Search Documents

By A. H. Daane, B. J. Beaudry

The Sc-Y and Sc-Zr systems were studied by thermal and X-ray methods. Both systems are characterized by complete solid solubility in the low temperature hexagonal form and in the high temperature bcc form. In the Sc-Y system, there is a minimum in the solidus at 50 at. pct and 1365°C, while the solidus in the Sc-Zr system follows a nearly straight line relationship between the melting point of scandium and zirconium. There is a minimum in the temperature of transition from hexagonal to bcc in the Sc-Y system at 43 at. pct Y and 1175°C; while the temperature of transition is raised in the Sc-Zr system to a maximum of 1415 °C at 30 at. pct Zr. INTEREST in the metals of the first transition series has usually stemmed from their useful properties; however, there is now a great deal of interest in determining the fundamental nature of these metals. Since scandium is the first of these transition metals, a study of the preparation and Properties1 and the alloying behavior of scandium2 was initiated. In a continuing study of the alloying behavior of scandium, the systems of scandium with zirconium and yttrium have been established. Extensive solid solubility in both the Sc-Zr and Sc-Y systems was expected from application of the classical rules of Hume-Rothery. Also, the modified Darken and Gurry plot as suggested by Gschneid-ner3 showed ideal conditions for solubility in the Sc-Zr system with less favorable conditions in the Sc-Y system. The effect of scandium on the transformation temperature of zirconium and yttrium was of interest, since a recent empirical observation by Uly and Burr4 predicted that the solute scandium would raise the transformation temperature of zirconium and lower the yttrium transformation. In addition to noting the validity of the above predictions, the SC-Y and Sc-Zr systems were established. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar zirconium, distilled scandium prepared by the method described by Spedding, et al.1 and yttrium prepared by the method described by Carlson, et a1.5 The major impurities present in these metals are listed in Table I in ppm. Alloy Preparation. All the alloys examined were initially formed by comelting the two metals in a nonconsumable electrode arc-melting furnace under an atmosphere of purified helium or argon. The buttons were inverted at least five times and re-melted each time to ensure homogeneity. During preparation of Sc-Zr alloys, approximately 1 wt pct was lost which was attributed entirely to the loss of scandium by distillation. When preparing Sc-Y alloys, approximately 1.5 wt pct was lost, but it was assumed that the intended composition was maintained, since the relative weight lost when arc melting the component metals was nearly the same. Samples weighing 15 to 20 g were prepared for time-temperature thermal analysis, while only 1- to 2-g samples were prepared for the optical pyrometer and X-ray diffraction studies. Thermal Methods. The solidus and the melting points of the metals were determined by an optical pyrometer method described previously.2 The temperatures at which the transformation from hexagonal to bcc occurs were determined by differential thermal analysis. Several points on the solidus and liquidus in the Sc-Y system were also determined by this method and are in good agreement with those obtained by the optical pyrometer method. The procedure followed in the preparation of samples for thermal analysis and the furnace used have been described elsewhere.2'6 Since a limited quantity of scandium was available, most of the alloys were not melted during thermal analysis, thus avoiding contamination by the crucible. The alloy could then be reused and the composition changed by adding the desired quantity of solute to obtain the next alloy. Heat Treatment and X-Ray Methods. In order to ensure homogeneity, the "as arc-melted" alloys Were wrapped in tantalum foil, sealed in quartz capsules and heated at 1100°C for 15 hr and then cooled at a rate of 8 deg per min. Samples for X-ray diffraction were filed from these heat-treated alloys, sealed in 1/8 in. by 1/2 in. tantalum capsules under

Jan 1, 1963

By V. G. Cawagdan, E. M. Sacris

The performance of the grinding circuit, from the initial stages of operation to the present, is discussed. The mill efficiency as measured by the Bond (Bond and Maxson, 1943) grindability data and the operating work index is presented. The objective was to produce a sand cyclone overflow containing not more than 6% 210 µm (+ 65 mesh). This has never been attained, even at low milling rates. Significant improvements in throughput were achieved by instituting equipment changes and process modifications within the grinding circuit. Grind improvements were achieved with enlargement of cyclone spigots, grinding at reduced densities, and decreasing the opening of the ball mill discharge. Additional grinding capacity was realized by converting the concentrate regrinding mill into a secondary ball mill. The previous 20% 210 µm (+ 65 mesh) grind improved to under 15% 210 µm (+ 65 mesh). The latest approach to solving the coarse grind problem is also discussed.

