By Cyril Stanley Smith

For many years sulphur and its congeners selenium and tellurium have been regarded as very harmful elements in copper and copper-rich alloys. Like many similar prejudices, this has been found to be partly wrong. All three of these elements actually have no great effect on the working properties of copper and its alloys, and are desirable additions in that they considerably enhance the machinability of alloys in which they are present. Because of their possible commercial importance, a study of the machinability and other properties of the pure binary alloys was made, as described in this paper, and the effect of selenium on a large number of copper alloys was determined. The current opinion regarding the deleterious effects of elements in this group undoubtedly arose because of occasional failures of tough-pitch copper containing unusually high tellurium, and because of the well-known fact that sulphur causes spewing and unsoundness in tough-pitch copper. Siebe,1 also Deretchey and Margolina,2 studied the effect of sulphur on copper and showed that in the absence of oxygen it was present in the form of copper sulphide, which was less harmful to the properties than an equivalent amount of copper oxide. No data have been published on selenium and tellurium, although the statement is often made, following Eggleston,3 that tellurium makes copper hot-short. Copper specifications call for only traces of these elements. Skowronski and Mosher4 give data on the effect of selenium and tellurium on the conductivity of tough-pitch copper. In private communication Mr. Skowronski says that the samples were hot-forged from small castings and drawn to 0.081 in. diameter, but it should not be inferred from this that these elements are harmless to the working properties of wirebars and commercial shapes. Constitution and Microstructure Constitution.—Sulphur, selenium and tellurium exist in their alloys with copper in the form of copper sulphide, selenide or telluride. These compounds are practically insoluble in the solid state and possess limited

Jan 1, 1938

By Leslie F. Tedsen, John E. Dorn, Alan E. Flanigan

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By Cyril Stanley Smith

For many years sulphur and its congeners selenium and tellurium have been regarded as very harmful elements in copper and copper-rich alloys. Like many similar prejudices, this has been found to be partly wrong. All three of these elements actually have no great effect on the working properties of copper and its alloys, and are desirable additions in that they considerably enhance the machinability of alloys in which they are present. Because of their possible commercial importance, a study of the machinability and other properties of the pure binary alloys was made, as described in this paper, and the effect of selenium on a large number of copper alloys was determined. The current opinion regarding the deleterious effects of elements in this group undoubtedly arose because of occasional failures of tough-pitch copper containing unusually high tellurium, and because of the well-known fact that sulphur causes spewing and unsoundness in tough-pitch copper. Siebe,1 also Deretchey and Margolina,2 studied the effect of sulphur on copper and showed that in the absence of oxygen it was present in the form of copper sulphide, which was less harmful to the properties than an equivalent amount of copper oxide. No data have been published on selenium and tellurium, although the statement is often made, following Eggleston,3 that tellurium makes copper hot-short. Copper specifications call for only traces of these elements. Skowronski and Mosher4 give data on the effect of selenium and tellurium on the conductivity of tough-pitch copper. In private communication Mr. Skowronski says that the samples were hot-forged from small castings and drawn to 0.081 in. diameter, but it should not be inferred from this that these elements are harmless to the working properties of wirebars and commercial shapes. Constitution and Microstructure Constitution.—Sulphur, selenium and tellurium exist in their alloys with copper in the form of copper sulphide, selenide or telluride. These compounds are practically insoluble in the solid state and possess limited

Jan 1, 1938

By E. P. Jennings

Large deposits of titaniferous iron-ore occur at Caribou, an old silver-mining camp in Boulder county, Colo., 17 miles west by south of Boulder, and a few miles northwest of the tungsten-mines. Professor Regis Chauvenet1 published a part analysis of the ore many years ago, but gave no description of the wall-rock. Caribou hill, which contains both the silver-bearing veins and the iron-ore deposits, is a low dome of gabbro surrounded by the Archæan schists and gneisses of the Front range of the Rocky mountains, the peaks of which, a few miles west of Caribou, attain an elevation exceeding 12,000 ft. The gabbro stock is roughly elliptical in outline, with approximate diameters of 1 and 3 miles. The crest of the dome is 10,500 ft. above sea-level, and the town and ore-cleposits are 500 ft. lower. Outcrops of the iron-ore occur in the town and extend NW. for 2,000 ft., where they disappear under the swampy meadows of Caribou park. Portions of the deposit are covered by drift, but one continuous outcrop is 900 ft. long and from 200 to 250 ft. wide. A second deposit is 0.25 mile south of the town along the eastern slope of the hill. It is not as well defined as the north bed, but is approximately 1,000 ft. long and from 100 to 200 ft. wide. The easily disintegrated ore does not form prominent outcrops, but the outlines of the deposits are readily traced by the large amount of ore fragments that cover the ground. Trenches and pits sunk on the outcrop expose a roughly banded magnetic iron-ore, with pyroxene as the principal gangue-mineral. The Gabbro. This rock was classified in the field as a gabbro from the presence of pyroxene and striated feldspars, and for convenience the field-name will be retained.

