Search Documents

By Sung-Mo Jung

Experiments were carried out on a system with artificially prepared slags in a graphite crucible, in order to examine the possibility of recycling BOF slags produced in the steelmaking process. More than 80% of FeO and P2O5 was reduced within 20 minutes and the FeO reduction rate was greater than that of P2O5. P2O5 reduction began after more than 60% of FeO was reduced. Increasing slag basicity enhanced the reduction of FeO and P2O5. Temperature also improved slag reduction. The overall reduction rate was controlled by the chemical reaction at the slag/carbon interface. The reduction rates of FeO and P2O5 were second and first order with respect to their respective contents. Most of the reduced phosphorous is believed to vaporize in the form of P2 gas.

Jan 1, 2006

By A. V. Tarasov

The proposed process is based on creating a controlled frothed layer of molten slag, in which fine particles of carbonaceous reductant and raw material to be processed are mixed with emulsified iron. Frothing of the slag layer without external blowing occurs as a result of intensive evolution of gaseous reduction products. The froth reaction process is maintained due to the heat of an electric arc in the slag layer. When the metal bath is heated by the arc to 1400- 1 500°C, the low temperature of the slag surface of about 1200-1 300°C is maintained due to low thermal conductivity of slag froth preventing heat loss. In order to maintain the required slag froth level and control the process temperature, air tuyeres are installed above the slag bath; blowing air serves also for oxidation of zinc in fumes and for its transportation. High adsorption and thermal insulating properties of slag froth ensure virtually complete elimination of dust and mist entrainment along with low heat losses. The main macrokinetic regularities of the carbon thermal reduction of zinc-containing slag melts have been studied under frothing conditions. The mechanism of formation of gas-slag emulsion has been identified under the conditions of reaction [C]+[O]=CO occurring locally at the slag-metal interface. It has been demonstrated that under the froth reduction conditions the zinc removal rate from the melt increases on the average by 3 to 5 times. Based on the physical and chemical data obtained, basic principles of the dezincing technology have been developed for different intermediate oxide iron-containing products produced in the process of ferrous and non-ferrous metals production.

Jan 1, 2002

By Gordon A. Irons

"Powder injection for melt refining is widely practiced in the steel industry, and is gaining acceptance in the non-ferrous industries. In these commercially-important systems, the thermodynamics and kinetics may be very complicated. More than one element may be removed by refining, and often the refining agents are not just one compound. In this paper, the thermodynamic and kinetic aspects of these processes are reviewed. A number of examples are given, such as the desulphurization of iron with a variety of reagent mixtures, and selenium removal from copper with several different reagent combinations.IntroductionI am very pleased and honored to present a paper at this Symposium recognizing the many contributions of Professor Howard Womer. Even at the time I was an undergraduate student, the WORCRA process was part of the curriculum. I remember at the time that I was fascinated by the concept, and due to it and the many other rapid developments in Process Metallurgy, I chose it as my field of study. I think the Symposium is testimony that Professor Womer has touched the lives of many others as well.My original assignment was an overview of the basic aspects of gas and solids injection. However, I reviewed most of this material at the Savard/Lee Symposium [1]. In the present paper, I will present some of the basic issues related to refining with powder injection, using work that we have recently completed in both ferrous and non-ferrous systems."

