By Carl E. Swartz

For many years kettles used in the melting and refining of lead and other nonferrous metals and alloys have been made of cast iron. The logic of this probably lies in the fact that cast iron has been known as a material of construction for vessels of this type much longer than steel, and satisfactory fabrication from it has been more easily accomplished and better understood. As the capacity of lead refineries has increased, it has been only natural to increase the size of kettles. Today kettles of 150 to 250 tons are not uncommon. As the size of the kettles increased and better shapes were designed, the uniformity of material of construction became more important. Records kept over comparatively long periods of time have shown that the length of service of kettles has not been uniform. Many causes contribute to this and the importance of each has not yet been evaluated. Kettle design, kettle setting, method of firing and material of construction have been changed from time to time to obtain better service, but the variation in length of service is still great. A kettle may fail during the first few heats or may last through more than one thousand heats. The purpose of this article is not to present the conclusions of a finished piece of research on kettle manufacture and use, but to present a series of observations made over considerable time in the hope that others will publish data and that all may be correlated into a logical scheme which will result in better service and longer kettle life.

Jan 1, 1931

By Y. A. Chang

Heat content values of tantalum monocarbide and tungsten monocarbide have been determined from 325" to 985°K by means of a drop-type diphenyl ether calorinzeter. Based on the values obtained in the present study and those available in the literature, best values lected and computed from 298. 15°K to temperatures close to their respectiue melting points. At temperatures higher than 1700°Kfor TaC and 27000 K for WC, values of Cp and related thermodynamic quantities were extrapolated based on the two Debye parameters: one corresponds to the metal sublattice and the other to the carbon sublattice. The contrzbutzon In the total specific heat due to lattice dilation was evaluated using the Nernst-Lindemann relalionship. The calculated values of Cp were in good agreement with the In view of their refractoriness, tantalum monocar-bide (TaC) and tungsten monocarbide (WC) are of con- experimentally determined ualues. Furthermore, the calculated values of the absolute entropies at 298.15"K were 5.03 and 4.15 in comparison to the experimental values of 5.05 and 4.15, all expressed in the unit of cal per degg-atom. Using the same Debye parameters, values of the linear coefficients of ther mal expansion for TaC and WC were calculated from absolute zero to their respective melting points using the Grüneisen equation. The calculated values are in excellent agreement with the experimental values available in the literature. Finally, the values of the bulk modulus of TaC from room tenzperature to temperature near its melting Point were also calculated using the equation recently derived by Anderson. No cot~ipari-son between the calculated and experimental values can be made due to lack of experimental data. siderable practical interest. In order to completely define these materials, it is necessary to know their thermal properties as a function of temperature. Tantalum rnonocarbide having a NaCl structure (B-1 type) melts congruently at 4250PK,1 while tungsten monoearbide with a simple hexagonal structure (Bh type) melts per itectically at 3049°K into melt and graphite.2 In the present study, the heat content values (from which

Jan 1, 1968

By F. E. Pawlek, J. K. Gerlach

The chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. In the first part of the investigations the reaction rate of the chlorides of sodium or calcium with gas mixtures of SO,-0, or SO ,-O2 ,-SO , was measured. The rate for reactions with gas mixtures SO2-O2 is ThE chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. At present the process is mainly applied to produce nonferrous metals which occur in pyrite cinders in small concentrations. Thereby the nonferrous metals are converted into water-soluble, acid-soluble, or volatile compounds whereas all the iron remains as insoluble oxide. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. The reactions occurring during the roasting process can be divided into two groups: solid-solid reaction and gas-solid reaction. The reactions between solids proceed by means of solid-state diffusion and are therefore of low velocity. The heterogeneous reactions between solids and gases of the roasting atmosphere5 are high-velocity processes and determine the velocity of the chloridizing roasting. These gas-solid reactions shall be the subject of the paper presented. In order to investigate the still little-known processes which occur during the chloridizing roasting 6-' the complex reaction is split into several partial steps. First the reactions of NaCl and CaCl, with gas mixtures of SO2 and 0, have been investigated at temperatures between 500" and 600°C by measuring the weight increase of the samples. The gas mixtures used in this series of experiments had first variable compositions, then the amount of SO 2 had been increased. Furthermore the influence of Fe 2 O3 admixtures upon these reactions, the behavior of pure Fe 2 O3 with the gaseous reactants, and the chlorination of the sulfides of lead, copper, nickel, and zinc have been investigated. FORMATION OF GASEOUS CHLORINE Pyrite cinders are never completely roasted and therefore contain still a small amount of sulfide sulfur. When heated again in air, this sulfur is converted into SO,. Accordingly the formation of chlorine can first be described by the reactions: dependent on the composition of the gas phase. If more than 1 pct SO 3 is added to the roasting gas, the reaction rate is determined only by the concentrations of the SO,. In the second part the reactions between chlorine and metal sulfides are discussed. The rate of formation of gaseous chlorine is higher by me order of magnitude than is the reaction rate between ZnS and chlorine. The reaction rate of NiS and PbS lies considerably below that of ZnS. The conversion rate of both pure Fe 2 O 3 and Fe 2 O 3 containing NaCl or CaCl2 when reacting with SO2-O2, mixtures with and without SO3 portions was measured at temperatures of 500", 550°, and 600°C. The weight increase of pressings was determined by means of a spiral balanceg and the reaction rate calculated therefrom according to Eqs. [ll to [31 and [5] to [7]. The prepared samples were suspended on a platinum filament in a vertically mounted tube of mullite (ID 4 cm, length 110 cm) which could be heated by a resistance tube furnace. The platinum filament was tied to the lower end of the spiral balance. A supremax glass tube (length 70 cm) was mounted gas-tight on top of the reaction tube. The unit was sealed up at its top by a ground-in stopper which was holding the spiral balance with the sample. The spiral balance therefore hung outside the high-temperature region of the furnace. Fig. 2 shows the experimental arrangement schematically. While lowering the sample into the reaction tube pure nitrogen was flowing through the reaction zone providing a protective atmosphere. After the sample had reached the reaction temperature within approximately 1 min, the protective gas was replaced by the sulfur dioxide-oxygen reaction mixture. It took about 30 sec until the mixture filled the tube homogeneously. A Ni/NiCr thermocouple placed in the center of the furnace where the sample hung during the measure-

