Search Documents

By John Campbell

An approximate theoretical model is proposed to quantitatively predict freezing ranges Tf and hydrostatic tensions P developed within solidifying binary alloys, allowing for a certain amount of diffusion of solute in the solid during solidification. The maxima in ATf and AP as functions of composition are shorn to occur at smaller solute concentrations than would be expected from the equilibrium diagram, and are found to correspond closely to experimentally observed maxima in microporosity. THE freezing range of simple binary alloys appears to have been little studied, except for certain indirect observations on the defects, particularly microporosity and hot tearing, arising in long freezing range materials. Two theories relating to the freezing range of alloys and its effect upon porosity are reasonably well established, and appear to have been held in isolation from each other: a) From purely equilibrium considerations early researchers expected that an increase in solute content of an alloy should increase the freezing range (defined here as the equilibrium freezing range ?Tf = Tl-Ts where TL and Ts are the liquidus and solidus temperatures, respectively) and thereby increase the width of the pasty zone for a given set of conditions. This in turn should increase the difficulty of feeding the residual liquid through the dendrite mesh to compensate for the contraction on solidification, and consequently tend to increase the observed amount of porosity. From qualitative observations on steels Czikel1 reports an increase in porosity with increasing carbon content up to 0.46 pct C. More careful measurements by Whittenberger and Rhines2 on fourteen different alloy systems showed an approximately linear relation between ?Tf and pct porosity (although unfortunately the precise experimental data is not given). b) Conversely however, other authors3"5 propose that porosity is reduced by the presence of increased amounts of eutectic present at the final solidification temperature. Lees7 and Bochvar6 claim that the hot tearing of alloys is similarly reduced. Scheuer8 has put forward a theory to explain this effect, Fig. 1. The argument is basically that solidification progresses on a plane front through a relatively open dendrite network and is thus (the argument is not developed more explicitly) easier to feed. One would expect effect a) to operate at low solute contents, and b) to be important at higher solute contents, so that at some critical composition a max-

Jan 1, 1970

By Lyman Johnson

Single crystals qf copper in "single slip" orientatiorzs have been deformed in compression. During defortnation all of the independent deformation parameters have been measured. These parameters consist of thefive strain components and three components descrihing the lattice rotation. By a finite strain analysis these pararmeters , forrming a deformation gradient martrix, are related to the amounts of slip on each of the twelve slip systems. The results show that the amount of secondary slip is about equal to the amount of primary slip. This is an order of magnitude larger than has been believed previoutsly. ACCORDING to early theory and experiments, when a single crystal of a fcc metal is deformed in tension or compression it should deform by slip on only one slip system until the stress axis reaches a symmetrical orientation.' However. the observation of a large increase in the secondary dislocation density during ..single slip" makes it clear that some slip does occur on secondary systems. Knowledge of the amount and distribution of this secondary slip is essential to a complete understanding of the mechanisms of single-crystal deformation. Ahlers and Haasen 2 and Mitchell and Thornton1 have tried to detect the amount of secondary slip in single crystals of silver and copper, respectively. Each simultaneously measured the angle A, between the tensile axis and the primary slip direction and the length 1 of a gage section of the specimen after incremental amounts of deformation in tension. The measured A, was then compared with the theoretical single slip angle hp. given by sin Ap = j sin . hO where ?o was the initial angle between the tensile axis and the primary slip direction and lo was the initial gage length. In both sets of experiments a small but systematic difference between ?e and ?p was found. This difference must be due to the occurrence of secondary slip. However, as Mitchell and Thornton1 pointed out. nothing quantitative can be said about the amount and distribution of this secondary slip from the measurements that they made. The reason that no quantitative conclusions could be made is because no unique solution for the distribution of slip on the twelve fcc slip systems can be determined from only two measured deformation parameters such as A and 1. There are, in fact, eight independent macroscopic deformation parameters that can be measured when a single crystal undergoes a homogeneous deformation. Physically these can be thought of as the five finite strain components and the three angles describing the crystal lattice rotation. All eight of these parameters were measured by Taylor4,5 for aluminum deformed in tension and compression. At that time the concern was to show that slip occurs on {111 (110) systems in fcc metals, and the mathematics were not available to determine what slip distributions were compatible with the measurements. In this paper the mathematics6,7 are developed that allow the slip distribution to be determined from these measurable macroscopic deformation parameters. The analysis is applied to the measurements of the strain and lattice rotation of copper single crystals deformed in compression. The results show that the amount of secondary slip is an order of magnitude larger than had previously been thought. CRYSTALLOGRAPHIC DESCRIPTION OF A HOMOGENEOUS DEFORMATION The deformation of a solid body can be represented by a transformation matrix F that transforms the un-deformed state into the deformed state. Consider a vector X connecting two material points in the unde-formed material and the vector x connecting the same two material points after deformation, where both vectors are referred to the same set of Cartesian axes. The final vector x is related to the initial vector X by the equation: X = FS. [2] Eq. [2] can be considered as the equation defining F, which is called the deformation gradient matrix. Its components are: If the deformation is homogeneous, the transformation is linear and the components of F are constants. Using subscript notation, if P is the unit vector in the initial direction of a material line, the components of the unit vector p in the direction of the same material line after deformation are given by:

Jan 1, 1970

By G. Sachs, L. J. Ebert, W. F. Brown

INTRODUCTION ISOTHERMAL transformation, or "austempering," of a carbon-containing austenite at elevated temperatures yields so-called "intermediate products." Their structure and properties are, for a given hardness, rather different from those of "tempered martensite" obtained on conventional quenching and tempering.1 Several investigators2,3 have found that for high carbon and slightly alloyed steels the intermediate products formed at temperatures close to that of the martensite reaction possess strength properties superior to those of tempered martensite. The structure of these low temperature, intermediate products is generally acicular (bainite) but clearly different from that of martensite. However, at higher austempering temperatures, between 1000 and 1300°F (540 and 700°C) carbon steels were found to exhibit a rather low ductility.4-5 Thus notch bar tensile tests showed the ratio between notch strength and regular tensile strength to decrease with increasing austempering temperature. For ductilities below a few percent this notch strength ratio is a measure of ductility, according to investigations on low alloy steels.6-7 Furthermore the presence of intermediate products formed unintentionally on quenching was considered as responsible for the low ductility and impact energy of some heat treated steels.8 These intermediate products could result from partial transformation at the so-called "nose-temperature" where the rate of the transformation is a maximum. Tempering improved such mixtures of martensite and intermediate products, their properties approaching those of tempered martensite of equal hardness. The following investigation constitutes an attempt to determine certain strength properties of a partially austempered and subsequently quenched low alloy steel, namely, a chromium steel (SAE 5140). The structures formed by such a treatment should consist of a mixture of intermediate products formed on austempering and a martensite formed on oil quenching from the austempering temperature. It was intended, by varying the austempering time, to vary the quantity of the intermediate products between zero and 100 pct. The austempering temperature of 860°F was selected after extensive preliminary tests close to the nose-temperature. Austempering at this temperature yielded an acicular intermediate product. Additional tests under less exacting conditions were made for an austempering temperature of 950°F where the intermediate product appeared to be very fine pearlite. To determine the effects of tempering on structures containing various amounts of

Jan 1, 1948

By L. R. Jackson, W. T. Lankford, K. F. Smith

ComMercial steel sheet is prepared by a combination of hot and cold rolling and annealing. This treatment usually results in more or less pronounced anisotropy. The anisotropy may manifest itself both as preferred orientation and in the manner in which impurities, segregations, and the like, are aligned in the sheet. The type of preferred orientation and the organization of impurities or segregations may affect the elastic moduli, the yield strength, the tensile strength, and almost always the amount of ductility in different directions. In any case, the most important directions concerned in the anisotropy are along the rolling direction, along the width direction, and along the thickness direction. Considerable data exist on the anisot-ropy of sheet steel as demonstrated by conventional tensile tests; however, few attempts have been made to measure the constants of plastic anisotropy and use them to describe the flow of anisotropic sheet under combined stresses. In this paper, evidence is presented indicating that plastic flow in anisotropic sheet can be described by the shear-strain energy flow theory provided that the anisotropy is properly taken into account. Materials Used in the Investigation Table I lists the sheet materials used in this investigation and describes the condition in which materials were tested. Direction, of Tests and Test Methods Two types of tests were run—tensile tests and hydraulic-bulge tests. Characteristic parameters of anisotropy were determined from the tension tests by methods which will be described later. In all cases, the tensile test pieces were cut from the same quarter line and adjacent to the bulge test pieces in the sheet in order to minimize

Jan 1, 1949

By Ernest Klepetko

A notable amount of fossil resin exists in many of the bituminous coal beds of Utah. The upper part of these show a marked concentration of resin, which occurs primarily in the fracture seams. In general, these seams are less than 1/8 in. thick, but it is not uncommon to find coal with areas as thick as 3/8 inches. The resin is of the hard kauri variety, with coloration varying from deep blood red to lemon yellow and almost colorless. There is also an almost black variety, which is not readily soluble in the same solvents as the lighter colored resins. These resins are valuable for many industrial purposes. When refined, they are suitable for uses similar to those for which lac resins are usually employed. They are particularly desirable for preparing dielectric varnishes. They are also desirable in preparing printing inks, waterproofing agents, special synthetic rubbers and rubber cements. They are especially suitable as an admixture in synthetic rubbers and cements, as they supply the essential tackiness the synthetics lack. The following chemical trade characteristics have been found by Inter-Chemical Co. research chemists in the refined resins: Specific gravity (melted)....... I .03 -I.06 Acid number.................. 6-8 Softening point, mercury method 160º-165ºC Iodine value (Wijs)............ 140-150 Refractive index............... 1.544 Color (Hellige, 25 pct toluol)... 14 Molecular weight, average...... 732 Purity, 99 + pct pure hydrocarbon "Unaffected by alkalies and resistant to one hour fusion with solid potassium hydroxide. Completely soluble in aliphatic and aromatic hydrocarbons. Insoluble in alcohols, ethyl acetate and other commonly used alcohols and esters. Compatible with natural and synthetic rubbers, chlorinated and cyclized rubbers, waxes, vegetable oils, mineral oils, rosin, ester gum, phenolic and modified phenolic resins and other natural and synthetic resins of like solvent solubility."* The recovery and refining of these fossil resins has been the subject of much research work and has intrigued many investigators. Broadly speaking, the problem involves separation of the resin from the coal into a very high-grade concentrate, and subsequent treatment of this concentrate to produce an acceptable refined resin for its various usages. Obviously it is also desirable to recover the residual coal without excessive size degradation. The late W. D. Green, concentration ennineeru for Combined Metals Reduction CO., obtained U, S. Patent No. 1773997 for the recovery of resin from coal through

Jan 1, 1948

By Ernest Klepetko

A notable amount of fossil resin exists in many of the bituminous coal beds of Utah. The upper part of these show a marked concentration of resin, which occurs primarily in the fracture seams. In general, these seams are less than 1/8 in. thick, but it is not uncommon to find coal with areas as thick as 3/8 inches. The resin is of the hard kauri variety, with coloration varying from deep blood red to lemon yellow and almost colorless. There is also an almost black variety, which is not readily soluble in the same solvents as the lighter colored resins. These resins are valuable for many industrial purposes. When refined, they are suitable for uses similar to those for which lac resins are usually employed. They are particularly desirable for preparing dielectric varnishes. They are also desirable in preparing printing inks, waterproofing agents, special synthetic rubbers and rubber cements. They are especially suitable as an admixture in synthetic rubbers and cements, as they supply the essential tackiness the synthetics lack. The following chemical trade characteristics have been found by Inter-Chemical Co. research chemists in the refined resins: Specific gravity (melted)....... I .03 -I.06 Acid number.................. 6-8 Softening point, mercury method 160º-165ºC Iodine value (Wijs)............ 140-150 Refractive index............... 1.544 Color (Hellige, 25 pct toluol)... 14 Molecular weight, average...... 732 Purity, 99 + pct pure hydrocarbon "Unaffected by alkalies and resistant to one hour fusion with solid potassium hydroxide. Completely soluble in aliphatic and aromatic hydrocarbons. Insoluble in alcohols, ethyl acetate and other commonly used alcohols and esters. Compatible with natural and synthetic rubbers, chlorinated and cyclized rubbers, waxes, vegetable oils, mineral oils, rosin, ester gum, phenolic and modified phenolic resins and other natural and synthetic resins of like solvent solubility."* The recovery and refining of these fossil resins has been the subject of much research work and has intrigued many investigators. Broadly speaking, the problem involves separation of the resin from the coal into a very high-grade concentrate, and subsequent treatment of this concentrate to produce an acceptable refined resin for its various usages. Obviously it is also desirable to recover the residual coal without excessive size degradation. The late W. D. Green, concentration ennineeru for Combined Metals Reduction CO., obtained U, S. Patent No. 1773997 for the recovery of resin from coal through