Jan 1, 1913

By Leslie F. Tedsen, Alan E. Flanigan, John E. Dorn

It is necessary occasionally to use aluminum-alloy sheet where moderately elevated temperatures are encountered. Considerable attention has been directed toward determining the influence of "artificial aging" on the room-temperature properties of the precipitation-hardenable alloys, as testified by numerous company reports and by references I to 4. Investigations on the properties at elevated temperatures are few, however, and have not always covered the range of times and temperatures of greatest interest. The present investigation was instituted to overcome this deficiency. The work was done for the Office of Production Research and Development of the War Production Board, under the supervision of the War Metallurgy Committee, as a part of the "restricted" Project NRC-548. It has been released for publication by the Office of Production Research and Development. AS is well known, the high-strength aluminum alloys achieve their remarkable properties as a result of precipitation-hardening. In production they are subjected to a solution heat-treatment followed by quenching, to retain the supersaturated solid solution. The solution treatment is followed by "aging" (precipitation-hard- ening) either at room temperature or at a suitable elevated temperature. A considerable increase in tensile and compressive yield stresses results from precipitation at room temperature ("natural aging"). Through the elevated-temperature process ("artificial aging") it is possible to obtain values of yield stress considerably higher than those attainable by natural aging. The increase in yield stress is accompanied by a smaller gain in ultimate tensile stress and by a decrease in elongation. During the first stages of artificial aging the yield stress increases steadily until it reaches a maximum value. In this condition the material is said to be "fully aged." Further exposure results in "averaging," attended by a steady decrease in yield stress. In the production of the artificially aged materials, temperatures and times are selected to achieve full aging. The following important characteristics are associated with the process: 1. The higher the temperature, the more rapidly is the fully aged condition attained. :7

Jan 1, 1946

By C. C. Wright, T. S. Spicer, R. G. Bowman

In recent years considerable publicity has been given to the problem of atmospheric pollution by fuel-burning equipment. Legislation has been stimulated and smoke ordinances have been enacted, the provisions of which show a definite trend toward stricter control of the emissions not only from the stacks of industrial fuel users but also from the chimneys of domestic consumers. As a result of war conditions, some slackening in the enforcement of these ordinances may be noted, but this is only a temporary expediency caused by the changes necessary in the distribution of the nation's fuel supplies and difficulties in securing the necessary equipment. Previous trends may be expected to continue in the postwar period. Largely because of the consumer demand for automatic heat, but partly because of the legislation against smoke emission, there has been a marked increase in the use of domestic underfeed stokers with the past decade. When correctly adjusted and operated, these units reduce the smoke emission materially, so that even the high-volatile bituminous coals may be burned with little or no emission of objectionable smoke. Unfortunately, however, the use of the domestic underfeed stoker introduces another problem; namely, fly-ash. Production of Fly-ash The term "fly-ash" is a misnomer, since the fly material is generally a mixture of small carbonaceous particles varying from green coal to coke, and inorganic particles ranging from fluffy ash to small particles of fused clinker. For want of a more comprehensive name, however, the term fly-ash is used throughout this paper to include all the fly material. Even with hand-fired furnaces a certain amount of fly-ash is produced, which necessitates periodic cleaning of the boiler flues or furnace radiator, the smoke pipe, and occasionally the chimney itself. With stoker operations the amount of fly-ash is increased many fold, because of the higher velocity of air travel through the fuel bed. Frequently the amount of this fly-ash attains such proportions as to constitute a definite nuisance to the householder and his neighbors and distracts very materially from the otherwise automatic or semi-automatic performance of the stoker. Virtually all the boilers and hot-air

