Search Documents

By Zuomei Jin

A laboratory study was conducted on the separation of Zn, Pb, Cu and Ag from a finely dissem-inated interlocked silver-rich multimetal sulphidc ore. These are often difficult to separate from each other by flotation. The thermodynamic calculations of Zn-S-O, Cu-S-O systems at different tem¬peratures were presented on predominance diagrams. Based on these diagrams the optimum temperature and gas composition were selected for roasting. The results of separating Zn, Cu from calcine by neutral leaching and acid leaching were found to be satisfactory. The distribution of silver in the roasting and leaching processes were tested. A flow sheet was proposed.

Jan 1, 1993

By Xi Yun Yang

Ultrafine (0.1µm) spherical magnetite powder was prepared successfully by hydrothermal reaction of ferrous sulfate and sodium hydroxide with activated pyrite as reducing agent in the temperature range 120-140?. XRD and XPS analyses indicate that pH value and pyrite amount have a direct influence on the composition of the product. Stoichiometric Fe3O4 can be obtained only when pH value is 12 and the molar ratio of pyrite/ferrous sulfate is 1:1.8. The hysteresis loop of Fe3O4 shows a ferromagnetic behavior with a saturation magnetization of 75.2 emu/g and a coercivity of 152Oe.

Jan 1, 2006

By Daojin Cao

The chemical components in the saturated aqueous solution of ammonium dimolybdate (ADM) were investigated at room temperature by comparative Raman spectroscopy. In order to explore the further detailed results, a new method of qualitative and half quantitative analyses, based on the main vibrant frequencies and the intensity ratio of the strongest peak to the second strongest peak recorded in Raman spectrum of saturated aqueous solution of ammonium heptamolybdate tetra hydrate (AHM), was put forward and attempted to analyze the chemical components of saturated aqueous solution of ADM. The results showed that there was obvious difference between Raman spectrum of saturated aqueous solution of ADM and that of ADM, but there were good relationships between Raman spectrum of saturated aqueous solution of ADM and Raman spectra of the three samples including AHM, the saturated aqueous solution of AHM and monomolybdate ion in aqueous solution. It was found that aggregated dimolybdate ion ({Mo2O72-}n)did not exist in the saturated aqueous solution, and was changed into heptamolybdate ion (Mo7O246-) and monomolybdate ion (MoO42-), which were in equilibrium each other, but the distribution ratio of heptamolybdate ion was larger than that of monomolybdate ion. In addition, Raman spectral pattern of saturated aqueous solution of ADM was reported.

Jan 1, 2006

By Renaud Metz

The DOPA process (Direct Oxidation of a Precursor Alloy) was used to prepare ceramic powders based on doped SnO2 and ZnO. The DOPA process consists essentially in the direct oxidation of a homogeneous precursor alloy. A unique advantage of this process is its rather benign environmental impact since no dangerous reactants are used and no harmful by-products are generated. Only oxygen and the alloy metals participate on the chemical reaction to produce the multi-component oxide. Homogeneous alloys of niobium, cobalt and chromium doped tin have been prepared. The molten metal alloy is atomised in air using a double fluid nozzle to produce metallic powders. A subsequent thermal treatment is carried out to fully oxidise the sprayed metal alloy powders. These raw powders are used to prepare a ceramic powder through a mill homogenisation and atomisation process. The ceramic powder is then uniaxially compacted in disc shape and sintered in an oxidising atmosphere. The resulting sintered bodies are metallised on their flat faces and the cylindrical surface is passivated using lead free glass enamel. These ceramics present excellent semiconducting properties with non-linear (non-ohmic) characteristics. The DOPA process is found to be an attractive procedure to obtain ceramic powders for the preparation of SnO2 varistors.

