By Joseph A. Sutton

This study was undertaken by the Bureau of Mines to determine whether the sulfur-oxidizing bacterium Thiobacillus thiooxidans could use sulfur compounds to produce sulfuric acid in sufficient quantities to leach valuable metals from low-grade ores. The results of extended tests indicated that the bacterium is capable of extracting appreciable amounts of copper and cobalt from ore and mineral samples when sulfur is available in a state that can be readily assimilated by the organisms. Under the conditions of these tests, this organism was not able to assimilate and oxidize the sulfur as it occurred in the ores and minerals. Ores containing copper minerals in the silicate, carbonate, and oxide forms, in the presence of elemental sulfur, were more susceptible to bacterial action than ores containing copper minerals in the sulfide form. Thiobacillus thiooxidans remained active on elemental sulfur in the presence of some of the ores which were tested, but could not tolerate others. Therefore, strains of the bacterium were progressively adjusted to increasing concentrations (0.5 to 10 grams) of the individual ores until they could remain active on 10-gram portions of all ores being tested.

Jan 1, 1961

By Carl Fisher

A microseismic roof fall warning system was field tested in Western and Eastern coal mines in the United States to better define the capabilities and limitations of the microseismic method in predicting roof fall Microseismic event and energy type data were obtained and documented for twenty-three coal mine roof falls. Field test results indicate that both the microseismic event and energy methods, as applied in this development effort, have a high probability for successful application in a commercially practical roof fall warning system. Based on the results and experience obtained during field testing, a commercial prototype microseismic roof fall warning system was designed and constructed. Although it was the intent of the program to field test the commercial prototype system, delays in equipment fabrication and contract time limitations did not permit field testing.

Jan 1, 1980

By C. W. Van Noy

The procedure suggested in this report is intended for the use of engineers, esters, accountants, etc., in estimating the cost of chemical-type operations. It is intended to over operating costs, not investment costs, as the latter have been covered numerous other publications. However, as capital investment costs are reflected to a high degree in operating costs, it is important to point out that accuracy of investment costs is highly essential. Therefore, all factors that might be included under plant -capital costs should be considered, such as requirements of shops, employees' housing, etc. The procedure is designed primarily for use in types of chemical oper¬ations, such as the production of synthetic liquid fuels, anhydrous ammonia, and others of like or similar nature. Yet, no attempt has been made to cover the entire chemical industry.

Jan 1, 1949

By Robert C. Dyni

This U.S. Bureau of Mines (USBM) report summarizes a field demonstration of pneumatic backfilling technologies conducted at the abandoned Hillside Coal and Iron Slope in Vandling, P A. Researchers demonstrated two pneumatic backfilling technologies recently developed under the USBM's Abandoned Mine Reclamation Research Program, the Pneumatic Pipefeeder and the High-Efficiency Ejector. Both systems had previously been evaluated at the USBM's subsidence abatement investigation laboratory near Fairchance, P A. The objective of the demonstration was to fill 100% of the abandoned tunnel with backfill stone to prevent further subsidence. The Pneumatic Pipefeeder was used for 21 days, at a rate of 63 to 124 t/ d (69 to 136 st/d), to fill 88% of the tunnel. The High-Efficiency Ejector was used for 2 days, at a rate of 125 to 132 t/d (138 to 146 st/d) to fill the remaining 12% of the tunnel. The backfill placed by both systems was tightly compacted. The major problem encountered was wear on the polyethylene pipeline from the abrasion of the high-velocity backfill. The use of heavier steel pipe minimized the problem. A cost analysis for the entire project is given.

