By J. W. Halley, G. L. Plimpton

BECAUSE of the two distinct stages in the solidification of rimmed steel, segregation in the rimmed ingot is more complex than that in the killed or semikilled ingot. In the earlier stage, chemical reactions, resulting in evolution of gas and vigorous stirring of the metal, effect a degree of negative segregation unique to rimmed steel. The composition of this zone constitutes the principal quality advantage of this type of steel. In the later stage of solidification, after the evolution of gas has ceased, the segregation follows the general pattern of a more completely deoxidized steel. However, the composition of the liquid remaining after the first solidification stage varies markedly from that of the original melt, some constituents having been partially removed as reaction products while the concentration of others has been intensified by rejection from the metal solidifying in the first zone. The aim, from the standpoint of segregation, in rimmed steel of high quality is to effect a maximum negative segregation in the rim zone without excessive concentration of undesirable elements at the center of the ingot. To achieve this aim, the composition of the melt may be varied and the furnace and pouring practice may be adjusted within certain limits. It is the purpose of this study to discuss segregation in rimmed steel from the standpoint of the mechanisms that produce it and to survey the phases of open-hearth practice that influence those mechanisms. MECHANISMS PRODUCING SEGREGATION The mechanisms that determine the degree of segregation in the rimmed ingot are closely interrelated, making it difficult to select the primary factors and to determine a satisfactory order for presenting them. For instance, the question of sulphur segregation is relatively simple, since sulphur is not directly involved in chemical reactions in the ingot; but its concentration in the rim zone is dependent not only on its original analysis in the melt, its segregation coefficient, and the freezing rate, but also on the rate of its removal from the impure film on the solidifying surface. This washing action involves all the factors (such as freezing rate, the carbon-oxygen product, pressure, etc.) that determine the rate of gas evolution and hence the efficiency of film removal. Sulphur distribution between the rim and core is affected by the volumetric ratio between the two zones, and its segregation in the core is a function not only of the freezing rate of the core but also of all the foregoing factors that determine its concentration in the metal when solidification of the core starts. To simplify the presentation, it is proposed to treat the mechanisms affecting segregation independently in this section, reserving a discussion of their over-all effects for the section in which actual segregation data are given. The factors affecting segregation will be treated in the following order: (I) differential solidification, (2) removal of constituents as

Jan 1, 1944

By L. H. Robinson

A proposed method of drilling utilizes sequential detonation of two types of explosive charges delivered to the hole by a conventional drilling fluid through pipe. A shaped charge first produces a long thin hole. A second charge, called a gauging charge, is pumped into the thin hole, explodes, and enlarges it to full gauge. In one suggested configuration, the explosives are contained in cylindrical capsules 4- to 5-ft long. A drilling head is positioned 2- to 3-ft off bottom. When a capsule is pumped to the bottom of the hole and stops, pressure inside the drill pipe increases and differential pressure detonates the explosive. Primacord along the length of the capsule disintegrates the capsule. The debris circulates out of the hole with the drilling fluid. The gauging-charge action was examined using 2-ft cubes of Berea sandstone. The sandstone (18 per cent porosity) was vacuum-saturated with water and surrounded by concrete. To prevent reflected tensile pulses, the acoustical impedance of the concrete matched that of the sandstone. A 750-psig pressure was applied to a drilling fluid within a shaped-charge-formed hole before detonating the gauging charge. In these tests, 190 gm of rock were removed for each gram of explosive detonated. A similar series of experiments on low-porosity (0.40 per cent) metamorphic limestone provided a more rigorous test. Extensive fracturing from the gauging-charge action prevented an estimate of the volume of the expanded hole. The diameter of the hole was irregular, ranging from about 2 to 4 in, or about fivefold larger than the hole created by the shaped charge. INTRODUCTION In the past, explosives have found a varied but somewhat limited use in the oil field. An early well stimulation technique, still in use today, in vo lves shooting ni troglycerin to en large the borehole and to increase matrix permeability near the wellbore. Bullets and jets are now the conventional method of perforating casing and tubing. Detonations are frequently used to "back off" or "shoot off" stuck pipe and, of course, seismo-graphic work has long depended on explosive-generated pulses to find attractive earth structures. Efforts to use explosives in drilling operations have received limited examinations1-3 which, in one respect, is surprising because explosives offer one way to transmit large amounts of energy directly to the bottom of the hole. Recently, Ostrovskii l described a Russian method of drilling with explosives that utilizes small capsules containing explosives which are pumped into the mud stream to the bottom of a borehole. As the capsules leave the end of the drill pipe, a detonation mechanism is armed. Impact detonates the explosive. In another configuration, two liquids (an oxidizing agent and fuel) in the capsule are separated by a frangible membrane. Separately, the liquids are nonexplosive. Near the bottom of the drill pipe, the capsule passes through a narrow constriction which ruptures the membrane. The mixing of the liquids produces an explosive. Impact is again used to detonate the explosive. About the time Ostrovskii was developing his method, Humble Oil & Refining Co. was independently doing research on another explosive drilling concept based on the sequential detonation of two types -of explosive charges. The proposed technique consisted of alternately pumping a shaped charge and then a "gauging charge" down a well. The shaped charge should drill a long, tapered hole, and the gauging charge should expand it to full gauge. This paper presents the visualized drilling concept and gives results of laboratory work which showed that sequential firing of charges can form hole at an attractive charge-to-rock removal ratio. An important finding was that increased environmental pressure, which is to be expected in wells, increases rock removal efficiency of the gauging charge.