Jan 1, 1996

By Hideyuki Takahashi, Taro Aichi, Kazuyuki Tohji, Makoto Muramatsu, Rie Sato

"There are several ways to condition lead-based alloy anodes for zinc electrowinning: electrochemical treatment, chemical treatment and physical treatment. Two advantages of physical treatments are their productivity and variety. In this report, physical treatments, including blasting with silica, alumina, steel grit and cut zinc wire, were tested. The laboratory tests confirmed there were differences in the formation of anode scales during electrowinning and in the suppression of lead dissolution from the anodes. With an increase in the surface roughness, the misfit between the PbC""2 and the MnC>2 was mitigated and the anchor effect was promoted; these effects resulted in dense Mn oxide scales on the anode.IntroductionZinc is widely used for hot-dip zinc plating and for die casting alloys. As a supplier of materials, we have endeavored to produce zinc that is economical and contains as little impurity as possible. As a result of our efforts, a technology for consistently providing special high-grade (SHG) zinc has been established. However, as seen in the issuance of the Restriction of Hazardous Substances (RoHS) Directive, public awareness of the industrial impact of heavy metals on the environment has been heightened. Increasing efforts to control environmentally sensitive substances will be necessary for our production processes.Electrolytic SHG zinc is produced by electrodeposition in an acidic solution with a Pb-Ag or Pb-Ag-Ca alloy for the anode and an Al alloy for the cathode. Pb alloy anodes are widely used because of their excellent durability; however, they are a source of Pb, which is the main impurity of the product."

Jan 1, 2012

By Patrick R. Taylor

A kinetic study of the fluosilicic acid leaching of galena was performed under the presence of different oxidants. Fluosilicic acid concentration, agitation speed, concentration of solids and particle size, type and concentration of oxidant, and temperature were the variables studied. Hydrogen peroxide was found to be the most effective oxidant, its effectiveness being proportional to its concentration. As expected, an increase of leaching temperature increased the overall extraction and extraction rate. The same was found by decreasing the galena particle size. It is thought that leaching using hydrogen peroxide is controlled by fluid film mass transfer due to the calculated apparent activation energy. Reaction by-products such as sulfur and sulfur compounds retard the leaching rate. A mathematical model is proposed and compared to experimental results.

Jan 1, 2003

By Jürgen Antrekowitsch, Thomas Griessacher

The recovery of valuable metals from residues like dusts and sludges is nowadays state of the art. Depending on the complex constitution, a recovery of different metals can – in the majority of cases – only be performed with considerable energy input in high temperature processes together with insufficient yields and newly generated residues. Often, the behavior of the dust or sludge in the process during melting or reduction is unknown. In this work, a detailed characterization of selected residues like steel mill filter dusts, cupola furnace dusts and leaching residues is done. The different steps of getting from solid particles into a homogenous liquid phase were investigated. Although high temperature processing leads to high reaction speeds, the complexity of residues keeps the system away from thermodynamic equilibrium. With this research program, some basics are generated to understand smelting and reduction and the gap between thermodynamical calculations and real behavior can be explained.

Jan 1, 2008

By R. Harris

Blister copper melts of 800 g to 1000 g containing less than 1 wt % S and up to 3 wt % Ni were desulfurized at 1523 K in air or by a pure oxygen jet blown at 75,500 and 1000 cm3/min, from 1 cm above the melt. Rates of desulfurization and oxygen pickup were measured and visible surface phenomena were photographed and videotaped. It was observed that SO2 was evolved from Cu-S melts in a manner reminiscent of the effervescence seen in carbonated drinks. The effervescence lasted up to 20 minutes and resulted in the ejection of material up to a height 50 cm above the melt surface. Sporadic discharge of large bubbles was also observed in a Ni containing melt top-blown with oxygen at 1000 cm3/min. The Cu-S melts top-blown with oxygen experienced faster sulfur elimination as compared to stagnant melts exposed to air and experienced only a single period of turbulent SO2 evolution, which occurred almost immediately after oxygen injection commenced. The Cu-S melts exposed to air experienced multiple episodes of effervescence. The stagnant blister copper melt containing nickel did not exhibit effervescent behaviour and experienced a lower rate of sulfur elimination compared to Cu-S melts tested under similar conditions. The present article examines the role of surface phenomena in determining the observed behaviour.

