By John C. Draper

The principal object of an underground coal mine transportation system is to move coal from the face where it is produced to the outside of the mine where it is prepared for market. In addition to the movement of coal, a transportation system must also move supply materials to the inside ; it must move men in and out of the mine ; and it must move rock and other debris out of the mine for disposal. Usually, mine haulage is divided into three categories named for the various areas of the mine served : 1) Pace Haulage. This is used at face from the mining machine to the intermediate transport system. 2) Intermediate or Secondary Haulage. Generally this is used between face haulage and main haulage. Sometimes this is merely an extension of the main haulage. 3) Main Haulage. This extends from the secondary haulage to the outside and is usually either a track or conveyor system, sometimes a combination of both. Transportation modes of coal in the various areas pose different problems, but the whole system must be synchronized. For instance, at the face the coal should be removed quickly from the various places to facilitate the movement of machines, whereas the intermediate system just passes the same coal on to the main transportation system. Selection of the transportation system must be based on the seam height, mining methods used to extract the coal, capacity required, ease of coal handling, and haulage efficiency. When driving rooms, mine cars can be used. They often simplify supply haulage and rock handling because they can also handle these items. Conveyors could be used and would have a greater haulage capacity but they cannot handle supplies easily or segregate the rock. When using a different mining method, such as longwall, mine cars cannot be used because there is not sufficient space to move the cars at the face nor can the cars haul the coal without delays which would cause excessive losses in production. As for ease of handling

Jan 1, 1981

By M. Cohen, R. T. Howard

The purpose of this paper is to direct attention to the lower part of the austenite transformation diagram, or TTT curves, where considerable uncertainty still exists as to the blending of the bainite and martensite reactions. The dissimilarities between these two low temperature transforrnations have been summarized recently by Troiano and Greninger.' Of particular importance to the present work is the fact that martensite formation, unlike bainite formation, is not suppressed by the fastest quenching rates attainable. However, most of the investigations in this direction have been concerned primarily with the start of the martensite transformation (Mg) during cooling, rather than with the quantitative aspects of the subsequent reaction on either further cooling or isothermal holding. Several years ago, Cohen2 suggested a form of transformation diagram which reconciled, at least schematically, the isothermal characteristics of the bainite transformation with the insuppressible nature of the martensite transformation. In essence, the diagram consisted of a family of horizontal lines (representing the progress of the austenite-martensite reaction during quenching) which were interrupted in point of time by the bainite family of C-curves extending down from higher temperatures. This picture received later support by metal-lographic3 and dilatometric4,5 studies, but the techniques employed were not sufficiently critical to substantiate some of the details. Elmendorf6 and Grange and Stewardi have shown that the Greninger-Troiano metallographic technique8 may be used not only for M, determinations, but for studying the course of further austenite decomposition. In fact, the latter investigators have observed the amount of martensite formed as a function of temperature below M, in fourteen commercial steels. In the present paper, the Greninger-Troiano technique has been combined with the lineal method of Howard and Cohen9 to provide a unique, quantitative treatment of the austenite-martensite reaction. Furthermore, isothermal transformations have been similarly measured on holding at temperatures above and below M., thus permitting a fairly detailed presentation of the lower part of the conventional austenite transformation diagram. Experimental Details Materials The steels, listed in Table I, were selected for study because they exhibit a satisfactory range of M. temperatures and have not received as much attention as the lower carbon grades. They were prepared as 30 lb induction furnace heats in the laboratories of the Vanadium-Alloys