Jan 1, 1968

Jan 1, 1969

By L. C. Brown, E. B. Hawbolt

The formation of grain boundary precipitates has been studied in Ag-5.64 wt pcl Al alloys at 688°C. Large-grain specinzerzs were used and the boundary misorientation measured by X-ray diffraction. At low-angle grain boundrrries Primary sideplates form. u)hile abore a 17-deg misorientation lenticular precipitates predominate. Growth of the lenticular precipitates was studied on individual grain boundaries using a statistical technique. The thickening and lengthening rates appeared to be independent of &apos;pain boundary misorientation, indicating that grain boundary diffusion was not significant in this system. The precipitates grew urith constant shape, with both the length and thickness increasing parabolically with time. The parabolic lengthening rates were unexpected since previous theory and experimerztal results had indicated linear growth. By approximating the shape of the precipitate to that of an oblate spheroid grouling with constant shape an equivalent diffusion coefficienl was calculated. The zlalue obtained was in good agreement with nleasurements obtained fron, diffusiorz couples. IF a single-phase alloy is heated or cooled to a temperature such that the phase becomes supersaturated, there is a tendency for a second phase to precipitate from it in order to remove the supersaturation. Precipitation takes place initially on grain boundaries due to preferred heterogeneous nucleation, but subsequently Widmans kitten plates may form in the grain interiors if the grain size and supersaturation are sufficient. The type of grain boundary precipitate formed depends on the nature of the boundary. Aaronson1 and clark2 have shown that grain boundary misorientation can be characterized by the simple parameter R, where and X, Y, and Z represent the minimum rotations about three orthogonal axes required to bring the two lattices forming the grain boundary into coincidence. The maximum value for R is 60 deg. In using this parameter the orientation of the grain boundary itself is, of course, neglected. However it was found in both Fe-si3 and A1-Ag2 that the precipitate shape depended only on the parameter R. Clark found that the vast majority of precipitates formed were allo-triomorphs— lens-shaped precipitates that grew along the grain boundaries. At low-angle boundaries, however, (R < 15 deg) Widmanstatten sideplates nucleated at the grain boundaries and grew into the adjacent grains. It has been reported that the rate of growth of grain boundary precipitates is controlled by diffusion within the supersaturated phase.&apos; The theories which have been developed for growth rates have assumed the diffusion coefficient constant over the composition range of the supersaturated phase. This is a fairly good approximation if the composition range involved is not large. Thickening rates have been calculated using the theory developed by Zener4 and by Frank5 for the growth of planar precipitates. A parabolic growth law

Jan 1, 1968

By H. Ries, R. E. Somers

Bodies of pyritic ore in schistose rocks have long been known in different parts of the world. The several occurrences resemble each other in being usually of more or less lenticular shape, inclosed in walls of schist or gneiss, and carrying pyrite, chalcopyrite, and pyrrhotite in varying proportions, as the chief ore minerals. The deposits differ, however, in that sometimes one, sometimes another, of the three sulphides mentioned may predominate. The orebodies in general are more or less closely conformable with the schistosity of the wall rocks, although in cases this may not hold true. The boundaries may or may not be sharp, but in general are fairly distinct. The lenses vary in size, may occur singly, or in groups; in the latter case they may be in line, overlapping, or occasionally parallel. Pinching and swelling of individual lenses is not uncommon. The genesis of these pyritic bodies has provoked much discussion, and they have been variously classed as sedimentary, igneous intrusions, hydrothermal replacements or impregnations, etc. Indeed, in some cases different geologists have most positively assigned widely diverse origins to the same deposit, as in the case of Rio Tintol and Rammels-berg.2 It is true that in the light of modern criteria, we have been able in a few cases to decipher clearly the process of origin and so there seems no. doubt now regarding the genesis of the deposits at Rio Tinto, Spain;3 Rammelsberg, Germany;4 Ducktown, Tenn.;5 southwestern Virginia;=