Jan 1, 2010

By S. B. Christy

This report on the electrodeposition of gold and silver from cyanide solutions represents work that has occupied my time at intervals during the past 20 years. The investigation has been carried on simultaneously with my duties as professor of mining and metallurgy of the University of California. During shis long investigation I have been assisted in the details of the work by, a number of my former students, acting in turn as assistants. Particular mention in this connection is due W. H. Hilton, who graduated in 1900; C. T. Dozier, 1902; N. C. Stines, 1905; H. N. Herrick, 1907, and L. C. Uren, 1911. It is impossible to publish full details of the many thousands of experiments performed. Effort has been made to present only the essential data. Wherever possible, the results of the experiments have been expressed in diagrammatic form by curves showing the relation between the simultaneous variables of the experiments. It is necessary to show, as nearly as may be, the state of the art. This is difficult because of the meager literature on electrodeposition in the cyanide process; hence resort must be had to the specifications and claims of patents, most of which seem never to have been applied on a working scale. Such information consequently can not be taken at its face value. Expressing the essential ideas evolved in such specifications is no easy task. Clearly, in quoting from patent records it is not ·feasible to enumerate all of the specifications or the claims allowed the inventors. A statement of the chief contributions to the art in the patent cited must suffice. Legal details, of course, must be obtained from the original patent. In the study of patent literature, when one compares the ardent hopes of the inventors with the results realized from their efforts, it becomes clear that in the development of an art no one man contributes everything. Each subsequent inventor stands on the shoulders of the one who has gone before. It is only through the summation of the contributions of many inventors that the art as a whole prospers. On October 19, 1887, a British patent was granted to McArthur and Forrest for the use of dilute cyanide solutions for treating gold and silver ores. The rapid extension of this process, in various forms, all over the world, has almost revolutionized the treatment of ores containing precious metals. It is a remarkable fact, however, that long before this patent was granted there was issued, on February 5, 1867, to J. H. Rae, U. S. patent 61866, for an electrocyanide process. Thus a method of electrodeposition from cyanide solutions used for treating ores was invented 20 years before the McArthur and Forrest patent .was granted, although the process did not come into general use. On May 24, 1889, U. S. patent 403202 was granted to McArthur and Forrest for the use of zinc shavings for removing gold and silver from cyanide solutions. The use of finely divided zinc is still the standard method for recovering 'gold and silver from cyanide solutions. Since this patent was granted, many attempts have been made to replace the precipitation upon the zinc by methods of electrodeposition. It is the purpose of this report to give an outline of some of these methods, as well as to show the relative advantages and disadvantages of the zinc and the electrical methods of recovering gold and silver from cyanide solutions.

Jan 1, 1919

By John W. Sweeney

Shales and clays from Illinois were sampled, tested, and evaluated to determine feasibility of producing lightweight aggregate by rotary-kiln methods. Sampling procedures and the 1 ,,,y of the Pennsylvanian shale units are discussed. Chemical, X-ray spectrographic and X-ray petrographic analyses were run on the samples to determine if a correlation existed between chemical mineralogic composition and expansion. Preliminary expansion testing was conducted in a muffle furnace. Rotary-kiln tests were conducted in a 16- inch by 14-foot rotary kiln. The weight of the aggregate ranged from 27 to 59 pounds per cubic foot. Concrete cubes employing the aggregate were tested to determine the qualities of the concrete. Compressive strength of the concrete using the 7-bag of cement cement per cubic yard mix, after autoclave curing for 6 hours, ranged from 2,950 to 6,750 psi. No correlation was found between the chemical, X-ray spectrographic, and X-ray and petrographic analyses and expansion, Sixteen samples made suitable lightweight aggregates in the laboratory rotary kiln. The expansion temperature range of eight of the samples was extremely narrow, and difficulties would probably be encountered in processing these materials commercially.

Jan 1, 1965

By Wilbert J. Huff

For the past 9 years , the technical studies conducted by the Explosives Division of this Bureau have been summarized in a series of reports issued annually . The following account presents investigations undertaken from July 1 , 1943 , to June 30 , 1944. The work is detailed under a number of main headings corresponding to the organizational structure of the Division , the various activities being under the immediate direction of unit chiefs , who report directly to the author . Specific credit , however , is due to the individual unit leader and his assistants .

Jan 1, 1945

By R. L. Marovelli

ANTICIPATING the eventual use of the huge tonnages of nonmagnetic taconites of the Mesabi range of the United States, the Federal Bureau of Mines is classifying and evaluating these deposits in detail. This introductory report describes work begun in 1954 as part of a long-range program to sample, classify, and evaluate important occurrences of nonmagnetic taconite on the Mesabi, range. Included in this report are brief discussions of the geology, history, and potential of the Mesabi range district and mining industry, together with a more detailed presentation of the sampling and metallurgical evaluation of these nonmagnetic taconite deposits. A total of 898 field samples was collected. Most of these were taken in the region between Grand Rapids and Chisholm, Minn., but a few came from the area between Chisholm and Buhl, Minn. Of the total samples, 865 were from open pit bank faces where the greater vertical distances presented by the cherty members facilitated the taking of a large number of samples. Conversely, the narrow face presented by the slaty members confined and limited the areas from which samples were taken. In addition, 33 of the field samples were taken from rock dumps in order to determine, in a preliminary way, the characteristics of these materials.