Jan 1, 1949

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By M. Cohen, R. T. Howard

The purpose of this paper is to direct attention to the lower part of the austenite transformation diagram, or TTT curves, where considerable uncertainty still exists as to the blending of the bainite and martensite reactions. The dissimilarities between these two low temperature transforrnations have been summarized recently by Troiano and Greninger.' Of particular importance to the present work is the fact that martensite formation, unlike bainite formation, is not suppressed by the fastest quenching rates attainable. However, most of the investigations in this direction have been concerned primarily with the start of the martensite transformation (Mg) during cooling, rather than with the quantitative aspects of the subsequent reaction on either further cooling or isothermal holding. Several years ago, Cohen2 suggested a form of transformation diagram which reconciled, at least schematically, the isothermal characteristics of the bainite transformation with the insuppressible nature of the martensite transformation. In essence, the diagram consisted of a family of horizontal lines (representing the progress of the austenite-martensite reaction during quenching) which were interrupted in point of time by the bainite family of C-curves extending down from higher temperatures. This picture received later support by metal-lographic3 and dilatometric4,5 studies, but the techniques employed were not sufficiently critical to substantiate some of the details. Elmendorf6 and Grange and Stewardi have shown that the Greninger-Troiano metallographic technique8 may be used not only for M, determinations, but for studying the course of further austenite decomposition. In fact, the latter investigators have observed the amount of martensite formed as a function of temperature below M, in fourteen commercial steels. In the present paper, the Greninger-Troiano technique has been combined with the lineal method of Howard and Cohen9 to provide a unique, quantitative treatment of the austenite-martensite reaction. Furthermore, isothermal transformations have been similarly measured on holding at temperatures above and below M., thus permitting a fairly detailed presentation of the lower part of the conventional austenite transformation diagram. Experimental Details Materials The steels, listed in Table I, were selected for study because they exhibit a satisfactory range of M. temperatures and have not received as much attention as the lower carbon grades. They were prepared as 30 lb induction furnace heats in the laboratories of the Vanadium-Alloys

Jan 1, 1949

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By Robert B. Kistler, Ward C. Smith

The borate industry is one of the few sectors of the mining and mineral-processing industry which the United States still dominates. Since about 1927, the United States has supplied over half of the world's total boron and borate raw materials, and many of the chemical derivatives as well. Chiefly responsible for this record are companies producing sodium borates from two large deposits in southern California, at Boron (Kramer) and Searles Lake. The sodium borates, or products derived from borax and borax-containing brines, are the preferred borates for industry because they are soluble in water and combine readily with most other chemicals. Calcium borates are required for certain end uses, and these are produced from smaller colemanite-ulexite-probertite bodies. Sodium-free borate compounds also are produced from boric acid, which can be manufactured from either sodium or nonsodium borate minerals. During the past hundred years, the use of boron compounds throughout the world has risen from a few tons per year to the equivalent of over a million tons of B2O3. Leadership in supplying borates shifted from country to country and from region to region during this period, generally as the result of the development of newly discovered deposits that were better in quality, more accessible, or more economically exploitable than previous sources (Table 1). Primary Products and End Uses The principal borate products offered by primary producers in the United States are listed in Table 2. In general, these products are utilized worldwide by almost all consumers, regardless of the original source of the primary borates, In the United States, the primary borates all originate in southern California. Colemanite is produced as crude or processed crude ore from the Death Valley area and is utilized by the fiber glass and ceramic industries without further treatment. Production from Searles Lake, CA is from brines that are processed in chemical plants where borax and other compounds are recovered and the principal borate products are produced. At Boron, CA, the world's leading producer is mining a deposit of mineral borax and operating a chemical refinery. The mineral borax is mined together with included clay, and refined borax or "10-mol" is one of the refinery products. The mineral and the chemical compound are identical, Na2B4O7 • 10H2O. In addition to ship¬ping all major refined borate products from [ ]

Jan 1, 1983

The Institute maintains a dual relationship with students: (1) an individual relationship with a Student Associate; and (2) a relationship with local organizations of students, known as Affiliated Student Societies or Student Chapters. 1. The conditions of Student Associateship are set forth in Section 9, Article I, of the Bylaws of the Institute (see page 64 and following pages). During 1934, sundry amendments were made for the purpose of improving the student relationship. Postgraduate students are now eligible; and associateship can be maintained, with the payment of the regular dues of $2 per year, for 18 months following graduation in June. With his regular dues, each Student Associate is entitled to receive during the year his choice of MINING AND METALLURGY, METALS TECHNOLOGY, MINING TECHNOLOGY, PETROLEUM TECHNOLOGY, or two "classes" of Technical