Jan 1, 2006

By T. Iriyama, Y. Fujita, R. Omatsuzawa, T. Nishio, N. Okochi

Sm-Fe-N hard magnetic materials are good candidates for high performance bonded magnets. Rapid-quenching method should be highly favorable for the fabrication of isotropic magnet powder with high coercivity. We report here the magnetic properties of Sm-Fe-N powders produced by a few kinds of rapid-quenching processes. Sm2Fe17 powders were prepared by gas-atomization (GA), rotating-disk atomization (RDA), or melt-spinning (MS) method. The Sm2Fe17 GA powder had dendritic solidification structure, while the RDA powder had micro crystalline structure with size of 3-5 µm. Coercivities (HcI) of their nitrides were 56 (for GA) and 217 ka/m (for RDA). The H cI of nitrided Sm2Fe17 MS powder with wheel velocity (V5) of 5-20 m/s, which had also microcrystalline structure, was 53 to 509 Wm. These coercivity values are not sufficient for bonded magnet applications. From the study of additive effects, it was found that C, C-Si, C-Ga, or C-Al addition decreased the crystal size of quenched Sm2Fe17 powder. Consequently, high coercivity was obtained; the HcI of nitrided Sm2Fe1C1Si1 MS powder with V5 of 10 m/s was 898 kA/m, and 708 kA/m for the nitrided Sm2Fe15C1Si1 RDA powder. The compression-molded bonded magnet made from Sm2Fe18Si0.1Nx MS powder showed a high (BH)max of 82.7 kJ/m3.

Jan 1, 2000

By Gaifeng Xue, Lei Zhang, Aimin Duan, J. Y. Hwang, Lina Wang

"The removal of chemical oxygen demand (COD) from coking wastewater was experimentally investigated using a three-dimensional electrode reactor. The experimental results showed that the refractory organics in coking wastewater can be effectively removed by this process, and COD removal efficiency was affected by the operating parameters, such as electrolytic retention time, particle electrode dosage, initial pH, current density, aeration amount and electrical conductivity. The experimental results show that the three-dimensional electrode could have a COD removal efficiency of more than 60% and a running cost of no more than 6 YUAN (RMB)/t. This indicates the great potential of a three-dimensional electrode reactor in engineering applications as an advanced treatment methods for coking wastewater.IntroductionCoking wastewater is generated from coal coking, coal gas purification, and by-product recovery processes of coking; it is composed of phenolic compounds, heterocyclic compounds, polycyclic aromatic hydrocarbons, ammonia, cyanide, polycyclic nitrogen-containing aromatics, acyclic compounds, etc. Most of these constituents are refractory, poorly biodegradabile, toxic and carcinogenic [1-3]. Currently, coking wastewater is usually treated by different forms of A/O biological nitrogen removal processes as the primary treatment means, but the aforementioned processes are not efficient enough to meet the requirements of the National Discharge Standard in China (GB13456-1992). According to the continuous requirement on improving environmental protection for the coking industry (revised 2008), increasing wastewater utilization ratios and reducing the discharge of effluent in the coke industry have to be implemented for cleaner production and sustainable development. Therefore, advanced technologies need to be developed to treat coking wastewater and reutilize the product as industrial cooling water, which would be one of the best choices to achieve zero discharge of wastewater and reduce water consumption per ton of steel produced. In this study, a three-dimensional fluidized bed electrode reactor was adopted for the advanced treatment of coking wastewater, and the effects of operating conditions, including particle dosage, initial pH, current density, supporting electrolyte, as well as aeration amount on the COD removal rate, were investigated. Its running costs were also estimated."

Jan 1, 2012

By Walter E. McCulloch

Recent laboratory bench scale and pilot plant metallurgical tests at Mountain States R and D International have demonstrated that some copper ores because of relatively coarse copper sulfide mineralization can be preconcentrated by heavy media separation (HMS). In tests with a copper ore from the AMT Copper Creek project near San Manuel, Arizona, HMS preconcentration rejected about 75 to 80 percent of the feed as a minus 13 mm gravel. The HMS concentrates copper recoveries were about 93 to 95 percent. With the incorporation of HMS preconcentration, significant capital and operating costs savings have been projected for the proposed AMT Copper Creek concentrator. An overview of the HMS preconcentration step development for the AMT Copper Creek project is presented. Also presented are other potential applications of HMS preconcentration for copper ore processing.