Jan 1, 1948

By J. F. Martin, L. M. Melnick, R. Rapp, R. C. Takacs

Recent studies on the determination of hydrogen in steel have shown that the hot-extraction method for removing hydrogen from a solid sample is preferable to its removal from a molten sample by vacuum fusion or by fusion in vacuum with tin. A number of techniques are available, however, for determining the hydrogen so extracted. They include: thermal conductivity, gas chromatography, pressure measurement before and after catalytic oxidation of the hydrogen to water and removal of the water, and pressure measurement before and after diffusion of the hydrogen through a palladium membrane. These techniques have been evaluated on the basis of initial cost, maintenance, speed and accuracy of analysis, and applicable concentration range. The results of this study showed that the palladium-membrane technique is best suited for routine use. FOR some time investigators have been concerned with the origin, form, and effect of hydrogen in steel. In such stdies', the analysis for hydrogen constitutes one of the most important phases. It is quite apparent that the results for hydrogen concentrations in a given steel are dependent on the method of obtaining the sample, storage of the sample until analysis, preparation of the sample, and analysis of the sample, including all the facets inherent in the calibration and operation of an apparatus for gas analysis. There are a number of means available for determining hydrogen. This is a critical study of some of the more common techniques in use today. In most conventional melting and casting methods, hydrogen concentrations of 4 to 6 parts per million (ppm) in steel are quite common. Because of the undesirable effects of hydrogen on steel there has been increased use of techniques such as vacuum melting,' vacuum casting, and ladle-to-ladle stream degassing, which lower the hydrogen content to levels on the order of 1 to 2 ppm. Therefore, the method used for determining hydrogen in steel must be sensitive and precise. In any analytical procedure for gases in metals there are two distinct operations—the extraction of the gas from the metal and the analysis of the extracted gas. To extract the gas from the steel, three methods have been employed: 1) fusion of the sample with graphite at high temperature; 2) fusion with a flux, such as tin, at a lower temperature; and 3) extraction of the hydrogen from the solid sample at a temperature below the melting point of the steel. Fusion with graphite is the least-acceptable method. The blank in this method is higher and more variable than in either of the other two methods. The hydrogen fraction of the total gas composition usually is between 10 and 50 pct; thus, a larger analytical error is possible. The vacuum-tin fusion4 extraction of hydrogen is probably the most rapid method in use today; the extraction time is usually about 10 min. However, with this system a bake-out of the freshly charged tin for 2 hr is necessary and a change of crucible and a charge of fresh tin are required after each day of operation whether one or thirty samples have been analyzed. In addition, frequent checks of blank rates are required since CO and Na are continually being given up by the steel samples dissolved in the tin bath. The composition of the gas in this method lends itself readily to analysis; although the hydroge concentration may fall to as low as 50 pct, more often it is above 90 pct, thus allowing a more precise analysis (because of less interference from other gases). In 1940 ewell' published the hot-extraction method for extracting hydrogen from the solid sample, comparing analysis for hydrogen extracted at 600°C with similar analysis for the gas extracted at 1700°C by fusion with graphite. Good agreement for hydrogen was obtained between these two methods, provided sufficient time was allowed for extraction at the lower temperature. carsone obtained good results in his comparison of this hot-extraction method with vacuum-tin fusion. Subsequent work by Geller and sun7 and Hill and ohnson' has shown that steel samples should be heated to at least 800°C to effect the release not only of the diffusible hydrogen but also of the "residual" hydrogen that may be present as methane. Since the rate of evolution of hydrogene9l0 depends on such factors as sample size and composition, thermal history, and extent of cold work, a fixed extraction time is not possible. Extraction times of 30 min are normal, but 2 hr are not unusual. Induction or resistance heating may be used in the hot-extraction method. With resistance heating the

Jan 1, 1964

By S. C. Langdon, Henry S. Rawdon

The following note describing the behavior of copper under rather unusual conditions is offered for its suggestiveness rather than as a complete study of the question. The examinations described were made because of a request for information concerning the embrittlement of copper when heated in a molten salt bath (sodium chloride) for the purpose of cleaning, as well as softening it. It is well known that metals may be rendered very brittle by electrolytic action in aqueous solutions, in all probability by the action of nascent hydrogen, and it was suspected that perhaps the embrittlement of the copper by means of the molten salt was produced in a somewhat similar manner. It was found that the copper was in contact with iron (or steel) while immersed in the molten salt, through the occasional use of an iron stirring rod, iron forceps for handling the pieces, and an iron pot for containing the fused salt. In the electrochemical potential series iron and copper stand some distance apart, copper being electronegative to the iron. Assuming that the two metals bear 2 similar relation to each other, when immersed in a bath of molten salt, as they do in an aqueous solution, they would be expected to form a galvanic couple, the copper being the cathode. By this means the copper might be embrittled, as often happens in aqueous solutions, by the action of the liberated hydrogen. In this case, however, the embrittlement must be attributed to some other agent than hydrogen. TO demonstrate how copper may be embrittled under these conditions, two small rods, one of copper and the other of mild steel, approximately 3/8 in. (9.5 mm.) in diameter, were immersed in a bath of sodium chloride that had been heated somewhat above its fusion point (melting point of sodium chloride is 801" C.) and an electromotive force of approximately 6 volts from a storage battery was impressed upon the system. The copper was made the cathode and the action was continued for several minutes. When removed from the bath, cooled, and tested for brittleness by bending the specimen back and forth, while clamped firmly at one end in a vise, the copper rod was found to be very brittle, as compared with a rod of the same length of the untreated copper tested

