By Y. Wang, L. Liu, G. Xu, Y. Lv J. Sheng H. Zhang

In order to increase the service life of large scale coke dry quenching furnaces, the damage mechanism of lining was investigated, and the structure and properties of lining refractories used in cooling section were researched. The results showed that the abrasive wear volume of lining bricks at one fourth height section under skew tunnel was smaller than other sections. The wear loss of mullite brick and dense clay brick used in the lining of cooling section were respectively 8.02 cm3 and 11.65 cm3 in fifteen minutes. The mullite brick was laid with clay brick alternatively. By the different wear rate, the surface of lining was rough and uneven in the later service life, and short brick was easily dropped from lining. During the service, the basis wore off more easily than the aggregate. It is necessary to improve the wear resistance property, which will increase the service life of cooling section’s lining for coke dry quenching furnaces.

Jan 1, 2016

By Liu bing-guo, Peng Jin-hui, Guo Sheng-hui, Kong dong-cheng, Hu jin-ming, Zhang Li-bo

The novel technology of calcination to prepare triuranium octaoxide（U3O8）from ammonium uranyl carbonate in microwave fields was investigated on the basis of the temperature rising characteristics of ammonium uranyl carbonate, triuranium octaoxide (U3O8), and their mixture. The result of experiments show that ammonium uranyl carbonate had weak capability to absorb microwave energy, while triuranium octaoxide has the very strong capability to absorb microwave energy and the sample temperature increased rapidly with an increase mixture ratio of triuranium octaoxide. The optimal calcination conditions were as follows: microwave power 700 W, calcination time 10 min and 60 g in this experiments range, respectively. Under these conditions the value of total uranium and 4 U of triuranium octaoxide was 84.28% and 31.02%, respectively. It is feasible to prepare triuranium octaoxide by calcination from ammonium uranyl carbonate, which mixed with small amounts of triuranium octaoxide under microwave fields.

Jan 1, 2015

By Yong Hack Lee

Nonferrous smelting processes have been through a rapid transformation since the beginning of 1980. The copper smelting technology has changed from the conventional Blast Furnace process to the Flash Smelting and MIB process. In the field of lead smelting, the technology has changed from the Blast Furnace Smelting to the Direct Smelting such as QSL and KIVCET. In 1992, Onsan Refinery successfully commissioned Direct Smelting QSL technology for lead. The QSL could produce more than 160,000 ton per year of lead bullion from lead concentrate and various residues. Moreover, since the year 2000, the TSL (Top Submerged Lance) Technology utilizing the same Direct Smelting process has been successfully commissioned to treat lead concentrate as well as lead sulfate residue produced from a hydrometallurgical zinc plant. This paper presents and compares the energy flows of lead smelting processes such as a conventional process and the Direct Smelting Processes plotted on the Pb-O-S phase diagram. The oxygen potential diagram suggests how to control the oxygen potential in the fum ace. Also, it describes the recent operational experience in the TSL plant of Onsan Refinery with necessary mass balance of key elements.

Jan 1, 2003

By Kim Verbeken, Evelien Van de Steene, Marc Verhaege, Jeriffa De Clercq

"AbstractThe industry is confronted with stricter discharge levels and an increasing awareness to avoid toxic waste (such as heavy metal containing sludge obtained in physicochemical water treatment) and recover valuable metals. This can be realized by ion exchange or by electrodeposition. Both techniques however show an optimum concentration range to efficiently remove and/or recover metals: electrolysis can recover the metal in its metallic form but suffers from low efficiency when applied to diluted solutions, whereas ion exchange can only be applied economically in the low ppm range.A combination of ion exchange followed by electrodeposition was applied to an industrial wastewater. The strong acidic ion exchange resin was stripped with H2SO4 giving a solution of 9g/L nickel. From this solution, nickel was electrodeposited in an ammonia buffer on a Ti-mesh cathode with high current efficiency. It is shown that organic compounds (surfactants, brighteners, …) present in the industrial wastewater do not influence the recovery process.IntroductionAlmost all rinse waters emerging from metal plating plants are generated during the washing operation of plated materials. These solutions with low metal content must either be recycled within the process or be discarded to the surface water after decreasing their metal content to acceptable levels determined by the local environmental regulations, which become more and more stringent. Today, the most commonly used practice is a physico-chemical treatment (precipitation) and a resin post treatment to meet the standards. A more sustainable approach should use a technology to recover efficiently the metal or metal salt without the production of sludge and the effluent should be consistent with environmental regulations."