Jan 1, 1966

By E. J. Rapperport, M. F. Smith

A presentation of the W-Ru constitution diagram is given. Techniques utilized in the determination of phase boundary values include electron micro-probe analysis of two-phased alloys and diffusion couples, as well as normal metallographic and X-ray methods. The primary features of the diagram are: 1) a terminal solid solution of ruthenium in tungsten with a maximum solubility of 23 at. pct Ru at 2300°C; 2) a terminal solid solution of tungsten in ruthenium with a maximum solubility of 48 at. pct W at 2205°C; 3) a o phase of maximum breadth about 6 at. pct based on the composition W3Ru2 which forms peritectically from the melt at 2300°C, and which decomposes eutectoidally at 1667 °C to form a twigs ten and 0 ruthenium; 4) a eutectic at 45 at. pct Ru and 2205°C with the products being o plus ß ruthenium. THE W-Ru diagram has previously been studied only in a cursory fashion. Raub and alter' obtained a 1400°C isotherm in which they observed no intermediate phases, and on which they established the limits of solubility as 36.5 at. pct W in ruthenium and about 1.5 at. pct Ru in tungsten. In addition, Obrowski2 found a o phase forming peritectically from the melt and existing only above 1650°C. Below this temperature the phase was presumed to decompose eutectoidally. The present work finds the diagram as given in Fig. 1. I) EXPERIMENTAL PROCEDURE The materials used for alloy preparation in determining the W-Ru constitution diagram were 99.9 pct pure ruthenium powder supplied by Baker Chemical Co., and 99.9 pct pure tungsten powder from General Electric Co. Typical analyses of these elements are given in Table I. Initial alloys at 10 at. pct intervals were prepared from the metal powders by the following method. Powders sufficient for 25 g of the alloys were weighed out with an accuracy of 0.1 mg and blended mechanically. After blending, the powders were compacted, in a steel die, at approximately 30,000 psi. The compacts were sintered in an electric vacuum furnace in order to remove adsorbed gases and to achieve partial densification prior to arc-melting. Vacua of 10-4 mm Hg or less were maintained in sintering as the furnace temperature was raised to approximately 2000°C. Sintering times ranged from 10 to 20 hr. The sintered compacts were arc-melted under a protective atmosphere of purified helium. Melting was conducted on a water-cooled copper hearth, utilizing a nonconsumable tungsten electrode. In the melting process, each alloy was turned over and re-melted on opposite sides from four to six times to ensure complete melting and to eliminate gross in-homogeneities. The arc-melter used had a vacuum capability of 5 X 10-6 mm Hg, and a leak rate of about 20 -liters per hr. Chemical analysis techniques for refractory metal-platinum group metal combinations are not well-established; therefore, composition control and determination depended principally upon weight-loss observations and calculations. This consisted in weighing each alloy after sintering and after arc-melting, and calculating the maximum and minimum composition values, assuming the total weight losses to be first all tungsten, and then all ruthenium. Since composition uncertainty was directly related to weight loss, care was taken to minimize losses in handling, compacting, and melting. Prior to homogenization and equilibration the as-arc-melted alloys were analyzed in several

Jan 1, 1964

By Leo F. Reinartz

Part II of a four-part series on the history of steelmaking in the US, points out the inadequate safety and living conditions that existed in steel mills at the turn of the Century. Also defined are furnace and process developments. OPERATIONS in steel plants today are highly mechanized. Men work in light, clean, orderly melting shops, making it difficult for old timers to convince young men that primitive, hazardous conditions existed in steel plants at the turn of the century. Working conditions then were very poor as compared to present day standards. In small plants especially, sanitary, locker, and washroom facilities, first-aid practices and stations were un- known Accidents were frequent and severe. Workers had a fatalistic attitude toward getting hurt. He who had an accident was looked upon as a hero. A dirty bandanna often served as a bandage. Infections were frequent. Electric cranes were in their infancy and broke down often Cables had not as yet replaced chains. Pig iron and scrap iron were loaded by hand in the stockyard, and stockyard locomotives were un- known; mules served as the usual motive power. It was not unusual to see recorded a delay of ½ hr in charging a furnace because of a balky mule. Furnace operations A few plants had primitive charging machines, but most furnaces were charged by placing scrap or pig iron on the paddle of a long peel, which rested on a bar across the furnace door opening. Laborers at the handle end of the peel, using the bar as a fulcrum, would heave the material into the furnace by a down and sideward motion of the peel handle. In time they became expert in placing these materials in the furnace, but it was hard, hot work, and a long time was required for charging. Cold charges of 25 tons required more than 12 hr for melting and re- fining the steel. Ports, doors, and frames were not water cooled. The charging and working area in front of the furnace was covered with steel plates. They were hot and often warped by the intense heat of the un- insulated checker chambers directly below. In the summer, working conditions on the charging floor were almost unbearable. Silica refractories were of poor quality. Because of this, and the inadequate training of furnace men in fuel control and furnace operations, roofs, front and back walls, and ends burned out rapidly. Dolomite machines were unknown; consequently, furnace banks and hearths were fettled with dolomite by the use of hand shovels. The round system required six or more men. Each man took a shovelful of dolomite and, in his turn, deposited it on the back wall and bank by a dexterous forward swing and twist of the shovel. The upward swing of the shovel partially protected his face from the searing heat of the furnace coming out through the wide-open door. Considerable skill and stamina were required to do this job properly. Reverse valves, usually of the cast-iron butterfly type, were located below the charging floor. They were operated by long levers on the charging floor level men they became warped, because of heat and abuse, great strength and skill were required to reverse them. Furnace operations were difficult. The quality and quantity of producer gas coming from irregularly stoked, hand-operated gas producers was uncertain and unreliable. Furnace Linings and ports were quickly burned out. Poor bottom and side-wall refractories, indifferent and inexperienced crews, as well as irregular re-