Jan 1, 1921

By J. T. Norton, Joseph Gurland

IN spite of the extended use and high state of practical development of the cemented tungsten carbides, the structure of these alloys is still a matter of considerable controversy. The characteristic high rigidity and rupture strength of sintered compacts have been attributed to a continuous skeleton of tungsten carbide grains, formed during the sintering process. This view is based mainly on the work of Dawihl and Hinnuber,1 who reported that a sintered compact of 6 pct Co maintained its shape and some of its strength after the binder was leached out with boiling hydrochloric acid. After leaching, only 0.04 pct Co was reported to remain in the compact. They also showed that the assumed increasing discontinuity of such a skeleton, as the cobalt content is increased, could be made to account for the observed discontinuous increase of the coefficients of thermal expansion, the loss of rigidity, and the impaired cutting performance of alloys of more than 10 pct Co. Contradictory evidence was cited by Sanford and Trent,' who mentioned that a sintered compact was destroyed by reacting the binder with zinc and leaching out the resulting Zn-Co alloy. The skeleton theory also does not account for the observed change of strength of sintered compacts as a function of cobalt content. If the skeleton is responsible for the strength, the latter would be expected to decrease with increasing binder content. Actually, the strength increases and reaches a maximum around 20 pct Co. In addition, tungsten carbide is brittle and undoubtedly very notch sensitive. The highest value found in the literature for the transverse rupture strength of pure tungsten carbide prepared by sintering is 80,000 psi.3 herefore, such a skeleton does not easily account for a rupture-strength value of 300,000 psi and higher, commonly found in sint.ered tungsten carbide-cobalt compacts. In view of the conflicting data present in the literature, experiments were undertaken to determine whether the sintering of tungsten carbide-cobalt alloys leads to the formation of a carbide skeleton or whether the densification behavior and the properties of cemented compacts are consistent with a structure of isolated carbide grains in a matrix of binder metal. The specimens were prepared from powders of commercial grade. Tungsten carbide powder ranged in particle size from 0 to 5x10-4 cm. Mixtures of tungsten carbide and cobalt were ball milled in hexane for 48 hr in tungsten carbide lined mills. After milling, the specimens were pressed in a rectangular die (1x1/4x1/4 in.) at 16 tons per sq in. NO pressing lubricant was used. Sintering of the tungsten carbide-cobalt compacts was carried out in a vertical tube furnace equipped with a dilatometer (Fig. I), by means of which the change of length of the powder compacts could be followed from room temperature to 1500°C. An atmosphere of 20 pct H, 80 pct N was maintained inside the furnace. Decarburization of the samples was prevented by the presence of small rings of graphite inside the furnace tube. The temperature of the sample was measured by a platinum-platinum-rhodium thermocouple, which also was part of a temperature control system able to maintain a constant temperature within ±100C. Pure tungsten carbide compacts were prepared by sintering the carbide without binder or by evaporating the binder from sintered compacts in vacuum at 2000°C. Since complete densification of these samples was not desired, they were sintered only to 60 or 80 pct of the theoretical density of tungsten carbide. The specimens were prepared for metallographic examination by polishing with diamond powders and etching with a 10 pct solution of alkaline potassium ferricyanide. Cobalt etches light yellow and the carbide gray. The amount of porosity is exaggerated since it is difficult to avoid tearing out carbide particles, especially from incompletely sintered samples. Experimental Observations A number of specific experiments were carried out in order to study some particular aspect of the sintering problem. The details of these experiments, together with their results, are as follows: Electrolytic Leaching: The binder was removed by electrolytic leaching from sintered tungsten carbide-cobalt compacts for the purpose of determining the continuity of the carbide phase. The method used was based on the work of Cohen and coworkers4 on the electrolytic extraction of carbides from annealed steels. If the sample is made the anode, using a 10 pct hydrochloric acid solution as the electrolyte, the binder is dissolved, but the rate of solution of tungsten carbide is negligible. A current density of 0.2 amp per sq in. was applied. As shown in Fig.

Jan 1, 1953

By Arnulf Muan, Hobart M. Kraner

Ferromanganese alloys react with aluminu-silica brick in blast furnace hearths and cause the formation of new phases with low refractoriness and consequent failure of the refractory lining. The nature of these reactions is explained on the basis of petrographic observations, thermodynamic data, and Phase equilibrium considerations. Animproued hearth design resulted from these findings. The production of ferromanganese in blast furnaces presents many problems which are not encountered in the production of iron in the same furnaces. One of the most serious of these problems is the rapid failure of refractories caused by their reaction with the ferromanganese metal. The present paper describes such a "hearth attack", its symptoms, causes, and cure. Following an introductory discussion of operating practice in ferromanganese blast furnaces, results are presented of a petrographic examination of samples from a furnace which had to be shut down because of refractory failure. The causes of this failure are then analyzed on the basis of petrographic observations combined with thermodynamic and phase equilibrium data available in the literature. The latter type of data were subsequently used as a guide in recommending improvements in hearth designs which have since proven themselves successful in practical operations. I) FERROMANGANESE BLAST FURNACE PRACTICE It is considered good practice to blow in a furnace on iron and operate it in this way for a period of time preliminary to producing ferrornanganese. During this time, iron generally penetrates the bottom refractories six or more feet below the original working surface of the hearth. Not only does this metal pervade the joints to these depths, but the pores of the refractories are usually also filled by molten iron. The high throughput of the iron furnace provides ample heat to maintain a high temperature in the hearth refractories. This, together with a high ferrostatic pressure, causes porous clay brick of the hearth to shrink. During subsequent use of such a furnace in ferromanganese production, the iron in the pores of hearth brick if; replaced to some extent by ferromanganese. The replacement is usually not complete. This is probably due to the lower metal throughput and lower prevailing temperatures resulting from this in the brick of the hearth bottom. When the ferrornanganese furnace is banked—or when the temperature in the furnace falls due to a furnace delay—-manganese oxidizes even though the atmosphere is largely CO. Considerable expansion accompanies this oxidation of manganese from metal to oxide. The hearth refractories are then subjected to the disintegrating forces of the volume expansion. These forces may in extreme cases be large enough to lift the furnace off its mantle supports as was described in a previous paper.' When cooling takes place slowly, however, and the temperature remains at a fairly high level, the refractories undergo fluxing action by the MnO. This latter reaction and the reduction of SiO2 of the clay brick is the general subject of the present paper. The observations to be described herein were made on a ferromanganese furnace located at the Johnstown plant of Bethlehem Steel Co. The furnace was lined entirely with clay refractories and had operated on iron for 266 days and on ferromanganese for 96 days prior to being taken off because of a hearth wall failure. II) PETROGRAPHIC EXAMINATION AND CHEMICAL ANALYSIS The photograph reproduced in Fig. 1 shws a cross section of the upper part of an 18 by 9 by 4-1/2 in. bottom block removed from the blast furnace. This brick came from a depth of approximately 6 ft below the original working face of the bottom. It will be noted that the 4-1/2 in. dimension is almost the same as when the brick entered the furnace. Three characteristically different zones marked I, II, and III on the print of Fig. 1 are apparent. Results of chemical analyses of the original brick and samples from each of these zones are listed in Table I. Petrographically the various zones were characterized as follows: The central zone marked I was essentially un-reacted brick. The microstructure consisted of fine needles of mullite, and the pores in this entire area were filled with iron. This is characteristic of

