By Jilai Xue

Fe-Ni alloys can be used as raw material in making stainless steel. Laterite nickel ore is one of mineral resources for producing nickel alloys. In this work, the laterite ore after dehydration at 800 °C and the anthracite as reducing agent were mixed for pre-reduction at 900 °C, and then reduced to form Fe-Ni alloys at 1550-1620 °C through carbon-thermal reduction process. A high Ni-content alloy component in the metallurgical mixture can be formed through pre-reduction. Better separation of the resulting metals from the slag is found with lower Ni-content alloys produced or higher temperatures during reduction. An effective processing of Fe-Ni alloys needs further understanding of the process fundamentals and optimizing of the process parameters.

Jan 1, 2010

By A. L. D. Skury

In the synthesis of diamond, the precursor graphite must present a degree of crystallinity to assure optimum yield and quality for the transformed crystals. X-ray diffraction, SEM and TEM analyses were carried out to investigate the structural and morphologic transformations produced in natural graphite by high pressure-high temperature treatment. The present study had as its objective to characterize the morphological and structural changes suffered by a natural graphite that was subjected to high pressure and high temperature treatments in the region of diamond thermodynamic stability. The results indicate that the material that constitutes the gasket, for the deformable capsule, could act as catalyst in the graphite recrystallization process.

Jan 1, 2006

By Bowen Li

Silicon Carbide is an excellent refractory material. Its physical properties make it extremely useful, particularly in applications where corrosion resistance and wear are important considerations. Commercial silicon carbide refractory is frequently manufactured by bonding silicon carbide particles with clay; however, clay may cause problems in the sintered products. This study investigates the potential of replacing a portion of the clay with andalusite powder. The results show that micron size andalusite powder can improve not only the strength of the refractory but also the sinterability. The mechanisms for these improvements are discussed.

Jan 1, 2006

By Bowen Li

Andalusite is an excellent raw material for refractory applications due to its high aluminum oxide content and phase transformation to mullite at high temperature. Granular andalusite in particle sizes of about 1 to 2 mm was traditionally utilized for the manufacturing of refractory brick. However, if powder andalusite in micron particle size is utilized in high-alumina refractory products, reinforcement on the refractory brick can be obtained and the sintering temperature can be decreased. The phase transformation of powder andalusite plays a key role for the difference.

Jan 1, 2006

By C. E. M. Meskers

End-of-life Electronic and Electrical Equipment, o_cially called WEEE, is unjustly regarded as mainly a waste management problem. What is structurally overlooked is the enormous resource impact of these devices. EEE rep- resents a tremendous metal resource, which should be uti- lized through e_ective recycling, which has a much lower environmental footprint than primary production. The actual amount of end-of-life EEE recycled today is embar- rassingly low since insu_cient EEE is collected and part of the collected EEE is exported to developing countries, where it is largely not entering o_cial recycling systems. To achieve a global recycling society issues like technol- ogy, economics, life cycle structure, stakeholder aware- ness and legislation have to be addressed in a global, co-operative manner so that sustainable closed product cycles can be obtained. Requirements for a "global re- cycling society" are de_ned to address today's reality of global ows of used consumer products, taking into ac- count the likely needs of the future.

Jan 1, 2009

By Hector Carreon

Due to elevated temperatures, excessive stresses and severed corrosion conditions, turbine engine components are subject to creep processes that limit the components life such as a turbine bucket. The failure mechanism of a turbine bucket is related primarily to creep and corrosion and secondarily to thermal fatigue. As a result, it is desirable to assess the current condition of such turbine component. By using eddy current images, it was shown that the eddy current technique could be used to monitor creep damage in a nickel base super-alloy. The eddy current results also show a significative variation in the electrical conductivity on the creep damage zone with respect to the background zone in nickel-base super-alloy samples. In addition, the absolute thermoelectric power coefficient show also a strong dependence associated with creep damage in nickel base super-alloy samples using a copper hot tip reference. The eddy current and thermoelectric power techniques seems to show promise as nondestructive evaluation tools for monitoring the level of creep damage in metallic alloys.

Jan 1, 2010

By Sadegh Firoozi

Experiments measuring the kinetics of oxidation and making visual observations of the oxidation of approximately 6 g static lead baths containing arsenic, antimony and tin were conducted in the temperature range from 500 to 600 oC. A range of repeatable behaviours were observed, notably: the formation of a coherent, solid oxide layers on pure lead and lead-tin alloys; the formation of liquid oxide droplets during the initial oxidation of lead-arsenic and lead-antimony alloys and the eventual formation of a complete oxide layer covering the entire free surface of these alloys. Thermogravimetric measurements revealed that the rate of oxygen uptake was strongly influenced by the form of oxides being generated at the melt/gas interface. Compared to the rates of oxidation of pure lead, arsenic increased the rate of oxygen uptake throughout the temperature range via the formation of liquid oxidation products. The presence of antimony resulted in a moderate increase in the rate of oxygen uptake as compared to arsenic. Tin was effective in lowering the rate of oxidation even in the presence of arsenic because the oxidation product was always a coherent layer that acted as a physical barrier to oxygen transport to the underlying alloy.