Jan 1, 1944

By T. S. Spicer, C. C. Wright, R. G. Bowman

In recent years considerable publicity has been given to the problem of atmospheric pollution by fuel-burning equipment. Legislation has been stimulated and smoke ordinances have been enacted, the provisions of which show a definite trend toward stricter control of the emissions not only from the stacks of industrial fuel users but also from the chimneys of domestic consumers. As a result of war conditions, some slackening in the enforcement of these ordinances may be noted, but this is only a temporary expediency caused by the changes necessary in the distribution of the nation's fuel supplies and difficulties in securing the necessary equipment. Previous trends may be expected to continue in the postwar period. Largely because of the consumer demand for automatic heat, but partly because of the legislation against smoke emission, there has been a marked increase in the use of domestic underfeed stokers with the past decade. When correctly adjusted and operated, these units reduce the smoke emission materially, so that even the high-volatile bituminous coals may be burned with little or no emission of objectionable smoke. Unfortunately, however, the use of the domestic underfeed stoker introduces another problem; namely, fly-ash. Production of Fly-ash The term "fly-ash" is a misnomer, since the fly material is generally a mixture of small carbonaceous particles varying from green coal to coke, and inorganic particles ranging from fluffy ash to small particles of fused clinker. For want of a more comprehensive name, however, the term fly-ash is used throughout this paper to include all the fly material. Even with hand-fired furnaces a certain amount of fly-ash is produced, which necessitates periodic cleaning of the boiler flues or furnace radiator, the smoke pipe, and occasionally the chimney itself. With stoker operations the amount of fly-ash is increased many fold, because of the higher velocity of air travel through the fuel bed. Frequently the amount of this fly-ash attains such proportions as to constitute a definite nuisance to the householder and his neighbors and distracts very materially from the otherwise automatic or semi-automatic performance of the stoker. Virtually all the boilers and hot-air

Jan 1, 1944

By F. H. Kihlstedt

The Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 60 per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1949

By F. H. Kihlstedt

The Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 60 per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1949

By Cyril Stanley Smith, Earl W. Palmer

STRIP of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal The effect is known as "caring" and the protuberances are called "ears" Other terms frequently heard are "tips," "scallops," and "corners " It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip Numerous papers dealing with various aspects of the caring effect have appeared in the literature, those listed in the references' being especially interesting and valuable An investigation of the factors influencing caring of brass cups has been in progress in the laboratories of the American Brass Co for several years, and it was thought desirable to make some of the results generally available in summarized form The present paper discusses many factors that do and do not contribute to ear formation In addition, a section is devoted to methods of minimizing the caring tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced In the space available, it is impossible to quote detailed experimental procedures and numerical results However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill MECHANISM OF EAR FORMATION It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip The two-ear form that sometimes appears is also traceable to gauge variations However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself

Jan 1, 1942

By J. R. Mihalisin

Phase changes in as-cast alloys in the Ni2 CoCr-Ni, Ti-NSAl system containing 0.1 wt pct C were studied after heat treatment at 1650°F. It was found that a vegion of CrCo-type s was developed in this system after I1000 hr. The tendency for s formation was dePendent upon the aluminum and litanium content, the s -forming tendency generally becoming more pro-nounced as the latter two elements are increased. s lended to form in interdendritic regioues and was associated with solutioning- of- carbide phases. Electron- vacancy computations for prediction of s formation on these alloys mere in sufficient agreement with what was observed experimentally to indicate that the method should be of value in assessing a-forming potential in cast alloys. However, the correlation of electrotz- vacancy numbers may not be as favorable in cast as cormpared to wrought alloys. THE increasing use of high-temperature alloys for longer times at higher temperatures has resulted in a real need for obtaining information on the phase changes taking place in these alloys since these changes often have a direct effect on properties. This paper reports on a study of the phase changes in Ni-Cr-Co-Al-Ti alloys after prolonged heating at 1650°F. The alloys were selected from the pseudo-ternary system Ni2CoCr-Ni3Ti-Ni3Al and this system was chosen because it is the basis of many of the newer cast commercial superalloys. The attempt here was not to define accurately the boundaries of s formation in the NizCoCr-Ni3Ti-Ni3Al system but to delineate the phase transformations taking place upon heating alloys covering a wide range of chemistries in this system. An addition of carbon was made to all alloys to further simulate commercial alloys. It was hoped that the information generated in this manner would be of more direct use to superalloy designers than an equilibrium diagram approach since commercial alloys generally have outlived their usefulness when equilibrium is attained. EXPERIMENTAL PROCEDURE The alloys were vacuum-melted from carbonyl-nickel pellet, vacuum-grade chromium, electrolytic cobalt, high-purity aluminum and titanium, and spec-trographic-grade carbon.

