By A. B. Hersberger, R. S. Dean

Although it is obvious that in any flotation process we must have a froth, in recent years the development of collecting reagents has caused the possibilities of better frothing agents to be overlooked. Some investigators have even gone so far as to say that the number of satisfactory frothing agents was sufficient. A little consideration will show, however, that the reagents available in the past were far from ideal frothers. The properties of an ideal frother for flotation work may be set down as follows: 1. It must form in low concentrations a copious but not too persistent froth. 2. It must be insensitive to hydrogen-ion concentration of the pulp; that is, it must froth equally well in an acid or alkaline medium. 3. It must be insensitive to salts, even in high concentration. 4. It must be absolutely noncollecting to both sulfides and nonsulfides. 5. Its frothing properties must not be affected by collecting reagents, including soap, the most generally used nonsulfide collector. 6. It must readily emulsify and disperse any insoluble collecting agent that is likely to be used. Clearly the existing frothers do not qualify. Pine oil, for example, is an acceptable frother for many purposes but if used in soap flotation a delicate balance between pine oil and soap must be struck because, as pointed out by Coghill1, these two reagents are incompatible in certain concentrations. The objections to soap itself as a frother are obvious, and the cresols and their substitution products all have some collecting power and very little emulsifying power. The mechanism of frothing in flotation was early explained on the basis of the Harkins-Langmuir theory of oriented molecules.2 These investigators showed that if an organic compound having an unsym-metrical molecule (in which one end of the molecule contained water-

Jan 1, 1939

By R. S. Dean, A. B. Hersberger

Although it is obvious that in any flotation process we must have a froth, in recent years the development of collecting reagents has caused the possibilities of better frothing agents to be overlooked. Some investigators have even gone so far as to say that the number of satisfactory frothing agents was sufficient. A little consideration will show, however, that the reagents available in the past were far from ideal frothers. The properties of an ideal frother for flotation work may be set down as follows: 1. It must form in low concentrations a copious but not too persistent froth. 2. It must be insensitive to hydrogen-ion concentration of the pulp; that is, it must froth equally well in an acid or alkaline medium. 3. It must be insensitive to salts, even in high concentration. 4. It must be absolutely noncollecting to both sulfides and nonsulfides. 5. Its frothing properties must not be affected by collecting reagents, including soap, the most generally used nonsulfide collector. 6. It must readily emulsify and disperse any insoluble collecting agent that is likely to be used. Clearly the existing frothers do not qualify. Pine oil, for example, is an acceptable frother for many purposes but if used in soap flotation a delicate balance between pine oil and soap must be struck because, as pointed out by Coghill1, these two reagents are incompatible in certain concentrations. The objections to soap itself as a frother are obvious, and the cresols and their substitution products all have some collecting power and very little emulsifying power. The mechanism of frothing in flotation was early explained on the basis of the Harkins-Langmuir theory of oriented molecules.2 These investigators showed that if an organic compound having an unsym-metrical molecule (in which one end of the molecule contained water-

Jan 1, 1939

By W. B. Coleman

Considerable discussion on the effect of iron and steel scrap in blastfurnace burdens was presented in the January, 1927, issue of Mining and Metallurgy. Therein the question is asked as to what causes the difference in physical properties of pig irons where the chemical analyses are practically the same. This point no doubt has been noticed by a number of furnace operators, but several years ago very little thought was given to it. The foundries purchased pig iron, had it analyzed and found it to be within their specification. The castings made from this iron at times would be satisfactory and at other times hardness and shrinkage would occur. Since the iron was chemically correct the foundries generally were at a loss as to what to do. They changed their method of melting in the cupola and in some cases this corrected the trouble. In some instances the foundry would continue eliminating a brand of iron until the castings produced were satisfactory. Through this process of elimination they would finally arrive at the conclusion that a certain brand of iron was causing the trouble. During the course of this elimination minor changes might have been made in the melting and in the end satisfactory castings were secured without discovering any definite reason for the trouble. Frequently the foundries blamed the manufacturer of the pig iron although the seat of the trouble was in their own method of melting. I have in mind one foundry in particular that was using three brands of pig iron for producing their castings and their losses were rather high. Three entirely new brands of iron were substituted in the charge and still the losses continued. Even after using six brands of pig iron the management felt that the pig iron was the cause. The difficulties encountered in the melting of iron in the cupola, over the past several years, reflect in a great many cases on the operation of the cupola. At different times certain brands of iron were unsuitable for producing a certain class of castings, but at the same time one could see no reason why the iron should be considered abnormal. Irons from furnaces where production and low cost are the main factors that are being used in foundries produce in most cases harder cast-

