Search Documents

By S. F. Turcotte, B. J. Grierson

At the Q. I. T. ilmenite smelter, nine electric furnaces produce titania slag and iron At high power levels, a furnace requires either a slag or an iron tap approximately once an hour, using rail cars as slag receptacles and ladles for iron. The correct scheduling of taps is an important operational tool due to peak power load and operational considerations. Over recent years, large increases in furnace capacity have imposed severe strains on the product handling facilities. This situation results in loss of production when several taps are bunched, because of an in- ability to handle many taps simultaneously. An on-line computer program has been developed to generate schedules for tapping a single furnace. By improved scheduling, this program can en- large the tonnage of each tap and minimize the number of taps, while reducing traffic congestion and unit cost s. Future plans call for extension of this technique to all nine furnaces with addition of a master scheduling program to optimize the overall traffic flow in the smelter aisle.

Jan 1, 1969

By David B. Reger

The discovery of prolific oil wells in old territory hitherto regarded as doubtful, if not worthless, and the rapid extension of a gas pool opened late in 1938 were the most interesting petroleum features in West Virginia during 1939. Oil activity in general was slow because of crude prices that were still fairly low at the end of the year, although substantially increased above those in January. Fewer oil wells were completed, but the average results were better than in 1938. Fewer gas wells, also, were completed, with greatly lessened average initial production. Many old oil and gas wells were abandoned, so that the total number of active wells has not changed appreciably. The account of operations, as gathered from trade journals and other sources, shows that 561 new wells were drilled, resulting in 101 new oil wells with 2261 bbl. of daily initial production; 366 new gas wells with 602,400,000 cu. ft. of daily open flow; and 94 dry holes. Besides these new wells, 61 old wells were drilled to deeper sands, with 12 bbl. and 13,328,000 cn. ft. of added production. On the new wells the oil average was 22.38 bbl. per well per day; and the gas average was 1,645,900 cu. ft. per well per day; the ratio of dry holes to completions was 16.76 per cent. From an exploratory standpoint one partly discredited oil area was revived by good new production, and another small oil pool may have been opened. Some of the results in gas exploration will require more drilling for true appraisal. It is certain, though, that one very considerable gas field in the sands of Mississippian age has been proved; and there is a probability of six new pools in the Middle Devonian shale. In the Oriskany sand (L. Dev.) the Elk-Poca pool has been extended considerably farther northwest into Jackson County; and farther north in Jackson County two widely separated wells, which may be pool openers, have been successfully completed. On the other hand, several important wildcats in various counties have been dry. Stratigraphically lower, some additional wells have been completed in the Newburg sand (Sil.) and one small producer has been completed in the Clinton sand (Sil.), the importance of which can scarcely be overestimated, because no Clinton production has previously been found in the state, although at least seven wells have been drilled through the sand.

Jan 1, 1940

By David B. Reger

The discovery of prolific oil wells in old territory hitherto regarded as doubtful, if not worthless, and the rapid extension of a gas pool opened late in 1938 were the most interesting petroleum features in West Virginia during 1939. Oil activity in general was slow because of crude prices that were still fairly low at the end of the year, although substantially increased above those in January. Fewer oil wells were completed, but the average results were better than in 1938. Fewer gas wells, also, were completed, with greatly lessened average initial production. Many old oil and gas wells were abandoned, so that the total number of active wells has not changed appreciably. The account of operations, as gathered from trade journals and other sources, shows that 561 new wells were drilled, resulting in 101 new oil wells with 2261 bbl. of daily initial production; 366 new gas wells with 602,400,000 cu. ft. of daily open flow; and 94 dry holes. Besides these new wells, 61 old wells were drilled to deeper sands, with 12 bbl. and 13,328,000 cn. ft. of added production. On the new wells the oil average was 22.38 bbl. per well per day; and the gas average was 1,645,900 cu. ft. per well per day; the ratio of dry holes to completions was 16.76 per cent. From an exploratory standpoint one partly discredited oil area was revived by good new production, and another small oil pool may have been opened. Some of the results in gas exploration will require more drilling for true appraisal. It is certain, though, that one very considerable gas field in the sands of Mississippian age has been proved; and there is a probability of six new pools in the Middle Devonian shale. In the Oriskany sand (L. Dev.) the Elk-Poca pool has been extended considerably farther northwest into Jackson County; and farther north in Jackson County two widely separated wells, which may be pool openers, have been successfully completed. On the other hand, several important wildcats in various counties have been dry. Stratigraphically lower, some additional wells have been completed in the Newburg sand (Sil.) and one small producer has been completed in the Clinton sand (Sil.), the importance of which can scarcely be overestimated, because no Clinton production has previously been found in the state, although at least seven wells have been drilled through the sand.

