By Naiyang Ma

High zinc concentration in basic oxygen furnace (BOF) steelmaking offgas (OG) cleaning system solid wastes is one of the main barriers for recycling of the solid wastes in sintering – blast furnace ironmaking process. One of the possible solutions is to utilize zinc-free scrap in BOF steelmaking so that the BOF OG solid wastes will not be contaminated with zinc and can be recycled through sintering – blast furnace ironmaking. This paper describes a model for helping to decide whether to use zinc-free scrap in a BOF process. A model computing marginal price increment of zinc-free scrap is developed. The marginal price increment is proportional to value change of the BOF OG solid wastes after and before using zinc-free scrap, to ratio of BOF solid waste rate to purchased galvanized scrap rate, and to price of galvanized scrap. Due to the variations of consumption rate of purchased galvanized scrap and home galvanized scrap, iron ore price, landfill cost, and price of purchased galvanized scrap, using zinc-free scrap in a BOF process might be economically feasible for some ironmaking and steelmaking plants or in some particular market circumstances.

Jan 1, 2015

By C. B. Catanach

The development and in place leaching of a chalcocite ore body at Mountain City, Nevada is described. Block caving was used to induce permeability while ore removed during development was leached in heaps on the surface. Copper was recovered by precipitation on iron. Excess ground water which seeped into the mine was pumped into a deep disposal well. A parallel system was used to purify water by lime neutralization. Copper extraction was at an annualized rate of 11% during the first six full months of underground leaching and totalled approximately 30% during six months of heap leaching. Leach solution flow and distribution had a major effect on extraction rate. Enrichment of leach solutions with ferric sulfate did not produce conclusive results until analyzed with the aid of a leaching model.

Jan 1, 1976

By Masao Suzuki

Over 5 million cars are scrapped yearly in Japan. After dismantling. scrapped automobiles, they are put into a shredder for differential recovery of ferrous and nonferrous metals. The residue, which is called shredder dust, runs over 1.2 million tons per year. This paper reports a entire sequence of scrapping. cars. in Japan with the following sections: (1) production and scrapped car management, (2) material composition, (3) dismantling, (4) shredder plant, (5) differential recovery of metals including specific gravity separation and newly developed color separation.

Jan 1, 1995

By Bryce Clark

An outline of the current world's known sources and resources of cobalt, looking at both land and possible undersea deposits, is given as a prelude to an examination of current and historical actual world production on geographic/company basis. These production figures will be compared to apparent consumption by segments, both geopraghically and end-use based. Consumption of cobalt has been regarded as price sensitive and a historical look at prices against all other figures will be considered. Included in this scenario will be a brief overview of cobalt's uses and a comment on future trends. Tables will include: Resources, Production, Consumption, Prices, Markets.

Jan 1, 1993

By S. Neogy, M. Gupta, D. Srivastava, V. Kain, S. Roychowdhury, R. C. Prasad, G. K. Dey

"Austenitic stainless steels are an important material of construction for Boiling Water Reactors (BWR). These stainless steels are amenable to strengthening by strain hardening. Various deformation modes at different test temperatures and strain become active. In the present investigation type 304LN stainless steel was used in the annealed and strain hardened condition. Thin foils were prepared from gauge section for transmission electron microscope (TEM) investigation after tensile testing at room temperature and at 288°C. TEM investigation reveals that twinning is the major mode of deformation for the tests done at room temperature while dislocation cross-slip is the major mode of deformation at higher temperature. Stacking faults were also observed to a limited extent. The extent of twinning was much higher for the tests done using the rolled material. The formation of martensite in the stainless steel due to straining was investigated by the analysis of selected area diffraction patterns.IntroductionAustenitic stainless steels (type 300 series) are an important material of construction in Boiling Water Reactors (BWR). These stainless steels cannot be heat treated but can be strengthened by cold working [1]. Nitrogen alloying of these stainless steels result in high strain hardening rates and higher strength without any loss in toughness [1]. Stress Corrosion Cracking (SCC) in BWR of these types of stainless steels have been attributed to surface strain hardening and strain hardening ofregions adjacent to constrained weldment [2].The test temperature [3, 4], prestrain [5] and nitrogen level [5] has been reported to affect the deformation mechanism during tensile testing. Byun et al. [3] have reported the formation of martensite, dislocations, stacking faults and twinning during tensile deformation, the extent of each depending on the test temperature. Strain localisation has been reported to occur during tensile deformation in irradiated stainless steels [ 6]. The behaviour of rolled material during tensile testing is similar to that of irradiated material to a large extent [3]. Austenitic stainless steels are low stacking fault energy (SFE) materials in which various types of microstructures have been reported to form during tensile deformation and the strain is also highly heterogeneous in nature in these stainless steels which aides SCC in BWR environment to a large extent [7]. During cold working of austenitic stainless steels second order twinning has also been reported [8]. Knowledge about the deformation mechanisms operative in the strain hardened austenitic stainless steels during tensile testing at different temperatures is essential to understand the material deformation behavior and the present study aims at enhancing the existing understanding."