Jan 1, 1961

By R. D. Reiswig, J. M. Dickinson

The 0s-Ir equilibrium diagram was determined. The diagram is of the simple peritectic type, with a peritectic temperature of about 2660°C. The solid miscibility gap is narrower than previously reported, the nearly vertical solvus lines occurring at about 42 and 63 wt pct 0s. Widmanstaetten figures resembling martensite in some of the two-phase alloys account for a previously suspected transformation. In view of the long history of use of such alloys, it is surprising that the 0s-Ir equilibrium diagram has not yet been completely determined. The boundaries of the miscibility gap in this system have been estimated to be between 24 and 39 wt pct 0s and 79 and 100 wt pct OS. It has been predicted3 that alloys of ruthenium, osmium, and rhenium with the fcc platinum metals should solidify peritectically in their two-phase regions. The metallographic examination of natural osmiridium alloys has been said4 to indicate, by the presence of a martensitic structure, the existence of a transformation or a phase separation. On the basis of superconducting transition temperature measurements, a 70 at. pct 0s alloy was found5 to be two-phase prior to annealing. EXPERIMENTAL The elemental components used in this work were obtained from several suppliers as sponge. The purities, stated by each supplier to be in excess of 99.8 pct, were confirmed in each case by a semiquantitative spectrographic analysis. The pure components were premelted in an inert-gas tungsten arc furnace with the evolution of some fume, crushed, and pickled for use as alloy melting stock. Upon arc melting to the final compositions, no fume evolution was observed. Because weight losses of the order of 15 mg or less were observed in preparing alloy buttons weighing 15 g, "synthetic analyses" were used in determining the compositions of the alloys. Alloys used in this investigation contained 15, 20, 33, 40, 42, 43, 45, 50, 55, 60, 63, 64, 66, 70, 79, and 80 wt pct 0s. Heat treatments of the alloy buttons and pieces thereof were performed in a previously described6 tungsten tube furnace under pressures of 105 torr or less. It was found that homogenization treatments on the specimens were essential to remove the severe coring which was present, a 3-hr treatment above 2300°C removing all the metallographi-cally visible evidence of coring. Following the various heat treatments, the specimens were "vacuum-quenched" by melting a tungsten fuse wire and allowing them to drop onto a water-cooled copper plate. In a few instances, specimens were quenched into molten tin for comparison, but no difference was apparent. Vacuum-quenched specimens cooled from 2400°C to below a red heat in less than 60 sec. Typical equilibration times varied from 3 hr above 2300°C to 88 hr near 1100°C. The utilization of successively longer equilibration times and the approach to equilibrium from both directions indicated that the times used were sufficient to give a close approach to true equilibrium. Heat-treatment temperatures were measured with a calibrated Leeds and Northrup optical pyrometer through a 0.120-in. lateral sight hole in the tungsten heater tube. It was known that the assumption of black-body conditions inside the 1-in.-diam by 10-in.-long tube was unwarranted. The empirical results of work with thermocouples and melting

