By P. Payson

EMBRITTLEMENT of hard-tempered martensite (500°F embrittlement) appears to be coincident with the beginning of the third stage of tempering. During the first stage, primary martensite of steels containing over 0.25 pct C decomposes to a mixture of c carbide and martensite of appreciably constant carbon content close to 0.25 pct.' During the third stage of tempering, cementite forms. In steels with

Jan 1, 1955

By C. V. Millikan

THE year 1930 in the petroleum industry has been characterized by the establishment of large potential production of crude oil. This has resulted in closer cooperation between companies by proration and unit operation agreements in order to afford an equitable outlet to all, and to prevent a flood of oil being forced on the market with attendant tremendous material and economic waste. Drilling wells in proved areas and wildcat wells are fewer than in the past several years. Restricted production and low prices have caused greater effort to increase producing and recovery efficiencies. Increased refinery efficiencies have amplified the effect of overproduction. Pipe line departments have been especially busy. New oil lines have reached more refineries by new and shorter routes. Establishing greater gas reserves by new fields has justified new gas lines to industrial centers, and has brought this fuel to thousands of new domestic consumers. Two long gasoline lines, a new venture in pipe lines, are being built to obtain a lower cost of transportation and less loss between the refineries and their distribution centers. The chairmen of the various divisions have discussed the developments of their respective branches more fully in the following reviews.

Jan 1, 1931

By AIME AIME

THE iron and steel activities of this meeting opened on Monday morning with the steel melting session," with G. B. Waterhouse in the chair and A. L. Feild as vice-chairman. N. A. Zeigler's paper, on "Gases Extracted From Iron Carbon Alloys by Vacuum Melbing," created considerable interest and the discussion in general was most favorable. H. W. Gillett and Louis Jordan of the Bureau questioned the method of analysis for oxygen and C. H. Herty, Jr., and J. M. Gaines, Jr., I , expressed their surprise at the large amount of oxygen with the high ,carbon alloys. Whether the gases found existed as gas in blowholes or as oxide inclusions was also a moot point. A paper by C. D. King, on "Basic Open-Hearth Yields," was an extremely interesting and valuable contribution. It was discussed by C. E.Kinney and A. L. Feild and numerous questions were asked throughout the presentation. Mr. King then presented a critical analysis of the losses together with novel methods of calculating them. A paper by C. H. Herty, Jr., and J. M. Gaines, Jr., on "Unreduced Oxides in Pig Iron and Their Elimination in the Basic Open-Hearth Furnace," followed. The question of silicates and oxides in pig iron created much discussion, notably by Henry Hanson and W. J. MacKenzie, who gave figures on chipping cost as a function of blast-furnace practice.

Jan 1, 1929

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members who registered at Institute headquarters during September: William B. Phillips, Austin, Texas. Will L. Clark, Jerome, Ariz. Olof Wenstrom, Boston, Mass. Robert H. Richards, Boston, Mass. Anthony F. Lucas, Washington, D. C. Hennen Jennings, Washington, D. C. P. H. Griffin, New York, N. Y. Waldemar Lindgren, Boston, Mass. H. N. Lawrie, Portland, Ore. C. Snelling Robinson, Youngstown, 0. Clarence P. Linville, Everett, Pa. E. P. Ross, Johnson, Tenn. Members of the XII International Geological Congress who made the Institute Office their headquarters while in New York A. Bigot, Caen, France. E. Gentil, Paris, France. J. Caillebotte, Paris, France. H. Saint-Clivier, Paris, France. John Ashworth, Manchester, England. Tadasu Hiki, Kioto, Japan. T. Dahlblom, Falun, Sweden. L. Milch, Greifswald, Germany.