Jan 1, 1940

By William R. Webster

At the Florida meeting of the Institute, in March, 1895, I presented a Note on a Proposed Scheme for the Study of the Physics of Cast-Iron,1 giving an outline which, for convenience of reference, I here repeat. Suggested Lines for DiScuSsion and IvestiGation. I.—Correspondence between chemical composition and melting-point, fluidity, shrinkage, fracture, chill, micro-structure, and other physical properties. II.—Influence of: 1. Cupola-mixture, use of steel and other scrap, oxidized or clean material, 2. Manner of melting, flux, etc., 3. Casting-temperature, A. Fracture. 4. Manner of handling melted metal and B. Micro-structure. method of casting, C. Physical properties. 5. Size and form of casting, D. Shrinkage. 6 Kind of mold, green sand (under dif- on E. Chill. ferent conditions of ramming, amount F. Residual strew of moisture, and skin-dried), dry sand, G. Condition and quan- loam, and chills, tity of carbon and 7. Rate and mode of cooling castings, other elements. 8. Manner and temperature of heating for annealing, 9. Additions of nickel or aluminum, III. —-Segregation as affected by : 1. Composition ; 2. Casting-temperature; 3. Rate of cooling ; 4. Size and shape of casting. IV. —Blow-holes, their volume and position as affected by: 1. Composition; 2. Casting-temperature; 3. Casting-pressure ; 4. Rate of cooling; 5. Size and ehape of casting ; 6. Special additions. It was hoped that a discussion might thus be elicited, similar in interest and value to the discussion of the physics of steel, which had been so widely and gratefully welcomed by students and practitioners in that department. That this hope was not

Jan 1, 1905

By C. S. Roberts

Microstructural studies of a Mg-10.3 pct Al alloy showed that discontinuous precipitation during aging multiplies the grain boundary area available for easy deformation in elevated temperature creep. An increase of strain rate for a 6.2 pct Al alloy at 400°F, where precipitation and creep are concurrent, caused an increase in the volume percentage discontinuously precipitated at the completion of the process. The relatively poor elevated temperature creep resistance of heat treated alloys of the Mg-AI-Zn type was explained in these structural terms. C resistance of the heat treatable Mg-A1 based alloys is poor compared to that of Mg-Ce based alloys. While the latter show a continuous precipitate, Mg-A1 alloys prefer a discontinuous precipitate at grain boundaries. '.:' It has been concluded that the excellent creep resistance of Mg-Ce alloys was primarily due to the continuous precipitation which especially localized at the grain boundaries.' The purpose of the present investigation was to obtain a parallel correlation, if such exists, between the poor creep resistance and the state of precipitation in Mg-A1 alloys. Discontinuous precipitation produces about three times as many true grain boundaries as originally existed. This microstructure would be expected to have a marked influence in creep, where quantity of grain boundary area is important. Experimental Procedure The two experimental alloys contained 6.2 and 10.3 pct Al. They were made from electrolytic magnesium by alloying under flux and casting in 3 in. diam permanent molds. The ingots were extruded into 1 1/4 x 1/8 in. flat stock under the following conditions: billet preheat 700°F (2 hr), container and die temperature 700°F, speed 3 fpm, and area reduction ratio 45:1. The creep specimens were machined from blanks which had been solution heat treated 24 hr at 770°F and aged 16 hr at 400°F. Attempts were made to control the grain size as closely as possible for extruded stock. The grain size after solution heat treatment was about two thousandths of an inch for the 6.2 and five thousandths for the 10.3 pct Al alloy.

Jan 1, 1957

By N. M. Raju, B. Singh

The paper seeks to present the results of experimentation in room and pillar stopes with different ground conditions to determine the safe working span. In the experimental stopes, ground movement was monitored with gradual widening of the room span. The field measurements included closure between the stope walls and the extent of ground movement in the hangwall using borehole extensometers. hock bolting was used as an exclusive support system which enabled introduction of scrapers for improving productivity. In one nine, phosphate bed, 3 to 3.5 m thick dipping at 45O and overlaid by weak laminated shale, was worked at shallow depth of cover. h the experimental panel, five s topes were worked with spans varying from 5.5 to 7 m. In the second mine, the chalcopyrite orebody up to 6 m in thickness dipping at 25 - 30" was worked at a depth of 1100 m. The hangwall consisted of fairly competent schistose rocks and therefore 10 to 15 m wide spans could be experimented. The field measurements confirmed that in the phosphate mine with weak shale roof, 7 m span could be safely worked with subsequent caving of the bolted roof. In the copper mine, 15 m span could be worked and the stopes required subsequent backfilling for better ground control.

Jan 1, 1983

By H. Siebert, G. Raitt

With the advent of the Interstate Highway Pro- gram, many problems have been encountered in the application of highway design standards to topography, particularly rock cut design. A rigid application of slope ratios with little respect to rock type, dip, foliation, structure and height of cut face is a problem. Generally a slope ratio of ½ : 1 or 63º for shallow cuts and 1/3: 1 or 71º in deeper cuts are used in Connecticut. The deepest cut face constructed recently was greater than 185 ft. With cuts of this size, rock fall and stability become a problem, and a way to reduce the problem is to construct a stable face initially. A search of the literature indicates that adequate information on the construction of stable rock slopes is not available. A major highway contract was awarded in 1962 to Savin Brothers, Inc., in which line drilling on 6-in. centers was required in many portions of the contract where the cut was greater than 60 ft and one or more benches were to be constructed. From the start of the project many variations were attempted regarding slope hole spacing and distribution of explosives in the holes. Rock ranged from a competent granitic gneiss to an incompetent soft graphitic schist. Generally, the roadway alignment was roughly normal to the strike of the foliation having a dip of ± 60º. An important factor affecting construction of rock slopes was the existence of intersecting joints and faults. The spacing used in less competent rock was about one ft on center. Loading of holes was purposely varied. As competency of the rock increased, hole spacing was also increased. Thus, on a different project in similar rock, spacing was kept at 4 ft.