Jan 1, 1918

By A. T. Chatas

A description of the geometrical characteristics of spherical reservoir systems, a discussion of unsteady-state flow of such systems and examples of engineering applications are presented as backgmund material. The fundamental differential equation, a description of average spherical permeability and the introduction of the Laplace transformation serve as theoretical foundations. Engineering concepts are investigated to indicate particular solutions of interest, which are analytically obtained with the aid of the Laplace transform. These are numerically evaluated by computer, and presented in tabular form. INTRODUCTION A tractable mathematical analysis of unsteady fluid flow through porous media generally requires incorporation of a geometrical symmetry. The simplest forms include the linear, cylindrical (radial) and spherical. Most analytical endeavors have concentrated on cylindrical symmetry because it occurs more often in petroleum reservoirs. Nevertheless, some reservoir systems do exist that are better approximated by spherical geometry. Review of technical literature revealed but a single reference to unsteady spherical flow in petroleum reservoirs.l The motive and purpose of the present work was to remove this gap in technical information, and to provide the practicing engineer with some useful analytical tools. The mathematical details associated with the particular solutions of interest involved use of the Laplace transformation. Hurst and van Everdingen previously demonstrated the efficacy of this operational technique, and in many respects the present treatment was patterned after their earlier work.2 PRELIMINARY CONSIDERATIONS GEOMETRICAL CHARACTERISTICS Geometrically, a spherical reservoir system is defined at any instant of time by two concentric hemispheres whose physical properties of interest vary only with the radial distance. Every physical property is thus restricted to be a space function of only one variable: the distance along a radius vector emanating from the center. Such a system is composed of an outer region and an inner region, separated by a defined internal boundary. The inner region simply extends inward from this boundary, whereas the outer region extends outward from it to an external boundary. The position of the internal boundary is presumed fixed, so that the size of the inner region remains constant. On the other hand, the position of the external boundary at any given instant of time is determined by the distance into the system that a sensible pressure reaction has occurred, Thus, the external boundary may change position with time. It initially emerges from the inner region and advances outward to its ultimate position. When this ultimate position coincides with a geometric limit, the reservoir system is said to be limited. When it coincides with points subject to pressure gradients furthest removed from the internal boundary, yet short of a geometric limit, the system is said to be unlimited. In this investigation two different boundary conditions are imposed at the ultimate boundaries of limited systems. The first requires that no fluid flow occur across this boundary; the second that the pressure remain fixed at this boundary.3-5 UNSTEADY-STATE FLOW In a strict sense virtually all flow phenomena associated with a reservoir system are unsteady-state. The transient behavior of these phenomena requires accounting, however, only when time must be introduced as an explicit variable. Otherwise, steady-state mechanics may be used. Analytically, steady-state conditions prevail in a reservoir system only over that portion of its history when this relation is satisfied:

Jan 1, 1967

By T. Johnston, B. Cox

The results of oxidation and corrosion experiments on niobium in oxygen and steam at temperatures of 350° to 650°C, and in dilute sulphate solutions at 300°C are presented. The oxidation of niobium in oxygen can be explained in terms of a pre-transition period, which obeys an approximately parabolic rate law, and a post-transition period in which a more rapid linear rate is partially stifled by restriction of the gas flow due to the gvowth of the porous outer film. Due to changes in the porosity of the outer layers the restriction presented by the porous outel. film attains a limiting value. Subsequent oxidation obeys a linear rate law and shows an almost linear dependence of the rate on gas pressure. liltimately a second failure of the protective film may take place leading to a further acceleration in the oxidation rate. In water vapor the oxidation of niobium follows a parabolic rate law and does not show a transition to linear kinetics. The higher oxide, Nba05, was usually absent from the NbO/NbO2 film which was formed. The addition of a small partial pressure of oxygen to the water vapo3, resulted in accelerated oxidation according to the normal kinetics for oxidation in oxygen. The oxygen reacted preferentially with the niobium, and the protective oxide film was reformed when all the oxygen had been consumed. This behavior supports the theory that nucleation of Nb205 on the surface of the protective NbO/NbO2 film is the cause of the accelerated oxidation. After oxidation in steam at high-pressure Nb2Os was found in the protective film. The mode of formation of Nb2O5 under these conditions did not produce a change in kinetics, but was thought to explain the comparatively large dependence on pressure of the oxidation rate. The kinetics of oxidation in oxygenated aqueous solutions at 300°C were similar to those for oxidation in oxygen. A penetrating attack on niobium sheet may be related to the second breakaway observed by some investigators of oxidation in oxygen.