Jan 10, 1913

By AIME AIME

THE first meeting" of the Iron and Steel Division was held Tuesday afternoon, Feb. 17, with nearly 100 men present and C. B. Murray as chairman. This was a round table discussion of iron ore beneficiation and of its relation to blast-furnace operations, and only one paper was presented, by Clyde E. Williams. Mr. Williams discussed the future of the Lake Superior district in its relation to the iron and steel industry. He stated that although estimates had shown that the total life of the present known iron ore reserves of the Lake Superior district was 20 to 30 years and that many believed that as a result of this depletion foreign ores would be brought to the Atlantic Seaboard, thus causing a displacement of the steel industry to the East, he believed that the Lake Superior district would continue to be the important producer of iron ore used in this country for decades beyond the predicted time before the exhaustion of the present known reserves. He described the three general types of ores that required concentration and pointed out the needs for research and the proper methods to be used in processes for the beneficiation of these low-grade materials. He discussed the effects of fine concentrates and the use of agglomerated ores in the blast furnace. This general summary led to interesting and valuable discussion on the various economic, ore-dressing, and blast-furnace problems in large-scale development of beneficiation. Perry Harrison described recent developments in sintering and the properties of iron ore sinter. T. B. Counselman and W. H. Coghill discussed the merits of classification of iron ore previous to tabling. Robert Faulkner and J. E. Little described the beneficiation plant of the Bethlehem Steel Corporation.

Jan 1, 1931

By H. F. Yancey, M. R. Geer, C. L. Allyn, R. H. Eckhouse

W. M. Bertholf—This is an excellent report of a well-conducted investigation, of sufficient scope to provide generally useful information. Some years ago we had occasion to test the Humphreys spiral on the middling from our table plant. The conclusions reached in this investigation come as no surprise to us. In certain applications it is virtually impossible to improve on the spiral from the monetary returns point of view even though its "efficiency" may be low. We have noted that in all successful applications of the spiral the feed is "classified," hence we were somewhat disappointed in the showing the spiral made on the Poplar Ridge coal, the only one of the four which could really be considered the equivalent of a classified feed. As was noted in the paper, however, this coal contained a considerable amount of middle and high-gravity material, apparently more than enough to make up for the theoretical advantage of small particles in these categories. A comparison of particle size in the various specific gravity classes of the four coals is given in table XXV. Table XXV. Comparison of Particle Size in Various Specific Gravity Classes. (Unit size, 150 m to 0.105 mm) Black Eagle Clements Poplar Ridge Rosly,n 1.3 Float 7.47 10.60 8.68 9.66 1.3 x 1.4 7.89 7.96 7.58 8.20 1.4x1.6 7.24 8.36 5.58 6.85 1.6 x 1.8 7.98 8.31 3.42 7.33 Sink 1.8 7.85 7.13 5.09 7.41 Avg 7.69 10.08 7.15 8.38 This tabulation indicates that there was very little difference in the size of the various gravity fractions for three of the coals, Poplar Ridge varying the most. Examination of figs. 3, 6, 7, and 8 reveals a general similarity of behavior for all coals except Black Eagle. Would the authors care to speculate on the reasons for the difference in the distribution curve for the sink 1.60 material in the washed coal of fig. 3 as compared to the others? This difference is particularly noticeable in the 8xl4-mesh size. Was there a "shape effect"? J. D. Price and W. M. Bertholf—The performance data on three of the coals studied appear to be typical, but there are certain departures from the general pattern in the case of the Poplar Ridge coal which are large enough to deserve special consideration. For example: 1. Despite the high proportion of sink 1.60 material in the feed, it was not possible to make a corresponding proportion of high-ash reject. (See table XVI.) 2. Even though approximately 70 pct of the feed was 1.40 float with an ash content of 6.6 pct, and this