Jan 1, 1968

By R. W. Powers, M. V. Doyle

ThE solution of a diatomic gas such as 0, or N2 in a metal usually follows Sieverts' law; i. e., Here C is the solute concentration at equilibrium and P, the gas pressure. The proportionality constant Ks is also the equilibrium constant for the reaction 1/2 02 (at pressure, P) - 0 (in solution at [21 concentration., C). to use oxygen as an illustrative gas. Sieverts' law is therefore interpreted to indicate that diatomic gases go into metallic solution atomically and that the solute "gas" atoms interact negligibly with each other. Of course, this interpretation is strictly valid only over the temperature interval in which the reaction indicated in [Z] can be investigated. At temperatures several hundreds of degrees below this interval, the possibility of interactions between solute atoms is conceivable. Indeed, from internal-friction measurements some evidence for the existence of groupings of oxygen atoms in tantalum solid solutions was presented a few years ago.1,2 Over a range of solute concentration, the experimental oxygen internal-friction peak in tantalum, measured as a function of temperature at constant frequency of vibration, can be described as the sum of two elemental peaks, each corresponding to a separate relaxation process. At 0.7 cps, the height of the elemental peak found at 137°C is proportional to the oxygen content, whereas the height of the one at 162°C varies as the square of the oxygen concentration. The 137°C peak was presumed to arise from the stress-induced ordering of oxygen atoms among various classes of octahedral sites in the manner proposed by Snoek.3 The 162°C peak was attributed to a somewhat similar stress-induced ordering process, in which each oxygen atom was interacting with a neighboring oxygen atom. Similarly, the experimental peak due to nitrogen in tantalum can also be described as the sum of two peaks. The height of one varies as the nitrogen concentration and the other as the square of this quantity. In fact, some evidence of solute interactions exist for all oxygen and nitrogen solid solutions of Group V transition metals. However, the interaction energy was not obtained previously for any alloy. The determination of this quantity, as a part of a more intensive study of the interaction between oxygen atoms in solid solution in tantalum, is reported in this paper. PRINCIPLE OF THE EXPERIMENT Consider an equilibrium in a solid solution of tantalum between oxygen atoms which are bound together pairwise and those solute oxygen atoms which are not so associated. 20 (Ta) - O2 (Ta) [3]

Jan 1, 1960

By C. O. Rison

HIGH explosives, particularly nitroglycerin, have been used in torpedoes for the purpose of shooting oil and gas wells for more than 60 years. The early history of the oil industry in Pennsylvania is not clear as to who actually torpedoed the first well, although in 1865 the Roberts Torpedo Co. procured a patent covering the process. Gunpowder was first used, although nitroglycerin was substituted shortly afterwards. Wells are shot for the purpose of increasing the flow of oil and gas A shot-hole in the producing horizon, with its contributory fissures and fractures, increases the area of and stimulates drainage into the hole. The shot-hole also acts as a collecting basin from which the oil is pumped. As a rule, hard or close-grained sands or limes are shot, other more or less porous and soft formations usually do not require shooting. and might be injured by blasting. Shooting is also resorted to in mechanical trouble such as straightening crooked holes, sidetracking pipe or tools, and for severing frozen strings of casing or drill pipe. Explosives arc also used sometimes to extinguish oil or gas-well fires although that work, which involves unusual conditions and methods, does not properly come within the classification of oil-well shooting. Some Factors to Be Considered in Shooting Wells Although nitroglycerin has been used extensively for more than half a century in shooting oil and gas wells, there is still a great deal of uncertainty as to the proper method of shooting or the amount of explosive required to produce best results in a particular formation. The possibility of shooting unproductive or cavey formations above or below the productive horizons, shooting into lower water, destroying casing seats, and the splitting or collapsing of casing strings, are factors that require consideration. The engineering departments of a number of the larger oil companies are making a study of methods of shooting, and the amounts of liquid nitroglycerin or other explosives required in shooting various productive