Jan 1, 1964

By R. S. Kinasevich, D. D. Crabtree, D. W. Fuerstenau, T. P. Meloy, A. L. Mular

This paper presents details of the concept that size reduction in comminution machines takes place by three mechanisms; namely impact, abrasion, and chipping grinding. Experimental evidence is presented to show that each of these comminution mechanisms produces particles of a characteristic size distribution. The actual product from a comminution device has been postulated to be the result of a composite of these three types of mechanisms. Composite curves are demonstrated for a material following the Gaudin-Schuhmann, Gaudin-Meloy, and Rosin-Rammler size distributions. About forty years ago, Gaudin1 showed that grinding may be considered a combination of impact and attrition. Since that time, major efforts have been devoted to studies, both experimental and theoretical, of impact and compression fracture, while attrition has been almost wholly neglected, at least quantitatively. A significant attempt to distinguish between attrition and impact grinding is the work of Tanaka2 in Japan. By means of an instrumented abrasion grinder and a drop weight device, he determined coefficients relating the increase in surface area of various materials to the energy expended by the two methods of comminution. He showed that physical properties of a material determine its response to attrition and impact grinding. By extending his ideas to ball milling, he concluded that to a large extent the basic comminution process in a ball mill is due to the impact of falling media. Because Tanaka used a mass of particles in his drop weight device, however, he did not obtain pure impact size reduction. The purpose of this paper is to define basic mechanisms of size reduction, to verify that each has a characteristic and meaningful distribution curve, and to show how a combination of these mechanisms results in a size distribution very like that produced by grinding mills. DEFINITION OF COMMINUTION MECHANISMS The product from a grinding device will be considered to be the sum of the contributions resulting from the action of three basic mechanisms of size reduction which operate in a ball and rod mill. These are impact grinding and two forms of attrition, namely abrasion grinding and chipping grinding. Each is defined below. Impact Grinding: If a straight line is obtained when the cumulative weight fraction finer than a given size is plotted on log-log paper as a function of that size, the slope of the line is defined as the distribution modulus. A number of investigators 3,4,5 have shown that impact fracture of single specimens of different composition and shape results in a distribution of daughter particles that exhibit a distribution modulus of unity. This has also been true for materials broken in slow compression. Moreover, under slow compression or impact fracture conditions, theoretical distribution equations6*' which approximate the Gaudin-Schuhmann distribution when the distribution modulus is close to unity agree reasonably well with the experimentally obtained products. If one now considers a comminution process where many impact or compression fracture events are taking place, then any rational summation of the individual events yields, in the finer size range, a Gaudin-Schuhmann distribution whose distribution modulus is also unity. If the size distribution of the product from a mill has a distribution modulus of unity, it is implied that particles are fractured in a manner which results in a comminution event having a distribution like that obtained for the breakage of single specimens. These impact events would occur when a particle is smashed between balls or between a ball and the mill liner. Attrition, on the other hand, is that form of grinding which cannot be called impact grinding, and comprises both abrasion and chipping grinding. Abrasion Grinding: Abrasion is a form of surface wear resulting when particles rub against each other or against balls or the mill liner of a tumbling mill, somewhat like a piece of wood being rubbed over a piece of sandpaper. The surface wears at a more or

Jan 1, 1964

By E. A. Breitenbach

A computer program has been developed to afford rapid and complete quantitative log analysis for exploration and production decisions. The computation consists of automatic selection of tops and bottoms of porous intervals from the digitized data, and then point-by-point calculations within each selected interval. Nearly all log types can be analyzed. This paper presents the calculation techniques found to be appticable to machine evaluation and gives examples of their use. INTRODUCTION As the quantitative interpretation of well logs entails repetitive use of charts and equations, it is natural that digital computer programs would be written. A Universal Log Interpretation Computer Program (ULICP) has been developed to afiord rapid and complete analysis for exploration and production decisions. Application of this program enables the log analyst to: (I) apply rapid quantitative log analysis for exploration and production decisions on either a field, a well or on a single zone basis; (2) apply concepts of interpretation requiring detailed numerical analysis; (3) analyze all porous intervals on each log, rather than a few selected zones, and complete the analysis in less time than previously required. Computations are reported for every digitized point in each zone; (4) use empirical techniques applicable to a given area as an integral part of the computation; (5) experiment with the empirical coefficients and exponents in the interpretation equations to find the best possible solution; and (6) automatically plot both the original and computed data to scales analogous to the field prints. The primary utility of a log interpretation program stems from its ability to do an overwhelming amount of work with very little man-power. If a calculation procedure or thought process can be formalized to the extent that step-by-step logic can be written, a computer program can be developed that follows this logic. The major question is one of economics. A feasibility study of the costs for such a program indicates that digital processing is economical primarily as a means of increasing the productivity of the log analyst. In effect, the probability of missing productive intervals in any well, because of a lack of time to do detailed calculations, is greatly reduced. The nucleus of ULICP is programmed to compute large sections of a suite of logs by selecting zones automatically and then performing all pertinent computations on a data point by data point basis within each zone.'.' An entire suite of logs can be processed in this manner with very little manual intervention. Sufficient programming logic is available so that each log analyst can request computations pertinent to his area. These requests are made by simple additions or deletions of information on the input header cards. Hence, the log analyst is always in complete control of the computation process. The evaluation of a suite of logs requires pre-editing, digitization, computation, presentation of results and interpretation. Work by the log analyst is reqilired only in pre-editing and interpretation. Thus, he is allowed more time for comprehensive interpretation, rather than calculation. For continuity, the discussion of ULICP is organized sequentially: pre-editing, digitization, computation and presentation of results. DISCUSSION PRE-EDITING The extent of pre-editing prior to computation is dependent on the format of the original data. For analog prints, it requires inspection, correlation and editing of the logs, plus the entering of required data an special forms. For digitized data such as magnetic tape field recordings, only the special forms are necessary. The process for analog prints will be given here. The inspection and correlation process involves the selection of sections for digitization and the correlation of the traces to a common depth. To decrease the cost of digitization, traces that exhibit large variations in shale formations can be redrawn to a non-zero baseline. The next step is to enter all pertinent data on the input header cards. The header cards presently used for ULICP are presented as Figs. 1 through 6. Cards 1, 2, 3 and 4 (Fig. 1) are defined as the Main Header Cards. They describe the particular well for output identification and give basic information. Cards 5 through 15 (Figs. 2 through 6) are defined as the Block Header Cards. As such, they define the log types and the interpretation parameters for the block of data immediately following. Cards 1 through 10 are required for every computer run. Cards 11 through 14 pertain only to nuclear logs. Card 11 is required if any nuclear log is supplied, and cards 12 through 14 are required only when gamma-ray, density or neutron log data, respectively, are supplied. Card 15 (Fig. 6) must be supplied when cross-plot calculations are required. Either two- or three-component