Jan 4, 1966

By E. T. Hayes, A. H. Roberson, M. H. Davies

R. F. Dornagala and D. J. McPherson (Armour Research Foundation, Chicago)—I should like to compliment the authors for a workmanlike job in determining the partial phase diagram of a system comprised of two rnetals which are certainly not easy to work with. We are completing work at Armour Research Foundation on an Atomic Energy Commission-sponsored project for the determination of eight zirconium binary diagrams. Work on the Zr-Cr system has been completed and should be published within the next year. For our work, Westinghouse Grade 3 iodide crystal bar served as the zirconium melting stock. Johnson-Matthey, electrolytic chromium, specially treated for oxygen removal, was employed. The overall constitution of the system determined at Armour Research Foundation is in very good agreement with the present work. We found a eutectic at 18 pct Cr and 1280 °C, somewhat lower than the value reported. This temperature was confirmed by thermal analysis, incipient melting studies, and regular isothermal anneals. The eutectoid was located close to 1 pct Cr and 835°C by metallographic analysis of annealed specimens. Maximum solubility of chromium in /S zirconium was 4.5 pct at the eutectic temperature. Chromium solubility in a zirconium was less than 0.28 pct at all temperatures. We found the compound at 53 pct to melt around 1700°C, with an open maximum, but determined its crystal structure to be hexagonal close-packed (MgZn, type). The lattice parameters were in excellent agreement with those determined by Wallbaum in 1942. The diagrams are in substantial agreement, and .part of the differences are undoubtedly due to the use of different zirconium melting stock. M. K. McQuillan (Birmingham, England)—I read this paper with a great deal of interest, as it covered the same field as some work of my own.' There are a number of points in the present paper on which I would like to comment. First, I should say that I, too, used zirconium prepared by magnesium reduction of the tetrachloride and electrolytically prepared chromium, and melted the alloys in a Kroll-type arc furnace. The purity of my alloys should, therefore, be comparable with the purity of those of the present authors, and any differences in our observations would not be expected to be attributable to this cause. The differences between my observations and theirs concern the presence of the eutectic, the temperature of the eutectoid, and the melting point of the compound. I would be very much interested in any further evidence the authors may have for the occurrence of the eutectic at 1380°C. During the course of my work I noted that a number of my alloys containing 60 to 90 pct Zr melted at about 1400 °C, and for a time assumed that a eutectic occurred at this temperature as described in the paper. On further investigation, however, I found that the structures of the as-melted alloys could not be made to fit in with this interpretation of the system. If a eutectic exists in this region of the system it would be expected that the as-melted alloys would show the usual type of cast structure, i.e., dendrites of the compound plus eutectic. This, however, does not occur, as may be seen from Fig. 9. The compound seen there is not dendritic in form, and the remaining material is by no means certainly eutectic. It may be argued that a compound such as ZrCrl would not form dendrites but would tend to crystallize in geometric shapes. In this case, however, I have evidence to the contrary, as on the chromium side of the compound, where a eutectic occurs at about 1545"C, the compound formed from the liquid takes on a conventional dendritic form, and the eutectic is observed in the interdendritic spaces in the usual way. There is no reason to suppose that the compound would behave differently in an alloy lying on the zirconium side of the compound composition if a eutectic existed there too.

Jan 1, 1953

By H. E. Cline, T. H. Alden

A study zvas made of rate-sensitive plastic deformation and superplasticity in alloys of lead and tin. These alloys (lead, PO-19 pct Sn, Sn-38 pct Pb, Sn-2 pct Pb, tin) were extruded, aged at room temperature, or melted and resolidified to produce a variety of ~nicrostrnctures. Flow stress us strain rate data were obtained frorn tension tests for strain rates between 10-6 and 1 min-1. The curve log o .us log £ was S-shaped jor fine-grained materials and approxinzately linear for coarse-grained nzaterials. At constant grain size, the behavior was relatively insensitive to conposition. High rate sensitivity (d log o/d log k) and superplasticity occurred at intermediate strain rates in fine-grained materials and are believed to be associated with a transition with strain rate in the mode of plastic flow. This transition was shifted to higher strain rates with increasing temperataire or decrensing grain size. The high rate rneclzanisrn is presunzed to be slip, while rnetallographic evidence sug-gests that the low rate lnechanism is pain boundary sliding. PEARSON' discovered that extruded eutectic alloys of Pb-Sn and Bi-Sn could be elongated as much as 2000 pct in tension. The ability for stretching decreased with aging time or annealing to increase the grain size. At high strain rates, or if the material was in the cast condition, normal ductility was observed. Following deformation of the extruded Pb-Sn eutectic at low rates, Pearson observed an equiaxed granular structure on an initially flat surface, while rapid straining produced elongated grains. He attributed the large deformation in the extruded alloys to the persistence of extremely small grains to a temperature sufficiently high for inter granular flow. Avery and backofen2 measured the strain rate sensitivity of the flow stress, m = d In old In 6, in the Pb-Sn eutectic and established a correlation between m and the tensile elongation. In the extruded eutectic alloy the strain rate sensitivity was 0.1 to 0.2 at rapid rates and the elongation was small, while at low rates m increased to 0.4 to 0.6 and superplastic elongation was observed. They also noted a grain size effect. In the case of the cast Pb-Sn eutectic the strain rate sensitivity remained at 0.1 over the range of strain rates of their experiment (3 x 10"3 to 2 min-I). These authors suggested that diffusional (Nabarro-Herring) creep was the mechanism by which deformation occurred at low strain rates, while climb-controlled creep occurred at high rates. Two predictions of this model are that, at low strain rates, the strain rate sensitivity approaches 1, i.e., Newtonian viscosity, and that the strain rate at constant stress varies as D/L2, where D is the coefficient of self-diffusion and L the grain size. More recently, a mechanical and microstructural investigation of the dilute superplastic alloy, Sn-5 pct Bi, has been done.3 The results show that the high strain rate sensitivity is associated with a transition with strain rate of the mechanism of plastic flow. At low strain rates, grain boundary sliding and its associated accommodation processes were evident, while at high strain rates quasi-uniform slip was concluded to be the dominant deformation process. The following experiments were performed to extend our knowledge of the phenomena of superplasticity to a larger range of strain rates, compositions, temperatures, and microstructures in the Pb-Sn alloy system. The question of why a cast structure does not exhibit viscous behavior although it appears to have a fine microstructure2 was investigated.

