References are in all cases to the earliest known editions. In the few cases where the first edition has been unavailable for consultation, the particular one studied is indicated. English translations are included when known, but not others. [ ]

Jan 1, 1942

By F. Weinberg

WHEN impure Zn (< 99.99 pct)&apos;&apos;Z or Zn-Cd alloys3 are progressively solidified, a cell or "corrugation" substructure4 is produced in the solid, with a high impurity or solute concentration along the cell walls. When these materials are polished and suitably etched, etch pits are often observed along the cell walls. For the Zn-Cd alloys these etch pits have been associated with decorated dislocations, present in the corrugation boundaries to accommodate the lattice strain. In the course of an investigation of Zn-2 pct Au alloy, molten metal of this alloy was poured into cold water and the resultant solid pieces were sectioned, polished and etched with a Cr0 ethant. An extremely regular cell pattern was observed on the etched surface, similar in general to the corrugation structure previously reported for impure zinc and Zn-Cd alloys. At higher magnification, regularly spaced pits were observed along the cell boundaries. An example of the regular cell pattern at the center of a specimen is shown in the center and lower portions of Fig. 1; the top of the figure shows the pattern near the specimen surface. Typical etch pits in the cell walls are shown in Fig. 2. It was surprising that a cell pattern as regular as that shown in the center of Fig. 1 was produced at the very rapid solidification rates used (estimated as > 1 cm per sec). In addition, the distribution coefficient for the Zn-Au system is greater than 1. Accordingly, the center of the cells should be rich in solute and should etch

Jan 1, 1963

United Engineering Trustees, Inc Engineering Foundation Engineering Societies Research Board Other Committees United Engineering Trustees, Inc. ARTHUR S. DWIGHT GEORGE D. BARRON J. V. N. DOER Engineering Societies Library Board ROBERT PEELS PHILIP W. HENRY GEORGE C. STONE JOSEPH E. POGUE The Engineering Foundation H. C. BELLINGER GALEN H. CLEVENGER J. V. N. DORR

Jan 1, 1929

By M. D. Hassiallis

The claim is made in a number of patents1&apos;2&apos;3&apos;4 that some compounds of the class known as aryl sulphides have collector properties. One of these patents generalizes the claim to include all aryl sulphides, whose generic formula is R-S2-R&apos; (where x = 1,2, . . . ), with the restriction that if the aromatic radicals R, R&apos; contain substituent groups these groups may not contain nitrogen or oxygen. Moses, Hess, and Perkins cite as evidence for their claims the results of flotation tests on Anaconda and Miami copper ores using diphenyl sulphide, ditolyl disulphide and dinapthyl disul-phide as collectors. The use of alkyl sulphides as collectors has also been reported5 with the conclusion that the alkyl sulphides are better collectors than the corresponding aryl sulphides. The experimental work cited appears to confirm this contention. In order to test these claims with respect to diphenyl sulphide, a sample, purchased from the Eastman Kodak Co., was tested against Anaconda ore. The procedure followed. was that of Moses, Hess, and Perkins. A sample of ore weighing 500 • grams was placed in a laboratory ball mill. To this was added 220 grams of water, 0.06 grams of commercial diphenyl sulphide (1/4 lb. per ton of ore), and 0.8 grams of lime (3 lb. per ton of ore). The material was ground until 93 per cent passed a 65-mesh screen. This pulp was diluted to 16 per cent solids. A sample of the diluted pulp was placed in a Minerals Separation type of laboratory flotation cell. After a a-min. agitation period, pine oil was added and the froth collected for a period of 15 min. This test recovered 68 per cent of the copper, with a ratio of concentration of 6.8:I. The tailing assay was 0.3 per cent Cu. Moses, Hess and Perkins attained a recovery of 75 per cent, with a ratio concentration of I2:I. Although these results do not compare too well with those of Moses, Hess and Perkins, subsequent tests showed an improvement, as judged by vanning of the tails. It is concluded, therefore, that the patent results are confirmed. Contact-angle Tests In order to study the response of the various minerals, found in Anaconda ore, to commercial diphenyl sulphide, some contact-angle tests were made. Polished particles of bornite, chalcodte, chalco-pyrite, pyrite and quartz were conditioned for 15 min. in a suspension of diphenyl sulphide in water. The concentration of this suspension was 0.284 grams per liter, this being the concentration of this reagent in the ball mill. The conditioned particles were rinsed with water (not rubbed with filter paper or boiled linen) and then tested against an air bubble in the bubble machine, with the following results: born-