Jan 1, 1927

By Joseph C. Mead, James R. Cudworth

THE Birmingham district of Alabama has utilized the slag from its blast furnaces consistently since the earliest development of the slag industry. Today there are producers of slag cement who started business in 1900, and who have, under a progressive policy, expanded the number of their products to meet present demands. There are producers of slag aggregates and other crushed slag products who have been successful for periods of over thirty years. There are at the present two companies, Cheney Lime and Cement Co. and the Southern Cement Co., manufacturing puzzolan cement; two companies, Birmingham Slag Co. and Woodstock Slag Co., making slag aggregates and by-products; one company, Tennessee Coal, Iron and Railway Co., a subsidiary of the U. S. Steel Corporation, producing ground open-hearth basic slag for soil conditioning. Two companies, the Sloss Sheffield Steel and Iron Co. and the Woodstock Slag Co., make slag concrete in ready-mix plants and one company, the Superock Company, manufactures fine and coarse slag aggregates under a new granulation process. No Portland cement is made with slag as an ingredient, because dolomite is used so extensively as a blast-furnace flux that the magnesium content of the slag is excessive. Sources Of Slag In the Birmingham district there are 22 blast furnaces, of which the majority are in blast. The present production is 165,000 tons of pig iron monthly; the production in 1935 was 1,297,960 gross tons1. There are also two blast furnaces at Gadsden and one ferroalloy electric furnace at Anniston. From these two sources is obtained slag to approximately 1.1 tons per ton of pig iron.

Jan 1, 1937

By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By B. M. Larsen

A discussion based on three commercial furnace tests and electrical analogue calculations is presented. It shows that while regenerator efficiency is mainly dependent on loading or relative amount of heat exchange surface plus the heat transfer coefficients as effected by flow velocity, the actual air preheat temperature can be high or low, largely independent of regenerator efficiency, mainly due to the diluting or unbalancing effects of cold air leakage into various parts of the furnace system. THERE are many signs of a renewal of interest in the heat regeneration aspect of the open hearth process, among them being the recent paper by Marsh,' the introduction of auxiliary checkers in the stacks of the Isley furnace design, and a number of recent installations of two-pass checkers in new and old furnaces. However, there are also signs of yielding to the usual temptation of oversimplifying a problem. Faced with the job of obtaining better draft on a furnace, for example, a good designer always recognizes that focusing attention on some one factor, such as height of the stack or capacity of the exhaust fan, does not make his problem any easier; rather he must look at the whole system, including such items as valve resistances, bends in the flues, and flow resistance in the waste heat boiler; then he must make his design in relation to the available draft so as to avoid any serious bottleneck in the system. Yet this example is really much simpler than the problem of air preheating, and again, the latter problem is not really made easier by concentrating on air temperature in uptakes and on the more obvious methods for making this air as hot as possible. Also to be considered are such things as the total amount of air needed theoretically for complete combustion at any selected fuel rate, together with that needed for oxygen absorbed into the bath and for burning the combustible gases given out from the bath, plus some excess air. Furthermore, how does this total air requirement relate to the regenerator efficiency at various loadings? How much of the total air equivalent in stack gases will come from preheated air passed through the whole length of the incoming regenerator and how much from air leakage into various zones of the whole furnace system? Does the effect of leakage air differ depending on whether it leaks into the ingoing regenerator, the furnace above floor level, the outgoing regenerator, or the stack zone? Over a number of years we have in this Laboratory experimented with methods for measuring hot gas temperatures; we have measured, approximately, the efficiency of a few regenerators on commercial furnaces and we have developed an electrical analogue' for calculations of regenerator efficiency. The whole problem is too complex to cover in one paper even with a more complete background of data than we possess, but we can attempt here to clarify certain aspects in a general way, hoping to assist specific plant studies on individual furnaces. Some of our earlier experience has been incorporated into chaps. 4, 19, 20, and 21 in the book "Basic Open Hearth Steelmaking,"" and on the assumption that this text is available to most readers, this discussion has been shortened by references to that book. The most recent design of a flowing-gas thermocouple which we are now using for measurement