Jan 1, 1985

By J. Versluys

When a well strikes an oil-bearing layer, the oil has a pressure which is generally sufficient to enable it to rise to near the surface (sometimes above the surface). As soon as a well begins to produce, however, the liquid moves through the pores of the reservoir bed and the pressure in the well becomes much lower than the pressure originally prevailing there. At some distance from the well, however, the pressure in the reservoir bed remains unaltered; thus the pressure of the oil has not only to lift the oil, but also to overcome the friction resistance in the pores. The fact that so many oil wells are gushers is a consequence of the energy accumulated in the gas. In gushing the well acts as a gas-lift. A mixture of liquid and gas (the latter partly dissolved in the former) rises vertically from the oil-bearing layer through a cylindrical casing to the surface. In time conditions alter and the well ceases to gush regularly, then the gushing can be further promoted by inserting a narrower tube in the well and connecting the top of the oil string to the tubing. If the action in time becomes irregular, the gushing can be kept up for a further period by forcing gas between the two tubes. In the oil fields the term "gas-lift" is used actually only where extraneous gas is applied, as in the last of the stages mentioned. The action, however, is just the same whether the gas exclusively originates from the formation, or is partly applied artificially. Thus by gas-lift we simply mean a vertical tube in which the energy of gas under pressure, and of dissolved gas, is utilized for raising a liquid. In gushing oil wells the pressure is frequently very high and the absorption coefficient 0.4 (expressed in vol. ratio) of the coexisting gas is not particularly high, so that in reality it should be assumed that a considerable portion of the gas, at any rate at the bottom of the gas-lift, is dissolved in the oil. For water-producing wells this is not usually of such importance. Where the volume of the flowing gas is much greater than that of the flowing liquid, the latter can be suspended in the former in the form of

Jan 1, 1930

By B. A. Wilcox, A. H. Clauer

The tensile and creep deformation characteristics of fiber reinforced composites have been studied, primarily at room temperature. The matrix was an alloy of Mg-14 wt pct Li-1 wt pct Al (LA141A alloy) and the reinforcing fiber consisted of continuous wires of a high strength precipitation hardening stainless steel (AFC-77 alloy). The ultimate tensile strength and strength-to-density ratio of composites were much improved over that of the mmix, both at room ternperatwe and up to 200°C. Creep studies at room temperature revealed logarithmic weep behavior for wires and composites and steady state creep for the nonreinforced matrix. It was concluded that creep of the fibers controlled composite creep. The instantaneous logarithmic weep rate of the composite, 6, was related to the average tensile stress on the fibers, where n = 3.4. Mg-Li alloys are the lightest structural metals commercially available, e.g., the alloy LA141A (Mg-14 wt pct Li-1 wt pct Al) is 27 pct less dense than beryllium Although Mg-Li alloys have moderate tensile strengths at normal strain rates and ambient temperature, their creep strength is relatively poor, even at room temperature. Reinforcement by fibers offers a means of increasing the tensile strength as well as overcoming the limitations of low creep strength. With a proper choice of reinforcing filament, composites could be designed with higher strength-to-density and modulus-to-density ratios than the matrix alloy. This communication reports a study on the tensile and creep characteristics of alloy LA141A reinforced with continuous wires of a high-strength precipitation hardening stainless steel (AFC-77 alloy). The matrix has a bcc structure, with possible precipitates of AlLi and MgLi2A1,3 and is ductile at room temperature Stainless steel wire was chosen as the -reinforcing filament since previous work at Battelle4 showed that a good bond between wire and matrix could be produced in this system. For all volume fractions of reinforcing wire, the theoretical composite strength-to-density ratio is greater than that of the matrix and the modulus-to-density ratio is somewhat lower than that of the matrix. EXPERIMENTAL PROCEDURES The 0.004-in. diam AFC-77 wire was obtained from two suppliers: National-Standard Co.* and Crucible 0.13 Si, 0.18 V, 0.011 P, 0.012 S, balance Fe. In the as-received condition, wires from both sources had room-temperature ultimate tensile strengths of 585,000 to 590,000 psi with approximately 2 pct total elongation and 40 pct reduction in area. Composite preparation was accomplished by the vacuum infiltration technique. This involved placing the continuous wires in a mild steel tube (1/8-in. ID), capping one end of the tube with a sheet of the matrix alloy, and evacuating the other end of the tube. When the capped end was placed in a crucible of the molten matrix alloy and held for 31/2 min at 70O°C, the liquid metal was drawn up the tube approximately 7 to 8 in. A cross-sectional view of a typical composite is shown in Fig. 1. This preparation technique promoted excellent bonding between the matrix and wires, and porosity was rarely observed. Test specimens for both creep and tension studies were prepared by machining off the steel tube. Tensile tests on the wires and composite specimens were made in an Instron using a cross-head speed of 0.01 in. per min. The composite specimens had no reduced section and were held in self-tightening grooved serrated grips. Most of the specimens broke in the effective 1-in. gage section. Even though several tests fractured in the grip section, their ultimate strengths were essentially the same as those of specimens which fractured in the gage section. Creep specimens of the composite were gripped in a similar manner, and

Jan 1, 1970

By John Wulff, H. H. Uhlig

Since its first mention in the literature in the eighteenth century12 the phenomenon of passivity in metals has stimulated much speculation and attendant controversy as to its nature and cause. No one of the numerous theories so far proposed has been generally accepted. ‡ Faraday,' in 1836, associated the passivity of iron with a protective film over the surface of the metal, which materially prevents or slows down reaction with corrosive environments. His theory was that oxidizing acids like nitric acid form an unstable oxygen or oxide layer over the iron surface, which protects the underlying metal from further attack. This concept was simple yet plausible, and without alteration has frequently been assigned in present-day discussions as explanation of the passivity of many metals. With the advent in recent times of stainless steels, it is not surprising that this oxide film theory of passivity proposed by Faraday has been used to explain the phenomenal corrosion resistance of stainless steels and other passive alloys. The passive alloys, such as the chrome-iron alloys, are supposedly covered with a protective oxide film, which forms on exposure of the alloy to air, is extremely stable and self-healing, and accounts for the remarkable resistance of these alloys to corrosion. Within the past few years, several investigators, following the theory of film protection, have attempted to gauge the resistance of the supposed film on steels. Brennert8 and Donker and Dengg9 determined the potential at which a negative ion (e.g., C1-) moving in an electric field reacted with the metal anode, as detected by increased current flow or change in potential of the steel electrode in an electrolytic cell. The potential corresponding to reaction Brennert called the film break-through potential.

