By John R. Lewis

DURING the past few years there has been considerable interest in the sizing and the preparation of the iron ore fed into blast furnaces. Furnacemen know that proper sizing of ore tends to increase the efficiency of the furnace. It has been shown by Joseph1 and his associates that there is a direct relationship between the porosity of an ore particle and the time required for its reduction in the blast furnace. This relationship may be stated as follows: All other factors remaining constant, the time for reduction of a given sample of ore is inversely proportional to its porosity. As a consequence, large pieces of very porous ore, say 3 or 4 in. in cross section, will be completely reduced by the time they reach the hot zone just above the tuyeres, while large pieces of dense, nonporous ore may reach the hot zone with their centers unreduced. This means that for the latter complete reduction will be accomplished by the so-called "direct method;" i.e., where carbon reacts directly with the ore. Some recent work by Philbrook2 seems to contradict this rule. He found that of two unlike ores he studied, the one with the lower porosity reduced more readily. He explained his results as "possibly due to an apparently greater tendency of the `A' ore (lower porosity) to crack during preliminary dehydration and during reduction." This brings his results in line with the rule stated above. It is not the author's intention to enter into a discussion of the merits of "direct" versus "indirect" reduction. It is enough to say that, in general, indirect reduction is desirable. For the greatest efficiency, Gruner's theorem3 requires that all reduction in the blast furnace be indirect. Joseph seems to believe this also, because in his recent article on Some Comparisons between Iron Ore, Sinter and Nodules as Blast Furnace Feed' he concludes that: "In general, the carbon in blast-furnace coke is used most efficiently when the largest amount of the carbon charged reaches the tuyeres." However, P. V. Martin,' in an excellent paper, has shown that some direct reduction may actually increase the efficiency of the furnace; that is, increase its rate of production while maintaining maximum fuel economy. For nonporous ores there is more opportunity to have an excess of direct reduction unless the factors that make for indirect reduction are favored; for instance; the proper sizing of the ore particles. Another factor that has an important bearing on the reduction rate, as it is affected by particle size, is the flow of heat into the particle. The ore particle

Jan 1, 1947

By R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-C and Fe-Ni solid-solution alloys has been investigated at 25°C. It is found that the rate of solid-solution strengthening is dependent upon the strain at which the yield stress is measured, the macroyield stress being much more concentration-dependent than the microyield stress. In fact the addition of nickel does not lead to any increase in the microyield stress of iron. The primary effect of increasing the carbon or nickel content is to increase the slope of the stress-strain curve in the microyield region; this effect has been correlated, by means of transmission electron microscopy, with a decreased ability of the dislocations to cross-slip. It is concluded that the Mott-Nabarro theory is a good description of true solid-solution hardening in these and other iron-base alloys. A.LL theories of the solid-solution strengthening1-4 indicate that the flow stress of an alloy increases both with solute concentration and "misfit" between the solvent and solute atoms. The functional relationship between strength, solute concentration, C, and misfit depends upon the particular theory. Mott and Nabarro1,2 and Schoeck and Seeger3 both predict a linear increase in strength with concentration, while Fleischer4 indicates that the strength should be proportional to C1/2; there are in the literature experimental observations to support both these compositional dependencies.1'8 The experimental evidence used to support the theories is the change in macroscopic yield stress (strain, e, = 10-3) with composition. However, recent investigations have revealed that solid-solution strengthening in a Cu-Al single crystals7 and in Fe-V polycrystal-line" alloys depends upon the strain at which the flow stress is measured; a flow stress in the microplastic range (e = 10-6 to 10-5) is much less concentration-dependent than the macroyield stress. Since the theories of solid-solution strengthening are concerned in particular with the stress to move a dislocation in a dislocation-free matrix, they should only be compared with microyield-stress data; it will be shown that in a material deforming homogeneously the microyield stress (e = 10-6) is approximately the stress to move through the matrix those dislocations which have been nucleated by stress concentrations such as particles or grain boundary ledges.9-11 In contrast, the macro-yield stress is more complex in that it is affected by several phenomena: dislocation multiplication, dislocation interactions, and the ease of propagating slip across grain boundaries. For example, it is experimentally observed that when long-range order12'13 or solute effects10 restrict cross alip the grain boundary