Jan 1, 1963

By E. E. Underwood, L. L. Marsh

Aluminum single crystals, alloyed with 0.042 atomic pet Cu and 0.11 and 1.1 atomic pct Mg, were subjected to constant stress creep tests, tensile tests, and hot hardness measurements within a temperature range of 300° to 866OK. Calculations based on Dorn&apos;s temperature-compensated time parameter, 6, gave a value of DH, = 27,000 cal per mol for the activation energy of early creep in aluminum single crystals. Correlations have been obtained for aluminum alloy single crystals with the parameter E for solid solution strengthening, as well as with the parameter F for solid solution hardening, by using a valence of three for aluminum. Limited measurements on tensile specimens show that the slip band density tends to decrease with increasing temperature and with decreasing solute concentration. INCREASING interest is being shown in the mechanisms of plastic deformation in single crystals during tensile and creep testing. The complexity of deformational processes in polycrystalline materials has led to a search for simpler experimental conditions. Numerous creep and tensile investigations have been conducted with pure, metallic single crystals. To a lesser degree, the effects of alloying elements on the tensile properties of single crystals have been determined. However: the literature dealing with the effects of alloying additions in single crystals under creep conditions is vanishingly small. This paper represents an attempt to narrow this gap in the knowledge of the subject. Previous investigations of creep behavior at the Battelle Memorial Institute1-1 have been of great value in the analysis of the present single crystal data. It is equally desirable, however, to ascertain the extent of correspondence between the behavior of single crystal and polycrystalline materials. For this purpose, correlations, similar to those developed for polycrystalline aluminum alloys by Dorn and co-workers, have been made with the single crystal data. The results from this study have tended to confirm and extend those correlations to the case of alloyed single crystals. Materials and Procedures Three dilute binary aluminum alloys were prepared for this investigation from 99.99 + wt pct Al, 99.8 wt pct Mg, and 99.92 wt pct (electrolytic) Cu. The nominal compositions of the alloys were 0.042 atomic pct Cu, and 0.11 and 1.1 atomic pet Mg. Precautions were taken to avoid contamination of the stock during melting and casting of the alloys. After a heat treatment of 8 hr at 925°F the alloys were extruded, then machined into) threaded tensile specimens with a 3 in. reduced section and a 0.505 in. diam. Spectrographic examination showed less than 47 ppm metallic impurities in each alloy. The single crystals were grown by the strain-anneal method, with a critical strain of about 11/4 pet giving the optimum results. In general, 3 in. crystals were obtained with the Al-Cu alloy, but smaller crystals in the magnesium alloys necessitated the use of 2 in. and 1 in. gage lengths with the low and high magnesium alloy specimens, respectively. After an electrolytic polish, the orientation of that portion of the specimen containing the largest single crystal was determined from Laue back-reflection photographs. Tensile tests were conducted at a constant load rate of about 2 lb per min. Creep runs were made in a constant temperature room, under constant stress at the higher creep temperatures, and constant load at the lower temperatures. The eloneation was measured to within ±5 microin. by a specially designed capacitance extensometer. The ex-tensometer arms were attached to the 3 in. specimens at the shoulders of the test piece or, where the crystals were smaller than 3 in., by knife-edge grips.

Jan 1, 1957

By J. G. Bouwkamp

This paper presents three general approaches towards the solution of the stress distribution and the behavior of tubular connections as used in offshore well drilling structures. First, the possibilities of using plastic models and photoelasticity techniques in evaluating the stress distribution in gusset plate connections are analyzed. The results of photoelastic studies on the stress distribution in the in-plane gusset plate of two-dimensional joints are presented. The influence of the configuration of the gusset plate (with and without cut-outs) is discussed. Second, the paper deals with recent developments and applications of computer programs to analyze connections with directly inter-welded tubes and with gusset plates. The possibilities and limitations of these programs are discussed. Stress patterns analyzed with these programs are presented for different joint configurations. Finally, the basic test procedures and results of a test on a tubular joint under static and alternating loads are discussed. INTRODUCTION The effective design of tubular connections as encountered in offshore well drilling towers or floating platforms has been complicated basically by the radial flexibility of the tube walls. This flexibility is a source of severe stress concentrations which can initiate an early failure of these joints. In an attempt to reduce the influence of the wall flexibility of the column tube, certain joints are presently designed by inter-welding the incoming branch members. In those designs, the force acting normal to the chord tube can be reduced considerably. A second group of joints incorporate gusset plates or stiffening rings to stiffen the column wall and to distribute the incoming branch member forces over a larger part of this wall. A third approach to improve the stress distribution in a tubular joint is to increase the wall thickness of the column member. This can be achieved by simply applying a thicker wall section in the vicinity of the joint. A fourth possibility to restrain the radial flexibility of the tube wall is to fill the column member with concrete. Also, a single, cast steel seat welded to the column tube can be used to improve the stress distribution in this wall. Although all these designs improve, in general, the state of stress in the column wall, the altered stiffness often causes the development of critically stressed areas in the web members. At the same time the actual design in most instances is decisively influenced by the site which governs the depth and controls the forces produced by waves, earthquakes and ice flow. Also, the towing, erection and foundation requirements of offshore structures can affect the actual design selection. Because of the complexity of the structural configuration of tubular joints, the stress analysis of these connections has necessarily been based on simplified and often crude assumptions. For the earlier and smaller type of connections with about 4-ft diameter column sections, the primary problem was to evaluate the relative stiffness of the column wall section and the load transfer between joint members. Due to the recent developments of offshore drilling structures with increasingly larger connections (e.g., column diameter. 32 ft; web members, 8.5 ft) this problem has become even more critical. One design philosophy for such large joints follows a member-to-member connection with radially heavy reinforced column sections. This radial stiffness can be attained by closely spaced and intensively stiffened horizontal diaphrams together with vertical stiffeners. A second solution incorporates a concrete-filled section between the outer and inner walls of the column tube. Another philosophy considers large gusset-plated joints. The problem in these joints is to develop an effective load transfer between the branch tubes and the gusset plate and to minimize the stress concentrations in the member walls as effectively as possible. Several concepts are followed to achieve this gradual transfer between web-member walls and gusset plates. Because the number of joints in these huge platforms is limited compared to the over-all size, a proper design of these joints is even more important than was the case for the many joints in the smaller, but multi-legged towers. A failure of one of those ultra-large joints could well cause the complete collapse of such a structure. Under these circumstances an accurate analysis of the large joints is of the greatest importance, together with information regarding the expected behavior of such joints under critical alternating load conditions. Recent applications of photoelastic model techniques have proved to be quite effective in evaluating the elastic behavior of such joints. Although a complete study of such connections is quite well possible with present-day photoelastic techniques, it might often be feasible and necessary to limit the objectives and to restrict these investigations to the study of a specific aspect of the joint. Another very promising avenue of approach to solve the complex stress pattern in these connections seems to be the recent development of digital computer programs. In this category, cylindrical shell programs and finite element methods for more complex configurations have