Jan 1, 1999

By D. M. Hausen

Multiple drill sections through many of the numerous breccia pipes in the American Eagle copper deposit at Copper Creek, Arizona, have been evaluated by means of alteration and geochemical data. Contoured plots indicate vertically plunging, concentric, cylindrical shells of alteration and mineralized rock that are similar in structure, geometry, magnitude and petrology to the San Manuel-Kalamazoo Deposit, located about 14 miles to the southwest. Both deposits are similar in dimension and consist of multiple, irregular, rod-shaped injections of porphyry into a granodiorite host. Analogous to the San Manuel-Kalamazoo Deposit, most of the porphyry plugs are oriented parallel to the cylindrical axis of the "ore shell". A continuously mineralized, elliptical shell, inferred from deep drilling, is capped by a flatter zone of copper mineralization. Above this flat zone, copper-bearing fluids were channeled upward along conduits that correspond with quartz-sericite "breccia pipes". At depth, zones of sericite and K-feldspar alteration products exhibit conformable relationships with the copper deposition. A "bullet-shaped" ore shell, with a nearly vertical axis, is proposed to explain the conformable zones of altered and mineralized rock. The "nose" or top of the "bullet" is 1800 to 2300 feet below the surface, and structurally controlled in part by steeply dipping Hi and ENE faults. If correct, this model suggests that the vertical ore shell may extend to great depth.

Jan 1, 1988

By Sebastiaan Peelman

NdFeB permanent magnets are the best available magnets used in many technology applications. However, at their end-of-life (EoL) most of magnets and the contained REEs are lost during the recycling of the bulk metals. The REEs are classified as the most critical raw materials in the European Union, and recycling of REEs from EoL products will reduce their criticality and contribute to the sustainability of REE. Various technological routes have been reported, but most of the methods are effective for highly concentrated magnets or magnet scrap, which is greatly dependent on expensive pre-dismantling processes. This paper presents various innovative metallurgical solutions to the effective REE recovery from current industrial practice for WEEE recycling, including the ferrous scrap from WEEE shredder products and shredder residues from computer hard disk drives. Both hydrometallurgical and combined hydro- and pyrometallurgical REE recovery routes are developed after demagnetization and physical upgrading.

By Yuanbo Zhang, Zhixiong You, Zijian Su, Bingbing Liu, Guanghui Li, Guang Yang, Tao Jiang

Sodium stannate is widely used in the electroplating and tin alloy industry. But the traditional processes for sodium stannate production are characterized by long flowsheet, high production cost and strict requirement for the equipments, etc. In this study, a novel process for sodium stannate preparation from cassiterite concentrate and sodium carbonate via roasting in CO/CO2 mixed gas then followed by leaching was developed. The effects of roasting parameters on the Sn leaching efficiency were conducted. A Sn leaching efficiency of 77.2% was obtained under the optimal conditions. Sodium stannate (Na2SnO3·3H2O) with a purity of 95.8% was produced by the new process, which is better than that specified for the industrial first-grade product.

Jan 1, 2014

By Takayuki Ichikawa

Hydrogen storage properties of ballmilled mixtures composed of the hydrogenated nano-structured carbon (CnanoHx) and lithium hydride (LiH) were examined by thermal and optical spectroscopic analyses. LiH needs higher temperature than 600°C for hydrogen desorption even under vacuum condition, while CnanoHx, which was mechanochemically synthesized from graphite powder by ballmilling under hydrogen atmosphere, reveals hydrogen and hydrocarbons desorption in wide temperature range from 300 to 800°C. Nevertheless, the composite of CnanoHxand LiH prepared by ballmilling desorbs hydrogen in relatively lower temperature range from 150 to 450°C. These phenomena indicate that the thermally liberated hydrocarbon radicals immediately react with LiH and release hydrogen instead of hydrocarbons emission, because CnanoHx contains hydrocarbon groups at the edge of nano-meter sized graphenes, which are recognized as IR active C-H stretching mode, and LiH is well-known as an ionic crystal. Furthermore, it is of interest that a nanostructural feature persists in this composite even after annealing at 350°C, which shows excellent cycle properties as hydrogen storage media.

Jan 1, 2006

By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with C02 is expected to occur at as low temperature as possible. In order to get a highly reactive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of C02. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining al\ the obtained data.