Jan 1, 1967

By James K. Stanley

IRON-COBALT alloys in the range of 35-50 pct cobalt are of interest in the electrical industry because they possess the highest magnetic saturation of any magnetic material known.1,2 The magnetic saturation induction of the 35 pct alloy is 24,200 gausses, compared to 21,600 for pure iron (Fig I). This difference is significant in electrical apparatus, where weight or space is at a premium. Saturation values higher than that for iron can be attained up to about 70 pct Co but economics restrict the use to as low a cobalt content as possible without sacrifice of saturation. Fig 2 shows the iron-cobalt equilibrium diagram. Up to the present time, two factors have retarded the use of iron-cobalt alloys in the electrical industry for magnetic purposes.† One is the high cost of cobalt ($1.50 per pound) and the other is the inherent brittleness of the binary iron-cobalt alloys. Straight iron-cobalt alloys up to 25 pct cobalt are ductile and easy to process to thin sheet or strip by conventional methods of hot and cold rolling, but the alloys containing higher percentages of cobalt, including those for which the saturation magnetization is a maximum (35 to 40 pct), are increasingly brittle with increasing cobalt, at least up to 50 pct, and are consequently difficult to process, either hot or cold. Work by White and Wah13 indicated that iron-cobalt alloys could be made ductile by alloying with vanadium, and after quenching the alloys (vanadium up to about 4 pct) were found to be cold rollable to very thin gauges. With this as a background, we resumed our work on these alloys with the objective of developing methods for economical commercial production of wide strip. For this purpose we have concentrated on the 35 pct alloy in order to obtain the highest possible saturation value. Experiments were carried out on many alloy additions to the iron-cobalt alloys and on the response of these compositions to heat treatments. This work finally culminated in a commercially producible iron-cobalt alloy which has been named Hiperco. * MATERIALS STUDIED AND PROCEDURE Binary alloys of iron and cobalt in the range of 35 pct cobalt are difficult to hot work (by forging or rolling) without such additions as C, Mn, Si, V, Cr, Mo, W or perhaps others. Another beneficial effect of such additions is that they in-crease to a greater or less extent the strangely low electrical resistivity of these alloys (about 10 microohms per cm3

Jan 1, 1947

By Sylvan Z. Beer

Aluminum phosphide was synthesized and grown in solution of excess aluminum using a modified two-temperature technique. An inversion in the density difference between ALP and molten aluminum takes place at about 1100°. Dispersed nuclei can act as sources for further crystal growth in a manner resembling ripening. Advantage was taken of this phenomenon by introducing a stirring motion into the molten liquid. This was done with a split-phase 10-kH2 rotating magnetic field produced by four horizontal coils placed symmetrically about the furnace at the level of the molten metal. The method also prevents the formation of a surface film which would impede the reaction. By this technique vastly improved yields were obtained and flat crystals 5 by 5 by 0.5 mm were grown at lower temperatures and at greater rates than heretofore. THE family of III-V intermetallic compounds has received much attention since the prediction of their semiconducting properties in the early 1950s. Of the family, A1P has perhaps the highest band gap of those compounds normally possessing the zinc-blende structure. But it has been least studied because it is difficult to handle and grow. The handling difficulties have been dealt with elsewhere and it is sufficient to say here that, by various techniques, many of the difficulties can be overcome.' The difficulties encountered in crystal growth can be related to the refractory nature of A1P and in turn to its high band gap. Because of the anticipated high melting point of the material and the accompanying high phosphorus vapor pressure, the reported work on synthesis and growth was done by epitaxial synthesis-growth via chlorine2 and iodine3 transport and from solution of excess aluminum by the two-temperature technique.4'5 The transport-grown crystals take on the dimensions of the substrate but do not grow easily in thickness. In the usual two-temperature technique as applied on the synthesis of Alp, the temperature of the molten aluminum is kept at 1000° to 1250°C while the phosphorus is maintained at 1 to 20 atm. A thin film of aluminum phosphide and oxide form immediately, impeding the reaction and affecting the yield. Attempts to grow the Alp from such solutions by the methods used to grow Gap and InP from excess gallium and indium have not been successful. As discussed in the preceding paper,5 the yield can be greatly increased