Jan 1, 1962

AN intermetallic compound, Ni3A1, has an ordered fcc structure of type Ll2, and shows peculiar dependence of the yield stress upon temperature; i.e., the yield stress increases by a factor of six upon raising the temperature from 77" to 900K1, 2 This compound is technologically important, since many nickel-base superalloys owe their high-temperature strength to the peculiar yield stress behavior of Ni3Al. The only study of the elastic behavior of this compound was made by Davies and Stoloff,1 who determined Young's modulus of poly crystalline Ni3A1 between 300" and 730°K. The determination of single-crystal elastic constants of Ni3A1 is therefore of interest in connection with dislocation dynamics and is reported in this paper. A single-crystal specimen, 1 by 1 by 3 cm, was cut from an ingot generously supplied by Dr. B. H. Kear of Pratt & Whitney Aircraft. Following initial machining with a Servomet and a surface grinder, the specimen was etched and annealed at 1100°C for 5 hr in vacuum followed by furnace cooling. Two parallel faces were oriented normal to within ±l deg of a [I101 crystallographic axis by the back-reflection Laue technique. The parallel faces were hand-lapped, etched, and polished by the usual metallographic procedures. Final thickness along the [I101 axis was (0.9325 * 0.0005) cm. Chemical analysis gave an average composition of 87.35 pct Ni. Total impurity content is esimated to be no more than 0.1 pct. The elastic constants were calculated from measurements of ultrasonic waves which were propagated along the [110] axis. A longitudinal wave and two shear waves whose displacements are aligned along the [ 110], [li~], and [001] directions, respectively, are necessary in order to completely specify the three elastic constants. Two 3/6-in. quartz transducers were bonded to the parallel faces of the sample with ~ac-seal.3 Although this bond was sensitive to thermal shock, it performed satisfactorily over the entire temperature range for both longitudinal and shear wave propagation. A frequency of 5 mHz was employed in the method of Williams and Lamb4 in order to measure the absolute value of the ultrasonic velocity. The pulse-overlap technique of Mcskimin5 was also used at this frequency in order to determine the shift in the ultrasonic velocity

Jan 1, 1970

By Ferid Kromer

Geography: The Tagtepe district of the Vilayet of Eskigehir is about 20 miles northeast of the city of Eskigehir (approximately midway between Ankara and Istanbul) in western Anatolia. The area is a mountainous one, the highest peak being Tagtepe Mountain (5200 ft) which is approximately in the center of the district. The mountains drop off to the deep valley of the Sakarya River on the north and to the plain of Eskigehir on the south. FERID KROMER, Junior Member AZME, is a Consulting Mining Engineer and General Manager, Bagtag Turk Maadin Ltd., Istanbul, Turkey. New York Meeting, February 1950. TP 2629 H. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Dec. 29, 1948. For the most part, the watershed is on the northern side of the mountain barrier, draining into the Sakarya River, which in turn empties into the Black Sea midway between Zonguldak and the mouth of the Bosphorus. The approximate area covered by the Tagtepe district is shown in fig. 1. Transportation to shipping points is available via the Istanbul-Ankara railroad. The station on this line nearest the mining district is Alpikoy station, about 20 miles by road southwest of Tagtepe Mountain. Interior roads within the district are poor. Being of dirt, the winter rains and snows render them almost impassable for trucks from about the middle of December until the end of March, thus presenting a considerable transportation problem. However, the roads from the Bagoren and Tagtepe chromite mines to the railroad shipping point at Alpikoy station have recently been repaired and will be maintained for all-weather truck transportation. Detailed climatic data are not available. However, in general the spring, summer, and early autumn months are dry, and good weather may be expected from May until early November. Then the winter rains commence, and heavy snow is usual during January and February. Geology: The mountainous structure of Tagtepe belongs to basic rocks of serpentine (Variscan Orogeny) which is in contact with Paleozoic schists at west, and an Oligocene outcrop of red clays in Margi-Sepetci region (see fig. 1) at southeast. The northwest and southwest borders of Tagtepe district are, respectively, surrounded by Paleozoic schists and pebbly gray and yellow Neogene clays. More recent formations of alluviums overlay the plain of Eskigehir. Dark basic rocks of trachytes with hornblende are visible on Turkmenbaba Mountain, at the west of Tagtepe. Mineral Occurrences: Chromite: the most important mineral found in any quantity in the Tagtepe district. The alignment of the deposits of chromite is in general along the line Bagoren-Tagtepe (see fig. 1). The first mines in the area were those of Tagtepe and Bagoren, which were developed over 20 years ago with Swedish capital. Other deposits of chromite, more recently discovered and so far of less importance, are being worked at Kurucor, Komurcu, Gelinmezari, and Lacin (see fig. 1). Deposits average generally between 46 and 48 pct chromic oxide, with the exception of the Bagoren mine which averages 44 pct. However, a new lode, very recently plotted, in the Tagtepe mine averages 50 pct Cr,O,, 4.6 pct SOz, and 7 pct FeO. Geological character of the chromite occurrences in the Tagtepe mine may be considered typical of most chromite lodes in this area. The indications are that the formations of ore lenses are developed by the segregation of chromite crystals intruded into the serpentinized rock, and exposed later to tectonic movement within the zone of crystallization. All lenticular masses are more or less regular in shape and follow each other in southeast-northwest direction and dip generally 70" NE. Ore lenses do not seem to persist in depth, average depth of two lenses is 60 ft below surface. Three lodes .have been mined as open-pit. The average dimensions of individual lenses are as follows: pitch length, 100 ft; breadth, 27 ft; and width, 20 ft. The lenses and their enclosing rocks are broken by parallel fractures in approximately east-west direction. These joints are filled, except in one lode, with cementing material, which gives to the ore a

