By W. E. Wallace, J. A. Warren, D. Josell, D. Wheeler

"We present the results of experiments and modeling of flip-chip geometry solder joint shapes under shear loading. Modeling, using Surface Evolver, included development of techniques that use an applied vector force (normal and shear loading) as input to determine a vector displacement of the pads connected by the solder joint (standoff height and misalignment). Previous solutions solved the converse problem: fixed displacements used to determine required applied force. Such solutions were inconvenient for applications, where the applied force (chip weight) is known. Also, for geometric and materials studies of solder joint shapes involving multiple parameters, determining the equilibrium displacement from applied force by bracketing solutions could become computationally expensive. Measurements of solder joint standoff height and misalignment as functions of the applied force (normal and shear), solder volume and pad diameter are presented. Experiments were carried out for solder ball diameters from 0.38 mm (0.029 mm3 volume) to 0.15 mm (0.0019 mm3 volume) on pads of diameter 0.64 mm and 0.35 mm. Fitting of simulation to experimental results gave optimized values for the contact angle and surface tension of the solder which were consistent with measured and literature values. IntroductionIn packaging technology flip-chip has become an important method for attaching semiconductor devices to substrates. Generally, the chip and substrate are bumped with solder and then the chip is flipped onto the substrate and the solder reflowed to form conductive interconnects. An epoxy underfill is normally flowed between the substrate and chip to reduce the thermal fatigue on the solder joints. A flip-chip assembly is illustrated in Figure 1.In flip-chip applications, the use of an integrated underfill/solder bump system [1, 2) removes an extra process step, namely infiltration of the underfill. However, the presence of an underfill will retard the self-alignment of the flip-chip. A first step in understanding and predicting this retardation is to develop a model to describe normal and lateral force-displacements curves when underfill material is not present. At this stage it is unclear whether static surface tension theory is sufficient to describe a complete model for flip-chip realignment even without underfill."

Jan 1, 2001

By D. M. Fermino, C. G. Bastos Andrade, V. F. Justo, F. R. Valenzuela-Diaz, M. G. S. Valenzuela, C. Volzone

The present paper presents the study of light green smectite clay, from Paraiba, Brazil, submitted to mild acid attack under moderated conditions. Usually, clays are subjected to treatment with strong inorganic acids at temperatures near the boiling point and at high acid concentrations and then, widely used as bleaching agents. The treatment occurred under bellow boiling temperature and at short times of reaction (90°C, reaction times of 1, 6, 12, 18 and 24 hours in close reactor, concentration of the aqueous solution of hydrochloric acid 1.5 M, clay/acid solution ratio of 1g/10mL). The purpose of these attacks is to reduce the concentration of impurities providing color, with minimal change in the clay minerals structure, aiming at use in products of high value such as cosmetics and polymer/clay nanocomposites. The raw clay and the attacked samples were characterized by X-ray diffraction (XRD), cation exchange capacity (CEC), stereomicroscopy, scanning electron microscopy (SEM) and energy dispersive X-ray detector (EDS).

Jan 1, 2015

By Takashi Nakamura

Dismantling and detachment of parts from e-scrap are essential and involve higher cost techniques in pretreatment processes for physical separation. New techniques are desired for effective recycling of minor rare metals, therefore, we are trying to develop new detachment processes such as a new break down process. The principal of this new process is an electrical disintegration by electric pulse. E-scrap is broken down by high voltage electric pulses in water. IC chips and LSI can be detached from printed circuit boards under proper conditions. Ta- capacitors are also broken down to plastic parts and Ta sinter with lead wire. This is very useful in terms of pretreatment for e-scrap recycling. Also in the case of metallurgical production, with its intrinsic potential of smelting, extraction, enrichment and separation methods, play an important role in the context of minor rare metals.

Jan 1, 2015

By Jörg Wallner

In order to limit SO2 emissions, the Montanwerke Brixlegg AG has installed a desulphurisation plant with the primary aim of reducing the peak emissions from the copper converter that are of particular ecological concern. The author discusses the process requirements, the desulphurisation process selected and the results achieved.