Jan 1, 1951

By R. H. Eckhouse, M. R. Geer, H. F. Yancey, C. L. Allyn

W. M. Bertholf—This is an excellent report of a well-conducted investigation, of sufficient scope to provide generally useful information. Some years ago we had occasion to test the Humphreys spiral on the middling from our table plant. The conclusions reached in this investigation come as no surprise to us. In certain applications it is virtually impossible to improve on the spiral from the monetary returns point of view even though its "efficiency" may be low. We have noted that in all successful applications of the spiral the feed is "classified," hence we were somewhat disappointed in the showing the spiral made on the Poplar Ridge coal, the only one of the four which could really be considered the equivalent of a classified feed. As was noted in the paper, however, this coal contained a considerable amount of middle and high-gravity material, apparently more than enough to make up for the theoretical advantage of small particles in these categories. A comparison of particle size in the various specific gravity classes of the four coals is given in table XXV. Table XXV. Comparison of Particle Size in Various Specific Gravity Classes. (Unit size, 150 m to 0.105 mm) Black Eagle Clements Poplar Ridge Rosly,n 1.3 Float 7.47 10.60 8.68 9.66 1.3 x 1.4 7.89 7.96 7.58 8.20 1.4x1.6 7.24 8.36 5.58 6.85 1.6 x 1.8 7.98 8.31 3.42 7.33 Sink 1.8 7.85 7.13 5.09 7.41 Avg 7.69 10.08 7.15 8.38 This tabulation indicates that there was very little difference in the size of the various gravity fractions for three of the coals, Poplar Ridge varying the most. Examination of figs. 3, 6, 7, and 8 reveals a general similarity of behavior for all coals except Black Eagle. Would the authors care to speculate on the reasons for the difference in the distribution curve for the sink 1.60 material in the washed coal of fig. 3 as compared to the others? This difference is particularly noticeable in the 8xl4-mesh size. Was there a "shape effect"? J. D. Price and W. M. Bertholf—The performance data on three of the coals studied appear to be typical, but there are certain departures from the general pattern in the case of the Poplar Ridge coal which are large enough to deserve special consideration. For example: 1. Despite the high proportion of sink 1.60 material in the feed, it was not possible to make a corresponding proportion of high-ash reject. (See table XVI.) 2. Even though approximately 70 pct of the feed was 1.40 float with an ash content of 6.6 pct, and this

Jan 1, 1951

[MINING AND EXPLORATION DIVISION Established as Mining, Geology and Geophysics Division, Sept. 27, 1949 Name changed February 19, 1958. Lyman H. Hart, Chairman Robert J. Lacy, Assistant Chairman Vice Chairmen: John C. Wangaard, Membership J. M. Ehrhorn, Program John G. Hall, Publications C. E. Nelson, Secretary American, Smelting and Refining Co. 120 Broadway New York 5, New York Editor, Rock-in-the-Box: J. W. Chandler.]

Jan 1, 1961

By D. Turnbull, A. M. Turkalo

It is well known that if copper that has been severely cold-worked by rolling (70-98 pct) is heated to high temperatures a small number of large grains are formed at the expense of the fine grained structure that appears upon primary recrystallization. Dahl and Pawlek,' Cook and Mac-Quarie,2 Ward,3 and Boas and Bowles4 have studied this phenomenon in copper. It has been reported as taking place with measurable velocities in the temperature range 700-1080". Boas and Bowles have reported that the time necessary for the transformation is of the order of days at 700°C. According to Ward3 the number of secondary grains which appear in OFHC copper decrease with increasing perfection of cubical alignment after primary recrystallization; also the perfection of cubical alignment increases with decreasing grain size prior to the final reduction. In this investigation two heats, A and B, of especially high purity copper (99.999 pct) supplied by the American Smelting and Refining Co., were used. The behavior of samples prepared from the two heats was qualitatively very similar providing that the grain sizes established prior to the final reduction were about the same. We observed that in specimens prepared from bars which were relatively coarse grained prior to final reduction secondary recrystallization took place at a rapid rate at temperatures as low as 500°C. This is about 200-300°C lower than the temperature necessary to obtain fairly rapid transformation in OFHC copper. A 0.22 in. thick rectangular bar of lot B was cold-reduced 60 pct by straight rolling and given a penultimate annealing treatment at 250°C. Following this it was cold-reduced 90 pct and heated to various temperatures in the range 450-1040°C. The specimens were about 8 mils thick