Jan 1, 1955

By J. S. Kirkaldy, D. G. Fedak

The extra degree of freedonz introduced by a second independetzt concentration in a tenzary system gives rise to the possibility of unstable planar phase interfaces in semi-infinite diffision layer couples. Diffusion paths which pass continuously in and out of too-phase regions of the phase diagram but which are not coincident with tie-lines give rise to super saturated zones which may be either adjacent to or isolated from planar phase interfaces, with corresponding nonisolated or isolated precipitates. Nonisolated precipitates are equivalent to morphological development of the interface. Selected couples in the ternary systems Fe-Ni-Cr and Cu-Zn-Sn have been examined nzetallographically and ifz the latter case both isolated and uo~zisolated precipitates have been observed. The diffusion path in one of the couples showing interface morphological developtnent has been examitled using electron probe microanalysis. IGNORING the spurious effects of preferential grain boundary diffusion and anisotropic crystal growth7 it can be unequivocally stated that it is impossible for a binary isothermal diffusion couple constructed of two unsaturated phases to sustain a nonplanar phase interface. Consider for demonstrative purposes the schematic phase diagram of Fig. l(a). Given an initial flat phase interface, semi-infinite boundary conditions and the internal boundary condition fixed by the constitution diagram, xB = xB(T), the unique solution of the diffusion equation requires a persistent flat interface. No other solution is possible. If, however, we anticipate the involvement of surface tension, then the internal boundary condition must be written xB = xB (T,Y) where r is the radius of curvature of a hypothetical nonplanar interface. The introduction of a new parameter such as r can be equivalent to the release of an internal constraint, so that a stable nonplanar interface may be possible after all. Consider a perturbation to the interface as indicated in Fig. 1(b). According to the Ostwald-Freundlich equation: which is applicable to a system of this constitution, the solubility of A in the matrix ß ,xB (Y), at a point of curvature r is given by where Va is the molar volume of the a-phase, R is the gas constant, and a is the interfacial tension. Since the right hand side is positive, xB(r) >xB cm, as indicated in Figs. 1(a) and 1(c). Accordingly, the perturbation will carry the interface concentration in a direction which is opposite to that which would sustain local equilibrium. Such a perturbation is necessarily moderated and the system is returned to its initial condition. This result is general for all binary couples since we can regard an interfacial perturbation as an attempt to precipitate within un-

Jan 1, 1962

By B. Bernstrom

A 22-ft diam, 7-ft long, wet autogenous grinding mill was installed in the new Cretaceous plant of the Jones & Laughlin Steel Corp. to prepare crude iron ore for concentration in spirals and flotation cells. The paper describes the flowsheet and gives a description of the operating and metallurgical results that have been obtained. These results include capacity, horsepower, operating problems and a comparison of pilot plant results with those obtained in commercial operation. The Cretaceous plant at the Hill Annex mine of the Jones & Laughlin Steel Corp. was designed with a wet autogenous mill for grinding low grade iron ore so that it could be concentrated by spirals and flotation cells. The plant, on the west end of the Minnesota's Mesabi Range, went into operation in June 1961, and preliminary operating and metallurgical information describing the performance of this mill can now be given. The crude is lean ore from the Cretaceous iron foundation. This formation is a beach deposit of Cretaceous age that overlies the Precambrian direct shipping and concentrating ores. This rock in nature is not extremely hard but is quite resilient, resisting blasting in mining and size reduction in milling. It contains hematite as water-rounded particles and other fragments of the underlying iron formation and adjacent rocks cemented together by a high alumina-silica ferruginous matrix. It is interspersed with hard dense hematite agglomerates and also contains granite pebbles and boulders that were not cleaned off during removal of the surface. It has a 3.48 sp gr and in the stockpile the material consists of frag-

