By L. J. Buck

Lead smelting in the ore hearth, first practiced in Europe, whence the traditional name "Scotch hearth, and later developed in America to its present efficiency, is based upon the roast reduction process and is applicable to relatively high-grade galena concentrates. The roast reduction process embraces not only the roast reactions: 2PbS + 70 = PbO + PbSO4, + SO2 PbS + 2PbO = 3Pb + SO2 PbS + 2PbSO4 = Pb + 2PbO + 3SO2 but also, by reason of the addition of extraneous fuel, the reduction reaction: 2PbO + C = 2Pb + CO2 Thus in the ore hearth the roasting of lead sulphide, forming lead oxide and lead sulphate, the reaction of lead oxide and lead sulphate with lead sulphide producing lead, and the reduction of lead oxide by carbon producing lead, go on simultaneously. The Ore Hearth Function of the Ore Hearth.—The ore hearth, through the roast reduction process, provides for the extraction of lead and the immediate disposal of the smelting products—fume, hearth slag and lead, all of which are subsequently treated as follows: the fume is recovered in the flue system and baghouses, mixed with concentrates, and returned to the ore hearth in the form of ore mix; the hearth slag is smelted in a blast furnacc for the further recovery of lead; and the lead is refined and cast into a marketable product. Concentrates Amenable to Ore-hearth Smelting.—Only concentrates that are high in lead content, 70 per cent or more, are ordinarily considered amenable to ore-hearth smelting. Silica should not exceed 2 per cent and iron is allowable only to 4 per cent. These slag-forming constituents occlude both sulphide and mctallic lead, prevent the elimination of sulphur and decrease the lead extraction. Lime and magnesia are beneficial in that both favor a dry slag, promote elimination of sulphur, and prevent occlusions of metallic lead.

Jan 1, 1937

By AIME AIME

LEROY SALSICH has had 37 consecutive years of operating and executive experience in the Lake Superior iron region during 35 of which he has been a member of the A.I.M.E. His recent election as an institute Director to represent the iron and copper country therefore brings to the Board a man long known throughout the area that he represents and well acquainted with the history of the Institute. Mr. Salsich is a native of the area in which his professional life has been spent, having been horn at Hartland. Wis., and graduating from the state university's college of engineering in 1901. A call had come to the college from the Lake Superior Consolidated Iron Mines, at Duluth.

Jan 1, 1938

By AIME AIME

POSSIBILITY of a greatly increased manganese production from domestic source; is indicated by news that the Bureau of Mines has been successful in producing concentrates with high manganese content from the low-grade deposit, in the Las Vegas, Nev.) area. The first unit of the comprehensive group of pilot plants built by the Bureau of Mines at Boulder City, Nev., under a defense appropriation has started operations, demonstrating definitely the applicability of a process developed in the Bureau laboratories. About 12 1/2 lb. of manganese is needed for the production of every ton of steel, and substitution is difficult. The United States produces only about 3 per cent of its total needs of this ore. Only high-grade ore, such as the Russian ore, containing 18 per cent or more manganese, is generally used by American producers in making ferro¬manganese the form in which manganese is usually added in steel manu-

Jan 1, 1941

By John Mathews

IT is twenty years since the writer made his first molybdenum steels and others were making them commercially five years earlier but the prevailing opinion seems to be that molybdenum steels are new; from time to time the daily press speaks of important discoveries in Europe and intimates that American steel makers have much to learn in regard to alloy steels. The earlier experiments were largely confined to the use of relatively high percentages of molybdenum in tool steels and permanent magnet steels. Recent developments deal with the types of alloy structural steels used for airplane, automobile, and other engineering requirements; in these, the molybdenum content is usually less than 1 per cent. The earlier types generally have been unsuccessful commercially, but the newer types of steels are becoming of increasing importance. The war showed our dependence on foreign sources for alloying metals; molybdenum alone is widely distributed in the United States and seemingly abundant. Many deposits are not now of commercial interest, owing to location and relatively small amount of ore available, but other deposits are being developed and a stable source of supply seems well assured. In tool and magnet steels, it was early found that 1 part of molybdenum was equivalent to from 2 to 2.5 parts of tungsten. The permanent magnet steels investigated by Madame Curie,1 in 1898, contained from 3.36 to 4.05 per cent. molybdenum; in 1902, Dr. E. L. French and the writer thoroughly tested steels containing from 2:0 to 4.0 per cent. These steels gave satisfactory tests for permanence, but were low in residual density and much more sensitive to hardening than the corresponding tungsten products. We discontinued work with them, therefore, and have no advice that such steels have been used commercially here or abroad.