Jan 1, 1939

By John Wulff, H. H. Uhlig

Since its first mention in the literature in the eighteenth century12 the phenomenon of passivity in metals has stimulated much speculation and attendant controversy as to its nature and cause. No one of the numerous theories so far proposed has been generally accepted. ‡ Faraday,' in 1836, associated the passivity of iron with a protective film over the surface of the metal, which materially prevents or slows down reaction with corrosive environments. His theory was that oxidizing acids like nitric acid form an unstable oxygen or oxide layer over the iron surface, which protects the underlying metal from further attack. This concept was simple yet plausible, and without alteration has frequently been assigned in present-day discussions as explanation of the passivity of many metals. With the advent in recent times of stainless steels, it is not surprising that this oxide film theory of passivity proposed by Faraday has been used to explain the phenomenal corrosion resistance of stainless steels and other passive alloys. The passive alloys, such as the chrome-iron alloys, are supposedly covered with a protective oxide film, which forms on exposure of the alloy to air, is extremely stable and self-healing, and accounts for the remarkable resistance of these alloys to corrosion. Within the past few years, several investigators, following the theory of film protection, have attempted to gauge the resistance of the supposed film on steels. Brennert8 and Donker and Dengg9 determined the potential at which a negative ion (e.g., C1-) moving in an electric field reacted with the metal anode, as detected by increased current flow or change in potential of the steel electrode in an electrolytic cell. The potential corresponding to reaction Brennert called the film break-through potential.

Jan 1, 1939

By Leendert de Witte, Fred J. Radd

In many areas caring failures can be directly related to electrical currents observed in the casings. It is the thesis of this paper that the observed casing currents are mainly due to electrochemical potentials of the type in evidence on spontaneous potential curves of electrical logs. The general nature of these potentials are discussed and an equivalent circuit is given for current and potential distributions around open holes. The casing forms a short circuit to these potentials and tends to average the effects of local cells. The case of casing corrosion opposite the Dakota water sands in the salt-mud area of Kansas is discussed anil used us a qualitative, illustration of the relation between SP's and casing currents. A method of quantitative derivation of casing current distribution frorn electric log SP curves, using linear transform theory, is described and results are compared with a measured current profile. The effects of hydrogen over-potentials at the cathodic portions of the pipe are considered and some laboratory data are given in support of conclusions regarding the over-1.01tuge.s. INTRODUCTION To date an appreciable amount of work has been done on the measurement of oil well casing currents and on the correlation of the anodic portions of the current profiles with corrosive casing failures. Speculations on the origin of the casing currents have, however, remained rather vague; and although almost every plausible cause has been mentioned, there is to the writers' knowledge no clear-cut expose' on the details of the causes of the corrosive currents in the literature. A study of current surveys and casing failures in the N.W. Burnett field, Ellis County. Kan.. indicated the probability that concentration cell emf's between the Wellington salt section and the relatively fresh waters in the Dakota sands were a major cause of the corrosion currents. A more general concept evolved upon analysis of the severe corrosive conditions in the Pleistocene sands in the Ventura Avenue and San Miguelito fields in California. In this area no major variations in the salt content of the formation waters occur and yet large casing currents are observed. An explanation is found in the fact that the local spontaneous potentials which are set up due to concentration contrast between the drilling fluid and the connate water are short circuited when casing is set. The very conductive path through the casing increases the magnitude of the currents and has the tendency to average local sources over fairly large intervals. Current will flow between the sections that are predominently shaly and the sections that are mostly sandy. At the places where the current leaves the pipe, corrosive attack will occur. This same phenomenon will be present wherever unprotected pipe is set through sections that show large SP kicks on the electric logs over reasonably thick interval~. GENERAL- NATURE OF THE SPONTANEOUS POTENTIALS When a sequence of sedimentary rocks is penetrated by a drill hole filled with a mud which has a different salt concentration from that in the formation waters, various types of electrochemical potentials are established between the formations and different parts of the mud column. Opposite clean sand sections. a simple liquid-liquid junction potential will be observed; while opposite argillaccous formations, a membrane potential, often referred to as shale potential, will be established. The first quantitative analysis of these emf's in terms of liquid junction and membrane potentials is due to Wyllie.1