Jan 1, 1951

By Ferid Kromer

Geography: The Tagtepe district of the Vilayet of Eskigehir is about 20 miles northeast of the city of Eskigehir (approximately midway between Ankara and Istanbul) in western Anatolia. The area is a mountainous one, the highest peak being Tagtepe Mountain (5200 ft) which is approximately in the center of the district. The mountains drop off to the deep valley of the Sakarya River on the north and to the plain of Eskigehir on the south. FERID KROMER, Junior Member AZME, is a Consulting Mining Engineer and General Manager, Bagtag Turk Maadin Ltd., Istanbul, Turkey. New York Meeting, February 1950. TP 2629 H. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Dec. 29, 1948. For the most part, the watershed is on the northern side of the mountain barrier, draining into the Sakarya River, which in turn empties into the Black Sea midway between Zonguldak and the mouth of the Bosphorus. The approximate area covered by the Tagtepe district is shown in fig. 1. Transportation to shipping points is available via the Istanbul-Ankara railroad. The station on this line nearest the mining district is Alpikoy station, about 20 miles by road southwest of Tagtepe Mountain. Interior roads within the district are poor. Being of dirt, the winter rains and snows render them almost impassable for trucks from about the middle of December until the end of March, thus presenting a considerable transportation problem. However, the roads from the Bagoren and Tagtepe chromite mines to the railroad shipping point at Alpikoy station have recently been repaired and will be maintained for all-weather truck transportation. Detailed climatic data are not available. However, in general the spring, summer, and early autumn months are dry, and good weather may be expected from May until early November. Then the winter rains commence, and heavy snow is usual during January and February. Geology: The mountainous structure of Tagtepe belongs to basic rocks of serpentine (Variscan Orogeny) which is in contact with Paleozoic schists at west, and an Oligocene outcrop of red clays in Margi-Sepetci region (see fig. 1) at southeast. The northwest and southwest borders of Tagtepe district are, respectively, surrounded by Paleozoic schists and pebbly gray and yellow Neogene clays. More recent formations of alluviums overlay the plain of Eskigehir. Dark basic rocks of trachytes with hornblende are visible on Turkmenbaba Mountain, at the west of Tagtepe. Mineral Occurrences: Chromite: the most important mineral found in any quantity in the Tagtepe district. The alignment of the deposits of chromite is in general along the line Bagoren-Tagtepe (see fig. 1). The first mines in the area were those of Tagtepe and Bagoren, which were developed over 20 years ago with Swedish capital. Other deposits of chromite, more recently discovered and so far of less importance, are being worked at Kurucor, Komurcu, Gelinmezari, and Lacin (see fig. 1). Deposits average generally between 46 and 48 pct chromic oxide, with the exception of the Bagoren mine which averages 44 pct. However, a new lode, very recently plotted, in the Tagtepe mine averages 50 pct Cr,O,, 4.6 pct SOz, and 7 pct FeO. Geological character of the chromite occurrences in the Tagtepe mine may be considered typical of most chromite lodes in this area. The indications are that the formations of ore lenses are developed by the segregation of chromite crystals intruded into the serpentinized rock, and exposed later to tectonic movement within the zone of crystallization. All lenticular masses are more or less regular in shape and follow each other in southeast-northwest direction and dip generally 70" NE. Ore lenses do not seem to persist in depth, average depth of two lenses is 60 ft below surface. Three lodes .have been mined as open-pit. The average dimensions of individual lenses are as follows: pitch length, 100 ft; breadth, 27 ft; and width, 20 ft. The lenses and their enclosing rocks are broken by parallel fractures in approximately east-west direction. These joints are filled, except in one lode, with cementing material, which gives to the ore a