Jan 1, 1943

By E. A. Anderson, P. W. Ramsey, E. J. Boyle

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By E. C. Pechin

THE Lucy furnace, owned by Messrs. Carnegie, Kloman & Co., and located on the Alleghany River, on the outskirts of Pittsburgh, is a splendid modern furnace, 75 feet high, and 20 feet bosh. She had been working well on low grade ores of about 50 per cent., producing daily 68 to 75 tons. There was on stock 500 tons of Republic ore, one of the purest and best of the Lake Superior ores, averaging over 68 per cent. of iron, which had been procured for the purpose of making a trial for Bessemer iron. This was charged by itself, and Mr. Skelding, the founder, reports that he did not succeed in getting a single cast when it came down, before the furnace chilled from the hearth to the top of the boshes, some 25 feet. Every effort was made to save her, without avail, and the disagree-

Jan 1, 1874

By R. W. Gurry

IN the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and 1110°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon content of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched. The mean result of concordant measurements is that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C. (1755°F.) and 1.89 per cent at 1110°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutectoid temperature (738°C. or 1360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature 1135°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. EXPERIMENTAL PROCEDURE The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.1 In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (16°F.) but at a given location the temperature remained within ±0.5°C. (0.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (1760°F.) and 1110°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with

Jan 1, 1942

By R. H. Brown, F. Keller

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By F. Keller, R. H. Brown

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By Edmund C. Pechin

The Lucy furnace, owned by Messrs. Carnegie, Kloman & Co., and located on the Alleghany River, on the outskirts of Pittsburgh, is a splendid modern furnace, 75 feet high, and 20 feet bosh. She had been working well on low grade ores of about 50 per cent., producing daily 68 to 75 tons. There was on stock 500 tons of Republic ore, one of the purest and best of the Lake Superior ores, averaging over 68 per cent. of iron, which had been procured for the purpose of making a trial for Bessemer iron. This was charged by itself, and Mr. Skelding, the founder, reports that he did not succeed in getting a single cast when it came down, before the furnace chilled from the hearth to the top of the boshes, some 25 feet. Every effort was made to save her, without avail, and the disagree-