Jan 1, 2008

By Marta Cabral, C. A. Nogueira, F. Margarido

"Physical processing of spent batteries which includes shredding and sieving operation is the first step for chemical treatment by hydrometallurgy. A laboratory study was carried out to evaluate physical processing efficiency, by analysing the resulting particle size, of alkaline and saline mignon-type Zn-MnO2 batteries. After shredding with a tip shredder, results obtained showed that alkaline batteries were more efficiently size reduced than saline batteries. Difference in particle size distribution was larger for granulometric fraction -20+11.2 mm and also higher for saline batteries. Average diameters (d50) for saline and alkaline batteries were respectively 9.1 and 6.2 mm. Chemical composition carried out on several granulometric fractions allowed to identify metals distribution through size categories. This analysis showed that zinc concentration with the grain size was almost constant, while manganese decreased when particle size increased. More than 95% of iron scarp from the battery cases had a particle size higher than 5.6 mm.IntroductionRecycling process of spent batteries includes physical unit operations which involves a fragmentation step in order to open the battery cases and to allow the access of chemical reactants to the electrode materials, on further chemical unit operations. Shredders are usually used for that purpose, using cutting mechanisms and allowing efficient fracture of residues in order to promote further processing of the contained materials. Batteries are complex products with a large variety of sizes and shapes which causes serious difficulties for predicting and carrying out its fragmentation.Domestic-type batteries are essentially of the Zn-Mn systems and with cylindrical shape, varying from the large size Mono (or D) type to the small size Micro (or AAA) type [1]. Recycling of batteries involves collection, sorting [2] and metallurgical processing [3, 4]. In some processes, the first step of metallurgical processing is dismantling and size reduction by shredding. Research work on spent batteries considering grinding/shredding and physical separation of fractions is scarce [5-7], but investigation in this domain is very necessary."

Jan 1, 2008

By Javier Antoñanzas, Susana Caballero, Eduardo Fernández, Jorge Aragón, Juan Carlos Múgica, Lourdes Yurramendi

Air Pollution Control (APC) residues treatment by plasma was studied as a technology for vitrification. During the project a protocol to verify the plasma technology was developed and afterwards applied to a specific case study: the APC residues from Municipal Solid Waste Incinerators (MSWI). Different operational conditions were tested and the vitrified products obtained were analyzed using standardized leaching tests in order to evaluate their new properties concerning safety storage. Two leaching tests were used for the evaluation, the European EN 12457-4 compliance test for leaching of granular waste materials and the French XP X 31-211 test for the determination of the leachability of a solid waste material initially massive or generated by a solidification process. Finally, conclusions about the environmental performances of the technology were obtained.

Jan 1, 2008

By C. Pichler, A. Ressler, D. Gregurek, A. Spanring

In order to improve the refractory lining life at one of the RHI key customer test procedures were developed within a two years collaboration project. In the first year of cooperation detailed refractory corrosion work in the rotary kiln with Ca-ferritic slag was performed. The main results of the second year of cooperation, reported in this article, involve a detailed testing work with nickel matte and pre-selected refractory brands which was performed in TBRC. A first part of this work was a complete chemical and mineralogical characterization as well as FactSage calculations carried out on provided matte samples. According to these results testing in the TBRC was realized at different process temperatures with several magnesia-chromite bricks. Based on the mineralogical investigation a high chemothermal load caused by sulfidic matte resulted in a deep reaching infiltration of the brick microstructure and partly corrosion of main brick components.