Jan 1, 1929

By John C. Draper

The principal object of an underground coal mine transportation system is to move coal from the face where it is produced to the outside of the mine where it is prepared for market. In addition to the movement of coal, a transportation system must also move supply materials to the inside ; it must move men in and out of the mine ; and it must move rock and other debris out of the mine for disposal. Usually, mine haulage is divided into three categories named for the various areas of the mine served : 1) Pace Haulage. This is used at face from the mining machine to the intermediate transport system. 2) Intermediate or Secondary Haulage. Generally this is used between face haulage and main haulage. Sometimes this is merely an extension of the main haulage. 3) Main Haulage. This extends from the secondary haulage to the outside and is usually either a track or conveyor system, sometimes a combination of both. Transportation modes of coal in the various areas pose different problems, but the whole system must be synchronized. For instance, at the face the coal should be removed quickly from the various places to facilitate the movement of machines, whereas the intermediate system just passes the same coal on to the main transportation system. Selection of the transportation system must be based on the seam height, mining methods used to extract the coal, capacity required, ease of coal handling, and haulage efficiency. When driving rooms, mine cars can be used. They often simplify supply haulage and rock handling because they can also handle these items. Conveyors could be used and would have a greater haulage capacity but they cannot handle supplies easily or segregate the rock. When using a different mining method, such as longwall, mine cars cannot be used because there is not sufficient space to move the cars at the face nor can the cars haul the coal without delays which would cause excessive losses in production. As for ease of handling

Jan 1, 1981

By F. J. Plecity, J. T. Michalak, W. C. Leslie

Isothermal recrystallization and grain growth in zone- and vacuum-melted irons and Fe-Mn alloys, up to 0.60 pct Mn, were studied in the range 480° to 650° C, after 60 pct cold reduction. In initial stages, rate of grain growth and rate of recrystallization of iron decrease with time. The recrystallization is typical of a growth-controlled process, and rate of growth is determined by the extent of recovery. Mn decreases rates of growth and of recrystallizatzon. The recrystallization process changes at about 0.30 pct Mn and nucleation may become time-depetzdet~t. In recent years, considerable effort has been expended in determining the effects of solute elements on recrystallization and boundary migration in fcc metals. The results have indicated that the effects produced by single solute additions are dependent upon both the element added and its concentration.'-' In contrast, there have been very few attempts to determine the characteristics of recrystallization and boundary migration in high-purity bcc metals, especially after heavy deformation, and the effects thereon of single solute elements.9-11 This study was undertaken to determine the recrystallization characteristics of various "high-purity" irons and the effects of manganese additions at two levels of base purity. It was hoped that the information obtained would improve our understanding of the recrystallization of pure metals and aid in formulating a theory for the effect of solute elements. The interest was not entirely academic, for the annealing of low-carbon steels, which is of very great commercial importance, is but poorly understood. MATERIALS The compositions of the irons and iron-manganese alloys used are listed in Table I. The zone-melted iron and Fe-Mn alloys were made by Battelle Memorial Institute. Iron S-1 was arc-melted in a water-cooled steel mold in an argon atmosphere. The ingot was forged into a bar, then given two horizontal zone-refining passes in an alumina boat. Iron V-4 was treated in a similar manner, but was not zone-refined. The iron for the zone-melted Fe-Mn alloys was induction melted in vacuum in MgO crucibles and cast into alumina molds. The ingots were forged into bars, machined to shape, and a groove milled down one side of each. The best available electrolytic Mn was placed in the grooves, and the bars were zone melted. The vacuum-melted Fe-Mn alloys were induction melted in this Laboratory in MgO crucibles and poured into cast-iron molds. Iron V-5 was purchased from National Research Corp. in the form of a small vacuum-cast ingot. The low-carbon steel was made by induction melting in air at the U.S. Steel Corp. Applied Research Laboratory. The history of the materials prior to the final cold reduction differed; these details are given in the Appendix. The penultimate grain size of the principal materials was kept in the range ASTM 2 to 4, except for the low-carbon steel. PROCEDURES The cold work prior to the final recrystallization anneal was kept constant at 60 pct. It is known that rolling procedure can influence the kinetics of recrystallization of ironI2; therefore, all specimens were rolled in one direction only, between clean,