Jan 1, 2011

By Takashi Ikeda, Masafumi Maeda

"Demand for solar cells is increasing linearly throughout the world. Last year production totaled 3000 tons worldwide. The market size of solar silicon is expected to increase further because of international ""political"" demand to reduce carbonaceous emission from energy consumed. Most elemental silicon is produced by the carbon reduction of Silica in an electric arc furnace. Purity of silicon at this stage is 90-99%. Major impurities are Fe, Ti, Ca· and Al, and minor ones are P, B and carbon. The oxidizing metallurgical process is no longer effective to remove transitfon metals because those are less noble to silicon. Nonmetallic impurities such as phosphorus and boron must be reduced to 0.001ppm for semiconductor use. The most common process for high purity silicon is the Siemens C process, which is basically distillation of hydro-chlorinated silicon followed by CVD of SiHCl3. The cost of such silicon is expensive to allow its popular use in solar cells. Currently scrap silicon -of semiconductors is used for this; however, the supply-of that scrap is limited to just a portion of semiconductor production.In this paper world demand for silicon will be reviewed and some of the processes proposed summarized.IntroductionSilicon is element 14 in atomic number and has an atomic weight of 28.0855. Little elemental silicon is found in the earth, and it is mostly found as oxides or silicate. The Clark number of silicon is very large and the second in its number. If we were discussing the volatility of silicon element on the globe, we would never worry about it. However, it is very difficult to obtain pure elemental silicon because a high purity silicon compound is very rare. In most cases these are silica (silicon oxide SiO2). As shown in Table 1, there are many grades of silica ore classified mainly by their content of iron and alumina."

Jan 1, 2000

By Lanre M. Oshinowo, André Bakker

"An understanding of the parameters that govern the just-suspended impeller speed, Njs, and the distribution of solids, is critical to the efficient operation of hydrometallurgical and other processes involving solid-liquid suspensions. In this paper, the distribution of solids in stirred tanks under a range of solids loadings (0.5 to 50 vol%) was predicted using CFD and validated against experimental data obtained from the literature. The multiphase flow is modeled using the Eulerian Granular Multiphase model. This paper will also review the established design parameter Njs in the context of scale-up and compare it to the quality of solids dispersion as a means of assessing correct scale-up in suspension tank design. The results of this study will describe a straightforward procedure to obtaining comprehensive information about reactor behavior with complex CFD models.The performance of hydrofoil impellers and a 45° pitched-blade turbine at suspending solids under different agitation speeds was studied. Both single and dual impeller operation have been evaluated. The settled solids fraction for speeds below N js, and the cloud height for impeller speeds above Njs were predicted. The CFD predictions are in good agreement with experimental literature data on velocity distribution and cloud height."

Jan 1, 2001

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By Mariana H. Staia

The present communication reports the results obtained by applying different concentration methods, at laboratory level, to the black sands from Estado Bolivar, Venezuela, with the aim of obtaining an adequate ilmenitic concentrate for the subsequent chlorination process. Sizing analysis was performed and plasma emission spectroscopy method was used to determine the chemical composition. It was found that from the two hydrogravimetric methods used, the Humphrey spirals is much more effective than Wilfley tables, leading to a 85% recovery. The most convenient particle size group for these concentration methods was the one corresponding to ASTM 40-140 mesh. When magnetic concentration was applied to the concentrate, obtained as a product from Humphrey spiral, a recovery of ilmenite more than 90% was obtained in the first step. It has been shown that the ore would respond to the separation techniques employed, giving individual minerals: ilmenite, zircon and silica as concentration products.

Jan 1, 1995

By Shanlu Yang

In this study, laser-GTAW hybrid welding was used to the lap joint of galvanized dual-phase (DP) 980 steel in a gap-free configuration. The effects of welding parameters such as the laser power, the distance between the laser beam and the electrode torch, the arc current on the quality of hybrid welds were fully studied. The reason for the formation of different weld defects arises from the development of the highly-pressurized zinc vapor at the interface of two metal sheets. Experimental results demonstrated that the elongated molten pool introduced by the GTAW can suppress the formation of spatters to some extent. However, the hybrid laser-arc welding process still suffers from a large amount of spatters that degrade the weld quality. Furthermore, it was found that the weld quality was enhanced with the increase in the laser beam-arc distance and welding current.