Jan 1, 1943

By M. D. Hassiallis

The claim is made in a number of patents1&apos;2&apos;3&apos;4 that some compounds of the class known as aryl sulphides have collector properties. One of these patents generalizes the claim to include all aryl sulphides, whose generic formula is R-S2-R&apos; (where x = 1,2, . . . ), with the restriction that if the aromatic radicals R, R&apos; contain substituent groups these groups may not contain nitrogen or oxygen. Moses, Hess, and Perkins cite as evidence for their claims the results of flotation tests on Anaconda and Miami copper ores using diphenyl sulphide, ditolyl disulphide and dinapthyl disul-phide as collectors. The use of alkyl sulphides as collectors has also been reported5 with the conclusion that the alkyl sulphides are better collectors than the corresponding aryl sulphides. The experimental work cited appears to confirm this contention. In order to test these claims with respect to diphenyl sulphide, a sample, purchased from the Eastman Kodak Co., was tested against Anaconda ore. The procedure followed. was that of Moses, Hess, and Perkins. A sample of ore weighing 500 • grams was placed in a laboratory ball mill. To this was added 220 grams of water, 0.06 grams of commercial diphenyl sulphide (1/4 lb. per ton of ore), and 0.8 grams of lime (3 lb. per ton of ore). The material was ground until 93 per cent passed a 65-mesh screen. This pulp was diluted to 16 per cent solids. A sample of the diluted pulp was placed in a Minerals Separation type of laboratory flotation cell. After a a-min. agitation period, pine oil was added and the froth collected for a period of 15 min. This test recovered 68 per cent of the copper, with a ratio of concentration of 6.8:I. The tailing assay was 0.3 per cent Cu. Moses, Hess and Perkins attained a recovery of 75 per cent, with a ratio concentration of I2:I. Although these results do not compare too well with those of Moses, Hess and Perkins, subsequent tests showed an improvement, as judged by vanning of the tails. It is concluded, therefore, that the patent results are confirmed. Contact-angle Tests In order to study the response of the various minerals, found in Anaconda ore, to commercial diphenyl sulphide, some contact-angle tests were made. Polished particles of bornite, chalcodte, chalco-pyrite, pyrite and quartz were conditioned for 15 min. in a suspension of diphenyl sulphide in water. The concentration of this suspension was 0.284 grams per liter, this being the concentration of this reagent in the ball mill. The conditioned particles were rinsed with water (not rubbed with filter paper or boiled linen) and then tested against an air bubble in the bubble machine, with the following results: born-

Jan 1, 1943

By Clyde Ross

The Thunder Mountain mining district is in eastern Valley County, Idaho. It is of undefined extent but nearly all of the development is confined to the ridge between Monumental and Marble creeks in unsurveyed T. 19 N., R. 11 E. (Fig. 1.) The district is still remembered among the mining men of Idaho because of the ill-advised rush there in 1902, but available evidence indicates that optimism regard-ing the future development of the gold deposits of the district is warranted. The former disappointment arose from the fact that many who took part in the early rush hoped for bonanza deposits, whereas the district is characterized by large masses of low tenor. In 1926 the writer,, assisted by C. Y. Behre, 3r., incidental to other work in the region, devoted four days to the detailed examination of the then access-ible workings in the district. Tha major workings in the Sunnyside, Venable, Standard and H-Y mines, most of which were still in good shape, were examined., Surface exposures at the Dewey were studied, but the main workings there have long been caved. The time available did not permit more than a cursory examination of the surface at a distance from the mines. Sufficient data have been gathered, how-ever, from published and unpublished accounts, production records and mine maps so that the major features of this deposit, by far the most productive in the dis-trict, can be summarized. The kindness of Messrs. Dan McRae and R: A. Davis in making available information regarding the mines of the district, a rd of these men and others in recounting early history and their observations in now inaccessible workings, have aided materially in preparing the present paper. A brief summary of the salient characteristics of the district has already been published.1/ Cir-cumstances have contributed to delay in the publication of the full official report, which will contain mine maps and ?such other detailed data as could be ontained. In view of the present interest in gold deposits it seems desirable to present here a summary of results of the study.