Jan 1, 1967

By G. F. Bolling

Single crystals of each metal were deformed at 77°K and heated at constant rates, variously in the range 0.125" to 4o°Kper min from 77" to -390oK, while being monitored in an X-ray diffractometer. Changes in diffraction-peak heights and line breadths were used to ascertain the temperature ranges of recrystalliza-tion. The results were subjected to the analysis of nicholas' in order to obtain the rate-controlling activation energies,Q. In this analysis no recourse to a separate and distinct nucleation stage is required and the results of studying recrystallization proved consistent with the hypothesis of a constant number of nuclei or equivalent hypotheses. The values Pb = 5.5 ± 0.5 keal per mole Zn ~ 7.5 Sn - 5 Bi - 9. 5 correspond for lead, zinc, and tin to activation energies obtained elsewhere for grain boundary migration, and for bismuth and lead to previous studies of re-crystallization by Barrett.6 This correlation allows the conclusions that interference from recovery was minimal and that the observed recrystallization rates in these pure metals are effectively governed by grain boundary migration. Good agreement was not found between the results of this kind of study in zone-refined aluminum and previous work; and supplementary isothermral experiments involving hardness tests and metallography did not resolve the discrepancy. Nevertheless, at least a range,Q = 11.5 ± 2 keal per mole, can be assigned to the activation energy for boundary migration in aluminum. An experimental study of one aspect of the recrystallization process is presented here for four metals of different crystal structure. The metals chosen for study were all zone-refined to reduce impurity effects, but the attendant high purity presented a difficulty. For any reasonably high driving force a "re-crystallization temperature", TR, is in the range of 0.25 T,, where T, is the absolute melting point, and study was therefore restricted to lower temperatures. An X-ray technique under constant heating-rate conditions adequate above 90°K was devised for the study; in consequence, a newer type of analysis following Nicholas1 had to be used to obtain quantitative information about activation energies. The standard methods of studying recrystallization have involved the comparable analyses of Johnson and Mehl2 and Avrami3 which are reviewed by Burke and Turnbull.* The general analysis4 which is applied only to isothermal studies using any of various investigative techniques states:

Jan 1, 1968

By George F. Comstock

It has been known for many years that the alloy containing 90 per cent. copper and 10 per cent. aluminum can be hardened, like steel, by quenching from a suitable temperature, and that the hardened alloy can be softened again by annealing or drawing the temper. It does not seem to be generally appreciated, however, that the effect of the first slight reheating after quenching is actually increased hardness, the softening effect not taking place until a certain temperature of "drawing" has been exceeded. This paper gives the results of a few experiments on various specimens of cast 10 per cent. aluminum bronze, quenched for maximum hardness, and subsequcntly annealed at different temperatures. The hardness measurements were made with both a scleroscope and a standard Swedish Brinell machine; some peculiarities of the scleroscope test on this material are described. The author is not aware of many previous investigations of the hardness of this alloy when quenched and drawn, but two important papers on the subject should be mentioned. The earliest was by Portevin and Arnou,1 in which it was stated that tempering quenched 10 per cent. aluminum bronze at 400" C. increased the hardness as compared with the quenched untempered alloy and that reheating above that temperature ' was necessary to obtain any softening effect. A later paper was by Seidell and Horvitz,2 who mentioned Portevin and Arnou's work, but did not report any increase in hardness obtained

Jan 1, 1925

By C. G. Durdaller, W. H. Robinson, G. M. Pound

The nucleation rate of the a (pay) to 0 (white) tin transformation was measured as a function of temperature and a tin particle size using an X-ray diffraction technique. The powder specimens of a tin were essentially monodisperse and the small dinzension of the particles of these specimens was varied from 13 to 75 p. Several types of nucleation sites of differing potency were fbund to be operative in the nucleation process, but it could not be determined whether these sites were on the free surface of the tin particles or within the volume. Assuming that they were on the free surface, the average density of the most potent sites was calculated to be 2.5 to 5.3 x 10' sites per sq cnz through the application of a Poisson distribztion finction to the isothermal data. Analysis of the temperature dependence' of the rate constmts at a given fraction transformed suggests that the active sites are regions of higher free energy and not catalytic interfaces. Appreciable induction periods were observed at the lower temperatures of transformation. Experimental studies1 of solid-solid phase transformations have led to the belief that the new phase nucleates at structural imperfections. The purpose of the present work was to learn more about the mechanism of nucleation in solids and the nature of the singularities at which nucleation occurs. In this investigation nucleation rates in the isothermal transformation of gray to white tin were measured by an X-ray diffraction technique using essentially monodisperse powders of gray tin. This particular phase transformation was chosen for study because it presented fewer experimental difficulties than most others. The experimental temperature-control problems were minimal because the two phases coexist in equilibrium at 13.3"C, and measurable transformation rates occur at temperatures only slightly above room temperature. The growth rate of the P phase into the a2 is sufficiently fast to make the measured transformation rate equivalent to the nucleation rate, provided that the particle size of the samples is small enough; for the experimental temperatures used in this study, the particle diameter must be less than 100 p. EXPERIMENTAL TECHNIQUE The P tin used in this study was obtained from Capper Pass and Son Ltd., North Ferriby, Yorkshire, England, and was of 99.999 pct purity. It was transformedS to the a phase and ground into a fine powder in an agate mortar. This powder was separated by a Roller air classifier into seven fractions whose dimensions, as determined by microscopic measurement of many thousands of particles, are given in Table I and whose distribution of size within each fraction is given in Figs. 1 and 2. The shape of the particles was roughly that of an oblate spheroid,