Jan 1, 1956

By J. L. Walter

Extra-low carbon iron sheet, when deformed and annealed, undergoes exaggerated or abnormal grain growth in the critically deformed regions of the sheet. This exaggerated pmth occurs, for low strains (3 to 6 pct), only in sheet which has a fine dispersion of precipitates in the subsurface region of the sheet and fewer and coarser precipitates in the sheet interior. These particles have been identified as manganese sulfides. Wing the anneal, grains near the surface are gvowth-inhibited by the fine particles but the grains in the interior are free to grow normally. With the additional driving force provided by the strain energy, the interior grains first grow into the small subsurface pains. Eventually, these growing grains grow completely through the sheet. Calculations of limiting grain sizes at various values of strain indicate that a volume fraction of precipitates in excess of 10-' would be required to eliminate exaggerated growth in material strained to 10 pct. OPEN-COIL annealing has made decarburization of sheet steel both efficient and economically practical. Use of such material for porcelain-enameling stock is one of many possible applications of low-carbon iron since carbon in steel is deleterious to porcelain-enameling properties.' However, the extra-low carbon iron presently available presents another problem, that of exaggerated grain growth in regions where the sheet has been deformed as by bending or stretching. In exaggerated grain growth a few grains start to absorb their neighbors and these may become very much larger than the average grains of the sheet. Other names for exaggerated grain growth are coarsening, critical grain growth, secondary recrystallization, abnormal grain growth, or discontinuous grain growth. While this grain growth does not affect the enameling qualities of the low-carbon iron sheet, their presence results in a marked reduction of tensile-yield strength in the region of the sheet containing the large grains. The loss of tensile yield strength may render the material unsuitable for many applications . This report describes the results of a study undertaken to determine the cause of the exaggerated grab growth in extra-1ow carbon iron and, if possi- ble, to prescribe practical procedures for its prevention. GENERAL THEORY The driving force for exaggerated grain growth is the grain boundary free energy. This driving force is proportional to (l/rl + l/r2) where rl and r2 are the mutually perpendicular radii of curvature of the boundary between the growing grain and the grain being consumed. Thus, the greater the difference in size between the growing grain and the matrix grains, the higher the driving force for grain growth. If, however, the matrix grains are free to grow simultaneously, the driving force for exaggerated growth will be diminished. Stability toward growth of the matrix grains may be caused by a) a strong single orientation texture (texture inhibition),' b) a dispersed second phase,3"5 c) the thickness effect,' or d) intergranular segregation.7"9 As exaggerated growth occurs when growth of the matrix grains has been slowed by the stabilizing processes mentioned above, there must be an additional factor acting to promote growth of a few of the grains to the point where they are enough larger than the matrix grains that boundary energy driving forces are sufficient to cause continued growth. For instance, at the annealing temperature, growth-inhibiting inclusions may slowly dissolve and coalesce. Eventually, a grain boundary becomes unlocked and migration occurs at the expense of neighboring grains. Or, an additional driving force may be supplied to some of the grains if the material is strained. Then, since some grains will be strained less than others, the difference in strain energy between adjacent grains may be sufficient to overcome boundary locking and allow growth of the grains with lower strain energies. In the present study, therefore, such factors as the presence or absence of dispersed phases, the nature of the exaggerated growth, and the effect of strain have been considered. EXPERIMENTAL PROCEDURE I) Material and Processing. Three types of low-carbon iron were used in this study; types A and B were commercial grades, each from a different supplier.* The precise details of the processing of

Jan 1, 1963

By C. S. Giggins, F. S. Pettit

The oxidation of Ni-Cr alloys in 0.1 atm of oxygen has been studied at temperatures between 800" and 1200°C. For alloys with 30 wt pct or more Cr, continuous layers of Cr2O3 are formed during oxidation. In the case of alloys with chromium concentrations between approximately 5 to 30 wt pct, external scales of Cr203 are formed over grain boundaries whereas internal precipitates of Cr2O3 and external layers of NiO are formed at other areas on the alloy surface. When such conditions are present on the alloy surface, chromium diffuses laterally from those areas covered with a continuous layer of Cr2O3 to areas where a Cr2O3 sub scale exists and it is possible for the sub-scale zone to become separated from the alloy by a continuous layer of Cr2O3. Whether such a state will be attained depends upon the initial grain size of the alloy and the oxidation time. When the concentration of chromium in the alloy is less than 5 pct, Cr2O3 is formed internally both at grain boundaries and within the interior of grains and the alloy is covered with an external layer of NiO. MECHANISMS which describe the growth of oxide scales on nickel-base superalloys are complex and the effects produced by the various elements in these alloys on the oxidation behavior of superalloys are not clearly understood. In order to determine the influence of the different elements on the oxidation behavior of superalloys, it is first necessary to examine the oxidation properties of binary nickel-base systems which contain the principal elements present in the superalloys and then progressively more complex systems until compositions typical of the superalloys are attained. Chromium is present in virtually all nickel-base superalloys and the purpose of the present studies was to examine the selective oxidation of chromium in Ni-Cr alloys. The oxidation characteristics of Ni-Cr alloys have been extensively studied1-" to date principally as a result of the high oxidation resistance exhibited by some of these alloys. Ni-20Cr* has long been known *All compositions are given as wcight percent unless specified otherwise. to be oxidation resistant and is commonly used as resistance heating elements for service temperatures up to 1100°C. This alloy cannot be used for extended periods of time at higher temperatures because of the apparent reaction of the external scale with oxygen to form gaseous CrO3. In spite of the considerable work cited above some important aspects of Ni-Cr oxidation still remain unresolved. Virtually all of the previous studies agree that small additions of chromium to nickel, e.g., <10 wt pct Cr, result in increased oxidation rates as compared to that of pure nickel, whereas larger additions, e.g., 20 to 30 wt pct Cr, form alloys with substantially lower oxidation rates. The controversial aspects of the oxidation mechanisms for these alloys that still remain unresolved are as follows: 1) A description of the oxidation mechanism for the low chromium alloys. 2) A description of the oxidation mechanism for the high chromium alloys, particularly with respect to the composition of the external scale which results in the lower oxidation rates. 3) The specific alloy compositions at which the oxidation mechanism changes from that obtained for low chromium contents to that of the high chromium alloys and the reason for this transition. EXPERIMENTAL The Ni-Cr alloys listed in Table I were prepared from high purity metals by nonconsumably arc melting and casting as buttons. These alloys were then given a preliminary annealing treatment in argon at 815°C for 100 hr to promote homogeneity. Each button was cut into 0.250 in. thick sections that were subsequently cold-rolled to 0.050 in. thicknesses and annealed in argon at 815°C for 48 hr to provide a twinned, equi-axed grain structure. The grain size for these alloys was not uniform and the limits, within which the average grain size lies, are given in Table I for the single-phase alloys. All the alloys were single phase with the exception of the Ni4OCr alloy in agreement with the Ni-Cr phase diagram.&apos;&apos; Rectangular specimens were cut from the sheet to provide surface areas of approximately 2.5 sq cm. Exact areas were determined with a micrometer after surface preparation was completed. All of the specimens except the Ni-40Cr alloy and pure chromium were polished through 600-grit Sic abrasive paper, ultrasonically agitated in ethylene trichloride, rinsed with ethyl alcohol, and electro-polished. The specimens were electropolished in a 10 vol pct H2SO4 (conc), 6 vol pct lactic acid, methyl alcohol solution at 70" to 80°C for 2 min at a current density of 0.8 to 1.2 amp per sq cm. This electro-polishing procedure did not produce acceptable surfaces on the Ni-40Cr alloy nor on pure chromium and the oxidation properties of these materials were obtained for specimens polished through 600-grit Sic