Jan 1, 1933

By G. S. Hume

RECENT developments in the Turner Valley gas and oil field, 40 mi. southwest of Calgary, Alberta, have indicated a large producing crude-oil area. Drilling be¬gan in Turner Valley in 1913 but no major developments took place until the fall of 1924, when Royalite No. 4 well at a depth of 3740 ft. in the upper part of the Paleozoic (Mississippian) limestone obtained a production - of 20,000 M cu. ft. of gas with a content of about one imperial gallon of naphtha (73° A.P.I.) per M cu. ft. This well produced as much as 600 bbl. of naphtha per day, and until abandonment in 1934 produced 911,313 bbl., which together with the gas sold was valued at about $5,000.000.

Jan 1, 1937

CONTENTS DAVIS, CARL R., WILLEY, J. L., and EWING, S. E. T.-Recent Developments in the Fine Grinding and Treatment of Witwatersrand Ores. Discussed by Charles E. Locke, H. W. Hardinge, H. N. Spicer, G. M. Brown, Justice F. Grugan, R. C. Canby 1 WEINIG, A. J., and BOWEN, MAX W.-Determination of Dissolved Oxygen in Cyanide Solutions. Discussed by A. L. Blomfield, M. F. Dycus, A. W. Bull.... 4 LEPSOE, ROBERT.-Precipitation Efficiency of Zinc Dust in Cyanide Process. Discussed by G. M. Brown, Charles E. Locke 5 Recent Developments in the Fine Grinding and Treatment of Witwatersrand Ores Discussion of the paper of CARL R. DAVIS, J. L. WILLEY, S. E. T. EWING, presented at the New York Meeting, February, 1925, and issued as Paper No. 1386-B, with MINING AND METALLURGY, December, 1924. CHARLES E. LOCKE, Cambridge, Mass.-In this country, we have come to think that we should use smaller size of feed in our ball-mills. I will admit that a ball-mill is not comparable to a tube-mill, as conditions may not be the same, but there we have an unusual demonstration of the advantage of a coarser feed. Further investigation along this line is going to lead to some valuable results. The authors have overcome the difficulty of this coarse feed by taking out what I would call the difficult lumps, It is not clear from the paper whether many of these difficult lumps&apos; may not be &apos;reduced portions of their grinding media. H. W. HARDINGE, New York, N. Y.-The idea is not exactly new because in 1911 they used the miner to reduce the finer material. We proceeded three or four years using many tons, about 15 tons. or nearly the same proportion of ore to grinding medium. Another thing to be taken into account is the hardness of the ore being ground. In South Africa, the transportation costs must be, taken into account. They are also making progress in the method of using tube-mills and ball-mills instead of stamps. Experiments are to be conducted with 10-ft. diameter mills there, with the object of increasing the mass action and agitation which, as has been demonstrated under different circumstances, increases the overall efficiency.