Jan 1, 2006

By Paul-Dominique Oudenne

For many years, CMI NESA has gained considerable experience in the field of alternative thermal processing processes by which useful by products result in addition to the destruction of the raw wastes. The CMI NESA pyrolysis process has been extensively applied to a wide range of sewage, industrial sludge and residues. This paper describes in details the development works carried out at the pilot stage as well as the key parameters of the process. Some of the industrial realisations are briefly described, the most recent one being the erection of a sludge pyrolyser on predried sludge at 90% dryness of a capacity of 100 tons of dry matter per day for the Valenton plant of the SIAAP (city of Paris).

Jan 1, 2006

By Xiaowen Liu

The DSC/TG, IR and XRD analysis were used to characterize the heating phase transformation of illite, which came from Ouhai deposit, China. It was discovered that the dehydration and de-hydroxylation of illite carried out stage by stage during heating. The adsorptive water and layer-inter water were dehydrated from room temperature to 500°C; and dehydroxylated in the range 500°C~800°C. In these stages of process, illite?s layer structure kept almost unchanged. After 800°Cillite began to change into disorder structure. At about 1100°C, the layer structure of illite had been destroyed, and amorphous SiO2 and mullite crystallite appeared. At about 1200°C the structure of illite completely destroyed and mullite crystal phase had become perfect..

Jan 1, 2006

By A. J. Sideris

It is known that Mg can act as a catalyst/solvent in the high pressure high temperature diamond synthesis. However, above pressure levels of the order of 7 GPa, and temperatures from 1700 ? 1800oC, it was not possible yet to use Mg for the industrial production of diamond. A possible alternative is the use of MgNi based alloys. However, owing to the great Mg reactivity, it was consider, so far, a difficult task to deal with such alloys. The present work presents successful results regarding the production of MgNi alloys, with different composition, at high pressure conditions. The behavior of the alloys and their microstructural characterization is analyzed.

Jan 1, 2006

By Cem Colakoglu

In this study, nickel containing iron alloys were produced by carbothermal reduction of lateritic nickel ores obtained from Manisa - Caldag region of Turkiye in order to investigate the reaction mechanism of nickel and cobalt. In the experiments, the lateritic ore containing 1.58 wt.% Ni and 0.12 wt.% Co was calcined in a semi-pilot scale rotary furnace at 1100°C for 1 hour. Then, a mixture of calcined ore and metallurgical coke was reacted in sintered alumina crucibles using a graphite resistance tube furnace at different time (0- 60 min) and temperature (1500-1600°C).

Jan 1, 2009

By Ramona Prillhofer

Salt slag is a waste product produced by the recycling of aluminum. In most European countries (e.g. Austria, Germany) the landfill disposal of this waste is forbidden because the slag contains soluble salts and these represent a potential source of pollution to the surface and groundwater. Additionally, consisting metal and some compounds in the salt slag can react with water and resulting from this, noxious gases are generated. The recovery of useful materials from these wastes is accordingly both environmentally necessary and economically feasible. This study describes a complete recycling-process for the salt slag, which includes a leaching-cristallization-process to obtain the oxidic residue, a pyrometallurgical-step to clear the oxidic residue and finally an extensive characterization of the achieved products. Due to the increasing price of raw materials, the utilization of the oxidic residue into commercial products has been investigated and application possibilities will be discussed.

Jan 1, 2009

By Linli Wu

During the measurement of contact angle, a misty band was observed near the substrate. Hsien-Nan Ho and Shinn-Tyan Wu thought this was because the oxygen atoms on the interface migrate to the droplet surface to form an oxide band near the substrate. But from our experiments misty band appeared before the drop reach to the substrate. Theoretically speaking, the oxygen partial was the same everywhere in the vacuum furnace. So there was no condition to provide enough oxygen forming oxide. This appearance would be explained more reasonably with the optics principle. Most reflected light would be absorbed by the substrate and the light cannot reach the observation area, so the misty band formed.

Jan 1, 2006

By Xuan Li

Aluminum slag is generated when aluminum metals are recycled through a smelting process in the presence of salt. There are small amounts of aluminum metals trapped in the aluminum slag. This research aims at evaluating the use of aluminum slag as an expansion agent for the production of lightweight concrete by taking advantage of the residual aluminum metals in the slag. The research identified key elements of producing lightweight concrete products through utilizing various mixture components including sodium hydroxide (NaOH), lime (CaO), cement, and gypsum. The volumetric expansion rate was investigated and the density and strength of the products were determined. The results show that aluminum slag can be utilized for the production of lightweight concrete products.