Jan 1, 2015

By Shigeru Ueda, Shin-ya Kitamura, Shohei Koizumi, Xu Gao

Steelmaking slag was confirmed to be a useful fertilizer for paddy growth as it efficiently supplies Ca and Si to soil water. In addition, supplement of Fe from slag fertilizer has been expected to suppress the H2S generation in paddy soil, especially for the degraded paddy soil. However, on the basis of our previous research, the Fe dissolution ability changed with slag brands, and even some brands could dissolve Fe under paddy soil pH, the supplying ability were not high. To improve Fe dissolution, we found that among various kinds of Fe-rich mineralogical phases in slag, the CaO–SiO2–FeO glassy phase showed highest water solubility of Fe. Because the CaO–SiO2–FeO glassy phase was a quenched molten phase, its dissolution behavior may depend on chemical composition, and this is important for controlling slag composition to produce fertilizer which can easily release Fe. Therefore, in this research, the CaO–SiO2–FeO glassy phase of various CaO/SiO2 ratio, Fe2+/T–Fe ratios, and FeO contents were synthesized, and the dissolution behaviors of Fe as well as other cations from these synthetic glassy phases into an aqueous solution at pH of 5 were investigated. The result showed that the dissolution ratio of Fe increased significantly by increasing Fe2+/T–Fe ratio. An increase in FeO content of glassy phase also increased the dissolution of Fe. In addition, the Fe dissolution ratio showed a local maximum with increasing CaO/SiO2 ratio.

Mar 1, 2017

By José Palacios, Mario Sánchez, Fernando Parada

As an alternative method of reducing the large amount of slag generated during metallurgical processes in the primary copper production, it is to use the remaining iron in the slag as feed material for the iron and steel industry. The slag is generated during copper concentrates smelting in ratios ranging from 2 to 5 ton per ton of produced copper, and it contains 42–45% of iron. However, copper, sulfur and other detrimental elements affecting iron properties need to be reduced prior to use the slag in steel production. Therefore, some laboratory experimental run has been conducted to reduce copper by slag oxidation followed by leaching and recovering the dissolved copper by SX-EW, and smelting the solid with coke to produce a metallic phase containing 98% iron and 0.9% molybdenum. In further reducing steps, copper content is lower down and a molybdenum rich iron phase is obtained. Recovery of iron from copper slags considering reduction and control of harmful elements for iron properties was studied.

Mar 1, 2017

By K. Morita, S. Ueda, Y. Matsuki

Tellurium has mainly been used as an alloying element for resulfurized free-machining steel. It globularizes MnS inclusions and improves both machinability and mechanical properties of such steel. This effect is quite sensitive to tellurium concentration.Therefore,its incorporation should be controlled accurately during the secondary refining process, using the thermodynamic properties of tellurium in molten iron. In the present study, Wagner’s interaction parameters of various elements on tellurium were experimentally evaluated by vapor-liquid equilibration, and the vapor pressure of tellurium was controlled using the transpiration method. The values obtained were compared with those of oxygen and sulfur, and they were found to be correlated with the standard Gibbs energy of formation of the corresponding oxides, sulfides, and tellurides.The results indicate that the relations described here could provide estimates of interaction parameters that have not been experimentally determined thus far by using available thermodynamic quantities.

Mar 1, 2017

By Patricia Negrini Siqueira Poveda, Leonardo G. A. Silva

Thermoplastic materials are sensitive to ultraviolet radiation (UV), which can cause structural changes, causing variation in mechanical properties and appearance. UV range between 250 and 400 nm is considered the most aggressive to polymers, and prolonged exposure to it results in breakage and/or crosslinking chains. Light stabilizer additives, blockers or absorbers are added to the polymers for protection in order to extend the life of the final product. The choice of the adequate light stabilizer additive system depends on factors such as resin final application, thickness, geographic location of exposure, presence of fillers in the composition, contact with chemicals, among others. This study evaluates different additive systems: conventional organic, inorganic nanotechnologyc base and the synergy between them when applied to polyethylene considering carbonyl index and UV/VIS results after aging by QUV chamber.

