By E. Almendras de Siegel

Pyrometallurgical processes have the thermodynamic capability of treating complex and dirty ores and concentrates to produce high purity metals and inert slags. Modem pyrometallurgical processes are environmentally sound and competitive with other processes. However, there is still a need for sensors and other practical tools that permit a rapid evaluation of the performance of these processes. In order to contribute to satisfying this fundamental requirement, the authors developed the IDENT.LA software that permits the automatic mineralogical analyses of inorganic materials, including the final and intermediate products of pyrometallurgical processes. The technique allows determining the grain size distribution of mineralized inclusions, the surface relations between metallic phases, and conducting modal analyses of the essential phases that are present in the samples. Three basic automatic operations are performed: creating a representative image of the sample; identifying the metallic and non-metallic phases; and measuring the features of the resulting image. The results are used to evaluate the performance of pyrometallurgical and other processes. In this paper, the authors discuss the application of the technique to a sample of slag from a slag cleaning process that uses a carbonaceous reductant. In this case, process performance impacts not only on the efficient reduction of the slag magnetite and on copper recovery but also on the quality of the process off-gas. The mineralogical analysis of the slag is a valuable tool in assessing process performance and in recommending changes of operating conditions.

Jan 1, 1999

By E. García-Ramos, P. Flores-Sánchez, E. G. Palacios, B. Zeifert, A. Romero-Serrano, M. Hallen-López

Chromium containing slags from stainless steelmaking may eventually be leached by acidic environments, therefore they should be treated before being stockpiled or land filled. In this work, synthetic slags were prepared and the effect of CaO/SiO2, Cr2O3, MgO and Al2O3 contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that CaCr2O4 and CaCrO4 are present in slags prepared with neither MgO nor Al2O3. The Al2O3-based slags mainly produced Ca2Al2SiO7 and the Cr(VI)-containing oxide complex Ca4Al6CrO16, whilst MgO-based slags produced MgCr2O4 as main mineralogical species. Additionally, Eh-pH diagrams for the Ca-Cr-H2O and Mg-Cr-H2O systems at 25 °C were constructed. The lowest Cr concentration levels in the leaching liquors corresponded to MgO-based slags owing to the stable binding of Cr in spinel with MgO. It was also observed in the Al2O3-based slags that increasing the slag basicity from 1 to 2 the leachability of the slags are notably increased.

Jan 1, 2008

By Joo Hyun Park

A history of the research regarding the spinel in the community of the stainless steels has simply been reviewed, followed by the recent studies for the formation mechanism of the spinel in the ferritic stainless steel melts equilibrated with the highly basic slags and the crystallization behavior of spinel phase in the calcium aluminosilicate melts containing MgO and CaF2 during slow cooling cycles. It has been proposed that the content of aluminum and calcium in the steel melts as well as the basicity and the content of MgO and Al2O3 in the slags are quite important factors affecting the spinel formation in view of the formation mechanism based on the reduction of MgO (or CaO) and Al2O3 in the slags by the aluminum and silicon added to deoxidize the molten steel. The use of magnesia refractory was also recommended. The formation mechanism of spinel from the MgO inclusions readily formed in the steel melts equilibrated with the highly basic slags has newly been proposed on the basis of the ionic exchange reactions at the inclusion/metal interface and the crystal chemistry of oxides. The crystallization behavior of the spinel phase in the calcium aluminosilicate melts was enhanced by the Al2O3 based on the ionic reaction of spinel formation in the oxide melts, while the size of the spinel crystals in the oxide melts decreased by addition of CaF2.