Jan 1, 1961

By Paul Hatmaker

Lime was a highly useful commodity thousands of years before the simple chemistry of its manufacturing process was known. The employment of lime for agriculture, building, and even certain essentially chemical purposes is so old that its origin is among the unrecorded details of man's first ventures into the manufacture and use of prepared substances. Lime is a most versatile material and consequently has come to be widely utilized in modern civilization. Immediately before the depression of the early 1930's the annual production of lime in the United States was more than 4 million tons, valued at 33 to 42 mil-million dollars. This output was sold to many industries, so many that mere enumeration becomes tedious.

Jan 1, 1934

By Todd M. Ruff

Researchers at the National Institute for Occupational Safety and Health are investigating technologies that could be used to detect objects, small vehicles, and pedestrian workers that may be in the blind areas of haulage equipment used in mining and construction. A detection system that warns the equipment operator that there is an obstacle nearby could prevent collisions and save many lives each year. One popular technology for collision warning systems is radar. Several different types of radar have been tested in the laboratory and on mining equipment. Early in the study, questions arose concerning the best way to test radar systems. Many factors affect the performance of radar, including the size, shape, and composition of the object that is to be detected; the height of the radar antenna(s); and the relative motion of the radar system and/or object. This report discusses several different test procedures and test targets and recommends methods to determine how effective a radar system will be in detecting a person near heavy equipment.

Jan 1, 2002

By Fei-chiu Huang

The principle of time domain reflectometry (TDR) is being used by the U.S. Bureau of Mines to monitor strata displacements induced by mining. The Northwestern University TDR Signature Analysis (NVTSA) Program was developed under contract with the Bureau to allow for visual comparison of three TDR waveforms quickly and easily. This program is interactive, and on-line help is available. The Northwestern University Remote Control TDR Data Acquisition System and Modification of Tektronix SP232 Host Application Program (NUMOD) was then developed to allow acquisition of TDR wave-forms from a remote cable tester via modem. The NUMOD system utilizes commercially available software while the NUTSA program is available from the Bureau. This report begins with a discussion of TDR principles followed by a description of the NUMOD system. An interactive example of signature analysis is then used to demonstrate features of the NUTSA program.

Jan 1, 1993

By Donlad B. Lindsay

This report describes a field-test program to determine the effectiveness of a polymeric wall sealant to reduce the excape of naturally occurring radio-active gas radon from the walls of an underground uranium mine into the ventilation air. A 75-foot-long, dead-end drift with a surface area of about 6,000 ft2 was used as the test site in which the average natural radon flux from the normally dry rock was 16 fCi/cm2-s. The effect on radon emanation of wetting the walls with water to a depth of 3 inches was tested, after which the rock was completely covered with a coating of dry-mix concrete to provide a base for the sealant, an acrylic latex. Sealant was applied in two coats to about 0.25 mm thick. An overall reduction of average radon flux of about 75 pct was achieved. Radon production and other environmental values were measured continuously and automatically by a Bureau of Mines data acquisition system. A commercial microcomputer was programed to convert raw data to engineering units and to perform other useful operations while recording all data on magnetic diskettes. Direct measurements of radon flux from the rock surface were made by a charcoal adsorption technique.