Mar 1, 2017

By Peter K. Liaw, Niann-i Yu, Wei Zhao

"For a plain-weave Nicalon ™ fiber fabric-reinforced silicon carbide (SiC) ceramic composite, little attentation has been paid to the effect of fabric stacking sequence on its mechanical behavior. In this paper, fiber-fabric stacking sequence effects on the elastic stress distributions, ceramic matrix-cracking stress, effective elastic moduli, and flexural strengths of laminated flexural test bars are quantified. A quantification model is established based on the combination of classical laminated plate theories and a fiber undulation model developed by Chou et al. A FORTRAN program is compiled to implement the modeling, which can be run in a SUN work station. The mechanical performance of a continuous fiber-reinforced ceramic-matrix composite (CFCC) with a [0/30/60] lay-up was analyzed and predicted. The variation in the fiber-fabric stacking sequence can vary the elastic stress distributions along the thickness direction of specimens, magnitude of ceramic matrix-cracking stress, effective elastic moduli of the laminate, and crack initiation sites as well as fracture modes. Moreover, all these factors contribute to scatter in flexural strengths of the CFCC.I. IntroductionWith enhanced fracture toughness and the ability of non-catastrophic (graceful) failure behavior, CFCCs are currently under evaluation for high-temperature structural applications in heat exchangers, combustors, hot-gas filters, boilers components, first walls and high-heat flux surfaces gas turbines, space vehicles and nuclear reactors.[1-8] Extensive applications of CFCCs by industry are still hampered by an insufficient understanding of the mechanical behavior, and sometimes, the lack of a well-developed and widely accepted design philosophy, in addition to the high-production costs."

Jan 1, 1998

By Osamu Iida

Since 'start-up of the larger Mitsubishi Continuous Copper Smelting Process in 1991, furnace relining campaign was gradually prolonged to once every 2 years according to deregulation of governmental boiler inspection. On the other hand, in 1998 Naoshima smelter embarked on an intermediate strategic expansion plan to strengthell its international competitiveness. As part of this plan, modifications were implemented in the copper smelter designed to increase output of anodes from new charge source to 270,000 tpa. In May 1998, treatment of dried neutralized residue was started in C furnace, and during the shutdown for brick relining in April 1999, intensive modifications to the boilers as well as the installation of new spray coolers for furnace off gas treatment were implemented. Finally, the new larger oxygen plant was commenced its operation in May 2000 and the expansion was achieved around 30% increase of anode production from original design.

Jan 1, 2001

By O. A. Ogunseitan

The contamination of aquatic ecosystems by mercury wastes is one of the most serious forms of environmental pollution associated with the metal mining and electrochemical industries. The transformation of inorganic mercury to alkylated species is a reversible bacterially-mediated process. The production of methylated mercury is of ?major public health and eco-toxicological concern because these forms of mercury are highly toxic ?and they bioaccumulate in aquatic organisms. We determined the response of the genetic determinants of mei:cury transrormation by Pseudomonas species (that predominate in contaminated soils and sediments), to the concentration and species? or available mercurfiations. By combining selective isolation and gene. ?probe techniques, the intrinsic genetic potential for mercury detoxification in a contaminated environment ?can be estimated. We determined that genetic units required for mericury volatilization (merA ?for mercuric reductase) are naturally amplified in response to mercury. Mercury-resistant bacteria that tolerate up to 100 ug Hg(Il)/ml of medium contain about 10 times more DNA fragments encoding merA than in unadapted bacteria. The exposure of bacteria to methylated.Hg (10 ug/ml lake water) produced increases (up to 10 times) in .genetic units, and higher levels of genetic expression (up to 50 times) per ml of lake water for the mercury reductase system, than on-induced lake water. The findings suggest that in environments where methylated Hg may accumulate as a result of bacterial activity, the reverse reaction which leads to the removal of mercury through volatilization from the system, may be achieved by inducing genetic ?amplification and expression of the mercuric reductase gene system.