Jan 1, 1969

By O. Chanute

all of' level atid grade curve excepting Nos. 897, 898, 899, and 900, because of the impossibility of grouping them in the same nlonner, no two Iraving the chemical composition and physical prnprtiw as tho only v:iriubles. Phosphorus ~tnits have been taken to show the relatia h:wdnes. Of these 16 groups, 10 decidedly indicate slower wear firr tile harder rail. Of the remaining 6 groups, three (groups 2, 9, and 15) come well within the limits of error (.25 pound per yard) inherent in the palculation of the data as pointed out by Dr. Dndley; they catrnot, therefore, be considered tls exceptions. Group 2 and 15 arc but little outside of the limita of error. Rail 923 of group 9 is obviously abnornlal. This is probahly due to its being overheated, which the chemical analysis shows might easily be the case, and which the physical tc~ts and its low specific gravity tend to c-nfirm. We inry say, then, thnt 13 of these 16 groups fairly indicate, if they do not definitely point out, th:kt, under the same condition% tbe harder rail gives the slower wear. Of course, these comparisons are too few to enable us to arrive at positive ~?o-nclusions; but indications thus obtained are, I believe, fir more vsluitblc and tresttvc~rthy than those fhzt averages rvottld give us, mnde up from any ~lumhr of rails under intloy difi~rcal, conditions. Finally, it, seems to me, that the conclusions arrived at earlier in my remarks, together with, and confirmed by the last, show strong evidence that, under the same conditions, the harder rail will givc the slower wear. 0. C~~anute, New York CITY: We are very much shlipl, 1 ant sure, to Mr. Sandberg for his paper upn " Rail Ryaifications and Rail Inspertion in Europe." We have in thp United States bithhrto Been inspecting mils sonlewl~at haphazard, and we ore glad to gtbt tfie results of Mr. Sandberg's long experience. We recognize that he was an)ong the first, if not the very firwt, to iipply mare rittional and scientific rules to the designing of irou rails., niora recently, to adapt tlitve rules to the clesigtting of steel I':I~]R, to conform to the oapaljilities and rqniretnento of this new n1:ttcrial. Although we have generally adopted, in this country, sectinns for hteel rails which marly of our railway men think even bottar than those of Mr. Snlldlmrg, he is neverthelees the Ieat3er in foot.iito11~ we have followed ever since it has been est~blished

Jan 1, 1881

By L. K. Oliver, Marshall

The use of model studies for the development of invasion patterns for cycling is .illustrated by model studies obtained with a recently developed apparatus in the solution of actual cycling problems. Introduction Depletion of a gas reservoir by cycling under pressure maintenance may be divided into three general phases. In the first phase, injection of dry gas is used to move all possible wet gas to producing wells prior to breakthrough of appreciable quantities of dry gas into producing wells. In the second phase, injection moves additional wet gas to producing wells while moderate quantities of dry gas are being produced. The third phase consists of production without injection to deplete the commercial gas reserve which remains after the cycling operation. Thus, in the first phase, a portion of the reservoir is invaded by dry gas, and the dry gas usually displaces something less than 100 pct of the wet gas from the invaded portions of the reservoir. The second phase enlarges the invaded portion of the reservoir and, at the same time, increases recovery from that zone invaded by dry gas in the first phase of the cycling operation. The result is an early yield of a substantial quantity of the liquefiable hydrocarbons in the reservoir with a minimum of the retrograde losses which occur in some reservoirs. The overall recovery from such an operation is usually high. The summation of the paths taken by dry gas in a cycling operation can be termed an invasion pattern. The use of electrical models to predict invasion patterns has been the subject of several contributions to the literature.1-3 The results of such model studies as applied to actual cases has been discussed by Kelton4 and Miller and Lents.= Recently, an improved apparatus for conducting potentiometric model studies has been developed, as described by Lee.V he purpose of this paper is to present model studies or invasion patterns obtained with this instrument in the solution of actual cycling problems. The percentage of displacement of wet gas within the invaded portion of the reservoir in cycling, increase in recoveries of wet gas by continuing cycling after dry gas breakthrough, recoveries of wet and dry gas by production after cycling, or economic factors in cycling are beyond the scope of this paper. Discussions which follow will be limited entirely to the development of suitable invasion patterns for cycling under pressure maintenance and the use of model studies therein. Discussion OF Results In using model studies to predict invasion patterns in cycling, some factors which influence the results are the following:

Jan 1, 1948

By Marshall, L. K. Oliver

The use of model studies for the development of invasion patterns for cycling is .illustrated by model studies obtained with a recently developed apparatus in the solution of actual cycling problems. Introduction Depletion of a gas reservoir by cycling under pressure maintenance may be divided into three general phases. In the first phase, injection of dry gas is used to move all possible wet gas to producing wells prior to breakthrough of appreciable quantities of dry gas into producing wells. In the second phase, injection moves additional wet gas to producing wells while moderate quantities of dry gas are being produced. The third phase consists of production without injection to deplete the commercial gas reserve which remains after the cycling operation. Thus, in the first phase, a portion of the reservoir is invaded by dry gas, and the dry gas usually displaces something less than 100 pct of the wet gas from the invaded portions of the reservoir. The second phase enlarges the invaded portion of the reservoir and, at the same time, increases recovery from that zone invaded by dry gas in the first phase of the cycling operation. The result is an early yield of a substantial quantity of the liquefiable hydrocarbons in the reservoir with a minimum of the retrograde losses which occur in some reservoirs. The overall recovery from such an operation is usually high. The summation of the paths taken by dry gas in a cycling operation can be termed an invasion pattern. The use of electrical models to predict invasion patterns has been the subject of several contributions to the literature.1-3 The results of such model studies as applied to actual cases has been discussed by Kelton4 and Miller and Lents.= Recently, an improved apparatus for conducting potentiometric model studies has been developed, as described by Lee.V he purpose of this paper is to present model studies or invasion patterns obtained with this instrument in the solution of actual cycling problems. The percentage of displacement of wet gas within the invaded portion of the reservoir in cycling, increase in recoveries of wet gas by continuing cycling after dry gas breakthrough, recoveries of wet and dry gas by production after cycling, or economic factors in cycling are beyond the scope of this paper. Discussions which follow will be limited entirely to the development of suitable invasion patterns for cycling under pressure maintenance and the use of model studies therein. Discussion OF Results In using model studies to predict invasion patterns in cycling, some factors which influence the results are the following:

Jan 1, 1948

By J. F. Butler

The degree and type of carbide dispersion resulting from changes in the cooling rate from austenite determine the amount of carbon remaining in solution after slow cooling- from a subsequent subcritical annealing treatment. A difjusion model has been proposecl to explain the effect of carbide dispersion on the amount of carbon retained in solution and the amount of carbon in solution has been related to the degree of carbon strain aging. COTTRELL and Leak' have shown that the rate of strain aging in low-carbon steels is dependent upon the amount of carbon and nitrogen in solution. Carbon can be effectively removed from solution as Fe , C by quench aging at temperatures of 200" C or lower; however, the relatively higher solubility of nitrogen at these temperatures prevents sufficient removal of nitrogen as iron nitrides. For this reason, nitrogen in solution has been considered the major cause of strain aging in rimming grades of commercial low-carbon steels. Nitrogen can be effectively removed from solution and nonaging steel produced through the addition of aluminum to form the stable nitride, AlN; however, the aluminum also causes deoxidation resulting in a killed steel. III an attempt to produce a rimmed steel which was also nonaging, Morgan and Shyne 2 investigated tile strain-aging properties of low-carban steels containing boron and found that strain aging was suplx-essed in steels containing as little as 0.007 pet B. The original purpose of this investigation was to determine the mechanism of strain-aging suppression by boron. Early in the study, the function of boron was discovered to be much like that of aluminum in that the formation of a nitride, BN, removed the nitrogen from solution.' However, during the course of the investigation, an effect of heat treatment upon the strain-aging properties and the amount of carbon in solution was found which could be related to the microstructure of the steel. The purpose of this paper is to examine these relationships among heat treatment, microstructure, carbon in solution, and strain aging in steels where nondetectable amounts of nitrogen are present in solution. EXPERIMENTAL PROCEDURE The investigation was carried out using 0.030 in. by 12. in wire specimens which had been cold swaged and drawn to the final diameter. Table I lists the compositions of the low-carbon steels used. Those with 'V' designations were vacuum melted and cast; the alloys designated 'AISI' were prepared from high-purity iron obtained from the American

Jan 1, 1962

By J. K. Stanley

Iron-cobalt alloys in the range of 35-50 pct cobalt are of interest in the electrical industry because they possess the highest magnetic saturation of any magnetic material known. l1,2The magnetic saturation induction of the 35 pct alloy is 24,200 gausses, compared to 21,600 for pure iron (Fig I). This difference is significant in electrical apparatus, whcre weight or space is at a premium. Saturation values higher than that for iron can be attained up to about 70 pct CO hut economics restrict the use to as low a cobalt content as possible without sacrifice of saturation. Fig 2 shows the iron-cobalt equilibrium diagram. Up to the present time, two factors have retarded the use of iron-cobalt alloys in the electrical industry for magnetic purposes.? One is the high cost of cobalt ($I.50 per pound) and the other ig the inherent brittleness of the binary iron-cobalt alloys. Straight iron-cobalt alloys up to 25 pct cobalt are ductile and easy to process to thin sheet or strip by conventional methods of hot and cold rolling, but the alloys containing higher percentages of cobalt, including those for which the saturation magnetization is a maximum (35 to 40 pct), are increasingly brittle with increasing cobalt, at least up to 50 pct, and are consequently difficult to process, either hot or cold. Work by White and Rah13 indicated that iron-cobalt alloys could be made ductile by alloying with vanadium, and after quenching the alloys (vanadium up to about 4 pct) were found to he colt1 rollable to very thin gauges. With this as a background, we resumed our work on these alloys with the objective of developing methods for economical commercial production of wide strip. For this purpose we have concentrated on the 35 pct alloy in order to obtain the highest possible saturation value. Experiments were carried out on many alloy additions to the iron-cobalt alloys and on the response of these compositions to heat treatments. This work finally culminated in a commercially producible iron-cobalt alloy which has been named Hiperco.* Materials StudIEd and Procedur' Binary alloys of iron and cobalt in the range of 35 pct cobalt are difficult to hot work (by forging or rolling) without such additions as C, Mn, Si, V, Cr, Mo, W Or perhaps others. Another beneficial effect of such additions is that they increase to a greater or less extent the strangely low electrical resistivity of these alloys about 10 microohms per cm3