Jan 1, 1950

By Augustus Locke

I WISH to urge on this Committee the task of evaluating mining geology. -My motive is as follows: It, is a. duty of the Institute from time to5 time, to establish the social perspective of the professions grouped within it, not simply to promote their use, but to determine with engineering definiteness their true powers and functions. This becomes the delegated duty, therefore, of this committee in respect to geology. Be- cause my own subject is mining, I shall confine my remarks to mining geology. But I believe that the evaluation should be made to include all of that geology termed economic. The perspective for such evaluation is shown in the nature of the public support given to geology. The federal Geological Survey, the leading organization on the economic side, is actuated by the zeal of a small group of devoted professionals who consider its work valuable, ' It proceeds, however, on a starvation ration of appropriations, and that implies that neither the corporations, the voters nor the vote getters consider it important. Altogether, in' the public consciousness, geology is negligible. That, at the same moment, .the profession should act with full confidence, while everyone else should act' with opposite motives, is not fitting. For us, as a committee, to remain incurious regarding such a disparity of beliefs is quite impossible.

Jan 1, 1931

By J. J. Hauser, H. C. Theuerer

A cathode sputtering technique is described which elin7inates the need for ultrahigh vacuum in preparing thin films of materials sensitive to gaseous impurities. This technique uses a fraction of the atoms sputtering within an anode container to getter actice gases, such as HzO, Oz, and Nz. The gases alzd gettering metal are deposited on the container walls, thus shielding the coating zone of the system from contamination. The use of the method for preparing superconducting-normal metal couples such as Ph-Cu and Ph-Pt is described, and the properties of the individual and composite films are given and discussed. GETTER sputtering is a method which greatly simplifies the preparation of thin films in cases where composition control is critical. A major difficulty with conventional sputtering and other vacuum-deposition techniques is the contamination of the forming film caused by residual gases, such as H20, CO, Oz, and Nz, in the coating equipment. The difficulty arises from the fact that even when the residual pressure in the system is as low as 1 x 10"6 Torr, with a deposition rate of 10A per sec, there are as many contaminating gas collisions with the substrate as there are with film-forming metallic atoms. It is not surprising, therefore, that with reactive metals, such as tantalum and niobium or with semiconductors, such as silicon and germanium, films with properties far different from the starting materials are obtained. In the case of niobium and tantalum, deposited either by sputtering or vacuum evaporation in systems with reactive gases at pressures of the order of 1 x l0-' Torr, the loss of superconductivity is traceable to interstial oxygen or nitrogen. On the other hand, working in vacuum of the order of 1 x l0-" Torr, Marchand and enema' have shown that superconducting films of tantalum with properties approaching those of bulk material are possible. At this level of gaseous impurities -lo6 metallic atoms arrive at the substrate before a contaminating collision occurs again assuming a deposition rate of 10A per sec. It is evident from the above that any successful vacuum technique requires the elimination of reactive gases from the region of the system where coating is occurring. Getter sputtering accomplishes this using conventional vacuum equipment with residual pressures in the 106 Torr range. In fact? vacuum systems with residual pressures of lo-" Torr are adequate for most purposes. With this method, sputtering is confined within an anode can and, by geometric design, sputtering itself is used to purify the argon at the lower and upper parts of the system by the gettering action of the reactive metal. In consequence, the central region of the system where coating occurs is shielded from gaseous contamination. Getter sputtering is particularly useful for the preparation of alloy and compound films. With this method, if a cathode of homogeneous composition is bombarded with high-energy argon ions, transfer of material to the substrate having the same composition as the cathode will occur. This is true after an initial equilibration time, even though the constituents of the cathode may have different sputtering rates. During equilibration, the surface of the cathode changes composition due to differences in sputtering rate, but mass conservation demands a steady-state condition such that the atoms sputtered from the surface have the same composition as the cathode material from which the surface is generated. GETTER-SPUTTERING APPARATUS The original form2 of the getter-sputtering apparatus is shown in Fig. 1. It consists of a closed nickel or stainless-steel can 4 in. tall and 2-3/8 in. in diameter. Mounted symmetrically from each end