Jan 1, 1962

By J. Szekely, J. W. Evans

A formulation is given for radiant heat loss from the surface of molten steel held in a ladle and numerical solutions are presented for the resultant integrodif-ferential equations. The results are shown on plots of the net rate of heat loss against time, with the geometlry, emissivities, thermal properties of the walls, and Preheat as parameters. It was found that the rate of the vadiant heat loss from the exposed metal surface was comparable to the conductive losses from the Portion of the metal in direct contact with the walls. The radiant heat loss was markedly affected by the geometry and by the thermal properties of the walls the net radiant heat loss from the steel could be drastically reduced by providing a top cover and also by the provision of preheat. The results of this work are thought to be relevant to heat loss calculatious concerned with vacuum degassing and with operatzons in which molten metals are held in ladles. WhEN molten steel is held or transferred in ladles heat losses inevitably occur. The accurate assessment of these heat losses is of importance in process design considerations, as the temperature of the metal may have to meet rigid specifications in certain stages of the processing sequence. As shown in Fig. 1, the principal mechanisms responsible for heat loss are: i) Conduction into the walls and ii) Thermal radation from the top metal surface (possibly augmented by natural convection) The conductive heat loss may be readily calculated as much information is available in the literature on both the general theory1'' and on its particular applications to ladle heat loss calculations. Evaluation of the radiant component of the heat loss is less straight-forward. In two recent papers it has been shown that the presence of a slag layer 2 to 3 in. thick would prevent any significant heat loss for periods up to an hour,5'" however, should bare metal be exposed, constituting the radiant surface, substantial heat losses could occur. This latter case is of considerable practical interest in various degassing operations and in the vacuum processing of certain specialty steels, where the top surface of the metal is not covered by a protective slag layer. Under these conditions a substantial radiant flux is emitted by the top metal surface; part of this flux leaves the system, part of it falls in the ladle walls. The radiant flux incident on the ladle walls is in part absorbed and conducted away, and in part reflected and re radiated. The purpose of the paper is to present a general formulation of the problem, the resultant solution of which should enable computation of the net radiant heat loss from the metal surface. The principal variables, the effect of which will be investigated, include initial metal temperature, geometry, thermal and radiative properties of the wall, and various modes of preheat. FORMULATION Consider a cylindrical enclosure, shown in Fig. 2, with a diameter D, height H, and wall thickness W, the cover at the top of the cylinder having a wall thickness L. If the temperature of the base (representing the top surface of the metal) is kept constant, say, Tb, the problem is to calculate the net rate of heat loss from the base as a function of time, geometry, the initial temperature distribution, and the thermal properties of the system. As customary, the formulation will consist of the mathematical statement of the conservation of thermal energy within the system.

Jan 1, 1970

By Robert H. Merrill, David W. Wisecarver, Raymond M. Stateham

The US. Bureau of Mines, in cooperation with US. Borax and Chemical Corp. and Kennecott Copper Corp., has investigated the use of the microseismic method to evaluate the stability of large, open-pit slope walls. The method is based on the phenomenon that stressed rock normally emits subaudible rock noises, and the number of rock noises per unit time (noise rate) and the magnitude of the rock noises (amplitude) increase as the stresses in the rock approach the failure stress of the rock. Therefore, the detection and recording of those rock noises serve as a semiquantitative method of predicting the incipient failure of rock. This report briefly describes the three different types of micro-seismic apparatus, the procedures, and the results of microseismic investigations in the slope walls of the Boron mine near Boron, CaL, and the Kimbley, Liberty, and Tripp-Veteran open-pit mines near Ely, Nev. Microseismic monitoring within a frequency band of SO to 5000 Hz indicates noise rates in stable, inactive mining areas are between 0 and 10 noises per hour; the rates in stable, active mining areas are between 10 and 50 noises per hour; and the rate in unstable areas is as high as 2500 noises per hour. High microseismic noise rates in the Liberty pit correlate with the time of nearby earthquakes, indicating that the earthquakes affected the slope wall. The results provide evidence that the microseismic technique is applicable to large pit walls, and that the wide-band, wide-range microseismic equipment appears to be suitable for open-pit investigations. The microseismic method is based on the phenomenon that stressed rock normally emits subaudible rock noises, and the number of rock noises per unit time (noise rate) and the magnitude of the rock noises (amplitude) increase as the stresses in the rock approach the failure stress of the rock. Therefore, the detection and recording of those rock noises serve as a semiquantitative method of predicting the incipient failure of rock. The method has been used for many years to detect incipient failure in roofs or pillars in underground mines. In 1963 the U.S. Bureau of Mines (USBM) started an investigation of the microseismic method in large, open-pit slope walls. The purpose of this investigation was to evaluate the method in open-pit slopes where the rock may be fractured and broken and where the size of the rock mass under investigation is much larger than normally encountered underground. In addition, both the stresses in the rock and the strength of rock near pits are lower than usually found underground. Consequently, there was some doubt concerning the feasibility of the method for open pits, and the economics of such an investigation may have been prohibitive especially if large walls had to be monitored with closely spaced geophones. The successful application of the microseismic method to underground operations has improved safety at little, or no sacrifice, to production or extraction ratios. The anticipated reward in open-pit mining would be the improvement of safety with a minimum sacrifice to mining operations. There is also a possibility that the method could be used to optimize the unloading (stripping) of potential failure areas by the removal of intact rock from the slope wall rather than the cleanup of a slide from the bottom of the pit. This report contains a brief description of three types of microseismic apparatus used in four different pit walls, each of which is different in height, slope, rock types, or has different planes of weaknesses, such as faults, fractures, or joints. Because the geologic features of the pit walls are varied and complex, for brevity, this report dwells mostly on the microseismic apparatus, techniques, the rock noise rates, and the slope movements measured at the various sites. PROGRESS AND DEVELOPMENT The microseismic method was developed over 20 years ago; and the method and examples of investigations in underground mines are summarized by Obert and Duvall. 1 In more recent years, the method has been applied in several underground mines, and an in-situ test under controlled stress conditions is described by Morgan and Merrill. 2 Experience has shown that, on occasions, the microseismic noise rate and amplitude reach a peak value and then start to decrease before a failure occurs in an underground mine; on other occasions, the noise rate steadily increases to a maximum at failure. The method has been applied to slopes by Goodman and Blake,3 and by Paulsen. 4 Goodman and Blake found that the noises corresponded with failures in the slope