Jan 1, 1962

"In the spring of 1927, six members of the American Institute of Mining and Metallurgical Engineers met for dinner at the Chemists' Club in New York to discuss the possibility of setting up a committee within the Institute to further the current interest in the science of steelmaking. Attention' to this subject had been crystallized by a symposium held by the Faraday Society in 1925. ' After a prolonged discussion, ranging from thermodynamics to slag conditioning, it was decided to approach the Institute with the request that a standing committee on "The Physical Chemistry of Steel Making" be set up. This committee proposed to promote scientific and practical papers on the subject, and was designed to cooperate with the Open Hearth Committee of the Institute in bringing scientific developments to the attention of open-hearth operators throughout the country... . "As the life of the [Physical Chemistry of Steelmaking] Committee lengthened and general interest in the technical phases of steelmaking grew, it became evident that there was a distinct need for a book that might serve the open-hearth interests to better advantage than standard texts whose scope is necessarily wide and whose detailed exposition of the open-hearth process is, therefore, somewhat limited. With this thought in mind, the Committee, after some years of consideration and debate, embarked on the venture of writing a manuscript on `Basic Open Hearth Steelmaking'." The foregoing paragraphs, taken from the introduction by C. H. Herty, Jr. to the first edition, well describe the circumstances which led to the publication of "Basic Open Hearth Steelmaking" in the spring of 1944. The book consisted of nineteen chapters contributed by twenty-three authors and edited by the staff of Alloys of Iron Research and T. S. Washburn, B. M. Larsen, and J. S. Marsh with Frank T. Sisco as consulting editor. The Engineering Foundation and the Open Hearth Steel Committee of the Iron and Steel Division, AIME, made financial grants; steel companies and other organizations supported the publication by contributing time and expenses of staff members in their capacity as authors or editors. The volume was sponsored by the Seeley W. Mudd Memorial Fund and appeared under the

Jan 1, 1951

By R. Simon

Maurer's review1 summarizes quite thoroughly the various theoretical developments and experimental findings that contribute to the knowledge of rock mechanics in drilling. This discussion supplements Maurer's paper by including generalities that either have been incompletely treated in his review, or formulated from new considerations by the discussant and from hitherto unpublished experimental data. These generalities are associated with the observation that all mechanical methods of rock drilling essentially comprise a sequence of indexed, concentrated loadings on the bottom of the hole being drilled. A concentrated loading is defined as a mechanical loading by a tool that contacts at any one time only a small fraction of the surface of the body being worked and penetrates only a small fraction of the body thickness. The surface in this application is the bottom of the hole. The deformation of ductile material by concentrated loading has received considerable attention because of the importance of indentation tests for measuring hardness of metals. Some of the generalities involved in concentrated loadings on ductile materials apply also to concentrated loadings on more brittle materials such as rock. Among these generalities is the applicability of similitude considerations to scaling laws and to force-displacement and energy-volume characteristics for tools of various shapes, as summarized by Tabor.2 Vork on the flow and fracture behaviors of glass loaded with pyramidal and spherical indenters is reviewed by Douglas.3 Maurer refers to the work of Evans and Murrell on wedge loadings on coal and on mixtures of pitch and sand. It is evident from Maurer's paper that a considerable portion of the studies of rock mechanics in drilling, such as crater formation experiments, has involved concentrated loadings on rock.