Jan 1, 1970

By H. R. Ogden

The notch sensitivity of titanium alloys is affected by impurity content, microstructure, and heat treatment. Using notch tensile properties to evaluate notch sensitivity, three commercial titanium-base alloys were investigated over the temperature range of -320o to 390°F. The alloys studied were Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo. Six interstitial levels were studied for each alloy in four mi-crostmctural conditions. The ff- 0 alloys were studied in both the annealed and heat-treated condition. All tests were conducted using 1/4-in. diam round tensile samples. The notched samples had a 50 pct notch with a notch sharpness (a/r) of 53, corresponding to Kt 6.3. Notch sensitivity was increased by increased interstitial content, low temperature, and acicular-type microstructures. The heat-treated, high-interstitial content - 13 alloys were more notch sensitive than the same alloys in the annealed condition. In addition, minima in the notch tensile-temperature curves were observed at temperatures near 32°F. These minima became more pronounced with increasing interstitial content. 1 HE increaseduse of titanium alloys in high strength applications at subzero temperatures requires that a better under standing of the low-temperature behavior of the alloys be obtained. At low temperatures, metals generally exhibit increased strength with lowered ductility and tohness. Notch sensitivity and the factors which influence it become more important as the strength level is increased and the temperature is decreased. Some of the factor s which affect notch sensitivity in ti- tanium alloys are composition, interstitial content, microstructure, and heat-treatment condition. In this paper, the results of a study of these variables on the notch sensitivity of three titanium alloys at temperatures from —320o to 390o are reported. The notch geometry selected for this program was chosen to provide a severe test of notch sensitivity. The ability of the metal to flow without initiating fracture under these severe conditions is reflected in the notch-strength values. Since notch strength is, in part, determined by the constraint exerted by the combined tensile stresses, the behavior of notch specimens reflects the properties of the material under combined stresses. For example, a material with a high notch-unnotch strength ratio may be expected to withstand the biaxial stresses encountered in a pressure vessel better than a material with a low ratio of notch-unnotch strengths. This implies that maximum strength alone is not a sufficient criterion for applications of this type. It further may be concluded that the various conditions that promote poor notch behavior also will affect adversely the performance of materials under combined stresses. In the alloys studied, these included low temperatures, high interstitial levels, and hasformed microstructures. EXPERIMENTAL PROCEDURES Three alloys, Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo, were purchased from commercial producers as 2-in.-dam rod stock. Oxygen and nitrogen were added to these alloys by remelting to obtain a variety of interstitial contents as shown in Table I. In order to Compensate for the much more potent strengthening effect of nitrogen compared with oxygen, an oxygen equivalent content is used to describe the total oxygen plus nitrogen contents studied. It has been suggested previously1 thatnitro-gen is approximately twice as effective in strengthening as oxygen, and carbon, to the extent it is in so-

Jan 1, 1962

By V. Vahatalo, E. Hakapaa, H. Tanner

Recently modernized, the surface plant of the Outokumpu mine in Finland incorporates a number of ideas meriting close scrutiny from this side of the Atlantic. The mining methods make extensive use of concrete in some unusual ways. Design of the headframe and surface plant represents the latest thinking of European engineers and includes an integral Koepe hoist. The deposit is in eastern Finland, province of North Karelia, 30 miles west northwest of Joensuu and at 60&apos;44&apos; N, latitude. Pyrrhotite, pyrite, chalcopyrite, and sphalerite mineralization occurs in a shear zone in quartzite near a body of serpentinite. Two lenses have a total length over 12.000 ft, with remaining reserves of the 3 to 4 pct Cu ore estimated at about 15 million metric tons.