Jan 1, 1999

By Yonggang Liu

Microstructure and precipitates in hot rolled low carbon steel sheet by CSP were investigated in this paper. It is pointed out the precipitates in low carbon steel sheet by CSP are different with that by traditional hot rolling. The bainites were found in CSP hot rolled steel sheet by TEM testing and these bainites could maintain in the sheets even after batch annealing. The selected area electron diffraction analyzing indicated that there were many CrB2BN and FeB4BN phases precipitated in hot rolled steel sheet and no AlN grains precipitated. The nitrides forming can limit AlN grains precipitating during the batch annealing processing, and this could do harm to the texture pipeline along orientation line forming with formed properties.

Jan 1, 2006

By A. Onozaki

The Iijima Refinery was put into operation in 1972 and today has an annual production capacity of 156,000 tons of SHG electrolytic zinc. At the Iijima Refinery, the recoveries of gold and silver are 98.0% and 98.2%, respectively. Gold contained originally in the zinc concentrates reports in the Cu-Pb-Ag residue produced in the residue treatment process. Silver contained in the concentrates is distributed between the Cu-Pb~Ag residue and the copper cake produced in the purification process. The Cu-Pb-Ag residue, which contains gold and silver, is sent to the Oyachi flotatfon plant of the Kosaka Smelter; about 82% of the gold and about 85% of the silver are recovered in the copper flotation concentrate.. In this paper, the distribution of gold and silver in the Iijima. Refinery is discussed and operational results of the Oyachi flotation plant are presented.

Jan 1, 1990

By Kazuhiro Nisizono, Takashi Kuroki, Nobuyuki Mori, Keisaku Ogi

"The improvement of critical current density and mechanical property is essential to the practical application of the superconductive oxides. A solidification technique is developed in this study for the growth of columnar or single Y123 crystal with finely dispersed Y211 and Ag particles through a monotecto-peritectic reaction of Li.(Ba-Cu-Ag-0 rich liquid)+ Y211-+ Y123+Lz(Ag rich liquid). The large solidification rate and temperature gradient can refine the Ag and Y211 particles. But Ag-free region is widely formed along the crystal growth direction in the central part of the Y123 cell. Since this phenomenon occurs because of the cellular growth, it is necessary to narrow Y123 cell width or to grow Y123 crystal with flat freezing interface. By controlling crystal growth direction using a seed crystal, Y123 columnar or single crystal with uniformly dispersed fine Ag particles are obtained. The· behavior of Ag and Y211 particles during the solidification of Y123 crystal is simulated by the peritectic growth model of faceted Y123 crystals.IntroductionY-Ba-Cu-0 superconducting oxide (YBCO) with high critical temperature also has excellent superconducting characteristic under the high magnetic field. The critical current density (Jc) has been enhanced by ·using unidirectional-solidification technique, which can overcome the weak-link problem at grain boundaries and control the crystal orientation and the distribution of Y211 particles which give effective magnetic flux pinning centers in the Yl23 matrix [1-4].In addition to improving superconducting properties, it is necessary to improve mechanical property for the practical application. The silver addition to the melt-textured YBCO superconducting oxide has been reported as the effective method to improve mechanical properties without degrading superconducting properties. Since the material properties are considered to be largely affected by silver particle size, form, dispersion state etc. in the Y123 phase, it is important to control Ag distribution in YBCO/Ag composites. Besides, it is also reported that the silver addition improve the corrosion resistance to the water and CO2 [5,6]. Nishizono et al. [7-9] have reported that the silver distribution in the YBCO/Ag composites is largely affected by the solidification condition, but yet some unclear points are also remained. YBCO has been also fabricated by the zone melting method [10-12], and Furuya et al. [5] and Hirano et al. [13] have reported the fabrication of silver added YBCO composites, but the distribution and behavior of Ag are not investigated in detail"