Jan 1, 1967

Jan 1, 1928

By P. D. Merica, J. R. Freeman, R. G. Waltenberg

Contents Page Constitution of Commercial Aluminum.................. 4 Solubility of CuAl2 in Aluminum at Different Temperatures........ 9 Effect of Magnesium on Solubility of CuA12 in Aluminum ......... 15 Solubility of Mg4Al8 in Aluminum at Different Temperatures........ 15 Solubility of Metals and Metal Compounds in Aluminum.......... 20 Summary and Conclusions......................20 Aluminum and its alloys have been the subject of much investigation1 during recent years, in the course of which the principal features of the constitution of most of the binary alloy systems with aluminum have been determined. Except in the case of a few metals—silicon, bismuth, cadmium, lead, zinc, and tin—an aluminum-rich compound is formed in each binary system, which forms a eutectic with the aluminum or its solid solution with this compound: Thus such compounds as FeAla, CuA12, Mg4Al3, and NiAls are formed, which are found in aluminum-rich alloys of their respective series as eutectics with the aluminum solid solution. These compounds are, in all cases, hard and brittle and their presence affects profoundly the physical properties of the alloys in which they occur. Within the zinc-aluminum system a compound, Al2Zn,, is formed that decomposes at lower temperatures. Silicon and tin each form a simple eutectiferous series with aluminum; bismuth, lead, and cadmium are only partly miscible in the liquid state with it. The extent of the solubility in aluminum, in solid solution, of these compounds or of the elements themselves, in the case of those series in which compounds are not formed, is of the greatest importance in

Jan 1, 1921

By Carl Pierce

THE writer of this article has not attempted to write a technical paper; on the contrary, he has tried to express in "steel-plant English," for steel men, a viewpoint drawn from his practice and experience. It is not his thought that it shall be taken as the "last word" in the making of this class of steel, or that good rimming steel cannot be made by any other practice. The paper was written to serve as the basis of a discussion from which it is hoped much benefit may be derived. The paper deals only with rimming steel made by the open-hearth process, and with the lower carbon steels, such as sheet and tin bar, rivet stock, skelp, etc., although good rimming steel as high as 40 to 50 carbon can be made by having good open slags and giving proper attention to working and tapping temperatures.

Jan 2, 1926

By E. C. Bain, E. S. Davenport

When annealed carbon, or low-alloy, steels are suitably heated the ferrite (alpha iron solid solution) and the carbide, of which they are composed, react together to form a single solid solution of carbon (and other elements) in gamma iron (austenite). This reaction may begin only at a certain minimum temperature called the eutectoid temperature. The first ferrite and carbide thus to react together do so in definite proportions known as the eutectoid composition. With further heating the original constituent that is present in excess is dissolved in the austenite until exhausted. Whether the excess constituent be ferrite (hypoeutectoid steels) or carbide (hypereutectoid steels) the procedure is much the same, and upon slow cooling the homogeneous austenite expels the excess of either (proeutectoid ferrite or carbide) until the eutectoid composition is reached. Thus the reaction upon heating is strictly reversed upon cooling and accordingly an equilibrium diagram of this process may be constructed. Such an equilibrium diagram concerns itself only with the temperatures involved and with the proportions and compositions of the phases developed under conditions that suffice to permit equilibrium. Specifically it has no concern for the type or mode of distribution of these constituents nor with any extra-equilibrium conditions such as undercooling, which is almost universally encountered in metals. Actually, however, of great importance is the sluggishness toward equilibration caused by the not inconsiderable time involved in diffusion. Thus instead of the theoretical transformation point AF, we find for a certain rate of heating or cooling the use of the designations Ar and Ac (transformation temperature found on cooling and upon heating). These figures obviously have no particular meaning except as measured and expressed for a definite heating or cooling rate, and represent the apparent temperature displacement caused by an inadequate time allowance. In this paper are presented the results of a study of the time required for the transformation of austenite to ferrite and carbide at a variety of temperatures and also of the time required for the reaction austenite? martensite at the temperatures at which this reaction occurs instead of