Jul 1, 1955

By Otto H. Henry, J. J. Cordiano

THOUGH powder metallurgy is one of the oldest of metallurgical processes, it is in its infancy as a branch of the modern field of metallurgy. As early as 3000 B.C., the ancients produced implements and weapons of iron by reducing iron ore in a charcoal fire and forging the resultant sponge while still hot into the desired shape. Melting and casting soon superseded the powder metallurgy practice, and it was not until the turn of the twentieth century that powder metallurgy was applied to the commercial manufacture of tungsten lamp filaments. From this beginning, the use of the powder metallurgy process spread to the manufacture of porous oil-impregnated bearings, cemented carbide tools, contact points, diamond grinding wheels, clutch facings, starter brushes, resin-bonded radio cores, magnets, metallic filters, and other parts. More recently, and particularly during the present war, there has been a definite trend toward the manufacture of machine parts by this process in competition with the more conventional fabricating methods. Notwithstanding these many developments, scientific progress has been slow. While many articles on powder metallurgy have appeared in the press and various publications, there have been too few contributions to our technical societies, with the result that there is a dearth of the type of information necessary for the full development of this science. It is of primary importance that the results of research and development be freely disseminated if powder metallurgy is to realize its fullest potentialities. PURPOSE OF INVESTIGATION Excluding the refractory metal field, all commercial powder metallurgical products made by a cold compressing and sintering operation contain voids. These voids can be substantially eliminated by subsequent severe working and heat-treatment, but such practice has not proved economical in most applications. By applying heat during the compressing operation, plastic deformation of the powder particles is substantially increased, and the resultant compact or briquette is practically free of voids. However, hot-pressing has many attendant problems, which at present preclude its use in the manufacture of precision parts. The more important of these are to devise: I. A die steel capable of withstanding high pressures at elevated temperatures. 2. A high-temperature lubricant capable of preventing excessive die wear and welding of the compact to the die walls. 3. A method of retaining a neutral or reducing atmosphere in the compacting zone of the die assembly. 4. A means of ejecting the hot-pressed specimen into a neutral atmosphere until reasonably cold.

Jan 1, 1945

By A. A. Bauer, M. S. Farkas, F. A. Rough

An investigation of the d-phase relationships between the uranium-zirconium and uranium-molybdenum systems was conducted. A ternary cut joining U-31.5 at. pct Mo to U-74 at. pct Zr is presented on the basis of differential thermal analysis, metallographic and X-ray diffraction data. HyDothetical isothermal ternary sections, inferred from the determined d-phase relationships, are presented for the uraniztm-zirconium-molybdenum system. A ternary eutectoid, at 454ºC, was found in zirconium-rich alloys. Its composition, based on metallography and electron-beam micro-analysis, is estimated as U-61.7 at. pct Zr-7.1 at. pct Mo. URANIUM binary systems have been studied extensively in the past to supply basic information needed in reactor-fuel development. Alloys of uranium with zirconium, molybdenum, and titanium are of particular interest because, in these binaries, extensive or complete solid solubility between the body-centered-cubic forms of these elements and y uranium exists. In addition, an intermediate phase of limited solid solubility forms in each of these systems by transformation of the high-temperature ?-uranium phase. Previous investigation of the phase relationships existing between the intermediate 6 phases in the uranium-zirconium-titanium and the uranium-molyb- denum-titanium ternaries have already been reported.1,2 The results of an investigation of the phase relationships existing between the 6 phases in the uranium-zirconium-molybdenum system is reported here. The phase equilibria that occur in the solid-state portions of the pertinent binary systems are shown in Fig. 1. Phase nomenclature appearing throughout the report is as shown in these diagrams. The crystal structure of the phases in this system are given in Table I. EXPERIMENTAL PROCEDURES Alloys were cast and fabricated to 1/4-in.-diam rod. Specimens were heat treated and examined by metallographic and X-ray techniques. Thermal-analysis data were obtained.

Jan 1, 1960

By Ziebell, Howard A.

THE Washington magnesite deposits, located in the hilly and mountainous northeastern part of Washington, occur as massive lenses in a sedimentary series made up of dolomite, shale, and quartzite, into which basic dikes have intruded. The ore pattern resembles a series of disconnected chain links extending approximately 25 miles in a south-west direction. Magnesite in this district is all crystalline and closely associated with dolomite, talc, serpentine, and basic dike rock. All deposits which have been developed are near the surface so that quarry-bench mining has been possible. For over twenty years hand sorting magnesite ore at the quarry face was standard practice. Ore cars were hand trammed on 30-lb rail systems which led from the face to ore passes or raises for the magnesite ore and to the waste dumps for disposal of the rejected waste material. This system was somewhat modified by the use of Dempster Dumpster trucks. The ore was, however, still sorted by hand from the calcium and silica bearing waste rock. Power equipment. consisting of one 3/4-yd electric shovel, was