Jan 1, 1967

By F. H. Wilson, R. M. Brick

With the papers of Palmer and Smith1 and of Burghoff and Bohlen,2 published in 1942, understanding of the problem of the development of ears on deep-drawn brass cups was brought to the point where, from a practical standpoint, producers of brass sheet could keep earing under control. However, these very practical results raised questions concerning the reasons for the observed behavior. Since plastic deformation is fundamentally a function of crystallographic slip, these reasons must be considered in the light of the textures to be found in the annealed sheet. Various attempts have been made. to interpret the mechanism of ear formation by correlation with the preferred orientation and the anisotropy of the sheet. However, none of these has satisfactorily explained why ears are usually found in the rolling and transverse directions for copper but at 45' to these directions for brass. This paper offers additional data on these two related subjects and has been divided into two sections The first section provides a survey of the recrystallization textures of brass as affected by annealing temperatures and prior reductions, and an account of the caring behavior which accompanies these textures. The second section reports new data on the anisotropy that accompanies a characteristic texture for brass and endeavors with partial success to establish the factors that account for the difference in earing behavior between copper and brass Earing BehavioR oF Brass Review of Textures The recrystallization texture of severely rolled brass was first reported by Bass and Glocker.3 The preferred orientation to which this texture, obtained from metal annealed at 500°C., was most akin was (II3)[I12] This texture has been confirmed by Bauer, von Göler and Sachs;4 Brick;' Brick, Martin and Angier;6 and Cook and Richards7 who, in general, used annealing temperatures under 500°C. Bass and Glocker3 also reported the recrystallization texture at 850°C. to be the same as at 500°C. They analyzed their textures by means of single photograms obtained with white radiation. The photo-grams for both temperatures are reproduced in their paper, and there is a strong similarity between the two. However, for the latter temperature, the number of spots registered on the film was remarkably large for the grain size to be expected, and the authors made no mention of using a technique that would integrate a large enough area of the specimen to produce so many spots. The only other attempt to determine textures resulting from high temperature

Jan 1, 1945

In Mr. Weed's interesting paper, frequent reference is made to the Cananea copper-deposits, which are said to have been so vigorously exploited that they produced 14,000,000 Ib. of copper in 1901. The ore-bodies which yielded this large quantity of metal are described as a product of contact-metamorphism, and in Mr. Weed's genetic classification of such deposits, they receive a place under the sub-heading, "Deposits impregnating and replacing beds of contact-zone."* They are considered by Mr. Weed to represent a special type under this head, and are further classified as: " l. Chalcopyrite deposits: (a) Pyrrhotite ores; (6) Magnetite ores, Cananea type." In condensing much information into a comparatively small space, the presentation of a subject may be so abbreviated as to detract from its clearness. The situation at La Cananea, considering its importance from an economic as well as scientific standpoint, may he worthy of more detailed description. As Mr. Weed rightly remarks, " structural differences are so important, and have SO marked a bearing, not alone on the theory of their genesis, hut also on the working of the deposits and a determination of their value as mines, that they merit a full discussion."† It is my present purpose: (1) to show that it is doubtful whether the copper of La Cananea is mined, except to a limited

Jan 1, 1903

By Hans Lundberg

By electrical prospecting, orebodies that do not otherwise manifest themselves at the surface may be located. Conditions favorable to success with the methods are: Favorable geological conditions, such a proportion of minerals of good electrical conductivity in the orebody as will render the latter materially a better conductor than the enclosing rock, situation of the orebody within the range of influence of the electrical currents used and in proportion to this range a sufficient area of horizontal cross section of the orebody. The result is to permit of spotting drill holes accurately and to save the expense of drilling barren ground. THE art of prospecting, like other branches of mining, has developed rapidly during the last ten years, mainly because of the advancement of mining geology, but also because of the development of "geophysical methods," which are based on the different physical characters of minerals and rocks, e. g., specific gravity, elasticity, and magnetic and electric properties. These methods have proved of great value, especially in countries where the rock is covered by soil and direct geologic investigation is out of the question. In prospecting for orebodies, the methods based on studying differences in electrical conductivity have proved most successful; for which reason, the methods of electrical prospecting have been subject to the most energetic and systematic work, especially in Sweden. This paper gives a brief description of the methods of electrical prospecting now in use, especially the new electromagnetic methods, which have not been described before. The great differences in the electrical properties, especially in conductivity, between ore minerals and rock minerals are fundamental to all methods of electrical prospecting, for which reason, the electrical conductivity of ore minerals and rock minerals has been carefully studied in connection with and previous to the development of the various methods of prospecting with electricity. Ore minerals with a metallic luster, such as chalcopyrite, iron pyrite, galena, specular iron, magnetite, etc., also graphite and a number of cows, have considerably higher conductivity than the surrounding rock and soil (see Table 1). The figures of the table denote the specific resistance W, expressed in ohms for a cube with an edge of 1 centimeter.