Jan 6, 1925

By F. N. Rhines, T. E. Leonitis

The oxide scale that forms upon magnesium at elevated temperatures is non-protective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth&apos; and has been verified by Suzuki2 and by ScheiL3 Pilling and Bcdworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki," he product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavaults observed that excrescences form upon liquid magnesium and alloys in thc course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium&apos; and calciums minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.~ Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Schcil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. Experimental Procedure and Results The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the 6c

Jan 1, 1946

By T. E. Leonitis, F. N. Rhines

The oxide scale that forms upon magnesium at elevated temperatures is non-protective in the sense that the rate of oxidation is constant and thus does not decrease with the growth of the scale as it does with other common metals. This generality was first stated by Pilling and Bedworth&apos; and has been verified by Suzuki2 and by ScheiL3 Pilling and Bcdworth argued that the nonprotective characteristic could be predicted from the fact that magnesium oxide occupies less space than does the metal from which it springs, wherefore the scale is not expected to cover the metal so completely as to exclude all direct access to the atmosphere. Linear oxidation is thought by Scheil to be common to all cases where the reaction occurs at the oxide-metal interface. According to Suzuki," he product of high-temperature oxidation in the air is MgO contaminated with no more than traces of a nitride. When the metal is allowed to burn freely a fume composed of cubic crystals of Mg04 is given off. Delavaults observed that excrescences form upon liquid magnesium and alloys in thc course of oxidation. Beyond this it is known that the use of atmospheres containing small quantities of sulphur dioxide6 or carbon dioxide serve to retard the oxidation of solid magnesium and that beryllium&apos; and calciums minimize the oxidation of molten magnesium exposed to the air. Many studies have been devoted to the nature and rates of "protective" oxidation, as exemplified by the cases of copper and iron, wherein the rate is characteristically parabolic. The theory of parabolic oxidation is well developed.~ Linear oxidation, on the other hand, has received but little attention and the theories proposed by Pilling and Bedworth and by Schcil have yet to withstand careful examination. There exists no comprehensive survey of the high-temperature oxidation of magnesium (or of any other metal that exhibits linear oxidation) over a broad range of temperature, under a variety of atmospheric conditions and covering a large group of alloys. It has been the purpose of the present investigation to provide such a survey, with the object of gaining a fuller understanding of linear oxidation, especially as applied to magnesium. Experimental Procedure and Results The experimental studies undertaken were of two kinds: (I) measurement of the rate of oxidation as influenced by the 6c

Jan 1, 1946

The Army Reorganization Act, which became effective July 1, 1916, contains a provision authorizing the organization of an Officers&apos; Reserve, in which will be included a Corps of Reserve Engineers. There will also be an Enlisted Reserve of skilled workmen in technical lines. The special provisions of the bill relating to the Engineer Officers&apos; Reserve were formulated with the help of the Joint Committee of the several national engineering societies, which has been at work on the matter for over a year with the War Department and Committees of Congress. Recognizing that engineering science is the basis of success in modern