Jan 1, 2003

By Mark R. Jolly, Jean-Christophe Gebelin, Aleksander Cendrowicz

"Injection of wax patterns is the first stage of the multi-stage process of investment casting. The quality of the final casting and its dimensional accuracy is highly dependent on this stage of the process. Pattern waxes used in the industry behave in a complex visco-elastic-plastic manner. The modelling of such material behaviour is therefore not simple.In this paper a number of configurations of die will be shown in which the injection of the wax has been carried out for a range of processing conditions. Some of the dies are transparent and the movements of wax front observed can be compared with those predicted by simulation. Surface defects in final components will also be shown and compared with the location predicted by simulation software. Some discussion will be presented on the limitations of the software used and the time-scales achieved for practical use as a design tool within the foundry environment. IntroductionThis paper presents the research activities carried out at the University of Birmingham on the modelling and prediction of the behaviour of industrial investment casting waxes during the injection of wax patterns. These research activities are done in the context of a more global study of the fundamental aspects of the investment casting process, the FOCAST project. Regarding the wax injection process, the aim of the project is to achieve a better understanding of the key factors that will lead to better castings. The filling of the die during the injection has been studied. Some other phenomena such as shrinkage/warpage or creep under residual stresses are also studied, but not presented here. Two commercial investment casting waxes have been characterised in order to model their behaviour and predict mould filling and subsequent defects.This paper will present the models that have been used in our work, the simulation packages used, the experiments carried out to validate the modelling and exhibit the defects due to bad filling, and finally the numerical simulation results."

Jan 1, 2001

By Cong Wang, Kexin Jiao, Yongan Zhao, Haibin Zuo, Jianliang Zhang

The carbon composite brick is a new refractory used in blast furnace hearth and bottom. It caused wide attention due to its high thermal conductivity and low erosion by molten iron. In this paper, chemical constituents, SEM-EDS and X-ray diffraction were carried out in order to understand reaction mechanisms. A series of experiments of oxidation resistance characteristics were made. The oxidation mechanisms of carbon composite bricks in the presence of air were analyzed. According to the analysis on many experimental results, the oxidation process of carbon composite bricks under different temperatures were controlled by different mechanisms. In the condition of high temperature, SiO2 as oxidation product hindered the diffusion of O2, and reduced the oxidation loss of graphite in the internal.

Jan 1, 2015

By J. Alberto Vázquez M.

A sensor employing yttria-stabilized zirconia (YSZ) was used to determine the oxygen activity of molten copper at laboratory scale at temperatures of 1200° and 1300 dc. The reference electrode was a Ni-NiO mixture. The amount of the deoxidizing agent (CU3P) ranged from I to 3% of the mass of copper. Thermodynamic analysis of the Cu-O-P liquid system was carried out to predict the required deoxidizing agent and the final composition of the molten copper. Both results, calculated and experimental, show that the oxygen removal is more efficient at lower temperatures. The kinetics of the deoxidizing reaction is very fast in the first minutes of the treatment. A metalography analysis of rapid cooled samples show the oxygen and phosphorus distribution

Jan 1, 2003

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By F. M. Wang, J. P. Lin, G. Y. Tang, H. C. Zhou, Y. F. Liang, F. Ye

"Fe-6.5%Si alloy is a very excellent soft magnetic material compared with conventional Si steel (Si content ~ 3.5%), especially in high frequencies with reduced iron losses and noises. But it is hard to be fabricated due to its brittleness at room temperature. Dynamic electropulsing is applied to the cold rolled Fe-6.5%Si sheet during tensile deformation. Mechanical and microstructural properties are investigated with different electropulsing and strain rate. It is found that the yield stress decreases and the elongation increases dramatically with the application of dynamic electropulsing. It is indicated that the work hardening could be reduced with the dynamic electropulsing during deformation, which provides a promising way to fabricate this alloy sheet much easier.Introduction Fe-6.5%Si (weight percent, same as below) alloy has more excellent soft magnetic properties compared with conventional silicon steel (Si content ~ 3.5%), such as higher resistivity, higher permeability, near zero magnetostriction, etc. and exhibits much lower core losses and noises [1]. However, Fe-6.5%Si is very brittle at room temperature and hard to be fabricated in strip by conventional hot-cold rolling process [2]. This lack of low-temperature ductility has been generally attributed to structural ordering ofB2 and D03 phases [3]. Several methods have been developed to avoid its brittleness, such as chemical vapor deposition (CVD) [4], rapid quenching [5, 6], dipping and diffusion [7, 8], direct powder rolling (DPR) [9], etc. However, hot-cold rolling method is still of interest for industrial applications. In our previous work, this alloy can be cold rolled after certain thermomechanical process and heat treatment [10-13]. The cold rolled sheet exhibits some extent of ductility [11]. However, side cracks are common for the rolled sheet, it is very necessary to improve the ductility of this alloy by other technical applications."

