By Hai-Xing Fang, Bing Xie, Hong-Yi Li

"In the duplex melting process, chromium forms chromium spinels, the study of which will help to exploit the Hongge ores (rich in chromium) in the Panzhihua-Xichang area in China. Mimicked chromium slag was synthesized. The oxidation and decomposition mechanism of the Fe-Cr spinels contained was studied in a sodium roasting process. The effects of temperature, roasting time, amount of soda added and filling reagents were investigated. The leaching-reduction-precipitation-calcination procedure to extract Cr2CO3 was optimized. The results showed that the optimized roasting temperature was 1000~1020°C with a stoichiometric Na2CO3 addition and without any filling reagents. Roasted materials were leached with distilled water and were filtered to obtain a chromium-containing solution, which was adjusted to pH 1.60-1.80. A reducing reagent, NaHSO3, was added in a stoichiometric ratio and the solution was then adjusted to pH 7.25~8.25. Maximum Cr2O3 precipitation was obtained and the precipitate was calcined at 1050°C for 2h to obtain Cr2Ü3 with recovery rate over 96%.IntroductionChromium is widely applied in the metallurgical industry, in refractory materials and in the chemical industry with its particular properties of hardness, wear-resistance, high temperature resistance and corrosion resistance [1]. There is no free state of chromium in nature and chromite is the main chromium containing mineral [2], China is poor in chromium resources, despite its large demand, and there are few deposits of high grade of chromite ores except in some regions in Tibet and Xinjiang province [1, 4]. Hongge, one of largest titanomagnetite mines in Panzhihua-Xichang area, is a polymetallic deposit mainly containing iron and titanium; it is also associated with various beneficial elements such as chromium, copper, nickel, etc. [3]. As investigated in Reference 3, the chromium reserves of Hongge ores are so large that it is of great importance to study how to extract the chromium from them."

Jan 1, 2012

By Yongyong Gong, Qijie Zhai, Zhichen Zhang, Qixin Li, Zhishuai Xu

"Microstructure of semisolid slurry of Al-4.5wt.%Cu alloy was investigated with pulse magnetooscillation (PMO) treatment, the results showed that the PMO treatment can refine the crystal structures of Al-4.5wt.%Cu alloy significantly. The discharging frequency of PMO had a great effect on the solidified structure transformation of semisolid slurry of Al-4.5wt. %Cu alloy, and the primary a-Al particles become much finer and rounder with an increase of discharging frequency. However, over a certain discharging frequency, the grains of primary a-Al become coarse.IntroductionOver the last decade, a lot of attentions have been paid on metal rheoforming process [1-4], since it has higher mechanical properties of formed components, strength to weight ratio and age hardenablity. Nevertheless, semi-solid forming is always performed at high solid fractions (40%-60%), so it has the limitation of viscosity, a tends to be difficult to pour semisolid slurry into the hole of the shot sleeve. Therefore, a series of novel semi-solid slurry preparation methods and rheoforming techniques have been invented, such as, semisolid vibration treatment [5], rheocasting [6], pulsed magnetic field process [7], annulus electromagnetic stirring [8], via ultrasonic vibration process [9], equal channel angular extrusion (ECAE) process [l0] and straininduced melt activation (SIMA) process [11].The electromagnetic field is characterized by its effective grain refinement, green, convenient manipulation and without contamination of melt. The mechanisms of dendrite was fragmentation by electromagnetic field have also been largely proposed [12-14]. The broken dendrite arms then undergo a coarsening process to provide the globular structures and obtain much finer and rounder a-Al particles. When compared with other external electromagnetic techniques, Pulse Magneto-Oscillation (PMO) has obtained more fuvors, owing to narrower pulse width and much lower energy consumption. Furthermore, the PMO treatment can reach finer grains with shorter time treatment [16, 17]. This work aims to study the effects of different discharging frequency ofPMO treatment on the microstructure transition of the semisolid slurry of Al-4.5 wt.%Cu alloy."