Jan 1, 1981

By J. P. Capp

This experiment, one of a series on underground gasification of coal, was an investigation by the Federal Bureau of Mines of hydraulic fracturing as a means of increasing the air acceptance of a coalbed to permit introducing combustion air and removing product gases. Specific objectives of the investigation included: (1) Fracturing a coalbed; (2) determining the distance the coal was physically affected; (3) ascertaining the effect of the fracture on air acceptance of the coalbed; and (4) gasifying the coal. The coal was fractured with a fluid consisting of 15,000 lb. of sand mixed with 10,000 gal. of fuel oil and 5,000 gal. of kerosine, injected at pressures up to 900 p.s.i.g. and rates up to 425 g.p.m. The oil served as the fracturing medium, and the sand as a propping agent to hold the fracture open. From the fracture point, (the place in the bed where the fluid was injected), the fracture extended 200 ft. or more along the face cleats, somewhat less along the butt. cleats, and was confined to the coalbed. At the fracture point, the bed accepted about 500 std. c.f.m. of air, which was an etghtyfold increase. Fracture effects were extensive, as airflow was noted from old mine workings and outcrops 600 to 800 ft. from the fracture point. It is probable the actual fracture was much less than 600 ft. and that normal coalbed permeability beyond the fracture limits was responsible for this flow. This indicated that effects of the fracture extended beyond the area of coal physically affected. Although no attempt was made to gasify coal more than 200 ft. away, these effects plus the natural permeability of the bed likely would permit combustion beyond the outer limit of the fracture. As these experiments continued for more than 2 years, and greater air acceptance due to the fracture was observed at the beginning of each test, it is apparent that the effects of the fracturing persist for a considerable time.

Jan 1, 1960

By Hugh D. Pallister

Alabama probably has the most extensive deposits of high-grade flake graphite in the United States and was the largest producer during World War I. Therefore, with the outbreak of World War II, users of flake graphite turned again to Alabama to supply their requirements. Flake graphite is the most important ingredient contained in graphite crucibles used in melting crucible steel and special alloys essential for war purposes. Early in World War II the Army and Navy placed flake graphite on the list of critical war materials. During World War I, when the supply of Ceylon graphite (then in demand) was cut off, large quantities of flake graphite were produced in Alabama, and about 40 mills were built. Most of these were abandoned after the war when imports of the cheaper Madagascar flake (which gradually replaced Ceylon graphite) began to reach this country. With the beginning of World War II, the Madagascar supply was cut off', and consumers were again compelled to look to domestic sources for their supplies. They found only one small mill in operation, that of the Ceylon Graphite Co. in Coosa County, Ala. The Bureau of Mines made a preliminary examination of the Alabama flake graphite deposits in 1940. Samples were taken and tested at the Southern Experiment Station at Tuscaloosa.

Jan 1, 1948

By L. Ozdemir

An investigation was made to determine the mechanical properties of oil shale at elevated temperatures and confining pressures, the thermal properties at elevated temperatures, and to provide mathematical models for mine design for in situ oil shale retorting. A review of current activity in in situ retorting is included with a comprehensive list of references. Tests were run at temperatures from 20°C to 500°C and confining pressures to 1500 psi with shale of 10 to 30 gallons per ton. A major loss of strength occured in heating 140°C with a partial regain from 380°C to 500°C. Higher grade shale had lower compressive strength. Elastic properties showed large variations. Brazilian tensile strength showed a similar temperature sensitivity as the compressive strength. Equations were developed for each property in terms of grade, temperature and pressure. Thermal, electrical and acoustical properties showed anomalies through the temperature range. Creep is a major factor in overall deformation of heated shale. Oil shale was found to be an excellent insulator. Loss of pillar support area at 800 hours of heating would be about 10 percent. Good correlation was found between a finite element model using the developed properties and an in situ heater test.

Jan 1, 1981

By Alan A. Campoli

The U.S. Bureau of Mines conducted research to characterize longwall gob loading under bump-prone geologic conditions. Bureau-designed stress meters were installed in the floor rock beneath two longwall panels and coal pillars in the gate road between them. Gob and gate road pillar stress was monitored continuously by a state-of-the-art data acquisition system. The timing of the final destruction of the abutment pillar's load-bearing core was optimal, since the pillar is located between two gob areas and no longer of significant importance for ground control. Maximum stress was observed immediately in front of the longwall face, and this pressure quickly dropped as the face moved past the instruments. The center of the longwall panels regained significant overburden load, while the instruments located less than 100 ft from the edge of the panel showed little or no increase in pressure due to gob reloading.

Jan 1, 2010

By D. Harrington

When the word "gas"' is mentioned in connection with mining almost invariably it is inferred that the explosive gas, methane, is in mind and that the reference is to coal mining. Although methane is likely to occur in any coal mine the metal mines of the world contain by far a greater variety of gases than do the coal mines. Often the gases in metal mines are as dangerous as the gases likely to be found in coal mines, and sometimes are even more deadly. A coal mine is more likely to contain methane than a metal mine. In rare instances it may contain high percentages of nitrogen or carbon dioxide or it may be deficient in oxygen where the air is confined in a blind end or in a sealed region. Much more rarely relatively small percentages of ethane or other hydrocarbons with an odor of ether, gasoline, or kerosene, or minute percentages of hydrogen sulphide are found in a coal mine. During a coal-mine fire or explosion carbon monoxide content is likely to be high (4 per cent or more), and if the coal contains much sulphur the high fumes may contain some sulphur dioxide.