Jan 1, 1991

By K. J. Martchek

"This introductory presentation will highlight recent efforts to quantify the positive value of recycling metals such as aluminum, magnesium, lead, zinc, nickel and copper in relation to the three pillars of ""sustainable development"" - environmental protection, economic development and improve social consequences.This presentation will provide an overview of life cycle assessment profiles increasingly being utilized by customers, regulators and environmental advocacy groups to holistically evaluate the environmental performance of materials and products. The environmental profiles of prodi.lcts containing recycled metal will be presented based on rules established by the International Organization for Standardization (ISO).Significant to the life cycle profile of metal products is recent confirmation. that recycling has the potential to reduce materials production energy consumption by 95% for aluminum, 80""/o for magnesium and lead, 75% for zinc, and 70% for copper. Furthermore, . ""metals are eminently and repeatedly recyclable, while maintaining all their properties (1 ). "" Their durability relative to many hydrocarbon based materials enhance .their life cycle performance. However, the persistence of metals when dispersed into our natural environmental makes recovery and recycling particularly important Overall, when considering life cycle effects, recycling is critical to a sustainable future for metal products.Finally, regional and international regulations will be highlighted which will effect the efficient recovery and recycle of metals and their overall contribution to environinental protection, economic development and the enhancement of society."

Jan 1, 2000

By N. Choi

The distribution behavior of selenium and tellurium in nickel sulfide smelting was investigated in the temperature range of 1250-1300 °C under an inert gas atmosphere and various oxygen partial pressures. The distribution coefficients of selenium and tellurium between nickel-copper-iron matte and silica-saturated iron silicate slag were detennined in terms of matte and slag compositions, temperature, and oxygen partial pressure. The effect of slag additives such as CaO, MgO, and Ah03 on the distribution coefficients of those elements was also investigated. It was observed that the distribution coefficients of selenium and tellurium increased with increasing matte grade and temperature. The solubility of selenium and tellurium in the slag decreased with increasing the partial pressure of oxygen within the range investigated in this study. The distribution coefficients of selenium and tellurium increased with the amount of CaO and MgO. Tellurium distribution coefficients also increased by the addition of Ah03. Meanwhile, the addition of Alz03 decreased the distribution coefficients of selenium at high matte grade.

Jan 1, 1996

By Katsunori Yamaguchi

Secondary materials, that contain relatively high concentrations of platinum group metals, (PGMs) are treated in copper smelting process. The PGMs lost in the slag is increasing with increasing quantities of scrap treated amount. To determine the portion of the PGMs chemically dissolved and that associated with the mechanically trapped matte in the slag will be a key factor to improve the recovery of those metals. An experimental study was carried out to determine the distribution of palladium between the FeOx–SiO2 slag and the liquid Cu2S–FeS matte at 1573 K and a fixed partial pressure of SO2 of 0.1 atm. It was found that the distribution ratios are around 10−3 for platinum and palladium. The distribution ratios show a tendency to increase when the grade of matte is increased above 60 mass% Cu. In addition, the solubility of platinum in FeOx–SiO2 slag equilibrated with a pure palladium and the Pd-Cu alloy was determined at 1573 K and the range of oxygen partial pressure from 10−9 to 10−7 atm. The solubility of palladium in the slag tends to increase with increasing oxygen partial pressure and activity of CuO0.5 in the slag.

By Cynthia Belt

"Energy management is critical to aluminum processing given the high energy requirements of melting and processing aluminum. Energy costs have always been a high percentage of the total production costs within this industry. Energy management at many plants relied on better technology that many times required high capital. As carbon management has grown in importance and project payback becomes more critical, a larger view of a plant's process is required. This paper looks at the energy requirement due to current typical practices in overall product recovery, metal loss, utilization, and technology to understand potential methods of reducing overall energy within a plant and within the aluminum processing industry.IntroductionFor many companies that process aluminum, energy is a major portion of their costs that can surpass the cost oflabor. Aluminum processing can include secondary processing of scrap and prime aluminum into sows and/or molten aluminum or casting aluminum by various methods such as direct chill, continuous casting, low or high pressure casting, mold casting, and extrusions. In the case of this paper, we are considering only plants that include the melting process as a portion of their process. The process of melting aluminum takes energy. In most cases, the aluminum must then be heat treated one or more times. Post processing of the aluminum includes rolling mills used for making sheet, extrusion lines, and machining such as saw cuts, drilling, or surface finishes that all take additional energy.While these high energy costs directly affect the profits of the company, energy management within the metals industry is still not widespread. A co=on misconception is that the solution to high energy costs is high cost capital equipment. While state-of-the-art equipment can certainly improve energy efficiency, it is not the only solution. To obtain a truly energy efficient plant, several directions needs to be addressed through an energy management thought process with a wider scope. Impact on potential savings is possible through: product recovery, metal loss, utilization, and new technologies. An understanding of the potential costs and savings from these means is important. Several of these methods provide low cost approaches to saving energy.The background data used in this paper is not a random sample within aluminum processing but yearly averages from various plants in different aluminum processing industries. As is normal in this industry, the plants have been under different corporate management over the years with different strategies for energy management. This data is not meant to be accurate for the entire industry but to suggest areas for energy efficiency work."