Jan 1, 2000

By Brian G. Thomas, Quan Yuan, Rajneesh Chaudhary, Rui Liu, Sana Mahmood

"A particle-entrapment model based on local force balances has been developed, implemented into computational models of turbulent fluid flow, and applied to simulate the entrapment of slag inclusions and bubbles during the continuous casting of steel slabs. Turbulent flow of molten steel is computed in the nozzle and mold using transient CFD models. Next, the transport and capture of over 30,000 particles are simulated using a Lagrangian approach. Particles touching the dendritic interface may be pushed away, dragged away by the transverse flow, or captured into the solidifying shell according to the results of a local balance of ten different forces. This criterion was validated by reproducing experimental results in two different systems. Finally, the model is applied to predict the entrapment distributions of different sized particles in a typical slab caster. Although more large particles are safely removed than small ones, the capture rate as defects is still high.IntroductionSurface defects such as slivers and blisters are often caused by captured inclusion clusters, slag, bubbles, and other particles. During continuous casting, jets of molten steel from the submerged entry nozzle (SEN) ports carry bubbles and inclusion particles into the mold cavity from upstream processing, as shown in Figure 1 [1]. In addition, droplets of liquid mold slag may become entrained into the flowing steel due to fluid flow problems, via several different mechanisms [2]. Figure 2 shows some typical inclusion particles [3] that can be entrapped from the flowing liquid into the solidifying steel shell to form defects in continuous-cast product.Liquid steel flow in the continuous casting mold has been modeled extensively. Reynolds Average Navier-Stokes (RANS and URANS) approaches are based on accurate computation of the ensemble-averaged velocity field. Particle transport can be tracked using a Lagrangian approach, introducing an extra model, such as ""random walk"" to generate realistic motion of every particle. Large Eddy Simulation (LES) models can accurately calculate both the transient evolving flow field and Lagrangian particle motion [4, 5] of this turbulent process."

Jan 1, 2012

By A. González

Arsenic is one of the main contaminants present in Chilean copper concentrates and its abatement represents a challenge for the process metallurgy, particularly under the strong environmental requirements in the global community. The possibility to form ferric arsenate directly from a gas phase by means of a heterogeneous reaction between an arsenic gas bearing and iron oxide was studied at laboratory scale. A thermodynamical analysis for the system Fe-As-O-S has been initially made, in order to obtain the stability conditions for the ferric arsenate or other FeAsyO2 type compounds. Experiments were made using an hematite sample suspended in a thermogravimetric device. AS4O6 gas generated from solid AS2O3 that was passed through the iron oxide sample and its instantaneous weight change was recorded directly. A kinetic study for the AS4O6 volatilization was made to control the gas composition. A chemical control between 300 and 600°C with an apparent activation energy of around 14 Kcal/mol As2O3 was determined. The samples after the reactions were chemically and XRD analysed. Arsenates detected corresponds to complex compounds. Results shows a dependence on temperature and oxygen content in the gas phase. The kinetics for iron arsenates formation is slow, reaching an arsenic capture of 6% after 80 minutes of reaction when an oxygen content of 50% is fed continuously at 800°C and 3,56% As in the gas. Experiences made at the same temperature but under higher oxygen content in a closed reactor, allowed arsenic capture close to 60%. For higher temperatures the capture is considerably lower.

Jan 1, 2003

By Robert Corson

Zinc has a large solubility in Fe and a completely filled ?d? shell. With the discovery of dramatic increase of the magnetostriction in Fe by Ga addition, an examination of element Zinc that is adjacent to Ga in the periodic table is of significant interest. In this work, the effect of binary alloying of Zn with Fe on the magnetic and magnetostrictive properties is examined. The FeZn alloys were processed using powder metallurgy and vapor phase synthesis, and Zn contents were varied from 5% to 30%. An examination of the influence of different processing parameters and the Zn content on the resulting alloy properties is presented. The alloys were characterized using X-ray diffraction and SEM. Magnetostriction measurements were carried out at different pre-stress levels. Magnetic properties were measured using a vibrating sample magnetometer.