By R. A. Meussner, C. T. Fujii

Chromium solution in wustite depresses the oxygen activity in a nonideal manner and expands the lattice slightly. Gravimetric measurements of the equilibrium compositions of wustite containing 0.00 to 1.38 wt pct Cr define the oxygen potential (CO2-CO atm) and the limits of the phase field at 1000°C. These data extrapolate to a maximum solubility of 2 wt pct Cr. The lattice parameter data, room-temperature measurements of quenched samples, differ significantly from those in the literature. Both pure and chromium wus-tites contract at uniform and equal rates as the oxygen content (metal deficit) increases. The a. US metal deficit relationships are straight lines showing none of the curvature previously reported. At constant metal deficit, the a. expands by 0.002? on alloying with 0.4 to 0.5 wt pct Cr but is insensitive to further chromium additions: a small expansion rather than a marked contraction. These results require a modification of the accepted alloying mechanism. IN the high-temperature oxidation of Fe-Cr alloys in Ha-H,and CO2-CO atmospheres the vapor transfer of oxygen from the continuous wustite outer scale to the porous inner scale/alloy interface sustains the high oxidation rates.1"3 The driving force for this transport is the difference in the oxygen activity of the outer wustite and that at the inner scale/alloy interface. In pure CO2, as well as in CO2-CO atmospheres, carburization of the alloy accompanies this oxidation. Current efforts to evaluate the parameters controlling this carburization have shown that the process is not simple; i.e., the carbon concentration in the alloy initially increases rapidly, reaches a maximum, and then decreases slowly as the oxidation time is extended. This is the same pattern reported by McCoy for the more complex oxidation-carburization of stainless steels and an Fe-Cr alloy in CO2 at lower temperatures.4 These changes in the carburization process occur while the overall oxidation rate and the lattice parameters of the scale layers remain constant. If this invariance of the lattice parameter is assumed to indicate a constant scale composition and thus a constant oxygen potential, the carburization results are not easily explained. Electron microprobe traces across the thickness of these outer scales, however, have revealed distinct chromium gradients penetrating 10 to 50 µ from the inner surface where the chromium concentrations were estimated at a few tenths percent. The variation of the chromium cmcentration on the inner surface of the scale, and the resulting change of the oxygen activity, during the oxidation process is considered to be important in defining the carburization process. Thus, to gain an understanding of the complex oxidation-carburization proc- ess, it was necessary to measure the properties of wustite containing known amounts of chromium (chromium wustite). Although the general features of the Fe-Cr-0 equilibrium diagram between 900° and 1300°C have been fairly well established by Richards and white: Wood-house and White,6 Seybolt,7 and Katsura and Muan,8 there have been no detailed studies of the limits of the chromium wustite phase field or the properties of these alloyed wustites. The recent results of a limited study of chromium wustite by Levin and wagner9 indicate that more than 0.67 wt pct Cr is soluble in wustite above 850°C and that this alloying is accompanied by a substantial lattice contraction. This change in the lattice parameter was not evident in the X-ray diffraction patterns of wustite layers from the oxidation experiments;1,3 the lines were sharp even though a chromium gradient existed in the scale. The present paper describes gravimetric equilibrium experiments which delineate the boundaries of the chromium wustite single-phase field at 1000°C and define the changes in the oxygen activity and the lattice parameter of wustite as functions of chromium and oxygen contents. The lattice parameter data of chromium wustite obtained from these equilibrium and special quenching experiments differ considerably from those reported.9 Those for pure wustite show significant differences from the widely accepted data of Jette and Foote.10 Since the causes of these differences are not easily assignable, and since the literature contains many sets of data on wustite which if not in conflict are at best not in harmony, the experimental procedures are discussed in the present paper. EXPERIMENTAL Oxide Preparation. The specimens used in these studies were porous pellets compacted from high-purity (Fe,Cr)2O3 or Fe2O3 powders. These powders were prepared from electrolytic chromium (99.8 pct purity) and electrolytic iron purified by consumable-electrode, vacuum arc-melting processing (299.9 pct purity).11 The oxides were produced by standard analytical procedures: solution of the metals in acids (HC1, then HNO3 added), coprecipitation of the hydroxides (NHaOH), and filtering and washing these precipitates. Initial dehydration of the coprecipitated hydroxides was done in a porcelain evaporating dish heated by a Meker-type burner, final dehydration by firing in a recrystallized alumina crucible at 1000" to 1050°C for 20 hr in an electrically heated furnace. Spectrographic analysis detected the following impurities: silicon, 0.01 pct or less; aluminum, 0.001 pct to trace; manganese and copper, 0.0001 pct to none. Each of these levels is at least one order of magnitude lower than in commercially available CP grade ferric and chromic oxides. Fluorescence analy-