Jan 1, 2012

By Peter Bates

"HIsmelt has faced and overcome many challenges in the understanding and development of injection technologies that satisfy process and engineering requirements for further scale up to a commercial plant.An overview of the design basis of bottom and top injection systems with plant results are described in this paper.IntroductionAn appropriate way to introduce this paper is to initially reflect on the genesis of the HIsmelt Process.It is appropriate that Professor Womer is the one we are honouring as it can be claimed that by the involvement of CRA in the WORCRA process that the concepts for irijection systems in iron and steel pyrometallurgical processes achieved significant attention by the company. The development of water cooled injection lances and their application injecting solids and gases with success was certainly a pre-cursor to the development of other injection systems commonly used today in arc furnaces and for top injection at HIsmelt.HistOrically it was the work of Savard and Lee in Canada with shrouded tuyeres and the subsequent commercialisation of this technology at the Maxhiitte Steelworks spawning the suite of bottom oxygen blown process as known as QBOP; OBM and the subsequent combined blowing process such as KOBM that first commercially succeeded in injecting solids under a molten metal bath. The next progressive step from the injection of calcined lime in the technology development was the injection of coal for coal gasification as developed by Klöckner technologies being called KG, KSG and KMS and also the injection of coal for increased scrap melting.A paradigm shift in thought process to leap from steelmaking and coal gasification to direct smelting by injecting coal and iron ore into a molten metal bath in the correct stoichiometric ratio to maintain the bath at a constant temperature and carbon level was the true genesis .of HIsmelt.A good overview of the state of the art of tuyere type injection technology is given in Ref. 1."

Jan 1, 1996

By Motohiro Horiguchi, Kazuo Ichii, Toshio Oishi

"As a fundamental study to prepare copper-based alloys with rare earths (RE: La, Gd, Nd, Ce and Y) without any inclusions, the solubility of rare earth in liquid copper was experimentally determined. Liquid copper alloys were equilibrated with carbon and rare earth carbide in a graphite crucible in an argon atmosphere at 1523-1873 K.Solubilities of rare earth in liquid copper were determined by approaching the equilibrium values from both the lower and the ·higher concentrations than those expected· in the preliminary experiments. They were expressed as a function of temperature. Carbon in Cu-RE alloy was also analyzed and thermodynamically discussed.IntroductionOver the past several years, the demand for highly conductive and high strength copper-based alloys, such as Cu-Cr, Cu-Zr and Cu-Cr-Zr for use in electronic materials has increased.1 -7 These alloying elements are very reactive and easily oxidized to form oxide inclusions during melting. To avoid the oxide inclusions, it may be effective to utilize the strong reducing power of carbon in conditions under which no carbides form.In this study, to provide fundamental data for producing Cu-RE( rare earth) alloys without any inclusions, the solubility of rare earth in liquid copper in equilibrium with .carbon .was determined and discussed on the basis of the experimental results and the thermodynamic data.ExperimentalSample preparation for equilibrium experimentsOxygen-free copper (99.99%), lanthanum (99.9%), gadolinium (99.9%), neodymium (99.9%), cerium (99.9%) and yttrium (99.9%), and their oxides were used as starting materials.Each rare earth carbide was prepared by mixing rare earth oxide with carbon, which is a little more than the stoichiometric composition, pressing it into a tablet form and sintering at about 2000.K for 20 ks in a vacuum furnace using a graphite crucible. Powder X-ray analysis showed that only the carbon and rare earth carbide (REC2) was present in each sample.Cu-RE mother alloys (5-20 mass % RE) were prepared beforehand by mixing metallic rare earth with oxygen-free copper, and melting in an electric arc furnace."

Jan 1, 2000