Jan 2, 1921

By K. A. Natarajan, I. Iwasaki

With a platinum electrode the Eh-pH response in aqueous systems follows an empirical relation [Eh = E- 0.059 pH](1) where E usually carries a value between 0.8 and 0.9 v. The same potential (E) is observed with a number of other noble metal electrodes in the absence of surface poisoning and of other well-defined redox couples. Many sulfide mineral electrodes also respond in a similar manner in solutions containing their respective ions over wide pH ranges, especially in the alkaline pH region. Such a parallelism between noble metal and sulfide mineral electrodes points to certain implications of their surface conditions, and the flotation and leaching behaviors of sulfide minerals under aerated conditions may be inferred with respect to the foregoing Eh-pH response. Comparison of Sulfide Mineral and Noble Metal Electrodes [Fig. 1] shows the Eh-pH response of pyrite, galena, chalcocite, and pyrrhotite electrodes, reported by Sato, and some experimental points obtained with a platinum electrode in distilled water. [Eq. 1] is seen to be followed by all these electrodes. It is interesting to note that the response of the pyrite electrode as shown is identical to

Jan 1, 1973

Jan 1, 1914

By T. P. Papazoglou, N. A. D. Parlee, W. C. Phelps

PRACTICAL designs for good "home made" molybdenum furnaces are hard to find in the literature. The one described briefly below left something to be desired but was good enough to operate as a rather long (30 in.) two-zone furnace for periods of over 2 months at temperature (1400° to 1600°C) without shutdown. The principal problem in our application was to establish a temperature profile with two distinct constant-temperature zones and no dip between the zones. This and other problems mentioned below would not arise, however, if both zones were operated at the same temperature and if a shorter furnace were acceptable. Since molybdenum windings oxidize very rapidly when heated in air, impervious refractory tubes were used for both the furnace core and the outer jacket tube shown in the accompanying figures. A protective atmosphere of forming gas (10 pct H2, 90 pct N2) was continuously passed through the gas-tight annular volume between the core and outer jacket. The water-cooled copper ends shown in Figs. 1 to 3 sealed the ends of the tubes. Annealed molybdenum wire (40 mil) was wound on the recrys-tallized alumina core (35.5 mm OD by 28.5 mm ID by 30 in.) at a spacing of 0.36 in. The spacing was reduced to 0.29 in. close to the ends to partially compensate for end heat losses. Fig. 2 shows two molybdenum-ground lead taps off the center of the winding to produce the two independect temperature zones. The ground lead was insulated with 1/4-in. alumina tubing and connected to the grounded copper end by passing the wires through the gas port tube and crimping each wire into notches cut at the mouth. To prevent sagging of the core at high temperatures, refractory "troughs" were cut from alumina and mullite tubing to cradle the core. The support "troughs" which were 6 in. long and located about 5 in. from each end of the annular volume also served as radiation shields. In view of the different expansion coefficients and operating temperatures of the core and outer jacket (3.5 in. OD by 3 in. ID by 30 in.), the ends of the tubes were smoothed and squared to produce good sealing surfaces, and the core was ground 1/32 in. shorter than the outer tube. The power terminals were passed through their respective conductor ports which were internally lined with alumina tubing and sealed with Armstrong adhesive A-6 leaving about 1 in. of protruding lead wire for external connections. (Adhesive A-6 is a two-component system consisting of an epoxy-type resin with a mineral fibrous filler and an amine catalyst.) Figs. 1 and 3 show the entire assembly of concentric refractory tubes, copper ends, and sealing o rings, held together with two brass flanges and 3/8-in. bolts with heavy springs for dimensional flexibility. The furnace shell (19 by 19 by 30 in.) consisted of a steel frame with sheets of transite forming a box. The copper ends protruded through two 3.75-in. circular holes cut at the center of each transite square end. Thermal insulation next to the transite exterior was effected by K-23 B&W bricks alld in a central volume of approximately 9 by 9 by 30 in. a row of K-30 bricks was lined up to support the hot assembly. The rest of the volume around the outer

