Al2O3,-WC Composite powder for cutting tools was synthesized by self-propagating high-temperature synthesis using A1 powder as a reducing agent. WC, W2C and Al2O3 were concurrently formed in WO3Al-C system. It was found that the complete reaction was achieved with excessive addition of carbon and appropriate processing parameters such as degree of dilution, particle size of aluminum, compaction pressures of green pellets and carbon source. The final product which was leached by 50% HN03+HF diluted solution was consisted of Al2O3-55wt% WC having 2-3um of mean particle size.

Jan 1, 1999

By K. R. Barrett

The cupellation of dore/lead bullion to recover precious metals is one of the oldest metallurgical processes known to man. In recent times this has been carried out in small reverberatory furnaces but the process suffers from a number of disadvantages. A new process has been developed at the Northfleet refinery of Britannia Refined Metals Ltd, which gives much improved performance. The process depends upon the injection of oxygen through a nitrogen shrouded lance at the bottom of the furnace. The lance is consumable and of unique design. Reaction rates are high giving short process time; fuel consumption is low; oxygen efficiency is high and dore recirculation is low. The new process has resulted in substantially lower operation costs.

Jan 1, 1989

By E. J. Peuraniemi

Primary copper production using suspension smelting techniques like Outokumpu Flash Smelting always causes some dust formation. Flue dust particles are formed when sulphide feed material reacts violently with oxygen inducing particle disintegration and total desulphurisation of fragments. In the process, flue dust follows the off-gases to the heat recovery boiler (HRB) where its sulphation takes place because of prevailing conditions. Sulphation releases heat and causes also a drop in particle melting temperature and, further, particle sticking to the walls and heat exchange tube banks. Sulphation of synthetic CU20 particles were examined using a laboratory scale fluid-bed reactor. This study aims to a better understanding of flue dust behaviour in a HRB and, thus, to a better operational practise and design of a HRB. The effect of PSO/PO2 -ratio and temperature on the sulphation kinetics were tested. Standard chemical analysis, light optical and scanning electron microscopy with energy dispersive spectroscopy were used to examine the samples.

Jan 1, 2001

By Bradley C. Bockrath

Some thirty coals were evaluated for liquefaction activity under a mixture of CO and H2 at 425° C. The viscosity of the liquid products was taken as an indicator of the degree of liquefaction. It was found that the direct liquefaction of a particular coal may be beneficially influenced by the presence of pyrite. Active pyrites are often found in the native mineral matter of the coal itself. For example, subbituminous and bituminous coals and lignites of relatively high pyrite content were found to liquefy more readily than similar coals or lignites which were poor in pyrite. The reactivity of inactive coals could be improved by using blends with active, pyrite-rich coals. In addition, pyrite was effective when added separately as pyrite concentrates obtained from coal beneficiation operations. Various other iron- and sulfur-bearing additives were also effective when used in combination as added slurry-phase catalysts, including iron oxides and mineral residues derived from liquefaction of active coals. Under liquefaction conditions, pyrrhotite ( Fe I- x5) is formed from pyrite or from the iron oxides and many sulfur containing species. Pyrrhotite was shown to be a hydrogenation/dehydrogenation catalyst for tetralin but is not active for initiating a variety of free radical reactions that do occur when pyrite is heated with tetralin. The role of pyrite in coal liquefaction is complex and still not well understood.