Jan 1, 1964

By W. C. Lilliendahl, H. W. Highriter

THE method developed and used in this laboratory for the production of metallic uranium of such purity that it is ductile and can be cold-worked to fine wire or thin sheet by rolling has already been described1. It consists, briefly, in the electrolysis of potassium uranous fluoride (KUF6) in a molten bath composed of equal parts of sodium and calcium chlorides. The bath is contained in a graphite crucible, electrically heated to about 775° C., the crucible serving as the anode for electrolysis. The uranium deposits in finely divided form mixed with salts upon a molybdenum cathode suspended axially in the crucible. Upon completion of the electrolysis the cathode is removed and cooled, the deposit broken and leached to remove salts. The metal powder is washed with water and dilute acetic acid and dried in vacuo to reduce oxidation. Suitable amounts are then pressed into pellets and heated in vacuo by high-frequency induction, using a thoria crucible. The uranium melts and flows away from the pellet, leaving a shell, which is largely oxide. In general, this method produced a satisfactory metal, although at times the uranium was not ductile. The investigations recorded here were made to find the cause of this embrittlement. It was known that the metal generally contained carbon, derived from disintegration of the graphite crucible in which electrolysis is conducted, in amounts dependent upon the thoroughness of washing the metal powder. Accordingly, analyses of several samples, both ductile and brittle, were made by combustion and absorption of CO2 in Ascarite, using air instead of oxygen to reduce the temperature and rate of oxidation. Several of these metals were made with special precautions to reduce carbon content. The results show no relationship between ductility and carbon content in the range investigated (Table 1).

Jan 1, 1935

By F. L. Wolf, G. E. Alderson

The reclaiming of nietallics from slag and sweepings is of vital interest to every brass-foundry man, but the first cost and interest on the investment often make it prohibitive for the small foundry to enjoy the benefits of a complete concentrating unit. However, the cost of such an installation and the cost of operation are often exaggerated to such an extent that foundries dispose of their copper-bearing refuse at a great loss. This paper gives the actual costs and the returns obtained in the reclaiming plant used at the Ohio Brass Co. This plant is divided into two sections—the preliminary treatment and concentrating departments. In the former occur the screening, crushing, and hand-picking operations whereby rnost of the non-valuable and heavy metallic constituents are removed. The concentrating equipment consists of an elevator, bins, jigs, ball-mill, arid table. Preliminary Treatment The preliminary treatment varies, depending on whether the material is slag, foundry-floor sweepings, or brass casting-floor sweepings. Material of the first class is produced from the operation of six Steele-Harvey and six Schwartz furnaces; the second class represents sweepings from an average of thirty-five. molding floors per day: and the last is collected around the sprue cutters and knockout bench. Treatment of Slag The slag, analyzing 30 to 40 per cent. copper, is passed over a 3-mesh yard screen (Tyler standard mesh) stretched on an inclined rectangular frame supported by adjustable legs and equipped with a hopper which directs the undersize into a barrow. The fine product, running about 20 per cent. copper and representing 20 to 25 per cent. of the total slag, goes direct to a storage bin for concentrator frrd. The oversize is charged into a No. 2 Hill cinder crusher, which takes 175 to 200 11,. to a charge and crushes two charges per hour through 'a No. 4 riddle. It

Jan 1, 1921

By Douglas A. Sloan

Who would believe that young elementary school children could understand something as complex as the mining industry? The Challenge The challenge of accomplishing this is tremendous. An examination of Canadian school children indicated that they knew very little about the world of work in general, and hardly anything about the mineral resource industry in particular. It calls to mind the story about two youngsters who decided to play house. The little girl played her role well as she went about the house doing things she had watched her mother do every day. When it was the little boy's turn, he grabbed his lunch, waved goodbye to his "wife," jumped on his bicycle and pedalled furiously down to the end of the driveway-where he stopped. The youngster explained that he saw his dad go out of the driveway each morning, but he didn't know where he went, or what he did on the job. When you stop to consider the number of families today with two working parents, you can begin to appreciate the importance of the opportunities for role identity provided by this project. The Approach The challenge of teaching the school children of Canada about the world of work and, specifically, the mining industry is the challenge which the Canadian Institute of Mining and Metallurgy met with the Curriculum Development Research project. It started when a small, dedicated group of Vancouver members met Dr. Doreen Binnington. After this meeting, Dr. Binnington, an expert in curriculum development at the University of British Columbia, set herself to develop a curriculum program for the elementary shcools which accomplishes two main goals: It uses the "Identity Approach," developed by Dr. Binnington, an expert in curriculum development at the enable students to understand and appreciate the contribution of people, in this case, working with mineral resources. It has pupils enthusiastically exploring the importance of rocks, minerals, and the mining industry in their lives [(Fig. 1)]. Evolution of the Curriculum Development Research Project When the curriculum development research project was presented to the Vancouver Branch of the Canadian Institute of