Jan 1, 1965

E. A. Peretti (University of Notre Dame, Notre Dame, Ind.)—Mr. Deitz and Professor Halpern are to be congratulated on a fine piece of work which adds to our knowledge of precious metal—cyanide-solution reactions. I should like to offer the following comments: The authors state, "the rate plots were always linear, indicating a zero order reaction rate." This appears to conflict with the data of Fig. 6 which clearly show the rate to vary with the NaCN concentration. It seems to me that the rate curves are linear because of the experimental setup. The volume of solution is so large that over a three-hour period the change in NaCN concentration is very small. A rough calculation for the experiments of Table I where the initial NaCN strength was 0.0096 mol per liter show a change of NaCN concentration of about 0.0009 mol per liter at the end of three hours. In short, over the period of time that the experiment was in progress, the NaCN strength was practically constant; hence the rate of dissolution remained practically constant. Eq. 10, as written, specifies that 1 mol of H202 and 2 mol of hydroxyl ion are formed when 2 mol of silver react. Is this true? The effect of H,O2 on the rate was made in solutions having an oxygen pressure of 4.8 atm. Were any tests made in solutions containing hydrogen peroxide, but no oxygen? G. M. Willis (University of Melbourne, Melbourne, Australia)—The authors have shown that, under their experimental conditions of high O2 concentrations, the rate of solution of silver in aqueous cyanide solutions is controlled by diffusion of O2 or CN- to the metal surface. With diffusion control, it is generally not possible to obtain further information about the mechanism of a process.

Jan 1, 1955

The members of the Institute will recall the account given in the March Bulletin of the inauguration exercises of the Engineering Foundation which was inhibited by an initial gift of $200,000 by Mr. Ambrose Swasey, to be administered by the United Engineering Society as trustees. The Engineering Foundation Board is now constituted as follows: GANG DUNN, Chairman, EDWARD D. ADAMS, Vice-Chairman FREDERICK R. HUTTON, Secretary, JOSEPH STRUTHERS, Treasurer, American Society of Civil Engineers. J. WALDO SMITH, CHARLES WARREN HUNT.

Jan 12, 1915

SINCE I promised you above when speaking of the melting of metals to teach you to make small crucibles and shells for melting, I do not wish to fail in my promise. For, in truth, since they are instruments that are much used for this procedure, they increase the work if they are not good, and often cause great extra expense as well as necessitating repetition of the work. If they are good they save everything. Therefore, if you have to make them, do it so that they, are greatly aided by art. It is first necessary to have the clay of a good nature, that is, resistant to the force of the fire by its own natural virtue, either when it is lean or when its viscousness is mixed with much talc, and whether it is yellow or white. This should be well freed from small stones and beaten well with an iron, and then thoroughly mixed by hand. With this should be mixed an eighth part of finely ground and sifted iron scale,* and also some [145] young ram's-horn ashes. These things should be well mixed together by hand and by beating them. If this clay should not be strong enough by itself, it is mixed with another lean clay, with crushed peperino, flintstone, or some other stone that in your judgment seems to be arid and resistant. Crucibles are worked on a low potter's wheel turned by hand, or on a high one turned by foot, just as plates are made. Both large and small ones are made. Most of them are given a triangular shape at the mouth, and the shells have a kind of spout for ease in pouring out the metal. This done they are well dried, and baked in furnaces like pots or other vessels. At the end, when they have been thus made they are used for melts.