Jan 1, 2006

By Sheng-hai Yang

The ultrafine, monodispersed, spherical cobalt powder has been fabricated by reducing cobalt hydroxide with glycol. It were investigated that the effect of NaOH concentration on the reaction rate and the effects of the concentration of cobalt hydroxide and surfactant on the morphology and particle size. The particles were characterized by the X-ray diffraction(XRD), scanning electron microscope(SEM), laser diffraction particle size analyzer and BET specific surface analyzer respectively. The XRD shows that the cobalt powders exist mostly in face centered cubic (fcc) structure, a little in simple hexagonal. The cobalt powders prepared at Co(OH)2150g/L, NaOH 40 g/L and surfactant 30g/L, its average particle size, specific surface area and cobalt content, were 0.88µm, 2.705m2/g. and more than 99.5% respectively.

Jan 1, 2006

By Dian Adisty, Leiv Kolbeinsen, Eli Ringdalen

In Si and FeSi production, the main Si source is SiO2, in the form of quartz. Reactions with SiO2 generate SiO-gas that further reacts with SiC to Si. During heating, quartz will transform to other SiO2 modifications with cristobalite as the stable high temperature phase. Transformation to cristobalite has been investigated and shown to be a slow process where the rate varies between the investigated quartz types. The effect of quartz versus cristobalite as SiO2 source has been studied for reaction (1) 2SiO2 + SiC = 3SiO + CO, by heating of pellets with SiO2 + SiC in Ar-gas. The reaction was faster with cristobalite than with quartz. Initial experiments indicates that this is the case only in Ar and not in CO-atmosphere The higher specific surface area of cristobalite is believed to contribute to the higher rate. The industrial consequences of the observed difference between quartz types are discussed.

Jan 1, 2014

By A. René Silva

The separation of Fe(III) from simulated Ni(II) solutions using different ion exchange resins was studied. The resins tested included cation exchangers with sulfonic and carboxylic groups and chelating resins with iminodiacetic, aminophosphonic, and mixed sulfonic and phosphonic groups. The dosage of resins was varied from 0.1 to 0.5 g/mL to study the impact of resin type and dosage on iron separation from simulated nickel leach solution containing 25 g/L Ni(II) and 25 g/L Fe(III) at pH 1.5. Also, the effects of different metal ion concentrations, Fe (III):Ni(II) ratios in solution, pH, and adsorption times were investigated. Experimental results demonstrate that all the chelating resins selected favored the adsorption of Fe(III) over Ni(II) with high Fe(III) loading. Soft cation exchange resins also favored the adsorption of Fe(III) over Ni(II), but no significant Fe(III) loading was observed. In contrast, strong cation exchange resins did not show adsorption preferences. The most efficient separation was observed using resin with aminophosphonic groups at resin dosage of 0.2 g/mL, having a Fe(III) adsorption over 94% and Ni(II) adsorption below 5%.

By R. E. Brewer

Pilot scale flotation tests were conducted with a l?ft-diam column at the Barrick Resources (USA) Mercur mine, Tooele County, UT, to scavenge unleached (0.01 to 0.018 oz/st) gold values from the tailings of a carbon-in-leach (CIL) circuit. The optimal recovery was 35 pct of the unamenable-to-leaching gold, at a grade of 0.353 ounces of gold per short ton, using a mixture of dithiophosphate, xanthate, and diesel fuel as a collector. This was achieved by floating approximately 1.6 wt pet of the CIL tailings. The gold values are believed to be contained in arsenic-bearing minerals, attrited carbon, and carbonaceous material in the ore. Redox potentials were measured with a gold electrode during the conditioning stage prior to flotation. The correlation between flotation recovery and redox potential values could be used to control reagent additions. Treatment of a previously leached and weathered tailings material, averaging about 0.055 ounces of gold per short ton, was also investigated. The tailings were first water leached at approximately 60? C, and the water-leached tailings, containing approximately 0.03 ounces of gold per short ton, were then fed to the column flotation unit. The effects of pH' and sodium sulfide addition on gold flotation recovery and redox potentials were examined. Maximum gold flotation recovery, 36 pct, was achieved at pH 8,5 with a sodium sulfide addition of 0.18 Ib/st. Overall gold recovery by leaching and flotation was in the range of 70 to 80 pet.