Jan 1, 1949

By G. L. Oldright, T. B. Brighton, C. M. Dice

The base bullion from the lead blast furnace contains varying amounts of the impurities left in the smelter feed by the concentrator, regardless of the method of smelter operation. These impurities may be held in part in mechanical suspension rather than being present as true alloys. However, usually there is little free space in the crucible in which to separate these drosses before the bullion is taken from the lead well. When such a dross is melted in a laboratory crucible and allowed to cool, the products obtained are lead bullion, speiss, and matte in well separated layers. Typical analyses of layers are: Analyses. Per Cent Element Bullion Speiss Matte Pb.............................................. 92.0 41.2 38.3 Cu.............................................. 2.4 36.3 40.6 As............................................... 4.0 16.5 4.3 Sb............................................... 0.7 0.2 0.4 S................................................ 0.6 1.9 13.1 Fe............................................... 0.0 0.0 0.0 Totals......................................... 99.7 96.1 96.7 The absence of iron in these products drossed from the blast-furnace bullion proves that the impurities for the greater part are not simply finely divided blast-furnace speiss or matte that has been dissolved or dispersed in the lead, but are held in solution by the liquid metal and rise to its surface as infusible compounds when the temperature of the bath is lowered. In general, the drosses made locally are metal sulphides and arsenides and not oxidized compounds. The large content of metallic lead also does not seem to be retained because of oxidized compounds

Jan 1, 1937

By Roy D. McLellan

Electrolytic production of cadmium at the Great Falls plant started in the first part of the year 1925. Prior to that time, an experimental unit had been in operation for a few months during the year 1922. At present the plant is the largest producer of cadmium, not only in the United States but in the world. Electrolytic cadmium is characterized by its very low content of impurities. The main impurities, which are lead, copper, zinc and iron, do not aggregate more than 0.05 per cent., leaving a cadmium content better than 99.95 per cent. The consumption of cadmium has increased rapidly since the war, with the growing use in the plating industry. Cadmium plating has come into prominence because of its connection with the automobile and radio industries. As a protective coating, a deposit of cadmium is superior to zinc. Cadmium is also used extensively in alloys. Important among these is the alloy with copper used in telephone and trolley wire. In proportion of 0.5 to 1.2 per cent., cadmium adds materially to the strength and wearing qualities. Practically all commercial zinc concentrates contain a small amount of cadmium. In the electrolytic zinc process, the cadmium that is dissolved in the regular leaching operation is removed from solution with metallic zinc, generally added in the form of zinc dust. This precipitate also contains the copper taken into solution and the excess of zinc dust, which is required in order to insure a complete removal of all impurities. The precipitate is treated by a separate process to recover the copper, cadmium and excess zinc. In order to make the metals more soluble and to render insoluble such impurities as iron, arsenic and antimony, the precipitate is roasted. The roasting is carried out in gas-fired McDougall furnaces, with a roasting temperature of about 700&apos; C. The roasted residue is leached with dilute sulfuric acid, spent electrolyte from the zinc electrolyzing, containing 10 to 12 per cent. free H2S04. The leaching is done in cylindrical tanks of 30 tons capacity, agitated

Jan 1, 1930

By J. T. Eash, N. B. Pilling

As a group, the alloys of iron, nickel and carbon are, in application, one of the most versatile of the ferrous alloy family, and while many investigations have been made of their properties and structure only a few attempts have been made to show the microstructural relation over a wide range of composition. It is necessary at once to be clear about the kind of structural relation with which we are concerned. The equilibrium diagram provides quantitative data regarding structural make-up and its variation with temperature, but equilibrium structures often are far different from the technologically significant ones. This is particularly true of steels and cast irons, and some of the most important components of their structure may have no place in the diagram of equilibrium. The fugitive phases that result from transformation are dealt with in a highly detailed and descriptive manner in the S-curves originated by Bain. The present effort lies in a still different field, which is to portray the relation between sweeping changes in composition and in resultant structure, under controlled but nonequilibrium conditions of thermal treatment. The Guillet1 diagram presented in 1903 was the initial attempt at such a correlation and frequent references to this diagram can be found in the literature even though later work has shown it to require considerable modification. Kase2 published in 1925 a diagram that was based upon observations of furnace-cooled melts. At low carbon contents this diagram agreed fairly well with experience in showing pearlite to exist in alloys containing up to 6 per cent nickel, and completely austenitic steels at 24 to 28 per cent nickel. At high carbon contents, however, irons were indicated as being martensitic at around 2 per cent nickel and austenitic at 12 per cent nickel; these interpretations are open to serious question. Based upon experience with steels and cast iron, Wickenden3 suggested a diagram that agreed fairly well with Kase&apos;s in the steel range but which presented a wide departure from it in the higher-carbon, high-nickel regions. In its broad picture, the Wickenden diagram is an approach to "practical" structures. [ ] Reference may be made at this point to the efforts of Marshy to construct an iron-nickel-carbon equilibrium diagram by the coordination of scattered data, which are described at length in the monograph cited. None of these preceding attempts has appeared to meet the need for an exposition of the structural sequence that is encoun-