Jan 1, 1981

By Xinhua Wang, Xuefeng Liu, Die Yang, Lifeng Zhang, Wen Yang

"CSP thin slab continuous casters are well used in recent years. The control of heat transfer in the mold is very important because it is correlated with several slab defects. The mean heat flux of CSP mold was studied based on the plant production data of LCAK steel and weathering steel. The effect of various operation conditions on the heat flux was analyzed and discussed. The results showed that the heat flux was 2.1-2.6 MW/m2 on the wide face and 1.2-2.2 MW/m2 on the narrow face for the casting of LCAK steels. During the casting of weathering steel, the heat flus was mostly 2.05-2.5 MW/m2 on the wide face and was 1.1-1.8 MW/m2 on the narrow face. The heat flux depended largely on the casting speed. The heat flux on the wide face increased obviously with increasing casting speed when the casting speed was relatively low; however, at high speed, the heat flux increased slowly or kept constant. At low casting speed, the heat flux depended little on the superheat of the molten steel. The mean heat flux depended little on the level fluctuation at continuous casting mold.IntroductionCSP thin slab continuous casters are used more frequently in recent years for its low cost of construction and manufacturing. The structure of CSP mold is very different from that of conventional thick slab casting mold, inducing the difference of heat flux between them. There have been some studies about the heat flux of thick and medium slab casters [l, 2]. Heat transfer in the mold is very important for the solidification of molten steel because it is correlated with several slab defects such as slab break-out, longitudinal crack, and surface depression. Moreover, higher casting speed is desired to improve the productivity. The control of solidified shell is extremely important. The heat flux is largely influenced by several casting parameters such as the cooling intensity of the mold, the casting speed[3], the mold flux powder [3, 4] and the carbon content of steel as well [5]. The investigation on the heat flux and affecting parameters can help to understand the solidification of molten steel in the mold."

Jan 1, 2013

By P. D. Lee

The effect of strontium on porosity formation in aluminum-silicon alloys is not well understood and there is no consensus upon the cause of the effects observed. This paper describes a series of experiments where the effect of adding strontium on pore formation was observed directly with combination of a traditional temperature gradient stage and real time micro-focus radiography. These in situ observations provide a new insight into the effect of strontium on the nucleation and growth kinetics of porosity. The addition of strontium was found to have a minor effect on the growth of the pores in the mushy zone. However, strontium appeared to alter the nucleation and stability of hydrogen bubbles within the melt. The interaction of strontium with titanium-boride grain refiners produced an even stronger change in the nucleation and stability of the bubbles formed.

Jan 1, 2002

By Tomoya Nihei, Hiroshi Hayashi

"A novel selenium removal process called Recycled Green rust/Ferrite Process is developed by MMC. In this process, a mixed Fe2+-Fe3+ hydroxide compound, green rust (GR), reduces selenate to elemental selenium, while GR is consequently oxidized to magnetite Fe3O4. Sequencing batch-mode experiment showed that the residual selenium concentration gradually decreased with the number of batch test increased. Stable selenium removal was achieved when the number of batch test exceed 15 times. Optimum selenium removal ratio reached 99.95% where initial Se concentration 2.1mg/L decreased to 0.001mg/L. Furthermore, the continuous feeding test carried out through a pilot-scale plant with a feeding capacity 600 L/hr. Approximately 860-hour-feeding test was carried out for the selenium-contaminated groundwater which had an averaged selenium concentration of 0.88 mg/L. Selenium concentration in the effluent from thickener maintained less than 0.01 mg/L (selenium removal rate of 99%) until a net operating time reached 800 hours.IntroductionJapan is one of the largest producers of selenium, and thus there are potential environmental impacts of selenium on soil and aquatic environments. The Mitsubishi Material Corporation (MMC) owns some real estate properties whose soil and groundwater was polluted by selenium and other heavy metals. These sites include former industrial plants: a smelter for nonferrous metal and a fabricating semiconductors and pigments. Selenium in aquatic environment commonly exists in four oxidation states, namely, VI, IV, 0 and -II. Selenate ion (SeO4 2-), the most oxidized form of selenium, and selenite ion (SeO3 2-) are highly soluble and mobile. Elemental selenium (Se0) is insoluble in water and therefore has much lower toxicity. Because selenium is carcinogenic and teratogenic at high concentration, the national effluent standard in Japan is fixed at 0.1 mg/L and the environmental standard at 0.01 mg/L. Although there are several selenium removal techniques, the most conventional process is coprecipitation with a ferric hydroxide because of its simplicity and low cost. It is known that selenite is adsorbed strongly on the surface of ferric hydroxide, but selenate is not. The low affinity of selenate on oxide mineral surfaces was demonstrated by the fact that selenate could be easily displaced by adding competing anions, particularly sulfate ion. Selenate removal from polluted water is one of the most difficult techniques, and more effective methods are desired. MMC developed a novel selenium removal process [1]. In this process, the concentrated slurry that contains Fe(II)-Fe(III) hydroxyl-salts known as Green Rusts (GRs) contributes to selenate removal. The main components of the iron precipitate in the reactor are GRs and their oxidation product, magnetite (Fe3O4)."