Jan 1, 1942

By Newell G. Alford

Forecasts of future timber consumption in soft-coal mining are handicapped by the lack of adequate experience records for estimating properly the timber requirements of the industry. Data were obtained from plants where records are kept or from operators who collected the information and to these were added composite figures for the continental United States in 1905 and 19191 and for central and western Pennsylvania and for Illinois in 1922.2 The result, representing slightly over 928,000,000 net tons, is shown in Table 1. Some of the companies furnishing data were unable to segregate the timber into classes of use but for those who did, Table 2 shows the board feet of posts and cross ban used per ton of coal mined and the percentage of the total timber consumed that was used in roof support. The wide variation in amounts of timber per ton of coal mined is the result of

Jan 1, 1924

By H. C. Gatos, J. T. A. Pollock

It is well known that the superconducting critical current densities of many alloy superconductors may be increased by cold working and in some cases further enhanced by a short heat treatment. This latter enhancement has been attributed to the redistribution of dislocations into cell-like networks' and to the precipitation of second phase particles,2'3 which act as flux pinning centers. In a manner analogous to dislocation pinning in precipitation hardening alloys,4 it is expected that here also a critical distribution of the pinning centers should result in maximum pinning effect. Concentration inhomogeneities exist in most or all commercial alloys yet there have been only a few attempts made to determine their effect on critical current capacity in the absence of cold working. Sutton and Baker,5 and Kramer and Rhodes6 have found that the complex precipitation processes occurring during the aging of Ti-Nb alloys can result in critical current density enhancement. Livingston7-10 has clearly shown, for lead and indium based alloys, that the distribution of precipitated second phase particles is of critical importance in determining magnetization characteristics. However, these '(soft" alloys age at room temperature and the time involved in specimen preparation prevents metallographic examination in the state in which the superconducting measurements are made. Thus results with such alloys are expected to be biased towards larger precipitates and interpar-ticle spacing. The present study of Ta-Zr alloys was undertaken to examine the influence of second phase precipitation, as controlled by heat treatment, on the critical current capacity of well annealed polycrystalline material. A study of the published phase diagram11 indicated that annealing supersaturated samples containing up to 9 at. pct Zr at suitable temperatures would result in the precipitation of a zirconium-rich second phase. It was MATERIALS AND PROCEDURE The alloys were prepared from spectrochemically pure tantalum and zirconium. Analysis was carried out by the supplier. Major impurities in the tantalum were: 12 pprn of 02, 17 pprn of N2, 19 pprn of C, and less than 10 ppm each of Mo, Nb, Al, Cr, Ni, Si, Ti. The crystal bar zirconium was pure except for the following concentrations: 15 pprn of 02, 17 ppm of C, 23 ppm of Fe, 11 ppm of Cu, and less than 10 pprn each of Al, Ca, N2, Ti, and Sn. Samples were prepared in the form of 8 to 10 g but-tons by arc melting using a nonconsumable electrode on a water-cooled copper hearth in a high purity ar-gon atmosphere. Each button was inverted and re-melted three times to ensure an even distribution of the component elements. The samples were then homogenized at temperatures close to their melting points for 3 days in a vacuum furnace maintained at 5 x 10-7 mm Hg. After this treatment the buttons were cold rolled to sheets approximately 0.020 in. thick from which specimens were cut, 0.040 in, wide and 1 in. long suitable for critical current density (J,) and critical temperature (T,) measurements. These strips were then recrystallized and further grain growth was allowed by an additional vacuum heat treatment at 1800°C for 60 hr. Some second phase precipitation occurred during cooling of the furnace and a solution treatment was necessary to produce single phase supersaturated samples. This treatment was successfully carried out by sealing the samples together with some zirconium chips in quartz tubes under a vacuum of 5 x 10-7 mm Hg, heating at 1000°C for 5 hr and then quenching into water or liquid nitrogen. The samples were then heat treated at either 350" or 550°C and quenched into water or liquid nitrogen. All samples which were heat treated at 350°C were quenched in both cases by cracking the capsules in liquid nitrogen. The samples treated at 550°C were quenched by dropping the capsules into water. Analysis for oxygen in randomly selected samples indicated that the oxygen content was in the range of 175 to 225 ppm. Values of Tc were determined by employing a self-inductance technique. Jc measurements were made at 4.2oK by increasing the direct current through the wire in a perpendicularly applied field until a voltage of 1 pv was detected with a null meter. The risk of resistive heating at the soldered joints during these latter measurements was reduced by first plating the ends of the wires with indium and then soldering to the copper current leads using tin. Metallographic examinations were performed after mechanical polishing of the same samples and etching in a 4H20:3HN03 (conc):lHF(conc) solution.