Jan 1, 1965

By J. W. Onuscheck

The oxygen-fuel oil burner lance is a very useful tool at the Monessen B.O.F. It increases the overall flexibility of the operation. An additional 15,000 to 20,000 ingot tons can be produced at a given hot metal supply. It helps overcome sporadic drops in hot metal thermal values and/or supply. It results in increased yield, in particular, on high carbon heats where much yield was lost on reblow triggered slag reactions. The burner has also been adopted as a standard tool to aid burning in new vessel linings. Overall, steelmaking performance has improved with the use of standard preheat practice. Scrap charges up to 50 percent have been used routinely in times of extreme hot metal shortages, but the performance is weak in some categories. Development of a single step oxy-oil process is in progress. In this process, scrap and hot metal are charged as in the normal B.O.F. practice, but fuel oil is fired with the refining oxygen.

Jan 1, 1972

By AIME

ENGINEERS have long pondered the answer to the question of "How am I doing?" and in large measure the answer from the economics angle is provided by the 1946 survey of the engineering profession now being published by the Engineers Joint Council as an eighty-page bulletin entitled "The Engineering Profession in Transition." The survey, based upon a completely precoded mail questionnaire, aimed at three major objectives: (1) to determine the general impact of World War II upon the profession in the period 1939 through 1946; (2) to obtain re- R liable data from which valid findings could be derived to predict how active the profession would be after 1946; and (3) to determine if the war's upheaval had changed materially the pattern of professional activities, education, background, and earnings from those which existed prior to 1939. Abundant data on the economic status of the engineer based upon years of experience in his particular field, the specific branch of the industry in which he served, and his educational background are presented. Relationships between years of experience

Jan 1, 1947

By G. S. Brooks

(New York Meeting, February, 1913.) THE tendency of the oxides of such metals as aluminum, zinc, chromium, and calcium to form compounds at high temperatures with iron oxide is well established by past investigation. Data of this reaction, as developed in laboratory research, have been contributed by Burleigh, Hofman, and Wells, in America, and by many others abroad. A partial bibliography of the subject is appended. From these authorities we learn that the ferric oxide here has the function of an acid, giving in the case of ZnO a zinc ferrite, with a normal composition of ZnOFe2O3. This formation of zinc ferrite particularly affects the success of such processes as leaching or magnetic separation, and thus becomes practically important to the metallurgist. But the meager existing data do not entirely agree; and quantitative results from muffle-practice are conspicuously absent. Furthermore, it being of some general importance to the zinc smelter in both roasting and reduction, the following few notes of operations on a commercial scale are contributed

Jan 5, 1913

MONTANA LOCAL SECTION Executive Committee F. M. SMITH, Chairman J. L. BRUCE, Vice-Chairman . D. C. BARD, Secretary, Box 267, Butte, Mont. FREDERICK LAIST W. C. SIDERFIN The semi-annual meeting of the Montana Section was held at the Silver Bow Block, Butte, Mont., on Friday evening, Oct. 8, 1915. An informal, subscription dinner, at $1.50 a plate, was enjoyed inn' the early evening, by 62 members and guests. After dinner a technical session was held, and a paper entitled Preliminary Outline of Paper on Mines in the Boulder Batholith was presented by J. A. Grimes, who is joint author of the paper, with Paul Billingsley. The paper elicited a lively and interesting discussion, in which a score of members took part. After the reading of the paper the rest of the evening was spent socially. D. C. BARD, Secretary.