Jan 7, 1925

By L. R. Jackson

It is convenient to have a consistent system of notation that will allow the representation of the entire range of complex stresses from hydrostatic compression to hydrostatic tension on plastic flow in a single diagram. Such a system is provided by making use of the fact that any complex stress system can be resolved into a hydrostatic tension or compression and a pure shear. Consider a stress system having the principal stresses This system can be resolved into a new system consisting of the three components and three pure shears. If Sm is positive, the net stress effect is hydrostatic tension; if it is negative, the effect is hydrostatic compression. In order to produce a systematic notation, a quantity that will be referred to as the "triaxial ratio" will be defined by the equation _ Sm Tr = Sm - Sm is given by Eq. I and Sl is the absolute magnitude of the largest principal stress without regard to sign. Table I lists the triaxial ratios for various common systems. Table i.—Triaxid Ratios for Various CommonSyslems Triaxial Ratio Stress System Tr Hydrostatic compression — SI - —St - -S³............................... -1 Torsion or shear -SI - S². S² = O..... O Simple tension SI. SI = SI = 0......... +0.33 Biaxial tension SI = S² S³ - 0......... +0.66 Hydrostatic tension +SI - +S³ = +S³. +1.00 Representation of Strains Strains will be plotted as "true" strains according to the system proposed by Ludwik.1

Jan 1, 1945

By L. A. Roe, E. A. Elevatorski

Wollastonite, named after William H. Wollaston, an English chemist, is a calcium metasilicate, CaSiO3; CaO: 48.30%, SiO2: 51.70%. It has a short history as an industrial mineral. The earliest production of wollastonite is reported to be from a deposit near Code Siding, located north of Randsburg, CA. At this locality small tonnages of wollastonite were quarried during 1933-34 and 1938-41, and processed into mineral wool. This operation was largely experimental and virtually no United States production was again reported until the 1950s when a large deposit near Willsboro, NY, was developed by the Cabot Corp. A processing plant was placed onstream in 1953, with nearly continuous production to date. It is currently operated by NYCO, a division of Processed Minerals, Inc. Since 1958, wollastonite deposits in the Little and Big Maria Mountains of Riverside County, and in the Panamint Range of Inyo County, both in California, have operated intermittently for production of both ornamental and commercial wollastonite. During 1980, the United States was the major producing country, furnishing about 75% of the world's output. Current production comes from Finland, Mexico, India, and Kenya. Small amounts have been shipped intermittently from the USSR, New Zealand, Republic of the Sudan, Republic of South Africa, and Namibia (South-West Africa). The principal use of wollastonite is in the manufacture of plastics. Other uses are for paints, ceramics, adhesives, fluxes, glazes, thermal insulation board, and refractory products. Mineralogy Pure wollastonite, CaSiO3, has the composition of 48.3% CaO and 51.7% SiO2. However, it is seldom found in the pure state due to the ease with which it takes into solution the metasilicates of manganese, magnesium, iron, and strontium. Predominantly, wollastonite occurs as a contact metamorphic deposit forming between limestones and igneous rocks. Commonly associated minerals are garnet, diopside, epidote, calcite, and quartz. It has a specific gravity of 2.8 to 3.0, and hardness of 4.5 to 5 on Mohs' scale. When pure, it has a brilliant white color, but with impurities it may be grayish or brownish. Luster is vitreous to pearly. Melting point of wollastonite is about 1540ºC. Wollastonite occurs in coarse-bladed masses, rarely showing good crystal form. It is usually acicular or fibrous, even in the smallest of particles. The most unique property of crushed and ground wollastonite is its cleavage. Fragments of crushed wollastonite tend to be needle-shaped, imparting a high strength, and this property is the basis for many of its uses. The fiber lengths are commonly in the ratio of 7 or 8 to 1, length to diameter. The average diameter of wollastonite is 3.5 µm. Some crystals of wollastonite fluoresce under short-wave or longwave ultraviolet light, or both, with colors ranging from yellow-orange to pink-orange. Specimens may also show phosphorescence. The acicularity of wollastonite is a property of considerable importance to the marketplace. The plastics industry makes utilization of high aspect ratio grades of wollastonite (20:1) for reinforcing thermoplastics and thermoset polymer compounds. The naturally high pH of 9.9 (10% water slurry) is a prime property to the coatings industry. The coatings industry uses milled grades of wollastonite as a pH stabilizer in interior and exterior PVA and acrylic latex systems. Processed wollastonite can have a G.E. brightness of 90 to 93. Chemically, wollastonite is inert and this property makes it useful as a filler and reinforcing agent. There are two polymorphs of calcium silicates: wollastonite, a low temperature form, and pseudowollastonite, a high temperature