Jan 1, 1970

By F. W. Bremmer

The experiments described in this paper constitute the preliminary work of an investigation outlined to determine the combined effects of steam and temperature on the endurance properties of certain steels. Essentially of a fundamental nature, it was found necessary, in order to make the investigation comprehensive, to test materials treated to give a wide range of properties. The work reported deals chiefly with nickel steel with one series of tests including nitriding steel. Such a study involves numerous variables, and requires an endurance-testing machine of rather special design. Testing Machines The testing machines used were designed by C. E. Weaver;l they are a modification of the White-Souther and McAdam types. Each was driven directly by an individual 1/2-hp. 115-volt direct-current motor, running at a speed of 2200 r.p.m. Fig. 1 shows the assembly drawing and Fig. 2, a photograph of one of the machines. Specimen B is held by the rotating specimen holder A inside the steam box F, which is closed at the top by a tight-fitting, elliptical cover G. The load is applied to the specimen through the rod D and bearing C. E is an oil pipe leading fromthe lubrication system to the bearing C. The steam, which comes from the power house, is admitted through an inlet (not shown in Fig. 1) at the side of the box, the drain being at the bottom. Steam packings were placed around the rod D and the rotating shaft at H, from which the water was drained by means of a vacuum, which usually showed a gage reading of about 10 in. The temperature was measured by a mercury thermometer, and the pressure by a steam gage. Method of Applying Load After the motor has been started and the specimen as a consequence put in rotation, the load is applied by placing the foot pedal A (Fig. 2) in contact with electromagnet B, the winding of which is connected electrically in series with the motor. This operation releases the support under the weights that constitute the load. By this means the load

Jan 1, 1930

ALBERT J. PHILLIPS, Chairman E. H. Dix, JR., Past-chairman R. H. LEACH, Vice-chairman R. F. MEHL, Vice-chairman W. M. COME, Treasurer LOUIS JORDAN, Secretary 29 West 39th St., New York, N. Y.

Jan 1, 1937

By Charles A. Kelliher

In November of 1957, the Aliquippa Works started operation of the third basic oxygen furnace shop in North America. This high speed basic steelmaking method provided a very economical increase in capacity at the Works. The success of these two (2) 81-ton furnaces led to the construction of a second B.O.F. shop, producing heats of 230 tons at J&L's Cleveland Works in 1962. The experience gained operating both shops provided the background for the design of the new steelmaking complex at the Aliquippa Works. This new complex consists of a three (3) furnace shop with two (2) furnaces blowing alternately producing heats ranging from 120 to 207 tons. This variation in heat size is predicated on the requirement that approximately 20% of the shop production will be used to supply steel to a six (6) strand casting machine, producing 4' through 7" billets. The new B.O.F. shop has replaced all other steelmaking units including the #1 Shop, where operations were discontinued in September of 1968. With the advent of the strand casting facilities in September of 1969, many of the standard shop practices had to be changed to compensate for higher tap temperatures, longer handling times, and reduced ladle availability. The subsequent changes in these areas led to the evolution of the strand cast ladle practice which is described in this paper.