Jan 1, 1970

By W. F. Boericke

THE recent completion by the United States Aluminum Company of a $4,000,000 addition to its plant at Massena, N. Y., consisting of a large blooming mill and structural mill, gives this organization, a subsidiary of the Aluminum Company of America, the distinction of possessing the largest aluminum rolling mill in the world, as well as the first mil1 in this country to roll aluminum exclusively. The plant is located near the international boundary line between Canada and the United States, about 3 miles from the St. Lawrence River, to take advantage of the development of cheap hydroelectric power which is needed not only for the manufacture of structural shapes from the ingots, but in the reduction of alumina to the metal by the well-known Hall process as well. A power canal from the St. Lawrence River to the power house on the Grasse River at the plant provides for the waterflow, which, coupled with a drop of 47 ft. in 2% miles, generates 80,000 hp. through vertical turbines. An additional 60,000 hp. is purchased.

Jan 1, 1930

By M. E. Straumanis, J. -P. Krumme

In basic ([KOH + KCl] with a total polarity of 2) or acidic (2N H2SO4) electrolytes and at anodic current densities of more thun 2 to 4 ma per sq cnz, n-type GaAs single crystals of lozo resistivity preferentially dissol~je forming etch tunnels with triangular or civc~ilay cross sections and of a width between 0.5 arid 5 p. These etch tunnels are oriented along any one of the four possible (111) directions of GaAs. However, their growth occurs only in one direction of a given (111) whick apparently is determined by the atomic sequence Ga —As (and not the rezlerse) in respect to an individual valence bridge in the crystal. It is concluded from comparison with the cubic lattice structure of GaAs that the etch tunnels represent macroscopic evidence for the tetrahedral bonds and their polar properties. If the anodic current density is increased the tunnel fomation results in the development of a fibrous surface layer consisting of GaAs. The latter separates frorn the substrate (in an anodic s~irface disintegration process) by the growth pressure of an As,0, filnz forming in the interior of the fibrous layer, 100 to 200 µ under the surface, at more than about 50 ma per sq cni. The fibrous GaAs film has the same crystallographic orientation as the substvate and represents a skeleton of the original crystal. Since the etch-tunnel density in a separated GaAs layer is about 108 c?n-', and the etch tunnels develop only along (111) in a given polar direction, it is assurraed tlmt the dislocations have no influence on the growth of these tunnels. ElECTROLYTIC treatment of smooth surfaces of poly- and single-crystalline GaAs at high anodic current densities causes the formation of porous surface layers.' This phenomenon suggests comparison with effects being observed with magnesium,' indium,, gallium,4 and aluminum5 and known as "anodic disintegration". The purpose of the present paper is to explore and to explain the reasons for the formation of such surface layers on GaAs and, in particular, to investigate the influence of the lattice polarity of this III-V compound semiconductor in the (111) direction on the anodic dissolution behavior. GaAs SINGLE CRYSTALS For the experiments described below GaAs single crystals from the Monsanto Co., St. Louis, Mo., were used. Their impurity levels were below 1 ppm and their dopant levels between 1 and 100 ppm. They were grown in (111) using the Czochralski or the gradient-freeze technique. The crystals had n-type conductivity and electric resistivities between 1 and 5 ohm-cm. EXPERIMENTAL The GaAs single-crystal rods were cut perpendicularly to (111) into wafers of about 1 mm thickness using a wire-blade crystal slicer and an aqueous slurry of Sic or a diamond saw. The orientation of the faces of these wafers were checked by Laue back-reflection patterns. If there was a deviation from (111) the faces were abraded under a certain angle using grinding paper and distilled water. The damaged