rating. Available in thirty days or less. Any location acceptable. M-699-3611-E-7-San Francisco.

Jan 1, 1952

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By W. W. Krysko

In order to calculate the critical particle size of lead oxide entrapped in lead, Stoke's Formula may be applied. All data were available except figures for the density of lead oxide at elevated temperatwes. The density of lead oxide was determined by means of dilatometmetrc and volumetric methods up to 1010°C. Graphs of the density of lead and lead oxide as well as the viscosity of lead are given and discussed, with the conclusion that the most unfavorable region for the separation of lead oxide from molten lead lies just above the melting point of lead. DURING previous investigations, particularly on the dedrossing of lead with aluminum1 and the oxygen solubility in lead,' the critical particle size of lead oxide which could be entrapped in solidifying lead was estimated by calculation, and it was shown that high values found for the oxygen content of lead may be due to the method of sampling and the entrapped particles of dross. Unfortunately, due to lack of data, an exact mathematical solution was not possible. The particle size which will separate under a given condition can be estimated from Stoke's Law, which states that where: d = diameter of the critical particle size ¦q = viscosity of lead in Poise V = constant velocity in cm sec-I g = 981 cm sec-2 61= specific gravity of lead 62= specific gravity of lead oxide The depth of the lead bath and the time before solidifying define the velocity. The viscosity of molten lead is known from earlier work by Krysko and is given in Table I. The specific gravity of lead is also known, see Table II. These values are according to Hofmann. A careful survey of literature revealed no values for the density of lead oxide at elevated temperatures. The present investigation was therefore conducted to provide this information. RESEARCH INVESTIGATIONS The density of lead oxide was determined from the following experiments: 1) Determination of the density of lead oxide at room temperature. 2) Dilatometric investigations on the same samples. 3) Determination of the shrinkage at the liquid-solid trans£ormation. 4) Density determinations on liquid lead oxide. 5) Time temperature curves during cooling. 1) The samples for the determination of the density of lead oxide in the solid state were prepared in the following manner. Molten lead oxide was cast into I hot mold which could be opened along the longitudinal (vertical) axis. The cast samples were cylinders of approximately 10 mm diam and approximately 80 mm length. The cylindrical hot mold was open at both ends and was placed on a large copper chill plate shortly before casting. The solidification of the lead oxides proceeded upwards without any formation of internal cavities. The sample was carefully checked with respect to density and crystalline appearance, and only the lower portions which were crystalline and free from porosity were used. The density was determined in a specially made pyknometer-like container, where the surplus liquid was squeezed out through an orifice approximately 1/10 mm in diameter. Mercury or water was used as the liquid. The densities of the samples were calculated from the weight, volume, and mean specific gravity of eight samples was 9.62 * 0.05 g cm"3 at 22"~. 2) The samples were machined to approximately 1 1/2 in. in length and fitted into a dilatometer. A

Jan 1, 1962

By J. O. Lewis

Oil wells usually reach their maximum daily output shortly after they are completed. From that time they decline in-production, the rapidity of decline depending on the output of the wells and on other' factors governing their productivity. The production curve of a well shows the mount of oil produced per unit of time for several consecutive periods; if the conditions affecting the rate of production are not changed by outside influences, the curve will be fairly regular, and, if projected, mill furnish useful knowledge as to the future production of the well. By the aid of this knowledge the value of a property may he judged, and proper depletion and depreciation charges may be made on the books of the