Jan 1, 1972

By A. R. Marder

Fe-C alloys have been investigated at temperatures below the eutectoid transformation to determine whether the superplasticity phenomenon exists for these materials. As a result of void formation at the carbide-ferrite interfaces that led to void coalescence and premature failure, the large elongations characteristic of superplustic matem'als did not develop. It had generally been assumed that the conditions for obtaining superplasticity include: a) T/Tm =0.5, b) a strain rate sensitivity of the flow stress that results in m s 0.3, and c) fine-grain structure. Although superphsticity was not observed in the alloys studied, stress-strain rate measurements indicated that an additional condition for the existence of superplasticitv in Fe-C allovs is that the fine-wain structure be equiaxed in agveement with previous results on Zn-Al al1oys. MANY investigations have been made on the hot deformation of iron-base alloys in order to obtain an understanding of the variables that may affect high-temperature strength and ductility.'-6 However, only a few papers have studied the effect of carbon content on the high-temperature properties of iron-base alloys. Peretayat'ko and Zaikov and Wallquist and carlen4 studied the effect of carbon on strength in the y temperature range, and recently Robbins, Shepard, and sherby6 studied the influence of carbon on the torsional behavior of iron in the a and cu-plus-cemen-tite temperature ranges. In addition to studying hot deformation behavior, current investigations have also been concerned with the phenomenon of superplasticity in nonferrous materials, and, in particular, ferrous alloys. Superplasticity is identified by the increased resistance to necking that results from a high strain rate sensitivity of the flow tress. ackofenr proposed the strain rate hardening coefficient m = d log a/d log e as a measure of strain rate sensitivity and showed that m must be "-0.3 for superplasticity to exist. In addition, a fine-grained microstrcture,- a eutectic or eutectoid ornosition,- and a test temperature in the creep range (TITm > 0.5)" have also been advanced as necessary conditions for superplasticity. Although many workers""23 investigated superplasticity associated with the allotropic transformation in iron and the eutectoid transformation in steel, and recently chadler " and orrison have studied superplasticity in the a - y phase region, no one has measured the superplastic effect in the a + cementite temperature region. Therefore, the purpose of this investiga- tion was to determine the effect of carbon content, microstructure, and test temperature on the strain rate sensitivity of Fe-C alloys at temperatures below the eulectoid transformation. EXPERIMENTAL PROCEDURE Fe-C alloys with carbon contents of 0.2, 0.4, 0.6, 0.8, and 1.0 wt pct were prepared as 100 lb 54 in. ingots by vacuum-induction melting. The compositions are listed in Table I. All the ingots were soaked at 2100°F for 2 hr prior to rolling to 4 in. plate. The minimum finishing temperature for rolling was 1800°F. The plate was sheared in 10-in. lengths and tensile bars were rough-machined prior to heat treatment. The samples were heat-treated according to the schedule in Table I1 in order to obtain a fine-grained microstructure consisting of finely dispersed carbides in a matrix of small ferrite grains. All the tensile specimens were heat-treated prior to finish machining, and tensile testing was accomplished on an Instron machine in conjunction with a clamshell furnace. The buttonhead specimen configuration is shown in Fig. 1. An inert atmosphere, helium, was maintained during testing with a steel tube shroud in a bell jar arrangement. Predried helium was continually purged over the buttonhead specimens and exhausted through ceramic fiber at the bottom of the tube to keep oxidation at a minimum and to prevent