Jan 1, 1983

By F. E. Buch

The smelter is designed for a production capacity of 10,000 short tons of blister copper per month, when operating on the present concentrate grade. The :smelter lay-out is shown in Fig I. The major units of equipment comprise two reverberatory furnaces, three 13 by 30 ft Peirce-Smith converters, two straight line casting machines, one being served by a 13 by 30 ft holding furnace and the other by a ladle tilting quadrant, two converter aisle cranes and two converter blowers. The plant is compact and the general arrangement of standard gauge railway tracks and conveyor belts provides for a smooth flow of incoming materials and metallurgical products. Concentrate is received by conveyor belts and fluxes in standard railway trucks. The local track system is covered by an electric trolley locomotive. The Smelter treats a wet (10 pet moisture) flotation concentrate containing approximately 53 pct total copper and 0.9 pet oxide copper. The predominating minerals are chalco-cite, chalcopyrite and bornite accompanied by small quantities of malachite and cuprite. The gangue is highly siliceous and requires limerock as a flux. Metallurgy would be straightforward were it not for the necessity for eliminating bismuth which occurs as an impurity in the ore along with the copper. Directly or indirectly most of the Smelter problems can be traced to the necessity for bismuth removal. Copper recovery, based on new copper treated, averages 97.5 pct. General Description Flotation concentrate, containing 10 Pet moisture, is conveyed from the filter plant to the smelter storage bins by conveyor belts, the material being weighed in transit by a revolving drum type of weigh-hopper manufactured by Samuel Denison and Son, Ltd. The weigher consists of a steel drum with dished ends carried on a horizontal shaft and rotated by an 8 hp squirrel-cage motor through a worm and Spur reduction gear. A feed mouth in the drum permits of filling and discharging. The whole unit is supported on a framework resting on weighing levers, which in turn connect to transfer levers, thence to an indicator of the steelyard type situated 16 ft from the centre line of the drum. The indicator is of the "Denison" patent equilibrium controlled ticket stamping type, insuring mistake-proof records by a combination of electrical and mechanical movements which Prevent the operator from printing until the cover enclosing the steelyard is closed and until the poise-weights have been Set correctly to the weight of the hopper and contents. The machine is capable of weighing 30 short tons at a time but the usual load is 28 tons. After obtaining the gross weight the drum is rotated and discharged into a receiving bin situated below it. The empty drum is weighed and the net weight re-