Jan 1, 2006

By Sijun Li, Bingyu Zhang, Haitao Zhou, Zhendong Zhang, Guofei Si, Xianghua Liu

"Hot compression test of Nb microalloyed coiled tubing steel is performed on Gleeble3500 at 1123K—1373K and strain rate from 0.001 to 5s-1. It is found that flow softening occurs and the flow curves exhibit a peak with a characteristic of dynamic recrystallization (DRX) and change with temperature and strain rate significantly. The peak stress and peak strain are dependent on the Zener-Hollomon relationship with activation energy of 390 KJ/mol. On the basis of Avrami equation and the Zener-Hollomon parameter, it is obtained that the dynamic recrystallization kinetics equation with which the calculated and measured recrystallization fraction is very close. On the results of hot compression test, the Nb microalloyed coiled tubing steel is rolled by Thermo-Mechanical-Control-Processing (TMCP), and it is obtained that the yield strength and tensile strength of Nb microalloyed coiled tubing steel are 565MPa and 685MPa respectively, and the elongation percentage is 30.1%.IntroductionCoiled tubing is widely used in oil field for well logging, well completion, drilling, work over and other operation in various fields to solve a number of conventional operating techniques problem which are difficult resolved, and it plays a more and more important part in exploration and production at oil field. [1] It will improve the efficiency of exploration and exploitation, studying, developing and using coiled tubing technology. Therefore, the development of domestic coiled tubing materials and manufacturing technology are great significance. It is well known that Coiled tubing has relatively poor working conditions and complex force state. So, the coiled tubing needs satisfier a kind of high strength, high plasticity, and corrosion resistant under complex oil gas condition. As the coiled tubing technology developed, the level of the coiled tubing steel is from CT55 originally to CT90 and CT100, and the corresponding tensile strength is 483MPa-758MPa. [2, 3]"

Jan 1, 2012

By Denise C. R. Espinosa

The amount of secondary batteries are increasing about 15% by year. Among these batteries, it can be highlighted the NiCd ones, due to their high consumption. In Brazil, the consumption of NiCd batteries grown quickly in the last 5 years, due to the dissemination of cellular telephones and other electronic devices. The first step of a process to recycle spent NiCd batteries is the pretreatment through unit operations of mining treatment. The aim of this work is to define a physical pretreatment to conditioning the waste to a pyrornetallurgical recycling process of spent NiCd batteries used in cellular telephones. Batteries were disassembled by hand to release the different components. The studied batteries are basically composed (by weight) of: 78% nucleus, 18% plastic case and 2% circuits. The grinding of the batteries was performed by knife mill and also by hammer mill. After grinding the material was screened and submitted to a magnetic separator.

Jan 1, 2001

By Alex I. Kociubczyk, Wilky Desrosin, Lucía Mabel Boycho, Alicia E. Ares, Carlos E. Schvezov

In the present research, commercially pure Sn and Zn, and Sn-Zn alloys (Sn-1wt.%Zn, Sn- 2wt.%Zn, Sn-4wt.%Zn, Sn-8wt.%Zn and Sn-8.9wt.%Zn, weight percent) were obtained by a horizontal directional solidification process with two opposite senses and heat extraction. The solidification process was realized using a horizontal furnace with two heat extraction systems at both ends. The temperature was measured using eight K-type thermocouples and an electronic recorder of temperature data. The resulting structures were analyzed using optical microscopy. From the solidification process the thermal and metallographic parameters were determined in all samples. The presence of defects in the solidified pieces was observed. Internal defects pretended to be dependent not only on the composition of the alloys under consideration but also on the size of the structures formed, also, on the velocities and accelerations of interphases, and on the variation of thermal gradients. A model of the phenomenon from the first principles is presented.

Jan 1, 2015

By Chang Wei, Zhigan Deng, Yizhao WANG, Cunxiong Li, Gang Fan, Xingbin Li

During the process of hematite precipitation, the transformation of Na jarosite convert into hematite has been studied in a batch reactor at different temperatures, ranging from 170°C to 200°C with 3h of the retention time in the presence of 30g/L Fe ( ) and 4g/L Na+. The composition of precipitation was seriously depended on the temperature, at 170°C hematite and sodium jarosite are the reaction products of iron precipitate, with an increasing in reaction temperature the sodium, sulfur content in precipitated decreased and sulfur mainly exist in forms of SO4 2-, and when temperature over 200°C hematite was the only phase in product. An increasing temperature was not only beneficial to iron precipitation, also conducive to jarosite conversion to form high quality hematite precipitate.

Jan 1, 2016

By Xiangru Chen, Qijie Zhai, Wei Zhang, Haicheng Li, Chao Yang

In this paper, ductile iron material with different content of niobium was prepared by a scientific melting method. Image Analysis Software was used to studied the effect of niobium microalloying on both pearlite content and pearlite lamellar spacing in ductile iron quantitatively. The results showed that the addition of a small amount of niobium could increase the pearlite content and decrease pearlite lamellar spacing of ductile iron effectively.

Jan 1, 2015

By Junji Shibata

Some fundamental studies were carried out in order to produce composite powders comprising of two or three metal salts by using liquid-liquid extraction and to develop the control technology of the particle size. The combination of samarium and cobalt was selected as the two component composite powders. Both stripping and crystallization occurred at the same time by emulsifying the organic phase loading the two metals extracted with Versa tic Acid 10 and the aqueous solution containing oxalic acid. The effect of aqueous pH, oxalic acid concentration and agitation speed was examined on some properties such as crystallization percent, particle size and shape of each metal oxalate powders obtained in this process. The analysis by using EDX showed that the two metal oxalates were distributed uniformly at the same ratio as the organic phase composition.