Jan 1, 1981

By Eugene A. Stephenson

The writer apologizes for presenting this very elementary analysis of one aspect of proration, but a search of the literature failed to disclose any concrete illustrations of the effect of various proration formulas upon the allowable oil produced by tracts of different sizes. Many engineers have doubtless made somewhat similar calculations and are fully acquainted with the results. The various allocation formulas that are in use are based on one or more of the following factors: (1) wide-open well potential, (2) potential through an orifice, (3) uniform well allowable, (4) acreage, (5) sand thickness, (6) bottom-hole pressure, (7) productivity index, and (8) volumetric displacement. Of these, the unrestricted potential formula, or open-flow test, and the uniform well allowable are commonly regarded by engineers as those least likely to give each producer his proportionate share of the oil or gas, as represented either by acreage or by sand thickness, or both, except when the wells are located on tracts of large size. Unless the mechanical equipment that may be used during the potential test and the method of taking the test are both specified, the net result of the potential formula is to practically force the operators to use special equipment and adopt special procedures prior to and during the potential test, so as to secure the largest possible allowables. Much ingenuity and skill have been devoted to this,problem, but the general effect is to permit excessive allowables for very small tracts, and stimulate unnecessary drilling. It is interesting to compare some of the high yields from the Wilcox horizon at Oklahoma City with each other, as an illustration of the effect of an allocation factor based solely on potential (Table 5). One of the glaring instances is a well on a ½-acre lease, which had produced, as of September 1936, at the rate of almost 3,000,000 bbl. per acre. This is at least twice as many barrels as could have been present under the property if the reservoir had consisted of a tank of oil 200 ft, deep and 56 acre in area. Numerous combinations of acreage, potential, bottom-hole pressure, sand thickness, etc., have been proposed and are in use in various fields.

Jan 1, 1937

By Wallace Ralston

The East Texas area includes the northeast 38 counties of the state of Texas. It covers all, and extends beyond, the borders of what is commonly described as the East Texas Basin. It is one of the most important oil and gas-producing areas of the Mid-Continent Province. It includes four important oil fields—Van, East Texas, Cayuga and Long Lake— and the recent extension of Rodessa field into Cass County, Texas, may prove to be of major size. Four commercial gas fields are in this area— Bethany, Waskom, Cayuga and Long Lake. Up to January, 1936, all of the oil has been produced from the Upper Cretaceous formations, and most of that from the basal member, the Woodbine sand. Gas is produced from both the Upper and Lower Cretaceous formations. Development in Fields East Texas Field.—This field continued to dominate the drilling and production situation throughout the United States. There were 4036 wells completed in this field during 1935; that is, 365 more wells than were completed during 1934. Drilling activity was due to close spacing of wells and the addition of 10,000 acres to the field. The field is now drilled to a density of one well to 6½ acres, which is certainly more wells than necessary for economic production of the field. The close spacing of wells is due mostly to the type of proration, which is per well allowable based on a potential test, and does not take acreage into consideration, and also to the numerous small acreage tracts such as town lots and excess strips. The field now has 19,519 producing wells. The allowable production for the field during 1935 was 161,118,659 bbl.; estimated production, including illegal or "hot oil," was 174,200,150. The illegal production of oil gradually decreased throughout the year, until an estimated low was reached of 20,500 bbl. daily during the months of November and December. The price of oil remained at $1.00 per barrel throughout the year. As stated, about 10,000 acres were added to the field during the year, making a total of 128,000 productive acres. There is a possibility that

Jan 1, 1936

By Roscoe C. Clark

In a previous technical note' by Walter Rose, evidence is offered in support of the contention that "the possibility of describing oil recovery features in terms of capillary pressure phenomena has not been established entirely." It is not the purpose of this note to present further discussion of this possibility but rather to point out that the argument presented there does not appear to be generally valid. In the cited note' reference is made to the experiments of Welge2 wherein it was shown that when water was displaced by oil from a core the pressure in the water phase was less than in the oil phase but that when this oil was then produced by water drive the pressure in the water phase was greater than in the oil phase. Rose has concluded from these observations that conditions of static equilibrium did not obtain since the fluid saturations were such that phase discontinuities seemed unlikely. The argument from which this conclusion was drawn is based on the contention that "the pressure is always greatest in the non-wetting phase at each static interstitial interface of contact with the wetting phase." This premise appears to have been reached from a consideration of capillary phenomena in cylindrical tubes, although it may a1so hold for other types of pore geometry, hut as will be shown below it does not hold for all pore shapes and hence is not generally applicable. Since the pore structure of porous media such as reservoir rocks i- in general so complex as to defy exact description. it is undoubtedly of great value to establish a model in terms of pore shapes of known geometry, provided of course that the limitations of the model are recognized. That the limitations of the capillary. or cylindrical, tube model have not always been fully recognized will be evident from the following discussion of a pore of different shape hut one which may a. logically he considered a.; the capillary tube. The pore space to be considered is that shown in Fig. 1, which may be thought of as the "hole in a doughnut."* Consider the interface, A-B-A', between two immiscible fluids, P, and P2, which interface meets the solid alone a line, A-C.A'-C'. The interface A-B-A' is the surface of a spherical segmen† while the line of mutual contact be-