Jan 1, 1930

By R. L. Slobod, C. Gatlin

This .study defines the basic mechanism of the mis-cible displacerrzent of oil and writer from porous Medici by various water-driven alcohol .slugs. Three distinct alcohol slug processes were .studied. Considerable data concerning the quanity of alcohol required for oil recovery were also obtained. All data were obtained in a 1-in. diameter, 100-ft long, unconsolidated core. The porosity of this system was 35 per cent. and the permeability was approxitrlately 4 darcies. Total core pore volume wax 5,716 cc. All displacements were conducted at a constant injection rate of 5 to 6 cc//min, which corresponds to a frontal advance of 5 ro 6 ft/hr. The first portion of this paper is concerned with 111 use of one alcohol—isopropyl—a\. the slug material. Isopropyl alcohol (IPA) is completely miscible with both oil rind water; however, miscibility of the threc-component systems, oil-water-IPA, requires a relutively. high concentration of IPA. Hence, the displocement is not of the misoible type unless the IPA concentration is maintained above some critical value. A slug of IPA equal to only 13.5 per cent of the pore volume was jound to be sufficient to obtain complete recover?, of residua1 naphtha. In later studies two distinct process variations were developed. The firsr of these utilized methyl alcohol (MA) and IPA as slug materials. It was shown that methyl alcohol may he substituted for IPA at the front and rear of the slug with no loss of oil recovery. A .slug of 4 per cent MA-4 per cent IPA-4 per cent MA was sufficient for complere oil recovery. Because MA is considerably cheaper than IPA, this represents an important step toward economic application. A .second process variation used normal butyl alcohol (nBA) and MA as the composite slug, the nBA segnzent being injected first. This technique requires the smallest total slug size (approximately 10 per cent) of all processes studied. The high cost of nBA, however, precludes commercial application. It is possible that this basic process, subject to changes of alcohol type, may lead to a commrercicil process. INTRODUCTION Within the last 10 years, considerable study has been devoted to the general mechanics of miscible phase dis- placements in porous media. These studies have. in general, dealt with two-component displacernent. All reported field trials to date have been modified gas drives of one type or another. These utilize either lean gas at high pressure, rich gas at lower pressure or an LPG slug. The irreducible water content of the reservoir remains immobile during these processes. Although these techniques hold great promise. certain drawbacks do exist. Poor areal sweep efficiency, inherent in any displacement having a highly unfavorable mobility ratio, is one disadvantage. Furthermore, the miscibility of all processes which use gas is dependent on pressure. These pressure limitations may prohibit application to shallow reservoirs. There are also many areas where large quantities of LPG and natural gas are not readily available. These factors emphasize the need for improved techniques. The alcohol slug process is also a miscible-phase displacement process. It differs from the previously mentioned two-component techniques, however, in that both the reservoir oil and water are displaced by the slug. This behavior is a consequence of the miscibility of certain oil-water-alcohol systems. In the simplest case, a relatively small volume (slug) of an alcohol (such as isopropyl) is injected into the system. Water is then used to drive the slug through the medium. Thus. three components—-alcohol. oil and connate water-—exist at the front side of the slug. Miscibility is obtained at some alcohol concentration, this being dependent on the solubility of the particular system. Miscibility is maintained within the slug until the alcohol concentration falls below that value required to maintain miscibility. When miscibility is lost, the process reverts to a water flood. Certain inherent benefits of this technique are apparent. High pressures are not necessary to obtain miscibility in these liquid systems. Furthermore, water is a more desirable driving agent than gas because of the improved mobility ratio and the attendant improvement in areal sweep efficiency. The main disadvantage is, of course, the relatively high cost of alcohols. The use of an alcohol slug to recover reservoir oil is not a new idea." &apos; However, this process has received only limited study, presumably due to the lack of industrial interest caused by the seemingly prohibitive cost of alcohols. The main purpose of this study was to investigate the mechanism of the displacement of oil and water by various alcohol slugs and to develop process modifications aimed toward possible commercial application.