Jan 1, 2009

By Stein Tore Johansen

The flow of a liquid through a large grain filter has been considered. An improved form of the fluid dynamic equations describing flows through porous media is proposed. The theory is applicable to all Reynolds numbers. Particulate inclusions are described by passive scalar fields where only very simple mechanisms for particle removal are included. However, the deposition of particles are allowed to change the "porosity" of the filter. Hence, the flow pattern through the filter will change as the filter ages. The theory is employed to the filtration of aluminum in an industrial grain filter. The model shows that the filter is not effectively designed and there is room for considerable improvement. The dynamic "aging" process of the filter is shown to change the filtration from bed filtration to cake filtration. Finally, the predicted inclusion collection efficiencies are compared to efficiencies measured in an industrial filter. The predicted initial efficiencies are in very good agreement with experimental results.

Jan 1, 1990

By Kimio Itagaki

The distribution ratios of Ag, Pb, As, Sb and Bi for the Cu2S-FeS or Ni3S2-FeS matte / FeOx SiO2, FeOx-SiO2-CaO or FeOx-CaO slag equilibration in a MgO crucible were determined experimentally at 1523~1573K under controlled partial pressures of S2 and O2 at given PSO2 of 10.1, 50.7 and 101.3 kPa (0.1, 0.5 and 1 atm) and be observed dependency of distribution ratio on the matte grade, SO2 pressure and slag basicity were analyzed on the basis of thermodynamics,

Jan 1, 2003

By Filippos Patsiogiannis

Laboratory size (4.5 kg) low carbon steel melts were deoxidized using Al and FeAl (33% Al), with and without synthetic fluxes, in alumina and zirconia crucibles. The dissolved oxygen, total oxygen, soluble aluminum, insoluble aluminum, silicon and carbon contents in the melt were determined as a function of refining time and temperature. It was observed that the reaction between aluminum and oxygen in solution closely follows thermodynamic equilibrium. Silica present in the alumina crucibles was found to be a source of oxygen for the melt, while this was not the case for zirconia crucibles. Reoxidation of the melt occurred through oxygen pick-up from the atmosphere. The extent of this reoxidation was found to be a function of oxygen content of the bath and the slag cover on the surface of the melt. The effectiveness of calcium-aluminate based fluxes in protecting the melt from the reoxidation and in increasing the rate of removal of inclusions was evaluated.

Jan 1, 1992

By D. Donald Downey

Pilot Testing Ion Exchange Resin (IEX) can go from very simple beaker testing to complicated column testing. Space velocities, regenerant quantities, loading capacities, ion leakage, are all terms that get accumulated together to prove or disprove a resin’s (or resins’) ability to load a single ion (or specific set of ions). Not getting all the resin’s operating parameters correct will disqualify (or at least skew) the results. Laboratory tests for capacity, moisture content, bead size, metals fouling, etc.—what does it all mean? At last count, there were over twenty-five separate ion exchange resin tests (analyses) that were available to end users. Standard testing procedures identify the resin properties but more specific procedures can be used to identify problems with equipment operation. Then, there are the costs to consider; simple cation resin testing (moisture content, total capacity and bead integrity) is in the $200/sample range. However, add to this Chatillon, Russian Ball Mill Test, HIAC particle size, metals and % regeneration test procedures and the lab work can increase to over $1000/sample. In this paper, the author will explain the “must-do” pilot and test procedures and why they are important and the key to understanding how resin performs ion exchange.

By Katerina Kryst

Antimony and bismuth are two of the elements that need to be removed from copper electrolyte to ensure a trouble free operation as well as to maintain copper cathode purity. One method to control these impurities is the use of aminophosphonic ion exchange resins. Antimony is present as both Sb(III) and Sb (V). Sb(V) is very difficult to remove from these resins, requiring excess amounts of highly concentrated hydrochloric acid. In industry this affinity of Sb(V) for the resin causes a buildup of Sb(V) and degrading resin performance due to continual reduction of resin capacity. A new method for regeneration of aminophosphonic resins loaded with Sb(V) has been developed, which utilizes catalytic regeneration of the resin. Ion exchange can then be utilized for continual control of Sb and Bi in copper electrolyte.