Jan 1, 1968

By Charles S. Barrett, F. W. Steadman

DEFORMATION bands of surprising regularity are found in large-grained polycrystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron' and brass.2.3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,5 and Brick and Williamson,3 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others,6 although the orientation (110) [112]-that is, (110) parallel to the rolling plane and [112] parallel to the rolling direction-is generally recognized as the most prominent orientation and (I12) [111] one of the lesser orientations. Other orientations have been given by some observers as (236) [533], (100) [001], and (I 10) [001]. The texture of copper has also been described as (135) [533].6.1 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,1 and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [113] and (110) [117] are about equally stable. MATERIALS AND METHODS The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slices 1/2 in. thick and 2 1/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By John Crawford

MUCH has been written of late regarding the flotation of coal as a means of reclaiming the valuable portion of the fines encountered in nearly all methods of coal preparation. Whether the process be wet or dry, whether the dust be sent through the entire process or removed prior to the cleaning by some such method as screening or aspiration, one of the final products consists of a considerable proportion of -48-mesh material. The percentage of this -48-mesh material depends upon the mining method, transportation, storage, and method of preparation. The ton-nage of this dust material ranges from 1 to 10 per cent of the total output of the cleaning plants. Four methods of disposal are available for this coal: 1. Disposal with the refuse from the plant. 2. Addition, after being reclaimed from the wash water, or dust collectors, without cleaning to the larger sizes. 3. Separate disposal as a pulverized fuel. 4. Cleaning so that addition to the larger sizes benefits the product as a whole. It is also true that flotation in one form or another is the only known way to effectively clean this material. While some processes do a reason-able cleaning job down to and including +100 mesh, by far the greater-majority stop at or short of the +48-mesh size.

Jan 1, 1935

By William M. Brewer

Since writing the paper on this subject,* which was presented at the Atlanta meeting in October, 1895, I have had opportunity for more thorough investigations in several localities, and venture, therefore, to offer some additional facts and opinions. The literature of the subject is not very abundant. Dr. George F. Becker's " Reconnaissance of the Gold-Fields of the Southern Appalachians "† contains some brief notes relating to Georgia, but does not include Alabama. The paper of Messrs. Nitze and Wilkens on " Gold-Mining in the Southern Appala-

Jan 1, 1897

By J. B. Cohen

EARLY investigators1-4 reported that additions of beryllium to silver caused embrittlement. The in-termetallic phases which are now known to exist5,' were not known at the time. Solidification appeared to occur by a simple eutectic reation.4,7 (The primary beryllium-rich phase appeared globular, when the liquidus temperature was near the melting point of pure beryllium, and angular when the liquidus was much lower; in discussion of Sloman's work,4 it was suggested that this difference was due to an intermetallic compound which was not revealed by the polishing technique.) In the investigation reported here, it was found that if the compounds now known to exist were avoided, certain beryllium-silver alloys containing large amounts of the primary beryllium phase possessed sufficient ductility to be cold formed. Alloys containing 14 and 20 at. pct Ag were prepared from vacuum-cast beryllium containing 1.0 to 1.2 pct impurities and silver, 99.99+ pct pure. The elements were melted together by induction in beryllia or alumina crucibles under argon at less than 1 atm pressure. The cooling rate was adjusted by regulating the temperature of the melt and by reducing the power to zero without stopping the water flow in the induction coils, which were in contact with the crucible. Ingots were about 0.75 in. in diam with a grain size of 0.12 to 0.25 in. Microscopic investigation of transverse or longitudinal sections of an ingot cast from a temperature well above its melting point showed that, in general, the compounds did not form, presumably because of rapid cooling; the alloys consisted of beryllium-rich particles in a silver-rich matrix as shown in Fig. 1. A eutectic structure was not observed, probably .due to the low beryllium concentration of the eutectic composition and eutectic divorcement. Within a given grain, the small globules of the primary phase were all oriented in the same direction, as indicated by examination under polarized light; the orientation varied from grain to grain. This suggested that the globules were branches of the same dendrites. If cooling was too slow, a third constituent was observed in the microstructure; because it formed around the primary beryllium-rich globules it was Fig. 1—Ag-Be alloy, 18.6 at. pct Ag, as-cast. Bright field illumination. Etched with an aqueous solution of NH,OH and H2O2. X500. Reduced approximately 21 pct for reproduction. probably the 6 compound. A thin ring around an ingot often contained this constituent. When this compound was present in large quantities, or the silver segregated so that large regions occurred with the beryllium-rich globules in contact, sections from the ingot were brittle. When the compound was initially absent, it was possible to carry out reductions in thickness of 50 pct by cold rolling with only limited edge cracking; failure did not occur until reductions of 80 pct. A typical cross section after cold rolling is shown in Fig. 2. After simple bend tests, microcracks were found; these apparently were difficult to propagate in the two-phase structure, as the specimens continued to behave in a ductile manner after the cracks appeared. Similar cracks would probably be closed during rolling. It is apparent in Fig. 2 however, that the primary beryllium particles undergo extensive plastic deformation. Hardness values of the alloys indicated that some work-hardening occurred during cold working. Fig. 2—Ag-Be alloy, 18.6 at. pct Ag, reduced 83 pct in thickness by cold rolling. Bright field illumination. Etched with an aqueous solution of NH,OH and H2O2. X500. Reduced approximately 21 pct for reproduction.