Jan 8, 1916

By P. N. Richards, M. K. Ormay

The present Paper extends the previous work on cold reduced, low carbon steels to preferred orientations developed after various heat treatments. In recrystal-lized rimmed steel, cube-on-comer orientations increased with cold reductions up to 80 pct. Above that {111}<112> and a partial fiber texture with (1,6,11) in the rolling direction dominated. During grain growth, cube-on-corner orientations have been observed to grow at the expense of {210}<00l>. In re-crystallized Si-Fe (111) (112) and cube-on-edge type orientations are dominant near the surface and the (1,6,11) texture near the midplane for reductions up to 60 pct. With larger reductions {111)}<112> and the (1,6,11) texture are dominant. In cross rolled capped steel a relationship of 30 deg rotation was observed between the (100)[011] of the rolling texture and the main orientations after re crystallization. Most orientations present in recrystallized specimens can be related to components of the rolling texture by one of the following rotations: a) 25 to 35 deg about a (110) b) 55 deg about a (110) C) 30 deg about a (Ill) THE orientation texture of recrystallized steel is of interest where the product is to be deep drawn, because preferred orientation is related to anisotropy of mechanical properties such as the plastic strain ratio (r value);1,2 and in electrical steel applications where a high concentration of [loo] directions in the plane of the sheet improves the magnetic properties of the material. It is interesting to note that both these aims are to a large extent achieved commercially, even though the orientation texture of cold rolled steel does not show large variation3 and the recrystallized orientations are generally given as being related to the as rolled orientations mostly by 25 to 35 deg rotations about common (110) directions.4-6 There is, as yet, no single completely accepted theory on recrystallization. The three mechanisms that have been investigated and discussed are: a) Oriented growth b) Oriented nucleation c) Oriented nucleation, selective growth Largely from the observations of the recrystalliza-tion process by means of the electron microscope,7-11 there is now considerable evidence that the "nucleus" of the recrystallized grain is produced by the coalescence of a few subgrains to form a larger composite subgrain, which finally grows by high angle boundary migration into the deformed matrix. From the intensive work on the recrystallization of rolled single crystals of iron, Fe-A1 and Fe-Si al-loys4-" he following observations have been made: 1) The change in orientation during primary recrys-tallization can usually be described as a rotation of 25 to 36 deg about one of the (110) directions. 2) The (110) axes of rotation often coincide with poles of active (110) slip planes. 3) If several orientations are present in the cold rolled structure, the (110) axis of rotation will preferably be a (110) direction that is common to two or more of the orientations. 4) With larger amounts of cold reduction (70 pct or more) departure from these observations became more frequent. 5) After larger cold reductions, rotations on re-crystallization about (111) and (100) directions have been observed. K. Detert12 infers that a rotation relationship of 55 deg about (110) directions is also possible, by stating that the recrystallized orientation {111}<112> can form from the orientation {100}<011> of cold reduced partial fiber texture A.3 The observation by Michalak and schoone13 that (lll)[l10] formed during recrys-tallization in fully killed steel containing (111)[112],— as well as (001)[ 110] which is related to the {111}<011> by a 55 deg rotation about <110>-implies a possible 30 deg rotation relationship about the common [Ill]. Heyer, McCabe, and Elias14 have recrystallized rimmed steel after various amounts of cold reduction, by a rapid and by a slow heating cycle and found that the preferred orientations strengthened with increased cold reduction. The most pronounced orientation up to about 70 pct cold reduction was found to be {1 11}< 110>, after 80 pct cold reduction both {111}<110> and {111}<112>, after 85 and 90 pct cold reduction, {111}<112>, and after 97.5 pct cold reduction it was {111}<112> and (100)(012). In the present work, the orientation textures of the recrystallized specimens are examined under various conditions of steel composition, amount and method of cold reduction, and method of recrystallization. The relationships between the preferred orientations of the as rolled and recrystallized specimens, and the conditions for the formation of the various orientations during recrystallization are investigated.

Jan 1, 1970

By Eugene H. Cowles

The German silver industry of the United States amounts in value to upwards of $6,000,000 or $8,000,000 annually. Several thousands of people earn a livelihood pursuing it, and the beautiful goods and articles manufactured from this time-honored and valued alloy are everywhere visible. German silver enters largely into our street signs, harness and house hardware, and all manner of table-ware, solid or plated. There is scarcely an hour in the day that German or nickel-silver is not before our eyes. The composition of this alloy is a very uncertain thing, and depends largely on the honesty of the manufacturer and the price the purchaser is willing to pay. It is composed of copper, zinc and nickel in varying proportions. The best varieties contain from 18 to 25 per cent. of nickel, and from 20 to 30 per cent. of zinc, the remainder being copper. The more expensive nickel-silver contains from 25 to 33 per cent. of nickel, and from 75 to 66 per cent. of copper. The nickel is used as a whitening element; it also strengthens the alloy and renders it harder and more non-corrodible than the brass made without it, of copper and zinc. Moreover, it reduces the odor emanating from brass, which is so disagreeable if it occurs about the dining-table. Of all troublesome alloys to handle in the foundry or rollingmill, German silver is the worst. It is unmanageable and refractory at every step in its transition from the crude elements into rods, sheets or wire. As a white-headed furnace-man recently said to the writer, in one of our large mills, " you can put eight crucibles into the fire, each containing exactly the same mixture of German silver, and when you take them out and pour them into slabs for rolling, seven will be a mass of scum or slag, or the stuff will swell up like rising bread and overflow the moulds, and be so full of blow-holes that it will look like a sponge. The eighth crucible will contain perfectly good metal. On remelting the next day, the bad stuff will, in nine chances out of ten, come out just as good metal as the eighth pot the day before, and under apparently the same conditions." With nickel at seventy or eighty cents per pound, German silver