Jan 1, 2008

By Duan Xin-hui, Wang Xin, Peng Jin-hui, C. Srinivasakannan, Zhang Li-bo

The work attempts to optimize the process of preparation of modified semi-coke from semi-coke using phosphoric acid (H3P04) as the activating agent using the response surface methodology (RSM). The influences of three major dependent variables, the impregnation ratio, activation time, and activation temperature were assessed on the independent variables yield and the iodine number. The empirical relationship between the dependent and the independent variables were established using the quadratic response surface models, which were utilized to optimize the process parameters. The significance of each of the parameters and interaction among the parameters on the independent variable was assessed based on analysis of variance (ANOVA). The process variables were varied within the range of impregnation ratio (IR) from 1.5 to 4, activation time from 30 to 90 min and activation temperature from 550 'C to 650 'C. The optimized process conditions were estimated to be an IR of 2.29, activation time of 32 min, and an activation temperature of 605°C respectively using the process optimization tool. The BET surface area of modified semi-coke of the optimized sample was estimated to be 915m2/g, with the pore volume of0.71cm3/g, with an average pore diameter of 3.09 nm, with micropore volume fraction being 52.36%. The scanning electron microscope (SEM) images were utilized to visualize the surface pore structure.

Jan 1, 2013

By Milton Manrique

The thermal decomposition of zircon concentrates in a non-transferred arc thermal plasma flow reactor was investigated. The plasma torch was operated using argon-helium and argon-nitrogen mixtures as plasma gases. The effect of power, feed rate and zircon particle size was studied. Products were characterized by XRD, SEM, TEM and chemical analytical techniques. The average size of the product was in the submicron range. Free energy minimization plots were used to predict the behavior of the system under different operating conditions. A kinetic model to describe the different stages of the thermal decomposition process is proposed. The results of this investigation showed a significant segregation process where the zirconia-rich product is collected in the reactor while the silica-rich product is collected in the filter. TEM analysis indicated that silica vapor is condensed on the surface of the zirconia particles.

Jan 1, 1996

By A. Mezei

Samples of cobalt and bismuth concentrates produced from the NICO deposit in Northwest Territories were subjected to a comprehensive metallurgical testwork consisting of: pressure oxidation, ferric chloride leach and carbon in leach, to recover the cobalt, bismuth and gold, respectively. A specific testwork program was designed to allow for the optimization of process parameters under multiple restrictive criteria. The overall objective was to establish leaching sequences that could produce acceptable recoveries while generating environmentally disposable residues as well as solutions suitable for further processing. The recoveries for the leaching stage, under the optimum conditions, were 97% for cobalt and 95% for gold, in the case of the cobalt concentrate. The bismuth concentrate produced recoveries of 99% for bismuth, 99% for cobalt and 97% for gold, respectively

Jan 1, 1999

By Hans von Michaelis

There has been a renaissance in gold and silver extraction and recovery that has taken place over the last fifteen years, since the price of gold was freed from the $3510~ level. Despite major advances in such areas as carbon adsorption processes for gold recovery, refractory gold ore treatment, crushing and grinding, process control, etc., there still remain several gold and silver mineral processing frontiers. Frontiers related to environmental management present significant challenges especially in the USA. More than ever it is appropriate to optimize total economics by adopting a "systems approach" that integrates mining, mineral processing and environmental management.