Jan 1, 1949

By W. H. Brandt

THERE has been much progress in the last two decades in understanding the hardenability of steel. Roughly, the progress has been along two lines, which may be designated as empirical and fundamental. This empirical work has progressed to the point where steels may be manufactured to the desired characteristics quite closely and heat-treatment and application problems can be approached with considerable confidence. Particularly noteworthy among the empirical work is that of Grossmann,12 who has given formulas for calculating hardenability as a function of composition, and the establishment of the isothermal transformation curve by Davenport and Bain.13 The latter does not fall entirely in the class of an empirical study, for while it provides a means of presenting a tremendous amount of empirical data in the form of a single curve, it also outlines clearly the problems that face the fundamental investigator. The isothermal transformation curve shows clearly that the phenomena occurring in the neighborhood of the knee of the curve are those that limit the hardenability of steel. Above the knee of the curve, the product of decomposition of austenite is lamellar pearlite and fundamental progress has consisted chiefly of a detailed study of structure and formation of pearlite, largely at the hands of Mehl and his collaborators.1-5 They have shown that formation of pearlite proceeds by a process of nucleation and growth and they measured both the nucleation and growth rate. However, there is still a wide gap between our empirical knowledge and fundamental knowledge, owing largely to the fact that there is no satisfactory theory of nucleation rate or of growth rate. This paper is being written in an attempt to fill in a small part of the gap. A method was presented recently14 for calculating the velocity of edgewise growth of pearlite using an expression for the carbon concentration that satisfies the diffusion equation. The edgewise velocity of pearlite growth in a plain carbon eutectoid steel was calculated, using linear extrapolations of the ferrite and cementite solubilities. While the results are in fairly good agreement with the experimental facts, the calculated velocity of edgewise growth is smaller at 600°C. than G, the radial growth velocity of pearlite nodules, whereas one would expect it to be larger. In this paper the calculation will be repeated using a new extrapolation for the ferrite solubility, which gives better agreement between G and V, the calculated velocity of edgewise growth. A calculation will also be made of the effect of carbon content on velocity of edgewise growth, and the problems of calculating the effects of other alloying elements on growth rates will be discussed. It will be assumed that the mechanism of pearlite growth, established by Mehl and

Jan 1, 1945

THE preceding chapter has recorded the initiation of mineral industry education during the period 1890-1910 in numerous institutions that had not previously offered it. It should also be emphasized that in many institutions where instruction had begun before 1890, as recorded in earlier chapters, but had not yet become firmly established, this period was one of marked growth and development. This was not universally true, however, for at the Universities of Pennsylvania, Michigan, Illinois, Wisconsin, Washington (St. Louis), Iowa, Vanderbilt and Tennessee, and at the Polytechnic College of Pennsylvania, mineral industry instruction was being dropped during this period, instead of gaining in strength. It is necessary to emphasize this, because writers on the subject have not infrequently attempted to make a much too simple correlation between mineral discovery or production and the intensity of student interest in mineral industry curricula. It would naturally be true that periods of large mineral production would, in general, coincide with cycles of business prosperity, and the latter are conducive to starting new ventures, educational as well as business. It should be equally evident that opportunities for business and professional success might, in such periods, appear to increase at a more rapid rate in industries other than mineral, or in the utilization of minerals rather than in their production. The author has not been able to perceive any simple and clear relation between interest in mineral industry education and mineral discovery, production, and utilization, or general business prosperity. On the contrary, the more the problem is studied the more complex the factors involved in it appear to be. In a later chapter an attempt will be made to analyze them in more detail

Jan 1, 1941

By T. Egleston

The manufacture of charcoal in kilns was declared many years ago, after a series of experiments made in poorly constructed furnaces, to be unprofitable, and the subject is dismissed by most writers with the remark that in order to use the method economically the products of distillation, both liquid and gaseous, must be collected. It is asserted with truth that the number of kilns required for a large production of iron would be so great that it is doubtful whether any works would be justified in making the necessary outlay for their constructiou, but it can also be asserted with equal truth that for any such production in a given locality the use of charcoal as fuel would be eqnally unjustifiable. It appears to have been forgotten that there were other manufactures besides iron in which large amounts of charcoal were used, but these consumers seen] to have been guided entirely by the results of the experiments of the iron men, who necessarily made the largest qnantity of it. Some authors speak in a doubtful way of the quality of the charcoal produced, and a few concede that with great care good charcoal can he made in kilns, but that most of the workmen do not like kiln 'charcoal. This is the real secret of the opposition to this method of manufacture. Most of these objections were written when charcoal was the most important fuel used by the iron manufacturer, and when what was a largeproduction of iron for several furnaces was less than that produced by a single modern one, in localities where other fuels can be had. Almost all that has been written on the subject related to the use of the fuel for the manufacture of iron in the blast furnace, where very peculiar properties are required, and where the qnantity produced is limited by the height of the furnace, and this in turn by the crushing resistance of the charcoal. A large production was, therefore, only possible when the best and hardest woods were used. Of all these objections there is not a single one which is not eqnally applicable to any method of charcoal manufacture, whether it be meilers, pits, or furnaces. Until recently, therefore, the manufacturers of charcoal iron

Jan 1, 1880