Jan 1, 1961

By Vittal S. Bhandary, B. D. Cullity

Swaged iron wire has a cylindrical {001} <110> texture. The texture is also cylindrical after re-crystallization in the absence of a magnetic field, but <111> and <112> components are added to this texture when recrystallization occurs in a field. The mecizanical properties in tension and in torsion are not greatly altered by these changes in texture. AS shown in a previous paper,1 cold-worked wires of the two fcc metals copper and aluminum can be made relatively strong in torsion and weak in tension, or vice versa, by proper control of preferred orientation (texture). The deformation texture can be controlled by selection of the starting texture (texture before deformation), because certain initial orientations are stable during deformation. The present paper reports on similar work performed on bcc iron. In this case it was clear at the outset that there was no hope of controlling the deformation texture, which is one in which <110> directions are aligned parallel to the wire axis. (1t has usually been regarded as a fiber texture, but Leber2 has recently shown that it is a cylindrical texture of the type {001} <110>. In either case, <110> directions are parallel to the wire axis.) There is general agreement on this texture among a large number of investigators, which in itself suggests that the starting texture has no influence on the deformation texture. More direct evidence was produced by Barrett and Levenson,3 who reported that iron single crystals of widely varying initial orientations all had a single <110> texture when cold-worked into wire. Thus <110> is a truly stable end orientation for iron and probably for other bcc metals as well. Under these circumstances attention was directed to the possibility of controlling the recrystallization texture. This texture is normally <110> in iron,4 just like the deformation texture. However, it is conceivable that this texture could be modified by a proper choice of the time, the temperature, and what might loosely be called the "environment" of the recrystallization heat treatment. In the present work the environmental factor studied was a magnetic field. The effect of heating in a magnetic field ("magnetic annealing") on recrystallization texture has been investigated by Smoluchowski and Turner.5 They found that a magnetic field produced certain changes in the recrystallization texture of a cold-rolled Fe-Co alloy. The texture of this material is normally a mixture of three components, and the effect of the field was to increase the amount of one component at the expense of the other two. Smoluchowski and Turner concluded that the effect was due to magnetostriction. With the applied field parallel to the rolling direction, the observed effect was an increase in the amount of the texture component which had <110> parallel to the rolling direction. In the Fe-Co alloy they studied, the magnetostriction is low in the <110> direction and high in the <100> direction. Thus nuclei oriented with <110> parallel to the rolling direction will have less strain energy than those with <100> orientations and will therefore be more likely to grow. In a later paper on the same subject, Sawyer and Smoluchowski6 ascribed the effect to magneto-crystalline anisotropy and made no mention of magnetostriction. In the papers of Smoluchowski et al. the intensity of the magnetic field was not reported but it was presumably large, inasmuch as it was produced by an electromagnet. In the second paper6 it is specifically mentioned that the specimens were magnetically saturated. But if magnetostriction has a selective action on the genesis of stable nuclei during recrystallization, that selectivity must depend only on differences in magneto-strictive strains between different crystal orientations and not on the absolute values of those strains. Thus the saturated state does not necessarily produce the greatest selectivity, because the relative difference in magnetostrictive strains between different crystal directions may be larger for partially magnetized crystals than for fully saturated ones.7 In the present work the specimens were subjected to relatively weak fields (0 to 100 oe) produced by solenoids. MATERIALS AND METHODS Armco ingot iron rod (containing 0.02 pct C and 0.19 pct other impurities) was swaged from 0.25 in. in diam. to 0.05 in., a reduction in area of 96 pct. The mechanical properties in tension and torsion were measured as described previously.&apos; Textures were measured quantitatively with chromium or iron radiation and an X-ray diffractometer,8,1 and