Jan 1, 1996

By Martin Reyes, Juan Hernández, Julio Cesar Juárez, Isauro Rivera, Ma. de los Ángeles Hernández, Francisco Patiño

The dissolution of Ag contained in metallurgical tailings was studied by adding ions Cu2+ and Zn2+ in S2O3 2- medium. Chemical analysis of mine tailings by cupellation revealed a Ag concentration of 71 g/ton. The XRF and XRD analysis confirmed the preponderance of SiO2 in the mineral matrix. The experimental dissolution process was conducted in alkaline solution using six concentrations of NaOH and five of S2O3 2-, at different temperatures, also using five concentrations of Cu2+ and Zn2+ as a catalyst. The results showed similar values for both systems (96.8% and 97.13%). The ion Cu2+ and Zn2+ increases the dissolution of Ag, and decrease the reaction time of dissolution. Under the conditions used, pH and stirring rate did not affect the dissolution of Ag.

Jan 1, 2015

By C. B. Piazzarollo

Red Ceramic materials are widely used in Civil Construction in Tropical Countries. However, these materials have high porosity and low mechanical strength. Thus, in order to improve these properties, recycle mineral wastes was incorporated into clay from Campos - RJ, ornamental rock waste, from the gneisses cutting of Cachoeiro - ES, 150 km from Campos. After the addition of up 10% of waste in clay mass, ceramic pieces were produced and subjected to the tests of porosity (P) and flexural strength (FS). The test material contains 53.3% clay and 67% waste slit. The X-ray diffraction identified the presence of kaolinite, quartz and feldspar for the clay and, for the waste, quartz and orthoclase. The results of FS and P showed that the residue influenced, positively, the ceramic piece, with strength gains especially from 920º up to 960°C.

Jan 1, 2015

By Hao Rang

The article Is specially to Introduce the recovery process of Nb, Mn, P from slags and reutilization techniques of the remaining slags. Nb-Mn-Fe alloys which contain 14-16% Nb, 40-60% Mn can be obtained after using fire refining process of " Blast Furnace-Revolving Furnace-Electric Furnace -Electric Furnace, "meanwhile, phosphorous slags which the content of phosphorus pentoxide Is 29.21%. Further going through wet metallurgical processing and electrowinning technics to recover grading 99°o metallic manganese. Finally, phosphorous slags are grinded finely to be as phosporous fertilizers to be directly used for farmlands. Small particle size (0-8mm) rich slags are mixed with slight solid additions for balling directly, and taken Into blast furnace with blocky slags all together. The remaining tall slags are fully used as constructional materials, slags cement as well as a serial of wall materials, road materials, ground ornamental materials without burning operation and steam curing. The compressive strength range of those materials is up to 15-30 MPa. There is no more solid waste slags effluent In the full technical process.

Jan 1, 1994

By M. Wu, A. Kharicha, J. Bohacek, A. Ludwig

"During the horizontal spin casting of rolls, vibrations and mould deformations seems to have a significant effect on the final quality of the product. Sources for vibrations can be found in the poor roundness and a static imbalance of the chill itself. The bending of the mould axis is also considered. Both, vibrations and axis bending, are used as an input for CFD simulations of the flow dynamics of the liquid metal inside the rotating cylinder. The aim is to study the feedback of the free surface behavior in terms of wave propagation and various wave shapes. Introduction The horizontal spin casting process (HSC) is a casting process that has several advantages over the traditional gravity casting processes. Centrifugally cast products have a high degree of metallurgical purity and homogeneous microstructure. A significant gain is observed for the rupture strength, the rupture strain, and the Young modulus. These properties naturally depend on the centrifugal force and thus, the best mechanical properties can be found at the largest distance from axis of rotation. However proper selection of the angular frequency has to be done in order to prevent the so-called ""metal rain"" i.e. metal droplets can fall down from the upper part of the cylinder due to a too weak centrifugal acceleration. In the same time excessive speeds can lead to the appearance of longitudinal cracks caused by the hoop stress in the initially solidified layer. From empirical knowledge other parameters have important influence on the casting products, it includes the pouring temperature, the pouring rate, the mould coating etc. Recently the presence of natural or forced vibrations have been identified as possible additional factors to be taken into account [1-2]."

Jan 1, 2012

By C. H. Bucknam

A review of phase analysis methods used to characterize refractory gold ores is presented. Updating of assay methods using database technology, on-line instrument interfacing and response surface modeling is highlighted. The use of assay results to classify ores for metallurgical purposes is demonstrated.