By Jared Ball, Darren Snashall, Paul Telford, Pengfu Tan, Ben Hogg

"The foamed converter charges were up to 3 8 per month in Xstrata Copper Smelter at Mount Isa. The issue of high converter foamover frequency had remained unsolved for many decades in Mount Isa. A thermodynamic model of copper P-S converter and a viscosity model of converter slag have been developed to simulate the slag blow and copper blow, in order to understand the mechanism of converter foamover. The model predicts the chemistry and viscosity of slag during slag blow and copper blow. The effects of oxygen potential, charge of dirty reverts, slag carryover, under-blowing, over-blowing, and temperature on the foamover and viscosity of slag in copper blow have been discussed. A theory has been developed to understand the mechanism of converter foamover. The practical solutions have also been developed and implemented in Mount Isa Copper Smelter. Some improvements of the industrial operations have been presented. After a series of improvements, the number of foamed charges per month in the converter operations has been decreased significantly from 35 in Aug 2008 to only one per month in 2009/2010.1. IntroductionThe Copper Smelter in Mount Isa receives the concentrate containing about 25% copper and produces anode copper that contains about 99% copper. There are several stages in the process. The first stage carries out in the ISASMELT™ furnace. The ISASMELT™ process produces a molten copper matte containing about 60% copper. An iron-silica slag and a sulfur dioxidebearing off-gas are the by-products of the process. The slag is taken to the slag dams for cooling before it is recycled through the Mount Isa Copper Concentrator.The matte is sent to Peirce-Smith converters. The converters further remove iron and sulphur to produce blister copper which contains about 97% copper. The anode furnaces remove any remaining sulphur and oxygen to produce anode copper that is about 99. 7% pure. This is cast into anodes and sent to the Xstrata Copper Refinery in Townsville for final refining.In the copper pyrometallurgical industrials, slag foaming is an important phenomena which occurs when the gas bubbles have stability and not rupture. Foaming greatly increases the interfacial area between matte, slag and gas and is essential for the operation of high intensity smelting processes. However, foaming or foamover is undesirable in P-S converter since it can damage the equipment and injure the operators. Figure 1 shows that the whole process of a foamover development in a converter."

Jan 1, 2011

By William Petruk

"Heap leaching is a developing technology for recovering native gold and electrum from low grade deposits and from tailings. Recovery depends on permeability of the rock and ore minerals, size of particles in the heap, and ore textures that influence exposure of gold grains to cyanide solutions. These ore textures include gold-bearing veinlets and microveinlets along fractures and microfractures, gold grains in porous minerals and rocks, and gold graim. occurring along grain boundaries of other minerals. On the other hand, small encapsulated gold grains arc not likely tote exposed even with fine grinding. Most gold grains that occtir along grain boundaries of other minerals can be exposed with a moderate to fine grind, but the. resulting material will be too fine-grained to be permeable in a heap. Such finely ground ore, as well as tailings from flotation operations, can however be prepared for heap leaching by agglomerating the material into porous briquettes. Oxidized and weathered zones above. orebodies are frequently amenable to heap leaching because the gold-bearing pyrite and arsenopyrite have become permeable by conversion to porous iron oxides and ferric oxyhydroxides. A review of ore textures in several types of gold deposits suggests that:(1) the gold in vein deposits would gtmerally be amenable to heap leaching of both oxidized ores and fresh non-refractory ores,(2) the gold in Carlin-type deposits and in volcanogenic massive sulfide deposits is not likely to be amenable to heap leaching fresh ore, but oxidized zones above the orebodies are generally amenable to cyanidation, and(3) the gold in porphyry copper-gold deposits and in Witwatersrand-type deposits would likely be amenable to heap leaching of both fresh and oxidized ores but with high cyanide consumption."