Jan 1, 2010

By Tianjiao Luo

The electroless copper plating process for continuous carbon fiber using CuSO4?5H2O as the main salt and formaldehyde as reducing agent was experimentally studied, including the effects of pH values and concentration of chelating agents, stabilizing agents and reducing agent on the electroless plating process. The surface morphology and the composition of coating were investigated by means of Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS), and deposited the coating thickness was measured by way of dissolution. The results indicated that the pretreatment of carbon fiber before plating was so important. This pretreatment could prevent the formation of the black cores, furthermore, it could form many active absorption cores with Ag as the center on the carbon fiber surface. Used the optimized parameters in this process, which led to a stable solution for plating, a homogeneous copper coating was conducted with the carbon fiber plated with favorable mechanical performance and high adhesion strength.

Jan 1, 2006

By A. Gibson

Most methods for the treatment of scrap printed circuit boards do not reclaim the components in working order as the boards are either fed to a copper smelter, to recover the valuable elements, or, simply landfilled. This work reports the dissolution of the solder in fluoroboric acid containing Ti4+ ions which was particularly selective for solder, allowing the components to be recovered. The solder was subsequently electrowon from the leachant. The boards were then shredded and the copper dissolved in ammonium sulfate and, then treated via solvent extraction to give an electrolyte suitable for electrowinning. The remainder of the metals were dissolved aqua regia, silver remained unattacked by the aqua regia, palladium precipitated as Pd(NH4)Cl6 in the presence of zinc and nickel, the gold was removed by solvent extraction and precipitated as nanoparticles. The aqua regia was then diluted and the zinc and nickel separated by solvent extraction.

Jan 1, 2009

By Clara María Lamus Molina

The following minerals found in the residual black sands from gold mining in El Bagre Antioquia (Colombia) were identified as having major economic interest: Ilmenite (FeTiO3), with an average of 49% of TiO2, frequently altered presenting crowns; lamellaes of rutile and alteration textures; titanomagnetite with up to 25% of TiO2; magnetite (Fe3O4) in individual grains or associated with others minerals as hematite and ferromagnesian silicates rutile (TiO2) with considerable quantities of Nb2O5(0.1-3.7%Wt); zircon (ZrSiO4) with 66%Wt of ZrO2 and monazite with an average of 63.43%Wt of REE, this frequently associated to xenotime and thorite forming textures as little drops. Analysis in EPMA and SEM/EDS showed percentages of minor elements and traces, thereby clearly establishing the applications of these minerals in diverse industries. Furthermore, a detailed granumetric study of the different minerals and textural relationships among them also allowed for establishing the basis for possible processing and exploitation.

Jan 1, 2006

By Kunihiko Takahashi, Gjergj Dodbiba, Hisayoshi Umeda, Toyohisa Fujita

"An increasing number of mobile phones is increasing the number of the discarded mobile phones. Many efforts are thus being made to collect and recycle these devices. This paper is a short introduction of the recycling system of precious metals from the discarded mobile phone, currently available in Japan. Moreover, an attempt has been made to compare the energy recovery and the mechanical recycling of plastic wastes from the discarded mobile phone. The assessment has been carried out in the context of the life cycle assessment methodology (LCA). The environmental impact of each option was assessed by calculating the following impact indicators: depletion of abiotic resources (ADP), and global warming potential (GWP). 1. Introduction In 2003, the demand for mobile phones was increased since the camera was included in a mobile phone and the 3rd generation of mobile phones was introduced. In turn, the number of discarded mobile phone is rising sharply. Generally speaking, all the metallic parts of mobile phones can be recovered and recycled by using smelting and purification techniques. The recycled materials are then used to fabricate other new products."

Jan 1, 2008

By Taegong Ryu

A thermal plasma process was used to synthesize nanosized tungsten carbide -cobalt composite powder, in which ammonium paratungstate and cobalt oxide were reacted with a gas mixture containing CH4, H2 and Ar. The reduction and carburization of vaporized precursors produced nanosized tungsten carbide (WC1-x) - cobalt composite powder, which sometimes contained small amounts of W2C and/or W phase. The effects of gas composition, plasma torch power, and the flow rate of plasma gas on the product composition and grain size were investigated. The grain size of synthesized tungsten carbide powder was less than 20 nm. The synthesized composite powders were also subjected to a hydrogen heat treatment to fully carburize WC1-x, W2C, and W phases to the WC phase as well as to remove excess carbon in the product. Finally nanosized WC-Co composite powder of grain size less than 50 nm was obtained.

Jan 1, 2009

Gas-liquid contacting in the packed bed is a common operation in metallurgical reactors. Research has shown that, unlike wetting flow, non-wetting liquid flows in the form of discrete droplets or rivulets. Thus, modeling of the liquid phase as a continuum is in contradiction to the observations. Also, for the non-wetting case, continuum models have failed to describe liquid flow path when the liquid source is a point source. The aim of the current work is to put forward a combined Lagrangian-Eulerian approach to model the liquid and gas flow in the packed bed. Liquid is assumed discrete and modeled using a force balance approach. Gas is assumed to be interpenetrating continua and modeled using k-emodel for turbulent flow. Structured packing is assumed and x- ray imaging technique is used to visualize liquid flow lines in the bed. Simulation results for liquid flow path compared with the experiments.

Jan 1, 2006