Jan 2, 1918

By T. E. Davidson, C. G. Homan

This report deals with a study of the effects of extreme hydrostatic pressure on a polycrystalline material which exhibits a high degree of elastic anisotropy. Metallographically prepared polycrystalline bismuth samples were subjected to pressure levels up to 20,000 atm in a piston type gas-liquid system. The observed structural changes consisted of deformation localized along the grain boundaries, which appears to be a boundary migration phenomena, and widespread slip and cross slip. Subsequent deformation is progressive with increased pressure, and is substantially different in type from the deformation characteristic of uniaxial compression. A large amount of interest has been shown in recent years in the effects of extreme pressure on metals. In this connection, many investigations into the effects of pressure on physical and mechanical properties and reactions have been undertaken. Due primarily to the experimental difficulties involved, there has not been a great deal of study of the structural changes resulting from exposure of metals to extreme pressure. It has been difficult, for instance, to produce a true hydrostatic stress state in many of the extreme pressure devices used, and also to directly examine specimens metallographically before and after pressurization. The results of a preliminary investigation into one of the effects of extreme pressure, and its associated true hydrostatic stress state, on the structure of metals are discussed herein. Metals exhibit varied degrees of anisotropy in their physical and mechanical properties. Significant among the anisotropic properties is the modulus of elasticity, which varies by a factor of as much as three in some of the fcc metals, and by much larger factors in some of the less symmetrical elements. As a result of the variation of the modulus of elasticity with crystallographic direction, shear stresses will be induced in polycrystalline samples under true hydrostatic compression. Depending on several factors, these shear stresses could become of suffi- cient magnitude to cause localized plastic deformation. Presented herein are some of the structural changes observed in polycrystalline bismuth as a result of exposure to hydrostatic pressures of up to 20,000 atm. Although several other materials in both bicrystal and polycrystalline form are also currently under investigation, bismuth was chosen initially, due to its low symmetry and moderately high degree of anisotropy in the elastic properties. The fact that extreme hydrostatic pressure can induce structural changes in some elements in the polycrystalline state is of importance in itself. However, it may also be a factor in many of the other extreme pressure effects. For instance, this localized plastic deformation could substantially lower the recrystallization temperature, thus altering the effects of extreme pressure on this phenomenon. Also, as commented on by ridgman,' the hysteresis in the polymorphic transition of polycrystalline bismuth under extreme pressures could possibly be attributed to structural changes brought about by unequal compressibility. Therefore, to accurately determine the true effects of extreme pressure on metallic substances, one first must determine if any structural changes due to hydrostatic compression are also simultaneously occurring. The purpose of this work has been to determine whether the shear stresses induced by hydrostatic pressure in an anisotropic polycrystalline material, such as bismuth, could reach a magnitude great enough to cause plastic deformation and to study the resultant structural changes and effects. THEORY In a metallic crystal, the elastic properties are dependent upon the crystallographic direction and plane. Depending upon the degree of anisotropy of the elastic properties and other factors, internal shear stresses of sufficient magnitude to cause localized plastic deformation may be induced in polycrystalline material by true hydrostatic compression. The following highly simplified two-dimensional model of two adjacent grains in a polycrystalline aggregate under hydrostatic pressure serves to schematically demonstrate how these shear stresses arise in an anisotropic material.

Jan 1, 1963

By J. G. Thompson

IRON, iron everywhere, but hardly a particle of pure unadulterated iron for the metallurgist to use as a base for the protean characteristics that he develops in the alloys of iron-the modern steels. Iron, next to aluminum the most abundant metal in the crust of the earth; one of the oldest metals known to man and serving him as the most indispensable metal in both war and peace; yet man's knowledge of its properties is based on specimens that are not pure and hence probably differ considerably in their properties from the truly pure metal. Purification of iron has brought about startling changes in its electrical and magnetic properties and has modified its behavior in changing its crystal form with temperature, the basis of the heat-treatment of iron. So both the research metallurgist and the metallurgist of the steel plant are intrigued by the possibilities that might unfold were 100 per cent pure iron available in sufficient quantities to determine its properties.

Jan 1, 1940

By J. A. Roberson, Robert A. Rapp

From the observation of platinum wire marker movement in the oxidation of columbium at high lemperatures and low oxygen pressures, predonzinant cation diffusion in CbO, has been demonstrated. The Cu,0 molecule was used as an oxidizing species to study the nature of the porous scale and the location of the reduction site in the oxidation of colum-bium. The Cb205 scale contains microporosity and forms by alternate ionic diffusional growth and fracture. The oxidation of columbium at high temperatures and very low po, results in a relatively compact and protective Cb205 layer. THE observation of marker movements during oxidation is one means for the identification of the mobile ionic species in an oxide lattice. Previous marker experiments in the oxidation of columbium have all resulted in the markers being found on the outside surface of the Cbz05 scale. The Cr203 powder markers of Klopp et a1.,' the gold film marker of Kofstad and ~jijllesdal,' and the platinum wire marker of Cathcart et a1 .3 were found at the oxide/gas interface for oxidation temperatures ranging from 450" to 120O0C. However, in all experiments relatively high oxygen pressures were used. As discussed by Mrowec, even the interpretation of marker experiments in simple scales containing only one compound is not without ambiguities. In brief, it can be said that a marker may be found almost anywhere in the scale layer if the metal oxidizes by cation diffusion through the scale; the position of the marker depends upon morphological happenings in the scale. When considering marker movement in a polyphase scale one must proceed with extreme caution. For example, in the past (and present) work markers have never been found at the columbium-scale interface, and one might infer that the oxygen ion is mobile in CbO and CbO,. However, only trace quantities of CbO and CbOz have been present on any of the specimens, so no firm statement is justified on this basis. Despite previous experimental work, considerable doubt still exists concerning the role of the oxides CbO and CbOz in the oxidation of columbium. The identification of the mobile ionic species in CbO and CbOz from the observation of platinum wire markers was one goal of the present investigation . The linear kinetics of columbium oxidation at high temperatures (T - 1000°C) suggests that the Cbz05 scales which form on columbium are porous. From mercury absorption measurements on a Cbz05 scale formed at 500"C, Aylmore et al.' reported a minimum volume fraction of connected voids equal to 0.15. While these scales often appear to be quite porous when viewed in metallographic cross section, they are so brittle that metallographic preparation is likely to exaggerate any porosity originally present. In this investigation, porosity developed during the oxidation of pure columbium and present at the high temperature was detected by oxidizing specimens in sealed evacuated capsules containing large compacts of mixed copper and CuzO powders. wooda has demonstrated that the CuzO, or (CuzO),, molecule is volatile and that oxygen is transferred by the CuzO molecule from a Cu/CuzO mixture to materials having a greater affinity for oxygen. For each molecule of CuzO that is reduced at a sink for oxygen, two atoms of copper are deposited. Quantitatively, essentially all of the oxidation carried out by a Cu-Cu20 compact results from a displacement reaction involving the CuzO molecule. When a metal which oxidizes to form a porous scale is exposed to the CuzO vapor, the CUZO molecules are reduced in the pores leaving a deposit of metallic copper to mark the site of the reduction. This technique has the rather unique advantage that any copper-coated pores found in the scale are unambiguously related to the reduction site in the growth of the scale under consideration. Pores or cracks which form in a msition*- external to the reduction site or which occur as a result of cooling or handling of the specimen will not exhibit the copper deposit. EXPERIMENTAL PROCEDURE Marker experiments were made on columbium metal, and on pellets of CbO which had been pressed and sintered. Platinum wire markers (0.001 and