By A. J. Garnier, N. H. van Lingen

Rock downhole is known to be lesc. drillable than when brought to the surface. This must be ascribed mainly to the presence under downhole conditions of a pressure differential across already made chips, which hinders their being lifted. The pressure differential has partly a static and partly a dynamic origin. Balling-up of bits is another consequence of this pressure differerztial. Reduction in penetration rate owing to an increase in the strength of the rock is governed by the difference between the mud pressure and the pressure of the for/nation pore liquid. Rotationally symmetric geostatic stresses have 170 effect on drillability. Fracture of rock when drilling will be brille in most cases. The above is supported by laboratory drilling experiments with drag bill and roller bits an elevated mud, pore, and confining pressures On rocks differing in strength and permeability. INTRODUCTION In oil well drilling drillability of rock is found to decrease with increasing depth of the hole. Naturally deep rock will be more compacted and, therefore, harder to drill than shallow rock of the same type. However, apart from this the drillability of a sample of deep and compacted rock brought to the surface is generally much higher than in its original location downhole. In view of the economic implications of this reduction in drillability, it seems worthwhile to analyze its causes. The origin clearly has to be sought in the difference of environment. The only conceivable factors would seem to be the presence of mud under pressure, the pressure of the formation pore liquid, and the overburden of the rock. Down the borehole the rock is compressed triaxially by mud pressure and overburden. It is well known that the strength of rock is increased when confined by external pressure1. Various authors have, therefore, ascribed the difference in drillability mainly to the strengthening of rock by triaxial compression. Another factor, mentioned by Bobo and Hoch5, is that forces. including "pressure differential forces", tend to hold a dislodged particle in place. However, the conditions determining their magnitude are not clarified nor is their effect on drilling rate assessed. In the laboratory, drilling experiments on pressurized samples of rock yielded evidence that pressure differential forces holding the chips down are the major factor in reducing rate at depth. This paper describes the experiments and shows how the results enable both a qualitative and a quantitative interpretation of the factors determining the effect of chip hold-down on drilling rate. The implication with respect to balling-up and jet action is also discussed. The greatcr part of the experiments were performed in the pressure vessel shown in Fig. 1. The spacc between the sample of rock and the vesscl is divided by "0" rings into three separate chambers. The rock sample is confined laterally by pressurized oil in thc middle chamber. Penetration of oil into the sample is prevented by partly jacketing it with brass foil. Thc pressure of the drilling fluid in the hole can be adjusted via the upper chamber. Permeable rock specimens arc water saturated before being drilled. With a properly plastering mud as drilling fluid the pressure of the pore water can be adjusted independently via the lower chamber.

By H. T. Sumsion, A. U. Seybolt

The results of an investigation of vanadium-rich V-O solid solutions are presented, indicating the structure and lattice parameters of two solutions, a and ß, and their approximate temperature-composition existence. The a solution is the terminal body-centered cubic one, and contains up to 3.2 atomic pct 0. The ß solution has an ordered body-centered tetragonal structure, is formed at 1270°C, and exists from about 15 to 22 atomic pct 0. From the evidence available, the various phase boundaries have no appreciable temperature dependence. Evidence has been found for a polymorphic transformation in pure vanadium at 1550°C. IN an earlier investigation&apos; dealing with the preparation of pure vanadium by calcium reduction of the oxide, it was found that small amounts of oxygen drastically reduced the ductility of the metal. Because this effect was so marked, it was decided to make a study of the solubility of oxygen in solid vanadium. This report deals principally with this solubility and the nature of the phase relationships in the vanadium-rich region, particularly at temperatures below 1300 °C. However, during the investigation enough data on the V-0 system were obtained to make it appear worthwhile to present a tentative phase diagram up to the composition VO. The only significant prior work found on this system are the contributions of Klemm and Grimm,&apos; and Mathewson et al.3 Klemm and Grimm prepared a wide range of V-O compositions by powder techniques including the compositions VO.l, VO.2, VO.3 and VO4 (9.1, 16.8, 23, and 28.6 atomic pct 0, respectively). The first three compositions were found to consist of a body-centered tetragonal solid solution, while the last also showed lines of VO (NaCl structure). They found that the parameter c, increased and the parameter a, decreased with increasing concentration of oxygen. For their composition VO.27, or about 16.8 atomic pct O, they cite the values a, = 2.948A, c, = 3.53A, and c/a = 1.2. Klemm and Grimm made no attempt to determine the solid solubility limit nor to construct a phase diagram. They did, however, give some data on the homogeneity range of VO, and they proposed a structure for the body-centered tetragonal solid solution; these points will be taken up later. Materials and Preparation of Samples The vanadium used in this investigation was prepared in the laboratory by the method previously mentioned.&apos; A typical analysis is as follows: Fe, 0.007 pct; Si, 0.02; Ca, 0.06; C, 0.224; O2, 0.044; N,, 0.0017; H2, 0.003; and V, 99.34 ±0.3 (assay). The vanadium assay is probably low by about the error given. The impurities total about 0.36 which, if subtracted from 100, gives a purity of about 99.6. At the time material was being prepared for this work no suitable technique was available for melting vanadium without appreciable contamination. The procedure adopted therefore was to cut the calcium-reduced regulii into slices which were then rolled to strip about 0.025 in. thick for oxygen diffusion. Pieces of rolled vanadium of approximately 0.025xY4xl in. and weighing about 0.3 g were suspended in a vertical fused-silica tube which was part of an ordinary gas absorption apparatus. The silica tube was heated by an electric resistance-tube furnace which could be raised around the silica tube or lowered away from it as desired. This apparatus had no novel features which require detailed description. Other than the silica tube and furnace, it consisted of a glass system evacuated by a liquid nitrogen trapped mercury diffusion pump, a mercury-operated gas burette, a McLeod and a Pirani gage, and a mercury manometer. It was also equipped with suitably located stopcocks for isolating various parts of the system; the vacuum ordinarily attained was between 10" and 10-6 mm of mercury. Oxygen generated by decomposing MnO2 was passed through anhydrous magnesium perchlo-rate before introducing it into the gas burette and thence to the absorption chamber.