Jan 1, 1950

By Arthur F. Taggart

In 1900, Elmore found that if an acidulated pulp was stirred up with an oil which was relatively insoluble in and lighter than water, and the mixture was allowed to stratify, much of the sulfide would be found hanging to the lower surface of the floating body of oil and could be skimmed off or overflowed with it. The action of the flotation agent here is twofold, first to select the sulfide from the gangue—what today is called collection—and second, to buoy the collected sulfide away from the gangue. The action in collecting is illustrated by Fig. 1: which contrasts the behavior of drops of oil brought, under water, to the surfaces of gangue and sulfide particles, respectively. The oil displaces water from the surface of the sulfide; the water displaces oil from the gangue surface. If, instead of considering the solid particles the fixed parts of the system of oil, water and solids. we consider the oil and water fixed and the solids presented to the surface of contact, the condition will be as shown in Fig. 2; the sulfide tends to be drawn into the interface and the gangue to be excluded. The sulfide particles are held in the oil-water surface by the tension of this surface. The buoyant effect is supplied by the oil droplets in bringing the sulfides to the water surface, but not in holding them there. Gas as Buoyant Medium of Flotation In 1906 Sulman. Picard and Ballot discovered a practical and substantially fool-proof method of doing what Everson, in 1886, and Fro-nlcnt. DeBavay Bessel and Elmore had been doing in the intervening years, viz.: using gas in place of oil as the buoyant medium for flotation, but retaining oil as the agent. To all of these inventors "oil," with no qualification as to its kind and no true understanding of its function, was the important thing. Hut they placed on the oil an additional burden viz.: froth-making, and it soon became apparent that not all oils were suitable for the dual purpose. As a matter of fact, it is probable that each of these inventors knew only one suitable oil at the time he wrote his patent, but used the generic term in the patent with the usual idea

Jan 1, 1928

By L. W. Page

PREVIOUS to the introduction of the motor vehicle the broken stone or macadam road met the conditions of rural horse-drawn traffic better than any other type of road, but under fast motor traffic it has been proved to be quite unsatisfactory, and necessitates high maintenance charges. Such a road depends for its success upon the fact that the rock dust fills the voids between the stones and acts as a cement or binder. Under ideal conditions it should be constructed of rock so suited to the volume and character of horse traffic that only enough fine dust is worn from the stones of which the road is composed to take the place of that carried off by wind and rain; and when these conditions are met, the fine dust resulting from the wear. of traffic forms with the stone a smooth, impervious shell, shedding the surface water and protecting the foundation. With increase in the number and speed of motor vehicles, however, it was soon found that the cost of maintenance also increased, until at the present day highway engineers consider the old method of constructing and maintaining broken-stone roads increasingly inadequate, and are introducing every known type of binding material other than rock dust to cement the stone together. Among the most prominent types of products in use are those produced from our various petroleums. That the value of modern methods of road preservation was appre¬ciated in this country much earlier than we have been accustomed to believe is demonstrated by the recent revival of an old patent which was granted to one John Martineau, of Elbridge, N. Y., in 1834. Petroleum had, of course, not been discovered at that time, but he claims as his invention and improvement "The application of tar, turpentine, or any of that class of tenacious, cohesive substances, reduced before use to a fluid state, and that state used as a cement, to apply to, and combine with sand, gravel, pebbles, and pulverized stone, such as is used for a Mc-Adam road, or cobble stone, the interstices of coarser material being in all cases filled, as well as may be, with sand and gravel and cemented with tar or turpentine, to form the wearing face or surface of streets,

Jan 2, 1914

By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.' The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.' Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,' one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

By Frank F. Aplan

In looking into the crystal-ball scene of minerals beneficiation for 1970 and beyond, an impartial observer becomes con- fused as to what has been done and what is possible in the way of improvements. The mining official must balance the burden which is being shouldered by the mineral industry for maintaining our environment in its pristine state on one hand, with the solid advancements made in technology and cost savings on the other hand. Then the official wonders if this is really the criterion for judging overall performance today. As a prospective engineer, Dave Bolles sees it this way: "Specialization has caused many engineers to subordinate everything to doing their job the cheapest and fastest way. In the future this won't be enough. The engineer in the mineral industry will be responsible not only for mining, concentrating and smelting, but also for the resultant wastes- the mine dumps, the tailing dams and the slag piles." (See Drift on page 63).

Jan 1, 1971