Jan 1, 1987

By L. J. Lutz

The U.S. Bureau of Mines has developed an electrorefining process to recover Ni, Co, Cr, and other metals from mixed and contaminated superalloy scrap. The superalloy scrap is cleaned then directly electrodeposited as a Ni -Co deposit. The process recovers approximately 90 pct of the Ni-Co available from the scrap as a 99t pct pure Ni-Co alloy. During electrorefining the electrolyte undergoes a purification process which results in Cr and other refractory metals reporting to the purification residue. Operating data is given for a 3-L compartmented electrolytic cell. Techniques for the removal of Fe, Cr, and trace impurities from the recycled electrolyte are outlined. The economics of a facility producing 15 mt/d of a Ni-Co alloy are also discussed.

Jan 1, 1993

By Jiann-Yang Hwang

A study on microwave assisted chalcocite leaching was carried out with a microwave hydrothermal reactor. The leaching was conducted with thick mineral slurries (50-100 g/l). The leaching media is a mixed solution of CuCL2 and NaCL The investigation included the effect of leaching temperature, quantities of the minerals per unit slurry volume as well as the initial concentration of cupric ions were investigated. The results were discussed and compared with that using conventional leaching method.

Jan 1, 2003

By Yuanbo Zhang, Zhixiong You, Daoxian Duan, Guanghui Li, Tao Jiang, Xiaohui Fan

"Presently, high-grade manganese oxide ores are usually utilized by a coal-based reduction roasting process. However, there were some obvious drawbacks, including serious environmental pollution, high energy consumption, etc. The reduction temperature is relatively high (850-900 °C). In this study, a kind of biomass, pine black charcoal, was used as a reductant to reduce low-grade manganese oxide ores. Under the optimal conditions of reduction temperature of 600~650 °C, roasting time of 30~45 min and ratio of ore to reductant 5:1, the leaching efficiency of manganese reached more than 98%. Compared with the traditional coal-based reduction process, the reduction temperature is reduced by 250-300 °C.IntroductionManganese plays a very important strategic role in the national economy, and it is widely used not only in the metallurgical industry, but also in the light industry, chemical industry, medicine, agriculture, etc [1]. The average grade of manganese ores in China is evenly about 21%, which belongs to typical low-grade manganese ores [2]. Therefore, large quantity of high-grade manganese ores is required to import in order to meet the rapid development of Chinese manganese industry. As reported, the conventional treatment of reduction roasting has been widely applied for processing manganese oxide ores, in which coals or reducing gases (CO, H2 or CHi) were usually used as reducers [3]. However, there were some insuperable problems, such as high energy consumption, poor operating conditions, serious environmental pollution, etc [ 4-9]."

Jan 1, 2013

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3-PbZrO3-Pb(Mg1/3Nb2/3)O3) system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densifieation by the normal sintering was slow even at high temperatures. When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.

Jan 1, 2003

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3 PbZrO3-Pb(Mgl/3Nb2/3)O3 system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densification by the normal sintering was slow even at high temperatures, When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.-

Jan 1, 2003

By T. E. Warner

In order to detect arsenic and antimony in zinc, various electrochemcial experiments were performed involving the electrochemical introduction of sodium atoms into molten zinc using a solid electrolyte. Under high rates, the formation of the intermetallic phase NaZn13 was assumed to form. Under more moderate injection rates of sodium, employing a symmetric "zinc/zinc cell", a qualitative relationship between the current generated during cyclic voltammeuy and the arsenic and antimony concentrations in molten zinc was observed.

Jan 1, 1999

By F. Kongoli

Nonferrous and ferrous smelting industries have recently faced the unavoidable necessity of changing and/or improving the smelting technologies as a result of the use of new raw materials which are becoming available from different geographical areas. These new feed materials usually contain different ore composition and higher level of minor components, which adversely affect the smelting process. Due to the problems encountered in several processes as a result of this feed diversification some work has been undertaken in order to make uniform the feed and avoid later surprises in the smelting process. However this has proven to be very difficult and sometimes almost impossible. In this work a more viable approach is undertaken to deal with this problem. It consists of controlling not the cause of the problem i.e. the feed composition but instead the results of this feed change, i.e. the end-point of smelting technologies. It is shown that this approach, when carried out through advances physicochemical modeling and simulation tools is not only easier and less costly but it also helps the control optimization and automation of the smelting processes. Several examples are given and future work is underlined.