Jan 1, 1969

By Arnold S. Epstein

Tlze green electroluminescence occurring at liquid-nitvogen temperature in epitaxial gallium phosphide diodes is exarnined using the donor dopants silicon and sulfur. Zinc is used as the p-type diffusant. Two tt~ain peaks are found, namely til 0.56 and 0.535 p. The intensity of the gYeen peak occurring at 0.56 is found to oary as -4"' wlzere Jf is the forward current density and to first order appears to be dependent on the concet~tvation of ionized donovs. Tile vadintive lifetinze fov this process is -10-'sec. The intensity of the 0.56-p lu~ninescence is nt least several ovdevs of magnitude greate,, at liquid-nitvogen temperature than that noted jor the 0.538 radiation for current densities up to about 35 amp per sq cm. The variation oj- the intensity of. the 0.538-p peak with current density caries according to the donor dopant. With sulfur as the donor one has a J12 dependence, whereas when silicon is the donov a J1.5 dependence is noted. Tl~e above can be fitted to a In molecular process (in first order) such as a band to band recombination. The constant B fir band to band vecombination) is found from our experitt~etlt to be of the order of 2 CZI cm per sec, zcl~ereas for tlze impurity vecombination peak (0.56 p]) tile A cotzstor~t is of the order of. 7 x 10-' cu cm per sec. The structuve o/. the diodes at liquid-nitvog-en tett~peruture is oj tlze double injection type, and by carefi~lly selecting. the thickness of the structure one can regulate the onset of the 0.538-p radiation. The diode clzavaclevistics follow an I-Vx laiv where x is >1. Llregatiue resistance in these structures con be correlated with saturation of tlze 0.56- peak. ThE development of high-purity, large single crystals of epitaxially grown gallium phosphide is the ultimate aim of the studies to be reported. While a number of papers and reviews' have been presented on properties of gallium phosphide grown from gallium solution and from the melt, less attention has been paid to the properties of epitaxial gallium phosphide grown from the vapor. In the studies to be reported we have examined the effects of shallow donor impurities, primarily silicon and sulfur, at liquid-nitrogen temperature, on both the electrical and green electroluminescent properties of carefully characterized single-crystal epitaxial Gap. I) EXPERIMENTAL PROCEDURES A) Material Preparation and Properties. The samules used in this investigation were single-crystal n-type epitaxial gallium phosphide. he single crystals were synthesized from the elements by vapor transport and epitaxial deposition on single-crystal gallium arsenide substrates. Typical transport agents used were chlorides. The growth procedures are described in more detail in Ref. 2. The samples were grown in the (111) orientation and had thicknesses up to 480 . Following the growth, the GaAs substrate was removed from the epitaxial Gap by etching in nitric acid. The Hall effect and resistivity of these n-type samples were measured as a function of temperature and analyzed for impurity content and compared with spectroscopic emission analysis. The results are given in greater detail in Ref. 3 but a summary is noted in Table I. In Table I, AED denotes the donor ionization energy, Nd is the donor impurity concentration, lvA is the acceptor impurity concentration, NI is the total impurity concentration, Rip vs temperature is the measured Hall mobility-temperature relationship from liquid nitrogen to about 400"K, n(77"K) is the measured carrier concentration at liquid nitrogen, and R/p(77'~) is the measured Hall mobility at liquid nitrogen. Good agreement is noted between electrical and emission analysis for the major donor impurity, silicon, in the two materials where it is a major constituent. In the case of the two samples SC90-6 and AP138-3(111) B which were sulfur-doped the ionization energy found from the electrical data is in good agreement with that reported for sulfur.4 The acceptor impurities are not known, although from the presence of magnesium in the samples as indicated by emission analysis and its known role as an acceptor in GaP,4 magnesium could be present as an acceptor. Similarly, since silicon is known to be an amphoteric impurity4 it may also be present as an acceptor in the Gap.* The *A small band has been noted at 0.625 11 in samples SC90-6, SC76-4, and SC77-4, suggesting according to Ref. 5 that sillcon could be present as an acceptor In these samples since these authors have found this peak to represent a donor-silicon emission. presence of calcium deduced from emission analysis is not correlatable with the electrical analysis and its presence as an electrically active impurity should be questioned. B) Sample Preparation and Diode Fabrication. The original slices were of the order of 2 sq cm in area witi the (111)B face up. The material was cleaved and sectioned and the best pieces selected (i.e., those which visually appeared to have the least strain and defects). The samples were polished, lightly etched, and cleaned in trichloroethylene. Zinc was diffused in a closed tube at 800°C to form a p-n junction. Diodes were made from these samples. The depth of junction varied, but did not exceed 10 p depth. The back side of the slice was lapped back and a low-resistance n-type contact was formed (at 600°C in forming gas) to an Au-Mo tab with a hole in the middle for