Jan 1, 2014

By M. C. Flemings, S. B. Brown

"Metallurgy, as all of material science and engineering, rests on the intellectual foundations of processing-structure-property-performance relationships. Today it is widely recognized that processing has been too long neglected and presents exciting opportunities for exploitation. New processes, many of them already in the laboratory, will be exploited in the year 2000 and beyond, for near net shape forming and for achieving-new metallurgical structures and composite structures. Process modelling will alter the way we think about process and product design. Processes themselves will increasingly be automated and controlled by computers, altering the nature of the workplace and the tasks of the metallurgical engineer of the future. IntroductionInnovations in metal processing is hardly a new phenomenon, with the field thousands of years old. Nonetheless, the next few decades offer particularly important opportunities to improve our ability to process these materials. We appreciate today the variety of processing paths available to us, including vapor-, plasma- and electro-deposition, multiple phase and casting technologies, and non-equilibrium processes, and how these affect structure at the atomic level and at higher levels of aggregation. We understand the basic physical mechanisms involved far better than even before and have remarkable new abilities to predict, control, and simulate the kinetics underlying processes, and the processes themselves.The following sections describe these new opportunities in greater detail. First, we examine developments in the modelling of metal processing. We then consider some implications associated with process control and automation. Finally we present what we consider to be particularly promising metal processing technologies, and conclude with a few summary comments."

Jan 1, 1988

By Weng Fu

In this study, Resin-in-Pulp (RIP) technology is used to separate Pb from a chalcopyrite slurry. Solvent-impregnated resin, Lewatit® VP OC 1026, which contains di(2-ethylhexyl) phosphoric acid (D2EHPA) in a macroporous polystyrene matrix was used, as the functional group exhibits selectivity for Pb over Cu. Adsorption pH, kinetics, as well as resin and CuSO4 concentrations were investigated. The results show that the kinetics of Pb and Cu loading are fast, reaching the adsorption equilibrium within 30 min. The equilibrium pH of 2 was chosen as optimum for operation in order to achieve a high Pb extraction rate and extent as well as selectivity for Pb over Cu. High Cu(II) concentration in solution results in Pb(II) requiring a larger amount of resin for the same degree of extraction. Regeneration and reuse tests show that the loss of adsorption capacity happens in the 1st and 2nd cycles and then the adsorption capacity stabilises for the 3rd cycle.

By S. C. Sharma

The aluminium matrix composites with ceramic dispersoids can be separated by density difference concept. In the proposed work composite scrap is recycled using an oil fired furnace. The scrap is melted in the furnace and temperature is maintained below 740 degree centigrade. Because of the density difference the lighter dispersoids will float and heavier dispersoids will settle down. The clean melt is separated be removing the floating and settled disperssoils, and then filtering using ceramic filters.

Jan 1, 1995

By Steve Johnston, Mowafak Al-Jassim, Fei Yan, Omar Sidelkheir, Alain Blosse, Katherine Zaunbrecher

"Imaging techniques are applied to multi-crystalline silicon wafers and solar cells throughout the production process. Photoluminescence imaging, both band-to-band and defect-band, is used to characterize defects and wafer quality at all process steps. These steps include bricks sawn from ingots, wafer sawing, cleaning and texturing, emitter diffusion, edge isolation and glass removal, anti-reflective coating/passivation, and metallization of finished cells. Bricks, wafers, and cells can be imaged at a rate commensurate with in-line measurement, giving spatial information to characterize quality and defect content. Photoluminescence images on silicon bricks can be correlated to lifetime measured by photoconductive decay and could be used for high-resolution characterization of material before wafers are cut. The defect areas in as-cut wafers are compared to imaging results from electroluminescence and lock-in thermography, and cell parameters of near-neighbor finished cells, showing correlations to efficiency, open-circuit voltage, and short-circuit current.IntroductionImaging techniques can rapidly characterize material quality and defect density. Photoluminescence (PL) imaging can be applied to silicon from the brick level to all wafer process steps [1-8]. At the brick level, material thickness allows for measurement and correlation to lifetime where surface recombination effects are minimized [6, 7]. At the as-cut wafer level where thin unpassivated wafers prevent accurate lifetime assessment due to surfaces, defects can still be categorized and quantified to predict finished cell performance [3-5]. Defect regions can be identified by recombination-limited band-to-band PL or by defect-band emission [9-12]."

Jan 1, 2012

By F. San Martin, Y. Lefevre, F. Tamargo

The San Juan de Nieva smelter was commissioned in 1960 with an electrolytic zinc capacity of 15,000 t/y. After a number of minor expansions, the capacity was increased to 320,000 t/y in 1991 and will reach 440,000 t/y by August 2001. The expansion involves the construction of a 900 t/day Lurgi roaster and a new acid plant. The leaching will be fully revamped and modernised, including the construction of a new building for residue treatment and for j arosite precipitation with a separate circuit for silver-containing concentrates. The project also includes the construction of a fully automated 137,000 t/y zinc cathode tankhouse fitted with 3.4 m2 cathodes designed by Asturiana de Zinc, and based on the existing tankhouse and introducing some improvements. New melting and casting facilities, also designed by Asturiana, will be constructed.