Jan 1, 1890

By James C. Ray

DURING the summer of 1931, I spent four months in a study of the Willow Creek district, Alaska. This work was part of a general investigation of the territory contiguous to the route of the Government- owned Alaska Railroad. It was conducted by the U. S. Geological Survey to determine the real and potential merits of the mineral deposits, to stimulate development of them, and thus to increase the traffic on the Alaska Railroad.

Jan 1, 1932

By John Henderson

Densities of melts 0f the lime-iron oxide-silica system in contact with solid iron have been measured by the maximum bubble pressure method in the temperature range 1250° to 1440°C and the composition range 0 to 40 mol pct lime, 15 to 100 mol pct iron oxide, and 0 to 55 mol pct silica. Densities range from 4.65 g cm 3 for wustite at 1440°C to 2.75 g cm-&apos; at 1350°C for a melt containing 30 mol pct lime, 20 mol pct iron oxide, and 50 mol pct silica. The results are interpreted in terms of a postulate that the melts can be regarded as a random array of oxygen ions in which regions of local order exist to satisfy the coordination requirements 0.f the cations. An understanding of the nature of metallurgical slags is basic to the development of a sound theoretical description of heavy metallurgical extractive and refining processes. Because these liquids are complex, direct measurements of their properties has not thrown much light on their structure. This has led to the approach of measuring the properties of simpler liquids, and building up their complexity until slag compositions are reached. In this way the density of liquid iron silicates was measured in a previous study1 and the present work represents a further stage in this synthesis. EXPERIMENTAL The technique used in the measurement of density was the maximum bubble pressure method. Details of the apparatus and procedure were similar to those previously reported,&apos; with the exception that a constant voltage transformer was used to supply the power input to the furnace and six silicon carbide resistance elements were used in place of the molybdenum winding. With these modifications melt temperature could be maintained within 1 centigrade degree during the course of a run. The silica used to prepare the melts was washed natural quartz ignited at 1000°C; wustite was prepared by air-melting A.R. grade ferric oxide in an iron crucible and lime was prepared by air ignition, at 1000°C, of weighed quantities of A.R. grade calcium carbonate, previously air-dried at 110°C. The finely ground constituents were intimately mixed in a glass ball mill prior to melting. Temperatures quoted are accurate to * 5°C and the standard deviation of the density values, calculated by the method of least squares, ranged from 0.5 to 1.8 pet. However, replicate determinations of density on different melts of the same nominal composition at the same nominal temperature did not vary by more than 1 pct, Table I, and this figure has been taken as an estimate of the accuracy of the density results. The density of carbon tetra-chloride was also measured as a check on the absolute performance of the experimental method. At 20°C a value of 1.593 * 0.002 g cm"3 was obtained; this compares with the literature value2 of 1.595 g cm"3. Results of experiments designed to measure the dependence of the density of lime-iron oxide-silica melts, in contact with solid iron, on composition and temperature are shown in Table I. Because iron sometimes precipitated in the sample during quenching, the Fe203 chemical analyses were only poorly reproducible and should be taken as a guide rather than as absolute values. Fig. 1 shows the data from various sources for the density of liquid iron silicates and Fig. 2 shows isodensity contours at 1410°C for lime-iron oxide-silica melts, calculated by graphical interpolation of smoothed curves drawn through the experimental results, together with the 1400°C results of Adachi and ogino3 and Pope1 and Esin.4 Fig. 3 shows the isothermal variation with composition of the volume of melt per gram ion of oxygen at 1410°C and Fig. 4 shows regions in which the temperature coefficient of this volume is negative, positive, or negligible (<0.005 cm3 deg-I). DISCUSSION a) Disparity Between Reported Density Results. Consider the system iron oxide-silica, the results for which are summarized in Fig. 1. Although there is some difference in the temperatures at which the various densities apply, this difference is not sufficiently large to account for the observed discrepancies. The reliability of the present results for the low-silica region has been confirmed by measurement of the density of liquid wustite by three different techniques. At 1410°C the density measured by a balanced-column method was 4.55 g cm"3, by a combination balanced-column and gas-densitometer method 4.59 g emd3, and by a pycnometer method 4.53 g cm"3. Schenck, Frohberg, and Hoffermann&apos; have also reported a value of 4.55 g cm"3 for the density of liquid wustite at 1400°C. It must be concluded, therefore, that neither Pope1