Jan 1, 1968

By AIME AIME

FOR constructive research in copper and brass and other non-ferrous metals and their alloys, and his contributions to the establishment of the present accepted high standards of quality William H. Bassett, technical superintendent and metallurgist of the American Brass Co., has been awarded the James Douglas Gold Medal for 1925. Mr. Bassett was born in New Bedford, Mass., on March 7, 1868, and was graduated in chemistry at the - Massachusetts Institute of Technology in 1891. In the same year he went to Pope's Island Manufacturing Co., at New Bedford, as chemist where he remained until 1895, where he became a teacher in chemistry at the Swain Free School, which position he retained until 1900. He then became chemist for the New Jersey Zinc Co., at Newark N. J., and in 1902 went to the Coe Brass branch at Torrington, Conn., as Chemist. In 1903 he became chief chemist and metallurgist and since 1912 has been technical superintendent and metallurgist of the American Brass Co., with head- quarters at Waterbury, Conn.

Jan 1, 1924

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By Frank Corwin

It is the purpose of this article to give a brief account. of the experimental work and to show how the increase in efficiency was brought about. Part of the experimental work described in this paper was carried out by the writers, while in the employ of the Anaconda Copper Mining Co., under the direction of M. W. Krejci, Metallurgist, and Arthur Crowfoot, Chief Sampler. Complete records of all of the MacDougall testing work have been placed at our disposal through the courtesy of A. E. Wheeler, Superintendent. II. BRIEF HISTORY OF PRESENT MACDOUGALL PLANT. The first change from the Brueckner cylinders used for roasting concentrates at Great Falls was the construction of a MacDougall roaster of the Herreshoff type. This furnace was first started on June 15, 1898. It bad eight hearths, was lined with fire brick, and had an air-cooled central shaft, but no provision was made for cooling the rabble arms. It was operated for a while, and accomplished the work of roasting, but ran so hot that the rabble arms became twisted and distorted out of shape. To prevent the furnace from becoming too hot a device was then installed to draw the heated gases away from the hearths. This consisted of a pipe connected to alternate hearths of the MacDougall furnace and also connected to the flue. It was equipped with dampers, 'so that the hot gases could be drawn away from any one of the alternate hearths directly into the flue.

Jan 7, 1913

By Harrison Everett Ashley

Slimes are usually defined as all material passing a certain sized sieve, which is invariably the finest sieve employed by each metallurgist in his tests; 100-mesh and 200-mesh have been taken as the limits by different writers in recent volumes of the Transactions; 150-mesh is common practice. The reader of the first two volumes of Richards' is impressed by the inflexibility with which all grinding-arrangements are praised or condemned according as they make little or much slime. Until recently, one of the principal aims of the mill-man was to keep down the slimes. He was obliged to have separate apparatus for sand- and slime-treatment. The latter was sometimes puzzling and erratic. Often it was found most economical to omit treatment of the slimes entirely, or to store them in immense basins or heaps, waiting for possible future improvements in methods of treatment. Recently, improved processes of agitation and filtration have made possible the successful extraction of values from many slimes. The tendency, when the metal is exceedingly finely disseminated, is to cut out all sand-treatment and to slime everything. These processes have been almost entirely mechanical in their conception, and it is the object of the present paper to show that certain chemical considerations may greatly hinder or assist their successful operation. It has long been a source of dissatisfaction to chemists that their analyses fail to be of much help to the clay-worker; that it is a matter of common occurrence for clays of closely identical ultimate chemjcal constitution to show the widest possible divergence in physical properties.

Jan 1, 1911