Jan 1, 1970

By Gerhard Derge

The extension of metallurgical control of steelmaking processes has always made it desirable to have some quick method for determining the oxygen content of molten steel. To meet the practical demands of the steel industry, this method must also be simple enough so that the sampling can be done by the regular furnace crew. This requirement was kept in mind continually in the work to be described. An oxygen value is required for proper control, whether it be of a rimming steel or of a fully killed steel. However, two factors have discouraged the development of such direct methods: i. The reaction C + FeO Fe + CO is rapid enough to make the correct sampling Of the bath a difficult problem. The most generally accepted means of circumventing this difficulty have been the aluminum-killed bomb test of McCutcheon and Rautiol and the aluminum-killed spoon test of Herty.2 The theory of these tests is that all of the oxygen in the iron is converted to Al2O3, which can then be determined by chemical methods. Even when simplified so that the analysis is made by a measurement of turbidity, this method is too slow to be used in routine control. Furthermore, the results obtained have never been entirely satisfactory, and some of the reasons for this will be discussed later in this paper. z. The ordinary chemical methods of analysis for oxygen in steel are not reliable. The only analysis that seems to possess sufficient dependability to be of value is vacuum fusion,3 and the apparatus and technique developed for this have been too complex and slow for routine work. Indirect Methods Indirect methods of estimating the oxygen have been resorted to in mill practice. Generally these depend upon the chemical equilibria involved. The oxygen in the bath is related to other components in the slag or metal that can be analyzed the readily. These methods have many difficulties in common. Steelmaking processes involve a complicated set of interrelated reactions, all of which tend to approach equilibrium at varying rates. The degree to which any particular equilibrium is approached is not well established. Moreover, a proper use of theoretical equilibrium constants requires a more extensive knowledge of the activities of the con- than we now have. This is well illustrated by the irregularities observed when trying to determine the oxygen in the metal by its ratio to the iron oxide in the slag. Equiliblium relations may be used mole readily if they are evaluated by plant experience, but the extent of approach to equilibrium remains an undetermined variable and lack of an entirely satisfactory mean, of determining oxygen for the calibration is felt keenly, For example, the statistical analysis of the relation between carbon and oxygen4.6 illustrates that even iia a single plant wide variations exist under llormal conditions of operation. Never. theless, this is one of the best methods now

Jan 1, 1943

By Gerhard Derge

The extension of metallurgical control of steelmaking processes has always made it desirable to have some quick method for determining the oxygen content of molten steel. To meet the practical demands of the steel industry, this method must also be simple enough so that the sampling can be done by the regular furnace crew. This requirement was kept in mind continually in the work to be described. An oxygen value is required for proper control, whether it be of a rimming steel or of a fully killed steel. However, two factors have discouraged the development of such direct methods: i. The reaction C + FeO Fe + CO is rapid enough to make the correct sampling Of the bath a difficult problem. The most generally accepted means of circumventing this difficulty have been the aluminum-killed bomb test of McCutcheon and Rautiol and the aluminum-killed spoon test of Herty.2 The theory of these tests is that all of the oxygen in the iron is converted to Al2O3, which can then be determined by chemical methods. Even when simplified so that the analysis is made by a measurement of turbidity, this method is too slow to be used in routine control. Furthermore, the results obtained have never been entirely satisfactory, and some of the reasons for this will be discussed later in this paper. z. The ordinary chemical methods of analysis for oxygen in steel are not reliable. The only analysis that seems to possess sufficient dependability to be of value is vacuum fusion,3 and the apparatus and technique developed for this have been too complex and slow for routine work. Indirect Methods Indirect methods of estimating the oxygen have been resorted to in mill practice. Generally these depend upon the chemical equilibria involved. The oxygen in the bath is related to other components in the slag or metal that can be analyzed the readily. These methods have many difficulties in common. Steelmaking processes involve a complicated set of interrelated reactions, all of which tend to approach equilibrium at varying rates. The degree to which any particular equilibrium is approached is not well established. Moreover, a proper use of theoretical equilibrium constants requires a more extensive knowledge of the activities of the con- than we now have. This is well illustrated by the irregularities observed when trying to determine the oxygen in the metal by its ratio to the iron oxide in the slag. Equiliblium relations may be used mole readily if they are evaluated by plant experience, but the extent of approach to equilibrium remains an undetermined variable and lack of an entirely satisfactory mean, of determining oxygen for the calibration is felt keenly, For example, the statistical analysis of the relation between carbon and oxygen4.6 illustrates that even iia a single plant wide variations exist under llormal conditions of operation. Never. theless, this is one of the best methods now