Jan 1, 1997

By Chen-Ming Kuo, Esher Hsu

"The importers and manufacturers who import or produce products with packaging containers are charged a recycling fee in Taiwan. The amount of waste packaging containers used for calculating the recycling charge is based upon the amount declared by importers and manufacturers which might be underestimated. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explores its distribution. The sampling survey and ratio estimation are conducted for estimating the recycled amount; while the refuse sampling method for municipal solid waste composition is employed to estimate the un-recycled waste packaging containers. The estimated total amount of waste packaging containers in 2011 generated by households in Taiwan is 696,511 m.t., of which, 79.49% of the waste packaging containers were recycled and 20.51 % were landfilled or incinerated. This study shows that the amount of waste packaging containers declared by importers and producers is underestimated around 20%.IntroductionWaste packaging containers including iron cans, aluminum cans, glass bottles, plastic containers, paper containers, aluminum foiled paper packs are officially announced to be recycled in Taiwan. In order to create the economic incentive for raising recycling performance, associated manufacturers and importers are charged a recycling fee to subsidize recyclers. The amount of packaging containers declared by importers and manufacturers is used for calculating the recycling charge and recycling rate. The importers and manufacturers might underreport their producing (importing) amount to pay less recycling fees. Therefore, the estimated waste packaging containers based upon the amount declared by importers and manufacturers is usually underestimated. Related previous studies about waste packaging containers recycling in Taiwan are done by Hsu and co-workers [1-4]. Hsu and Kuo [1] estimated total production values of recycling and evaluated the performance of recycling performance based upon the estimated production values. Hsu and Liu [5] provided a cost analysis of recycling for waste packaging containers in Taiwan. Bor, Chien, and Hsu [2] presented a market-incentive recycling system for waste packaging containers in Taiwan. Hsu and Kuo [4] provided an amending mechanism for product charge and recycling subsidy in response to the social economic changes for waste packaging containers recycling. Lee and Hsu [ 6, 7] explored the distribution, fee rates, and collection rate of waste containers. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explore its distribution."

Jan 1, 2014

By J. A. Innes

"""The oxygen, next uniting with the carbon, sent up an ever-increasing stream of sparks and a voluminous white flame. Then followed a succession of mild explosions, throwing molten slags and splashes of metal high up into the air, the apparatus becoming a veritable volcano in a state of active eruption.""IntroductionHenry Bessemer F.R.S(An autobiography, 1905)Thank you Mr Chairman for the opportunity to speak: at this, the opening session of your International Symposium on the subject of ""Injection in Pyrometallurgy"". Judging from the list of papers to be presented over the next three days, the Symposium promises to provide a most valuable addition to our existing knowledge base in what is now an extremely active area of R&D investigations. Whilst we have obviously come a long way since Sir Henry Bessemer's pioneering experiments of the mid-19th century, there is still much for us to learn.Most importantly, the Symposium offers a further opportunity to acknowledge the many significant technical contributions made in this field by the Organising Committee's special guest, Professor Howard Worner - one of this country's most respected research leaders.When first approached to give this talk I had two areas of concern. Firstly, I was not entirely clear just what injection metallurgy was meant to cover. How should the overall scope of this particular subject be defined?My second concern related to Howard Worner himself - a man for whom I have the highest personal regard and who, in fact, played a most influential role in respect of shaping my own career. Having already spoken about Howard's achievements on earlier occasions, I wondered what I could sensibly add.Notwithstanding these personal reservations, I am delighted to be here with you this morning. If my thoughts on the meaning and scope of injection metallurgy appear to be slightly off-course, and if Howard should perhaps recognise some repetition in my remarks, then I hope I can be forgiven."

Jan 1, 1996

By R. L. Player

"The Copper Isasmelt process has been developed over the past 15 years by Mount Isa Mines Limited (MIM) and the Commonwealth Scientific and Industrial Research Organisation (CSIRO). The first two commercial plants were commissioned in mid 1992.The results of four heat balances on the Mount Isa plant are presented. At a smelting rate of 98 t/hr of chalcopyrite concentrate plus 14 t/hr reverts, the total heat generated was -91MW. Approximately 39% of this energy came from coal, while 50% of the energy reported to the process waste gas. To a first approximation the furnace is near chemical equilibrium.The impurity distribution in the Mount Isa plant was presented. Approximately 91 % As, 85% Cd, 75% Bi, 68% Zn, 60% Sb and Tl, 45% Pb and 30% Te in concentrate was eliminated from the matte.The ""bubble"" frequency of the gas cavity below the foot of the lance was measured at -2. 1Hz. Side bands displaced by -l.lHz modulated the bubble frequency. This was consistent with radial gravity wave motion in the slag bath. The two processes, gas bubbling and wave motion appeared to be coupled together; the bubble frequency was twice the slop wave frequency. IntroductionCopper Isasmelt has been developed over the past 15 years by Mount Isa Mines Limited and the Commonwealth Scientific and Industrial Research Organisation. The process is based on the Sirosmelt lance, invented by researchers at the then Division of Mineral"" and ProcessEngineering ofCSIRO in 1973.The first two commercial scale copper furnaces were commissioned at Mount Isa and the Cyprus Miami Mining Corporation smelter at Miami, Arizona in August and June 1992 respectively.The process concept, the history of the development, and the Mount Isa plant have been described (1, 2, 3).This paper sununarises heat balances obtained on the furnace, the impurity distribution among the output streams and lance injection characteristics."

Jan 1, 1996