Jan 1, 1948

By J. K. Stanley

Iron-cobalt alloys in the range of 35-50 pct cobalt are of interest in the electrical industry because they possess the highest magnetic saturation of any magnetic material known. l1,2The magnetic saturation induction of the 35 pct alloy is 24,200 gausses, compared to 21,600 for pure iron (Fig I). This difference is significant in electrical apparatus, whcre weight or space is at a premium. Saturation values higher than that for iron can be attained up to about 70 pct CO hut economics restrict the use to as low a cobalt content as possible without sacrifice of saturation. Fig 2 shows the iron-cobalt equilibrium diagram. Up to the present time, two factors have retarded the use of iron-cobalt alloys in the electrical industry for magnetic purposes.? One is the high cost of cobalt ($I.50 per pound) and the other ig the inherent brittleness of the binary iron-cobalt alloys. Straight iron-cobalt alloys up to 25 pct cobalt are ductile and easy to process to thin sheet or strip by conventional methods of hot and cold rolling, but the alloys containing higher percentages of cobalt, including those for which the saturation magnetization is a maximum (35 to 40 pct), are increasingly brittle with increasing cobalt, at least up to 50 pct, and are consequently difficult to process, either hot or cold. Work by White and Rah13 indicated that iron-cobalt alloys could be made ductile by alloying with vanadium, and after quenching the alloys (vanadium up to about 4 pct) were found to he colt1 rollable to very thin gauges. With this as a background, we resumed our work on these alloys with the objective of developing methods for economical commercial production of wide strip. For this purpose we have concentrated on the 35 pct alloy in order to obtain the highest possible saturation value. Experiments were carried out on many alloy additions to the iron-cobalt alloys and on the response of these compositions to heat treatments. This work finally culminated in a commercially producible iron-cobalt alloy which has been named Hiperco.* Materials StudIEd and Procedur' Binary alloys of iron and cobalt in the range of 35 pct cobalt are difficult to hot work (by forging or rolling) without such additions as C, Mn, Si, V, Cr, Mo, W Or perhaps others. Another beneficial effect of such additions is that they increase to a greater or less extent the strangely low electrical resistivity of these alloys about 10 microohms per cm3

Jan 1, 1948

By Carl F. Floe, John Chipman

THE system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or C02 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modem metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100° to 1500°C., and pressures from about 20 mm. of mercury to somewhat above atmospheric. REVIEW OF PREVIOUS WORK The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as 02, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: [2M -}-G2 = 2MGK =G) IYf X[I]] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: [MG = Ki Pa,[2]] Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: [6Cu + S02 = Cu2S + 2Cu20[3] K Cu2S X (Cu20)2(Cu)e(Psm)[4]] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: [K1 =or Vdo,= K2/PBO [5] PsO]

Jan 1, 1941

By E. DeGoyler

The Furbero oil field lies in the Gulf coastal plain of Mexico between the important ports of Tampico and Vera Cruz and about one-third of the distance between the two points from the latter (Lat. 20" 22' N., 97" 30' W. Gren.). It is in the State of Vera Cruz, about 14 miles west by south of the village of Papantla in the canton of the same name, and is the most southern of the developed oil fields of the Tampico-Tuxpam region being a distance of 50 miles south by east from the Potrero del Llano field and 42 miles in the same direction from the Alamo field. The field has been developed by the Oil Fields of Mexico Co. and is in the midst of a large block of lands owned or leased by them. Communication is through the port of Tuxpam with which it is connected by a narrow-gauge railway and 6-in. pipe line some 52 miles in length. This field is of more than ordinary interest since it represents a type of oil deposit hitherto unknown. So far as I am aware, no other commercially valuable deposit of oil is known to occur under conditions of accumulation similar to those found here. The igneous nature of the so-called 'sand' encountered in drilling was not recognized until a number of wells had been drilled; and it was not until recently that the geological relations of the sill or laccolith, which gives rise to the accumulation of oil, were known and the so-called 'anticline' was known to be, in part at least, the result of igneous intrusion. Geological surveys in this general region were made in 1900-1901 by W. H. Dalton and in 1907-1909 by P. C. A. Stewart, F. W. Moon, Leonard V. Dalton, and Dr. Max Muhlberg. More recent surveys have been made, however, under the direction of the author, by E. L. Ickes, B. C. Belt, B. Hartley, and Harve Loomis. Notes of the earlier examinations were not available with the exception of the report by Dr. Muhlberg who apparently first recognized the true nature of the Furbero intrusion. This paper is indebted to his work and that of the more recent surveys for much of the detail regarding stratigraphy and to Messrs. Percy Furber and Arthur C. Payne, President and General Manager of the Oil Fields of Mexico Go. for permission to publish, and for much of the in-