surface layer was removed from each crystal by chemical etching with a mixture of 1HF:1HNO3: 1H20 or 2HF:1HNO3:2HAc (glacial). {110) faces were obtained by mechanical cleavage, producing surfaces which did not require a further treatment. The GaAs wafers were mounted using "alligator" clamps instead of soldered electrical contacts.' Only the bare crystal surfaces were dipped into the electrolyte. The clamps were coated with insulating wax to prevent any contact with the electrolyte. The experiments were carried out in aqueous 2 N H2so4,' or in an aqueous solution of KOH and KCl1 (1 mole KOH + 1 mole KCl in 1000 cu cm solution). Anodic current densities up to several hundred ma per sq cm were applied for periods between 30 sec and 2 hr. For the purpose of investigating the initial steps of disintegration the anodic current density applied never exceeded 20 ma per sq cm. The films which partially separated from the anodic surfaces under high-field conditions were treated with KOH to further their detachment by dissolving the As2O3 formed. The washed and dried films were pasted to strips of filter paper, and Laue pictures were made. The back-reflection patterns obtained were compared with those of the original anode surface before and after anodic dissolution. Furthermore, space reciprocal lattices7 were constructed from asymmetric rotation crystal patternsa which permitted the determination of the crystallographic orientation of the detached films of the corrugated anodic surfaces. The disintegration products were identified from assymmetric powder patterns.8 The polarity of the {111) faces was determined by chemical etching with mixtures of 1HF:1H2O2(30 pct): 2H2O or 1HNO3:2H2O. Different patterns on each of two inverse (111) sides appeared.'-l8 The correlation of these patterns to the Ga{111) or the As(111) side has already been established by the use of light figures,18-20 by X-ray diffraction near the absorption edges of gallium and arsenic,'lmZ4 and by LEED measurements.25 The geometric structure of these surfaces and the interior of the anodically attacked crystals were observed and photographed with a high-power microscope using oil immersion objectives up to magnification of X1720.

Jan 1, 1968

By Kurt Stock

The war caused a demand for enormous quantities of high-grade zinc, which were not available and could not be produced from pure ores in sufficient amounts and in the time required. Redistillation of virgin spelter on a large scale was practiced to supply this demand; this paper gives a full description of the process used by the Oklahoma smelters of the Bartlesville Zinc Co. As the redistillation of zinc has become of historical interest only, having been superseded by the electrolytic process, it was deemed advisable to give expression to this phase of the metallurgy of zinc that, in the past, had never gone beyond laboratory experimentation. THE grades of spelter demanded by the consuming industries were not definitely established until the American Society for Testing Materials undertook to fix specifications, based on the varying percentages of the common impurities (lead, iron, and cadmium) as follows: TOTAL, NOT LEAD, IRON, CADMIUM, OVER. PER PER CENT. PER CENT. PER CENT. CENT. A. High grade 0.07 0.03 0.05 0.10 B. Intermediate 0.20 0.03 0.50 0.50 C. Brass special 0.75 0.04 0.75 1.20 D. Prime western 1.50 0.08 The question which grade was the best for certain purposes and why was left unanswered. The conservatism of the zinc-smelting industry and the unwillingness of the spelter-consuming industries to engage in research work prevented the full benefits being obtained that such standardization promised. The custom smelters, producing spelter in pigs or plates, found it impossible to adhere closely to the established limits on account of the variety of ores treated; and the smelters with long-established and known brands, or those manufacturing their metal into marketable products, like sheet zinc, did not have to abide by the newly established grades based on chemical percentages.

Jan 7, 1924