Jan 1, 1962

By John L. Miles

John L. Miles (Arthur D. Little, 1nc.)—Pollack and orris" have reported measurements on electron tunneling through A1-A12O3-A1 sandwiches in which the oxide was formed by gaseous oxidation in a glow discharge. From these measurements they deduced the asymmetry of the barrier and, since this is small, conclude that the mechanism suggested by Mott19 for the growth of oxide in thin A12O3 films is inapplicable. In earlier papers20 Pollack and Morris report similar work for oxide films grown thermally. In this case they find a greater asymmetry and conclude that the Mott mechanism is valid. I would like to point out that both these conclusions are quite unjustified. Mott suggests that the growth of the oxide film on aluminum results from the passage of ions through the already present film of oxide under the action of an electric field. This field results from a constant voltage which is in effect a contact potential between metal on one side of the barrier and adsorbed oxygen ions on the other side of the barrier. The theory does not require that the oxide grown is nonuniform either in stoichiometry or structure. It does however specifically assume that the partial layer of ionized oxygen on the surface remains adsorbed on the surface of the growing oxide. In other words, the so-called "built-in field" remains in the oxide only as long as the ionized oxygen is present. When a counter electrode of aluminum is deposited on the oxide, it will react with the adsorbed oxygen on the surface of the oxide, thus forming a small additional amount of oxide. It is clear, then, that there is no requirement in the Mott theory of oxide growth which would necessitate tunneling currents through an Al-A1203-A1 sample to be different when the polarity is reversed. Neither does the theory eliminate the possibility that some additional mechanism could cause the tunneling barrier to be asymmetric and hence tunneling currents to be a function of polarity in such a sandwich. Thus these tunneling-currents measurements are not germane to the question of whether the Mott mechanism is the true method of growth of aluminum oxide films. In fact, it is not surprising that there should be a difference between the oxide properties at the two interfaces (with resulting asymmetry in the tunneling barrier) since the growth conditions and growth rates must have been quite different at these two positions. S. R. Pollack and C. E. Morris (authors&apos; reply)— The point raised by Miles above is one has caused some confusion in the past. The following is an attempt to clarify this point. The built-in field which is responsible for the growth of the thermal oxide at low temperatures arises, according to Mott, because of the passage of electrons from the Fermi surface of the oxidizing metal to surface states introduced by the adsorbed oxygen. It is assumed that the energy of these surface states lies below the Fermi energy of the metal. Electrons therefore continue to flow from the metal to the surface until the built-in electric field raises the potential energy of the surface states to the value of the Fermi energy in the metal, at which time equilibrium is obtained between the surface states and the metal. That is in equilibrium as many excess electrons pass from the metal to the surface per unit time as vice versa. The surface of the oxide prior to deposition of a metallic counterelectrode can then be pictured as follows. The Fermi energy lies in the energy gap of the oxide and is essentially pinned at the energy of the oxygen surface states. The vacuum work function of the oxide is then given by the sum of the electron affinity of the oxide (i.e., the difference in energy between the vacuum and the conduction-band minimum) plus the energy difference between the conduction-band minimum and the Fermi energy. The deposition of a metal onto the surface of the oxide can result in a transfer of electrons across the extremely thin oxide only if there is a contact potential difference between the deposited metal and the parent metal or oxide. That is if the vacuum work function of the deposited metal differs from that of the parent metal, then charge can be redistributed across the oxide in order to equilibriate the Fermi energy across the structure. (It should be

Jan 1, 1965

By R. L. Bell, T. G. Langdon

A technique was developed- for determining the grain strain, and hence the grain boundary sliding contribution, occurring during the high- temperature creep of a magnesium alloy, from the distortion of a grid photographically printed on the specimen surface. The results were compared with those obtained from measurements of grain shape, both at the surface and interrwlly, and it was concluded that the grain shape technique may substantially underestimate the grain strain and overestimate the sliding contribution due to the tendency for migration to spheroidize the grains. ALTHOUGH a considerable volume of work has been published on the role of grain boundary sliding in high-temperature creep, many of the estimates of Egb (the contribution of grain boundary sliding to the total strain) have been in error due to the use of incorrect formulas or inadequate averaging procedures.&apos; One of the most easy and convenient measurements from which to compute Egb is that of v, the step normal to the surface where a grain boundary is incident. Unfortunately, this parameter is also the one associated with the treatest number of pitfalls. Values of v have been used to calculate Egb from the equation: egb =knrVr [1] where k is a geometrical averaging factor, n is the number of grains per unit length before deformation, v is the average value of v, and the subscript ,r denotes the procedure of averaging along a number of randomly directed lines. If the dependence of sliding on stress were assumed, it would be possible, in principle, to calculate k from the known distribution of angles between boundaries and the surface. This in itself is difficult because the distribution depends on the history of the surface,&apos; but the problem is even further complicated by the fact that v depends on other factors such as the unbalanced pressure from subsurface grains.3 However, the great simplicity of the measurement procedure for v makes it highly desirable that this problem of k determination should be overcome. In the present experiments, this was achieved by the use of an indirect empirical method in which the grain strain, eg, at the surface was determined by the use of a photographically printed grid. The assumption here is that the total strain, et, is simply the sum of that due to grain boundary sliding, egb, and that due to slip or other processes within the grains, eg. SO that: Et = Eg + Egb [2] Thus k is given by: In practice, it is customary to indicate the importance of sliding by expressing it as a percentage of the total creep strain; this quantity is termed y (= 100Egb/Et). The determination of Eg from a printed grid within the grains avoids the difficulties due to boundary migration which should be considered when the grain strain is calculated from measurements of the average grain shape before and after deformation. As first pointed out by Rachinger,4,5 however, this latter technique has the particular advantage that it can also be applied in the interior of a polycrystal. Recently, several workers have produced evidence on a variety of materials6-&apos;&apos; to support the observation, first made by Rachinger on aluminum,4,5 that 7 can be very high, 70 to 100 pct, in the interior, even when the surface value, determined from boundary offsets, is very much lower.10&apos;11 Although there have been criticisms both of the shortcomings of the grain shape technique&apos;&apos; and of the different procedures used to determine y at the surface,&apos; it seemed important to check whether measurements of sliding by grain shape gave values of y which were truly representative of the material. In the present experiments, grain shape measurements were therefore made both at the surface and in the interior for comparison with one another and with the independent measurements of grain strain using the surface grid technique. EXPERIMENTAL TECHNIQUES The material used in this investigation was Magnox AL80, a Mg-0.78 wt pct A1 alloy supplied by Magnesium Elektron Ltd., Manchester. Tensile specimens, about 7 cm in length, were prepared from a 1.27-cm-diam rod, with two parallel longitudinal flat faces each approximately 3 cm in length. The specimens were annealed for 2 hr in an oxygen-free capsule, at temperatures in the range 430° to 540°C, to give varying grain sizes, and, prior to testing, the grain size of each was carefully determined using the linear intercept method. This revealed that the grains were elongated -0.5 to 5 pct in the longitudinal direction. Testing was carried out in Dennison Model T47E machines under constant load at temperatures in the range 150" to 300°C. At temperatures of 200°C and below, tests were conducted in air with the polished flat faces coated with a thin film of silicone oil to prevent oxidation; at higher temperatures, an argon atmosphere was used. To determine v,, each test was interrupted at regular increments of strain and the specimen removed from the machine. At the lower strains, when v, was less than about 1 pm, measurements were taken on a Zeiss Linnik interference microscope;