Jan 1, 1931

By M. K. Quinn, A. W. Khair

"This paper presents an analysis of respiraple dust generation due to the action of a continuous miner. Underground coal cutting by a drum-type continuous miner was simulated in the laboratory using a specially designed unique automated rotary coal cutting simulator (ARCCS). An analysis of -400 mesh particles was done on gravity collected material. Samples of entrained dust were collected through the use of cascade impactors. Both samples were analyzed for size distribution and particle shape. Using the simulated coal cutter permitted variation of operating and in-situ parameters to provide information on the effects on generation of -400 mesh particles. In these tests coal blocks with an approximate dimension of 18 in. x 15 in. x 6 in. (45.7 cm x 38.1 cm x 15.2 cm) were first subjected to confining pressures, equivalent to in-situ conditions. Such blocks were then cut by the cutting head of the ARCCS, thus simulating the action of the continuous miner in underground coal mining. During the tests under a particular set of in-situ and operating parameters a number of other parameters such as 1) penetration of bit into coal, 2) penetration resistance (thrust and cutting pressures), 3) rotating velocity of cutting head, and 4) acoustic emission activity in the coal block were monitored. After each cutting cycle the fractured surfaces were photo¬graphed and a velocity survey was conducted by using a sonic technique. At the end of each experiment the cutting paths of the bits in coal were photographed using an optical microscope with an attached camera.IntroductionThe continuous-mining machines introduced in the 1950's now account for more than half the production of coal from underground mines. Unfortunately, these continuous miners, designed for increased productivity, have also increased the concentration of respirable dust in mines. As a result, the Federal Coal sine Health and Safety Act of 1969 was enacted to enforce on the coal operators that the airborne respirable dust not exceed 2 mg/m3, and was intended to reduce the incidence of coal workers pneumo-coniosis. This plus the other aspects of the legislation and the subsequent monitoring and enforcement by MSHA made it very imperative that the coal operators provide a relatively healthier and safer working environment for the coal miners. Since 1970, the Federal government has paid over 11.7 billion dollars to more than 470,000 miners with coal workers pneumoconiosis and their survivors (Newmeyer, 1981). These regulations, coupled with the assessment of the continuing burden on miners, the mining industry and taxpayers appear to have provided an impetus for the mining community towards comprehending the different parameters that influence dust generation and entrainment."

Jun 1, 1988

By James L. Elder

Field-scale experiments were conducted at Gorgas, Ala., from 1951 to 1954. Three reaction paths were formed by electrolinking-carbonization, using electrode spacings of 150, 152, and 155 feet. The coal along these reaction paths was gasified, using air, oxygen, and steam separately or in various combinations. At the conclusion of operation, a drilling survey was conducted to determine the location and approximate area of the reaction zones. During the applications of the electrolinking-carbonization technique the maximum limitation on electrode spacing was not determined. Initial tests were conducted at 60-foot spacing. Successful path-preparation tests were made at 150-, 152-, and 155-foot spacings, and the indications were that much longer spacings were possible. The potential requirements appear to be constant, regardless of path length, while the gross power required probably will increase with path length. During the carbonization phase gas was produced that is similar in quality to coke-oven gas produced at low to intermediate temperatures.

Jan 1, 1957

By Joseph M. Kuchta

This Bureau of Mines manual is oriented to the technical needs of an investigation of fire or explosion accidents and includes various practical and theoretical information that is needed in analyzing accidents or evaluating conditions that might lead to an accident. It is applicable to accidents in the chemical, mining, transportation, and other fuel-related industries. Specific procedures for conducting an accident investigation are outlined, and various guidelines are given for developing the fire or explosion evidence. Ignitability, flammability, and physicochemical data are presented for over 500 combustible gases, liquids, and solids; empirical and theoretical expressions are also given for extrapolating the behavior of combustible-oxidant-diluent systems to various environmental conditions. In addition, various data pertinent to damage analysis are summarized to facilitate the task of the investigator in developing plausible accident scenarios.

Jan 1, 1985