Jan 1, 1964

By A. A. Smith, J. S. Smart

THE controlled amounts of phosphorus, arsenic, sulphur or selenium found in commercial coppers perform a variety of highly useful functions. Indeed, a large segment of modem copper technology is essentially dependent upon the presence of one or more of these elements. Consequently, the literature contains many references to their effects but the scope is broad and has been only partly covered. New data are presented herewith directed toward a better understanding of the basic behavior of these elements in copper, with particular emphasis on the composition range 0 to 0.05 per cent. These data are a part of a general program of research on the effects of impurities on the properties of oxygen-bearing and oxygen-free copper, other portions of which have been reported previously.1-2-3 Schematically, the behavior of individual elements is determined from measurements of conductivity and softening temperature,1, 2 and the binary alloys employed are synthesized from high-purity copper in order to eliminate interference from the effects of extraneous impurities. Alloys of selected composition were first prepared in the oxygen-free form by continuously casting the melts in the form of 3/8-in. diameter rod. Oxygen was added subsequently to portions of the alloys, either by remelting or by diffusion at 850°C. from a surface scale. Test wires were drawn one B. and S. number per pass, using four 30-min. 600°C. anneals at o.3125, 0.257, o.204 and o.162 in., and a final cold reduction of 95 per cent t0 0.081 in. Oxygen-bearing slugs made by remelting were hot-rolled to 5/16 in., drawn to 0.162 in., annealed for 30 min. at 600°C. and cold-drawn 95 per cent to 0.081inch. The alloys containing phosphorus, having been compounded very early in the program, were prepared in the form of 5/16-in. rod, and processed to wire with only the last three intermediate anneals listed above, all of these having been conducted in commercial nitrogen. In addition, the conductivity anneals on these alloys were also performed in the same atmosphere, and the small amount of oxygen present as an impurity in the gas resulted in some loss of accuracy at temperatures of 700° to 800°C., as will be shown later. Subsequently, the anneals for all oxygen-free alloys were conducted in hydrogen to prevent oxidation, and purified nitrogen was employed only for oxygen-bearing samples. All conductivity anneals were of one hour duration followed by a rapid quench in 10 per cent H2SO4. EFFECT OF PHOSPHORUS The widespread use of phosphorus as a deoxidant has resulted in universal appreci-