Jan 1, 2012

By V. L. Stolyarova

The high-temperature Knudsen effusion method was used to study partial pressures of vapour species, activities of components and the Gibbs free energies in the DyF3-Dy2O3 system at the temperature (1357±5) K. Partial pressures of vapour species were obtained by the ion current comparison method, with the DyF3 partial vapour pressure over pure DyF3 as a standard. The equilibrium constant of the gaseous reaction DyF3 + DyOF = Dy2OF4 is evaluated. Thermodynamic data obtained are in a agreement with the available phase diagram of the DyF3-Dy2O3 system. Results of the present study illustrate the negative deviations from the ideal behaviour in the system.

Jan 1, 1997

By Chang Wei, Zhigan Deng, Yizhao WANG, Cunxiong Li, Gang Fan, Xingbin Li

During the process of hematite precipitation, the transformation of Na jarosite convert into hematite has been studied in a batch reactor at different temperatures, ranging from 170°C to 200°C with 3h of the retention time in the presence of 30g/L Fe ( ) and 4g/L Na+. The composition of precipitation was seriously depended on the temperature, at 170°C hematite and sodium jarosite are the reaction products of iron precipitate, with an increasing in reaction temperature the sodium, sulfur content in precipitated decreased and sulfur mainly exist in forms of SO4 2-, and when temperature over 200°C hematite was the only phase in product. An increasing temperature was not only beneficial to iron precipitation, also conducive to jarosite conversion to form high quality hematite precipitate.

Jan 1, 2016

By Muhammad Abid, Kh. .. S. Karimov

"In this study, design and investigation of biogas digester consisting of methane tank with built-in solar collector to utilize solar energy for the heating of the slurry prepared from the dung and heat exchanger is designed, developed and tested. The digester was laboratory type and consists of cylindrical metallic tank of size of 0.5 m in diameter; 1 m in height and 200 liters in volume. The surface of the digester from outside was covered by thermo insulated material a glass wool, except of south side (in northern hemisphere). This side played the role of built-in collector and was blackened to increase absorption of solar irradiation and covered under 45o by glass. In the blackened side of the digester on the different heights it was installed metallic pipes for the inlet and outlet of the air, connected with heat exchanger installed inside of the digester. The heat exchanger was fixed in the level above of the inlet pipe. The horizontal plane reflector concentrates solar beams to blackened side of the digester. In the winter period, it was found that the retention time of this digester is shorter on 15% and produced biogas volume is larger on 20% with respect of ordinary biogas digester. This digester is used for the demonstrative purposes and as a teaching aid presently and base on the results it may be used for the construction of large volume digesters for use in the farms, especially located in the remote and mountain areas where the climate in the winter period is cold. Introduction At present many experts around the world have focused their efforts to energy crises because energy is one of the most important factors for the development of the society. It is known that consuming energy is proportional to quality or standard of life. There is a close relationship between energy consumption and the Gross National Product (GNP). It is obvious that for further development of the country additional sources of energy is required, which are cheap, safe and environmentally compatible with respect to the action on possible wastes. Utilization of renewable energy is one route to help in solving the above mentioned problems. In particular, biogas as a source of renewable energy is produced by biotechnology and used wide on residential scale [1]. The biogas was produced for the very first time in 1814 by Deivy from organic wastes. In 1900 production of biogas was started in Bombay (India) [2, 3]. Biogas consists of 55-70% methane (CH4) and around of 27-44% carbon dioxide (CO2) and less than 1% H2 and H2S. At present biogas is used widely in some countries for lighting, machines, and vehicles, generators, cooking and heating. Biogas generation is suitable for small to large scale operation and at present is realized in a number of developed and developing countries as USA, Hungary, China, India etc. Since 1990s biogas projects construction in China has developed steadily by the end of 1998, there were altogether 6.88 million household biogas digesters [4]. In Russia biogas digesters are used for processing of hard dung into biogas [5]. Over the last few years the very first biogas digesters were constructed in Tajikistan as well [6,7] and it was found that the digesters can work with sufficiently high efficiency in mountain areas as well ."

Jan 1, 2008