Jan 1, 2000

By Kai Tang, Casper van der Eijk

Natural gas has been used as reductant in the production of iron for several decades. Recently, the use of natural gas as reductant for other metals has been drawing attention because of the low price of natural gas, as well as the reduction of CO2 emissions compared to the use of coke and coal. In this work, the reduction of a mixture of Ti- and Ni-oxides by natural gas has been studied. Within the Ni-Ti system, the intermetallic compound Ni3Ti is thermodynamically the most stable one. Therefore, powders of Ni-oxide and Ti-oxides were mixed in an atomic ratio of three to one and subsequently pelletized. Reduction was performed in a TGA furnace at constant temperature with varying reducing gas atmospheres. In a natural gas containing atmosphere, the Ni-oxide was easily reduced to metallic nickel while the Ti was reduced to Ti-oxycarbides or Ti-oxynitride when nitrogen was present. Depending on the process parameters, several percent of Ti was dissolved in the nickel-based solid phase.

Jan 1, 2014

By Min Chen

A numerical simulation of the stress field of the solidified shell in the mold during continuous casting of peritectic steel slab was calculated with commercial software. The results showed that the maximal stress on wide face of the solidified shell was located at the corner and near middle of the slab, and it increased with increasing the width of slab. In addition, the stress was also influenced by operating parameters such as superheat degree, drawing speed and cooling intensity of the mold, and the maximal stress value and its position changed with these parameters. For the slab with section size of 3200mm×150mm, the proper drawing speed was around 1.2m/min, with cooling intensity of 5500L/min while the superheat degree was 15°C to 25°C in order to prevent longitudinal crack occurring during peritectic steel continuous casting.

Jan 1, 2009

By F. W. H. Dean

A very sensitive sensor for the detection and measurement of hydrogen in solid steel is described. This technique is non-invasive and uses a collector to sweep the hydrogen emanating from a steel surface and feed to it sensor. This method is particularly sensitive, resolving fluxes to < 2 pI cm?2 S?I, with a linear measurement up to 1000 pI cm&apos;2 S?I, The collector is held on the steel substrate by magnets and it is shown that emanation of hydrogen from the steel is controlled by bulk diffusion of the hydrogen through the steel. The technique is demonstrated to have an excellent response time and reproducibility.

Jan 1, 2001

By Erich Hovestädt, Hans-Jürgen Odenthal, Christian Wuppermann, Herbert Pfeifer, Antje Rückert

"During the argon oxygen decarburization (AOD) process high-chromium steel melts are decarburized by oxygen and inert gas injection through sidewall nozzles and a top-lance. Due to the large amount of the injected processing gas, low frequency oscillations of the vessel can be observed. It is suspected that these oscillations can influence the converter's structure. The exchange of forces between fluid and the surrounding vessel is the focus of this study. An oscillation model was developed and tested, one objective being to limit the computational effort which is necessary for fully coupled and time resolved CFD and FEM simulations. Experimental results obtained from water-model studies as well as from on-sight measurements are available and were used in order to validate the numerical results. The authors' intention is a contribution towards a more in depth understanding of the factors influencing vessel vibration during the AOD process.IntroductionDuring the last four decades the AOD process has been established as a reliable and efficient refining process in stainless steel making. The injection of process gases (O2, N2, Ar) through sidewall nozzles shows advantages in mixing effectiveness compared to other injection geometries e.g. bottom blowing [1]. Stainless steel grades contain usually more than 10% chromium. With decreasing carbon content during the decarburization periods the tendency of chromium oxidation increases according to the varying chemical equilibrium which depends on the partial pressure of carbon-monoxide (CO) in the gas phase. That's why oxygen is gradually replaced by inert gases, usually argon or nitrogen, in order to lower the CO partial pressure and thus to minimize chromium oxidation. Despite the high injection velocity of approximately Ma = 1, the kinetic energy of the gas jets is consumed within a short distance from the nozzle exits due to the large density ratio between gas and melt of approximately 1:8000. With increasing distance to the nozzle exit, the initial horizontal velocity of the gas jet decreases and due to buoyancy force motion of the detached bubbles turns into a vertical direction. Subsequently a gas plume develops with its typical conical shape described by various authors [1-4]. Due to the drag force between gas bubbles and melt also the liquid phase is forced into a vertical motion. Near the free surface and the wall regions the melt flow is deflected in different directions. Subsequently, the typical flow pattern in the AOD vessel arises, as sketched in Figure 1 and described in literature [5-9]."