Jan 1, 2001

By Paulo von Krüger

This paper deals with the cell design and operation of a tin electrorefining 1:5 pilot plant. The purpose of the work was the fitting of the basic parameters to be used in a full-scale tankhouse from a major Brazilian tin producer. The main specific difference was the use of permanent stainless steel cathodes instead of conventional tin starting sheets. The results of both product quality and operating parameters are discussed.

Jan 1, 2003

By M. Misra

The volume of low-level contaminated soil at the. Department of Energy's Nuclear Weapon Sites are in the order of several million tons. Most of the contaminants are uranium, plutonium, other heavy metals and organic compounds. Selected Physical separation processes have shown demonstrated potential in COD Centratingthe radio nuclides in a small fraction of the soil. Depending upon the size, nature of bonding and distributions of radio nuclides, more than 90 percent of the radio nuclide activity can be concentrated in a small volume of fraction of the soil. The physico-chemical separation processes such as flotation in a mechanical and microbubble tall column cell have shown, promising applications in cleaning up the high volume contaminated soil.

Jan 1, 1995

By Alicia Esther Ares, Alex Iván Kociubczyk, Verónica Liliana Scheiber, Roberto Rozicki

In the present research the horizontal solidification of Sn-Zn eutectic alloys (Sn-8.9wt.%Zn) is performed, with two opposite senses of heat extraction. From the process of solidification, the thermal parameters (local solidification time, cooling rates and interphases velocities) and grain sizes from macrostructures obtained were determined. The presence of defects in the solidified samples was analyzed, observing that they occur largely in the collision zones of solidification fronts advancing in opposite directions in the samples.

Jan 1, 2016

By G. Roderick Eggert

Material criticality reflects the degree to which a raw material is both necessary and subject to supply-chain risks. This study compares the criticality of selected raw materials from the differing perspectives of the manufacturing sectors of China, the European Union, Japan and the United States.

By Masahiro Sasaki, Wu Kepeng, Chang-Yong. Kang, Kohji Okada, Naohiro Igata, Kazuya Miyahara

"The damping capacity of the Fe-12 mass % Cr-6 to 30 mass % Mn alloys has been investigated. Particularly the effects of microstrucutre composed of the phases of a , a ' , y , and e on the damping capacity have been clarified. Various fraction of these phases were formed depending on the Mn content and cold work degree. The combination of 22 mass % Mn and 50% cold rolling formed the largest volume fraction of e martensite and showed the highest damping capacity. The other phases of a, a' and y had very small effect on the increasing of damping capacity.IntroductionFe-Mn alloys are known to be one of the high damping capacity materials [l-3]. In the present research, the damping capacity of the Fe-12 mass % Cr-6 to 30 mass % Mn alloys, in which 12% Cr is added for the improvement of corrosion resistance of the Fe-Mn alloys, has been investigated. Particularly the effects of microstrucutre composed of various phases of a (bee), a ' (bet martensite), y (fee), and e (hcp martensite) on the damping capacity have been clarified. The results of preliminary research on Fe-Cr-Mn alloys are reported by Igata et al. [4] Various volume fraction of these phases were formed depending on the Mn content and cold work degree. The combination of 22 % Mn and 50% cold rolling formed the largest fraction of e martensite and the measurement indicated clearly that e martensite had the largest effect on the damping capacity. The other phases of a ' y and a I had very small effect on the increasing of damping capacity."

Jan 1, 2000

By José Roberto de Oliveira

In a smelting reduction process the reduction reaction occurs predominantly in the liquid state. The main reduction agent is the carbon from the carbon saturated iron bath. The aim of the present work was to determine the velocity equation and the rate constant of the reduction rate of MnO content in a Mn0-SiO2-Fe0 slag by iron saturated carbon and the carbon dissolution rate in a Fe-Mn bath. The manganese content in the iron bath was in the range of 5 to 15 wt.%. It was observed that the rates of carbon dissolution in all Fe-Mn baths are faster than the rates of MnO reduction by the carbon saturated liquid iron.