Jan 1, 1951

By D. R. Parrish, V. J. Berry

Reverse combustion is one thermal method of recovering hydrocarbons from porous undergrortnd formations containing oil or tar. In applying this method, air is introduced via an injection well and the mixture of air and hydrocarbons is ignited in the production well. A combustion zone then recedes toward the injection well, counter-current to the air flow. If the combustion-zorie temperature is sufficiently high, the oil or tar irz place is distilled arid cracked. The hydrocnrhon flows as a vapor to the production well and subsequently is condensed at the surface. Maximum temperature and velocity of morcment arc the two dependent variubles defining the progress of the combustion zone. A theoretical analysis has been made of heat flow in the reverse-comhustion process as.srtrning linear flow in a homogeneous system. The differentirll equatious, which include the oxygen-hydrocar-hon rctrction rate, have been solved numerically. Rescllts indicate that the maximum temperature reached and he cornbustion-zone relocity both increase with an incrense in air-injection rote. Heat loss to surroundings has little effect on the maximum comhustion-zone ten?perature achieved, but it is reflected in a reduced com-bustion-zorzc, velocity. It is also predicted that an increase in the oxygen-hydrocarbon reaction rate results in a reduction in the maximum temperature reached. The calculated results are in agreement with results from reverse-combustion experinments using samples of a tar sand. INTRODUCTION Reverse combustion is one thermal method of recovering hydrocarbons from porous underground forma-tions containing oil or tar.' In applying this method, air is introduced into the underground formation via an in-jection well. In one or more adjacent production wells, the mixture of air and hydrocarbons is ignited at the sand face. The combustion zone thus formed recedes toward the injection well, counter-current to the air flow (Fig. 1). Under certain conditions, the rate of recession of the combustion zone is sufficiently rapid that only a small fraction of the hydrocarbon at any point in the formation is consumed by combustion. If the combustion-zone temperature is sufficiently high, the uncon-sumed oil or tar in place may be partially distilled or cracked. This material then can flow as a vapor with the gaseous combustion products to the production well and subsequently be condensed at the surface. Under other conditions, the combustion-zone temperature may be so low that little, if any, of the hydrocarbon is vaporized. Nevertheless, the viscosity of the hydrocarbon may be reduced enough so that other recovery methods subsequently can be applied to produce oil at attractive rates. The maximum temperature achieved in the combustion zone and the velocity of movement are the two dependent variables defining the progress of the combustion zone. Presumably. knowledge of these factors will permit estimates to be made of oil recovery efficiency, oil and gas producticn rates and average amount of injection air required per barrel of oil recovered. The maximum temperature and combustion-zone vclocity are, in turn, expected to be dependent upon air flow rate, heat losses to surrounding formations, physical properties of the rock and the hydrocarbon. the extent to which the porous formation is saturated with the hydrocarbon, the rate of oxidation of the hydrocarbon and the amount of heat released. It is desirable that the relative importance of each of these factors be understood so that the results of laboratory tests of oil recovery by reverse combustion can be properly interpreted in terms of expected field performance. It is particularly desirable to assess the importance of heat lcsses because these are difficult to control or eliminate

By H. L. Talbot, A. J. Hall, R. S. Young

A method for the chemical differentiation of oxidized cobalt from sulphide cobalt in complex mine and concentrator products is of considerable interest to a number of mining companies throughout the world. At Rhokana Corporation, in Northern Rhodesia, for instance, cobalt is found chiefly in the sulphide form, as carrollite, but a cobalt oxide mineral also occurs irregularly underground, and relatively small quantities in the mill feed from time to time are difficult to detect visually at the concentrator. The oxide cobalt is not amenable to the sulphide flotation process used at Rhokana and nearly all of it passes into the tailing. The occasional period when high tailing losses occur with no appreciable change in the cobalt content of the mill feed has naturally been disturbing to the concentrator staff, who had no means of determining whether an influx of cobalt oxide ore or laxity on the part of the mill flotation operators as responsible for these results. A procedure for determining oxidized copper minerals, based on their solubility in dilute sulphuric acid saturated with SO2, has been used for many years in the copper industry. In the presence of cuprite the procedure fails, but otherwise it gives results quite satisfactory for control pur- poses. Empirical methods for determining oxidized forms of zinc and lead have been proposed, but they are generally unsatisfactory except in isolated cases of a very simple ore. No published procedure for determining oxidized forms of cobalt or siinilar elements has come to the authors'notice. Experimental Procedure There are obviously two alternatives in attacking a problem of this nature. One is to employ a solvent for oxide cobalt that will not dissolve cobalt sulphide. The other is to find a substance capable of oxidizing the cobalt sulphide to sulphate, which of course is water-soluble and can then be leached from the water-insoluble oxide cobalt. A representative sample of Rhokana cobalt oxide ore was secured, ground to minus 200-mesh, and carefully rolled to furnish a standard sample for this work. The analysis of this material gave the following percentages: Co, 0.55; Cu, 1.64; Fe, 2.98; S, 0.08; SiO2, 41.42; Al2o3, 11.20; CaO, 13.82; MgO, 3.80. As a source of cobalt sulphide a similar large sample of carrollite was prepared, analyzing Co, 23.36 per cent; Cu, 27.32; and S, 31.13. This sample of course was not pure carrollite, but was the best obtainable in quantities sufficient for a standard intended for considerable work. It was a pure sulphide sample, microscopic examination showing only carrollite, a little bornite, and gangue, with no visible sign of oxidized ore present. A wide variety of reagents as used in an effort to selectively dissolve oxide cobalt or to oxidize sulphide cobalt to

Jan 1, 1949

By John V. Beall

Let's start at the beginning, Mr. Turner. Where and when were you born? In Lansing, Mich., on July 31, 1880. And what was your education? I went to the University of Michigan, where I got an A.B. degree in 1902; then to the Michigan College of Mines at Houghton, graduating from there in 1904 with a B.S. and an E.M. What was your first job in the mining industry, Mr. Turner, and what were you paid? In the summer of 1902, 1 was a field assistant for the U. S. Geological Survey in southwestern Idaho and southeastern Oregon, working under Israel C. Russell, professor of geology at the University of Michigan, who incidentally, had just returned from an expedition to study the effects of the eruption of Mt. Pelee, on Martinique. I was paid $60 a month and found; in addition to doing geologic and hydrographic work, I cooked many of the meals for a party of four, and wrangled four horses. I slept for four months under the stars, without a tent.

Jan 1, 1949

By Shiro Ban-ya, John Chipman

Using the same experimental method previously described, the activity of sulfur in a number of quaternary and more complex liquid iron alloys at 1550oC is determined. A "cross-product term zj.zk is determined for each of the quaternary alloys to take account of the mutual effects of the combinalion on the indi-vidual contributions to In 5 The interactiotl coefjicienls delermined for ternary solutions and cross-pvoducl coefficierlts from the quaternary systems are used to estimate the activity coefficient of sulfur in more complex alloys. OUR recent papers 1,2 have described new determinations of the activity of sulfur in Fe-S binary and Fe-S-j ternary solutions, but the practical applications of these data require the estimation of activity of sulfur in more complex systems. Previously, Sherman and chipman3 devised an approximate method for calculating the activity of sulfur in complex systems by summing the contributions to the logarithm of the activity coefficient of each element in the alloy. This procedure is more successful, as one of us has pointed out,4 when the concentration variable is taken as zs = ns/(nFe — nS t CLJ~ nj) rather than the conventional atom fraction x~ = nS/(nF, + nS + Enj). In the former definition, which is based on analogy to interstitial solutions, the value assigned to uj is normally +1 for metallic and -1 for nonmetallic elements." In addition, however, the effects of mutual interaction between alloying elements must be considered for the accurate estimation of the activity of sulfur in more complex systems. The purpose of this investigation has been to devise a more reliable method for estimating the activity coefficient of sulfur in nmIticomponent iron alloys. The measurements were carried out on some quaternary systems Fe-S-j-k for combinations of silicon, chromium, nickel, cobalt, molybdenum, and tungsten. Manganese was not included since the experimental method has been found unsatisfactory for volatile, sulfide-forming elements. The experimental method was the same in every detail as described previously. 1,2 The concentrations of sulfur, silicon, chromium, and copper in the quenched metals were determined by chemical analysis but those of nickel, cobalt, molybdenum, and tungsten were calculated from charged amounts. Iron sulfide was included in the charges in amounts estimated to furnish approximately the final sulfur content. CALCULATION W2 have shown2 that when zs and zj are the concentration variables in a ternary Fe-S-j solution the logarithm of the activity coefficient S = a~/zg is a linear function of the variables as and aj defined as follows:

Jan 1, 1970

By James A. Crookston, William D. Fitzpatrick

Committee C-8 of the American Society for Testing and Materials defines "Refractories" as "Material, usually nonmetallic, used to withstand high temperature," and it defines the term "Refractoriness" thus, "In refractories the capability of maintaining the desired degree of chemical and physical identity at high temperatures and in the environment and conditions of use." The ability to withstand high temperatures is critical to classifying a material as a "refractory." However, as the foregoing definition of "refractoriness" implies, the refractory material may be subjected to and is expected to resist not only high temperatures but a variety of other destructive forces incident to its use. These include abrasion, impact, thermal shock, chemical attack, and high level loads at high temperatures. The various industrial applications of refractories represent an infinite variety of combinations and degrees of severity of these destructive forces, including high temperatures. Naturally, such a variety of application conditions leads to a need for a wide variety of refractory products to satisfy those conditions. The number of refractory products available is great enough that some form of classification is necessary to a discussion of refractories. Refractories may be classified in several ways, but the most suitable one is based on their general compositions and to lesser degrees on their physical condition and distinctive properties. The primary types of brick include aluminosilicate brick (fire clay and alumina), basic brick (magnesia and chrome ore, alone and in various combinations), silica brick, insulating brick, and special refractories (carbon, Sic, ZrO,, zircon, borides, and nitrides). Brick are, of course, preformed and are usually heat treated at high temperatures before use, but are in some instances unburned and/or chemically bonded, including the relatively new class of tar-bonded magnesia and/or dolomite brick. In addition to preformed refractories, another broad category includes the so-called specialty refractories, which are usually made in the same types as itemized for brick-bonding mortars and high temperature cements, hydraulic setting castables or refractory concrete, plastic firebrick, and ramming mixes. Refractory grains, such as fire clay and high alumina calcines, dead-burned magnesite and periclase, and dead-burned dolomite are also considered refractory products. Brick are also classified on the basis of physical dimensions, as standard sizes and special shapes. The standard sizes are those which are of definite shape and design and are designated as 9 x 4 ½ x 2 ½ in. and 9 x 4 ½ x 3 in. straights and series. All other brick of non- standard sizes are referred to as special shapes. These come about as a result of a particular need for a given furnace or for a particular application.

Jan 1, 1975

By A. L. Engel

STRICTLY speaking, ore-dressing does not commence until after the ore is in the mill bins, but where complex ores are treated and their minerals separated to make the best commercial concentrate with the lowest economical tailing, ore-dressing problems begin and often center in the mine itself. This does not refer to the grade of the ore, but rather to the frequent condition in which metallurgical results radically different from customary are obtained because of changes in the character of the ore treated. Different varieties of ore can usually be identified as coming from well-defined depths or zones in the mine, or from known sections of the orebody. Varying degrees of alteration of the ore, inclusions of harmful gangue material, or variations in the quantities of component metallic minerals are often causes of temporarily bad metallurgical results in otherwise successfully operated plants, especially those employing differential flotation to. recover several valuable minerals contained in the ore.

Jan 1, 1931

By J. S. Marsh

The student of steelmaking is all too well acquainted with the fact that in many instances he must deal with data that in graphical representation exhibit the property most desirable in bird shot. This is scarcely mystifying, since the effort to establish one variable as a function of another is usually hampered by the simultaneous operativeness of two or three other factors that may be important. A large part of arriving at relationships that have the pleasing self-consistency of, say, precise measurements of thermal expansion, consists of determining what factors must be held constant-—an even larger part usually consists of collecting data for which those factors have been so maintained. It is not intended to imply that functional relationships in the physical chemistry of steelmaking are hopelessly obscure; on the contrary, it is merely necessary to be undisturbed by marked deviation of some points from a curve that otherwise makes sense. A reaction mechanism suggested by such a curve may call attention to hitherto unsuspected factors operative in the origin of the deviating points, and thus permit another step to be taken in the direction of fuller understanding. It is proposed, therefore, to suggest several empirical relationships. Even though the approach is not always rigorous, deviations caused by simplifying assumptions appear to be too small to obscure a provisional It has been appreciated for some time that the carbon-oxygen reaction in liquid steel is highly important. For example, Körber et al.,' in introducing a summary of their extensive work on steelmaking reactions, said: "... the far-reaching and truly dominating action of carbon upon the metallurgical reactions will be especially stressed ..." In "Basic Open Hearth Steelmaking"2 (hereafter BOHS, for simplicity), it is accepted repeatedly that the various slag-metal interactions are nearly always controlled by the carbon-oxygen reaction. Before further discussion of this reaction, however, it will be worth while to consider briefly the carbon-oxygen equilibrium. In BOHS (p. 483) it is stated that: When liquid iron is brought into contact with gases containing carbon monoxide it absorhs carbon and oxygen. Conversely the carbon and oxygen in the metal unite to form carbon monoxide which is evolved from the bath during the open-hearth boil or while rimming ingots are solidifying. . . . When the equilibrium pressure is one atmosphere the equilibrium-constant equation simplifies, on the assumption that the activity of each element is equal to its percentage, to a constant which has been so much used that it has acquired a special symbol m. where m = %C X %O

Jan 1, 1945