Jan 1, 1968

By C. E. Reistle

All crude oils become more viscous when chilled, but the only oils that congeal and precipitate paraffin to such an extent as actually to cause production troubles are those that contain an appreciable amount of wax. In handling these oils of high wax content, three distinct problems may be encountered before the oil reaches the refinery. The first problem is the precipitation and accumulation of paraffin in the well, either in the oil string or on the face and in the pores of the sand. The second problem is the accumulation of paraffin and the congealing of oil in the transportation lines. The third problem is the precipitation of paraffin and the formation of tank bottoms. Factors That Control the Solubility of Paraffin in Crude Oil Two main factors, possibly three, govern the solubility of wax in crude oil. The first of these is temperature. The solubility of wax in crude oil increases with an increase in temperature, and as the temperature approaches the melting point, the wax becomes soluble in all proportions in the crude oil. The higher the melting point of a wax, the less soluble it is in crude oil below its melting point. All crude oils containing wax can be chilled to a point where the oil is saturated with wax. If the temperature is decreased below this point, some of the wax will crystallize from solution. Fig. 1 shows the effect of temperature on the solubility of crude paraffin in oil. The second factor is the amount of volatile constituents and gas removed from the crude oil. Evaporation of the volatile constituents and gas lessens the volume of the oil and concentrates the solution of wax in the oil; therefore less wax can be held in solution at a definite temperature. As the natural amount of wax present in the oil is constant, this results in the oil becoming saturated with wax at a higher temperature than if the volatile constituents and gas were still in the oil. As an example of this, a fresh sample of crude oil having a gravity of 39.8

Jan 1, 1928

Jan 1, 1952

By Prof. B. Hopkinson

Introduction.-A short time ago Professor Stoughton asked the writer if he would present a paper for the February meeting of our Institute. In reply to this suggestion, some notes have been prepared relating to the subject mentioned in the title. It is to be hoped they may be of interest to our members. The research now described is the joint work of Prof. B. Hopkinson, F. R. S., and the writer. Those interested in the subject will find further data in a paper entitled The Magnetic and Mechanical Properties of Manganese Steel, which will probably be read at this year's May Meeting of the Iron and Steel Institute in London. This paper was submitted to the Institute in October last, and advance copies will shortly be available. The present paper has been drawn up by the writer on this side the water, and he has not had time to communicate with Professor Hopkinson with regard to the statements or opinions expressed herein. While the writer believes that Professor Hopkinson would in the main agree with the statements herein set forth, it should be understood that apart from the actual work described he is not otherwise responsible. The experiments described have been carried out on the material known as manganese steel, which one of the writers of these notes discovered in 1883. A paper by him describing this material was read before this Institute in 1893, entitled Iron Alloys, with Special Reference to Manganese Steel. It is not necessary to describe manganese steel nowa-days; its qualities are so well known, and its use throughout the world is on a very extensive scale.

Jan 3, 1914

By G. Sachs

According to Tammann,' the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes Ïn properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by Ewing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931