Jan 1, 2003

By Yuanbo Zhang, Xiaoming Mao, Zhixiong You, Zhenyu Fan, Tao Jiang

"It is generally known that the formation of calcium ferrite is favorable during the iron ore sintering, which dominatingly contributes to the improvement of strength and reducibility of the finished sinters. In this study, effects of roasting temperature and 02 content of inlet gas on the sintering mineralization properties of typical iron ores, including hematite, limonite, specularite and magnetite, were investigated. The results showed the amount of calcium ferrite initially increased then decreased with the increase of the roasting temperature. The temperature of maximum calcium ferrite generation amount for different iron ores was determined as follows: hematite and limonite was 1275 °C, whereas specularite and magnetite was 1250 °C. Increasing 02 content of inlet gas was advantageous to the generation of calcium ferrite during the sintering. The sequence of 02 content affecting the mineralization properties of different iron ores was determined as follows: magnetite > hematite > specularite > limonite.IntroductionThe mineralization property of iron ore plays a significant role in the mineral composition and microstructure of finished sinters, which determine the quality and output of the sinters [1-2]. The mineralization process of sinters is composed of solid-phase reaction, formation of liquid-phase and crystallization. The formation and crystallization of liquid-phase is the foundation to the mineralization as the quality of the sinter is poor when concreted by solid-phase consolidation [3-4]. With respect to the iron ore sintering, liquid-phase regarded as bonding phase is generated between the iron ores and fluxes at high temperature [5]. Calcium ferrite is the most favorable liquid-phase among the bonding phases which dominatingly contributes to the improvement of strength and reducibility of the finished sinters [6-8]. Especially for high iron-low silicon sintering and high basicity sintering, making sure sufficient calcium ferrite quantity and reasonable distribution is crucial to the sinters [9-10]. Therefore, carrying out the researches on the high temperature reaction properties of iron ores is of great significance [11]."

Jan 1, 2013

By Deepu Philip, Pratik Agarwal, Ajay Kumar Shukla, Ishani Shukla, G Rajesh

Steel plants generally employ static BOF end point control models to arrive at a given temperature and chemistry at the end of blow. These end point models have now been supplemented with chaos control models to steer the blowing process in the right direction while the blow is in progress. Merely arriving at the correct end point temperature is however not adequate because in the subsequent stages as well the temperature variations can be large and unpredictable. The present paper deals with an integrated model to take into account the effect of all parameters affecting temperature and composition from tapping to the start of casting to minimize the use of LF or aluminum heating, and also minimize grade mixing. The application of lean operations strategy is explained in which the previous “Push System’ is changed to a “Pull System”, minimizing the use of ladle furnace or aluminum heating during steelmaking.

Jan 1, 2014

By M. A. Cocquerel

The future economic necessity of mining copper ores with a high impurity content and increased environmental awareness will require closer examination of the distribution of arsenic within copper smelting processes. A generalized approach is developed which can be adapted to specific projects for the determination of an overall process configuration to satisfy all requirements in a cost effective manner.

Jan 1, 1983

By Yuanbo Zhang, Guihong Han, Guanghui Li, Tao Jiang, Zengqing Sun, Yanfang Huang

"Because of small specific surface area and poor ballability, vanadium/titanium-bearing magnetite is difficult for production of oxidized pellet. A novel organic copolymer binder, modified humic acid (MHA), has been authorized recently in China. Effects of the novel MHA binder on the quality of V/Ti-bearing magnetite pellets are studied in this paper. Experimental results show the MHA binder can obviously improve the strength of green pellet. Because of better heat endurance, the MHA binder pellet has a higher strength than Peridur pellet under the same preheating conditions. Moreover, TFe grade of pellet with the MHA binder is much higher than that of the bentonite pellet. The strength of preheated pellet containing MHA binder of 0.25%~1.0% meets the requirements of oxidized pellet production by grate-kiln process. Comparatively, MHA is a promising orgainc binder for iron ore pellets. Its price is only one tenth of Peridur price and about 3 times of bentonite price.IntroductionThe iron-making practices show that the use of pellet is beneficial to blast furnace life, productivity and fuel savings. Therefore, many iron-making plants have expanded the production of oxidized pellets in order to meet the needs of modern large-scale blast furnaces [1]. Presently, bentonite is widely used to improve the quality of iron ore pellets. The negative effects of using bentonite include decreasing total iron (TFe) grade and degrading the metallurgical properties of the final products [2, 3]. Many studies, therefore, have been conducted on the application of organic binders to overcome the weakness of the inorganic bentonite. In comparison with inorganic binders, one of the biggest strengths of organic binders is low residual silica content [4]. However, those studies showed that the economics of foreign organic binder addition into pellets was not attractive. For example, the compression strength of preheated pellets and roasted pellets are both too low, resulting in powder generation and ring formation in the industrial rotary kiln [3, 4]."

Jan 1, 2011