Jan 1, 1916

By J. B. Warriner

S. A. TAYLOR, Pittsburgh, Pa.-What was the distance of haul? J. B. WARRINER.-There is practically no limit to the haul. The length is determined entirely by the feasible location for a dump. -I have known of hauls up to 2 miles in length. R. V. NORRIS, Wilkes-Barre, Pa.-This paper was originally presented to the Anthracite Section as the result of the appointment of Mr. Warriner as the Chairman of the committee to study this matter and present this paper. As he has stated, he obtained data very freely from all the stripping operations in the region, and it is a type of paper of which we should have more in the Transactions. Two or three things in it strike me as particularly valuable. The two tables, 1 and 2, showing the coal remaining, have been the result of a great amount of study, as it is not an easy matter to obtain data as to the amount of coal left in mining. As an example, one of the, anthracite mines was mined and robbed out in 1850, so the maps show. That mine is today producing 250,000 tons of coal, over 50 per cent. from the bed which on the maps is marked as exhausted. What actually happened is that the seam was on a light pitch inconvenient to mine. There was ample thickness of coal and the chambers were driven at a convenient pitch through this 30,-ft. bed, leaving top and bottom, taking out about 10 ft. The pillars were removed and the working caved and marked as gone. That is the type of area that is now being stripped, which explains the reason for the enormous amount of coal left in, and the fact that Mr. Warriner has worked out the actual results from a large number of strippings is of great interest to the operators in any region handling thick coal which has been mined over in the past, generation. The modern mining, of course, is different. We do not have all the coal we want in big veins, and we do not mine it that way. Another interesting feature of the paper to me was the study of losses. It is not uncommon to assume that after you have stripped off the overburden all the coal goes to market. Mr. Warriner has shown that there is a loss ranging up to 10 or 15 per cent. that does not go, so 'that estimates made on stripping, figuring on all the coal, are subject to this very material correction.

Jan 4, 1917

By W. E. Wrather

SERIOUS consideration was given by the Petroleum Division to a wide variety of subjects, during six busy sessions at the Annual Meeting. Beginning with a joint session on engineering research and production engineering, Tuesday afternoon, conducted by E. A. Stephenson and H. C. Fowler, problems of petroleum technology, domestic and foreign production, proved oil re- serves, economics, and stabilization were mooied almost without interruption until nearly everyone was "talked out,' and the meeting was adjourned at the end of the annual Petroleum Division dinner, late Thursday night.

Jan 1, 1933

By Sherwin F. Kelly

THE present lull in engineering activities presents an advantageous moment for inquiring into the position now occupied by geophysics in its various fields of application. The recent over-expansion in all lines of work resulted in an uncritical employment of these methods of exploration which was bound to have its harmful reaction. The pendulum has now swung back, producing a decidedly hypercritical attitude toward the new science that had been recently welcomed so joyfully as the panacea for prospecting troubles. The severe retrenchment in exploration has forced upon us a period of waiting and, it is to be hoped, of profitable contemplation. This can well be employed in trying to pass a reasoned judgment on what position geophysics should occupy in the new geological exploration programs that will inevitably ac- company the looked-for industrial recovery.

Jan 1, 1931

By Blamey Stevens

(San Francisco Meeting, October, 1911.) My previous paper is entitled, The Laws of Igneous Emanation Pressure. The present paper lays no claim to the exactitude and completeness of a law, since it is of a provisional nature and may be disregarded when experiments have established a basis for more exact reasoning. The general physical states in which aqueous emanations may occur are first considered. The possible physical conditions under which the mineral elements may occur in emanations are then discussed, and a classification of deposits, dependent on emanation, is proposed. A system of scientific experimental investigation is outlined, and it is shown that the physical and chemical properties of emanation may be exactly determined thereby. The investigation is urged as feasible and simple, and not necessarily requiring large and costly apparatus. It is the only step necessary to make possible the formulation of a complete set of laws of igneous emanation. Process of Emanation. In a rising column, magma ranges in temperature from 900° to 1,200°C. Exhalation must begin at some fairly great depth. What this depth may be we can only surmise, since no experimental evidence is available. Exhalation, however, continues as the magma flows upward, until at another level the occluded gases have all escaped. This depth is probably upward of 5,000 ft. (See Fig. 1.) All exhalations must come from between these two levels. As the whole emanation is the sum of the exhalations and residues, the residues must come from below the uppermost level. They will be most abundant when coming, from those parts of the intrusion which have solidified below the lower level.