Jan 1, 2012

By Hai-Peng Guo, Lu Jiang, Xiao-Man Yan, Bing Xie, Hong-Yi Li

Traditional, calcium compounds cannot be used in vanadium extraction processing due to the limitation of sodium roasting technology, which results in unsatisfied dephosphorization for vanadium-containing hot metal in converter and thus increasing the dephosphorization burden for subsequent steelmaking. The calcium roasting technology is an alternative for vanadium extraction and allows adding lime into vanadium slag in converter. In the present study, vanadium was leached by soda from roasted vanadium slag with high calcium content. Effects of roasting temperature and time, leaching temperature, Na2CO3 concentration andliquid to solid ratio on vanadium leaching rate were studied. The results show that 94% of vanadium was extracted by roasting the vanadium slag at 950℃ for 2.5h and then leaching in 160g/L Na2CO3 liquid at 95℃ for 1h with liquid to solid ratio of 10:1 ml/g. Impurities of Si and P reacted with calcium and formed insoluble Ca2SiO4 and Ca3(PO4)2 respectively.

Jan 1, 2015

By Satian Niltawach

Iron sulphate jarosite through which iron in zinc sulphide concentrate feed is removed from the production circuit of conventional roast-leach-electrowin process, is chemically unstable and environmentally hazardous even if it is mixed with lime. If zinc silicate ore is used at similar chemical conditions in place of calcine in the jarosite precipitation, the resultant silico-jarosite residue having been mixed with lime is chemically stable and environmentally friendly. The recovery of zinc from silicate ore is also higher than that from calcine.

Jan 1, 1994

By T. J. A. Smith

This paper provides an overview of some of the key issues in design of smelter gas handling systems, with particular reference to smelter smelting plants. In both primary smelting and converting, gas handling and treatment systems often represent the major capital cost component. There is also ample evidence that poor system design can be a major cause of smelter down time, lost production and unforeseen high maintenance costs. The paper discusses these issues and offers guidance for improved design.

Jan 1, 1992

By T. J. A. Smith

This paper provides an overview of some of the key issues in design of smelter gas handling systems, with particular reference to sulphide smelting plants. In both primary smelting and converting. gas handling and treatment systems often represent the major capital cost component. There is also ample evidence that poor system design can be a major cause of smelter down time, lost production and unforeseen high maintenance costs. The paper discusses these issues and offers guidance for improved design.

Jan 1, 1992

By Guo Xian Jian

In this paper, an alternative process to recover the value metals from polymetallic gold ore by FeCh leaching was proposed. In the process, gold was recovered by direct cyanidation from the leaching residue, the isolative electrolyte in chloride solution was selected to recover lead, the cementation with copper powder was used to recover silver and the solvent extracting was applied to recover copper and zinc. The total recovery of gold, lead, copper, silver and zinc in the process is 90.8%,96.05%,84.3%,81.98% and 54% to the bullion of gold, lead and silver and sulfate of copper and zinc, respectively. The process conditions selected for FeCh leaching are the temperature of 104°C, leaching time of 6 hours, Fe3+ content of 140 g/l and stoichiometry of FeCl3.

Jan 1, 1996

By Daoxin Wu

Originated from(C4H9O)4Ti, nano--rutile TiO2 was synthesized by low temperature hydrolysis process in this paper. After being prepared by decomposing ammonium tungstate and covering on the surface of TiO2, TiO2/WO3 were characterized by means of X-ray diffraction(XRD), UV--vis difuse reflectance(DRS), fluorescence spectrum (FS). Results showed that with the increase of the supported concentration of WO3, the reflectance of DRS and the fluorescence spectrum intensity of TiO2/WO3 decreased accordingly, which indicated the powder?s increase in light absorbance and the decrease in luminescence respectively; with the increase of calcined temperature, the reflectance of DRS increased.