Jan 1, 1999

By Yong Xian, Zhaohui Sun, Honggang Zhong, Qijie Zhai, Jie Sun

Vacuum refining is admitted as an effective means to remove impurities in the process of alloy smelting. In this paper, Orthogonal and single factor experiments were carried out to investigate effects of multiple factors, such as superheat degree of the melt, degassing time and vacuum degree, on the vacuum refining process. The results showed that the best removal rate of oxygen and nitrogen is up to 82.71% and 61.3%, respectively, due to high vacuum degassing efficiency. It is found that the superheat degree is minimal impact on the deoxidization rate, in addition, nitrogen removal is controlled by the degassing time. The inclusions exist in the AlV55 alloy are mainly composed of oxides and vanadium-nitrogen compounds.

Jan 1, 2015

By Shan He, Qiang Wang, Xuling Chen, Min Gan, Lishun Yuan, Xiaohui Fan

"The sintering properties of vanadium-titanium magnetite concentrate(VTC) was studied in this paper. Through the optimizing the sintering process of VTC, the suitable granulation moisture and coke proportion were determined. The sintering velocity decreased from 23.05 mm/min to 18.22 mm/min. With the increase of VTC proportion from 0 to 46%, the specific productivity and tumbler index were respectively decreased from 1.55 t/(m2·h) to 1.21 t/(m2·h), and 62.93% to 57.73%. The temperature of liquid phase formations of mixtures increased, the amount of liquid lowered, and the content and sharp of sintering mineral gradually changed with the increase of VTC ,these lead that sinter quality became worse.IntroductionIn recent years, the steel industry of China is developing rapidly. And the steel production was 627 million tons in 2010. At present, the resources of vanadium-titanium magnetite concentrate(VTC) was about 14.4% of the total national iron reserves of China[1]. VTC has been used as sintering material by Magang, Chenggang and Pangang. The amount of VTC in Pangang is maximum. However, there exist many problems in VTC sintering, which involve in high specific productivity, bad sintering tumbler strength and high energy consumption[2~5]. That’s why the proportion of VTC is limited in sintering.The high quality of iron ore resources is worse in China. Therefore, it’s necessary to study the properties of VTC sintering, and to find out the reason how the VTC ratio affect the sinter performance. Purpose and significance of the research is to get high-quality sinter with the proportion of VTC greatly raised."

Jan 1, 2012

By Akihide Nagao

The behavior of impurity hydrogen that is contained in starting material or picked up during processing has been little investigated up to now. The hydrogen microprint technique is applied to determine the microscopic location of impurity hydrogen during deformation in aluminum without hydrogen charging. Three kinds of pure aluminum of 99.99% are prepared, in which hydrogen content is varied by changing the atmosphere when they are melted and heat-treated. After rolling, tensile specimens with a gage size of 4 x 4 rnm and 0.5 mm in thickness are stamped out from these three kinds of aluminum sheets. These specimens are covered with a liquid nuclear emulsion of silver bromide crystals, stretched by 5,10 and 15 percent plastic strain or fractured, developed and fixed. SEM micrographs reveal a number of silver particles on the slip lines and on the grain boundaries. Also shown is that the more hydrogen present in the specimen, the more silver grains appear on the slip limes and on the grain boundaries. Consequently, it is concluded that impurity hydrogen is transported to the surface with gliding dislocations during deformation.

Jan 1, 1998

By Xiaojie Gao, Shufeng Yang, Jingshe Li, Chengsong Liu

In the blast furnace process, the dust entrained in the blast furnace gas enters into the down-comer, flows through the gravity dust separator (to eliminate coarse particles) and then is collected in a bag-house. The powder collected by the baghouse is called bag dust, while both fractions are called blast furnace dust whose main components are C and Fe. The dust also contains small amounts of nonferrous metals such as Zn and Pb, which have some value. Also, due to the small particle size and low density the dust is easily suspended in air and so can endanger human health. Therefore it is necessary to develop a process to both treat the dust to recover the metal values and to dispose of the residue – preferably by recycling to the blast furnace itself via the sinter strand. These objectives will result in good economic, environmental and social benefits [1].

Jan 1, 2014

By C. J. Lewis

This presentation concerns calcium oxide-better known as high calcium quick lime High calcium quicklime is produced by calcining high calcium limestone, mostly in the many rotary kilns located throughout the United States and Canada. This paper presents suggestions on the handling of lime based on field experience. The subjects covered are chemical analyses, transporta¬tion, lime storage, lime slaking to form a water slurry of calcium hydroxide solids, slurry transportation, slurry viscosity, and scaling of lime slurries. It is hoped that the comments on the foregoing areas will be of use to those designing or operating lime systems.

Jan 1, 1992