Jan 12, 1915

By R. L. Dietrich

Magnesium alloy sheet has less ability to accept bending at room temperature than most of the heavier metals. In work designed to improve the bend properties, the preferred orientation of the sheet is of major importance as it is in all studies of the properties of wrought magnesium products. When rolled into sheet, all of the common magnesium alloys form an orientation texture having the basal (002) planes approaching parallel to the surface of the sheet. This texture is only slightly affected by annealing. Magnesium single crystals are highly anisotropic, and, as might be expected, so are magnesium alloy wrought products in which a strong preferred orientation is developed. It is therefore not surprising that bend properties are affected by orientation. Ansel and Betterton1 reported that the orientation of AZ3lXt sheet varies from surface to center and that bend properties are improved by etching away the sharply oriented material at the surface of the sheet to reach the more broadly oriented structure below. This paper covers a study of that orientation, either during the rolling process or by treatment of the finished sheet, in an effort to improve the bend properties and toughness of sheet. Literature The orientation texture of magnesium and magnesium alloy sheet has been studied extensively. Early determinations2 showed that pure magnesium sheet has a preferred orientation in which the basal planes are parallel to the sheet surface within very narrow limits. J. C. hIcDonald3 and J. D. Hanawalt4 reported that sheet containing a small amount of calcium develops a "double" texture, that is, the majority of the basal planes are a few degrees from parallel to the surface and there is a noticeable vacancy at the parallel position. Bakarian5 made careful quantitative pole figures of both pure magnesium sheet and MI alloy SEPTEMBER 1949 sheet which show these features. In all of these studies, however, the orientation was determined by transmission methods in which the resulting pattern is an average through the thickness of the sheet. The tendency of wrought metal to exhibit a different orientation at the surface from that in the center has been reported by many investigators. G. von Vargha and G. Wasserman6 found that with copper, aluminum, iron, and brass the textures of rolled compared to drawn wires were the same at the center but differed markedly at the surface. It was also reported by investigators7 that the orientation of rolled aluminum varies from surface to center. Har-greaves8 found that the surface texture of AM503 (magnesium alloy similar to MI) sheet was different from the center texture. It is reported by Edmunds and Fuller9 that zinc alloy sheet sometimes had a thin layer at the surface with a strong orientation of the basal planes parallel to the surface, which, if present, impaired the bend properties of the sheet. Part1 Surface Orientation ofMag- nesium Alloy Sheet and the Effect on Properties Attempts to correlate the bend properties of magnesium alloy sheet with tension ductility over short gauge lengths proved unsuccessful and the subsequent investigation showed that nonuniformity in orientation is a con- tributing factor as the properties of the surface material have a much more important effect in bending than in tension. A program to study the relationship between surface orientation at the surface and bend properties was then undertaken. First, the effect of etching away the surface of sheet on the bend properties and the orientations at the various depths were studied. Sheet samples of M1, AZ31X, and AZ61X were etched in dilute nitric acid to remove the surface material for various depths to 0.015 in. As may be seen in Table 1, the minimum bend radius improved considerably as the surface layers were etched away but it was necessary to etch the sheet quite deeply, much more so than was found necessary by Edmunds and Fuller9 on zinc sheet. It is also apparent that the amount of etching required is a function of the sheet thickness. In all of this work, radii were measured as R/t, the radius divided by the sheet thickness, in order to eliminate the effect of the reduction in sheet thickness produced by the etching. To determine the orientation texture of the sheet, X ray reflection patterns were taken using copper radiation with the bearn striking the specimen at an angle of 17' to the surface, which is the Bragg angle for the (002) planes of magnesium. Two exposures were made of each specimen, one with the beam perpendicular to the rolling direction and the other with the beam parallel to the rolling direction. The symmetry of the preferred orientation in magnesium sheet is such that these two photographs gave an approximation of the pole figure sufficiently accurate for qualitative work and it was not thought worthwhile to make complete pole figures. These X ray patterns show that the orientation has a much narrower spread at the original surface of the sheet than below the surface. The narrow spread is found in sheet having the majority of the basal planes (002) parallel to the surface, and since this is an unfavorable position for slip, it is