Jan 1, 1945

By Paul Beck

WHILE the recrystallization properties of most of the practically important metals are known in considerable detail, those of lead are still relatively little known in spite of some valuable contributions in recent years. This condition probably is due to the difficulties involved in applying the usual methods of investigation. The microscopic method of discriminating between the elongated deformed grains of the familiar lenticular shape and the equiaxed recrys-tallized grains is not successful with fully refined lead: lenticular grains cannot be seen under the microscope with any amount of deformation whatever. The probable cause of this phenomenon was recognized long ago. With large deformation the time of recrystallization at room tem-perature is shorter than the period of preparation of the specimen for microscopic examination; with small deformation the deformed grains are not noticeably elongated in the first place. However, with small deformation the migration of the grain boundaries can be observed. The only systematic investigations yet published on the recrystallization of lead, those by R. S. Russell,1-3 make use of the conditions just described. Russell considered recrystallization completed when no further migration of boundaries could be observed. A serious objection to this method arises from the fact that there is no evidence to support the view that grain-boundary migration results only from recrystallization. If such migration does result from other sources after recrystallization is com-pleted-after the deformed grains have been replaced by new unde-formed grains-the "time of recrystallization" as determined by Russell may be too long. Furthermore, the method is subject to the above-mentioned limitation because of the unavoidable period of preparation of the sample. According to Russell, even with the fastest technique 5 min. elapsed before the deformed samples were ready for examination, and consequently no recrystallization time shorter than 5 min. could be measured.

Jan 1, 1939

By A. I. Krynitzky, Henry S. Rawdon

The most commonly used material for terminals in spark plugs is commercial nickel wire, because of its relatively high temperature of melting, excellent heat conductivity, and slow rate at which the metal is oxidized, even upon continued heating at high temperatures. The grade commonly used for this purpose averages 97 per cent. nickel, the remainder being manganese, cobalt, iron, copper, with traces of other impurities always found in commercial nickel. A peculiar and interesting type of deterioration that occurs in these nickel terminals during the service life of the spark plug was recently brought to the attention of the Bureau of Standards. Commercial spark plugs vary greatly in their size and shape and the terminals differ considerably as to their relative size, shape, number, and arrangement with respect to one another. Although this defect was studied in detail in only one form of spark plug, the deterioration is a characteristic of the material, i.e., of nickel wire, rather than of the particular type of spark plug in which it was noted and studied. The mechanical features of the plugs, however, have a considerable bearing on the time required for the deterioration to become serious. The results of this study of the deterioration of nickel terminals in service should be of value to the makers of all types of spark plugs in which the terminals are made of this metal. CharacteR of Deterioration of WIres During Service Macroscopic Appearance and Properties of Changed Wire.—The nickel terminals in which the deterioration was studied were taken from spark plugs having a central terminal with the ground or side terminals attached firmly at both ends to the shell of the plug. In some of the plugs, two side terminals were used, one on each side of the central one. Although both terminals were found to have deteriorated to some extent, the attack of the central one was quite negligible compared to that of the side ones. These latter wires had developed, in service, transverse cracks that, in many cases, were as sharp and definite as a knife-cut. After a separation occurred, the breach widened by loss of material from the

Jan 1, 1921

By Gerald Sherman

LARGE part of the mining industry is still under the shadow of the depression, and unwilling to undertake changes in plant or methods of operation that require large preliminary expenditures of money. Certain metals command fair prices: nickel, tin, and molybdenum. The precious metals, gold and silver, have been given greater values by natural processes of economics or by proclamation, but are of so much less importance in industry, in total value, and number of men employed, that they have not greatly raised the average for the mining business. The increased value of gold which was established in 1933 has stimulated .the search for new deposits, and aided efforts to revive some of the old mines &apos;Where it is hoped to find quantities of marginal ore now become profitable. The higher price did not increase production very much for 1934, but two discoveries of major importance, and others yet to be proved, will help later. The two referred to are the Lupa gold field in Tanganyika Territory, and the Silver Queen mine on Soledad Mountain near Mojave in California. The first was recently discovered, and is being developed by the East African Goldfields, Ltd. Uncompleted explorations of the croppings early in the year had exposed for measurement and sampling to a shallow depth, three ore shoots as gregating 7400 ft. in length and 6 ft. in width, containing 0.375 oz. of gold per ton. In the Silver Queen. an ore-

Jan 1, 1935

By John Birkinbine

A specimen of brown hematite, taken from an iron-ore mine near Anniston, Alabama, exhibits a metallic streak or thread running throngh it. This specimen having been sent to me, I have no personal knowledge of its occurrence; but Mr. Albert E. Noble

Jan 1, 1895