Jan 1, 1943

By David R. Poirier

Activity data of carbon as a function of both temperature and composition throughout the stable austenite range is correlated by mearts of an equation derived from a quasi-chemical model. The carbon activity data of austmite for temperatures between 800° and 1200°C are utilized in conjunction with the activity of carbon calculated for the y solidus using the activity of carbon in liquid iron and published austenite-liquid equilibria. The results agree very well with Chip-man's correlation; however, a small difference in the activity of carbon in the high-temperature range of the austenite field is evident. Excellent agreement is found for the heat of solution of graphite in infinitely dilute austenite; from this study the value is 10,550 cal as compared with Chipman's value of 10,680 cal. AS part of a program to study microsegregation in dendritic solidification of ternary Fe-C-Cr alloys, it was desirable to be able to describe the equilibria between austenite and liquid iron in Fe-C-Cr alloys. In this regard, it was necessary to correlate existing data on the activity of carbon in Fe-C austenite as a function of both temperature and composition. At that time, Chipman's analysis1 of the thermodynamics of binary Fe-C austenite was not available. It will be shown that this study and Chipman's study agree rather well throughout the stable austenite range of temperature and composition; however, some small differences appear at temperatures greater than the eutectic temperature. Benz and Elliott 2 presented isoactivity lines for austenite superimposed on their revised Fe-C phase diagram. Using an expression from Darken and Gury 3 representing Smith's4 activity data between 800" and 1000°C, they found that the activities extrapolated above 1000°C to the solidus did not agree with the activities determined from the corresponding liquidus compositions. It is the purpose of the following argument to reconcile carbon activity data of austenite with the activity in liquid Fe-C alloys as determined by Rist and Chipman. 5 In addition, a simple analytical expression is sought for computational convenience. ACTIVITY DATA OF CARBON IN ZRON Fig. 1 shows the activity of carbon in Fe-C austenite as determined by Smith, 4 Schenck and Kaiser, 6 Scheil et a1.,7 and Bungardt et al.' The lines are merely drawn to separate the data into the respective isotherms. These data are inadequate to determine the activity of carbon at temperatures greater than 1200°C. The activity coefficient in Fe-C liquid alloys was assumed by Rist and chipmans to obey the following

Jan 1, 1969

By Koichi Kashida, Mayumi Someno, Kazuhiro Goto

The present work has two objectives: first to develop an experimental method which would give some new information on the micromechanism of the reduction of oxides by gases at elevated temperature; second to clari,fy the intermediate phases of the W-0 system, formed during the reduction. A Galvanic cell with the solid electrolyte , ZrO2 . CaO, was imbedded in powders of W03, CuO, or Fe20s with two measuring electvodes and with a reference electrode. The change of the intraparticle gas composition was measured at An oxygen concentration cell consists of two electrodes separated by an electrolyte through which the transference of electrical charge is accomplished predominantly by the migration of oxygen ions. Many works have been reported on the oxygen con- 600" to loo@ C during the reduction by the gas mixture of hydrogen and argon. The intraparticle gas composition changes stepwise with time. The electromotive force of such temporary interruption corresponds to the equilibrium electromotive force of two solid phases formed during the reduction. The intermediate phases of W-0 system, which are formed in a large quantity during the reduction by hydrogen, are W0 2 W02.72 and WOz. The micromechanism of the reduction of oxides by gases is discussed. centration cells with the solid electrolyte of solid solution of zirconia and lime, since Kuikkola and wagnerl demonstrated the possibility of determination of standard free energy of formation of oxides by an electromotive-force method with the Galvanic cell. One of the present authors (K.G.) and his coworkers have applied the cells with the solid electrolyte of zirconia and lime to the following measurements:

Jan 1, 1969