Jan 1, 1950

By Eugene Guccione

FOREWORD-In an interview published in the May 1975 issue of MINING ENGINEERING, one of the world's most respected scientists, nuclear physicist Hans Bethe discussed the reliability of nuclear power plants and their unmatched safety record. The Nobel laureate also refuted the anti-nuclear lobby's claims that nuclear plants emit harmful radioactive effluents. When asked whether the US has sufficient uranium resources, Dr. Bethe replied that "it depends on the time of introduction of the commercial and advanced breeder reactors which, in effect, can generate more nuclear fuel than they consume." The United States has enough U3O8 to last until the breeders can take over in 1995, said Dr. Bethe. But lie warned that extensive environmental damage would be caused if "environmentalists" succeed in delaying the development of the breeder. Any such delays, he noted, would vastly increase the demand for U3O8 in conventional reactors; this, in turn, would impose an immense burden on the US uranium mining industry, which would then have no alternative but to mine the low-grade Chattanooga deposits.

Jan 4, 1977

By R. W. Fountain, M. Korchynsky

The precipitation phenomena occurring in cobalt-tantalum alloys have been investigated in the temperature range frm 500" to 1050°C by correlating the results of metallographic, X-ray, micro-and macrohardness, and electrical resistivity studies. The property andmacrohardness,changes were found to depend on 1) general precipitation, and 2) lamellar precipitation. Two new intermetallic phases have been identified: 1) a Co3Ta, a metastable ordered face-centered-cubic compound, and 2) a stable ß Co3Ta phase of hexagonal structure. In addition, the previously reported Co2Ta phase was found to exist in two allotropic modifications: the hexagonal MgZn,-type and the cubic MgCu2-type Laves phases. SINCE a large variety of structures can result as a consequence of the decomposition of a solid solution, predictions on the nature of property changes are difficult, if not impossible, to make. For any rational attempt to correlate properties and structures of a precipitation-hardenable alloy, a detailed understanding of the kinetics of decomposition and morphology of phase separation, as well as knowledge of phase relationships, appears to be prerequisite. Information of this type has been accumulated in the past for many alloy systems, both of theoretical and pastforpractical importance.1,2 Although the presence of intermetallic compounds has been reported in cobalt-base alloys,3 the amount of published information on precipitation-hardenable cobalt-base systems is very limited. A survey of the binary phase diagrams of cobalt indicates that cobalt-tantalum alloys might be of interest as typical of other cobalt-base systems in which Laves phases of the A,B type can be precipitated from solid solution. The present work has been undertaken, therefore, to study the kinetics and morphology of the precipitation reaction in this system and to establish a base for a correlation between the structural aspects and properties in this class of alloys. PREVIOUS WORK The only available phase diagram of the cobalt-tantalum system is based on the work of Koster and Mulfinger. According to these authors, the maximum solubility of tantalum in cobalt is about 13 pct (at 1275°C) and. less than 7 pct at room temperature. Tantalum additions lower the temperature of allotropic transformation of cobalt (about 420°C), and at 7 pct Ta, the high-temperature face-centered-cubic modification (ß cobalt) is retained at room temperature. The precipitating phase was originally designated as Co5Ta2 compound (55.2 pct Ta, about 1550°C melting point), but subsequent investigations by wallbaum5" identified this constituent as the A,B-type Laves phase. Wallbaum's data indicate that there are two modifications of this intermetallic compound: one richer in cobalt (Co2.2 Tao.8)of the hexagonal MgNi, type; and another of a higher tantalum content (Co2Ta) of the cubic MgCu, type. On the other hand, Elliott7 found that the cobalt-rich alloy (CO2.10,Tao.~l) was predominantly the cubic MgCu, type at 800°C and a mixture of both the MgCu2 and the hexagonal MgZn,-type Laves phases at 1000°C. At 1200°C, Elliott found only the MgZn, type while at 1400°C, he observed only the MgCu2 type. At the stoichiometric composition, Co2Ta, Elliott reported only the cubic MgCu2-type Laves phase in the temperature range of 600oto 1600°C. The precipitation of the cobalt-tantalum intermetallic compound is accompanied by a marked increase in hardness. According to Koster's4 data, the Brinell hardness of an 8 pct Ta-Co alloy increases from 230 to 340 upon short-time aging at 800°C. EXPERIMENTAL PROCEDURE The binary cobalt-tantalum alloys investigated contained 5, 10, and 15 pct Ta. The range of tantalum additions was thus slightly broader than the reported minimum and maximum solid solubility limits of tantalum in cobalt (7 and 13 pct, respectively)4 The alloys were vacuum-induction melted in a magnesia crucible using cobalt rondelles and technically pure tantalum sheet as raw materials. Deoxidation of the melt was accomplished with carbon, and the chemical analysis of the alloys is given in Table I. The effect of isothermal aging treatments on the progress of precipitation was studied on samples cut from cast ingots. These samples were solution treated for 2 hr at 1250°C and water-quenched. Aging was conducted in the temperature range from 500" to 1050°C for periods between 15 min and 1000 hr and followed by water-quenching. To prevent contamination from the atmosphere, all samples were sealed in evacuated Vycor or quartz tubes for heat-treatments. For solution treatment, argon at 0.2 atmospheric pressure was introduced prior to sealing of the capsule to prevent collapse at high temperature, and titanium sponge was placed at one end of the capsule to act as a getter. MACROHARDNESS The effect of aging on Vickers hardness (Dph) of