Jan 1, 1993

By Lary L. Speakman

Typical heavy metal removal system generate a great deal of waste that must then be discharged somewhere. Using Bio-Fix Beads developed by the Bureau of Mines in combination with other waste stream minimization processes, Harrison Western Environmental Services has developed a "zero" discharge operation. Data from current on-site operations will demonstrate the effectiveness of the Harrison Western approach. For 1992 Annual TMS meeting,: "Future Trends and Innovations" Material category Key words: Residues and Effluents Technical category Key words: Extraction and Processing.

Jan 1, 1992

By Kazuyo Yokoyama

New environmental assessment model based on the Waste Input-Output analysis has been developed and applied for the "Landfill mining activity". "Landfill mining" implies the digging up of the landfilled wastes, the recovery of valuable material and energy resources and, thus, the reuse of the saved space as a new landfill site. In this study, the landfilled wastes are assumed to be treated by the gasification/melting processes. Two kinds of reactors, the fluidized bed type (FB) and the shaft furnace type (SF), have been considered in this work as the typical gasification/melting processes adopted in Japan. In FB, the dug-up wastes are heated in the sand fluidized bed zone under reducing atmosphere, Fe and Al are recovered in the metallic form, and then, the gasification/melting of residues is made in the second zone. In SF, the waste is charged in the high temperature coke bed, and the gas is recovered together with molten metal and slag. Both processes generate electric power by the recovered heat and fly ash as waste to landfill. It has been found in this study that the both processes can reduce the total volume of waste and save the available landfill space. SF seems to have higher potential for decreasing volume of wastes because of less emission than FB while FB has great benefit to recover metallic Fe and Al individually. The results of scenario analysis have also indicated that the landfill mining activity is effective for sustainable management of landfill sites.

Jan 1, 2006

By Fumito Tanaka

The Converting Furnace (C-furnace) of the Mitsubishi process has solely provided opportunities for producing blister copper continuously from molten matte. Continuous converting originates from the proven technology for controlling the behavior of magnetite in lime-ferrite slag of the CaO-FeOX-Cu2O system. Recent improvements in the C-furnace operation have included the slag controls reflecting the impact of minor oxides on magnetite behavior. Although previous investigations focused on magnetite behavior, sulfur has also affected the C-furnace operation because it is of practical importance to avoid the precipitation of gypsum from lime-ferrite slag and the separation of matte from blister copper. This paper will quantify the behavior of sulfur in C-furnace with respect to the gypsum formation and matte separation, and discuss better controls for C-furnace operation.

Jan 1, 2006

By Isrun Bohlinger

Resources recovery of brasses for semifinished products often results in the formation of hard spots impairing the quality of following abrasive and/or surface finishing processes. A short survey is given on the recycling processes, followed by the actual knowlegde of genesis, composition, and possibilities of avoidance of hard spots. Informations on genesis and composition of hard spots are completed by data from recent experiments.

Jan 1, 1998

By Mingchun Lu, Yunjin Yan

"This paper describes a new type of bell-less top installed on two relined blast furnaces at Tianjin Iron Works and another new-built at Echeng Steel Works in China. A compact installation was presented for existing furnace top innovation with the least reformation of existing top structure. A water cooling and sealing gearbox used for driving the chute discards completely the traditional idea about necessity of continuous supply of cooling gas for the gearbox. A multiring spreader and its dozens of selectable charging patterns enables an operator to achieve optimal burden distribution easily under the condition of a minimum investment of control equipment. Some useful conclusions have been made through a small-size model and a full-scale model tests. The excellent characteristics and the superiority of the new top have been fully proved at both works.IntroductionIt is known that there are some advantages with the bell-less top of a blast furnace: suitable for furnace to operate at high top pressure, capable of realizing optimal burden distribution, less investment and maintenance costs, etc. But why do most of blast furnaces in the world still remain using conventional bell top. One of the concerns is that current bell-less tops still have some shortcomings:1) The height of a current bell-less top might be lower than three or four-bell top or two-bell plus valve seal top, but still much higher than an ordinary two-bell top.2) The gearbox for driving the rotating chute is positioned onto the lip of the furnace. It is subject to attack by crude hot bf gas. Continuously pumping cooling gas (pressurized nitrogen or clean bf gas) into the gearbox is indispensable to withstand such a harsh working environment. Therefore, a plant furnished with blower8 and its ancillaries has to be built, It involves a large sum of investment and much expense in its annual running costs.3) Although the current bell-less charging device as a means of controlling burden distribution possesses a wide range of freedom, it is difficult to realize optimal burden distribution. There are some large blast furnaces realized better burden distribution, but sophisticated control means is indispensable so that the investment of control means is much higher."