Apr 1, 1912

By William A. Mitchell

AN X-ray diffraction pattern for "calcined cold precipitated ferric oxide" is reproduced dia-grammatically along with data for other iron oxides by R. C. Mackenzie.1' This pattern, which shows spacings higher than those for any other form of iron oxide, was obtained from material prepared and photographed at several different times over a period of weeks, but later attempts to reproduce the results were unsuccessful, the pattern of hematite being obtained every time.2 In an attempt to solve this problem, the original photographs showing the strange diffraction pattern were examined and a marked similarity to the hematite pattern was noticed, suggesting that the pattern was in fact due to hematite but corresponded to a shorter wavelength of X-rays than the Cu Ka which was assumed to have .been used. The eight strongest lines were provisionally identified with the strongest hematite lines and, by means of the corresponding hematite spacings, the X-ray wavelength was calculated for each line. This gave an almost constant value, with the exception of the innermost line which was somewhat diffuse, and confirmed the presence of hematite. The value obtained, 0.703 ± 0.015Å, corresponds to the molybdenum Ka wavelength. The X-ray tube used was a four-filament demountable tube with a copper target. Other photographs, mostly of soil clays, taken during the same period gave normal patterns of Cu Ka radiation with one exception. This was a calcined soil clay with a high iron content and also showed Mo Ka lines of the hematite structure. The explanation is almost certainly that the copper target was contaminated with molybdenum, but it is not known how this occurred. Specimens of alumino-silicates gave their normal Cu Ka pattern, but as the K absorption edge of iron is a little longer than the Cu Ka wavelength, specimens with a high iron content greatly reduced the intensity of the Cu Ka diffraction lines relative to that of the lines due to the shorter Mo Ka wavelength. The formation of hematite on calcining cold precipitated hydrated ferric oxide3 is thus confirmed. References R. C. Mackenzie: Investigations on Cold-precipi-tated Hydrated Ferric Oxide and its Origin in Clays. Problems of Clay and Laterite Genesis, p. 69, Fig. 4, F. AIME Symposium, St. Louis, Mo. Feb. 19-22, 1951. Published 1952. 'R. C. Mackenzie: Ref. 1. Note added on proof. V. C. Hansen and L. T. Brownmiller: Equilibrium Studies on Alumina and Ferric Oxide and on Combinations of These with Magnesia and Calcium Oxide. American Journal of Science (1928) 5, No. 15, pp. 225-242.

Jan 1, 1954

By D. C. Buffum, L. D. Jaffee

QUANTITATIVE measurements of the temper brittleness of steel are made by comparing the difference between embrittled and unembrittled specimens in the temperature of transition from ductile to brittle fracture. Since hardness affects the transition temperature, a study of the combined effects of hardness and temper brittleness appeared desirable. In this investigation a commercial SAE 3140 steel, which has been reported on previously in temper brittleness studies,* was used. Blanks from this steel were austenitized for 1 hr at 900°C and water quenched. The blanks were then divided into six groups and further heat treated as follows: Group 1—tempered at 675°C for 4 hr and water quenched; Groups 2, 3, 4, and 5—tempered at 675", 650°, 625', and 600 °C respectively for 1 hr and water quenched; and Group 6—tempered at 500°C for y2 hr and water quenched. Each of these groups was divided into two parts; one part was tested without further heat treatment, and the other was embrittled for 48 hr at 500°C and water quenched. Tempering treatments between 500" and 600°C were avoided because of the rapid embrittlement occurring in that range for this steel. The heat-treated blanks were machined into standard V-notched Charpy bars. Each group was tested over a range of temperatures on a 217 ft-lb Charpy machine. The energies necessary to fracture the bars and the percentage fibrous fracture of each bar were recorded. The transition temperatures were obtained from a plot of the percentage fibrous fracture as a function of testing temperature. They were taken as the lowest point on these curves at which the fracture was 100 pct fibrous. The transition temperatures for both embrittled and unembrittled specimens are presented in Fig. 1 as function of the hardness. It will be noticed in this figure that the point for the unembrittled condition at 21 Rockwell C is out of line. These specimens were tempered for 4 hr at 675 °C and this point indicated that under isothermal conditions at this temperature, as is well known, embrittlement may develop fast enough to more than offset the effects of softening. From this data, it was concluded that the difference between transition temperatures for the embrittled and unembrittled conditions at any given hardness, within the range of Rockwell C 24 % to 32lh, is constant. It is also concluded that, within the hardness range studied, the transition temperatures for embrittled and unembrittled specimens rise in a parallel fashion with an increase in hardness. The authors wish to acknowledge the assistance of Frank Carr in this work.