Jan 1, 1960

By Charles C. Hall

The following procedure in estimating mineral oil when mixed with vegetable or animal oils, is the result of a long series of cxperiments based on the method suggested by Sir William Thompson and Mr. A. H. Allen, in a paper read before the Royal Society.* Four to five grams of the oil under examination are weighed out into a porcelain capsule of 75 C.C. capacity. Thirty C.C. of a 10 per cent. solution of potassium-hydrate in alcohol are added, and the capsule covered with a watch-glass is placed in a water-bath heated to about 93' C. The mixture of oil and alkali should be stirred frequently, and after three-quarters of an hour it is boiled with stirring. This will secure the complete saponification of all the vegetable or animal oil. After the boiling has been continued some time, and most of the alcohol is expelled and a thick scum of soap forms on the surface, a little bicarbonate of soda is added to convert the excess of caustic alkali into carbonate. When the contents of the capsule have become pasty an equal bulk of fine, clean sand is stirred in. This makes the soap granular, and facilitates the removal of the last traces of alcohol. The capsule is now heated for two hours more on the water-bath. After cooling, the contents of the capsule are transferred to a short-necked funnel, having a thin plug of asbestos, and washed with petroleum-ether, or some other light petroleum spirit. The ether dissolves out the mineral oil from the soap, and is best collected in a quarter-liter flask having a short neck. The ether can be applied conveniently and effectively by a small washbottle. Care must be taken to effect a complete removal of the oil

Jan 1, 1883

By Herbert W. Graham

IRON ORE is widely distributed throughout the world. Ores sufficiently high in iron content to be practical for the operations of iron and steel making occur in so many places that it is only by the accident of political subdivisions that any given nation does not have adequate and suitable iron ore. Data prepared by various authorities show that in the Lake Superior region alone there are reserves of 1,200,000,000 tons of iron ore of an iron content and at the level of production cost to which the industry has been accus tomed. At an annual consumption of 80,000,000 tons these reserves will last fifteen years. Taken alone these figures would be alarming, but over a considerable period of years the total reserve tonnage has been more or less steadily increased by improvement and extension of mining and beneficiation methods. The rate of depletion of reserves has been only about one third of the rate of consumption. On this basis the cheap high-grade ores of Lake Superior would last 45 years.

Jan 1, 1947