Jan 1, 2000

By Jorge Alberto Soares Tenório

Household zinc based batteries contain some heavy metals such as zinc, manganese and mercury. There is a large effort from manufacturers in order to eliminate the last one. As a municipal waste, the disposal of batteries has become an increasing worry. The aim of the present work was to characterize dry batteries scraps, and establish a flowsheet for their processing. This was done using unit operations of mineral processing and parameters and yields of each stage have been defined. Such procedures have been chosen due to their low cost. The operations were hammer mill grinding, size separation, magnetic separation and specific weight separation in water. The characterization step was done through chemical analysis and x-ray difiactometry. After size classification, it was verified that 76.6% of the total amount of zinc was over 1.70mm. This fiaction was constituted basically of zinc and some coarse pieces from the steel body, paper and plastics. This fraction was submitted to magnetic separation followed by specific weight separation in water. A visual examination showed that during the grinding process, graphite was concentrated in the finer fractions. Manganese concentration in the fractions over 6,35mm was less than 2%. This means that there was low contamination by the paste in this fraction. It was due to the entrapment of the paste by steel scraps (from the body) and zinc (from the cup) during grinding.

Jan 1, 1999

By F. Patisson

During exothermic gas-solid reactions, heat generation makes temperature rise and modifies the rate of the various mass transfer processes, namely the chemical reaction itself, the pore diffusion and the external transfer. We have investigated this thermal effect during the oxidation of zinc sulfide porous pellets in a thermo balance furnace, between 550 and 900°C-and under O2-N2 atmosphere. The results have been' analyzed by using, firstly, the law of additive reaction times derived from the isothermal Grainy Pellet Model, and, secondly, a new numerical model taking into account non-isothermal conditions. Both the models can satisfactorily simulate conversion versus time, but the numerical model also depicts the temperature evolution within the pellet. Finally it is shown that owing to the heat generation the zinc sulfide oxidation takes place under diffusion control (3/4 internal, 114 external) in all the cases studied. During the course of reaction, the. pellet undergoes strong temperature variations, with thermal gradients confined to a shell oxide layer.

Jan 1, 1996

By Mark Jolly

"Over the last ten years or so many man hours have been dedicated to developing methods for simulating shape casting processes. The majority of the methods developed have been devised by a combination of computer, mathematics and materials specialists often with limited knowledge of foundries and foundrymen. As a result of this it would appear that although there are many software packages for the foundryman to use there still exist fundamental misunderstandings as to their usefulness and suitability within the foundry.The paper aims to identify how well current software packages perform. The relationships between physical phenomena, practical defects and software capabilities are presented. Some discussion of the use of criteria functions is also presented. Finally issues arising from the postprocessing of results are discussed as the presentation of the results to the lay-person in simulation techniques is possibly one of the most important aspects in influencing the adoption of this type of software in the foundry community."

Jan 1, 1999

By K. V. Sreenivas Rao

Solidification experiments have been conducted to study the effect of interface heat flux and air gap formation on cooling rate of the casting during solidification of Al-4.5wt%Cu alloy. The thermal history of the casting and mold during solidification is recorded using thermocouples connected to computer interfaced data logger. The measured temperatures in the mold are used as input to the IHCP (inverse heat conduction problem) algorithm for simulating multiple heat flux components at the boundary. It is observed that the filling effects induce spatial variation in the thermal field in the mold and casting regions and greatly influence the cooling rate of the casting. The study demonstrates the use of IHCP and in-situ measured thermal profile in analyzing the cooling rate and microstructure.

Jan 1, 2008