Jan 1, 1952

IN order that you may be expert in every phase of this art of parting, I wish to caution you upon twelve points, all necessary, so that you may know beforehand what may happen to you and what provision you must make to obtain good results. Understand that the gain derived from this art lies in carrying out the work that you wish to do accurately and with profit, which means nothing other than working with certainty and seeing that there is no loss of gold or silver [69v] or substance of anything that is valuable in itself. For, since everything lost is silver or gold, it is valuable however little. it may be, and many little things obviously make one large one; for gain increases gain, and loss, loss. Therefore, you will have as your first task to seek to have the materials that you are to use for making the aqua fortis of as perfect a nature as possible. I tell you this because the saltpeter is often weaker and of worse quality than the alum. For this reason it is necessary to make an effort to have it not only well refined and free from earthiness but also of a nature as powerful as pig [dung] saltpeter, the color of which tends strongly toward yellow. In order to work better, you also refine this again before you put it to use, as I shall tell you in its place. Likewise, see if you can get alum of the red kind that comes from the Levant or from Cartagena, for it costs less and is more powerful. Furthermore; see that you have a good number of well-formed cucurbits of properly purified glass not too large and of, equal content and size. Above all, see that they contain, no indentations, bubbles, folds, or scratches, especially, in the, body or in the bottom, because they break easily and the nature and great force of the acid pierces them by eating away, and makes a little hole. For this reason, cucurbits. are always divided into four grades; one is taken for making aqua fortis, another for drying the waters when they are laden with silver, the third for recovering the acids from the separations, and the fourth are either rejected as useless or dangerous, or are saved for recovering the whites or for some other service. Whoever wishes to practice this art well should remember to keep a large supply of cucurbits, receivers, and alembics. The third is the precaution which one must take in luting them; first, to

Jan 1, 1942

By R. J. Wasilewski

The resistivity of single crystal and of polycrystalline metal has been determined between 77° and 1500°K. At comparable purity, the resistivity of the poly crystalline metal differs from that calculated from the axial resistivity values. The observed anisotropy is briefly discussed. A zone refined titanium rod was obtained from F. J. Darnell.1 The hardness of this material varied between 52 and 64 Bhn, indicative of its high purity. Single-crystal specimens were cut out from a few large grains, elongated predominantly along <1120>. Resistance measurements were taken with specimens immersed in liquid nitrogen, solid CO,, and acetone, and at ice point, and then recorded continuously between room temperature and 1200" to 1250°C, throughout at least one full heating and cooling cycle at a rate of l° to 3°C per min. Four probe measurements were taken using spot-welded Pt wire 0.003 in. in diam as potential terminals, and the electromotive force drop was determined poten-tiometrically. A standard resistance, in series with the specimen, served to determine the dc current (generally about 80 ma) in the circuit. In order to eliminate spurious thermal electromotive forces, the circuit polarity was automatically reversed at 5-min intervals, and the mean of the two adjacent readings taken as the true electromotive force value. The discrepancy between the readings at reversed polarities was generally of the order of a few µ v, as all the spot-welded joints were contained within a volume of some 5 mm cube. The relative resistance (R T/R 273o) variation with temperature is tabulated below, and shown in Fig. 1, as measured during the first heating run. The discontinuous drop in resistance, corresponding to the a — ß transformation, started for both initial orientations at 1170°K; i.e., some 15°K above the accepted value of 882°C (1155°K). Judging by the temperature ranse of transformation—some 30°K for the single crystal and 20°K for the polycrystal-line specimen—this difference is believed caused by the solution of the oxygen present initially on the surface of the specimens. The general trend of the resistance vs temperature shown in Fi,;. 1 is in qualitative agreement with that previously reported for polycrystalline titanium metal. 2,3 Significant anisotropy is, however, indicated by the crossing over of the curves for <1120> and <0001> orientations at 273°, 650°, and 1000°K. This difference is most startlingly shown in Fig. 2, where instantaneous temperature coefficients (l/R273 x dR /dT) are plotted for both the first heat-

Jan 1, 1962