Jan 1, 1969

By Arthur Crowfoot

Page IntRodUction ................... The Round Table in Lake Superior Practice .........420 Early Use of Revolving Round Table in Butte District...... Use oF the Round Table at GREat Falls foR Sand-Slime Feed ., . The Round Table for Fine Slime........,.... Construction of Slime Plant at Great Falls..... &apos;..... 424 Tests on Wood, Linoleum, and Cement Decks.........426 Central Feed Apron Removed ....&apos;......... Re-treatment of Round-Table Tailing........... Determination of Conditions for Round-Table Treatment of Slimcs ... 430 Variation in Slope of Round-Table Deck........ ,... The Steel-Frame Cement-Deck Round Table ........ Tests on Cement and Canvas Dock Surfaces ..: ..... Conoidal Deck Round Tables............. Results with Sand-Slime Feed on Conoidal Deck....... Conclusions from Preliminary Tests on Conoidal and Conical Decks ... 446 Discussion of Results of Four-Day Test on Conical and Conoidal Decks . 452 Discussion of Results of Eight-Day Test.......... Qualitative Sampling of Concentrates Across Conical Deck.... Summary of Slime-Plant Practice............ Suggested Flow Sheet for Slime Classification and Treatment.... Conclusion...................467 Introduction The principal object of this paper is 60 presest, data on the development of the revolving convex round table as a concentrator for the through 0.07-mm. slimes from the ores of the Butte district, although some brief notes on the earliest recorded use of this type of concentrating table in the ore-dressing plants of the Lake Superior region and of the Butte district are also presented. The revolving convex round table belongs to the class of concentrating tables known as film-sizing. tables, these tables using the relative transporting power of a film, or thin sheet of water, as it flows over a quiet inclined surface, to separate the minerals of a sorted product. The grains of heavy mineral move down the slope of the table deck slowly, or, in some cases, not at all, after the initial force of the feed entry VOL. XLIX.—27

Jan 1, 1915

By L. F. Bryant, J. P. Hirth, R. Speiser

The surface, gain boundary, and twin boundary energies, as well as the surface diffusion coefficient, of cobalt were determined from tests at 1354°C in pure hydrogen. A value of 1970 ergs per sq cm was calculated for the surface energy, using the zero creep method. It was possible to measure the creep strains at room temperature because the phase transformation was accompanied by negligible irreversible strain and no kinking. Established techniques based on interference microscopy were used to obtain values for the other three properties. The gain boundary and twin boundary energies were 650 ad 12.7 ergs per sq cm, respectively, while a value of 2.75 x l0 sq cm per sec was determined for the surface dufusion coefficient. In the course of a general study of cobalt and cobalt-base alloys, information was required about the surface energy of cobalt. Hence, the present program was undertaken to measure the interfacial free energy, or, briefly, the surface energy, of the solid-vapor interface of cobalt. The microcreep method was selected for this measurement because other surface properties could also be determined from the accompanying thermal grooving at grain boundaries and twin boundaries. A brief summary of the methods for determining the various surface properties follows. At very high temperatures and under applied stresses too small to initiate slip, small-diameter wires will change in length by the process of diffu-sional creep described by Herring.1 The wires acquire the familiar bamboo structure and increase or decrease in length in direct proportion to the net force on the specimen. For a specimen experiencing a zero creep rate, the applied load, wo, necessary to offset the effects of the surface energy, y,, and grain boundary energy, y b, is given by the relation: where r is the wire radius and n is the number of grains per unit length of wire. The first results obtained from wire specimens were reported by Udin, Shaler, and Wulff.&apos; udin3 later corrected these results for the effect of grain boundary energy. The grain boundary energy is determined from measurements of the dihedral angle 8 of the groove which develops by thermal etching at the grain boundary-free surface junction. For an equilibrium configuration: Measurements of the angle 8 can be made on the creep specimens4&apos;5 or on sheet material, as was done in this investigation by a method employing interference microscopy.= If the vapor pressure is low, the rate at which grain boundary grooves widen is determined primarily by surface diffusion and, to a lesser extent, by bulk diffusion. The surface diffusion coefficient, D,, is obtained from interferometric measurements of the groove width as a function of the annealing time, t. As predicted by Mullins~ and verified by experiment, the distance, w,, between the maxima of the humps formed on either side of the grain boundary increases in proportion to if grooving proceeds by surface diffusion alone. For this case: where fl is the atomic volume and n is the number of atoms per square centimeter of surface. When volume diffusion also contributes to the widening, the surface diffusion contribution can be extracted from the data by the method described by Mullins and shewmon.8 Where a pair of twin boundaries intersects a free surface, a groove with an included angle of A + B (using the groove figure and notations of Robertson and shewmong) forms by thermal etching at one twin boundary-free surface junction. If the "torque terms", i.e., the terms in the Herring10 equations describing the orientation dependence of the surface energy, are sufficiently large, an "inverted groove" with an included angle of 360 deg-A&apos;-B&apos; develops at the other intersection. The angles A + B and A&apos; + B&apos; are measured interferometrically. When the angle, , between the twinning plane and the macroscopic surface plane is near 90 deg, the twin boundary energy is calculated from the relation: 1) EXPERIMENTAL TECHNIQUES Five-mil-diam wire containing 56 parts per million impurities was used for making ten creep specimens. These specimens had about 15 mm gage lengths with appended loops of wire and carried loads (the specimen weight below the midpoint of the gage length) ranging from 3.7 to 149.8 mg. The wires were hung inside a can made from 99.6 pct pure cobalt sheet. Beneath the wires were placed small specimens of 20-mil-thick, 99.9982 pct pure cobalt sheet from which the relative twin boundary and grain boundary energies and the surface diffusion coefficient were measured. All the specimens were annealed at a temperature of 1354" i 3°C which is 92 pct of the absolute melting point of cobalt. The furnace atmosphere was 99.9 pct pure hydrogen that was purified further by a Deoxo catalytic unit, magnesium perchlorate, and a liquid-nitrogen cold trap. As a precautionary measure the gas was then passed through titanium alloy turnings which were heated to 280" to 420°C and replaced after every test period. The hydrogen was maintained at a