Jan 1, 2009

By Yongqi Sun, Zuotai Zhang

Our study investigated the influence of P2O5 and B2O3 on the viscosity and crystallization behavior of Ti-bearing blast furnace (Ti-BF) slags for the purpose of Ti extraction. The investigation of the crystallization behaviors were carried out using a single hot thermocouple technique (SHTT) and the viscosity was obtained by rotating cylinder method. For the viscosity, the results showed that P2O5 substantially increased the slag viscosity. P2O5 is a network-forming oxide, which increased the degree of polymerization of slags and accordingly increased the slag viscosity. However, both of slag viscosity and apparent activation energy for viscous flow remarkably decreased with B2O3 addition. As a typical network forming oxide, B2O3 was introduced into the network and existed dominantly as 2-D structure, BO3 triangular, which caused a simpler structure and a decreasing slag viscosity. As for the crystallization behaviors of Ti-BF slags, both P2O5 and B2O3 enhanced the crystallization trend of rod-shape rutile and suppressed the crystallization trend of dendrite CaTiO3. Therefore the added P2O5 and B2O3 caused the primary phase change from CaTiO3 to rutile. Additionally, it was found that the rod-shape rutile showed a 1-D growth, whereas the dendrite CaTiO3 showed a 3-D growth style.

Jan 1, 2015

By P. C. A. Maia, J Alexandre, F. A. J. Saboya, A. R. G. Azevedo, G. C. Xavier

"This work shows the characterization of clay and the granite waste by-product from the sawing process of the granitic blocks, used as raw material for brick ceramic. Besides, shows the degradation of the ceramic material obtained with different by-product contents in the waste after lab test degradation, is investigated. The clay is obtained from mine use areas of ceramic industry in Campos-RI and the waste is originating from of the area of Cachoeiro-ES, an important center of decorative stone in Brazil. The mixes were made by the addition of 0% up to 10% of the waste in the raw material. After drying and firing up to 900°C, obtained prismatic pieces were considered intact. Physico-mechanical properties were obtained from wet and drying tests in laboratory considering 50 and 150 cycles. The results showed that the use of powder byproduct has a considerably influence on the weathering and strength of the material.IntroductionThe ornamental rocks and coating defines the most promising areas of business in the mineral sector [l]. In this context, the Espirito Santo appears as the main Brazilian state in production and export of ornamental rocks, representing 47% of national production [2] which in tum is one of the economic sectors most representative of this State, due of its transport logistics and port vocation that facilitates the export of such products.It is estimated that the state of Espirito Santo there are approximately 1,200 companies dedicated to the activities of ornamental rock by providing 20,000 direct jobs [ 1]. These mobilize support activities, such as companies that provide machinery, equipment and supplies for industries, including service providers for maintenance.However, the production of rocks produces about 15,000 tons of granite waste/month [3] only in the municipality of Cachoeiro ltapemirim-ES. This is justified by the presence of more than 500 extraction industries, cutting and processing of stone, with about 900 looms, waste generators.According to [4], there is great potential for the use of granite waste in red ceramics introduced for the manufacture of bricks, blocks structural ceramics. and other ceramic products, especially when evaluated on exposure to weathering."

Jan 1, 2014

By N. El-Kaddah, V. L. Acoff, M. Arenas

"Control of the weld penetration, weld pool shape and temperature field in arc welding is critical to achieve the desired microstructure and mechanical properties in the resultant welds. This is particularly important in welding gamma titanium aluminides (y-TiAl) where the weld pool is relatively shallow and the temperature gradient in the heat-affected zone is quite steep. This paper investigates theoretically and experimentally the evolution of the shape of the weld pool for stationary gas tungsten arc welds in y-TiAl alloys. A mathematical model has been developed for predicting the electric current flow, the resultant electromagnetic forces in the metal, and the transient development of the temperature and velocity fields in the molten pool generated by a spatially variable heat flux at the arc-striking zone. The governing equations were solved numerically using the control volume technique. Welding experiments were carried out to determine the shape of the weld pool and the extent of the heat affected zone at different welding times for model validation. The numerical predictions were found to be in reasonable agreement with measurements. It is suggested that the model presented in this paper is likely to provide the information needed for predicting the microstructure and mechanical properties of y-TiAl welds. IntroductionIn recent years, there has been considerable interest in the welding of gamma titanium aluminides as a means of manufacturing high-temperature, high-performance components for turbine and automobile engines. These alloys are highly reactive, and must be welded in vacuum or inert gas atmosphere, rendering electron beam, and inert gas tungsten arc welding (GTA) to be the only suitable welding techniques for joining these materials [1-3]. The GTA welding is especially attractive because of its flexibility and relative cost-effectiveness. However, previous studies on the weldability and weld properties of these alloys using this process revealed a decrease in the mechanical properties in the fusion zone [4]. This is generally attributed to the change of the original duplex structure to a dendritic structure amplified by the shallowness of weld spot. Quantifying the effect of arc operating parameters on the geometry and temperature profile of the welding pool prior cooling is the first step for controlling the fusion zone microstructure and mechanical properties."

Jan 1, 1999