Jan 1, 1954

ASHBEL WELCH, Lambertville, N. J.: Dr. Dudley has given the wear of steel rails under four different conditions. He arrives at the conclusion that the softer rails, or those that from their composition ought to be softer, wear better than the harder. But there is another condition which has an important bearing on the subject, and should not be overlooked,—the weight on a wheel. With the lighter weights of the past, the softer rails may have worn best; with the heavier weights of the future, the harder may wear best. Weights will probably be increased up to the capacity of steel to bear; then doubtless the harder steel will wear best. A leaden rail with ten pounds on a wheel might carry millions of tons, but with one hundred pounds on a wheel, it would be destfoyed by a few thousand tons. So in the days of iron rails, my experience was that the softer rails under light machinery stood better than some of the harder; but under heavy machinery the softer were muqh the most rapidly destroyed. It is doubtless the same with steel. The pounding motion of the wheels loosens or spreads the particles of a thin film of steel; the pull lengthwise on the rail de-

Jan 1, 1881

By Ulf S. Landergren

Diffusion coefficients and marker movements have been determined in brass using welded couples. Three different concentration ranges were employed at 750°C, while a fourth concentration range was measured at 500°, 600°, 700°, and 800°C. Marker displacements toward and porosity development in the high zinc side of the couple were observed in all cases. The results were interpreted as favoring a vacancy diffusion mechanism. IN the large amount of diffusion literature which has accumulated during the past half century, very few experimental data have been presented on body-centered-cubic metallic phases. The impressive combination of experimental and theoretical studies which has given the vacancy mechanism a fairly secure position as the preferred mechanism for most face-centered-cubic metals has no counterpart for body-centered-cubic phases, although the theoretical picture seems to be in a better state than the experimental work. The attempts to select diffusion mechanisms by the theoretical calculation of the activation energy for the various conceivable unit diffusion processes and the energy of formation of the type of lattice defect required have been based on models of two kinds. The first kind utilizes potential functions fitted for certain properties of pure crystalline copper; the second kind is fitted for sodium. The latter is an example of an open metal in which the metallic ion is small compared with interatomic distance,&apos; while the former is characteristic of the larger class of metals in which the ions have diameters about as large as the interatomic distance. brass should resemble copper in this fundamental property. It should be evident that results on the mechanism of diffusion obtained for one of these classes need not necessarily apply to the other. Huntington and Seitz, using a model of the copper type, showed that the activation energies to be expected for interstitial migration or a two-atom direct interchange were much higher than that for vacancy diffusion. Zener pointed out that a four-atom ring rotation would involve an activation energy considerably lower than the two unlikely mechanisms although still higher than the vacancy mechanism in the face-centered-cubic structure. Furthermore, he argued, the four-atom rotation would be relatively easier in a body-centered-cubic lattice and might be competitive with the vacancy mechanism. Paneth showed that a body-centered-cubic crystal-like sodium could form interstitial defects of special type, called a crowdion, by crowding an extra atom into < 111 > directions where the defects would affect a line of about eight atoms. The defect was constrained to move along the defining line. Unlike the face-centered-cubic case, therefore, the theoretical calculations for the body-centered-cubic mechanism do not provide a very clear-cut answer, and the absence of adequate experimental studies is the more serious. This investigation was undertaken for the purpose of obtaining useful information on diffusion in body-centered-cubic phases. brass was chosen for several reasons: 1—the phase field is sufficiently wide at high temperatures to permit the use of diffusion couples with adequate concentration ranges for satisfactory chemical analysis, 2-—thermodynamic activity data are available for the calculation of mobilities from diffusion coefficients, 3—the phase is as close to the theoretical model of the copper -type on which the calculations have been done as any body-centered-cubic metallic phase is likely to be. Measurements of the movements (if found) of inert markers during the diffusion process would indicate that a vacancy or Or mechanism played a major role in diffusion in brass. If no marker movement should be found, a ring mechanism would be indicated but not assured. Experimental Procedure The alloys used in these experiments, listed in Table I with analyses, were supplied by the Naval Research Laboratory. They were from ingots of 3x3 in. cross-section, heated to 760°C, reduced under a

Jan 1, 1957

By R. E. Cech

Metallographic observations on hydrogen-reduced nickel oxide crystals suggest that nucleation of nickel occurs at structural singularities in the oxide. The fully reduced structure contains micron-diameter, worm-like voids occupying 40 to 50 pct of the volume. The crystallographic orientation relationships between nickel oxide and nickel resulting from oxide reduction are recorded and discussed. THE process of reduction of oxide to metal is one of considerable complexity involving a chemical reduction reaction, mass transport of reducing agent to the point of reaction and of reaction product away from it, and finally a transformation whereby metal atoms released from the oxide rearrange to form a stable reduced phase. In addition, nucleation of the reduced phase affects the overall reaction kinetics. Thus far only the thermodynamic aspect of reduction has received the attention warranted by the importance of

Jan 1, 1960