Jan 1, 1969

By W. L. Chen

The Batac jig was first introduced in the US for fine coal cleaning in 1973 (Tackett, 1977; Hake, 1976). Since then, a total of six such jigs of various sizes have been installed in five US plants for a total capacity of 2346 t/h. The raw coal size ranges from 19 mm x 0 to 9.5 mm x 0-fraction sizes previously fed to heavy medium cyclones, Deister tables, or water only cyclones. Growing interest in the Batac jig as a replacement for the above equipment is due to the following reasons: • Unlike heavy medium cyclones, no magnetite is required. As a result, the operating cost of the plant is reduced. • The compactness of equipment is unique on a unit ton per hour basis as compared to other equipment. • Solid state electronic control of jig stroke length, frequency, and jig bed depth makes the equipment highly efficient. Installations of Batac jigs in the US as of June 1980 are shown in [Table 1]. Use of the Batac jig is even greater outside the US (Anonymous, 1980; Chen, 1980). Its use is not limited to fine coal but is applied to coarse coal as well, with 102 mm size in the feed (Zimmerman, 1975). In countries where consumption of magnetite associated with the heavy medium system of coal cleaning is considered a waste of iron ore resource, the Batac jig is regarded as the primary choice in the selection of cleaning equipment (Chen, 1980).

Jan 1, 1981

COMMITTEE OF ARRANGEMENTS. General Committee.-J. F. Lewis, Quinnimont, W. Va. Committee of Reception at Staunton.-Major Jed. Hotchkiss, Chairman ; W. A. Burke, M. E. Miller, R. N. Catlett, W. J. Nelson, J. T. Effinger, D. A. Kayser. Local Committee of Arrangements.-G. T. Wickes, Low Moor, Chairman; G. W. Bramwell, Stone Cliff, Secretary; J. E. Johnson, Longdale; H. Firm¬stone, Longdale; S. F. Morris, Quinnimont; O. A. Randall, Ferrol; William N. Page, Ansted; F. Lyman, Low Moor; S. M. Buck, Coalburgh; E. S. Hutchinson, Cannelton ; M. F. Maury, Saltpetre Cave. THE opening session of the Institute was held at Staunton, on Monday evening, May 30th, in the Opera House. Major Jed. Hotchkiss, Chairman of the Committee of Reception, called the meeting to order and introduced Mayor Balthis, who spoke a few words of welcome to the members present, and then introduced the Hon. A. H. H. Stuart. Mr. Stuart in addressing a formal welcome to the Institute to the " little city of the mountains," spoke of the value of the services of the mining engineer in developing the mineral wealth of Virginia and in solving the problems of her geological history. Mr. Metcalf, President of the Institute, replied on behalf of the Institute to the cordial welcome of the mayor and Mr. Stuart, and then read an inaugural address on Force. At the conclusion of the President&apos;s address the following papers were read The Electrolytic Determination of Copper and the Formation and Composition of so-called Allotropic Copper, by J. B. Mackintosh, Hoboken, N. J. Read by Professor Egleston. The New Unpublished Map of Chester County, Pa., by Professor Persifor Frazer, Philadelphia. The second session was held at the Opera House on Tuesday morning. The papers read at this session were: Investigations on the Ore Knob Copper Process, by Professor Thomas Egleston, School of Mines, New York city. A Volumetric Estimation of Manganese in Pig Iron and Steel, by F. H. Williams, Vulcan Steel Works, St. Louis, Mo. Read by the Secretary.

Jan 1, 1882