Jan 1, 1989

By B. A. Paponetti

The following report discusses the bioleaching of chalcopyrite of italian origin catalyzed by Thiobacillus ferrooxidans. The developments vcr.ius time of the main .biochemical and chemical reactions involved in the production of soiuble and insoluble species were investigated focusing on the times at which they begin and bow long they last. The precipitates were characterized both in quantity and in quality relating the rate of the process to the precipitates fonnatiom. A material. balance has been made to verify the proposed mechanism.

Jan 1, 1991

By N. V. Sujathkumar, I. Vasudhevan, R. Santhakumar

"Freshwater ornamental fish culture is gaining importance in India and cheaper and nutrient rich live foods such as infusorians, daphnids, copepods and tubifecids are needed urgently. In this regard, adequate research has been conducted to produce such live feeds through recycling of agriculture and animal wastes. By this venture, besides generation of additional income, environment is also kept clean. In order to popularise the technologies relating to production of live foods from wastes and generate employment opportunities, training programmes were conducted for 100 Self Help Group women belonging to Thoothukudi district. The topics of the training included, breeding of ornamental fishes by utilizing the building material wastes, production of live foods through recycling of agricultural and animal wastes. A study on feed back was conducted with 100 respondents represented from different villages. The variables such as socio economic status, economic motivation, usefulness of training and constraints were included in this study. The impact assessment of this training of rural women indicated that 79 percent respondents were in favour of using the training for self employment by utilizing different kinds of wastes. Similar training programmes have also been planned in other parts of Tamilnadu. Introduction Ornamental fish culture is one of the most appropriate sectors to provide opportunities of employment to uplift the status of rural women. To ensure women utilize their full potential in useful and profital activities like freshwater ornamental fish culture, it is necessary to provide training and support for rural women which will ultimately lead to empowerment. Self Help Group Women are being trained routinely in India on the production of live foods for ornamental fish culture through recycling of agricultural and animal wastes. In this regard, training programmes were organized for the Self Help Group Women on freshwater ornamental fish culture. Which is gaining much importance in India. Cheaper and nutrient rich live foods such as infusorians, daphnids, copepods and tubifecids are needed urgently. The techniques of live feed production through recycling of agricultural and animal wastes would not only generate additional income by would also keep the environment clean."

Jan 1, 2008

By Lars O. Werme

Already the KBS Project proposed copper as a suitable material for encapsulation of spent nuclear fuel. The basis for this choice was the thermodynamic stability of copper in water and the fact that deep granitic groundwaters in Sweden are oxygen free. With a limited supply of oxidants, a copper canister would have the potential for a very long service life. The research and development work aiming at encapsulating nuclear fuel entered a new phase in 1993, when SKB launched its Encapsulation Plant Project. Within this project, SKB has: ? designed a facility for encapsulation of nuclear fuel, ? laid down the design premises for a canister for disposal of nuclear fuel, ? tested and developed fabrication methods for copper canisters, ? evaluated the long term chemical and mechanical behavior of the canister, ? made preliminary plans for a factory for the production of copper canister, ? constructed a canister laboratory for full scale testing of the key operations in an encapsulation plant. The conclusions of this project were that a canister consisting of an outer layer (50 mm) of copper over an insert of cast nodular iron would provide sufficient corrosion protection and would have sufficient mechanical strength. This canister can be produced by several methods of which forming from rolled plates, hot extrusion, and "pierce and draw" have been tested at full scale. The canister will be sealed by electron beam welding in the encapsulation plant, and the integrity of the weld will be verified by ultrasonic testing and' high-energy radiography. The final development work in this area will be performed in the canister laboratory.

Jan 1, 1999