Jan 1, 1942

By J. T. Eash, N. B. Pilling

As a group, the alloys of iron, nickel and carbon are, in application, one of the most versatile of the ferrous alloy family, and while many investigations have been made of their properties and structure only a few attempts have been made to show the microstructural relation over a wide range of composition. It is neccssary at once to be clear about the kind of structural relation with which we are concerned. The equilibrium diagram provides quantitative data regarding structural make-up and its variation with temperature, but equilibrium structures often are far different from the technologically significant ones. This is particularly true of steels and cast irons, and some of the most important cornponents of their structure may have no place in the diagram of equilibrium. The fugitive phases that result from transFormation are dealt with in a highly detailed and descriptive manner in. the S-curves originated by Bain. The present effort lies in a still different field, which is to portray the relation between sweeping changes in composition and in resultant structure, under controlled but nonequilib-rium conditions of thermal treatment. The Guilletl diagram presented in 1903 was the initial attempt at such a correlation and frequent references to this diagram can be found in the literature even though later work has shown it to require considerable modification. Kase2 published in 1925 a diagram that was based upon observations of furnace-cooled melts: At low carbon contents this diagram agreed fairly well with experience in showing pearlite to exist in alloys containing up to 6 per cent nickel, and completely austenitic steels at 24 to 28 per cent nickel. At high carbon contents, however, irons were indicated as being martensitic at around 2 per cent nickel and austenitic at 12 per cent nickel; these interpretations are open to serious question. Based upon experience with steels and cast iron, Wickenden3 suggested a diagram that agreed fairly well with Kase&apos;s in the steel range but which presented a wide departure from it in the higher-carbon, high-nickel regions. In its broad picture, the Wickenden diagram is an approach to "practical" structures. Reference may be made at this point to the efforts of Marsh5 to construct an iron-nickel-carbon equilibrium diagram by the coordination of scattered data, which are described at length in the monograph cited. None of these preceding attempts has appeared to meet the need for an exposition of the structural sequence that is encountered in traversing the nickel-steel nickel-cast-iron range under what might be called ordinary departures from equilibrium. ExperimentaT. Conditions Since the intent has been to establish structures developed under arbitrary conditions, experimental details have perhaps more than usual importance. Three of these conditions should particularly be noticed: (I) the material was cast and not subjected

Jan 1, 1942

By J. T. Eash, N. B. Pilling

As a group, the alloys of iron, nickel and carbon are, in application, one of the most versatile of the ferrous alloy family, and while many investigations have been made of their properties and structure only a few attempts have been made to show the microstructural relation over a wide range of composition. It is neccssary at once to be clear about the kind of structural relation with which we are concerned. The equilibrium diagram provides quantitative data regarding structural make-up and its variation with temperature, but equilibrium structures often are far different from the technologically significant ones. This is particularly true of steels and cast irons, and some of the most important cornponents of their structure may have no place in the diagram of equilibrium. The fugitive phases that result from transFormation are dealt with in a highly detailed and descriptive manner in. the S-curves originated by Bain. The present effort lies in a still different field, which is to portray the relation between sweeping changes in composition and in resultant structure, under controlled but nonequilib-rium conditions of thermal treatment. The Guilletl diagram presented in 1903 was the initial attempt at such a correlation and frequent references to this diagram can be found in the literature even though later work has shown it to require considerable modification. Kase2 published in 1925 a diagram that was based upon observations of furnace-cooled melts: At low carbon contents this diagram agreed fairly well with experience in showing pearlite to exist in alloys containing up to 6 per cent nickel, and completely austenitic steels at 24 to 28 per cent nickel. At high carbon contents, however, irons were indicated as being martensitic at around 2 per cent nickel and austenitic at 12 per cent nickel; these interpretations are open to serious question. Based upon experience with steels and cast iron, Wickenden3 suggested a diagram that agreed fairly well with Kase&apos;s in the steel range but which presented a wide departure from it in the higher-carbon, high-nickel regions. In its broad picture, the Wickenden diagram is an approach to "practical" structures. Reference may be made at this point to the efforts of Marsh5 to construct an iron-nickel-carbon equilibrium diagram by the coordination of scattered data, which are described at length in the monograph cited. None of these preceding attempts has appeared to meet the need for an exposition of the structural sequence that is encountered in traversing the nickel-steel nickel-cast-iron range under what might be called ordinary departures from equilibrium. ExperimentaT. Conditions Since the intent has been to establish structures developed under arbitrary conditions, experimental details have perhaps more than usual importance. Three of these conditions should particularly be noticed: (I) the material was cast and not subjected

Jan 1, 1942

By J. E. Tiffany, S. S. Lubelsky

For blasting in coal mines the U. S. Bureau of Mines recommends that permissible explosives be used exclusively, that these shall be fired electrically, and that where feasible the working place shall be cut or sheared. These recommendations are made to promote safety and prevent mine explosions. Although permissible explosives are not flameless, their lower flame temperature and shorter duration of flanie make their use safer than that of nonpermissible explosives. Mixtures of air with both methane and bituminous coal dust, which are liable to occur in coal mines, may be ignited by coming in contact with any type of flame or spark of sufficient temperature and duration or by the firing of a blast. In a working place where a blast is to be fired, in addition to the use of permissible explosives, adequate ventilation for the dilution and removal of accumulations or outbursts of flammable gas should be provided. Bituminous coal mines should be rock-dusted as a means of rendering the coal dust harmless The efficient use of permissible explosives depends upon the proper preparation of the working place, standardized drilling, the strength characteristics of the explosive, and the use of a proper weight of charge. Experienced shotfirers should load, tamp and fire all holes. The major part of the information and data here presented is based on the results of efficiency tests made in large producing mines of Pennsylvania and Illinois. Bureau of Mines Report of Investigations, Serial No. 2697, describes how a standard method of blasting was worked out and put into operation in a mine in southern Illinois.&apos; This paper contains a description of the methods worked out subsequently in another mine in that district. Descriptions of tests in two Pennsylvania mines are given in Bulletins 11 and 19 of the Carnegie Institute of Technology.2 These tests

Jan 1, 1928